Many independent studies are being made on slag-metal relationships in the open-hearth furnace, and these studies cannot help but result in an ultimate improvement in the quality of open-hearth steel of both the open and killed types. In maintaining quality control at the National Tube Company's plant, emphasis has been placed on an evaluation of the iron oxide content of the steel in as quantitative a manner as possible, in order that the most desirable level of oxidation might be obtained for a given type of steel, and to secure a more precise basis for final de-oxidation. In the past, various methods were used for estimating FeO content of the metal at tap to ensure uniform and thorough deoxidation of killed steel, avoiding overdeoxidation to minimize the amount of inclusions present and to make as sound a steel as possible. For the open-type steels, such control involves obtaining the necessary level of oxidation for the most suitable action of the steel in the molds to provide good surface quality and cross section for the specific grade involved. While rapid analytical methods are available for determination of FeO in the liquid metal, such methods are still not sufficiently rapid for routine control on the open-hearth floor, nor do such analyses provide information as to what causes high or low FeO values. The method of sampling can still be considered a problem in view of the variability encountered in taking simultaneous duplicate tests. With the accurate rapid methods now available for determining carbon in the metal, estimating slag basicity and obtaining temperatures of liquid metal, it was believed possible to determine the influence of the various furnace reactions in establishiug the state of oxidation at a given time. Simultaneous slag and metal tests were used in this analysis, aided by statistical methods, to determine the factors that affect the metal FeO, and also to make a quantitative evaluation of these factors. Data obtained are from actual iurnace operations, the metal test being of the I spoon, Herty type, and taken in duplicate. Metal temperatures were taken with the open-tube bath pyrometer developed by the Research Laboratory of the United States I Steel Corporation. This method of taking open-hearth metal temperature was invented by Collins and Oseland,l and was developed into its present form by L. 0. Sordahl,2 of the Research Laboratory. The instrument and its mode of operation have been fully described by Sordahl and Sosman in three publications.3,4,5 lag components were obtained by chemical analysis. Data were taken from four 165-net-ton furnaces during the working period of the heat. Recognizing that additions of ore affect the metal FeO. no tests were included within 30 min. after ore additions. In all, 65 tests (48 heats) were used in this study.

Jan 1, 1942

By B. M. Larsen, L. S. Darken

Some years ago we collated all laboratory data then available to us on the distribution at equilibrium of manganese and of sulphur between metal and simple slags, and used the results in setting up an equation, which proved to be in accord with determinations of the distribution ratio of manganese and of sulphur between liquid steel and open-hearth slag, over a wide range of operating conditions. We now present an outline of our calculations and inferences on these two closely related questions, which are of especial importance because of the advisability of conserving manganese wherever possible. In general, our results show that in the open-hearth furnace equilibrium between metal and slag, with respect to both manganese and sulphur, is substantially attained during the finishing period of the heat, or in about a half hour to an hour after any additions were made. This implies that the end result will be identical whether manganese is added as alloy or metal to the liquid steel or as oxide to the slag. The proportion of total manganese retained by the steel is favored: (I) by use of the minimum amount of lime, consistent with other operating limitations, required to give a lime-silica ratio of about 2.4, which usually corresponds to a minimum practical slag volume; (2) by a high concentration in the slag of MnO relative to FeO; (3) by high operating temperature. Absorption of sulphur by the slag from the liquid metal is favored: (I) by large slag volume; (2) by a high concentration of active (or "free") lime and of manganese oxide dissolved in the slag; (3) by low concentration of silica, iron oxide, and phosphate dissolved in the slag. Distribution 02 Manganese between Slag and Metal at Equilibrium On the basis that the distribution of manganese between liquid steel and slag is controlled by the reaction FeO + Mn -& MnO + Fe [A] slag metal slag metal the distribution at equilibrium, at a given temperature, is expressed by the equilibrium constant for this reaction, which is defined as K,, _ aMnO' afe aFeO ' aMn where a is the activity of the molecular species denoted by the subscript. The activity of each of the several components, although it is not known precisely, is approximately equal to the concentration of each component expressed as its mol fraction; that is, as the ratio of the number of mols of the given component to the total number of mols of all the molecular species present in the metal or slag, as the case may be. Moreover, since the activity, or concentration, of iron in the liquid metal is in fact substantially constant, the term afe may be combined with K" to give a new constant K'. Making these changes, 7

Jan 1, 1942

By B. M. Larsen, L. S. Darken

Some years ago we collated all laboratory data then available to us on the distribution at equilibrium of manganese and of sulphur between metal and simple slags, and used the results in setting up an equation, which proved to be in accord with determinations of the distribution ratio of manganese and of sulphur between liquid steel and open-hearth slag, over a wide range of operating conditions. We now present an outline of our calculations and inferences on these two closely related questions, which are of especial importance because of the advisability of conserving manganese wherever possible. In general, our results show that in the open-hearth furnace equilibrium between metal and slag, with respect to both manganese and sulphur, is substantially attained during the finishing period of the heat, or in about a half hour to an hour after any additions were made. This implies that the end result will be identical whether manganese is added as alloy or metal to the liquid steel or as oxide to the slag. The proportion of total manganese retained by the steel is favored: (I) by use of the minimum amount of lime, consistent with other operating limitations, required to give a lime-silica ratio of about 2.4, which usually corresponds to a minimum practical slag volume; (2) by a high concentration in the slag of MnO relative to FeO; (3) by high operating temperature. Absorption of sulphur by the slag from the liquid metal is favored: (I) by large slag volume; (2) by a high concentration of active (or "free") lime and of manganese oxide dissolved in the slag; (3) by low concentration of silica, iron oxide, and phosphate dissolved in the slag. Distribution 02 Manganese between Slag and Metal at Equilibrium On the basis that the distribution of manganese between liquid steel and slag is controlled by the reaction FeO + Mn -& MnO + Fe [A] slag metal slag metal the distribution at equilibrium, at a given temperature, is expressed by the equilibrium constant for this reaction, which is defined as K,, _ aMnO' afe aFeO ' aMn where a is the activity of the molecular species denoted by the subscript. The activity of each of the several components, although it is not known precisely, is approximately equal to the concentration of each component expressed as its mol fraction; that is, as the ratio of the number of mols of the given component to the total number of mols of all the molecular species present in the metal or slag, as the case may be. Moreover, since the activity, or concentration, of iron in the liquid metal is in fact substantially constant, the term afe may be combined with K" to give a new constant K'. Making these changes, 7

Jan 1, 1942

By E. C. Wright

The bessemer process is nearly one hundred years old. William Kelly, the American inventor, was able to demonstrate that he had accomplished the pneumatic purification of molten pig iron as early as 1847; Henry Bessemer's English patent was granted in 1855. The application of this steelmaking process since then and the present position of bessemer steel are concisely discussed on pages 355 and 356 of the fifth edition of "The Making, Shaping and Treating of Steel." The great expansion of the automotive, machine-tool, chemical and oil industries after I9I0 opened up a large market for special steels, whereas the output of steel before that time was mainly for structural purposes. The need for building more blastfurnace capacity complementary to bessemer operations, combined with the availability of the' necessary amounts of steel scrap, both contributed to the extension of open-hearth plants at the -exense of besskmer capacity. The ability of the open-hearth furnaces to consume virtually all types of raw materials as far as phosphorus content is concerned, and the need for selecting low-phosphorus ores of rapidly decreasing sources for the bessemer, also played a part in the reduction of bessemer steelmaking operations and the increase in basic open-hearth plants. As a consequence, the proportion of bessemer steel made, in this country decreased from 65.7 per cent of the total in 1900 to 37.1 per cent in 1910, and only 6.8 per cent of the total in 1937. The metallurgical concepts existent between 1910 and 1920 caused the writing of many specifications of very low phosphorus and sulphur content, which definitely barred bessemer steel from many commodities. Now sulphur is being added to many open-hearth and bessemer steels in amounts far exceeding the maximum sulphur content of good bessemer steel. Re-phosphorizing is also widely practiced for several specific applications. Even today, the chemical-analysis limits of many important steel specifications have an arbitrary and archaic tinge. The old standard "0.30 to 0.60 per cent manganese" might be mentioned in this connection as similar to the rigid requirements for maximum sulphur and phosphorus that were established at least 25 years ago. The literature is full of vague and complee discussions of the effects of nitrogen and oxygen where these elements existed in steel in amounts less than 0.02 per cent. Many failures have been attributed to these elements without reasonable proof on which to base the conclusion. Methods of determining oxygen in steel require such complicated equipment that only a few research laboratories have the required apparatus. Even so, the accuracy of oxygen determinations in steel has been only recently reproducible. Up to the present time, no one has succeeded in obtaining a sample of molten steel that accurately indicates the full oxygen content of the metal in the furnace or ladle because the molten sample

Jan 1, 1944

By E. C. Wright

The bessemer process is nearly one hundred years old. William Kelly, the American inventor, was able to demonstrate that he had accomplished the pneumatic purification of molten pig iron as early as 1847; Henry Bessemer's English patent was granted in 1855. The application of this steelmaking process since then and the present position of bessemer steel are concisely discussed on pages 355 and 356 of the fifth edition of "The Making, Shaping and Treating of Steel." The great expansion of the automotive, machine-tool, chemical and oil industries after I9I0 opened up a large market for special steels, whereas the output of steel before that time was mainly for structural purposes. The need for building more blastfurnace capacity complementary to bessemer operations, combined with the availability of the' necessary amounts of steel scrap, both contributed to the extension of open-hearth plants at the -exense of besskmer capacity. The ability of the open-hearth furnaces to consume virtually all types of raw materials as far as phosphorus content is concerned, and the need for selecting low-phosphorus ores of rapidly decreasing sources for the bessemer, also played a part in the reduction of bessemer steelmaking operations and the increase in basic open-hearth plants. As a consequence, the proportion of bessemer steel made, in this country decreased from 65.7 per cent of the total in 1900 to 37.1 per cent in 1910, and only 6.8 per cent of the total in 1937. The metallurgical concepts existent between 1910 and 1920 caused the writing of many specifications of very low phosphorus and sulphur content, which definitely barred bessemer steel from many commodities. Now sulphur is being added to many open-hearth and bessemer steels in amounts far exceeding the maximum sulphur content of good bessemer steel. Re-phosphorizing is also widely practiced for several specific applications. Even today, the chemical-analysis limits of many important steel specifications have an arbitrary and archaic tinge. The old standard "0.30 to 0.60 per cent manganese" might be mentioned in this connection as similar to the rigid requirements for maximum sulphur and phosphorus that were established at least 25 years ago. The literature is full of vague and complee discussions of the effects of nitrogen and oxygen where these elements existed in steel in amounts less than 0.02 per cent. Many failures have been attributed to these elements without reasonable proof on which to base the conclusion. Methods of determining oxygen in steel require such complicated equipment that only a few research laboratories have the required apparatus. Even so, the accuracy of oxygen determinations in steel has been only recently reproducible. Up to the present time, no one has succeeded in obtaining a sample of molten steel that accurately indicates the full oxygen content of the metal in the furnace or ladle because the molten sample

Jan 1, 1944

By L. G. Graper, E. L. Ramsey

The present program of increased production of armament and lend-lease material for mechanized war has created a problem for the shops that must do the machining. They have naturally turned to the steel producers to provide them with a steel that can be accurately machined with the greatest possible speed. The adding of sulphur to steel as an aid to machinability has long been practiced; however, it may cause red shortness in rolling and may result in billets with seams and cracks, which must be removed before rolling can be continued. This conditioning of billets slows down production and adds to the cost of making steel. Experience with various grades of sulphur steel made to different specifications has shown that Bessemer sulphur steels roll better than similar grades made in the open hearth, and also that low-carbon steels that are open or semikilled as tapped roll better than completely deoxidized or killed steels. This has led to the belief that oxygen plays an important part in the rolling qualities of sulphur-bearing steels. It is generally held that the red shortness of sulphur steels is due to the low melting point of the sulphide compounds that separate out at the grain boundaries when the steel solidifies. At the rolling temperature of steel these sulphide compounds melt and cause cracking. Adding Sulphur as a Sulphite These difficulties can be avoided if sulphur is introduced into the stecl by means of an anhydrous sulphite, such as sodium sulphite or sodium bisulphite, which—upon decomposition—forms sulphur dioxide. It is assumed that, in this case, the oxygen of the sulphur dioxide forms part of the sulphide inclusions in the steel, and raises their solidification temperature enough so that the formation in the steel of a low-melting eutectic is prevented. The result is the prevention of hot shortness and a more uniform distribution of inclusions. Fig. I shows photomicrographs of steels made with sulphur, while Fig. 2 illustrates the structure of steels made with sodium bisulphite. These samples were cut from the steels as cast—that is, before rolling— and were polished and lightly etched to bring out the grain boundaries. Fig. I shows that sulphide inclusions segregate more or less at the grain boundaries, and it can be seen how the continuity of these low-melting inclusions would cause red shortness. Fig. 2 shows that the sulphide inclusions arc more or less uniformly distributed throughout the matrix. This arrangement of inclusions has no apparent effect on the rolling qualities of a steel. This statement has been substantiated by the observation of the rolling of over 6000 tons of steel made with a sulphite addition. Results As stated before, the sulphur dioxide is added to steel by means of the decomposi- 27

Jan 1, 1942

By L. G. Graper, E. L. Ramsey

The present program of increased production of armament and lend-lease material for mechanized war has created a problem for the shops that must do the machining. They have naturally turned to the steel producers to provide them with a steel that can be accurately machined with the greatest possible speed. The adding of sulphur to steel as an aid to machinability has long been practiced; however, it may cause red shortness in rolling and may result in billets with seams and cracks, which must be removed before rolling can be continued. This conditioning of billets slows down production and adds to the cost of making steel. Experience with various grades of sulphur steel made to different specifications has shown that Bessemer sulphur steels roll better than similar grades made in the open hearth, and also that low-carbon steels that are open or semikilled as tapped roll better than completely deoxidized or killed steels. This has led to the belief that oxygen plays an important part in the rolling qualities of sulphur-bearing steels. It is generally held that the red shortness of sulphur steels is due to the low melting point of the sulphide compounds that separate out at the grain boundaries when the steel solidifies. At the rolling temperature of steel these sulphide compounds melt and cause cracking. Adding Sulphur as a Sulphite These difficulties can be avoided if sulphur is introduced into the stecl by means of an anhydrous sulphite, such as sodium sulphite or sodium bisulphite, which—upon decomposition—forms sulphur dioxide. It is assumed that, in this case, the oxygen of the sulphur dioxide forms part of the sulphide inclusions in the steel, and raises their solidification temperature enough so that the formation in the steel of a low-melting eutectic is prevented. The result is the prevention of hot shortness and a more uniform distribution of inclusions. Fig. I shows photomicrographs of steels made with sulphur, while Fig. 2 illustrates the structure of steels made with sodium bisulphite. These samples were cut from the steels as cast—that is, before rolling— and were polished and lightly etched to bring out the grain boundaries. Fig. I shows that sulphide inclusions segregate more or less at the grain boundaries, and it can be seen how the continuity of these low-melting inclusions would cause red shortness. Fig. 2 shows that the sulphide inclusions arc more or less uniformly distributed throughout the matrix. This arrangement of inclusions has no apparent effect on the rolling qualities of a steel. This statement has been substantiated by the observation of the rolling of over 6000 tons of steel made with a sulphite addition. Results As stated before, the sulphur dioxide is added to steel by means of the decomposi- 27

Jan 1, 1942

By H. T. Bowman

For more than 80 years the Bessemer process has depended upon the ability, skill, and judgment of the blower, although as early as the I860's it was recognized that the process would benefit by some type of instrumental contro1.l IIowever, instruments with sufficient recording speeds did not exist, so the end-point determination was always dependent upon the blower's eye. This placed an obstacle in the way of precise experimental work, because of the absence of the necessary records and reference points as reported by Work.2 The use of the photocell provided the instantaneous record of the blow that made this experimental work possible and provided more scientific control for the process as discussed by Graham,3 A brief description of the progress of the blow will illustrate the recording function of the instrument. The silicon in the iron is being oxidized during the first minutes of the blow, as pointed out by Henning4 in a table showing the order of metalloid elimination. The product of this oxidation is a solid that remains in the converter, so there is virtually no flame during this part of the blow. This low flame luminosity is illustrated by the flame recording shown in Fig. I, where the silicon blow is plainly marked. The dull flame of the silicon blow gradually gives way to the brilliant carbon flame as the increasing quantities of carbon monoxide formed inside the converter burn to dioxide upon contact with the atmosphere above the vessel. When the carbon reaches some low value under 0.20 per cent, there is insufficient menoxide formed to maintain the dioxide flame, so its intensity drops. Throughout the flame drop carbon continues to burn, until at some value around 0.05 per cent an arrest occurs in the recorded drop. This point has been designated as the end point. The period of time from this end point until the vessel is turned upon its side and blowing has stopped has been called the afterblow. This afterblow is used as a measure of the degree of metal oxidation, and uniformity demands that it be controlled within narrow limits. Iron and blowing conditions are likely to change several times during a turn, necessitating corresponding changes in end-point control. It is the purpose of this paper to discuss these changes, the factors that make them necessary, and their bearing upon the quality of steel. Carbon-FeO Relationship In the Bessemer process oxidation relationships are precise. Fig. 2 shows a graph of the carbon-FeO relationship. The familiar "bomb-test" method, described by Mccutcheon and Rautio,5 was used for obtaining these and all other dissolved FeO values herein reported, all tests being taken from the converter before deoxidation unless otherwise noted. All tests of 0.10 per. cent carbon and above were obtained from metal blown for duplexing. McGinley and Woodworth6 reported iron oxide values for blown metal, but their tests were obtained by a . different method than were those

Jan 1, 1942

By H. T. Bowman

For more than 80 years the Bessemer process has depended upon the ability, skill, and judgment of the blower, although as early as the I860's it was recognized that the process would benefit by some type of instrumental contro1.l IIowever, instruments with sufficient recording speeds did not exist, so the end-point determination was always dependent upon the blower's eye. This placed an obstacle in the way of precise experimental work, because of the absence of the necessary records and reference points as reported by Work.2 The use of the photocell provided the instantaneous record of the blow that made this experimental work possible and provided more scientific control for the process as discussed by Graham,3 A brief description of the progress of the blow will illustrate the recording function of the instrument. The silicon in the iron is being oxidized during the first minutes of the blow, as pointed out by Henning4 in a table showing the order of metalloid elimination. The product of this oxidation is a solid that remains in the converter, so there is virtually no flame during this part of the blow. This low flame luminosity is illustrated by the flame recording shown in Fig. I, where the silicon blow is plainly marked. The dull flame of the silicon blow gradually gives way to the brilliant carbon flame as the increasing quantities of carbon monoxide formed inside the converter burn to dioxide upon contact with the atmosphere above the vessel. When the carbon reaches some low value under 0.20 per cent, there is insufficient menoxide formed to maintain the dioxide flame, so its intensity drops. Throughout the flame drop carbon continues to burn, until at some value around 0.05 per cent an arrest occurs in the recorded drop. This point has been designated as the end point. The period of time from this end point until the vessel is turned upon its side and blowing has stopped has been called the afterblow. This afterblow is used as a measure of the degree of metal oxidation, and uniformity demands that it be controlled within narrow limits. Iron and blowing conditions are likely to change several times during a turn, necessitating corresponding changes in end-point control. It is the purpose of this paper to discuss these changes, the factors that make them necessary, and their bearing upon the quality of steel. Carbon-FeO Relationship In the Bessemer process oxidation relationships are precise. Fig. 2 shows a graph of the carbon-FeO relationship. The familiar "bomb-test" method, described by Mccutcheon and Rautio,5 was used for obtaining these and all other dissolved FeO values herein reported, all tests being taken from the converter before deoxidation unless otherwise noted. All tests of 0.10 per. cent carbon and above were obtained from metal blown for duplexing. McGinley and Woodworth6 reported iron oxide values for blown metal, but their tests were obtained by a . different method than were those

Jan 1, 1942

By R. W. Gurry

Thermodynamic calculations indicate that boron is a better deoxidizer than silicon but probably is not quite as effective as aluminum. Boron should, therefore, be readily oxidized out of the open-hearth bath, which implies that it is not recovered in significant concentration from any scrap charged; also that, if added in the ladle, it tends to oxidize out during teeming unless protected by the presence of a better deoxidizing agent. These conclusions do not apply to liquid cast iron, in which the oxygen content is much lower than in liquid steel. The possibility of conserving certain strategic alloying elements widely used in steelmaking, notably manganese, chromium and molybdenum, by the use of boron, which in small concentration appears to be extraordinarily effective in promoting hardenability, raises a question as to what extent any boron present in the scrap charged into the open hearth is oxidized out during melting and subsequent refining. This question is significant because the optimum concentration of boron in the finished steel, which is fairly critical, would be very difficult to attain if the boron in the charge were largely retained in the metal. Moreover, unless boron is substantially eliminated in the open-hearth process its use on a large scale would eventually make it impossible to produce boron-free steel except by restricting the charge to virgin material. There is at present, unfortunately, virtually no satisfactory direct evidence to provide an answer to this question; but there are indications from practice that boron is oxidized out in the open hearth in the production of medium or low-carbon steel, although it may be retained if the carbon content remains fairly high; that is, if the oxygen is kept fairly low. In the absence of direct data, it is necessary to rely upon the indications of indirect evidence, the best approach now available being a thermodynamic calculation of the deoxidizing power of boron in liquid steel by the general method used so successfully by Chipman1 in his study of the reactions in the open-hearth process. The thermal data for boron, upon which such a calculation must be based, are reasonably satisfactory; the only quantities not directly determined are the entropy of melting of boron, the activity coefficient of boron in liquid steel, and the activity coefficient of B2O3in an open-hearth slag; but these values may be estimated with ample accuracy. The results of this calculation, which is presented later, are given in Table I, together with corresponding data for other deoxidizing elements. This table shows the calculated residual content of oxygen in equilibrium with different residual concentrations of the deoxidizer in the metal;

Jan 1, 1944

By R. W. Gurry

Thermodynamic calculations indicate that boron is a better deoxidizer than silicon but probably is not quite as effective as aluminum. Boron should, therefore, be readily oxidized out of the open-hearth bath, which implies that it is not recovered in significant concentration from any scrap charged; also that, if added in the ladle, it tends to oxidize out during teeming unless protected by the presence of a better deoxidizing agent. These conclusions do not apply to liquid cast iron, in which the oxygen content is much lower than in liquid steel. The possibility of conserving certain strategic alloying elements widely used in steelmaking, notably manganese, chromium and molybdenum, by the use of boron, which in small concentration appears to be extraordinarily effective in promoting hardenability, raises a question as to what extent any boron present in the scrap charged into the open hearth is oxidized out during melting and subsequent refining. This question is significant because the optimum concentration of boron in the finished steel, which is fairly critical, would be very difficult to attain if the boron in the charge were largely retained in the metal. Moreover, unless boron is substantially eliminated in the open-hearth process its use on a large scale would eventually make it impossible to produce boron-free steel except by restricting the charge to virgin material. There is at present, unfortunately, virtually no satisfactory direct evidence to provide an answer to this question; but there are indications from practice that boron is oxidized out in the open hearth in the production of medium or low-carbon steel, although it may be retained if the carbon content remains fairly high; that is, if the oxygen is kept fairly low. In the absence of direct data, it is necessary to rely upon the indications of indirect evidence, the best approach now available being a thermodynamic calculation of the deoxidizing power of boron in liquid steel by the general method used so successfully by Chipman1 in his study of the reactions in the open-hearth process. The thermal data for boron, upon which such a calculation must be based, are reasonably satisfactory; the only quantities not directly determined are the entropy of melting of boron, the activity coefficient of boron in liquid steel, and the activity coefficient of B2O3in an open-hearth slag; but these values may be estimated with ample accuracy. The results of this calculation, which is presented later, are given in Table I, together with corresponding data for other deoxidizing elements. This table shows the calculated residual content of oxygen in equilibrium with different residual concentrations of the deoxidizer in the metal;

Jan 1, 1944

By William J. McCaughey, Richard L. Barrett

For sixty years—in fact, ever since the inception of the basic steelmaking process —basic slags have been the subject of study by chemists, metallurgists and petrog-raphers! with the purpose of providing a better understanding of the reactions between the slag and the metal during the refining process. The result of this work and of the researches of mineralogists and physical chemists into the chemistry of oxide systems is a considerable body of literature dealing not only with slags themselves but with equilibrium relationships in systems synthesized from pure components. Since any actual slag is a multicom-ponent system more complex than any yet worked out in the laboratory, a complete solution to the problem is still far away. The writers have recently published a paper1 which they believe sheds light on the role of the slag in the elimination of phosphorus and it is the purpose of the present paper to discuss the metallurgical applications of that work. Since the pioneer investigations on the constitution of basic slags carried on by Stead and Risdale, Carnot and Richards, Hilgenstock and others in the I88o's, a considerable body of literature on this subject has appeared. Many of the more important of these papers were summarized in the previous paper,l therefore they will not be reviewed here. PetRographic Study The present writers have had occasion, over a period of years, to examine petro-graphically a great number of basic steel-making slags having a very wide range of chemical compositions and made under various conditions of operating practice. Although certain of these slags exhibit some unusual features, it is a remarkable fact that the great majority of mature slags show certain typical characteristics, which persist throughout the wide range of chemical compositions. The typical mature slag usually appears under the microscope to consist of two phases. The phase of primary crystallization is light colored and doubly refracting. If separated mechanically and subjected to chemical analysis, it is found to consist essentially of SiO2, CaO, and P2O6. Sometimes, although not usually, two such silicate-phosphate phases are found. The other conspicuous phase is dark in color and optically isotropic, and occurs as the interstitial material between the grains of the light colored phase. This dark colored interstitial phase when analyzed is found to consist essentially of FeO, Fe2O3, MnO, and MgO. In some 'lags high in iron oxide, particularly those from low-carbon heats, dicalcium ferrite is found. This phase is dark reddish brown in color and anisotropic.

Jan 1, 1944

By William J. McCaughey, Richard L. Barrett

For sixty years—in fact, ever since the inception of the basic steelmaking process —basic slags have been the subject of study by chemists, metallurgists and petrog-raphers! with the purpose of providing a better understanding of the reactions between the slag and the metal during the refining process. The result of this work and of the researches of mineralogists and physical chemists into the chemistry of oxide systems is a considerable body of literature dealing not only with slags themselves but with equilibrium relationships in systems synthesized from pure components. Since any actual slag is a multicom-ponent system more complex than any yet worked out in the laboratory, a complete solution to the problem is still far away. The writers have recently published a paper1 which they believe sheds light on the role of the slag in the elimination of phosphorus and it is the purpose of the present paper to discuss the metallurgical applications of that work. Since the pioneer investigations on the constitution of basic slags carried on by Stead and Risdale, Carnot and Richards, Hilgenstock and others in the I88o's, a considerable body of literature on this subject has appeared. Many of the more important of these papers were summarized in the previous paper,l therefore they will not be reviewed here. PetRographic Study The present writers have had occasion, over a period of years, to examine petro-graphically a great number of basic steel-making slags having a very wide range of chemical compositions and made under various conditions of operating practice. Although certain of these slags exhibit some unusual features, it is a remarkable fact that the great majority of mature slags show certain typical characteristics, which persist throughout the wide range of chemical compositions. The typical mature slag usually appears under the microscope to consist of two phases. The phase of primary crystallization is light colored and doubly refracting. If separated mechanically and subjected to chemical analysis, it is found to consist essentially of SiO2, CaO, and P2O6. Sometimes, although not usually, two such silicate-phosphate phases are found. The other conspicuous phase is dark in color and optically isotropic, and occurs as the interstitial material between the grains of the light colored phase. This dark colored interstitial phase when analyzed is found to consist essentially of FeO, Fe2O3, MnO, and MgO. In some 'lags high in iron oxide, particularly those from low-carbon heats, dicalcium ferrite is found. This phase is dark reddish brown in color and anisotropic.

Jan 1, 1944

By George B. Waterhouse

Jan 1, 1933

By Sam Tour

Some years ago, the writer described heat checks or thermal cracks that occur in die-casting dies.' The life of dies was considered in relation to. the casting temperature, the material used for the die and the heat to be absorbed by the die per unit volume of casting made. The mechanism of the action that results in thermal failure of dies was described. In the present paper the writer proposes to describe some additional observations in regard to heat checking, make one or two suggestions as to the method or methods for further attack of the problem, and give the results obtained on some work carried out along these lines. Importance of Heat Checking Heat checks in steel are the source of trouble in many industries besides that of die casting. Every shop where metals are subjected to hot working is searching for improvement and hoping for a cure. The development of a material of sufficient strength to be used as a die and yet devoid of the property of heat checking would be a godsend to many shops and many industries. The need for thorough study and research on the subject is evidenced by the wide variety of hot-working die steels on the market. It is peculiar, but true, that in practically every case the maker of the steel can give concrete evidence to prove his contention that his type of hot-working die steel is as good as or better than any other. A number of steel companies have several hot-working die steels from which choice can be made to fit a particular set of requirements. Possibly to expect one material to be universally the best hot-working die steel is unreasonable. In some hot-working operations, as in drop forging, the die must have great toughness to withstand the stresses developed; in other operations, as in hot piercing or punching, resistance to erosion at high temperatures, possibly defined as strength and hardness at elevated temperatures, is required. In still others, as in die casting, only sufficient hardness to resist scoring between moving surfaces is required, whereas the resistance to sudden changes in temperature must be at a maximum.

Jan 1, 1935

By Sam Tour

Some years ago, the writer described heat checks or thermal cracks that occur in die-casting dies.' The life of dies was considered in relation to. the casting temperature, the material used for the die and the heat to be absorbed by the die per unit volume of casting made. The mechanism of the action that results in thermal failure of dies was described. In the present paper the writer proposes to describe some additional observations in regard to heat checking, make one or two suggestions as to the method or methods for further attack of the problem, and give the results obtained on some work carried out along these lines. Importance of Heat Checking Heat checks in steel are the source of trouble in many industries besides that of die casting. Every shop where metals are subjected to hot working is searching for improvement and hoping for a cure. The development of a material of sufficient strength to be used as a die and yet devoid of the property of heat checking would be a godsend to many shops and many industries. The need for thorough study and research on the subject is evidenced by the wide variety of hot-working die steels on the market. It is peculiar, but true, that in practically every case the maker of the steel can give concrete evidence to prove his contention that his type of hot-working die steel is as good as or better than any other. A number of steel companies have several hot-working die steels from which choice can be made to fit a particular set of requirements. Possibly to expect one material to be universally the best hot-working die steel is unreasonable. In some hot-working operations, as in drop forging, the die must have great toughness to withstand the stresses developed; in other operations, as in hot piercing or punching, resistance to erosion at high temperatures, possibly defined as strength and hardness at elevated temperatures, is required. In still others, as in die casting, only sufficient hardness to resist scoring between moving surfaces is required, whereas the resistance to sudden changes in temperature must be at a maximum.

Jan 1, 1935

By Alden B. Greninger, Victor G. Mooradian

Microscopic examinations of quenched (beta) 60:40 copper-zinc and quenched (beta) 74:26 copper-tin alloys have frequently disclosed long, thin parallel bands or markings within the polyhedral beta grains. Apparently, it has been accepted that these markings are mechanical twin bands, although there is no published account of experimental data that might tend to substantiate this belief for the copper-zinc system, and only meager evidence has been submitted for the copper-tin system. Johnsonl0 commented upon the markings he observed after deforming a quenched brass of 55.6 per cent copper and 44.4 per cent zinc. Clark's papers4 on the heat-treatment of Muntz metal contain many photomicrographs of markings in beta brass; these she referred to as Neumann bands (inasmuch as repolishing and re-etching failed to remove them) and stated that markings present in Muntz metal as quenched were the result of shock imparted during the polishing operation. Van Wert18 first suggested that these parallel markings in quenched beta brass (60:40) might be alpha precipitated along certain crystallographic planes of the matrix lattice. He showed that upon reheating the specimens to temperatures below 800" C., obvious precipitation of alpha within the large beta grains first occurred at the markings. In a discussion of this paper, Phillips stated (pp. 505-507) that in his opinion the markings observed by Van Wert were mechanical twins resulting from contraction strains produced during the quenching operation. In a study of segregate structures in beta copper-tin, Smith17 observed that in the quenched beta phase (containing 74.92 per cent Cu) parallel . bands or markings very similar to those in metastable beta brass could be

Jan 1, 1938

By Alden B. Greninger, Victor G. Mooradian

Microscopic examinations of quenched (beta) 60:40 copper-zinc and quenched (beta) 74:26 copper-tin alloys have frequently disclosed long, thin parallel bands or markings within the polyhedral beta grains. Apparently, it has been accepted that these markings are mechanical twin bands, although there is no published account of experimental data that might tend to substantiate this belief for the copper-zinc system, and only meager evidence has been submitted for the copper-tin system. Johnsonl0 commented upon the markings he observed after deforming a quenched brass of 55.6 per cent copper and 44.4 per cent zinc. Clark's papers4 on the heat-treatment of Muntz metal contain many photomicrographs of markings in beta brass; these she referred to as Neumann bands (inasmuch as repolishing and re-etching failed to remove them) and stated that markings present in Muntz metal as quenched were the result of shock imparted during the polishing operation. Van Wert18 first suggested that these parallel markings in quenched beta brass (60:40) might be alpha precipitated along certain crystallographic planes of the matrix lattice. He showed that upon reheating the specimens to temperatures below 800" C., obvious precipitation of alpha within the large beta grains first occurred at the markings. In a discussion of this paper, Phillips stated (pp. 505-507) that in his opinion the markings observed by Van Wert were mechanical twins resulting from contraction strains produced during the quenching operation. In a study of segregate structures in beta copper-tin, Smith17 observed that in the quenched beta phase (containing 74.92 per cent Cu) parallel . bands or markings very similar to those in metastable beta brass could be

Jan 1, 1938

By E. M. Wise

The practice of adding moderate quantities of nickel to a variety of bronzes has been employed by foundrymen for many years with several objects in view. In some instances it was desired to harden the alloy; in others it was to increase the fluidity or to improve the solidity of the castings, or to refine their grain. These important matters have been considered in detail by Pilling and Kihlgrenl and by numerous other workers cited by them, and with the exception of the first will not be considered in the present communication. The possibility of reducing the cost of bronze by replacing a portion of the tin with nickel received attention some years ago by Burgess and Woodward12 and, as will be shown later, offers attractive savings in cost under present conditions. The age-hardening characteristics of the nickel bronzes of appropriate compositions have been known for some time and were mentioned by Price, Grant and Phillips3 and discussed by Wise4 in connection with their paper. These matters are further considered in recent patents15 and are becoming of commercial importance in the production of high-strength castings. The equilibrium relations existing in the high-copper region of the copper-nickel-tin system have been carefully studied by Eash and Upthegrove,6 and in somewhat less detail by Veszelka.7 The observa-

Jan 1, 1934

By George Espey, George Sachs, G. B. Kasik

IT has been reported frequently that the hardness and strength vary over the cross section of cold-worked, particularly cold-drawn, material. Brass rod and wire usually have been found to possess a maximum strength and hardness near the surface.1,2 According to Sachs,' the center fiber has about the same strength as a wire stretched by the same amount in a tensile-test machine, the strength increasing toward the surface (Fig. I). These differences are particularly large for wire given a small reduction on drawing through a die with a wide opening. However, with increasing reduction and hardness, a tendency to form a thin soft surface skin becomes apparent. On the contrary, copper wire has usually been found to possess a soft surface skin3-5 and it has been reported by Harris3 that during the cold-drawing of hot-rolled wire the surface layer becomes increasingly softer than the core, while the layer of maximum strength moves toward the core, it being found near the surface at first. The increase of strength and hardness from the core to the skin is readily explained by the observation that, in addition to the stretching, the layers of a rod or wire are sheared more the closer they are to the surface.1,6-8 However, the presence of a soft surface layer can be attributed only to an annealing effect. The source of such a softening might be the extremely high temperature that originates from the friction between

Jan 1, 1942