By Raymond D. Daniels, Frank E. Rizzo, James D. Gerber

ThIS discussion describes a method for the addition of small amounts of oxygen to columbium (niobium) in an accurate and reproducible manner. The method is based on the complete reduction by columbium of a carefully weighed amount of another metal oxide. The equilibrium Pq associated with Cb-CbO mixtures is extremely low, e.g., 10"25 atm at 100O°C, and the pressures over Cb-0 solutions are even lower. The equilibrium Pq associated with a given metal-metal oxide mixture can be easily obtained, with the aid of a Richardson-Jeffes chart.' Although columbium should effectively reduce almost any metal-metal oxide combination, the proper choice of a metal-metal oxide system is complicated by the low rate of oxygen transport in the gas phase at low oxygen pressures and the difficulty in reducing any columbium suboxide formed during the reduction of the oxygen source material. Thermodynamically, oxide formation on columbium will be avoided so long as the oxygen partial pressure over the columbium is below the equilibrium pressure associated with the mixture Cb-CbO. The logical choice of a source for oxygen would appear to be a mixture of Cb-CbO, since oxide formation would be precluded by nucleation difficulty. But calculations using the kinetic theory of gasses indicate that, for a temperature of 900°C, the reaction would proceed too JAMES D. GERBER, formerly Research Assistant, University of Oklahoma, Norman, Okla., is Research Metallurgist, Air Force Weapons Test Laboratory, Kirtland Air Force Base, N. Mex. FRANK E. RIZZO, Junior Member AIME, formerly Assistant Professor of Metallurgy, University of Oklahoma, is Associate Professor of Metallurgy, University of Texas at El Paso, El Paso, Tex. RAYMOND D. DANIELS, Member AIME, Professor of Metallurgical Engineering, University of Oklahoma, is an NSF Fellow, Institute de MBtallurgie Structurale, Universite de euch:tel, Neuchitel, Switzerland. Manuscript submitted October 28, 1968. IMD

Jan 1, 1970

By R. W. Heckel, R. A. Tanzilli

ANALYTICAL results have previously been presented for the diffusion-controlled solution of a second phase in a finite medium for planar, cylindrical, and spherical geometries.' These results were obtained by numerical methods using digital computer techniques and are applicable not only to the stage of the problem where the unstable phase shrinks to zero size, but also the subsequent stage where the concentration gradients in the matrix phase become negligible (essentially complete homogenization). It is anticipated that the results of such an analysis may be of use to those workers who are interested in the processes

Jan 1, 1970

By R. M. Waterstrat

The phase VPt has been reported to have a crystal structure of the B19 (AuCd) type at low temperatures.''' A recent investigation3 has indicated that this phase forms by an ordering reaction from the disordered fcc Pt(V) solid solution which is stable at high temperatures. olander4 has shown that there exists a close structural relationship between the orthorhombic B19 structure and a fcc structure possessing the L1 , (CuAu) type of atomic ordering. One may derive the B19 structure by a shear-like displacement of the atoms in the (002) plane of the ordered fcc lattice along the (010) direction through a distance equal to one eighth of the unit cell dimension, see Fig. 1, followed by an orthorhombic distor; tion of the cube axes such that a = 2.693A. h = 4.413A. and c =4.767A (estimated uncertainty 0.005A). Filings of this phase were produced by grinding a VPt alloy having the B19 structure with a diamond dental grinding disc. When these filings were subjected to X-ray diffraction examination, a pattern of a severely cold-worked fcc structure was obtained. higher solution temperature used (1200 C) or to a much lower oxygen pressure than he reported, due to transfer through many bends and tubes in his complicated apparatus. An interesting observation was made when an oxygen addition was attempted in a cylindrical sample of columbium in the cold worked condition rather than in the annealed condition. The interior of the sample re-crystallized during the oxygen addition at 900°C. The periphery, however. (1 mm) did not recrystallize. A similar sample without oxygen recrystallized throughout the entire cross section. It appears that the re-crystallization is hindered by interstitial oxygen. Presumably, the interior recrystallized before appreciable oxygen could diffuse into the core. This work was supported by the United States Atomic Energy Commission. When the filings were annealed in a high vacuum furnace for 15 min at 110O0C, however. they returned to the B19 structure perhaps as a result of reordering. Subsequent less-severe cold-working of these filings by grinding in a hardened steel mortar and pestle at room temperature produced a transformation into a cold-worked L1, structure which was slightly tetragonal. Thus it appears that the degree of deformation may influence the final structure. Considerable line-broadening was observed in X-ray diffraction patterns obtained from the cold-worked filings and therefore no attempt was made to obtain accurate lattice parameters. Vacuum annealing treatments at 1100'C intended

Jan 1, 1970

By Edward A. Loria

Vanadium is one of the materials being considered for use in fast-breeder nuclear reactors. It is a good heat conductor and nearly transparent to radiation, properties regarded as ideal for nuclear fuel containers. The problem has been the metal lacks ductility needed for forming. In our program at Reno Laboratory the effects of the U.S. Bureau of Mines (previous affiliation) the effects of oxygen, nitrogen, and carbon have been reported21,22 nd most recently the effects of boron and boron with carbon.23 The continuing study by the Ames Laboratory of the effects of hydrogen, the most subtle and fugitive element in its relationship to structure and properties, is commendable. The solubility of oxygen, nitrogen, and hydrogen in vanadium (and other bcc metals as well) is related to material purity. With the available limit on metal purity and the interaction (clustering) of hydrogen with the other interstitial and substitutional elements present in their base metal, would the authors comment on the tolerance of hydrogen in relation to oxy- gen that will avoid intergranular fracture and above what content or how seriously harmful in oxygen at various carbon levels? Understanding the true effects of hydrogen (and other interstitial impurities) in vanadium depends on knowledge of the amount present under various conditions and its distribution between various possible positions. Significant amounts of hydrogen may be in "thermo-dynamic" solution, but not as individual atoms in interstitial positions. It may be in grain boundaries, in subgrain boundaries, in vacancies, or in dislocations. Some of the hydrogen may be paired or in complexes with impurities in substitutional solid solution in vanadium. This makes the analysis of the effect of hydrogen vastly more difficult. It should not be expected that hydrogen in grain boundaries will affect slip in the same manner as hydrogen in interstitial positions, nor will the complexes react to heat treatment the same way as hydrogen in dislocations. It is gratifying that the authors have quoted results from two of our inestiations,' but neglected one2' which applied the Petch theory to electrorefined vanadium of high purity and analyzed the effects of oxygen, nitrogen, and carbon on the ai and ky values obtained by the extrapolation and grain size methods. Details can be found in the paper. Briefly, we obtained a ui value of 10,300 psi (t = 5150 psi) at 273°K. The metal also exhibited profuse twinning with high ductility at 123" and 77°K. Nitrogen was more effective than oxygen in increasing ui, the increase being about twice as much for the same impurity level. Carbon additions resulted in only minimal changes in Ui. The corresponding ky increased as oxygen and nitrogen increased, with nitrogen being more effective. Carbon additions resulted in little change. Although the difference in yield strength of vanadium was explained on the basis of the Cottrell-Bilby model of the tearing away of dislocations from the impurity atoms,

Jan 1, 1970

By W. A. Backofen, N. E. Paton

DEFORMATION twinning contributes to the plasticity of titanium and has been reported on {10i2}, {1121},{11221}, {1123}, and {1124} planes.' Twinning on {1011} has also been reported in commercially pure titanium as a result of quenching from 1000', but no reports of such twins occurring as a result of deformation alone are known to the authors. In this study single crystals grown from iodide titanium were compressed parallel to the c axis over the temperature range 25 to 800°C. From it has come evidence that (10il) deformation twins are the most common type between 400" and 800°C. Crystals about 6 mm high with a rectangular cross section measuring about 3 by 4 mm were used in the tests. Chemical analyses showed them to contain 220 to 250 ppm 0 arid 10 to 15 ppm N. The long axes of the crystals were made parallel to the c axis while the sides were parallel to (i100) and (1120), as shown in Fig. 1. The crystals were compressed between polished alumina platens with no lubrication, in a vacuum of 2 x lom5 torr. Between 25' and 300°C the predominant twinning mode was (11221, which is to be expected for this stress state. There was an abrupt change at 400°C, however, and from that temperature up to 800°C twinning took place almost entirely on (10i1 ). Twin planes were determined by the two-surface rnethd. Measurement of the crystal orientation within several (10i1) twins by means of polarized-light4 and transmission electron microscopy showed that the lattice reorientations were the same as those previously reported for the (10i l ) twinning in magnesium.' This reorientation is consistent with The calculated (10il ) twinning shear for titanium is 0.10, while that measured from surface offsets on a (1150) face, which is parallel to the shear direction, was about 0.15. Slip within the twins, or in the matrix adjacent to the twins, probably accounts for the larger measurement. Slip in both locations was judged to have occurred from observations on foils in the electron microscope.

Jan 1, 1970

By H. Biloni, H. R. Bertorello

GruZLESKI and winegard1 have recently reported on the origin and development of the cellular substructure in Sn-Cd eutectic unidirectionally grown with different amounts of constitutional supercooling (CS). This communication deals with the results obtained in a parallel study on the instability of a plane interface in Al-Cu eutectic unidirectionally grown. Similarities as well as differences with the results of these authors1 will be presented. A1-Cu eutectic alloy ingots of 99.999 pct purity were grown unidirectionally under different G/R ratios where G = thermal gradient in the liquid, R = solidification rate. The ingots were cut in slices perpendicular to the solidification axes and the substructure studied on parallel sections following the sense of growth. It was generally found that the last part of the ingot to solidify presented a well developed colony substructure as a result of impurity build up and constitutional supercooling. The results obtained were: 1) When the structure was observed with low niagnification (of the order of 150 to 300 times) the first instabilities were observed at the grain boundaries and node-like structures formed at the junctions of the growth-induced boundaries, as reported by Gruz-leski and Winegard.1 Inside the grains the first signs of instability appear later and correspond to the type shown in Fig. 1; this is a two dimensional cell substructure. ' 2) Figs. 2 and 3 correspond to the evolution from a two dimensional substructure to a cellular type. In the A1-Cu eutectic the boundaries of the two dimensional cell are always perpendicular to the laniellaes instead of parallel as in the Sn-Cd eutectic. 1

Jan 1, 1970

By P. O. Metz, E. L. Wiehe, J. S. Foster

BASED on their analyses of growth kinetics, ibbs' and Harris et al.' have recently proposed that the rate of subcritical graphitization of steel is controlled by the rate of diffusion of carbon in ferrite. illert has concluded that this is the rate controlling growth mechanism when the growing graphite particles are relatively large. Harris et al.' also propose that the matrix surrounding a growing graphite particle is plastically deformed to make room for the growing particle. If this plastic deformation does occur, then preferred recrystallization may be observed around the larger particles. If diffusion of carbon in ferrite is rate controlling, then a graphite particle growing in a matrix of, say, tempered martensite or pearlite, should be surrounded by a carbide depleted zone. Thus, the simple metallographic experiments reported here are sufficient to determine whether or not diffusion of carbon in ferrite is the dominant mechanism for the growth of graphite in steel. The present investigation considers graphitization in five alloys. The compositions are given in Table I. Graphitization was carried out at three temperatures: 900°K (627"C), 950°K (677"C), and 990°K ('717°C). Samples were reacted in both the martensitic and the pearlitic initial conditions. In the hypoeutectoid steels, Sets 7 and 8, .and in the hypereutectoid Fe-C binary, Set 6, graphitization was very limited after 1000 hr at temperature. In these samples graphite particles observed were less than 10 p in diam. In the hypereutectoid commercial steels, Sets 1 and 3, large graphite particles (100 p) did not appear until after 250 hr at temperature. The limited number of graphite particles observed and the range of sizes obtained prohibited measurement of growth rates in this investigation. However, in all samples showing graphitization, neithe a carbide depleted zone nor recrystallization was observed. illert's model predicts that diffusion of carbon in ferrite should become dominant for graphite particles larger than about 300 p in diam. The largest graphite particle observed in this investigation was approximately 450 p in diam. No evidence of carbide depletion was noted. Fig. 1 shows a typical graphite particle. This nodule is from an initially pearlitic sample from Set 3 after

Jan 1, 1970

By R. E. Miner, J. K. Jackson, T. L. Wilson

THE nature of the decomposition reactions producing hardening in aluminum-rich A1-Ag alloys is now fairly well understood. The silver is not uniformly dispersed even at temperatures above the solvus line: rather, it is clustered into zones and associated with dislocations.' During quenching, nearly all of the silver segregates into zones' and some is attracted to dislocations, producing stacking faults. Growth of these faults produces the semicoherent y precipitate.1 During aging, the larger zones and the y precipitates grow at the expense of the smaller zones. The large zones persist up to about 350°C; where they redissolve in favor of the y' and y precipitates.' The equilibrium hcp y precipitate occurs both by a cellular reaction at the grain boundaries1 and by growth of the Y' plates to a critical size where incoherency results. Damask and Nowick 4 observed an internal friction peak in an A1-6 at. pct Ag alloy at about 140°C (0.25 cps). The peak was found to exhibit a systematic instability. After aging at successively higher temperatures between 155' and 23Z°C, the peak first migrated to higher temperatures while increasing in height, then returned to lower temperatures and decreased in height. After aging at temperatures above about 200°C, the peak position remained constant while the height decreased very slowly. In quenched specimens, elastic after-effect measurements inhcated a rapid initial transient in peak position from low temperatures up to 155°C. The authors concluded that a stress induced growth and resolution of the clusters and the 7' was the most reasonable mechanism to account for the behavior. It would seem, however, very unlikely that both the clusters and the y' precipitate would provide damping contributions whose relaxation time and activation energies were identical, which is required for them to produce the same internal friction peak. The present investigation was motivated by this apparent anomaly and the development of a very low thermal inertia torsion pendulum5 capable of monitoring transient behavior. Low frequency internal friction measurements were made on four binary A1-Ag alloys nominally containing 5, 10: 15, and 20 at. pct Ag. The results of measurements made on a 10 at. pct Ag alloy in the quenched condition are shown in Fig. 1. There are two peaks apparent in the spectrum, one centered at about 160°C, the second at about 210°C. The two peak spectrum was observed in each alloy, but it was best resolved in the 10 pct Ag specimens. Because of the instability in the internal friction, 4 it seemed possible that the second peak was not a peak at all, but simply a manifestation of a single, sharply transient, peak. This effect has been observed in Au-Ni alloys.6 The existence of the higher tempera-

Jan 1, 1970

By Thomas C. Wilder

ALTHOUGH there is an abundance of thermodynamic information available in the literature today, no experimental data on the standard molar properties of formation of zinc oxide have ever been reported for the temperature range 419.5" to 908°C. This is the temperature range for which zinc metal is a liquid. so that the formation reaction is: Data have been reported for Reaction [I] where zinc is a solid or a gas. Maier. Parks, and nderson' measured the electromotive force of the cell: in order to obtain the free energy of the reaction: over a limited temperature range. With the known properties of H2O, those of ZnO were calculated. These workers found that t;j of ZnO is -75,930 ± 150 cal per gfw and Mtf is-83,000 300 cal per gfw at 25°C. akolkin made similar measurements to obtain ilF7 and AH; of -75,870 and -82,540 cal per dw respectively at the same temperature. Truesdale and arirlg and Kitchener and 1gnatowicz4 measured the equilibrium of the reactions: respectively, in order to determine Ff of ZnO from the known values of CO, CO2, and H/X The thermodynamic properties of ZnO, presumably taken from the above investigations, are tabulated by Kubaschewski and vans' and Wicks and Block" The latter reference also gives values for the range where zinc is a liquid. These numbers are probably acquired from the known extremities of the range plus Cp data of the components. In the present work the electromotive force of the cell: was measured in order to calculate the properties of ZnO from the well known values of NiO for the temperature range where zinc is a liquid. In Cell [B] the cathode reaction is: and at the anode: The overall reaction is: for which the free energy change is: where is the electromotive force in volts of cell [B] after correction for the Pt-Ta thermocouple. The standard molar free energy of formation of NiO is very well known as a function of temperature. Kiukkola and agner's data are used in most tabulations. The error is probably less than I00 cal per gfw, The latter authors were the first to use solid mixed oxide electrolytes in galvanic cells. Their work with NiO and other oxides was performed with cells similar to Cell [B] using a variety of reference electrodes of fixed oxygen potential. There may be a small composition range for which either NiO, ZnO or both exist. If nonstoichiometry does exist for these oxides, then the properties described herein are those for the metal saturated compositions. The simple cell design was the same as described elsewheres except that the molten metal electrode was about 125 g of pure zinc including a small (0.25 to 0.50 g) amount of ZnO. The mixture of pure nickel and NiO powders making up the reference electrode was contained in a tube of the ZrOl + CaO electrolyte which was immersed in the molten zinc. A platinum contact was made to the reference electrode; tantalum to the zinc. A refractory cement plug was necessary at the open end of the electrolyte tube in order to prevent zinc vapor from contaminating the reference electrode. Experimental details such as the vessel containing the cell, furnace, temperature control and measurement, and electromotive force determinations of the cell have all been outlined previously. The temperature was varied randomly in the range between the freezing and boiling points of zinc. After each temperature change, time was allowed for the drift at the new temperature to be less than +;"c whereupon a series of three cell readings was taken at least 10

Jan 1, 1970

By C. Laird, C. E. Feltner

IN previous workif2 we have shown that the steady state cyclic stress response of pure copper tested in the low cycle fatigue range was determined only by the plastic strain amplitude and the test temperature. hus, copper, at any given temperature, has a unique cyclic stress-strain curve independent of prior history. Cu-7.5 wt pct Al, however, showed a stress response for a given plastic strain amplitude and temperature which depended sensitively on prior history. From this work we predicted that all wavy slip mode materials, typified by copper, would have a unique cyclic stress-strain curve; whereas all planar slip mode materials, typified by Cu-7.5 pct Al, would not. This prediction has now been tested for a number of materials of widely varying crystal structure and slip character. Wavy slip mode materials studied include: Fe. Al, Cd, disordered FeCo-V, and Cu-3 pct Co (quenched and aged). Planar slip mode materials investigated include: Fe-3 pct Si, ordered FeCo-V, disordered Ni3Mn, ordered Ni3Mn, and Zn. The treatment and properties of these materials are listed in Table I. Cyclic stress-strain curves were determined by controlled plastic strain tests (see Ref. 1 for details) at room temperature for all materials in both the initially annealed and cold worked conditions. The results obtained for iron and Fe-3 pct Si are typical of wavy and planar slip mode materials, respectively. The cyclic stress-strain curves for these materials are shown in Fig. 1 and it can be seen that iron has a unique cyclic stress strain curve while Fe-3 pct Si does not. Aluminum, Cu-3 pct Co, and disordered FeCo-V showed a behavior like that for iron, while Ni3Mn in both the disordered and ordered condition behaved in the same manner as Fe-3 pct Si. These results therefore support the general conclusion drawn in Refs. 1 and 2 that. for wavy slip mode materials, a cyclic mechanical equation of slate it =t.(hcp, i. T) is approximated in which the satura-

Jan 1, 1970

By L. W. Sink, B. H. Kear, S. M. Copley, M. F. Hornbecker

IT is well known that under appropriate conditions of chill casting, many metals and alloys develop a columnar grain structure having a high degree of preferred orientation.' In cubic materials, this principle has been employed to produce shaped castings with a unidirectional cube oriented columnar grain structure as well as shaped single crystals with a cube axis parallel to the growth ais.' "he purpose of this note is to describe how this same principle can be enlployed to produce wires, rods, or more complex crystal Shapes with a variety of conlpositions in cube or random orientations by a single casting operation. The procedure for directional solidification of in Fig. 2. Examination under crossed polarizers indicated that the striations were a second phase (presumably the B19 phase) which frequently forms initially at primary grain boundaries and then grows toward the interior as thin ribbons. X-ray studies on filings of this alloy reannealed at 1300°C for 15 min indicated a strong pattern of the fcc phase together with a substantial pattern of the B19 phase. The un-annealed filings, however, showed only the pattern of a cold-worked, fcc structure. In these two-phase alloys it appears, therefore, that the B19 phase is transformed into a disordered fcc structure by cold-working. The mechanical properties of these alloys would be of some interest since a fcc structure might be expected to possess greater ductility than the or-thorhombic B19 structure from which it forms. The author wishes to thank Mr. Harvey Yakowitz and Mr. Richard Manuszewski for obtaining the photomicrograph in Fig. 2. This research was partially supported by Research Grant DE-02455 from the National Institute of Dental Research. columnar grained ingots involves pouring a melt into a preheated mold having a water-cooled copper chill at its base? and controlling the temperature gradient in the mold so as to maintain columnar grain growth from end to end of the ingot.4 This is illustrated schematically in Fig. l(a). It should be noted that the longitudinal temperature gradient promoting unidirectional columnar grain growth is maintained by heat loss primarily through the solidifying ingot to the chill, so that both the temperature gradient and the growth rate diminish with increasing distance from the chill. As the distance from the chill increases? the columnar structure coarsens, and the perfection in preferred orientation tends to increase progressively. Using this same procedure of gradient solidification, Fig. l(b) shows a simple scheme for producing a batch of crystals having the same cube orientation rather than an assemblage of columnar grains. Wires and rods are produced by cementing ceramic tubes to the wall of the mold. The steep temperature gradient produced in the central chamber is controlled by the mold heater to produce favorable conditions for crystal growth. Clearly the success of the operation lies in the selection of individual growing columnar grains by some kind of orifice at the base of each channel in the mold. Using simple constrictions, experience with nickel-base alloys has shown that 4 -in.-diam holes at a distance of -1 in. from the chill yield crystals within 7 deg of (100); closer control of orientation is possible by placing the crystal selector farther away from the chill.

Jan 1, 1970

By Michael A. Arkoosh, E. A. Peretti

ANALYTICAL results have previously been presented for the diffusion-controlled solution of a second phase in a finite medium for planar, cylindrical, and spherical geometries.' These results were obtained by numerical methods using digital computer techniques and are applicable not only to the stage of the problem where the unstable phase shrinks to zero size, but also the subsequent stage where the concentration gradients in the matrix phase become negligible (essentially complete homogenization). It is anticipated that the results of such an analysis may be of use to those workers who are interested in the processes

Jan 1, 1970

By B. C. Wonsiewicz, W. W. Wilkening

Following a procedure proposed by Wheeler and Ireland, Plane stress yield loci were constructed from Knoob hardness numbers. Basically, six differently oriented hardness measurements were made on three orthogml surfaces through pure poly crystalline magnesium sheet, a magnesium single crystal, and sheet of the magnesium alloys: Mg + 0.5 pct Th, Mg + 4 pct Li, AZ31B, and EKOO. Hardness loci were found to be in poor agreement at small strains (E < 0.05) with loci established by a more rigorous technique. At larger strains (E - 0.10) the agreement is fair, but at this stage in deformation the conventional locus has lost much of the asymmetry that characterizes these anisotropic materials. Two effects which will lead to distortions in the Khn locus are discussed with reference to the geometry of plastic flow during a hardness test. DETERMINING a material&apos;s resistance to multiaxial loading is of interest not only from a structural design viewpoint but also from that of deformation processing. Unfortunately, the determination of the yield locus, although simple in principle, involves tedious procedures if the results are to be at all rigorous.&apos; The idea, first proposed by Wheeler and 1reland2 of determining the yield locus by means of six Knoop hardness impressions along the principal directions in a material has obvious appeal. It is simple, quick, and should be applicable to very thin sheets. If such a technique could be demonstrated to produce consistently reliable results, it would be of interest to both researcher and designer. Lee, Jabara, and ackofen have compared the yield locus determined by Knoop hardness measurements (the Khn locus) to a locus determined by more rigorous techniques. They found good agreement for two titanium alloys at a plastic strain of about 1 pct. The purpose of this paper is to investigate if the Khn locus construction is a reasonable approximation to the locus of a highly anisotropic material. Examples of such materials are magnesium and magnesium alloys which have severely distorted yield loci which in turn reflect markedly dfferent yield strength in different directions.&apos; In pure magnesium, for example, the yield stress in tension along the transverse direction may be four times the yield stress in compression in the same direction and twice the tensile yield stress in the rolling direction. Predicting such large differences ought to serve as a severe test of the Khn locus construction. EXPERIMENTAL PROCEDURES Samples of rolled sheet, 0.250 in. (6.35 mm) thick, of pure magnesium and four magnesium alloys (Mg experimental materials. The pure magnesium together with the lithium and thorium alloys were those used in the study of Kelley and Hosford. The grain size was ASTM number 4 for the pure magnesium and number 6 for the alloys. HARDNESS TESTING The materials were sectioned along the rolling and transverse planes, mounted in a quick setting resin, and mechanically polished. Most of the hardness tests were performed on a surface prepared by electro-polishing (30 pct nitric acid in methanol at 0°C and 20 v) with the exception of the AZ31B and EK00 alloys which were made directly on a metallographically polished surface. However, subsequent hardness tests on the same sample after heavily electropolishing, revealed essentially the same hardness as before. At least twenty Knoop hardness impressions under a 100-g load were made in each of the six orientations shown in Fig. 1. The average hardness number and standard deviation were then calculated for each orientation. CONVENTIONAL LOCUS CONSTRUCTION Yield loci were constructed using a technique described in detail by Lee and ackofen,&apos; in which the flow stress (stress at a given plastic strain) fixes the coordinates of a point on the locus and measurements of the strain ratio serve to establish the slope of the locus at that point. The loading paths which correspond to uniaxial tension or compression tests establish the four intercepts of the locus with the coordinate axes plus one point on the balanced biaxial tension line Tensile testing was performed along the rolling and transverse (r, t) directions. Samples had a uniform rectangular gage length 1 by 4 by 4 in. (25.4 by 6.35 by 6.35 mm) and were deformed at a strain rate of 3.33 x 104 sec-&apos;. The tests were interrupted periodically to unload the sample and measure the plastic strains by means of X-Y post yield strain gages. Compression tests in the rolling, transverse, and through-thickness (r, f, z) directions were performed on 1/4 in. (6.35 mm) cubes at an initial strain rate of 8.33 x sec-&apos;. Lubrication was provided by 0.002 in. (51 pm) Teflon sheet which was renewed after unloading for micrometer measurements used to calculate the strains.

Jan 1, 1970

By R. J. Fruehan

The oxygen activity and concentration were measured in Fe-Cr-0 melts in equilibrium with an oxide phase at 1600°C (2912°F). The activity was determined by ,use of the following solid oxide -electrolyte galvanic cell CY-Cr8,(s) I ZrOz(CaO) I Fe-CY-G(saturated)(l) The oxygen concentration decreases with increasing Cr concentration to about 270 ppm 0 at about 7pct CY and then increases gradually. The activity coefficient of oxygen (fo) decreases with increasing Cr. In melts containing up to about 20 pct Cr, log f is approximately a linear function of wt pct Cr with a slope (e q 2) of —0.037. The activity of chromium was calculated and found to exhibit a small negative deviation from Raoult&apos;s law. From the activity and solubility data for low chromium melts, the free energy of formation of chromite, FeCr204, was found to be -79.8kcal per mole where pure liquid chromium and oxygen at I wt pct in Fe are the standard states. ThE effect of chromium on the chemical behavior of dissolved oxygen in liquid iron is of great importance in controlling the deoxidation of steels containing a significant amount of chromium. Chen and chipman&apos; equilibrated Fe-Cr melts in the presence and absence of slag with hydrogen-water vapor mixtures. They concluded that at 1595°C chromite was the oxide phase in equilibrium with Fe-Cr alloys containing less than 5.5 pct Cr while at higher chromium concentration Cr,O, was the stable phase. In the composition range 0 to 10 pct Cr they found that the interaction coefficient, was equal to -0.041. Turk-dogan,&apos; Schenck and Steinmetz,, and pargeter4 measured egr) in a similar manner and found the value to be -0.064,-0.04, and -0.052, respectively. McLean and Be11 evaluated egr) from their data on the equilibrium of Fe-Cr-Al-0 alloys with H2/H20 mixtures and found it to be -0.058. However, McLean and Bell&apos;s value should only be considered an estimate because the effect of aluminum on the activity coefficient of oxygen is about a hundred times greater than that of chromium. Consequently, an error in the value of egl) used, which at the present time is not well-known, or an error in aluminum analysis, which is present in very small quantities, will result in a significant error in egr). Fischer et a1.6 determined the interaction coefficient (eEr) in Fe-Cr-0 melts not in equilibrium with an oxide phase and containing less than 18 wt pct Cr at 1600°C electrochemically. They determined a value of -0.031 for egr). Hilty et aL7 measured the oxygen content of Fe-Cr melts in equilibrium with an oxide phase containing up to 50 pct Cr. They found that the solubility of oxygen decreased as the chromium content increased to about 6 pct Cr and then increased gradually. They concluded that the equilibrium oxide phase was chromite below 3 pct Cr, distorted spinel from 3 to 9 pct Cr, and Cr,04 above 9 pct Cr. Adachi and lwamotoa also investigated this system, but did not find Cr30,. They X-rayed the equilibrium oxide phases and did not find the presence of Cr,O,. They also X-rayed the oxide phase extracted from a 65 pct Cr melt which was heat treated and did not find metallic chromium as would be expected if Cr3O4 were the equilibrium oxide phase as indicated by the reaction : 3Cr3O4 — 4Cr2O:, + Cr [lj It was the purpose of the present investigation to determine the effect of chromium on the activity coefficient of oxygen in Fe-Cr melts by measuring the activity and solubility of oxygen equilibrated with an oxide phase in the composition range 0.18 to 50.5 wt pct Cr at 1600°C (2912°F). The activity of oxygen in the melts was determined by use of the following galvanic cell: The relationship between the partial pressure of oxygen in equilibrium with the melt and the reversible electromotive force of the cell (E) is where 11 = 4, F is the Faraday constant, pb, is the oxygen pressure in equilibrium with the meit and is the oxygen pressure in equilibrium with Cr203 as determined from the free energy data compiled by Elliott et al? The oxide phase in equilibrium with pure chromium was assumed to be Cr If Cr30, were the equilibrium phase the activities derived would be approximately the same, since the best estimated free energy of formation of Cr,O,, if it does exist, is approximately % the free energy of formation of The activity of chromium in Fe-Cr alloys at 1600° C was also determined from the measured electromotive force. The activity of chromium (aCr) is related to the electromotive force as follows: , The oxide phase in equilibrium with pure chromium and Fe-Cr melts from 10 to 52 pct is assumed to be Cr203 so that n equals three. If future work proves the existence of Crs04 in equilibrium with Fe-Cr melts and pure chromium, the experimental results can be reevaluated using a value of $ for n in Eq. 141. A value of ^ for n will make the activities about 10 pct higher. In order for Eqs. 131 and [4J to be valid the electrolyte, ZrOa(CaO), must exhibit predominantly ionic conduction at the temperature and oxygen partial pressure of its use. Previous work1&apos; has demonstrated that ZrOz(Ca0) is predonlinantly an ionic conductor

Jan 1, 1970

By Shiro Ban-ya, John F. Elliott, John Chipman

The activity of carbon in Fe-C austenite at 1150°C has been determined for concentrations up to about 2.1 pct C using the equilibrium: C + COz = 2CO; equations have been derived expessing the activity as a function of carbon content on the basis of twelve mathematical models. Several of these represent the data satisfactorily. ACCURATE information on the thermodynamic properties of austenite in the binary system Fe-C is needed as a basis for studies of transformation and precipitation in steels of all sorts, alloy as well as plain carbon. The many attempts to approach this problem through statistical thermodynamics require sound and dependable experimental data in order to evaluate the several models which have been suggested. In this paper we are concerned with the experimental determination of the activity-composition relation in austenite at the temperature of its widest range of stability, approximately the eutectic temperature (1153°C). Accurate investigation of the activity of carbon in austenite may be said to have begun with the work of Dunwald and wagner.&apos; A more detailed study was carried out by R. P. smith2 on the two equilibria: More recent work on these two equilibria has been reviewed by Chipman,3 who pointed out the experimental hazards associated with studies of Eq. [I]. Studies of this reaction involve rather small values of the ratio these are susceptible to errors due to traces of moisture in the apparatus according to the reaction: Ellis, Davidson, and Bodsworth4 evaluated K, for their experimental temperatures and used desiccants to control water vapor pressure. While they were able in this way to obtain consistent values for K1 it cannot be said that all of the uncertainties of the method have been overcome. Results by both methods reported by Schurmann, Schmidt, and wagener5 appear to be consistent except at very low carbon content. Reaction [2] was employed in the experimental work reported here. It is to be recognized, however, that it is not applicable to projected studies of certain alloy steel compositions involving stable oxide-formers.

Jan 1, 1970

By C. S. Samis, J. C. Mitchell

Sodion activity data have been obtained for the Na-A1 system for sodium concentrations in aluminum between NN, = 25 . 10-and 300 x 10&apos;. This concentration intert-a2 encompasses those sodium concentrations nor1)zally encountered in aluminum reduction cell operation. The sodium activity data were measured by a two-phase equilibration of sodium between a lead and an aluminam rich phase. The Na-Pb system was emplojed as a reference for the determination of the actiz7itj 0.f sodium. The activity of sodiin in aluminuwz exhibits large positi2.e deviations frorn ideality and a strong dependence, on concentration below NN, = 100 x 1K6. The inteated data indicate that the activity of aluminium is equal to its mole fraction over the range of miscibility of the Na-A1 sgstem. The data on the Na-A1 binary have been combined with experimental data on the cryolite-A1 system at 1025°C to obtain the activities of Na F and AlF, in liquid cryolite oz2er the cornposition 1-ange encountered in aluminum cell operation. The results are in agreement with activities calculated from the NaF-AlF, phase diagram. ALUMINUM is produced commercially by the electrolytic reduction of aluminum oxide dissolved in molten cryolite. There is considerable controversy over the actual mechanism of the discharge processes, but sodium potentials in the systems appear to play an important role in the reduction mechanism. The metal-salt reaction involving NaF and aluminum to produce A1F3 and sodium is responsible for the presence of sodium in the aluminum metal phase. Additional sodium may be produced from the simultaneous deposition of sodium and aluminum at the cathode as a result of a cathodic overvoltage. runert&apos; has suggested that sodium gas at atmospheric pressure would be the result of reaction between cryolite and aluminum at 1000°C. Subsequent investigations have shown that production of sodium at atmospheric pressure does not occur. These later investigations can be conveniently separated into two categories. The first involves sodium, aluminum, and cryolite, in which the sodium activity was measured. The second includes a lead phase for sodium activity measurement. Jander and errmann,&apos; studied the reaction: at 1090°C in alumina crucibles under an atmosphere of dry, oxygen-free nitrogen. The equilibrium constant for the reaction was expressed in terms of concentration. Their results in Fig. 1 show an increase in sodium content of the aluminum with increasing NaF/A1F3 weight ratio. Pearson and waddington3 performed similar experiments at 1000°C. Their results are included in Fig. 1. Dewing and ollinshead have measured the sodium content of aluminum as a function of the NF/AF, ratio at 1025"C, Fig. 1, and ewin&apos; measured the sodium content of the aluminum in a system involving the solid reactants NaF, cryolite, and liquid aluminum. This reaction is different from those discussed above. Two solid phases, NaF and Na3A1F6, and a liquid aluminum phase were present. The sodium concentration in the aluminum was determined by the temperature. Dewing&apos;s measurements covered the temperature range 679" to 896°C. Omo, Matsushima, and 1t02" investigated the equilibrium 6NaF ential thermal analysis. Stokes and Frank6 determined sodium activities by

Jan 1, 1970

By C. D. Williams, C. E. Ells

The susceptibility of quenched and aged Zr-2.5 wt pct Nb alloy to embritt2ement during irradiation has been examined for a number of solution temperatures and aging times. Material quenched from temperatures approximately 40°C below the transus has high tensile ductility, and this ductility is insensitive to aging at 500°C or to irradiation. If, however, the material is quenched from temperatures above the transus it becomes highly susceptible to loss of ductility either from aging at 500 or from irradiation. Inter granular failure is characteristic of the materials having low ductility. The distribution of the equilibrium phase is found to control the susceptibility to embrittlement by restricting 6 grain growth during heat treatment and thus influencing crack propagation. IN zirconium, as in titanium, -stabilizing alloy additions are used to obtain high strengths via quench and age heat treatments, and the Zr-2.5 pct Nb alloy has been developed1 because of its strength advantage over the Zircaloys. Early in the development of the Zr-2.5 pct Nb alloy the problem of 13 embrittlement was appreciated, and for this reason the solution temperature was chosen below the p transus.&apos; In the course of irradiation studies on quenched and aged Zr-2.5 wt pct Nb alloy it was found&apos; that irradiation introduced an important aspect of p embrittlement, riz., material quenched from the phase and aged 24 hr at 500°C was severely embrittled by moderate doses of neutron irradiation. This effect had not been studied in titanium alloys. In titanium the metallurgical features leading to 0 ernbrittlement were found to be structures with: a) coarse a platelets at the grain bondaries, b) finely dispersed a uniformly distributed throughout the (0) matrix,6 c) Widmanstatten a-13 with more than 50 pct P, d) the presence of some metastable p transformation products,3 and e) large prior -phase grain size.5 Alternatively, the presence of a uniform distribution of coarse a was conducive to high ductility and a structure largely of equiaxed a was very dctile. The detailed mechanisms of the embrittlement have not been worked out for all of these conditions, although weakness at either a-matrix boundaries or prior p grain boundaries have been prominent in the eculation. It was proposed that acicular a might act as a mild notch, and low ductility has been associated with easy fracture along its boundary.&apos; There have been two opposing suggestions for the source of the high ductility associated with equiaxed a phase. JaffeeB proposed that this a would accept a large por- tion of the oxygen, thus increasing the ductility of the matrix, whereas after study of a Zr-Nb-Cu alloy Weinstein and oltz proposed that the a phase, softer than the martensitic matrix, acted to blunt cracks formed in the matrix. In the present work we have studied the effect of neutron irradiation on the ductility, particularly the P embrittlement, of the Zr-2.5 wt pct Nb alloy. By a variation of solution temperature and aging time a variety of metallurgical conditions have been examined, and a range of resultant ductilities obtained. The ductility has been related to the material microstructure and mode of fracture. EXPERIMENTAL The alloy used in the present work came from two separate ingots fabricated into rod of 3/8 or i in. diam, Table I. For both batches the P transus temperature was approximately 890° C. Most of the heat treatments were done directly on lengths of the j} in. diam rod, after which the tensile test specimens were machined. Quenching was achieved by dropping rods from a dynamic vacuum into water, the cooling rate estimated to be 2 100°C per sec. For aging the rods were encapsulated in evacuated silica tubes. Round tensile test specimens, with gage diam and length 0.160 and 1.0 in., respectively, were used throughout and pulled at room temperature or 300°C on Instron tensile machines, at a crosshead speed of 0.05 ipm. Specimens were irradiated in the NRX and NRU reactors, in facilities described in previous publications.&apos;0 The metallurgical conditions examined have been: All tensile test specimens were machined with axes in the axial direction of the swaged rod. Although the specimen had a degree of preferred crystallo-graphic orientation with basal plane normals both parallel with and perpendicular to the tensile axis, the material was comparatively isotropic." The techniques of thin foil examination in the electron micro-

Jan 1, 1970

By Mark J. Klein

The creep of 043 was studied over the temperature range 1650" to 3200°F and over the stress range 3000 to 44,000 psi. The steady-state creep rate over this range of stress and temperature can be expressed by the equation where A is a constant, is the stress, and is -0.8 x 103 psi-&apos;. Over a narrow range of stress variations c0 a and for this proportionality n varies from 3 to 30 in accordance with the relation n = aB. Above about 2400° F, H, the apparent activation energy for creep, is 110,000 cal per mole, a value about equal to that estimated for self-diffusion in this alloy. Below 2400°F, H increases with decreasing temperature reaching a value of -125,000 cal per mole at 1700° F. In this temperature region, H appears to be a function of the interstitial concentration of the alloy. MOST of the detailed creep studies of dispersion strengthened metals have been concerned with metals having fcc structures. However, there are a number of important refractory alloys with bcc structures that derive part of their high temperature strength from an interstitial phase and whose creep behavior has not been well defined. This paper describes the creep behavior of the bcc alloy, D43, over the temperature range 1650" to 3200°F (0.4 to 0.7 Thm) and over the stress range 3000 to 44,000 psi. In addition to colum-bium, this alloy contains 10 pct W. 1 pct Zr, and sufficient carbon (-0.1 pct) to form a carbide dispersion throughout the matrix of the alloy. The effects of variations in temperature and stress on the steady-state creep rate of this alloy are presented in this paper. EXPERIMENTAL PROCEDURES Creep tests were made in a vacuum of 106 torr under constant tensile stress conditions using a Full-man-type lever arm.&apos; Creep specimens were machined from 0.020-in. D43 sheet (grain size -5 x l0-4 in.) processed in a duplex condition (solution annealed -2900°F, 40 pct reduction in area, aged 2600°F). The specimens were tested in this condition without further heat treatment. Specimen extensions over 1-in. gage lengths were continuously recorded using a high temperature strain gage extensometer. Differential temperature and stress measurements were used to determine temperature and stress dependencies of the creep rate. Activation energies were calculated from the changes in strain rate induced by abrupt shifts in the temperature during constant stress creep tests. The 100°F temperature shifts used in most of the activation energy determinations required 15 to 90 sec depending upon the temperature at which the shift was made. The dependence of strain rate on stress was determined by measuring the change in strain rate for incremental stress reductions during constant temperature tests. It has been shown that columbium-base alloys such as D43 are susceptible to contamination by gaseous interstitial elements during vacuum heat treatments.&apos; In this regard, it is unlikely that these alloys can be heat treated without some loss or gain of interstitial elements despite the precautions taken to control the heat treating environment. However, several factors suggest that changes in interstitial concentrations of the specimens during testing did not affect the results presented in this paper. First, the dependence of the creep rate on the stress or temperature determined during the course of a single creep test showed no variations with the duration of the test. A variation would be expected if a loss or gain in interstitial concentration during the course of the test affected results. In addition, precautions taken during this investigation to minimize interstitial contamination by wrapping the gage lengths of the specimens with various foils2 (Mo, Ta, W) did not produce a detectable change in the stress and temperature dependencies relative to the unwrapped specimens. The averages of duplicate analyses for carbon and oxygen in several specimens determined before and after creep testing are listed in Table I. The combined nitrogen and hydrogen concentrations which were ordinarily less than 50 ppm did not change in a detectable way with creep testing. The analyses show that only minor changes in carbon concentration occurred during creep testing except for specimen 4. This specimen which was tested at 3100°F lost a significant amount of its carbon concentration to the vacuum environment. Specimen 1 gained 100 ppm of O, while specimens 2, 3, and 4, which were tested at progressively higher temperatures, lost increasing portions of their initial oxygen concentrations during testing. RESULTS AND DISCUSSION The Temperature Dependence of the Creep Rate. The apparent activation energy for creep, H, was de-rived from creep curves similar to that shown in Fig. 1. Steady-state creep was rapidly attained at the beginning of the test and with each change in temperature. This behavior suggests that the alloy rapidly attains a stable structure with each shift in temperature or that the structure is constant throughout the test. Since the dispersion will tend to stabilize the structure, the latter is probably the case. The activation energy was found to be independent of the direction of the temperature shift and the magnitude of the shift (50" or 100°F). Although H was approximately independent of the strain, there was a tendency for it

Jan 1, 1970

By Hsun Hu, B. B. Ruth

The rates of migration of high-angle boundaries in zone-refined aluminum crystals rolled 20 to 70 pct in the (110)[i12/ orientation were studied. Following a recovery anneal at an appropriate temperature to stabilize the polygonized structure, boundary migration rates of artificially nucleated grains were measwed isothermally at several temperatures. Results indicate that the rate of boundary migration depends strongly on the amount of deformation and on the cell size of the polygonized matrix, and is related to the driving free energy by a power function. The degree of anisotropy in growth 0.f the re crystallized grains nn&apos;th preferred mientation is independent of deformation; the migration rates of the fast-moving and the slow-moping boundary segments of a gowing grain differ by as much as one order of magnitude. The actir\ation energy fm a grain boundary migration, although nearly the same for both the fast-moving and the slow-moving boundaries for a given deformalion, decreases from 45 to 30 kcal per mole with an increase in deformation from 20 to 70 pct reduction. Re crstallization by the growth of the artificially nucleated grains results in preferred orientation. The Percentuge of&apos; grains favorably oriented for growth increases with increasing deformation. None of these grains corresponds to the ideal Kronberg-Wilson orientation relationship. The observed growth aniso-tropy is discussed in terms of boundary structure. The boundary velocity as a function of the cell inter -facial area, or the driving free energy, is discussed in the light of current theories of boundary migration. It is well established that recrystallization with re-orientation occurs by the migration of high-angle boundaries of strain-free grains. The driving force for this process is provided by the free energy stored in the metal during deformation. A quantitative study of the effect of varying driving force on grain boundary migration in deformed metals has not been possible heretofore, primarily because of: 1) concurrent recovery steadily decreasing the available driving free energy for boundary migration, &apos;-3 and 2) in-homogeneity of strain in the deformed metal.4 Aust and Rutter3 studied grain boundary migration in striated single crystals of zone-refined lead. Although the driving free energy in such crystals remains unaltered during annealing, this method does not provide a range of driving free energies over which measurements of grain boundary migration can be made. In the present investigation, the rates of migration of high-angle boundaries in deformed aluminum zone- refined single crystals were studied at various temperatures, after deformation ranging from 20 to 70 pct reduction by rolling at -78°C in the (ll0)[i12] orientation. The boundary migration rates along different crystallographic directions were determined under steady-state conditions, i.e., in the absence of competing recovery processes or impingement of recrystallized grains growing into the deformed single crystal matrix. Simultaneous recovery was eliminated by suitable anneals prior to the boundary migration measurements. The recrystallized grains, which grew a ni so tropically into the homogeneously polygonized matrix, developed flat boundary segments during early stages of growth. These boundary segments subsequently migrated along a direction approximately normal to the boundary plane into the matrix rystal. Increasing deformation over the range employed was estimated to increase the driving free energy for boundary migration by about five times. The kinetics of the boundary migration process, examined under these conditions, indicate that the boundary velocity is greatly affected by a small change of the driving free energy in the matrix crystals. These results were examined in the light of the current theories of grain boundary migration. EXPERIMENTAL PROCEDURES Single crystal strips (9 by 1 by 0.125 in.) of zone-refined aluminum, were seed-grown by the Bridgman method in a high-purity graphite mold (<lo ppm ash) at 1 in. per hr. Precautions were taken to minimize contamination of the metal during crystal preparation and subsequent handling. Spectrographic analysis of the metallic impurities in the grown crystals is Qven in Table I. The crystals were rolled in the (110)[112] orientation at -78°C to various reductions in thickness, ranging from 20 to 70 pct, in 10 pct increments. The desired reduction was achieved by many rolling passes, each being no more than 0.002 in. To minimize surface friction, the crystal was rolled between two thin layers of teflon. For those crystals rolled more than 40 pct, it was necessary to remove the disturbed surface layers by electropolishing at -5" to -10°C at an intermediate stage of rolling. The edges of deformed crystals were removed by a jeweler&apos;s saw while submerged in alcohol at -78° C to obtain samples of about ? by i in. The distorted metal at the cut edges and the surface layers were then removed by electropolishing, with removal of a minimum of 0.004 in. from each surface. The thickness of the crystals prior to rolling was chosen so that the final thickness was 0.025 in. for all samples. These deformed single crystals were each prean-nealed for 1 hr at an appropriate temperature in the range of 130" to 280°C, depending upon the amount of deformation. The purpose of this preannealing was to

Jan 1, 1970

By Neils Hansen

The microstructure of dispersion-strengthened aluminum aluminum-oxide products containing from 0.2 to 4.7 wt pct of aluminum oxide has been examined by optical and transmission electron microscopy, and the flow stress has been determined at room temperature and at 400C by tensile testing. Products were examined as recrystallized and as high-temperature extruded, and the microstructures consisted of a fine dispersion of oxide particles in a matrix divided by respectively recrystallized grain boundaries and subgrain boundaries. The flow stress (0.2 pct offset) at room temperature of recrystallized dispersion strengthened aluminum aluminum-oxide products is the superposition of dispersion strengthening and grain boundary strengthening. This superposition has been found to be linear. The flow stress (a) can be related to the grain size (t) by the Petch equation: ing content of oxide and k is a constant independent of the oxide content. For extruded products a similar relation has been found by replacing the grain size by the subgrain size. The k-value is of the same order for the two types of structure, which shows that the subgrain boundaries are as effective slip barriers as grain boundaries. Tensile testing at 400C of re-crystallized and extruded products shows that oxide dispersion strengthening is very effective, whereas the strengthening effect of grain boundaries and subgrain boundaries is small. THE microstructure of dispersion-strengthened products consists of hard particles finely distributed in a metal matrix. The strengthening effect of the dispersed phase has been fairly well established,1 and it has been found that the size and volume fractions of the dispersed particles are important structural parameters. However, in many dispersion-strengthened products which have been worked and heat-treated during manufacture the matrix is divided into well-defined grains or sub-grains, which may also have a strengthening effect. A model of the matrix strengthening in dispersed products worked during manufacture has been proposed,2 introducing the energy of the structure as a strengthening factor, especially at low temperatures. A difficulty in this model is, however, to relate this (stored) energy to the structural parameters directly observable as for instance grain size. The strengthening effect of the matrix grain size after recrystallization has been in- vestigated for nickel-thoria (TD-Nickel) products3 and for copper aluminum-oxide products. Conclusive results were, however, not obtained as the grain size of TD-nickel was constant. 5 to II , after recrystallization at temperatures from 700 to 1200°C and as the copper products containing 5 to 1 wt pct of aluminum oxide could not be recrystallized even after severe cold reduction and heat treatment at 1050C. For aluminum aluminum-oxide products containing from 1 to 5 wt pct of aluminum oxide it has been shown that the tensile strength at room temperature decreases when an extruded product is cold-worked and recrystallized. The matrix in the extruded products is divided into well-defined subgrains of micron size, and as the grain size of the recrystallized products is about two orders of magnitude higher, it is obvious that grain boundary strengthening occurs. Preliminary results8 have indicated that the flow stress containing no grain boundaries, A is a constant and t is the subgrain size. At elevated temperatures the effect of boundaries is more complex; it has been shown11 that recrystallized products having an oxide content of about 3 wt pct are more creep resistant than extruded material in the temperature range 400° to 600°C, whereas on application of a higher strain rate the tensile flow stress (0.2 pct offset) is higher in extruded than in recrystallized aluminum—5 wt pct aluminum oxide products at temperatures from room temperature to 427°C (800), Finally it has been shown12 that the Brinell hardness at 350°C of extruded products having about the same content of aluminum oxide increases with decreasing grain size, determined by X-ray line-width measurements. The present study was undertaken to obtain a quantitative relationship between the tensile strength and the grain size of aluminum aluminum-oxide products in the recrystallized as well as in the extruded state. The tensile testing was performed at room temperature and at 400uC. The grain size of the recrystallized products was varied by changing the degree of cold-work preceding the recrystallization heat treatment. In extruded products grain (or subgrain) size variations were obtained by high-temperature heat treatment after extrusion. EXPERIMENTAL a) Materials. Aluminum aluminum-oxide products have been manufactured by consolidation of aluminum powder covered with a layer of aluminum oxide formed during powder manufacturing. The products examined were manufactured from atomized powder containing

Jan 1, 1970