One of the best known of the early mining districts of Nevada was that at Eureka, where gold was first produced in 1864. While the most productive period for the district was during the early 1900s, production was maintained until World War II. During this time it is said that the Eureka district produced as much as $200 million from over 3,200 km (2,000 miles) of tunnels and workings. The Windfall Mine was discovered in 1902; and a 100 ton cyanide plant was operated there during the periods 1907 to 1912 and 1932 to 1940. Since 1974, however, Windfall Venture has been operating a unique heap leaching facility on the site of the old Windfall Mine. Gold at the Windfall occurs primarily in the Cambrian Hamburg dolomite which has been "sanded" and in which the original cementing material has been destroyed. The gold is micron sized and is accompanied by anomalous amounts of arsenic and mercury; however, the ore is low in base metals which distinguishes it from the typical Eureka district ores. Mining the ore causes it to break down into very fine sizes, approximately 50% minus 150 microns (100 mesh). Conventional heap leaching by spraying proved to be impossible; and extensive test work on alternate methods, aided by the United States Bureau of Mines, was conducted using 9 m (30 ft) high columns and then large tonnage heaps. The leaching procedure adopted was to build 10.6 m (35 ft) high heaps on a 50 mm (2 in.) asphalt pad covered with a layer of gravel for drainage assisted by perforated pipe drains and gravel-packed sumps. A berm is constructed around the top of each pad and cyanide solution is allowed to “pond” on top of the heap. The resulting percolation is at the rate of 24 liters per sq m per hr (0.6 gal per sq ft per hr), a figure about 2.4 times the average used in other heap leaching operations. The dolomite furnishes its own protective alkalinity and no lime or caustic is used in the solution which contains 0.4 kg per mt (0.8 lb per st) of NaCN. Pregnant solution from the heaps averages about 0.7 g Au per mt (0.02 oz per st) with a cyanide content of about 0. 2 kg per mt (0.4 lb per st) and a pH of plus 9. Addition of NaCN brings the pH of the leach solution up to 11 to 12. Carbon adsorption of the gold was originally done in six enclosed columns mounted in a trailer but five conventional columns have been substituted as the size of the operations has increased. Carbon stripping is with hot caustic, cyanide and 10% ethanol solution. The

Jan 1, 1981

By D. B. Hobbs, L. W. Kempf, R. S. Archer

SILICON is one of the most important elements in the metallurgy of aluminum. It is always present in small amounts in the ordinary grades of "pure" aluminum, and hence in all alloys made therefrom. Within the last few years binary alloys containing up to 13 per cent. of silicon have come into extensive use for castings. Silicon is also added, beyond the amount present as an impurity, in alloys containing one or more other elements such as copper, manganese, magnesium and nickel. The binary aluminum-silicon alloys are not yet heat treated to any extent in commercial practice, although, as will be shown, their properties are affected to a very considerable degree by heat treatment. There are other aluminum alloys that develop higher strength, but the special characteristics of the silicon alloys may well lead to the application of heat-treating processes on a commercial scale. The role of silicon in the heat treatment of aluminum alloys is more important than would be indicated by consideration of the binary alloys alone, because many of the alloys that are heat treated in regular commercial practice contain some silicon in addition to that derived from the aluminum ingot as an impurity. Among these may be mentioned the heat-treated 195 alloy castings, and the wrought alloys 25S, Special 17S and 51S of the Aluminum Co. of America, and the German wrought alloy, Lautal. It is the purpose of this paper to present the results of experimental work and the conclusions derived therefrom regarding the heat treatment of the binary aluminum-silicon alloys. The products heat treated included forgings, chill castings and both "normal" and "modified" sand castings. REVIEW OF LITERATURE The literature on the heat treatment of aluminum-silicon alloys is not very extensive. The following review gives the principal references of which the authors are aware, in which appreciable information may be found.

Jan 1, 1928

By Charles Will Wright

The application of the camera as an adjunct to topographic mapping began practically with its invention, and it has been employed with varying success since that time. With the exception of the camera to be described, the plate-camera has been universally used in this work, thus giving a projection of the area photographed on a flat surface. From such projections or photographs, by the rules of geometry and of perspective, points defining topographic features and seen from at least two camera-stations may be projected upon a ground-plane—the map.' In 1904 I employed the plate-camera for this purpose in Alaska, but found that the labor necessary to plot the maps, even in a general way, was long and tedious. In 1905 a small Eastman panoramic camera was fitted with spirit-levels, a sight-alidade and a transparent scale, introduced inside the camera to register the degree-points in the sky-line of the film-negative ; also, arrows to indicate the horizon-line. This was, on the whole, successful; but the details in the topography were not brought out in the views with sufficient clearness, aid the photographs were too small. These difficulties were overcome by obtaining a larger and more carefully constructed instrument, which was satisfactorily employed in the field during the year 1906. A panoramic view is made up of an integral number of perspective views upon flat surfaces, and logically is the most accurate and direct means to obtain an impression of a field of * Published by permission of the Director of the U. S. Geological Survey. Stanley, H. M. Photographic and Co-ordinate Surveying, Bans., xx., 740 to 766 (1891). Also, Flemer, J. ,4. Phototopographic Methods and Instruments, Report U. 8. Coast and Geodetic Survey, pt. 2, app. 10, pp. 619 to 735 (1897).

Jan 1, 1908

By William H. Bassett, C. J. Snyder

Cable sheaths made from common lead have been used to protect underground cables since the beginning of the power-cable industry. Only within the last few years, however, has a systematic study of the production methods and of the causes of failures in cable sheathing been undertaken. Recent increases in the use and demands for service made upon power cables have emphasized the importance of high-quality cable sheaths. It was customary for the users to attribute the cause for their sheath failures to the lack of purity of the lead, but this contention has not been borne out by field and laboratory inspection of the sheaths. During the past two years the writers have had an opportunity to examine various types of sheaths that were removed from power cables after failure. These samples were obtained from various parts of the country and represent, it is supposed, the production of the principal cable manufacturers. Aside from corrosion, the common field difficulties can be classified either as mechanical or structural, as outlined below, and when structural irregularities are found they can all be attributed to manufacturing causes and in no way reflect the purity of the lead. Clasxification of Cable Sheath Failures Other Than Corrosive Mechanical Irregularities A. Splits caused by excessive internal pressure B. Injuries such as nail holes, cuts, tsars, etc. C. Intercrystalline cracks caused by vibration Structural Irregularities A. Splits C. Voids in wall of sheath a. Caused by imperfect welds a. Blisters 13. Holes through sheath b. Laminations a. Caused by yellow oxide inclu- D. Questionable structures sions in sheath wall a. Prominent flow lines b. Blowouts by entrapped gases b. Large areas filled with suboxide during manufacture c. Scattered yellow oxide or dirt C. Caused by inclusions of dirt and

Jan 1, 1933

By AIME AIME

The Washoe plant, 1 in Anaconcla. Mont., together with the local street-railroad, ranches a. foundry and machine-shop a brick-plant and the Montana hotel, form a property under one management; to which should be added the mines in Butte owned by the company, from which part of the ore-supply of the plant comes. The Anaconda Copper Mining Co., controlled by the Amalgamated Copper Co., was reorganized under the laws of Montana in 1893. A map of the plant, showing the numerous departments and illustrating the details of tracks, pipe-lines, and charging-stations for compressed-air locomotives, is given in Fig. 1.

Jul 1, 1906

By W. W. Norton

The gradually increasing proportion of sulphide ores which lead smelters of to-day are called upon to handle has caused the roasting problem to become one of ever greater importance. Mines have increased in depth, methods of concentration have improved, competition in the purchase of ores has become more keen and it has been clear that new and modern methods of eliminating sulphur must receive a large share of attention. We may look back a score of years or so and recall the old hand roasters, some of which turned out a finely divided roasted product, and others fashioned with a "fuse-box" wherein the roasted ore was slagged. Then came mechanical furnaces of several types, the Bruckner cylinder, the Brown-O'Harra, the Ropp, and others, all designed to cut out the cumbersome hand labor of the old reverberatories. Roasting costs were thereupon reduced and tonnages stimulated to a gratifying extent. However, it seems to have been early recognized that this very feature of a greater amount of roasted sulphide ore as compared with oxide ore brought with it a train of difficulties at the blast furnaces. The mechanically roasted ore was fine physically, the blast furnaces were choked and the troubles of the smelterman were not at an end. Then the Huntington-Heberlein pot system of roasting appeared upon the scene, and later on the Dwight-Lloyd machines were invented, and inasmuch as both of these processes were designed not only to roast the ore but to agglomerate it as well, it was apparent that distinct steps in advance had been achieved. At the Murray plant, modern up-to-date roasting practice is fully exemplified and there are now in successful operation roasting furnaces or devices of several sorts: namely, Godfrey revolving-hearth furnaces, Wedge multiple-hearth mechanical roasters, Dwight-Lloyd sintering machines, and Huntington-Heberlein pots. Godfrey and Wedge furnaces will properly handle material high in sulphur, say ores with 25, 30, and 35 per cent. of that element; D. & L. machines and H. & H. pots will positively not treat efficiently ores or mixtures containing anywhere near the sulphur content mentioned, but are confined to charges containing in the neighborhood of 15 or 18 per cent. In passing, it may also be explained that, so far as the knowledge of the writer goes, Godfrey and Wedge furnaces do not economically eliminate sulphur to an extent

Jan 1, 1915

By N. A. D. Parlee, I. D. Shah

The solubilities of oxygen in liquid Ag-Au, Ag-Pt, and Ag-Pd alloys have been determined in the range of 940° to 1200°C at 1 atm pressure of oxygen using an improved Sieverts technique. The additions of gold (0 to 57 pct), platinum (0 to 27 pct), and palladium (0 to 22 pct) to liquid silver continuously decrease the solubility of oxygen in liquid silver. Activity coefficients and interaction coefficients of oxygen in these alloys and have been calculated. The interaction coefficientscan be described by the following equations: Approximate second-order interaction coefficients (pM have been calculated. The contribution of the product, pMxNM, to In yo only becomes significant at high alloy concentrations. RECENTLY several investigators1"3 have redeter-mined the solubility of oxygen in liquid silver. In general the recent findings1" for Po, = 1 atm are in good agreement with the equation:4 log %O = 695.4/T + 1.086 [1] It is established1, 2 that the solubility of oxygen follows Sieverts' law reasonably well, at least up to 1 atm partial pressure of oxygen. It should be noted that a very slight deviation from Sieverts' law has been reported by Lupis and Elliott.3 Only recently has the solubility of oxygen in Ag-X binary liquid systems received much attention, and only the Ag-Cu, Ag-Au, Ag-Pt, and Ag-Pd systems have been studied. Par lee, Sacris, and zoellners reported that the solubility of oxygen in liquid silver increases progressively with the small additions of copper (0 to 0.5 pct) up to the point where the copper oxide phase appears. Lupis and ~lliott~ have reported that the solubilities of oxygen in liquid silver decrease progressively with the additions of gold, platinum, and palladium. However, their investigation was limited to 0 to 5 pct of these alloying elements, a range too limited to satisfy the requirements of the research program of this laboratory, where the solubilities of oxygen in the range of 0 to 30 pct were required for the calculation of chemical diffusion coefficients of oxygen in these alloys. The present paper deals only with the solubilities of oxygen in these alloys while another paper will deal with the diffusion of oxygen in these alloys. EXPERIMENTAL METHOD A Sieverts technique was employed which involved an improved design of the reaction tube, Fig. 1, as described briefly in a previous communication.4 Liquid melts (70 to 100 g) were held in Norton Alun-dum crucibles. The induction furnace used had a maximum output of 2.5 kw with very fine control. This induction system had excellent stability and the final equilibrium temperatures measured by calibrated Pt-Pt, 10 pct Rh thermocouples are believed to be within ±2C. These thermocouples were checked against the melting point of pure gold wire, and the results agreed with standard tables (±l°C). Each run involved a careful sequence of operations. The sample was heated to and held at about 900°C in vacuum for 3 to 4 hr with the thermocouple in a retracted position. After melting, the melts were usually exposed to a small amount of oxygen (0.5 to 2.0 cu cm) and then degassed slowly for 1 to 2 min to remove any oxidizable volatile impurities such as carbon and sulfur as CO, CO2, SO2, and SO forth. Argon gas was then allowed to enter the system. The protection tube containing the thermocouple was then

Jan 1, 1969

By A. J. Boynton

THIS paper is not the result of recent research with regard to any particular feature of iron metallurgy, blast-furnace practice or mechanical engineering. It is rather a series of notes with regard to contemporaneous progress in blast-furnace construction and operation, together with some suggestions as to changes and improvements that seem to be desirable. On April 1, 1930, a committee of the Chicago District Blast Furnace and Coke Association presented to that association a rather ambitious study of blast-furnace equipment, together with recommendations for the design of construction of a complete blast-furnace unit for the production of 1000 tons of pig iron per day. This report represented the result of months of study by members of the committee, all of whom were actively engaged in operation or design of blast-furnace plants. It is natural, therefore, that comments on the present state of the art should take this 1000-tons furnace, as recommended by the Association, as a basis for comparison with corresponding features of construction or design. See Table 1. In looking through this report at the present time, the significant difference is in the nature of the gas-washing equipment that today would be specified. In other respects, the installation would remain generally very much as it was outlined in 1930. The change in furnace dimensions would be very slight and of no especial significance, except with respect to changes in stock-line diameter, of which more will be said hereafter. The high-efficiency stove as developed by various designers is thoroughly described within this report, and few changes have taken place since. Blowing equipment shows refinement and reflects the improvement in steam engineering. Hoisting and charging equipment and ladles for the conveyance of iron and slag remain, in general, as they were in 1930. In accordance with a general tendency

Jan 1, 1935

By John H. Bassarear, A. A. Dor

INTRODUCTION Primary grinding mills as defined in this paper, are autogenous or semi-autogenous rotating, tumbling mills having a coarse feed with a top size usually varying from 150 to 300 mm (6 to 12 inches). Most frequently, the feed to these mills is the product of primary crushing plants but in some cases run of mine ore is used as feed such as at Benguet, McDermitt, L-Bar Sohio, Bear Creek and others. The size of the largest lumps in the mill feed is principally determined by limits set by the mill feed trunnion diameter and by the type and size of conveying equipment used for handling and of bins and stockpiles used for storage. The use of primary mills in mineral processing plants has expanded very significantly in the last twenty years, and they have been successfully applied to the treatment of a wide variety of ores in both wet and dry grinding applications. In the present state of technological development for primary grinding mills, there is a wide choice of acceptable options with respect to type and size, grinding flowsheet and grinding media. The choice of the optimum combination which would result in the most satisfactory condition of operation, from the standpoint of both metallurgical results and costs, depends on the nature of the ore, the required characteristics of the grinding products and on various geographic and economic circumstances. The effects of such factors and considerations on the choice and sizing of primary grinding mills and flowsheets are reviewed and discussed in the following pages. PRIMARY MILLS SELECTION Inherent Characteristics of Primary Grinding Primary grinding is complex because it involves several comminution mechanisms which occur simultaneously and to some degree interfere with one another. These mechanisms of impact, attrition and abrasion have been described earlier. The relative importance of these three main grinding actions and their mutual balance resulting in a continuous uniform operation of the mill depend to a very large extent on the nature of the ore and its physical properties. Homogenous, single mineral ores will behave quite differently from heterogenous ores consisting of different minerals bound together along defined

Jan 1, 1982

By J. F. Radavich

Many heats of steel of low carbon value have been known to produce brittle pieces of steel. The brittleness is believed to be due to the impurities located within the grain boundaries. Such brittle steels have been examined with an optical microscope to ascertain the nature and the amount of the impurities present at the grain boundaries. Due to the relatively low resolving power of the optical microscope, the impurities are not visible in fine detail. The writer obtained some sheet steel and proceeded to determine the location of the impurities and to show the application of the electron microscope to the study of grain boundaries. One sample was known to be capable of becoming embrittled, whereas another sample was believed to be much less susceptible to embrittlement. Treatment of Specimens The specimens were embrittled by annealing above the A3 point under mildly oxidizing conditions. One piece of ingot iron could not withstand a 90" bend, whereas another piece of ingot iron was not affected and could withstand a 90" bend. The brittle piece was then annealed at a high temperature in a hydrogen atmosphere. The annealed ingot iron was termed cured and could withstand a 90" bend very easily. The three specimens examined will be designated as brittle, good. and cured in the discussion that follows. Procedure The sizes of the specimens were as follows: one piece of brittle ingot iron-3/8 by 35 in.; one piece of good ingot iron-96 by 1/8 in.; one piece of cured ingot iron-36 by 54 in. The specimens were too small to be polished by hand and therefore were mounted in bakelite. The polishing procedure was carried out in the conventional manner with the use of 1/0 through 3/0 papers, and the final polish was done with alumina on a billiard cloth. The specimens were then etched in a 4 pct solution of picral in alcohol, and then they were examined through an optical microscope. An area was chosen that showed distinct grain boundaries, and an effort was made to keep near this area when pulling the replicas REPLICA TECHNIQIJE The replica technique used in the preparation of the replicas for examination under the electron microscope is described in Electron Metallography.' It consists essentially of the following steps: 1. Obtaining a suitably etched specimen. 2. Applying a swab of ethylene di-chloride on the surface. 3. Applying a formvar solution on the surface. 4. Placing a screen on any desired spot. 5. Breathing on the fornivar layer. 6. Applying scotch tape on the screen and film. 7. Pulling the film and the screen up with the Scotch tape. 8. Separating the screen from the Scotch tape. This replica technique is very similar to the one described by Harker and Shaefer. However, with the added step, the percentage of replicas removed is very much higher regardless of the length of the time from the etching of the specimen to the actual pulling of the replica. The replicas were then shadow cast with manganese at a filament height to replica distance ratio of 1 1/2:7. This produced a very high contrast replica for use in the electron microscope. One of the dificulties encountered with this study was the restricted area of the specimen. The width of the specimens was the same as that of the 200 mesh nickel supporting screen. In order to increase the effective area, the screens were cut down as shown in Fig 1. The arrow indicates the direction in which the replica was pulled. This operation made it possible to obtain a large percentage of good replicas. Fig 3 shows an electron micrograph of a brittle piece of ingot iron and a grain boundary that was polished mechanically. The surface is very rough probably due to the incomplete removal of the flowed layer by the picral etchant. The grain boundary does show evidence of impurities. It was decided to electropolish the specimens to obtain a much smoother surface than the one obtained by mechanical polishing. ELECTROPOLISHING The specimens were cut in half to expose the metal on the back side. The exposed metal had sufficient area to make good electrical contact and electropolishing was carried out easily. The conditions for electropolishing were 0.9 amp, 35 volts, and 25 sec. in an electrolyte composed of 850 cc of ethyl alcohol, 100 cc distilled water, and 50 cc of perchloric acid. The polished specimens were then etched in the 4 pct picral solution for a shorter time than was necessary for

Jan 1, 1950

By Jack A. Simon, M. E. Hopkins

GENERAL GEOLOGY Coal is defined as a combustible rock that had its origin in the accumulation and physical and chemical alteration of vegetation. Coal can be ignited and burned like the wood that was man's earliest fuel, but coal gives more heat than the same amount of wood and has many industrial uses. Unlike wood, coal is not generally found on the surface of the ground but is mined from the solid rock of the earth. Before taking up the occurrence, formation, and the somewhat unique character of coal in the rock sequence, let us briefly consider the general character of all rocks in the crust of the earth. Relatively little is known about the very earliest history of the earth, although a number of logical theories have been developed. Manned exploration of the moon and the rocks being returned to earth will, we hope, provide some answers to questions concerning the earth's origin and history. The period of earth history with which we concern ourselves here begins after great areas of water had evolved on earth and substantial land areas of once molten (igneous) rock existed. Weathering and other processes that attacked the surface of the rocks reduced them to small particles. Water provided by rainfall transported this material, ultimately, to large bodies of water where it was deposited. Thus was initiated the geologic sequence of sedimentary rocks that lie above the once molten igneous rocks. The crust of the earth is not completely stable, and throughout the geologic past portions of the crust have moved laterally and vertically. Even today, many coastal areas are slowly rising or sinking. More sudden earth movements are recognized by the earthquakes they cause. Throughout geologic history, rises in sea level or the sinking of the land areas have many times permitted the oceans to cover much of what are now the areas of the continents. Only relatively small parts of the present continents appear to have been above sea level throughout geologic time. Great

Jan 1, 1973

By H. O. Hofman

With the exception of the exhaustive paper on the Father de Smet mill, by its designer, Mr. A. J. Bowie, Jr. (Bans., x. 87), nothing, so far as the writer is aware, has as yet appeared on the stamp-mills of the Black Hills of Dakota, although they have been steady producers for the last ten years. Within the small area of about 6000 by 1600 feet, $2,271,341.14 was produced in 1887† from rock averaging $4 per ton in free gold. I. The Ores. Character of the Ores.—The gold of the district is found in quartz and pyrites finely distributed through vast bodies of mica- and amphibole-schists, argillites and phyllites, and also impregnating the schists themselves. The " Belt," embracing the section of Lead City, Terraville and Central City, is the only part worked at present. The principal associated mineral is iron pyrites, with some arsenopyrite and chalcopyrite, garnet and asbestos. The ores from open cuts and upper levels are more free-milling. than those from underground workings below water-line. Hence

Jan 1, 1889

By M. R. Geer, J. D. Davis, H. F. Yancey

ALTHOUGH the mechanical cleaning of coal is carried out at plants on the surface, preparation is actually begun at the face in the mine. Here the character of the coal and the amount, character, and distribution of the impurities within the bed may be seen. Blasting methods, dust-allaying procedures, location of mining cut with respect to bands of impurity, and the practice of discarding segregated impurities underground, all have an important bearing on the successful operation of surface cleaning units. The most important single characteristic of both coal and its associated impurities from the standpoint of cleaning is specific gravity. Other characteristics related in one way or another to the preparation , of coal are rank, petrographic composition, structure and hardness, and friability. These and still other coal properties are discussed in the first section of this chapter and impurity characteristics in the second. COAL CHARACTERISTICS RELATED TO PREPARATION Rank As a result of work done over a period of several years by committees of the American Society for Testing Materials and the American Standards Association, standard specifications are now available showing the 'classification of coals according to rank and quality of grade.' The term "rank" expresses the degree to which the original coal-forming material has been changed by metamorphism through successive stages from peat to anthracite. Table 1 shows the classification of coals according to rank as devised by the committees of the organizations mentioned. The basic scheme of classification for the higher-rank coals is according to

Jan 1, 1943

By George Burrell

INTRODUCTION THE senior author of this paper, while in Colorado on other official business, made a trip to the Cripple Creek gold-mining district to get more data than are at present available regarding the composition of the gas that issues from the rock into the mines of the district. This was done at the suggestion of George S. Rice, Chief Mining Engineer of the Bureau of Mines. There are many questions of interest and importance in connection with the ventilation of the mines in the Cripple Creek district, such as the menace to life and mining of a suffocating gas entering the mines from the rock, the danger due to powder smoke (from blasting operations), and danger of continued inhalation of rock dust by the miners. This report confines itself to the first problem, the gas from the rock, and principally to one phase of this question, the composition of the gas and its effects on men and lights. A more thorough study of this and other ventilation problems is planned. That the, rock gas is a real menace is shown by the fact that miners (variously estimated from 25 to 50 by different persons interviewed) have been killed by it in the 25 years that mining has been vigorously carried on at Cripple Creek. Many men have had narrow escapes from death, some of them having been incapacitated for days. In addition, much loss of time results because at certain periods of the year or on certain days it is impossible to enter some workings. At a few mines fans force air into the workings, thus supplementing the natural ventila-

Jan 5, 1916

By Jan Visman, S. J. Aresco

INTRODUCTION The accurate sampling of coal, as with most minerals, is a difficult task. Coal is a heterogeneous material made up of different types of coal and varying amounts of mineral matter. The product as mined may contain all the layers of coal and impurities found in the seam as well as portions of the stratas above and below the coal seam. The preparation plant is the device to size, crush, and/or remove impurities so the coal may be shipped as a salable product. Sampling may be needed at many stages in the preparation process. Although this chapter is primarily concerned with sampling in connection with preparation processes, the principles apply to all coal sampling. The main reasons for sampling in connection with coal preparation are: 1) To determine the washability characteristics of the raw coal by means of float and sink tests. These may be used for the design of a preparation plant, prediction of results to be obtained, or monitoring raw coal delivered to the plant. 2) To check the performance of various operating units in the plant, either by float. and sink tests or chemical analyses. 3) To determine the analytical characteristics of the products produced, such as moisture, ash, Btu, sulfur, etc. HISTORY The earliest accepted methods of sampling coal in the United States were given in US Bureau of Mines (USBM) publications by J. A. Holmes,l G. S. Pope,2 and A. C. Fieldner.3 The American Society for Testing and Materials (ASTM) more or less adopted the methods proposed by USBM in their Standard D-21-1916 and it remained a standard for many years. Briefly, this standard called for a 500 lb (227 kg) sample for coals less than 94 in. (19 mm) in size and a 1000 lb (454 kg) sample for all coals over 94 in. (19 mm) in size. No mention was made of increments, but there was an instruction that the sample should spread over the coal

Jan 1, 1979

By David B. Dill, Edgar R. Lea

The zinc deposits of the Balmat-Edwards Division of the St. Joseph Lead Company in northern New York State provide some 10 per cent of the domestic zinc produced annually within the United States. These complex ore deposits are contained within marbles of the Precambrian Grenville series, in a repetitive sequence of dolomites and silicated units. The Balmat ore bodies are localized at various intervals throughout some 1800 feet of the stratigraphic column on the northwest side of a band of gneiss that has continuity to the Edwards area, some 10 miles to the northeast. The Edwards ore bodies are located to the southeast of this gneiss. The marble formations are thought to have included repetitive intervals of marine sedimentation that provided mineralized source "beds" and were subsequently folded, flooded, and injected with melts at great depth and were sheared, recrystallized, and reconstituted. Detailed structural and stratigraphic studies throughout the northwestern Adirondacks, in the Balmat-Edwards district, and at each mine in particular indicate the close dependence of the ore deposits on the enveloping structure whether it be local, district-wide, or regional in scope. Primary folding has developed a northeast regional trend with northwest dips. Secondary folding has been developed by an almost horizontal northeast-southwest-oriented shear couple in the plane of the regional trend. The secondary folding has produced crossfolds that intersect the regional northeast trend and plunge north to northwest at various angles. The ore bodies are found within certain stratigraphic horizons where repeated alternation of competent and incompetent beds encouraged unusually complex folding. Analysis of individual mine structures indicates that the location of each deposit is controlled by structural crossing of primary and secondary folding. The ore bodies, which are tabular, lenticular, or pod-like in form, have features that suggest parallelism to true bedding or modified flow banding, developed by northeast-southwest shearing stresses related to the development of the crossfolds. The ore deposits in general follow both structural and recrystallization trends within the wall rocks. Mobilization of the pre-metamorphic ore minerals is believed to have involved a combination of plastic flow under stress and solution of the sphalerite, minor galena, and pyrite. The ore fluids are thought to have been guided by secondary shearing and microbrecciation into structurally prepared areas where reprecipitation took place. The presumed premetamorphic mineralization now exhibits epigenetic high-temperature features related to late-stage metamorphism.

Jan 1, 1968

By D. J. Jr. McAdam

PART I.-OUTLINE OF INVESTIGATION, DESCRIPTION OF METHODS AND MATERIAL Previous Investigation of the Influence of Stress on Corrosion IN 1917 Haigh1 presented evidence that under simultaneous corrosion and cyclic stress metals may fail at lower stresses than if the corrosion is prior to the cyclic stress. In 1926 the author, while investigating the cooling effect of water on the fatigue resistance of metals, found that under these conditions steel specimens fail at stresses far below the endurance limit.2 (By "endurance limit" is here meant the fatigue limit obtained with specimens as free as possible from stress concentration and corrosive influences.) This led to an investigation (at the Naval Engineering Experiment Station, Annapolis, Md.) of the influence of cyclic stress on corrosion. This investigation maybe divided into three parts. The first part was a general survey of the conditions necessary to cause complete failure under corrosion and cyclic stress of relatively high frequency. The entire process by which metals fail under these conditions was-called "corrosion-fatigue." "Corrosion-fatigue limits" for a large number of metals were determined and the relationships of these limits to chemical composition, heat treatment and physical properties were established. The conclusion was reached that corrosion-fatigue is due to the accelerating influence of cyclic stress on corrosion. Results of this part of the investigation were presented in five papers.2-6 The second part of the investigation was a preliminary study of the influence of cyclic stress on corrosion. Each experiment was conducted in two stages. The first was a corrosion stage in which the specimen was corroded under cyclic stress; the second was a fatigue stage, in which the previously corroded specimen was tested (without further corrosion) to determine its fatigue limit. The difference between this fatigue limit and the endurance limit was used as a criterion of the "damage" due to

Jan 1, 1931

By Earnshaw Cook, H. S. Avery, J. A. Fellows

TEe increased use of heat-resistant alloys (26 per cent Cr, 12 per cent Ni; 16 per cent Cr, 35 per cent Ni; 12 per cent Cr, 60 per cent Ni; etc.) in recent years has been accompanied by continued demands by the consumer for improvement in properties. The manufacturers of these materials, of necessity, have resorted to more critical studies of the basic causes of variations in fundamental properties. To keep pace with the need for augmented information, previous techniques of investigation have been refined and new test methods and instruments created. It is the purpose of this paper to describe the apparatus, experimental technique and precision of measurement that were employed in the exploration of properties of heat-resistant alloys presented in a companion paper. The detailed precautions in experimental procedure essential for attainment of accurate and comparable data at elevated temperatures cannot be too highly emphasized. The Creep Test Since the fundamental concepts of creep testing have been recognized for the past 20 years, present interest is restricted to refinements in equipment and experimental procedure. The creep-test iaboratory constructed for the American Brake Shoe and Foundry Co. is designed to permit I000-hr. tests in the temperature range of I200° to 2 200°F. with a choice of applied stress extending from jo to 50,000 lb. per sq. in. in increments of 50 lb. per sq. in. To simplify the calculation of weight combinations, the loading beams (Fig. I) are provided with counterweights to eliminate the tare. The precision of the knife-edges (10:I ratio) is such that a 10-gram weight placed on the upper specimen grip will be exactly balanced by a I-gram weight attached to the loading shackle. Check of the loading weights proved the maximum error to be 0.06 per cent. Axial alignment is provided by crossed knife-edges in the grip seats. The furnaces are similar in design to those of Crane and Company, Battelle Memorial Institute, and the U.S. Steel Corporation. An 80 per cent Pt, zo per cent Rh No. 19 B. and S. gauge wire is used as the heating element. The details of -construction are shown in the radiograph reproduced in Fig. 2. The windings are held in place on an alundum tube with aludum cement; the distribution of turns is adjusted to give a maximum temperature gradient of , I°F. over a 4-in. gauge length (Fig. 3). To avoid sharp temperature differentials at the ends of the test section, the length of the furnace is four times the gauge length. Sixteen-inch coupons are used „ to reduce the temperature of the threaded joints and thus to facilitate removal from the grips. Thermal losses are minimized by refractory insulators cut to shape and surrounded by diatomaceous ear,th. The taps

Jan 1, 1942

By J. A. Fellows, Earnshaw Cook, H. S. Avery

TEe increased use of heat-resistant alloys (26 per cent Cr, 12 per cent Ni; 16 per cent Cr, 35 per cent Ni; 12 per cent Cr, 60 per cent Ni; etc.) in recent years has been accompanied by continued demands by the consumer for improvement in properties. The manufacturers of these materials, of necessity, have resorted to more critical studies of the basic causes of variations in fundamental properties. To keep pace with the need for augmented information, previous techniques of investigation have been refined and new test methods and instruments created. It is the purpose of this paper to describe the apparatus, experimental technique and precision of measurement that were employed in the exploration of properties of heat-resistant alloys presented in a companion paper. The detailed precautions in experimental procedure essential for attainment of accurate and comparable data at elevated temperatures cannot be too highly emphasized. The Creep Test Since the fundamental concepts of creep testing have been recognized for the past 20 years, present interest is restricted to refinements in equipment and experimental procedure. The creep-test iaboratory constructed for the American Brake Shoe and Foundry Co. is designed to permit I000-hr. tests in the temperature range of I200° to 2 200°F. with a choice of applied stress extending from jo to 50,000 lb. per sq. in. in increments of 50 lb. per sq. in. To simplify the calculation of weight combinations, the loading beams (Fig. I) are provided with counterweights to eliminate the tare. The precision of the knife-edges (10:I ratio) is such that a 10-gram weight placed on the upper specimen grip will be exactly balanced by a I-gram weight attached to the loading shackle. Check of the loading weights proved the maximum error to be 0.06 per cent. Axial alignment is provided by crossed knife-edges in the grip seats. The furnaces are similar in design to those of Crane and Company, Battelle Memorial Institute, and the U.S. Steel Corporation. An 80 per cent Pt, zo per cent Rh No. 19 B. and S. gauge wire is used as the heating element. The details of -construction are shown in the radiograph reproduced in Fig. 2. The windings are held in place on an alundum tube with aludum cement; the distribution of turns is adjusted to give a maximum temperature gradient of , I°F. over a 4-in. gauge length (Fig. 3). To avoid sharp temperature differentials at the ends of the test section, the length of the furnace is four times the gauge length. Sixteen-inch coupons are used „ to reduce the temperature of the threaded joints and thus to facilitate removal from the grips. Thermal losses are minimized by refractory insulators cut to shape and surrounded by diatomaceous ear,th. The taps

Jan 1, 1942

By M. H. Forester, John D. Cooner

ANTHRACITE ALTHOUGH the unmined anthracite will last for approximately 150 years, most of the thicker and cleaner coal beds have been almost entirely first-mined and pretty well robbed, leaving much of the present and future production to come from thin and dirtier beds. Herewith is a section of one of the dirty beds being mined in the Wyoming region [ ] This section shows that 45.8 per cent of the bed is made up of impurities and that the 45 in. of coal in the bed is in five benches, the thickest of which is 19 inches. In some localities of the anthracite region there are 14 beds of minable coal. Orderly and proper mining of the coal makes it necessary to rob or second-mine-almost all beds have already been first-mined-in sequence from the top downward. Therefore the robbing of the few remaining portions of the thicker and cleaner beds is in many instances being held up by the mining of the overlying thin and dirtier coal beds. Impurities Impurities consist of fire clay, slate, rock, and bone. The latter, which is black, contains 40 to 60 per cent carbon and often resembles good coal. In some beds there are also bands of "blue" coal, which, as the name implies, is of a bluish slaty color. Although much of this "blue" coal has a carbon content almost as high as the good anthracite, it is not

Jan 1, 1943