By D. K. Crampton, H. I. Burghoff, J. T. Stacy

The effect of cold-working upon electrical conductivity of copper and of copper alloys appears not to be generally known in detail. Although several papers on the subject have been presented, showing variable effects according to alloy composition, it is often assumed that the 2 to 3 per cent lowering of the conductivity of ordinary tough-pitch copper by severe cold-working is typical for copper alloys. Because of this situation it was decided to carry out the present work upon several types of copper, copper-zinc alloys over the commercial range of brasses, other binary alloys, and numerous age-hardening alloys in the quenched, and quenched and aged conditions. The large number of alloys investigated made it impossible to study every one in the detail it may have merited. Inasmuch as several interesting points that could not be satisfactorily explained came to light, further work is contemplated by the authors. It is usually considered that the normal effect of cold-work on ductile metals and unordered alloys is to decrease conductivity slightly. In alloys that are in the ordered state, as annealed or otherwise heat-treated, cold--working tends to disorder the structure, resulting in very marked lowering of conductivity. The random state of atomic arrangement produces lower con- ductivity than the ordered state for the same composition.1 Previous Work Previous work in the authors' laboratory has shown the electrical conductivity of several copper alloys to be decreased by greater amounts than might have been expected, in view of the general knowledge on the subject, when cold-worked. Guillet and Ballay2 investigated the influence of cold-work upon the resistivity of several metals and alloys, including copper and some copper alloys. The increase of resistivity due to severe working w is less than 4 per cent for all pure metals tested, while the increases for the alloys were generally higher. In the copper-zinc alloys, they found that the increase of resistance due to drawing increased with zinc content, and reported a 21.7 per cent increase of resistance for an alloy contaiiiing 67.9 per cent Cu as severely worked. Masima and Sachs3 studied the change in electrical resistance of three brass crystals when stretched in the tensile test, obtaining increases in resistance of the order of 3 per cent for 30 to 40 per cent reduction of area of the specimens. The resistance decreased again when the cold-worked crystals were subsequently annealed. Bardenheuer and Schmidt4 found that the conductivity of copper was decreased by 3 to 4 per cent when reduced 50 per cent by working. The conductivity of 72-28

Jan 1, 1941

By D. K. Crampton, H. l. Burghoff, J. T. Stacy

THE effect of cold-working upon electrical conductivity of copper and of copper alloys appears not to be generally known in detail Although several papers on the subject have been presented, showing variable effects according to alloy composition, it is often assumed that the 2 to 3 per cent lowering of the conductivity of ordinary tough-pitch copper by severe cold-working is typical for copper alloys Because of this situation it was decided to carry out the present work upon several types of copper, copper-zinc alloys over the commercial range of brasses, other binary alloys, and numerous age-hardening alloys in the quenched, and quenched and aged conditions The large number of alloys investigated made it impossible to study every one in the detail it may have merited Inasmuch as several interesting points that could not be satisfactorily explained came to light, further work is contemplated by the authors It is usually considered that the normal effect of cold-work on ductile metals and unordered alloys is to decrease conductivity slightly In alloys that are in the ordered state, as annealed or otherwise heat-treated, cold-working tends to disorder the structure, resulting in very marked lowering of conductivity The random state of atomic arrangement produces lower conductivity than the ordered state for the same composition 1 PREVIOUS WORK previous work in the authors' laboratory has shown the electrical conductivity of several copper alloys to be decreased by greater amounts than might have been expected, in view of the general knowledge on the subject, when cold-worked Guillet and Ballay2 investigated the influence of cold-work upon the resistivity of several metals and alloys, including copper and some copper alloys The increase of resistivity due to severe working was less than 4 per cent for all pure metals tested, while the increases for the alloys were generally higher In the copper-zinc alloys, they found that the increase of resistance due to drawing increased with zinc content, and reported a 21 7 per cent increase of resistance for an alloy containing 67 9 per cent Cu as severely worked Masima and Sachs3 studied the change in electrical resistance of three brass crystals when stretched in the tensile test, obtaining increases in resistance of the order of 3 per cent for 30 to 40 per cent reduction of area of the specimens The resistance decreased again when the cold-worked crystals were subsequently annealed Bardenheuer and Schmidt4 found that the conductivity of copper was decreased by 3 to 4 per cent when reduced 50 per cent by working The conductivity of 72-28

Jan 1, 1941

By M. A. El-Aouar

Drilling muds are complex colloidal systems. In an effort to analyze the physical properties that affect their performance at high temperature, an investigation was made of the hydrothermal stability of the monoionic hydrogen, calcium and magnesium forms of montmorillonite and attapulgite. Samples were heated to 400°1F in a simple autoclave and analyzed for cation exchange capacity, c-axis X-ray diffraction spacing and pH factor us sodium hydroxide titration dependence. Out of the six monoionic clay minerals tested, calcium montmorillonite and magnesium attapulgite showed the least base exchange capacities and were relatively unaffected to heat. It is concluded that, of the six clays studied, these two clays were the most suitable forms for use in drilling fluids. INTRODUCTION The drilling of deep wells is dependent upon the drilling mud, and problems frequently arise concerning the effect of mud temperature and prolonged heating. Drilling muds are complex colloidal systems. In an effort to analyze their behavior in deep, hot boreholes, it was thought desirable in this investigation to study suspension of pure, monoionic montmorillonite and attapulgite clays before and after hydrothermal heating. Chemically, clays are hydrated aluminum silicates, such as montmorillonites and attapulgites. The structure of montmorillonite is composed of units made up of two silica tetrahedral sheets with a central alumina octahedral sheet. Attapulgite consists of double silica chains running parallel to the c-axis with the chains linked together at their longitudinal edges. The apexes of the tetrahedrons in successive chains point in opposite direc-tions.4,7,10 One of the most important characteristics of clay minerals is their property of sorbing certain anions and cations and retaining them in exchangeable state. The property of exchange capacity is measured in terms of milliequivalents (meq) per 100 gm of clay. The cation-exchange capacities are taken at pH 7 from titration curves which show the relation between pH and milliequivalents of added NaoH.9,11 The following are causes of cation exchange: (1) broken bonds around the edges of the silica alumina units would give rise to unsatisfied charges, which would be balanced by adsorbed cations; (2) substitution within the lattice structure of trivalent aluminum for quadrivalent silicon in the tetrahedral sheet and of ions of lower valence; and (3) the hydrogen of exposed hydroxyls may be replaced by a cation which would be exchangeable. The primary techniques employed to study the effects of hydrothermal treatment were titration curves and X-ray diffraction analyses. Titration curves were useful in characterizing the nature of the clay mineral surface and the stability of the various samples to attack by acid or alkali before and after hydrothermal treatment. X-ray diffraction analyses were used to determine changes in the nature and crystal structure of the minerals present and to determine the cations in exchange positions on the montmorillonite samples. EXPERMENTAL PROCEDURE PREPARATION OF SAMPLES Selected samples of Wyoming bentonite and attapulgite clay from mines along the Georgia and Florida border were purified by centrifugation to remove all particles larger than 2 microns. In preparing magnesium attapulgite, first a 1.00-normal solution of magnesium acetate was prepared. The pH of the solution was adjusted to 7.0 by adding magnesium oxide. One hundred grams of attapulgite clay were mixed in a blender for 30 minutes with the magnesium acetate solution. The attapulgite solution was left overnight, and then filtered in a Buchner funnel. The suspension was leached with further quantity of magnesium acetate solution and then washed with distilled water for 20 days, after which the filtrate was free from magnesium ions. The concentration of magnesium attapulgite in the clay slurry was adjusted and determined quantita-

By M. C. Chang, J. Dasher

The Crucible mine in Pennsylvania, operating on Pittsburgh seam coal, is rated at 5000 tpd. The washing plant, built in 1943, is rated at about 400 tph, using hydroseparator boxes to wash the coarse coal (4 x 5/16 in.) and hydrotator units for the fine coal (5/16 x 0). It is generally acknowledged that gravity concentration equipment cannot be used efficiently to bene-ficiate coal finer than about 65 mesh. Before the present flotation circuit was installed, Crucible recovered its fine coal slurry, predominantly —24 mesh material, by passing it through a battery of five 14-in. and one hundred and ten 3-in. Hey1 & Patterson cyclones in parallel with a 75-ft Dorr thickener. About two thirds went to the cyclones and one third to the thickener. Underflows from cyclones and thickener were filtered, respectively, in one 12-disk Eimco and two 4-disk Oliver filters fitted with stainless steel cloth. The resulting cakes were added to the coarse metallurgical coal. The filtrates, overflow from the 3-in. cyclones, and thickener overflow were recycled to the coarse coal plant. The three major problems encountered in this system became acute when the mine switched from track-mounted machinery to the more economical off-track equipment. The quality and uniformity of product declined, too much slime accumulated in the circuit, and waste pond disposal became highly impracticable. Lowering of Quality and Uniformity: Since the filter cake was not beneficiated in any way, addition of this material, which contained about 18 pct ash. would certainly lower the quality of metallurgical coal. Difficulties of handling the high-ash, high-moisture cake were compounded by the lack of adequate blending facilities at the mine, making it impossible to maintain uniform feed for the coke ovens. For a two-month test period, to verify the source of trouble, all filter cake was excluded from the metallurgical coal. The excluded filter cake was stocked in the yard. Slime Buildup: The moisture retained in the coarse coal products and the filter cake provided daily the only means of slime bleed from the circuit. As this bleed was not enough to offset the incoming fines in the raw coal feed, there was excessive buildup of slimes. To operate at all, it was necessary to purge the system each weekend by pumping all the solids from the thickener to a waste pond. The slimes built up during the week progressively increased the apparent viscosity and density of the circulating plant water, so that hydroseparators and hydrotator units had to be constantly adjusted. Uniformity, yield, and quality of the metallurgical coal suffered in consequence, and the filter cake ash and moisture contents increased from Monday to Friday. Limited Waste Disposal: Location of the plant does not permit unlimited waste pond area. Maintenance of a waste pond for the purpose of emptying the thickener during weekends became a costly burden that could not be tolerated. HOW THE PROBLEMS WERE SOLVED The flowsheet (Fig. 1) chosen to overcome these difficulties is considered the one most economical to install and operate. In a preliminary change made before the flotation circuit was installed, the cyclones and thickener were first operated in series, the overflow from the 3-in. cyclones, after flocculation, being discharged into the thickener and the thick-

Jan 1, 1960

By A. STEPHENSON

EXPERIMENTAL work conducted at the Petroleum Engineering Laboratory of the University of California by L. C. Uren, J. Domercq, Jr., and J. Mejia has shown that small diameter wells offer tremendous resistance to the flow of fluids in their immediate vicinity. This resistance is due in part to the constriction of the area through which the fluids must pass as they approach the wall of the well, but is also accentuated by the increased volume which results from gas expansion. The latter in turn is a function of the deduction in pressure, the fundamental cause of fluid movement. If the diameter of the bore is enlarged several diameters, the capacity of the well, or the volume of fluid passing per unit drop in pressure per unit of time, is greatly increased without necessitating such high fluid velocities. The fundamental features which should be taken into consideration in the design of casing joints were stressed by J. B. Graham and E. E. Smith. These involved such points as correct thread design, high efficiency, and small diameter, together with the insurance that leakage will absolutely be prevented. The practical features of such design were ably discussed by engineers from leading steel manufacturers.

Jan 1, 1935

By Kent R. Van Horn, W. P. Sykes

Since Honda and Murakamil in 1918 proposed their constitutional diagram of the carbon-free iron-tungsten system, considerable effort has been expended by several investigators in attempts to define more positively the structural features of the alloys. The existence of an intermediate phase corresponding to the formula Fe3W2 (68.7 per cent W) was proposed from evidence of a purely metallographic nature by one of the present authors2 in 1926. Since that time the identity of this phase has been confirmed by Arnfelt3 and by Takeda,4 both of whom employed X-ray methods as well as the microscope and the chemical analysis of isolated microconstituents. According to Arnfelt, Fe3W2, as crystallized from the iron-rich melts at a temperature above 1450° C., contains by analysis 68.7 per cent W. The lattice of this phase is characterized by trigonal symmetry. Arnfelt, moreover, proposed a second intermediate phase formed at some temperature between 1450" and 1000" C. by a peritectoid reaction involving Fe3W2 and the iron-rich solid solution. A melt containing 25 per cent W was cooled to 1000" C. and heated for 100 hr. The precipitated tungsten-rich constituent was separated and found by analysis to contain 62.6 per cent W. This composition agrees closely with that represented by the formula Fe2W (62.2 per cent W). Diffraction patterns from the concentrated precipitate showed a hexagonal unit cell. Takeda confirmed the data of Arnfelt regarding Fe3W2 but was unable to detect Arnfelt's second intermediate phase. While Takeda failed to describe in detail the treatments employed, he stated that in alloys containing 40 per cent W which were quenched after heating at various temperatures between 1200" and 1450" C. no evidence of the second phase (Fe2W) was observed 'either in the microstructure or in the diffraction patterns of isolated residues. He therefore considered the existence of this low-temperature hexagonal compound as disproved.

Jan 1, 1933

By Franz Wever

ACCORDING to Tammann,1 the explanation of the effect of mechanical deformation in producing changes in the properties of metals is one of the most important problems of physical metallurgy, taking rank with the study of the constitution of alloy systems; and this problem has long attracted-the attention of practitioner and scientist alike. Its solution was not advanced materially until Tammann2 set up his translation hypothesis with its crystallographic basis, while other hypotheses, such as the amorphous metal hypothesis of Beilby3 and Rosenhain,4 have been shown by more intensive studies to be less and less satisfactory. The principles of the Tammann translation hypothesis have proved to be useful even up to today and in spite of all of the recent accumulation of experimental data, while the differences of opinion which have arisen relate to the extent to which the hypothesis accounts for the observed changes in properties and to what extent further assumptions are necessary. Stimulated by the proposals of Tammann, there soon developed a lively experimental activity which aimed at the elucidation of the structural or crystallographic changes produced by the mechanical deformation of metals. Parallel movements of crystal "blocks" along definite crystal slip planes had already been observed by lowing and Rosenhain5 in 1900, in metals which had been moderately deformed but without shedding light on the crystallographic nature of the processes accompanying more severe deformation. The solution of this important problem was not advanced until a much later date, or until the methods of X-ray crystal analysis had become available. Shortly after the discovery of the diffraction of X-ray by crystals, symmetrical diffraction effects were

Jan 1, 1931

By F. R. Wadleigh

There are in commercial use today in the United States various classifications of coal, each based on one or more characteristics. The bases of these classifications may be described as follows: GeNeRaL Basis Examples 1. Geological By seams and basins (local). 2. Chemical By constituents, as determined by analysis—ash, volatilc, slilfur and hcating value. 3. Combustion Characteristics As frce-burning, smokeless, character of ash. 4. Carbonization Characteristics Coking, noncoking. 5. Physical Characteristics Splint, soft, hard, block. 6. Geographical States, Fields, Counties, Districts. 7. Sizes By dimension or name. 8. Company Names Producing or sales company names, as "C. C. B. Pocahontas," etc. 9. Trade Names, copyrighted or not 10. Uses Gas, steam, coking, locomotive, fuel, bunkers, etc. 11. Use Methods Stoker coal. 12. Pools (Tidewater Exchanges) Analyses Size Seams Railroads Uses Structure Districts There are also classifications founded on more than one basis, as follows: 1. Geographical and Geological. By locality of mines (State, District, County) and seam. Examples: Cambria County, Miller Seam, New River, Sewell Seam. 2. Geographical and Chemical. Alabama medium volatile. 3. Combustion Characteristics and Ash Content. Free-burning, red ash (anthra- cite). 4. Carbonization Characteristics and Analysis. Noncoking, high-volatile, low sulfur. 5. Physical and Carbonization Characteristics. Splint, noncoking. 6. Size and Use. ¾-in. gas coal; domestic sizes (prepared sizcs); stcam sizcs. 7. Company Name and Seam. Consolidation Co., Elkhorn. 8. Size and Analysis. Low-volatile run-of-mine; low-volatilc slack. 9. Sizes—size of screen and name. 6 by sin. lump. 10. Chemical and USP. High-volatile steam. 11. Geographical and Use. Youghiogheny gas. 12. District, Size and Use. Pittsburgh gas l¼-in. lump. ,

Jan 1, 1930

By Klaus Schwerdtfeger

The equilibria in the Cr-N system have been investigated in the temperature range 1100° to 1310°C by reacting chromium powder with Nz-Hz gas mixtures. The solubility of nitrogen in chromium in equilibrium with chromium subsitvide ("Cr,N") is given by Chromium subnitride is nonstoichiotnetric; its nitrogen content is always less than that corresponding to the formula CrzN. The lattice paranzeters of quenched samples have been measured; c, and a. parameters are found to increase with increasing nitrogen content. The growth rate of the subnitride layer on chromium plates was measured by a thermogravimetric technique, using a silica spring balance. The self-diffu-sivity obtained from the theoretical analysis of the parabolic rate constant is found to decrease with increasing nitrogen content, i.e., with decreasing vacancy concentration in the nitrogen sublattice. The intrinsic nitrogen diffuivity is derived from another series of rate measurements using "CrzN" plates; the intrinsic diffusivity, DN = 3.2 X 10-a cmZ sec-' at 1200 C, is found to be essentially independent of- the subnitride composition. The concentration gradient was measured in a chromium subnitride layer by the X-ray method and found to be consistent with the derived diffusivity value. TWO chromium nitrides are known to exist:' the nonstoichiometric subnitride "CrzN" and the nitride CrN. In the present work the kinetics of the formation of chromium subnitride from chromium and nitrogen have been investigated at 1100" and 1200°C. In additional experiments the relevant equilibria have been measured. The data are used to evaluate the diffusivity of nitrogen in chromium subnitride. Since chromium nitrides are often found in chromium-containing steels, the results are expected to be helpful in the interpretation of the chemical reactions between chromium steels and nitrogen. Equilibria in the Cr-N system have been determined by several investigators.2"3 The rate of nitriding of chromium was measured by Arkharov et a1 .' in ammonia in the temperature range 800" to 1200°C. The parabolic rate law was observed. Due to the undefined nitrogen activity of the ammonia atmosphere, it is dif- ficult to interpret these rate data theoretically. An additional difficulty arises from the fact that the two-layer scale consisting of CrN and "Cr2N" was formed at the temperatures below 1030°C. The rate of nitriding of technical chromium (95 pct) was measured by Zaks in nitrogen at -1 atm in the temperature range 800" to 1300°C. EXPERIMENTAL METHODS The chromium samples were reacted with Nz-HZ gas mixtures in a vertical tube furnace, wound with Pt-10 pct Rh resistance wire. The gas-tight reaction tube was of high-purity recrystallized alumina. In nitrogen solubility measurements the nitrogen content of chromium was determined by the Kjeldahl method, on samples quenched in the cold part of the furnace. The nonstoichiometry of the subnitride and the nitriding rates were measured thermogravimetrically using a sensitive (+0.1 mg) silica spring balance. For the equilibrium measurements samples of 1 g of chromium powder contained in high-purity alumina crucibles were used. In order to remove most of the oxygen and nitrogen impurities from the chromium, the samples were initially annealed in purified hydrogen until a constant weight was obtained. The chromium plates (approximate dimensions 2 by 1 by 0.08 cm) used for the rate measurements were machined from ingots obtained by arc-melting of iodine-processed chromium. According to manufacturers' specifications the purity of the chromium powder was 99.9 pct Cr and that of the iodine-processed chromium 99.99 pct Cr. Our own spectroscopic analysis of the chromium powder yielded 0.02 pct Fe, 0.05 pct Mn, 0.05 pct Si, and 0.02 pct Ti as major impurities with all the other detectable elements below 0.005 pct. The nitrogen partial pressure of the gas phase was controlled by mixing prepurified hydrogen and nitrogen with constant pressure head capillary flowmeters. Oxygen and water vapor were removed from the mixed gas by passing it through columns of platinized asbestos (450°C) and anhydrone. The gas flowed upward in the furnace with flow rates of 300 to 500 cu cm per min (25"~). Gas tightness of the furnace system was ensured by pressure checks at regular intervals. The furnace temperature was controlled electronically in the usual manner. The reported temperatures were measured with a Pt/Pt-10 pct Rh thermocouple and are estimated to be accurate within ±$C The X-ray measurements were made with a Debye-Scherrer camera and a diffractometer using chromium radiation {\Ka = 2.29092A). EQUILIBRIUM MEASUREMENTS The experimental results of the equilibrium measurements are contained in Tables I to In. Fig. 1 shows the solubility of nitrogen in solid chromium in the temperature range 1100" to 1310°C. In Figs.

Jan 1, 1968

By A. T. Aldred

HIS note reports the existence of several new scandium intermetallic compounds of the A2B and AB stoichiometries where the A element is scandium and the B element is from group VIII or IB of the periodic table. Alloys were arc melted from high-purity materials using 2-g charges. Typical lot analyses for the materials used are given in Table I. Chemical analyses were not made on the alloys as there was little or no weight loss on melting. After annealing the specimens for 14 days at 600°C and water quenching, metallographic and X-ray techniques were used to determine the occurrence of the various phases. Table II lists the relevant data for the A2B phases. The Ti2Ni structure,2 has ninety-six atoms in a face-centered cubic cell, whilst the Al2Cu structure is body-centered tetragonal.3 The occurrence and stability of the various A2B type phases in transition metal alloy systems has recently been considered by Nevitt.4 The Ti2 Ni-type phases occur over a relatively narrow range of radius ratios from 1.14-1.26 with A partners mainly from the titanium group and B partners predominantly from the cobalt group. This suggests that both a favorable relative size of the atoms and a favorable electron concentration are necessary conditions for the existence of this structure type. A12Cu-type phases involving Ti group elements as A partners are formed with B partners from the cobalt and nickel groups, predominantly the latter, and have a higher radius ratio (1.27-1.29) than the Ti2Ni-type phases. The occurrence of both Sc2Pd and Sc2Co can be rationalized in terms of these considerations but SczNi is anomalous because of its high radius ratio. The radius ratios are calculated from the Goldschmidt CN12 radii and it might be postulated that the scandium atom is reduced in size in the compound. Unfortunately the apparent atomic size of scandium in the compound cannot be calculated from a knowledge of the structure and lattice dimensions. The crystal structure of the Sc2Au compound could not be identified from the powder diffraction pattern, but it is interesting to note that it is isostructural with a series of A2Au phases where A is a rare earth element.5 Pertinent information concerning the AB phases found in this investigation is given in Table 111. All the phases have the ordered bcc CsCl structure. The occurrence and stability of CsC1-type phases have recently been discussed by Dwight,7 who concludes that the relative sizes of the atoms do not appear to be a controlling factor (the radius ratios of all the known phases vary between 0.985 and 1.439) but that the occurrence of the phase is predominantly dependent on the relative positions of the A and B partners in the periodic table. As a measure of the stability of a given CsCl phase it has been customary to define a lattice contraction on alloying, DAB — dAB, where DAB is the AB interatomic spacing as calculated from the Goldschmidt CN8 radii and dAB is the AB interatomic distance in the compound (= v3/2 ao). Values of the parameter DscB -dScB for the compounds found in this investigation are given in column 5 of Table III and are plotted in Fig. 1. If the lattice contraction does in fact reflect the stability of a phase then Fig. 1 shows two very interesting trends when the position of the B partner in the periodic table is considered. Firstly, within any given group the stability increases in order on going from the first to third long period. Secondly, within any given period the stability increases in order as the B partner is taken from the copper, nickel, and cobalt groups. In the case of the second long period, the lattice contraction reaches a maximum at ScRh and then decreases to ScRu. The same trend could

Jan 1, 1962

By Paul Weir

BLEACHING clays have been used extensively in the oil-refining industries for a number of years. Their use in water purification is relatively recent and less extensive. They are frequently classified as (1) those naturally active and (2) those active after artificial activation with acid. Fuller's earths fall within the general group of bleaching clays and gradually the commercial term "fuller's earth" has been applied to natural clays originating, for the most part, in the south-eastern section of the United States. Bentonitic clays are usually classed as activable and are prevalent in the southwestern section of the United States.1 Bleaching clays vary considerably in chemical and physical properties throughout the country, or even in different parts of one deposit (Table 1). TABLE 1.-Physical and Chemical Composition of Different Types of Clays Composition, Per Cent Constituents and Properties Bentonite Fuller's Mud Clay (Wyoming) Earth (P Peak)' (Alluvial) Silica (SiO2) 60.0 69.6 61.67 Alumina (Al203) 19.0 14.3 20.34 Ferric oxide (Fe203) 2.8 3.90 7.70 Titanium oxide (Ti02) 0.13 0.70 1.01 Lime (CaO) 0.5 0.80 0.00 Magnesia (MgO) 2.0 1.00 0.24 Soda (Na2O) 2.4 0.40 0.31 Ignition loss 4.7 6.77 8.51 Moisture content 8.0 10.0 20.0 Isoelectric point, pH 9.2 9.2 6.5 Average swelling volume 15.0 0.0 0.0 Weight per cubic foot, lb 55.0 40.0 65.0 Material passing 200-mesh sieve, per cent 90.0 85.0 50.0

Jan 1, 1939

By T. Cantwell, N. C. Rasmussen, H. E. Hawkes

Beryl is a mineral that may be difficult to distinguish from quartz by casual field inspection. The easily recognized green color and hexagonal crystal form of coarse-grained beryl are by no means universal, even in beryl from pegmatitic deposits. If it occurred as a fine-grained accessory mineral in an igneous rock, it would almost certainly escape detection unless samples were submitted for petrographic or chemical analysis. There may be substantial deposits of some beryllium mineral, other than beryl, that has been overlooked because that mineral also closely resembles the common rock-forming minerals. A reliable and simple method of identifying beryllium minerals and determining the beryllium content of a rock would be helpful in exploration. This article describes preliminary experiments in applying nuclear reaction to the qualitative identification of beryl and to the semiquantitative determination of the beryllium content of rock samples. Gaudin,1,2 the first to apply a nuclear reaction in detecting beryllium minerals, developed a method that irradiates the sample with gamma rays, which react with beryllium nuclei to produce neutrons. The neutrons are then measured with standard equipment. The cross section for this reaction is about 1 millibarn. The cross section is a measure of the probability that a reaction will take place, for example, between a beryllium nucleus and an incident gamma ray or alpha particles.3-5 At 1-millibarn cross section for the reaction, satisfactory performance required a source strength of the order of 1 curie (3.7 x 10"' disintegrations per sec, where each disintegration releases one or more gamma rays). The reactions will not take place if the gamma radiation is below a minimum energy, in this case 1.63 mev. The size of the source and the energy of the radiation made heavy shielding necessary for these experiments, both to reduce the background count of the neutron counter and to safeguard personnel. The original discovery of the neutron by Chad-wick in 1932 resulted from experiments with another nuclear reaction, induced by bombarding beryllium with alpha particles in which the products are carbon-12 and neutrons. The equation for this reaction is as follows:' " ,Be" + ,He'? 6C12 + 8,n' [1] re-particle neutron In the above nuclear equation (Eq. 1), the sub- script number indicates the number of protons in the nucleus (the atomic number) and the superscript the total number of neutrons and protons (approximately the atomic mass). For the alpha-neutron reaction the cross section is about 250 milli-barns, or 250 times that of the gamma-neutron reaction used by Gaudin. The positively charged alpha particle is repelled by the positive charge of the beryllium nucleus; it must, therefore, have a certain minimum energy in order to approach close enough to the beryllium nucleus to react. For reaction with the beryllium nucleus, the lower limit of the alpha-particle energy is 3.7 mev. The alpha-neutron reaction, with polonium-210 as an alpha source, was selected for the present experiments. Alpha particles are emitted by polonium-210 at 5.30 mev, which is adequate for the reaction with beryllium. Furthermore, this isotope of polonium emits alpha particles with negligible associated gamma radiation, thus eliminating the necessity of shielding. The half-life of polonium-210 is 138 days. Inasmuch as alpha particles carry a possible charge and are large compared with most nuclear particles, their energy is rapidly dissipated in passing through matter. Their range in standard air is 3.66 cm,3 and they penetrate only a few tens of microns into a mineral sample. The short range in air can be minimized by preparation of a flat sample surface that can be brought very close to the alpha source during analysis. On the other hand, short range of alpha particles in air lessens the radiological health hazard and makes it possible to use this method without shielding. It must be emphasized, however, that the alpha emitters are potentially very dangerous if they enter the human body. Polonium must be handled with extreme caution. The literature has reported experiments on the yield of neutrons from reaction of alpha particles with beryllium nuclei. Feld" reports that in intimate mixtures of polonium and beryllium, 3 x 106 eutrons per sec are produced per curie of polonium. Elsewhere in the same reference it is stated that a sandwich-type source yields about one third as many neutrons as an intimate mixture. A table of neutron yields for full energy polonium alpha-particles on thick targets as reported by Anderson7 is the basis of Table I. From Table I it can be deduced that the elements most likely to interfere, i.e., those that also produce neutrons when bombarded by alpha particles, are boron and fluorine. These data also show that it will probably not be possible to determine very small quantities of beryllium in rocks because of the masking effects of the major elements, sodium, magnesium, and aluminum. The neutrons emitted in the alpha reaction are detected by another nuclear reaction. Either of the

Jan 1, 1960

By S. Luszcz, R. W. Vook, Fred Witt

In situ X-ray investigations were made on polycrys-talline silver films deposited by vacuum evaporation on (111) CaF2 and (100) NaCl single-crystal substrates at 80°K. The films were evaporated and annealed in an X-ray diffractometer attachment having a residual gas pressure of 2 x lo-' Torr. All measurements were made without exposing the films to the atmosphere. Measurements were made on the films in the as-deposited state and after various annealing treatments. The intrinsic stacking and twin fault densities, the magnitudes of the uniform and nonuniform strains, and the crystallite sizes were determined. In addition the textures in the films were measured qualitatively. The results obtained for the as-deposited films on single-crystal substrates are in substantial agreement with previously reported results for silver films deposited on glass. Intrinsic stacking and twin faults, as well as uniform and nonuniform strains, were present in these films. During the various annealing treatments (up to 350°C) the faults and nonuniform strains annealed out. Considerable grain growth and texture changes occurred also. The effects were much greater for the NaCl substrate than for the CaFz substrate. The relative magnitudes of the grain growth in the variously oriented grains could be explained qualitatively in terms of the thermal strains and strain energies introduced into the differently oriented grains during the initial, irreversible anneal. These strains were due to the different thermal expansion coefficients of the film and substrate. X-RAY diffraction measurements on evaporated films deposited on substrates at low temperature have the advantage that many of the imperfections introduced into the film during deposition are "frozen in". Thus, the influence of a very important experimental variable, substrate temperature, on the imperfection structure of evaporated metal films may be studied. Moreover, the effects of annealing such films makes possible the study of thermally activated recovery processes in these films. The present study was designed to determine the influence of single-crystal substrates on the resultant film structure relative to the previous results obtained using glass substrates.' To this end great care was taken to keep the experimental variables the same in the two cases. Different experimental conditions would, of course, result in films having different physical properties. Again the initial substrate temperature was in the neighborhood of 80°K and the films were subsequently annealed to 350°C. The pure metal silver was chosen for evaporation, primarily because of its relatively low stacking fault energy and consequent high fault density in the as-deposited state. The silver films were formed by evaporation onto air-cleaved {ill} CaF, and (100) NaCl surfaces cooled to 80°K in an X-ray diffractometer attachment2 having a base residual gas pressure of 2 X l0-' Torr. The films were not exposed to the atmosphere until all of the X-ray data had been recorded. In this way one of the most important experimental variables, environment, could be well-controlled and reproduced. X-ray measurements were made at the temperature of deposition and included determinations of the diffraction line peak positions, line shapes, and integrated intensities. The peak position measurements were used to determine the intrinsic stacking fault densities and the average uniform strain in the film. The shapes of the diffraction lines provided information on the twin fault density, true crystallite size, and average nonuniform strain. The preferred orientation in the film was determined qualitatively from the integrated intensities. I) EXPERIMENTAL PROCEDURE The evaporator attachmentZ was charged with 99.999 pct Ag pellets positioned in a tantalum filament which had been outgassed previously at l0-8 Torr. The CaFz and NaCl single crystals were cleaved in air and then placed in position in the chamber so that their cleavage surfaces were on the diffractometer axis. The chamber was prepumped using a sorption pump, sealed off, and then baked at 150°C for 24 hr. The ion pump operated during the bakeout cycle. The substrate was then heated to 500° C by means of an auxiliary heater and kept hot until the rest of the chamber was cooled slowly to room temperature. This bakeout procedure consistently resulted in an ultimate pressure in the low lo-' Torr range. The substrate was then cooled down on 80°K. Its temperature was monitored by a thermocouple wedged into the rear of the copper substrate holder. The diffracted intensity and peak position of the 111, 222, and 333 CaF, lines were measured prior to evaporation. Nickel-filtered, pulse-height-discriminated copper radiation was used. Similar measurements were made for the 200 and 400 lines from NaC1. These measurements were used as a lattice parameter check and to determine the thickness of the evaporated silver films from the attenuation of the substrate lines. The evaporation rates were approximately 3A per sec for both films while the maximum pressures during evaporation were 3 x lo- ' and 7 x 10"8 Torr for the CaF, and NaCl cases, respectively. The film thickness was measured by the attenuation of the CaF, and NaCl substrate lines and by at optical interference method. Values of 1700 and 1500A, respectively, were obtained for the silver

Jan 1, 1969

By J. L. Gillson

The word "other" in paragraph 4, line 11, column 1, page 205, should read "over;" the correct version of reason 2, this paragraph, is: 'L. . . 2) to evaluate the usefulness of certain geo-chemical techniques, V. C. Kennedy and S. W. Hobbs of the USGS had already studied the distribution of copper, lead, and zinc in the soils (both in background areas and over veins) and in the water and plants, providing a criterion for measuring the magnitude and effect of soil contamination; ...9 On page 206, in the top left hand corner of Fig. 1 (in the area bounded by 47°35' and 116°10), the reference to Fig. 3 is incorrect. The area of Pine Creek, South Fork Coeur d'Alene River, and portion of Big Creek (the area which includes, from left to right, Kingston, Pinehurst, Smelterville, and Kellogg) should be identified as that of Fig. 2A. The headings for columns 1, 3, and 4, Tables I and 11, page 209, column 2, were reversed when the paper was printed. The corrected tables are:

Jan 1, 1961

By W. P. Blake

One of the most remarkable iron-ore districts of the world is found in Southern Utah, in Iron County, about 270 miles south of Salt Lake City, and 10 miles west of Cedar City. This region has long been known in a general way; but, being at present somewhat difficult of access, it has been rarely visited by 'any of our members. Professor Newberry has published somewhere a short description. Last year, by the invitation of J. R. Walker, Esq., of Salt Lake City, one of our associate members, I formed one of a party, including Professor G. W. Maynard and W. S. Keyes, to visit and inspect the region. A special car was placed at our disposal by the courtesy of Hon. John Sharp, Superintendent of the Utah Central Railway. From the present southern terminus of the road at Milford, a drive of 55 miles took us to Cedar City, about 10 miles east of the iron region. The ores outcrop in a low range of hills or mountains, and stand out in such bold relief from the general surface, and are so massive and jet black, that they may be seen for miles before they are reached. These outcrops extend in long lines over the hills, and mark very . clearly the course of the beds, conforming generally to the inclosing stratified formations, probably of Palaeozoic age. These rocks are somewhat obscure, but there are large outcrops of limestone without much alteration. This, in places, appears to be the adjoining rock, at others the wall-rocks are porphyry, and at others apparently a quartzite and a fine-grained felsite. The beds of iron-ore are from 10 to 100 feet and more in thick ness, and some of the outcrops extend unbroken continuously for 1000 feet and more. It consists chiefly of magnetite and hematite,

Jan 1, 1886

By G. Sachs

According to Tammann,' the explanation of the effect of mechanical deformation in producing changes in the properties of metals is one of the most important problems of physical metallurgy, taking rank with the study of the constitution of alloy systems; and this problem has long attracted the attention of practitioner and scientist alike. Its solution was not advanced materially until Tammann2 set up his translation hypothesis with its crystallographic basis, while other hypotheses, such as the amorphous metal hypothesis of Beilby3 and Rosenhain,4 have been shown by more intensive studies to be less and less satisfactory. The principles of the Tammann translation hypothesis have proved to be useful even up to today and in spite of all of the recent accumulation of experimental data, while the differences of opinion which have arisen relate to the extent to which the hypothesis accounts for the observed changes Ïn properties and to what extent further assumptions are necessary. Stimulated by the proposals of Tammann, there soon developed a lively experimental activity which aimed at the elucidation of the structural or crystallographic changes produced by the mechanical deformation of metals. Parallel movements of crystal "blocks" along definite crystal slip planes had already been observed by Ewing and Rosenhain5 in 1900, in metals which had been moderately deformed but without shedding light on the crystallographic nature of the processes accompanying more severe deformation. The solution of this important problem was not advanced until a much later date, or until the methods of X-ray crystal analysis had become available. Shortly after the discovery of the diffraction of X-ray by crystals, symmetrical diffraction effects were

Jan 1, 1931

By O. N. Carlson, E. D. Gibson, D. W. Bare

SEVERAL investigators have recently contributed to a clarification of the controversy concerning the allotropy of chromium. Ross and Hume-Rothery1 and Vasyutinskii et a1.2 have reported high-temperature X-ray data on unalloyed chromium from which they have concluded that no allotropic transformation occurs in this metal. Bechtoldt and vacher3 in their investigation of the Cr-Ni alloy system found no evidence for a transformation in chromium and Smart and Haynes4 in critically analyzing the data presented to date concerning this system could find no evidence for a eutectoid reaction in this system. Wyder and Hoch5 in research concurrent with our

Jan 1, 1964

By D. R. de Fontaine

By computing the values of the resolved shear stress for a great many orientations of the tensile axis on all 12 (111) <110> slip systems, Taylor and Elam&apos; were able to map out a stereogram of slip systems, given here, Fig. 1, in Diehl&apos;s notation (see, for example Hauser and Jackson&apos;). The purpose of the present note is to derive such a stereogram by mathematical reasoning and to give a simple method of defining the system with highest resolved shear stress for any direction of the tensile axis, thereby eliminating tedious computation of the Schmid factor. Let the tensile axis, of direction cosines [xyz], make the angles 0 and relative to the slip plane normal [HKL] and the slip direction [hkl] respectively. Fig. 2 shows a simple cubic cell whose edges define a Cartesian coordinate system. Let A be a unit vector of origin 0 supported by the tensile axis. Its end point [xyz] then lies on a sphere of unit radius, on the positive hemisphere of which the planes z = 0, x = y, y = z limit the so called primitive triangle of a standard [loo] stereographic projection. For any point of this triangle, the following hold: 0«2 «y *sx « 1 [l] Now, for given [xpz], the most highly stressed system will be the one for which the following expression of the Schmid factor has the largest possible value: (HKL) belonging to the form (111) and [hkl] to the form <110>, the denominator on the right hand side of Eq. [2] is equal to 1.fi.a. The unknowns H, ... h, . . . can now be determined by correctly distributing +1 and -1 to H, K, L, and +1, -1,O to h,k, 1 giving the numerator of Eq. [2] its greatest positive value (the angles 0 and cpare chosen acute) subject to the condition: Hh+Kk+Ll = 0 [3] since the slip direction must lie in the slip plane. Condition [3] can be satisfied only by having one of its terms vanish and the other two equal to +1 and -1. Taking the case of the tensile axis lying in the primitive triangle, x2y, z and therefore Hh will be chosen equal to +1 with H = h = +1 in order to retain a maximum of + signs. There remain two alternatives: either 1 = 0 or k = 0. 1) take 2 = 0 Then Kk = -1 and the numerator of [2] becomes: Retaining a maximum of + signs gives L = k = +1 and becomes: 2) take k = 0 Then L1 = -1and, likewise, the numerator of [2] becomes: xz - z2 + xy + yz [5] But the difference [5] - [4] can be written: (y - z)(x+y +z) [6] positive or zero by virtue of [I]. If [6] is positive (y > z), then the largest possible value for the numerator of [2] for any xyz inside the primitive triangle is given by [5], i.e., for: That is to say, the active slip system corresponding to an orientat:~on of the tensile axis inside the primitive triangle is:

Jan 1, 1962

By A. G. Guy

Thermodynamic activity rather than chemical composition is basic to the analysis of diffusion. This is the essential conclusion reached by Darken1-3 and by Birchenall and Mehl.4 If so, it is reasonable to expect that diffusion calculations should be carried out using activities. This paper will illustrate a method of employing activities in analyzing interstitial diffusion. For interstitial diffusion (of carbon in iron and probably generally) the diffusion of the solvent atoms, volume changes, and other such complexities not explicitly provided for in the usual diffusion equations cause a negligible error of the order of 1 pct. Therefore it is relatively easy to test the validity of an analysis based on activities in the instance of interstitial diffusion. The mathematical treatment of the more complex substitutional diffusion could be simplified once the adequacy of the activity method had been established for substitutional diffusion. Thus the present work has the purpose not only of providing a superior analysis of interstitial diffusion but also of indicating a possible approach to the more important question of an adequate treatment of substitutional diffusion. Development of the Diffusion Equation Although activities are convenient quantities to determine experimentally, they are derived from the more fundamental fugacities.9 Possible confusion in using activities can be avoided by basing equations involving their use on the relationship, dP = -D1d/ax dt [I] where, dP = the number of grams of solute crossing one cm2 in the time dt sec. D, = the diffusion constant for use with fugacities; it is assumed to be constant at a given temperature, and has units of secs. f = the fugacity of the solute in the solid solution; the units are those of pressure, dynes per cm2. x = the distance in cm. Eq 1 can be considered to be the basic form of the first Fick Law for one-dimensional diffusion. In order to convert Eq 1 into an equation involving activities, a choice of a standard or reference fugacity, f°, must be made: then. a = f [2] where a is the activity corresponding to the fugacity f. However, the value of a is also determined by the relation, a = a\c [3] where a is the activity coefficient and c is the concentration. For a given value of a (such as a = 1) it is evident that the units used for expressing concentration will affect the numerical value of a corresponding to a given amount of carbon dissolved in y-iron. Since weight per cent concentration is so widely used, this unit will be adopted as the standard in this paper. When the value off given by Eq 2 is substituted in Eq 1, the first Fick Law becomes, dP= -D,f°dl [4] Since D,f° is constant (at a given temperature), the second form of Fick&apos;s Law can be obtained in the usual manner, -dt D&apos;f° dx [5] where c&apos; is the concentration in g per cm3. In terms of weight per cent concentration, c, Eq 5 becomes, dc _ 100 d2a Tt = T /f w [6] where p is the density of the solid solution and will be assumed to be constant. In order to simplify Eq6, it is necessary to consider the standard state, f°. Standard states are chosen for convenience. There appears to be one especially convenient choice for the analysis of interstitial diffusion. If the activity coefficient, a, is set equal to unity at infinite dilution of the solute, 100 then — 100D1fl° is approximately equal P to the usual diffusion constant in dilute solutions. This is true since the activity, a, in Eq 6 can be replaced by the concentration, c, with little error in an infinitely dilute solution.* Here f1° is the standard fugacity necessary to achieve this standard state. It is proposed that a diffusion constant Da&apos; be defined, Da1=100/pD1f1° [7] where A is the metal whose diffusion is * The second derivative of a is equal to the second derivative of c in dilute solution only if -da/dr- is. zero. Although theory does not require this condition, in the systems C in Fe, and Zn in Cu, dc is in fact found to be essentially zero.

Jan 1, 1950

By AIME AIME

Annual net production of crude oil from the Anglo-Iranian, Oil Company&apos;s fields in Iran for the years 1940 through 1945 amounted to: YEAR TOTAL PRODUCTION (Long Tons) 1940 8,626,639 1941 6,605,320 1942 9,399,231 1943 9,705,769 1944 13,274,243 1945 16,835,000 (preliminary figure) All developed fields were on almost continuous production throughout the war, though their operation naturally was hampered by war conditions, which affected particularly supplies of equipment.

Jan 1, 1946