By H. H. Uhlig

Soon after general use of stainless steels began, it was observed in practice that certain combinations of factors tended to induce corrosion by pitting. For most applications this was a serious drawback, not SO much because the structural properties of the metal were impaired but because of the rapidity with which heavy sections of the alloys were penetrated by small elongated pits. These pits seemed to initiate readily in oxidizing metal salt solutions like ferric chloride and in chloride solutions like sea water. It was observed that in sea water pitting was more frequent in stagnant or polluted waters than in highly aerated, moving waters. The steels in these chloride solutions were observed to be sensitive to long contact with material such as sand grains or attached barnacles. At points of attachment or contact it was not uncommon to discover initiation of corrosion. Pits once begun at contact faces were observed to grow rapidly, usually elongating phenomenally in the direction of gravity until the metal was perforated. Hydrochloric acid and other nonoxidizing acids, on the other hand, were observed to corrode stainless steels generally; the weight losses often were higher, but the penetration less than for the pitting type of corrosion. The causes of pitting, a type of corrosion recognized as characteristic not only of stainless steels but of many additional metals and alloys, are important in corrosion studies. A possible explanation bears practical significance, for once it is known why pits begin where they do and continue to grow after initiation, intelligent direction can be given to diminishing corrosion. This can be done either by some alteration in the composition and treatment or' the alloy or by some alteration in the environment. It appears foremost in importance to discover the nature of pit foci, for if initiation of pits can be discouraged their growth will be no longer a factor to be considered. In a multi-component alloy containing many impurities normal to production of such an alloy, each of which may play a part in pitting, and whose corrosion resistance is sensitive to heat-

Jan 1, 1940

By H. H. Uhlig

Soon after general use of stainless steels began, it was observed in practice that certain combinations of factors tended to induce corrosion by pitting. For most applications this was a serious drawback, not SO much because the structural properties of the metal were impaired but because of the rapidity with which heavy sections of the alloys were penetrated by small elongated pits. These pits seemed to initiate readily in oxidizing metal salt solutions like ferric chloride and in chloride solutions like sea water. It was observed that in sea water pitting was more frequent in stagnant or polluted waters than in highly aerated, moving waters. The steels in these chloride solutions were observed to be sensitive to long contact with material such as sand grains or attached barnacles. At points of attachment or contact it was not uncommon to discover initiation of corrosion. Pits once begun at contact faces were observed to grow rapidly, usually elongating phenomenally in the direction of gravity until the metal was perforated. Hydrochloric acid and other nonoxidizing acids, on the other hand, were observed to corrode stainless steels generally; the weight losses often were higher, but the penetration less than for the pitting type of corrosion. The causes of pitting, a type of corrosion recognized as characteristic not only of stainless steels but of many additional metals and alloys, are important in corrosion studies. A possible explanation bears practical significance, for once it is known why pits begin where they do and continue to grow after initiation, intelligent direction can be given to diminishing corrosion. This can be done either by some alteration in the composition and treatment or' the alloy or by some alteration in the environment. It appears foremost in importance to discover the nature of pit foci, for if initiation of pits can be discouraged their growth will be no longer a factor to be considered. In a multi-component alloy containing many impurities normal to production of such an alloy, each of which may play a part in pitting, and whose corrosion resistance is sensitive to heat-

Jan 1, 1940

By C. H. Mathewson, J. A. Collins

The process of plastic extension of face-centered cubic single crystalline rods is so well understood, since the notable studies of Taylor and Elam,1 that the change in orientation of any crystal by slip and rotation may be predicted from the measured elongation. It is customary to assume a very homogeneous deformation, wherein gliding lamellar arc free to rotate so that their slip direction continually approaches the axis of the rod, until a second slip system comes into operation; whereupon conjugate slip proceeds quantitatively to an end adjustment with the [121] direction in the axis of the rod. This process has been checked in malty face.-centered cubie materialsand and readily permits the preparation of specimens that have been subjtvted to various determinable amounts of shearing action. It is elearly of interest to study in such measurably strained speeimens the, development of a recrystallized structure on annealing and if possilble detect the source of nuclei from which the new crystals grow. Strain-:~nneali~ig experiments of this charactcr have been performed by others but not in detail sufficient to permit a study, for example, of the number of recrystallized grains vs. the amount of shear. In the experiments now reported, this was done with a wide variety of orientations covering nearly the entire range of slip on a single system and corresponding to amounts of shear (ratio of shearing distance to distance between lamellae at the conclusion of a test of from 0.08 to 0.57. A particular point wa-made of determining the crystallite rotation, or small angular range. assumed by the octahedral slip plane after these various amounts of shear. The, mechanism of reerystallization and the magnitude and effeet of recovery on the recrystallization process was investigated.

Jan 1, 1940

By J. A. Collins, C. H. Mathewson

The process of plastic extension of face-centered cubic single crystalline rods is so well understood, since the notable studies of Taylor and Elam,1 that the change in orientation of any crystal by slip and rotation may be predicted from the measured elongation. It is customary to assume a very homogeneous deformation, wherein gliding lamellar arc free to rotate so that their slip direction continually approaches the axis of the rod, until a second slip system comes into operation; whereupon conjugate slip proceeds quantitatively to an end adjustment with the [121] direction in the axis of the rod. This process has been checked in malty face.-centered cubie materialsand and readily permits the preparation of specimens that have been subjtvted to various determinable amounts of shearing action. It is elearly of interest to study in such measurably strained speeimens the, development of a recrystallized structure on annealing and if possilble detect the source of nuclei from which the new crystals grow. Strain-:~nneali~ig experiments of this charactcr have been performed by others but not in detail sufficient to permit a study, for example, of the number of recrystallized grains vs. the amount of shear. In the experiments now reported, this was done with a wide variety of orientations covering nearly the entire range of slip on a single system and corresponding to amounts of shear (ratio of shearing distance to distance between lamellae at the conclusion of a test of from 0.08 to 0.57. A particular point wa-made of determining the crystallite rotation, or small angular range. assumed by the octahedral slip plane after these various amounts of shear. The, mechanism of reerystallization and the magnitude and effeet of recovery on the recrystallization process was investigated.

Jan 1, 1940

By C. H. Mathewson, M. R. Pickus

The study of the plastic deformation and recrystallization of metals has been the subject of many investigations. In regard to the simple deformational processes, such as tension and compression, the early knowledge gained from studies of polycrystalline material has been supplemented by many significant researches on the behavior of single crystals. Unfortunately, this has not been true for more complicated deformational processes. As far back as 1927, G. I. Taylor1 wrote: It is impossible in the present state of knowledge to do more than give a possible reason why (face-centered cubic) crystals set themselves with a (110) direction in the plane of rolling, and at right angles to the direction of rolling. The explanation of why the orientation of the crystal axes round the transverse direction is what it is, must be left till the distortion of metals, and particularly single crystals of metals in the process of rolling, has been studied in greater detail. That this gap in the systematic study of deformation and recrystallization has not yet been filled was indicated by C. H. Samans, who wrote in 1934 that "only four investigations upon cold-rolled single crystals of any of the face-centered cubic metals have been reported in the literature." Of these four studies, only those of S. Tanaka3 and T. Sakaoj4 both of whom worked with aluminum crystals, had quantitative significance. The other two, carried out by F. Wever5 and W. G. Burgers16 were of a qualitative nature. It is our hope that the present investigation may contribute something to the knowledge necessary for a rationalization of the origin of rolling textures in terms of the known behavior of single crystals, and may add pertinent information concerning the recrystallization characteristics of deformed single crystals.

Jan 1, 1939

By M. R. Pickus, C. H. Mathewson

The study of the plastic deformation and recrystallization of metals has been the subject of many investigations. In regard to the simple deformational processes, such as tension and compression, the early knowledge gained from studies of polycrystalline material has been supplemented by many significant researches on the behavior of single crystals. Unfortunately, this has not been true for more complicated deformational processes. As far back as 1927, G. I. Taylor1 wrote: It is impossible in the present state of knowledge to do more than give a possible reason why (face-centered cubic) crystals set themselves with a (110) direction in the plane of rolling, and at right angles to the direction of rolling. The explanation of why the orientation of the crystal axes round the transverse direction is what it is, must be left till the distortion of metals, and particularly single crystals of metals in the process of rolling, has been studied in greater detail. That this gap in the systematic study of deformation and recrystallization has not yet been filled was indicated by C. H. Samans, who wrote in 1934 that "only four investigations upon cold-rolled single crystals of any of the face-centered cubic metals have been reported in the literature." Of these four studies, only those of S. Tanaka3 and T. Sakaoj4 both of whom worked with aluminum crystals, had quantitative significance. The other two, carried out by F. Wever5 and W. G. Burgers16 were of a qualitative nature. It is our hope that the present investigation may contribute something to the knowledge necessary for a rationalization of the origin of rolling textures in terms of the known behavior of single crystals, and may add pertinent information concerning the recrystallization characteristics of deformed single crystals.

Jan 1, 1939

By T. L. Joseph

Blast furnaces are most efficient thermally when the CO2 in the top gas is highest. Oxygen introduced in the air blast is converted to CO in the combustion zones. The extent to which CO, generated in front of the tuyeres, is converted later to CO2 depends upon the ratio of ore to coke in the charge and the degree to which CO2, formed by reduction of iron oxides with CO, reverts to CO by the secondary reaction C + CO2 = 2CO. About 300 to 400 lb. of carbon' per ton of pig iron is normally involved in the solution-loss reaction or direct reduction of FeO with carbon, which produces the same over-all results; that is, lower CO2 in the top gas. Rich2 has recently reported a reduction in fuel consumption at slower rates of blowing on two furnaces in spite of higher heat losses per ton of iron. Lower fuel consumption at slow operating rates was due to more complete reduction of the ore that resulted in higher CO2 in the top gas and consequently more efficient use of carbon. Kinney3 has reported substantial savings in fuel as a result of crushing and sizing the ore charge. Improvements in practice brought about by sintering magnetite concentrates, flue dust and fine ores have been due to the establishment of conditions favoring more complete reduction of the ore in the upper part of the furnace. The extent to which oxides and fluctuations in composition in pig iron affect the quality of steel and finished product needs further study. There is evidence that more thorough preheating and reduction of the ore in the upper part of the furnace tend to give a better quality of iron. Bogatzkii4 found from laboratory work that the amount of oxygen entering electrolytic iron, melted under various slags, was directly proportional to the concentration of free FeO in the slag and inversely proportional to the basicity of the slag. Herty and Gaines5 concluded that the silicate content of open-hearth steel before deoxidation is related to the concentration of silica in the pig-iron charge, indicating that most of the persistent inclusions are silica from the iron. They also found that

Jan 1, 1936

By T. L. Joseph

Blast furnaces are most efficient thermally when the CO2 in the top gas is highest. Oxygen introduced in the air blast is converted to CO in the combustion zones. The extent to which CO, generated in front of the tuyeres, is converted later to CO2 depends upon the ratio of ore to coke in the charge and the degree to which CO2, formed by reduction of iron oxides with CO, reverts to CO by the secondary reaction C + CO2 = 2CO. About 300 to 400 lb. of carbon' per ton of pig iron is normally involved in the solution-loss reaction or direct reduction of FeO with carbon, which produces the same over-all results; that is, lower CO2 in the top gas. Rich2 has recently reported a reduction in fuel consumption at slower rates of blowing on two furnaces in spite of higher heat losses per ton of iron. Lower fuel consumption at slow operating rates was due to more complete reduction of the ore that resulted in higher CO2 in the top gas and consequently more efficient use of carbon. Kinney3 has reported substantial savings in fuel as a result of crushing and sizing the ore charge. Improvements in practice brought about by sintering magnetite concentrates, flue dust and fine ores have been due to the establishment of conditions favoring more complete reduction of the ore in the upper part of the furnace. The extent to which oxides and fluctuations in composition in pig iron affect the quality of steel and finished product needs further study. There is evidence that more thorough preheating and reduction of the ore in the upper part of the furnace tend to give a better quality of iron. Bogatzkii4 found from laboratory work that the amount of oxygen entering electrolytic iron, melted under various slags, was directly proportional to the concentration of free FeO in the slag and inversely proportional to the basicity of the slag. Herty and Gaines5 concluded that the silicate content of open-hearth steel before deoxidation is related to the concentration of silica in the pig-iron charge, indicating that most of the persistent inclusions are silica from the iron. They also found that

Jan 1, 1936

By W. J. Reagan

The problem of increasing output and decreasing percentage of rejections is a vital one in the manufacture of steel of any kind. The making of basic open-hearth steel for use in rolled steel wheels, tires for locomotive and car wheels, and forgings of various kinds, is a highly specialized industry. The increase in weight of railway rolling stock of all kinds, and the high speed that the public demands of transportation facilities, make it imperative that steel for use in this class of material shall be of the highest quality obtainable. During the past few years it has been the writer's good fortune to have opportunity to study the defects in basic open-hearth steel, and also the results obtained by various changes in open-hearth practice, on such defects. The opportunity for study and the details available are rarely found in the manufacture of steel of any kind. It seems reasonable to assume that many of the results determined here can be applied to the production of steel of other types with a decided improvement in quality, a decrease in the percentage of rejections and an increase in output. All of the material described is basic open-hearth steel with the following range of analysis: carbon, 0.50 to 0.85 per cent.; phosphorus and sulfur, 0.04 max.; silicon, 0.15 to 0.35; manganese, 0.50 to 0.75. All of this material is bottom-cast, therefore tapping and pouring temperatures are higher than in top-cast production. Ingots used in this type of work are of standard length with varying diameters. The ingot is known as duodecagonal, or twelve-sided. The standard body length is 88 in. and the hot top length, 14 in. Fig. 1 shows a typical ingot of this type. The diameter varies from 13 to 30 in. Ingots for special forgings, which cannot be made in molds of standard size, are made in molds of various sizes and designs. These ingots are sliced cold, into blocks of various lengths, depending upon the weight of the forging to be made. Fig. 2 shows the ingot after coming from the slicing lathe. Jusf sufficient metal remains between blocks to hold the ingot in one piece while it is being removed from the lathe; then steel wedges are inserted between the blocks and the blocks are broken apart. This affords abundant opportunity for inspection, as the interior of the

Jan 1, 1930

By Cyril Stanley Smith, Earl W. Palmer

A complete discussion of the literature on the subject of the influence of copper on iron and steel will be published elsewhere.' The present paper is concerned especially with the precipitation-hardening of copper steels, and brief mention will be made here only of the work of Kin-near,2,3 Nehl4 and Buchholtz and Koster,5 who alone have studied this phase of the subject. Kinnear found that normalized low-carbon steel castings containing about 1.0 per cent copper on drawing at temperatures in the neighborhood of 530" C. (1000" F.) increased in tensile strength and yield point, with little decrease in ductility. The maximum effect was obtained with about 0.9 to 1.0 per cent copper, and when the copper exceeded 3 per cent no improvement occurred on reheating. Kinnear did not study the effect of time of reheating—an all important factor where precipitation is concerned. Neh1,6 who apparently was unaware of Kinnear's work, recognized the change as due to precipitation and studied the interdependence of time and temperature of reheating, the temperature of the initial solution heat treatment, and the speed of cooling necessary to retain the bulk of the copper in supersaturated solution and to give an increase in hardness and tensile strength on reheating. Nehl found that if the final rolling or forging temperatures exceeded 700" C. (1300" F.) it was not necessary even to normalize the steel, but full precipitation occurred on merely reheating the forged or rolled shapes at 500" C. (930" F.). Buchholtz and Koster7 studied in detail the precipitation-hardening of a mild steel containing 1.0 per cent copper and 0.5 per cent chromium. From data on the electrical and magnetic properties of copper steels, they drew the portion of the equilibrium diagram in Fig. 1, assuming the

Jan 1, 1933

By R. H. Harrington

The definition of precipitation-hardening1 is well understood and its principles have been subjected to study for some time. However, the variation of properties with double aging, combined with strain-hardening, gives promise of new and useful phenomena. Properly to understand these distinctions, definitions of these terms are necessary. Precipitation-hardening1.—This reaction usually depends upon an alloy having such a composition that it consists only, or in major part, of but one phase, a solid solution, at a high temperature, so that, upon slow cooling, this solution breaks down into two phases, the solid solution and a compound. By heating the alloy to the temperature for maximum solution of the compound, quenching, and reheating to a suitable lower temperature for critical dispersion precipitation of the compound, useful properties of the alloy may be developed to a maximum. Double Aging.—Dougle aging in part is similar to the process for precipitation-hardening, consisting of heating a precipitation-hardening alloy to the solution temperature, quenching, reheating to the suitable dispersion precipitation temperature, strain-hardening, and again reheating to a suitable temperature to develop certain useful properties to a maximum. The strain-hardening may be induced by two methods: (I) a rate of cooling from the first reheat may suffice to strain the solid solution lattice of the alloy; or (2) the alloy may be cold-worked to a suitable degree between the two reheats. Pkecipitation-hardening of Copper-cobalt-beryllium Alloys1.2 The composition of principal interest is that of 2.6 per cent Co, 0.4 per cent Be, 97 per cent Cu. The alloy has been developed commercially and, with certain reasonable precautions, ordinary brass-foundry practice suffices to produce an alloy of high quality. Preliminary Precipitation-hardening Study.—Samples were cut from a I-in. round rod cast in a graphite mold. These samples were then

Jan 1, 1937

By J. W. Halley

Copper has frequently been recommended as an alloying element for steel and the precipitation-hardening of steels containing from 1 to 2 per cent copper has been studied by a number of investigators. The straight copper steels, however, have not been used extensively and little advantage has been taken of the precipitation-hardening of complex steels containing appreciable amounts of copper. It is difficult to produce a satisfactory surface on the straight copper steels and undoubtedly this has discouraged their use. During recent years a number of steels containing enough copper to make them susceptible to precipitation-hardening have been put on the market. These steels belong to the group usually referred to as "low-alloy high-tensile " steels. They were designed for use in the " hot-rolled" condition; transportation equipment and large structures that cannot be readily heat-treated have been their chief application. Little emphasis has been placed on the possibility of strengthening those containing substantial amounts of copper by precipitation-hardening. The present investigation was undertaken to determine the precipitation-hardening characteristic of one of the "low-alloy steels." Previous Work The first complete study of the effect of time and temperature on the precipitation-hardening of plain copper steels was made by Nehll in 1930. At about the same time Bucholtz and Koster2 studied copper-chromium steels but did not determine the relation between time and temperature to produce maximum hardening. Later, Smith and Palmer3 determined the rate of hardening at various temperatures for two I per cent copper steels containing different amounts of carbon. Their tests indicated that the higher carbon content decreased the rate of hardening. They made tests on many steels containing other alloying elements in addition to copper, but did not determine the time-temperature relationship for maximum hardening for any of the complex steels. Norton,4 in studying the limit of solid solubility of copper in iron, determined the time for maximum hardening of a 2.06 per cent Cu iron

Jan 1, 1940

By J. W. Halley

Copper has frequently been recommended as an alloying element for steel and the precipitation-hardening of steels containing from 1 to 2 per cent copper has been studied by a number of investigators. The straight copper steels, however, have not been used extensively and little advantage has been taken of the precipitation-hardening of complex steels containing appreciable amounts of copper. It is difficult to produce a satisfactory surface on the straight copper steels and undoubtedly this has discouraged their use. During recent years a number of steels containing enough copper to make them susceptible to precipitation-hardening have been put on the market. These steels belong to the group usually referred to as "low-alloy high-tensile " steels. They were designed for use in the " hot-rolled" condition; transportation equipment and large structures that cannot be readily heat-treated have been their chief application. Little emphasis has been placed on the possibility of strengthening those containing substantial amounts of copper by precipitation-hardening. The present investigation was undertaken to determine the precipitation-hardening characteristic of one of the "low-alloy steels." Previous Work The first complete study of the effect of time and temperature on the precipitation-hardening of plain copper steels was made by Nehll in 1930. At about the same time Bucholtz and Koster2 studied copper-chromium steels but did not determine the relation between time and temperature to produce maximum hardening. Later, Smith and Palmer3 determined the rate of hardening at various temperatures for two I per cent copper steels containing different amounts of carbon. Their tests indicated that the higher carbon content decreased the rate of hardening. They made tests on many steels containing other alloying elements in addition to copper, but did not determine the time-temperature relationship for maximum hardening for any of the complex steels. Norton,4 in studying the limit of solid solubility of copper in iron, determined the time for maximum hardening of a 2.06 per cent Cu iron

Jan 1, 1940

By Frank Foote, E. R. Jette

In recent years the constitution of the high-silver aluminum-silver alloys has been extensively investigated. Hansenl has reviewed the literature to 1935. More recently, Obinata and Hagiya,2 Hofmann and Volk,3 Taziri4 and Tishchenko5 have confirmed the general features of the phase diagram in the region around 25 atomic per cent aluminum. In this paper we present the results of high-precision measurements of lattice constants of the silver-rich alpha solid solution in the homogeneous range and the neighboring two-phase regions. These results are used to establish the nature of the solid solution, the identity of directly measured densities with those calculated from lattice constants and the homogeneity limits of the alpha solid solution with respect to three different neighboring phases. A study of the earlier investigations indicated that the last two subjects in particular required new and accurate data. Experimental Procedure Preparation of the Alloys.—The alloys were made from high-purity silver and aluminum. The silver was "Proof Silver," 99.999 per cent pure, supplied by the U. S. Metals Refining Co. The aluminum was 99.97 per cent pure (contained Si, 0.009 per cent; Fe, 0.0016 per cent; Cu, 0.004 per cent) and was supplied by the Aluminum Company of America. The lattice constants of these two materials have been reported by Jette and Foote.6 Weighed amounts of the two metals were placed in alundum crucibles and melted in vacuo in a high-frequency induction furnace. The melts were allowed to cool in the crucible, the ingots thus obtained weighed about 10 grams. These ingots were then filed clean, hamered, again cleaned and given a homogenizing anneal in vacuo of from 6 to 15 days at temperatures ranging from 500" to 695°C. The ingots were air-cooled from the annealing temperature. Lattice-constant Measurements.—Carefully prepared filings for X-ray analysis were sealed into evacuated quartz or Pyrex tubes and annealed for various periods of time at suitable temperatures. The furnaces used were vertical, rapid-quenching furnaces, the samples being quenched by crushing the sample tube under water by means of a heavy plunger. The general X-ray technique has been previously described6 The cameras were of the symmetrical, back-reflection, focussing type. Ka, radiation from a cobait-nickel alloy target was used. The wave-length values were taken from the second edition of Siegbaum's book.7 A correction for the index of refraction was applied and the lattice constants were calculated by the method of Cohen.8, 6 The lattice constants were calculated to a common temperature of 25°C., using the value of the linear expansion coefficient of pure silver as 18.9 X 10-6. Presumably the expansion coefficient for

Jan 1, 1941

By Frank Foote, E. R. Jette

In recent years the constitution of the high-silver aluminum-silver alloys has been extensively investigated. Hansenl has reviewed the literature to 1935. More recently, Obinata and Hagiya,2 Hofmann and Volk,3 Taziri4 and Tishchenko5 have confirmed the general features of the phase diagram in the region around 25 atomic per cent aluminum. In this paper we present the results of high-precision measurements of lattice constants of the silver-rich alpha solid solution in the homogeneous range and the neighboring two-phase regions. These results are used to establish the nature of the solid solution, the identity of directly measured densities with those calculated from lattice constants and the homogeneity limits of the alpha solid solution with respect to three different neighboring phases. A study of the earlier investigations indicated that the last two subjects in particular required new and accurate data. Experimental Procedure Preparation of the Alloys.—The alloys were made from high-purity silver and aluminum. The silver was "Proof Silver," 99.999 per cent pure, supplied by the U. S. Metals Refining Co. The aluminum was 99.97 per cent pure (contained Si, 0.009 per cent; Fe, 0.0016 per cent; Cu, 0.004 per cent) and was supplied by the Aluminum Company of America. The lattice constants of these two materials have been reported by Jette and Foote.6 Weighed amounts of the two metals were placed in alundum crucibles and melted in vacuo in a high-frequency induction furnace. The melts were allowed to cool in the crucible, the ingots thus obtained weighed about 10 grams. These ingots were then filed clean, hamered, again cleaned and given a homogenizing anneal in vacuo of from 6 to 15 days at temperatures ranging from 500" to 695°C. The ingots were air-cooled from the annealing temperature. Lattice-constant Measurements.—Carefully prepared filings for X-ray analysis were sealed into evacuated quartz or Pyrex tubes and annealed for various periods of time at suitable temperatures. The furnaces used were vertical, rapid-quenching furnaces, the samples being quenched by crushing the sample tube under water by means of a heavy plunger. The general X-ray technique has been previously described6 The cameras were of the symmetrical, back-reflection, focussing type. Ka, radiation from a cobait-nickel alloy target was used. The wave-length values were taken from the second edition of Siegbaum's book.7 A correction for the index of refraction was applied and the lattice constants were calculated by the method of Cohen.8, 6 The lattice constants were calculated to a common temperature of 25°C., using the value of the linear expansion coefficient of pure silver as 18.9 X 10-6. Presumably the expansion coefficient for

Jan 1, 1941

By P. W. Bakarian

Previous determinationl,2,3 of the texture of magnesium and its alloys have shown only slight variations in the principal features of the structure. This investigation presents pole figures for magnesium and two of its alloys, in which differences of some magnitude will be shown. Schmid and Wassermann have considered the texture of magnesium in analogy with that of zinc—also a hexagonal lattice. Whereas the zinc texture is said to be derived primarily through basal slip and secondarily through {IO2}† twinning, the {102} twinning is considered impossible at the later stages of the rolling in magnesium because of its smaller axial ratio. This state of affairs appears reasonable for pure magnesium, but for alloy textures the situation is more complex. A double orientation similar to that found in zinc has been reported by J. D. Hanawalt,4 and the addition of small amounts of calcium to magnesium and its alloys to produce a double texture was noted by J. C. McDonald.5 The pole figures of this investigation, using an improved X-ray technique, show these various textures. The dependence of directional properties of rolled sheet on modifications of texture is well recognized. Correlation of physical properties with existing texture should be even more significant if quantitative valuations are attached to the various areas on the pole figures. Such a quantitative technique is developed herein. Experimental Method Two alloys were used, besides high-purity magnesium. In each case, the metal was extruded to bars 1/2 in. thick and hot-rolled to a thickness of about 0.075 in. It had been established previously that such a reduction was more than sufficient to eliminate the extruded structure. The rolling proceeded in the same direction as that of the extrusion, without any cross rolling. The temperatures corresponded to normal commercial practice, averaging around 600°F. A unique method of preparing the sample was developed in this work. Instead of using a flat specimen, a stem of the metal was cut out of the rolled sheet in the desired direction (rolling direction) as shown in Fig. I. From a sheet of 0.075 to 0.065-in. gauge, the stem was cut to a square cross section with a jeweler's saw, rounded with a file and polishing paper to a diameter of 0.060 in. and evenly etched in dilute hydrochloric acid to a diameter of 0.038 + 0.001 in. In this way, a cylinder of the original sheet with its axis in the desired direction was produced. By using this type of specimen for the pin-point pictures, any variance in the absorption of the diffracted beam at the various angular settings of the specimen, was completely eliminated.*

Jan 1, 1942

By P. W. Bakarian

Previous determinationl,2,3 of the texture of magnesium and its alloys have shown only slight variations in the principal features of the structure. This investigation presents pole figures for magnesium and two of its alloys, in which differences of some magnitude will be shown. Schmid and Wassermann have considered the texture of magnesium in analogy with that of zinc—also a hexagonal lattice. Whereas the zinc texture is said to be derived primarily through basal slip and secondarily through {IO2}† twinning, the {102} twinning is considered impossible at the later stages of the rolling in magnesium because of its smaller axial ratio. This state of affairs appears reasonable for pure magnesium, but for alloy textures the situation is more complex. A double orientation similar to that found in zinc has been reported by J. D. Hanawalt,4 and the addition of small amounts of calcium to magnesium and its alloys to produce a double texture was noted by J. C. McDonald.5 The pole figures of this investigation, using an improved X-ray technique, show these various textures. The dependence of directional properties of rolled sheet on modifications of texture is well recognized. Correlation of physical properties with existing texture should be even more significant if quantitative valuations are attached to the various areas on the pole figures. Such a quantitative technique is developed herein. Experimental Method Two alloys were used, besides high-purity magnesium. In each case, the metal was extruded to bars 1/2 in. thick and hot-rolled to a thickness of about 0.075 in. It had been established previously that such a reduction was more than sufficient to eliminate the extruded structure. The rolling proceeded in the same direction as that of the extrusion, without any cross rolling. The temperatures corresponded to normal commercial practice, averaging around 600°F. A unique method of preparing the sample was developed in this work. Instead of using a flat specimen, a stem of the metal was cut out of the rolled sheet in the desired direction (rolling direction) as shown in Fig. I. From a sheet of 0.075 to 0.065-in. gauge, the stem was cut to a square cross section with a jeweler's saw, rounded with a file and polishing paper to a diameter of 0.060 in. and evenly etched in dilute hydrochloric acid to a diameter of 0.038 + 0.001 in. In this way, a cylinder of the original sheet with its axis in the desired direction was produced. By using this type of specimen for the pin-point pictures, any variance in the absorption of the diffracted beam at the various angular settings of the specimen, was completely eliminated.*

Jan 1, 1942

By P. A. Vukmanic, M. Gensamer

Only recently has it been realized that preferred orientations are common in hot-rolled steels. In a recent paper, N. P. Gossl stated that hot-rolled mild steel exhibits a texture different from that characteristic of cold-rolled steel. No complete study of these hot-rolling textures has been reported using the pole-figure method of Wever. The material used in the work reported in this paper was the same material used by Gensamer and Mehl2 in a recent study of preferred orientations in cold-rolled steel, to which reference may be made for the composition and thermal history of the steel. Automobile-body sheet bar 1/4 in. thick was hot-rolled at two temperatures, 780' and 910' C. (1436' and 1669' F.). These temperatures refer to the temperature of the furnace in which the steel was heated; after each pass the steel was returned to the furnace and held there long enough to return to temperature. Although no accurate method was used to measure the temperature after each pass, it was estimated by color that only a slight drop in temperature occurred. In order to determine the effect of any preferred orientation that might have persisted through the normalizing treatment, one specimen at each temperature was rolled in the same direction as the original working direction and the other at right angles to it. The total reduction in each case was 85 per cent, the specimens having been reduced from 0.250 to 0.0375 in. in five passes. Final cooling was in air. Pinhole reflection photograms were taken of all four specimens, with the rolling direction vertical and the X-ray beam at an angle of 7' with the transverse direction (the transverse direction is defined as that direction in the rolling plane perpendicular to the rolling direction). These photograms, taken with a Mo target at 35 kv., are reproduced in Figs. 1, 2, 3 and 4. They show that a more pronounced texture was developed by the low-temperature rolling (780' C.), and that of the two

Jan 1, 1937

By C. S. Barrett

It has been observed that deformation in iron takes place by slip on (110) + {112) + (123) planesl, 2, but in silicon ferrite with low deformation temperatures or high silicon contents (exceeding 4 per cent) the authors have found that slip is confined wholly to (110) planes, at least with small amounts of deformation. The purpose of the present investigation was to determine the effect of this alteration of slip mechanism on preferred orientations in cold-rolled and recrystallized strips. Incidental observations on the effect of the recrystallization temperature were also made. The numerous determinations of the texture of cold-rolled iron and steel have been in satisfactory agreement as to the principal features of the texture (with the exception of a few conclusions that apparently have been based on insufficient data). The texture is chiefly one in which 11101 directions of the grains lie along the direction of rolling, with a deviation of a few degrees, and in which the (100) planes lie in the plane of the rolled sheet, with a deviation from this position chiefly about the rolling direction as an axis. This deviation about the rolling direction as an axis has been measured by different observers and lies between about 45" and 50" or 60" for iron5, 6, 9 and is usually in the neighborhood of 50" for mild stee16, 7, 8. The range of this deviation is a function of the percentage of total reduction8, 10. Post8 reported that it decreases with increasing percentage reduction, but apparently he studied only the surface material, which Gensamer and Meh17 found to be somewhat differently oriented from the material in the inside of the sheet. McLachlan and Davey10 found that the deviation also decreases with increasing percentage of total reduction for the material in the interior of the sheet and is independent of the percentage of reduction per pass. The deviation about the cross direction as an axis (the direction in the

Jan 1, 1937

By R. F. Mehl, M. Gensamer

Although a large number of X-ray photograms of cold-rolled steel have been published, two circumstances have led to the experimental work reported in this paper. The first is that no complete study, making use of the pole-figure method of Weverl, has been made of cold-rolled low-carbon steel. Wever has published pole figures of mild steel subjected to plane parallel deformation1, 2 and undoubtedly he has applied the method to cold-rolled mild steel, but the authors have not found these data published. Kurdjumow and Sachs3 have applied the method to the study of rolling and recrystallization textures in electrolytic iron; their results will be referred to later. The reason for this dearth of papers using the pole-figure method is obvious; a greater number of photograms and more analytical work (although this work is quite simple and straightforward) are required to construct a pole figure than most investigators have felt worth while, despite the fact that no other method of which the authors are aware will satisfactorily depict the orientations of the crystallites in a polycrystalline aggregate. The second circumstance that led to the work reported in this paper was the appearance of a paper by Wayne A. Sisson4 on the same subject. In his valuable study of the factors influencing the development of preferred orientations in cold-rolled mild steel, Sisson made one observation that required confirmation; that is, that at some stage of the rolling process the type of preferred orientation changed from the type that gives a photogram characterized as a "six-point" X-ray pattern to that known as a "four-point" pattern. A similar observation had been made by Tam-mann and Heinzel5, who studied the orientations developed in the rolling of steel by the specular reflection of light from the etched surface of rolled samples. These workers also found that the type of preferred orientation changed during the rolling process. The authors had some difficulty in seeing how this behavior could be consistent with modern views on the genesis of preferred orientations, particularly with those of Wever2

Jan 1, 1936