By H. S. Munroe

The dressing-works of the St. Joseph Lead Company were destroyed by fire, February 26th, 1883. Within about four months, or on July 5th, 1883, the new mill, with a capacity of 500 tons per day, was built and in active operation. The capacity of the new mill has since been increased to 800 tons per day. The old mill was built in 1867, by Mr. C. B. Parsons, the present superintendent. It was a curious rambling old structure, which had grown with the demands of the business; a few jigs having been added in one place, a table or two in another and wings and sheds added to the main buildings, from time to time, as it was found necessary to increase the efficiency or the capacity of the mill. The old mill was, moreover, a most interesting place to the student, a perfect "museum of ore-dressing." Nearly every form of dressing apparatus known to the art had, at one time or another, found a place under its roof, jigs of many kinds, concave, convex, side-bump and stationary tables, tyes, buddles, dolly-tubs, etc., etc. The method of dressing followed in the main the lines of English practice, but with many modifications, both in the machinery and the methods of working, due to the inventive genius of Mr. Parsons. Different forms of crushing apparatus were tried, and the best method of handling the ore and the different products of

Jan 1, 1889

The Inspiration ore body was discovered in 1904, but a 50 -ton mill which was installed to treat the disseminated copper ore promptly failed. The original Inspiration Company then gave way to another, backed by W. B. Thompson, which found 40 million tons of ore. Control then passed to Anaconda and Dr. Louis Ricketts took charge as consulting engineer. He abandoned the mill which had been partially built (to the horror of the stockholders, according to Ira Joralemon) and spent a year and a million dollars experimenting with flotation. The first large copper flotation plant was then built and recovered 50% more copper than had previous gravity mills. It, of course, was highly successful and became the forerunner of modern flotation plants. Inspiration is distinctive as the first fully integrated copper operation in the United States. Three open pits supply sulfide ore to the concentrator and mixed oxide and sulfide ore to a vat leaching and electrowinning operation with leached ore also being sent to the concentrator. In addition, dump leaching supplies pregnant solution for scrap iron precipitation. Inspiration has recently constructed an electric furnace smelter and also operates a continuous casting and rod plant. The new primary 54 in. by 74 in. crusher was completed in May of 1972 and replaced an older unit which was in the way of the open pit development. It is of an unusual circular silo design, which permits dumping 0 from two positions at 90 from each other. One dumping position is in line with the spider, while the other one is at right angles to it. A box girder splitter bar hung from the dump pocket slopes downward from the second dump point, across the spider cap, and rests on the pocket bottom. This splitter was not installed to protect the spider but was to aid in distributing wet ore being dumped from that position to both sides of the spider. Any large amount of wet ore delivered to one side of the spider would pack in the crusher cavity. The round front wall of the 18 ft (5.5 m) deep pocket is unlined except for light steel protection at the top, while the straight back wall is lined with vertically positioned railroad rails. Water for dust suppression is sprayed into the pocket through a cluster of 3/8 in. (9.5 mm) nozzles at the back of the pocket. About 5 gpm (19 lpm) of water are mixed with 90 psi (620 kPa) air upstream of the nozzles to produce a fog which is effective in dust control. The 54 in. Allis -Chalmers gyratory is placed mostly within one quadrant of the circular enclosure to permit placement of the apron feeder on the lowest level in the proper position to transfer crushed ore to the

Jan 1, 1978

[Abrahamson, Guy C., (5'43) Lt., 0-880861, Hammer Field Fresno Calif. Adamec, LAW, (8'42) c/o Braden Copper Co., Rancagua, Chile. Adams, Karl S., (9'43) Univ. of New Hampshire, Durham, N. H. Agnilar, Roperto Q., (9'43) Texas College of Mines, El Paso Texas. Ainge, B'onald Farra, (943) Otago University, Dunedin, New Zealand. Akaran, Cevdet A,, (9'44) Pennsylvania State College, State College, Pa. Albala, Americo, (5'44) School of Mineral Industries, The Pennsylvania State College, State College, PA.]

Jan 1, 1946

By George D. Roberts

INTRODUCTION CIVIL engineers are primarily interested in maximum core recovery. This is even more important in foundation work than in mining investigations where sludge samples are of some value. The soft materials, such as clay, gouge, or partially decomposed seams that are most readily ground up or washed away, are the materials that usually have the greatest influence on foundation and leakage conditions. Undisturbed samples of such materials should be obtained for detailed geological examination and laboratory tests. Therefore the attainable goal of sampling in connection with foundation investigations is the recovery of 99.9 pct of undisturbed core. FACTORS CAUSING CORE LOSSES The principal factors contributing to core losses are: (I) coring badly fractured or very soft material; (2) use of improperly designed coring equipment, including the use of bits of too small a diameter; (3) lack of the proper training and attitude on the part of the drillers and pertinent technical information on the part of the supervising personnel. Little can be done about the character of the material being cored but the other two factors contributing to unsatisfactory performance can be corrected. Although the title of this paper is the improvement and standardization of core barrels, it is believed that the drillers' shortcomings and the lack of pertinent technical literature are more detrimental to good core recovery than either of the other factors. USES FOR LARGE DIAMETER CORE BARRELS It is well known that the use of larger diameter bits and core barrels generally produce better cores, particularly when sampling soft or broken material. The use of larger and larger bit diameters and the insistence on better core recovery is well demonstrated by the change in practices of the various districts of the Corps of Engineers. Today NX core is the smallest diameter commonly permitted for investigational work and the more active districts are using coring bits up to 6 in. in diameter, as well as 36 and 40-in. calyx rigs. The latter size has proved to be just as economical because it provides more room for core removal and cleanup operations. The use of large diameter cores to replace the driving and jacking methods of obtaining soil samples is also increasing. The 5 7/8-in. Denison sampler, developed by H. L. Johnson to obtain samples from soft formations, is one example. The principal uses for bits larger than NX are: sampling soils and semi-consolidated rock; sampling decomposed rock or rock with soft seams; sampling concrete; obtaining samples for laboratory tests; drilling drainage holes, and other miscellaneous work. CORE DRILLING PRACTICES OF SEVERAL ENGINEER DISTRICTS Little Rock District The writer was employed in the Little Rock District from 1938 until 1942. Prior

Jan 1, 1947

By B. A. Stainton, John D. Gill

OUR combined economic activities have as their goal the maximum of individual well-being and national security. In this age of intense international competition the two objectives are closely related. For many decades, the maximum of well-being and ability to maintain national security have moved generally upward. The best single measure-perhaps the only adequate measure -of the level of the rising goal is the per capita real national income (national income corrected for price changes). For centuries before the industrial revolution the income of the world's population changed little from generation to generation. In our country prior to 1800 the growth of national income was hardly measurable from decade to decade. Since 1850, perhaps since the "industrial revolution," the growth of per capita real income has been increasing geometrically. Of major importance is the accelerative growth of the productive ability of our economy. Inadequate consideration of its implications is partly responsible for periodic delays in solving our princi-

Jan 1, 1946

By Nicholas J. Grant, A. W. Mullendore

Measurements of grain boundary sliding were made on polycrystal and bicrystal tensile creep specimens of Al-2 pct Mg at 500oand 700oF. Grain and pain boundary orientation factors were studied with respect to their effect on the magnitude and direction of grain boundary sliding. It was concluded that a large part of the observed sliding may be caused by the operation of slip crossing the grain boundaries. Supporting evidence for this model from other investigations is also given. GRAIN boundary sliding in metals during elevated temperature deformation has frequently been thought of as an independent mechanism with its own characteristic stress, temperature, and structure dependence. Further, it is common to regard the grain boundary as the weak link during creep deformation since: 1) the strength of apolycrystallinemetal, as meas-sured by creep rate or rupture life, decreases at\a more rapid rate when sliding comes into action, and 2) grain boundary sliding, as revealed by "boundary darkening" and fold formation is often the first visible deformation. On the other hand, more quantitative observations, in both polycrystals and bicrystals, have shown boundary deformation to be closely related to the over-all deformation of the specimen. The curve of grain boundary contribution to elongation vs time takes a shape similar to that of the total creep curve,',' and the apparent activation energy for sliding appears in most cases to have the same value as that for total creep.3 In order to reconcile these observations, one is left with these possibilities: 1) The grain boundary and grain deformation rates are both controlled by the same rate limiting processes. 2) The rate of sliding is limited by accommodation deformation in the grains. 3) Sliding is the consequence of grain deformation. 4) Grain deformation is dependent on prior grain boundary deformation. Alternatives 2) and 3) would view grain boundary sliding as occurring in series with another deformation process which could be rate controlling. McLean prefers item 3) as the sliding basis,4 where subgrain rotation results from dislocation accumulation in the substructure at the grain boundary. Crussard and Friedel's5 treatment of grain boundary migration considers that dislocations are forced into the grain boundary and are dissociated into dislocations with Burgers' vectors nearly parallel to the grain boundary. The movement of these partial grain boundary dislocations then produces the sliding. The results of this investigation have indicated alternative 3) to be the most appropriate and it is this aspect of grain boundary sliding which will be analyzed. EXPERIMENTAL PROCEDURE Three types of tensile creep tests were employed in this study: (I) A constant load test of one very coarsegrained polycrystalline specimen at 500° F, 3600 psi, 1 pct per/hr strain rate to examine the grain and grain boundary orientation factors in grain boundary sliding. (II) Constant strain rate tests of polycrystalline specimens at 510o and 715o F, 2 pct per/hr strain rate to determine the grain boundary contribution to elongation at very low total strains. (m) Constant strain rate tests of bicrystals of various grain and grain boundary orientations at 500°F, 2 pct per/hr strain rate to obtain further information on the orientation effects in grain boundary sliding. The material used in the tests was a high-purity Al-1'.92 mg alloy, kindly furnished by Alcoa. Its composition is given in Table I. The alloy is a solid solution at the test temperatures. The coarse grained polycrystalline specimen for test (I) was prepared by recrystallizingthe machined specimen, straining it about 1pct intension at room temperature and annealing at 900°F for 8hr. The constant strain rate specimens (11), with an 178 in. sq. by 1/2 in. long gage section, were cut from 1/8 in. thick sheet of cold rolled and annealed (8 hr at 1000oF) material. The latter specimens were supported in a special jig during the milling operations to avoid any bending, and the gage section was subsequently heavily electropolished to remove the cold-worked surface layer. The bicrystals (ID) were machined in the same

Jan 1, 1963

Jan 1, 1971

By Willard R. Jillson

Within the last ten years Kentucky has become celebrated for its low-sulfur bituminous coals. Prior to this time, many investigators had discnvered the abundance of this coal but the fact was unknown to the general public until the last extension of Kentucky's mountain railroads' was completed. The coals of. Kentucky are, broadly, separated into two geographic units—the eastern and the western coal fields. On a basis of their sulfur content these coal fields fall into three units, which are indicated on the accompanying map, by numbers, 1, 2, and 3. The area marked 1, the very southeastern part of the state, shows the lowest sulfur, all coals being averaged. In this field the maximum is 1.04 per cent. and the minimum as low as 0.68 per cent.—both averages and not individual analyses, which would of course show much greater variation. Included in this group are the following counties: Lawrence, 0.87 per cent.; Martin, 0.75 per cent.; Johnson, 0.73 per cent.; Magoffin, 0.87 per cent.; Floyd, 0.88 per cent.; Pike, 0.68 per cent.; Knott, 1.04 per cent.; Perry, 0.77 per cent.; Letcher, 0.80 per cent.; Leslie, 0.70 per cent.; Harlan, 0.79 per cent.; Knox, 0.86 per cent.; and Bell, 0.92 per cent. The total average sulfur content for these thirteen counties is 0.82 per cent. Bordering the restricted low-sulfur field of eastern Kentucky is the No. 2 belt (slightly darker), 'which is commonly known as the western border of the eastern coal field. Here the maximum sulfur is 2.91 per cent. and the minimum 1.05 per cent. Again these are averages and not individual analyses. The counties in this group are: Greenup, 2.60 per • cent.; Boyd, 1.67 per cent.; Carter, 1.07 per cent.; Morgan, 1.40 per cent.; Wolfe, 1.83 per cent.; Lee, 2.93 per cent.; Breathitt, 1.85 per cent.; Owsley, 1.09 per cent.; Jackson, 1.06 per cent.; Rockcastle, 2.30 per cent.; Clay, 1.09 per cent.; Laurel, 1.08 per cent.; Pulaski, 2.24 per cent.; Whitley, 1.05 per cent.; McCreary, 1.50 per cent.; and Wayne. The sulfur percentage average for this area including fifteen important counties is 1.65 per cent. In the western Kentucky field, the great increase in the percentage of sulfur is at once apparent. Ohio County with 3.78 per cent. is the highest and Hancock with 2.87 per cent. is the lowest. The percentages by counties is as follows: Hancock, 2.87 per cent.; Henderson, 3.22 per cent.; McLean, 3.27 per cent.; Muhlenberg, 3.31 per cent.; Hopkins,

Jan 1, 1920

By Howard I. Young

WHEN so many statements are being made relative to the requirements of zinc metal, it is difficult for some of us who are acquainted with the industry to visualize how it is possible to step up production so as to supply some of the fantastic requirement figures that are published from time to time. I shall attempt to approach this subject from the standpoint of existing conditions which affect production, also keeping in mind the price ceiling under which the industry operates. Total production of primary and secondary zinc in the United States for 1941 will be about 878,000 tons, to which should be added about 36,000 tons of Mexican slab zinc available for consumption or export from the United States, giving a total available of 914,000 tons. Production of slab zinc of all grades in 1942 should be 953,000 tons. Adding the available Mexican supply should bring the total to 989,000 tons.

Jan 1, 1942

By C. E. Ells, A. Sawatzky

The effect of neutron irradiation on tensile properties of the Zr-2.5 wt pet Nb-0.5 wt pet Cu alloy has been evaluated for integrated neutron fluxes up to 3 x 1020 n per sq cm (E > 1 Mev). Specimen temperature during irradiation was normally 300°C. The material was studied both in annealed and in quenched and aged conditions. When the alloy (fab-ricatedfrom sponge zirconium) is quenched from a temperature =40°C below the a + ß/ß transformation and aged 6 hr at 535oC, neutron irradiation up to the maximum studied has little effect 071 reduction in area, although there is a drop in uniform elongation and the yield strength is increased by = 25 pct. Conversely, irradiation of the alloy in an annealed condition can result in much greater changes in properties, with yield-strength increases of up to 200 pet. The dose dependence of irradiation hardening obeys the saturation equntion proposed by Makin and Minter to explain hardening in copper and nickel: Act = C[1 - exp(-Døt)/1/2 A rnodel is proposed to explain the effect of niobium content and metallurgical condition on irradiatiotz behavior. THE Zr-Nb alloys form a class of material susceptible to marked strengthening by quench and age heat treatment. With niobium concentrations as low as 2.5 wt pet, strengths can be developed which are double those of annealed zircaloy-2.1 Since the neutron-capture cross section of the Zr-2.5 wt pet Nb alloy is nearly identical to that of Zircaloy-2, significant gains in power-reactor neutron economy could be obtained by replacing stressed in-reactor components of Zircaloy-2 with the heat-treated Zr-Nb alloy. When the solution heat-treatment temperature is in the high (a + ß) phase, then the tensile properties of the quenched (and aged at 500°C) material have been shown to be relatively insensitive to neutron irradiation.1-3 Addition of small quantities of copper to the binary Zr-2.5 wt pet Nb alloy gives a useful reduction to the corrosion rate in air and carbon di- oxide,&apos; and a ternary alloy of composition Zr-2.5 wt pet Nb-0.5 wt pet Cu was chosen for one component in the Douglas Point Reactor. This application utilizes both the corrosion resistance to a moist air-carbon dioxide environment and the strength developed by a quench and age heat treatment. By suitable choice of solution heat treatment and aging temperatures, tensile properties of the ternary alloy can be made nearly identical to those considered as optimum for the binary alloy. One effect of the copper addition, however, is to give marked changes in the aging kinetics of the alloy.&apos; For this reason, it appeared that neutron irradiation might promote overaging in the ternary alloy, particularly at the elevated service temperature (=300°C). This paper describes the effect of neutron irradiation on the tensile behavior of the Zr-2.5 wt pet Nb-0.5 wt pet Cu alloy in several metallurgical conditions pertinent to its use as a reactor material. The metallurgical conditions included those for which aging occurs in the unirradiated material, and fully annealed conditions for which a higher degree of thermal stability could be expected. 1) EXPERIMENTAL Two batches of alloy were used, both made from sponge zirconium. The fabricator&apos;s analysis of principle constituents showed no significant difference between the two batches, Table I. The rod material was rolled to 1.5 in. diam, and then swaged to final sizes of 0.5 to 0.375 in. diam at nominal temperatures of 785" and 625°C for the AM and AS batches, respectively. Subsequent hydrogen analyses at CRNL confirmed that the hydrogen concentration of the as-received rod was indeed <20 ppm. However, it was found that the (a + ß)/ß transus for the AM material was approximately 25°C lower than that of the AS material, indicating rather more difference in oxygen concentration than given in Table I. Except for a small difference in yield-point behavior, the tensile prop-

Jan 1, 1965

By C. S. Matthews, P. Hazebroek, H. Rainbow

It ha been suggested that lormation fractures created by well stimulation treatments will adversely affect sweep-out efficrency in injection operations. Fluid-flow model studies involving vertical fractures of various lengths and fluid systems of various mobility ratios have been carried out to study this subject. In addition, limited data have been obtained on one model containing a horizontal fracture. It was found that relatively long and highly conductive fractures (not generally obtained fracturing operations) were required to affect the sweep-out efficiency substantially. In a given case in the field an approximate distinction can be made between the presence of long conductive fractures and shorter or less conductive ones. This is done with pressure build-up analyses along with data on the relationship of fracture length and conductivity to well productivity. This type analysis shows that usually the fractures induced are either short or of limited conductivity and therefore do not damage sweep-out efficiency. INTRODUCTION Improved well productivity and in-jectivity can frequently be exploited in injection operations. Higher total throughput can yield improved economics. On occasion, the achievement of an increased productivity or injectivity in specific wells can bring about a more uniform sweep of the reservoir. Higher rates can be exploited particularly in water floods of "depleted" reservoirs where a rapid "fill-up" is desired and where low pressures contribute to low well productivity. The creation of fractures local to the wellbore is an excellent means for achieving these objectives. Even though fracturing has been employed in some floods with success,1"3 there still seems to be some reluctance to employ this tool for fear of undue damage to the flood pattern and ultimate recovery. We therefore need to examine the influence which fractures of varying length may have on flood performance and then determine the length of fractures which obtain in the field with conventional fracture treatments. A substantial influence of fractures on the recovery obtained at breakthrough of the injected fluid has been presented by Crawford and Collins for equal fluid mobilities for the line-drive pattern.4,5 In addition, the influence which a fracture has on the production performance after breakthrough and on the ultimate recovery warrants consideration in reaching a conclusion concerning the use of induced fractures in flooding operations. This report presents this type of data for the five-spot injection pattern for several fluid mobilities. In arriving at some conclusion concerning the fracture lengths obtained in field operations we must examine the performance characteristic most affected by the fracture. This is the change in the flow system as reflected in the change in productivity and pressure build-up behavior. A study of these changes is also presented in this report. RESERVOIR ANALOGS The X-ray shadowgraph technique, employing miscible displacement in porous models, has been used in the study of the influence of fractures on pattern sweep-out efficiency. The X-ray shadowgraph procedure is described in detail in an earlier report8. Fractures were represented by leaving the proper portion of the model surface exposed to either injection or production. This assumes the fracture resistance to be negligible compared to that of the formation. Actually the flow resistance in propped fractures obtained in the field is sometimes not negligible so that the results with this model indicate the maximum influence of the fracture. Two types of models were necessary to represent vertical fractures in a five-spot flood. These pattern elements are illustrated in Fig. 1. In studying the influence of the horizontal fracture, only one well spacing length to thickness ratio of 50 was used. The pool unit of a Carter Electric Analyzer was used in studying the influence of fractures on productivity and build-up behavior. The square drainage system of a well was represented by a network of 576 elements of equal volume and resistance. One-fourth of this drainage area was studied as a model unit using a network of 144 condensers and resistors. Vertical fractures were represented by a shunt directed from the well perpendicular to the drainage boundary. Horizontal fractures were represented by a circular shunt. Resistance of a shunt was varied in representing different conductivities for the fractures. FRACTURE DIRECTION AND LENGTH The direction at which a vertical fracture extends into the formation and its length and conductivity influence the sweep behavior. The two

By C. S. Giggins, F. S. Pettit

The oxidation of Ni-Cr alloys in 0.1 atm of oxygen has been studied at temperatures between 800" and 1200°C. For alloys with 30 wt pct or more Cr, continuous layers of Cr2O3 are formed during oxidation. In the case of alloys with chromium concentrations between approximately 5 to 30 wt pct, external scales of Cr203 are formed over grain boundaries whereas internal precipitates of Cr2O3 and external layers of NiO are formed at other areas on the alloy surface. When such conditions are present on the alloy surface, chromium diffuses laterally from those areas covered with a continuous layer of Cr2O3 to areas where a Cr2O3 sub scale exists and it is possible for the sub-scale zone to become separated from the alloy by a continuous layer of Cr2O3. Whether such a state will be attained depends upon the initial grain size of the alloy and the oxidation time. When the concentration of chromium in the alloy is less than 5 pct, Cr2O3 is formed internally both at grain boundaries and within the interior of grains and the alloy is covered with an external layer of NiO. MECHANISMS which describe the growth of oxide scales on nickel-base superalloys are complex and the effects produced by the various elements in these alloys on the oxidation behavior of superalloys are not clearly understood. In order to determine the influence of the different elements on the oxidation behavior of superalloys, it is first necessary to examine the oxidation properties of binary nickel-base systems which contain the principal elements present in the superalloys and then progressively more complex systems until compositions typical of the superalloys are attained. Chromium is present in virtually all nickel-base superalloys and the purpose of the present studies was to examine the selective oxidation of chromium in Ni-Cr alloys. The oxidation characteristics of Ni-Cr alloys have been extensively studied1-" to date principally as a result of the high oxidation resistance exhibited by some of these alloys. Ni-20Cr* has long been known *All compositions are given as wcight percent unless specified otherwise. to be oxidation resistant and is commonly used as resistance heating elements for service temperatures up to 1100°C. This alloy cannot be used for extended periods of time at higher temperatures because of the apparent reaction of the external scale with oxygen to form gaseous CrO3. In spite of the considerable work cited above some important aspects of Ni-Cr oxidation still remain unresolved. Virtually all of the previous studies agree that small additions of chromium to nickel, e.g., <10 wt pct Cr, result in increased oxidation rates as compared to that of pure nickel, whereas larger additions, e.g., 20 to 30 wt pct Cr, form alloys with substantially lower oxidation rates. The controversial aspects of the oxidation mechanisms for these alloys that still remain unresolved are as follows: 1) A description of the oxidation mechanism for the low chromium alloys. 2) A description of the oxidation mechanism for the high chromium alloys, particularly with respect to the composition of the external scale which results in the lower oxidation rates. 3) The specific alloy compositions at which the oxidation mechanism changes from that obtained for low chromium contents to that of the high chromium alloys and the reason for this transition. EXPERIMENTAL The Ni-Cr alloys listed in Table I were prepared from high purity metals by nonconsumably arc melting and casting as buttons. These alloys were then given a preliminary annealing treatment in argon at 815°C for 100 hr to promote homogeneity. Each button was cut into 0.250 in. thick sections that were subsequently cold-rolled to 0.050 in. thicknesses and annealed in argon at 815°C for 48 hr to provide a twinned, equi-axed grain structure. The grain size for these alloys was not uniform and the limits, within which the average grain size lies, are given in Table I for the single-phase alloys. All the alloys were single phase with the exception of the Ni4OCr alloy in agreement with the Ni-Cr phase diagram.&apos;&apos; Rectangular specimens were cut from the sheet to provide surface areas of approximately 2.5 sq cm. Exact areas were determined with a micrometer after surface preparation was completed. All of the specimens except the Ni-40Cr alloy and pure chromium were polished through 600-grit Sic abrasive paper, ultrasonically agitated in ethylene trichloride, rinsed with ethyl alcohol, and electro-polished. The specimens were electropolished in a 10 vol pct H2SO4 (conc), 6 vol pct lactic acid, methyl alcohol solution at 70" to 80°C for 2 min at a current density of 0.8 to 1.2 amp per sq cm. This electro-polishing procedure did not produce acceptable surfaces on the Ni-40Cr alloy nor on pure chromium and the oxidation properties of these materials were obtained for specimens polished through 600-grit Sic

Jan 1, 1970

By S. A. Mersol, C. T. Lynch, F. W. Vahldiek

The room-temperature microhardness of as-grown and annealed MoaC single crystals was measured on the (0001), {2110), and1012) planes using Knoop and Vickevs indenters at loads ranging front 25 to 1000 g. The orientatimz dependence of hardness with respect to crystal axes was also studied. The average random hardness of as-grown crystals was determined to be 1520 kg per sq nm. Annealing to 2000°C decreased. the average hardness by 150 units. An increase in hardness after annealing at 2200 ;C was noted. Optical and electron microscopy revealed slip and twin traces on all planes studied, as produced by mi-cvohavdness indentations. Basal (0001)(2i10) slip was determined to be the primary slip system and was substantiated by electron transmission microscopy. A secondary {1010)(2110) slip was produced by mi-crohardness indentations. The lattev also produced twinning- of the {10i2)[0001] type, as proven by electron diffraction. Electrical resistivity and elastic-modulus anisotropy were found and correlated with hardness anisotropy and Mo2C crystal structure. Elastic-modulus values were obtained by microhard-uess and ullrasonic methods. Bonding mechanism of Mo2C is discussed. ROOM-TEMPERATURE microhardness indentations are useful for studying hardness anisotropy, slip, and twinning in brittle materials. Slip has previously been produced in this manner in and WS~~.~ Recently, the authors5 reported slip of the {10i0)(11~0) type produced by high pressure and microhardness indentations on hexagonal TiBz (c/a = 1.066) single and polycrystals. This slip system was also reported by French and ~homas&apos; and Taka-hashi and ~reise~ for hexagonal WC (c/a = 0.976) crystals. These results suggest that prismatic rather than basal slip is favored in hexagonal nonmetallic materials having a c/a ratio considerably less than the ideal (1.633). Buerger precession and cylindrical X-ray rotation patterns were previously&apos; taken on cleaved sections of the Mo2C single crystals studied in this work. Th~y were found to be hexagonal MoaC with a. = 3.0233A, co = 4.7344A, and C/O = 1.5660. The latter ratio is close to that of the beryllium metal (c/a = 1.57), which slips primarily on the (0001) plane: but also slips on the (1010) planes.&apos;0 ~irconium" (c/u = 1.59) and titanium12 (c/o = 1.59) deform mainly by slip on nonbasal planes which contain a close-packed direction. This is due to the fact that for these two metals the initial resolved shear stress for slip on the (10i0) prismatic planes is lower than that on the (0001) plane. The prominence of basal rather than prismatic slip in metals of high c/o ratios is shown by cadmium (c/a = 1.89), zinc (c/a = 1.86), and magnesium (c/a = 1.62) which deform mainly by basal slip. However, in case of the latter, by stressing magnesium crystals in tension or compression parallel to the basal plane, slip on (10i0) planes can also be produced.13 Several hardness values for polycrystalline Mo2C are reported in the literature: Biickle &apos; and Samsonov&apos;~ give a value of 1800 and 1479 kg per sq mm, respectively, at a 100-g load; and Kieffer and Benesovsk~&apos;~ report a value of 1950 kg per sq mm at a 50-g load. ~ott&apos;~ reports a Vickers hardness value of 2000 kg per sq mm, with the load unspecified. A Rockwell A hardness value of RA = 88 has also been reported.&apos;&apos; In the present work, for comparison with single-crystal Mo2C hardness values, a Khnloo value of 1600 It 150 kg per sq mm was found on 99.6 pct pure and 99 pct dense hot-pressed Mo2C. This work was undertaken partly to explain the considerable differences in hardness values reported for polycrystalline Mo2C. EXPERIMENTAL The Mo2C single crystals investigated were prepared by a Verneuil-type process using an electric arc by the Linde Co. of the Union Carbide Corp.lg The largest specimens grown were boules 7 mm in diam by 40 mm in length. The crystals had an average density of 9.04 g per cu cm, with a Mo + C content of 99.8 wt pct. The major impurities were: 100 ppm each Na, Zr, and Ca; 85 ppm 0, 55 ppm Fe, and 10 ppm each Cr and Ta. The crystals were found to be carbon-poor, the average carbon content being 5.73 wt pct (stoichiometric value is 5.89 pct). The molybdenum content was found to be 94.08 pct, which is nearly stoichiometric. Electron-microprobe traverses of selected specimens were done with a Phillips-AMR microanalyzer. Thin-film and carbon replicas were used to prepare electron micrographs. This work was done with a JEM-6A electron microscope. Prior to optical and electron-optical studies, specimens were mounted in Lucite and polished on a vibratory polisher using diamond-paste grades ranging from 9-1 p and Linde A powder for up to 48 hr. Dilute nitric acid was used for thin-section polishing and chemical etching for 1-15 min. Electrical-resistivity measurements at room temperature were taken with a Rubicon bridge, using gold contacts. For hardness measurements, a Tukon Microhardness Tester Type FB with Knoop and Vickers indenters was used. Measurements were taken at loads ranging from 25 to 1000 g; however, the 100-g load was chosen as the standard load. All measurements were taken at room temperature. Indentations of cracking classes 1 and 2 only were considered for hardness determinations.20)21 (There are six cracking classes, ranging from "class 1" for a perfect inden-

Jan 1, 1967

By M. E. Wadsworth, K. C. Bowles, H. E. Flanders, R. M. Nadkarni, C. E. Jelden

The kinetics of precipitation of copper on iron of various purity were carried out under controlled conditions. The rate of reduction has been correlated with such parameters as copper and hydrogen ion concentration, geometric factors, flow rate, and temperature. The character of the precipitated copper as a function of flow conditions and rate of PreciPitation has been observed under a variety of conditions. ThE precipitation of copper in solution by cementation on a more electropositive metal has been known for many years. Basile valentine&apos; who wrote Currus Triumphalis Antimonii about 1500, refers to this method for extraction of copper. Paracelsus the Great2 who was born about 1493 cites the use of iron to prepare Venus (copper) by the "rustics of Hungary" in the "Book Concerning the Tincture of the Philosophers". Agricola3 in his work on minerals (1546) tells of a peculiar water which is drawn from a shaft near Schmölnitz in Hungary, that erodes iron and turns it into copper. In 1670, a concession is recorded4 as having been granted for the recovery of copper from the mine waters at Rio Tinto in Spain, presumably by precipitation with iron. Much has been published in recent literature on the recovery of copper by cementation, the majority of the articles being on plant practice.5-24 The rest include articles on investigation of the variables involved25-28 and a review of hydrometallurgical copper extraction methods." This literature has established: a) The three principal reactions in the cementation of copper are Cu + Fe — Fe+4 +Cu [ 11 One pound of copper is precipitated by 0.88 lb of iron stoichiometrically. In actual practice about 1.5 to 2.5 lb of iron are consumed. 2Fe+3 + Fe — 3Fe+2 [21 Fe +2H&apos;-Fe+2 + H2 [3] Reactions [2] and [3] are responsible for the consumption of excess iron. Wartman and Roberson&apos;28 have established that Reactions [ I] and [2] are concurrent and much faster than Reaction [3]. b) Acidity control is important in the control of hydrolysis and the excessive consumption of iron. he commercial workable range is approximately from pH = 1.8 to 3." c) Iron consumption is closely related to the amount of ferric iron in solution. Jacobi" reports that, by leaving the pregnant mine waters in contact wi th lump pyrrhotite (Fe7S8) for 3 hr, all the iron was reduced to the bivalent condition and scrap iron consumption was cut to 1.25 lb scrap per pound of copper precipitated. He also reported that SO2 has been used successfully to reduce ferric iron to the ferrous state. d) The ideal precipitant is one that offers a large exposed area and is relatively free of rust. e) High velocities and agitation show a beneficial effect upon the rate of precipitation, as it tends to displace the layer of barren solution adjacent to the iron and also dislodges hydrogen bubbles and precipitated copper to expose new surfaces. Little work, however, has been published on the reaction kinetics of copper precipitation on iron. Cent-nerszwer and Heller20 investigated the precipitation of metallic cations in solutions on zinc plates. They found the cementation reaction to be a first-order reaction. The rate constant was independent of stirring for high stirring rates and they concluded that the rate is governed by a diffusional process at low stirring speeds and by a "chemical" process at higher stirring speeds where the rate reaches a constant value. This conclusion has been challenged by King and Burger30 who could not find any region where the rate was independent of the stirring speed, although the rate constant they had obtained for high stirring speed was greater than the maximum value of the rate constant reported by Centnerszwer and Heller (by a factor of six). King and Burger, therefore, concluded that the rate of displacement of copper was controlled only by diffusion. Cementation of various cations on zinc has been summarized by Engfelder.31 APPARATUS A three-necked distillation flask of 2 000-mm capacity was used as a reaction vessel. A pipet of 10-mm capacity was introduced through one of- the side necks, the sample of sheet iron, mounted in a rigid sample holder, through the other, the stirrer being in the middle as shown in Fig. 1. The whole assembly was immersed in a constant-temperature bath. The stirrer was always placed at the same depth in the solution. EXPERIMENTAL PROCEDURE Reagent-grade cupric sulfate (J. T. Baker Chemical Co., N.J.) was used to make up a stock solution containing 10 g of copper per liter which was then diluted to various concentrations as required. Experimental data were obtained by measuring the amount of copper and iron ions in solution at successive time intervals. The initial volume of the solution was always 2000 ml, 10-ml aliquots being removed each time for chemical analysis. Because the total volume change of the solution was less than 10 pct, no correction was used for solution volume change. Nitrogen was bubbled through the solution before and

Jan 1, 1968

By A. R. Kinkel

THE Shasta copper-zinc district of northern California lies in the foothills of the Klamath Mountains at the northern end of the Sacramento Valley. It contains two main areas of base-metal ore deposits, the East Shasta and West Shasta districts shown in Fig. 1. The East Shasta includes the area from the Afterthought mine, near the settlement of Ingot on U. S. highway 299 East, to the Bully Hill mine, on the north side of the Pit River, 9 miles to the northwest. The West Shasta, a well-defined northeast-trending district about 8 miles long and 2 miles wide, west of the Sacramento River, Fig. 2, is the western part of the ore-bearing area formerly known as the Shasta copper belt. Referred to in the older writings as a copper arc, this belt was thought to form a crescent extending entirely around the head of the Sacramento Valley, the convex side to the north. Recent studies by the U. S. Geological Survey in cooperation with the California State Division of Mines show that there are two districts, one at each end of the so-called copper arc, which are distinct in geologic structure and ore occurrences, and that there is only sporadic and unconnected copper mineralization between them. Ore deposits of the two districts are similar in mineralogy, that is, they are largely massive pyritic ores containing copper and zinc with minor amounts of gold and silver, but the structure and structural control of ore deposition are different. The ores of the East Shasta district are replacements of steeply dipping shear zones in Triassic rhyolite and shale, whereas those of the West Shasta district are replacements of gently dipping rhyolite of Middle Devonian age and are essentially flat-lying. Thus there is marked lateral control of orebodies by shear zones in the East Shasta district and equally marked vertical control of orebodies by the stratigraphy in the West Shasta district. Geologic Setting The Paleozoic rocks of the West Shasta district range in age from Middle Devonian (?) to Missis-sippian. The oldest formation exposed is the Copley greenstone, probably Middle Devonian. It is composed of volcanic flows, volcanic breccias, and tuffs, all of mafic composition, but contains minor amounts of shale and rhyolitic tuff. Largely submarine in origin, it rests upon a base of older marine sediments, as shown diagrammatically in Fig. 3. The lower part of the formation is made up principally of flows, many of which are ellipsoidal, and the upper part contains most of the pyroclastic material. The formation is at least 3700 ft thick. The Balaklala rhyolite overlying the Copley greenstone is made up of many rhyolitic flows and beds

Jan 1, 1956

By H. NORTON JOHNSON

THE oil industry in California during 1929 reached new heights and new depths in the discovery and development of the oil resources of the State. The discovery of new fields, and more especially the discovery and development of deeper prolific sands in known fields has, for the first time in its history, brought the potential production of completed wells within the State to over 1,000,000 bbl. oil per day. Constant improvement in equipment and technique has made possible economic development to depths unheard of but a few short years ago. Commercial production from a depth of over 4000 ft. was considered quite an accomplishment in 1923 when the Meyer sand at Santa Fe Springs was developed, and when later oil was successfully raised from this depth.

Jan 1, 1930

By W. Jolley

Decarburized iron and Fe-3.28 pct Ni alloys were impact and tension tested in the temperature range of ambient to 4°K. It was found that alloying with nickel improves the fracture properties of the ferrite matrix. The improvement in toughness of iron alloyed with nickel is attributed to the effect of the nickel addition on the temperature and strain rate dependence of the yield stress as well as on slip behavior. The Fe-Ni alloy exhibits wavy slip when strained at temperatures down to at least 50°K. This behavior contrasts with that of the unalloyed iron where a change It is a generally accepted fact that of the common alloying elements of steel only nickel and manganese improve both the room-temperature yield strength and the notch impact properties. It has been argued for a number of years that manganese refines the ferrite grain size, the pearlite spacing, and the grain boundary carbides in medium- and low-carbon steels and thereby increases resistance to brittle fracture.&apos;&apos;&apos; This hypothesis recently was confirmed for a 0.04 pct C iron containing manganese, but at the same time from wavy to planar slip occurs at about 120°K. The observed lower temperature and strain rate dependence of the lower yield stress in the Fe-Ni alloy as compared to the unalloyed iron may be attributed to this difference in slip behavior. In contrast to suggestions published previously, transmission electron microscopy showed that the uniform dislocation distributions and the lack of dislocation tangles which are produced by low-temperature straining of bcc materials cannot be attributed to the absence of cross slip at these temperatures. no increase in notch toughness was observed in a decarburized Fe-Mn alloy.3 It thus appears that manganese only increases the toughness of Fe-Mn-C alloys by refining grain boundary carbides and has no toughening effect in carbon-free iron. On the other hand, the mechanism whereby nickel improves toughness has not been established. Hodge et a1.4 have clearly shown that a 3.28 pct Ni addition lowers the impact transition temperature of 0.02 pct C steel approximately 35°C when the grain size is maintained constant. Recently, Wullaert and Tetelman6 stated that nickel refined the grain boundary carbides of an Fe-C alloy and consequently increased the toughness. They also observed the previously reporteda-&apos;

Jan 1, 1969

By D. C. Jackling

I BESPEAK your indulgence for a brief expression of the views of a patriarch in the field of mineral industry technology relative to young men&apos;s problems in that sphere of education and endeavor. Wherever hereafter I employ the terms "technical education," "engineer," "technologist," or similar expressions, these are intended to be understood as relating to the broad field of the sciences and arts applicable to the mineral industries. First, the usefulness of technical education to either the possessor of it or those to whom its services may be made available industrially depends primarily upon the quality of the education and the capabilities of the educated to put his talents to effective and constructive employment in his chosen field of applied science.

Jan 1, 1940

By David T. Day

IN 1897 I published a proposed explanation t for the variation in color and specific gravity of Pennsylvania oils. A resume of this subject was also presented at the First International Petroleum Congress, in Paris, in 1900. Since that time much experimental work bearing upon this explanation has been carried on by myself, in the United States Geological Survey, and under my direction, by Dr. J. Elliott Gilpin, Marshall P. Cram, and 0. E. Bransky, at the Johns Hopkins University. The experimental results thus accumulated seem to throw considerable additional light upon the variations in color and specific gravity of petroleum, as found in different parts of the world, and also upon the variations in chemical composition. Therefore, it seems as if a, summary of the evidence thus obtained might be of value to those members of the Institute who are interested in the examination of oil-fields. The summary is here presented for that purpose. The phenomenon has often been observed in many oil-fields that oils of different color, specific gravity, and chemical composition may be found within short distances of each other. A conspicuous example of this is the occurrence at Jennings, Welsh, and Anse la Butte, La., of petroleum chemically somewhat similar to Russian petroleum; that is, characterized by the presence of naphthenes. Another characteristic is the presence of considerable percentages of asphaltic compounds, sufficient in quantity to disguise the presence of solid paraffin wax, and perhaps also to render that paraffin wax more soluble * Published by permission of the Director of the United States Geological Survey. 1 Proceedings of the American Philosophical Society of Philadelphia, vol. xxxvi., No. 154, pp. 112 to 115 (January, 1897).

Jun 1, 1910

By Joseph Lindmayer, Karl M. Busen

If silicon is in contact with silicon oxide, a heterojunction is formed which induces an inversion layer ("channel"). Influences of impurities and structural parameters on the channel are discussed. There seems to be no relation between surface damage in silicon and the channel. Phosphorz~s doping of the silicon oxide has no pronounced effect on the channel. Channels which were well above the range predicted by the heterojunction model were related to the action of H* at the silicon/silicon oxide interface. Channels which were well below tlze range predicted by the heterojunc-tion model were related to a transition region in the oxide adjacent to the interface. In support of the assumed transition region and the H+ are the ex-periments described on the paper. Furthermore, the concept of metastable OH groups in silzca, known from other publications, has been used to explain certain channel characteristics by the formation and the accommodation of hydrogen in the silicon oxide. THE electrical characteristics of a semiconductor device in many cases are influenced by the conditions of its surface. Because these conditions often are changing with temperature, time, ambient, or other parameters, numerous attempts have been undertaken to stabilize them by suitable processes. Several years ago Atallal studied the silicon/silicon dioxide interface and since then increasing attention has been given to the silicon dioxide as a means to stabilize silicon surfaces. This led to the evolution of the planar silicon devices where oxide layers are used to protect places at which the junctions are intersecting the surface. The formation of the oxide layers on silicon can be carried out by a variety of processes: high-temperature thermal oxidation (exposing the silicon surface to oxidizing agents such as 02, HzO, COz), evaporation of SiOz, or anodic oxidation of silicon. Originally the oxides were considered able to "passivate" the silicon surface and it was understood that they 1) protected the surface against any influence from the ambient and 2) stabilized surface conditions which were necessary for proper device performance. It soon was realized that the second quality was not always obtainable: Atalla and Tannenbaum showed that, in the process of forming a layer on doped silicon by thermal oxida- tion, electrically active impurities in the silicon near the interface are redistributed, thus giving rise eventually to the formation of unwanted charge distributions. The degradation of planar junctions during reoxidation of silicon was observed by Barson et a. Surface studies with silicon planar junction structures indicated that the breakdown voltage depended on the kind of procedure which was applied during or after oxidation.*" Yamin and worthinge report on charge storage and dielectric properties of SiOz films at elevated temperatures. Another influential parameter on the silicon surface is discussed by Lindmayer and usen,&apos; namely the appearance of a surface potential on silicon as a consequence of the heterojunction formed by the silicon/silicon oxide interface. In the present paper the influence of impurities and structural parameters in silicon oxide in connection with the heterojunction is a particular object of our investigations. I) EXPERIMENTAL The material used was 10 ohm-cm p-type silicon slices with either damaged surfaces (mechanically lapped or polished) or damage-free surfaces (chemically polished). The majority of the slices were oxidized for 1 hr and 20 min at 1250°C in a steam + oxygen atmosphere generated by passing O2 through HzO at 90°C (wet oxygen). This led to oxide layers of about 9000 A. On some slices oxide layers were grown in pure oxygen (dry oxygen). By a photoresist process a set of 20 by 200 mil windows was then etched out from the oxide layer. The pattern of the windows is shown in Fig. 1. In a subsequent process n-type pockets with surface concentrations between 2 x 10" and 5 x 10" cm"3 were formed by phosphorus diffusion. This allowed ohmic contacts between the silicon surface and tungsten probes which for electrical measurements were placed into two adjoining windows and

Jan 1, 1965