By Bowen Li

Copper vermiculite is a special nanomaterial with excellent antibacterial and antifungal performance. By means of ion exchange, copper vermiculite containing up to 5.8wt% copper was prepared. The chemical and mineralogical characterization of the material was investigated in this study based on the XRD, AAS, TEM and EDS analysis, as well as the calculation of crystalline parameters and crystal chemical formula. Cu2+ and Mg2+ have similar atom radius and same electrovalence. Correspondingly, the structure character of copper vermiculite is very close to that of standard Mg-vermiculite. Most of the CU21 may have occupied the interlayer cationic positions in the form of hydrate in vermiculite. However, some may have entered into octahedral coordinate positions. The values of au and bo of the copper vermiculite crystal cell have no obvious change compared to that of original vermiculite micropowder, but the Co value decreased slightly, which is desirable for the stabilization of the Cu2+ in copper vermiculite.

Jan 1, 2003

By R. L. Nyirenda

An investigation of the reducibility of a cassiterite concentrate with charcoal was made in the temperature range of 1123-1373 K. The course of the reaction was monitored by a combination of sample weight loss measurements, product gas analysis, and chemical analysis of the reaction product. It was found that the cassiterite could be best reduced by a combination? of high temperature, reasonably high charcoal proportions, high charge poroslty, and the addition of a small percentage of lime. Analysis of kinetic data obtained from isothermal experiments using theory from the oxidation of carbon by carbon dioxide gave an activation energy value of 255 lci/mole for the consumption of carbon by reaction with cassiterite.

Jan 1, 1990

02, NaCI03, H202, Na0CI and Ce+4 have been examined as oxidants in an alkaline carbonate system for uranium in in situ leaching. The South Texas and New Mexico ores contained up to 2.6 meqJg of reducing compounds which consume oxidants in the leading operation. Leaching rates did not increase linearly with the oxidation potential of the oxidants. A mild oxidant can be used to maximize uranium oxidation selectively and oxidant efficiency. 02 can oxidize most of the uranium mineral with an adequate rate and high oxidant efficiency.

Jan 1, 1990

By T. K. Bundtzen

Placer gold in the Iditarod and Innoko mining camps of western Alaska is derived from a suite of comagmatic, Late Cretaceous to Early Tertiary, alkali-calcic, meta-aluminous. volcanic-plutonic complexes and peralumi-nous rhyolite sills that intrude Mesozoic flysch. Heavy-mineral concentrates from 42 mining operations and streams draining known mineralized areas in the igneous complexes contain placer gold and a variety of ore minerals derived from epithermal to hypothermal conditions of formation. The minerals include cassiterite, ilmenorutile, samarskite, cinnabar, scheelite, chromite, stibnite, silver sulfosalts, monazite, and zircon. Results of the study show that 1) cinnabar. stibnite, and quartz formed with the bulk of the placer gold in an epithermal lode environment, 2) chromite appears to have originated in mafic phases of monzonite plutons and alkalic basalts, and 3) niobium-tin-tungsten-uranium-silver values may have been derived from stockwork accumulations in cupolas of monzonite plutons.

Jan 1, 1987

"Mechanical alloying (MA) synthesizing technology and thennohydrogen processing (THP) were utilized to produce nanocrystalline Ti-MMC's reinforced by TiB intermetallic compound by using TiH2-B powder mixtures. Powders MA'ed up to 8 hours were examined by X-ray diffraction and SEM study. All MA'ed powders afterwards were HIP'ed at 700, 800 and 950EC for 1 hour. Detailed XRD, SEM and TEM study of the samples were carried out to determine the structure and micrography of the Ti-TiB MMC material processed by MA+THP approach followed by HIP'ing at high temperatures.IntroductionThe fiber reinforced titanium base composites [1,2] which possess a great resistance to high temperature have been investigated. In these studies fibers of C and SiC were used as reinforcing materials. However, these fibers react with Ti-matrix at elevated temperature resulting in product formation at the interface between the matrix and the fiber. Because of the chemical reactions, strength of the product MMC material diminishes.In conventional techniques of whisker reinforced composite material production, the mixtures of matrix metal powders and dispersed fibers are consolidated by hot pressing, HIP and/or hot extrusion. These techniques, however, have some shortcomings. Hard and brittle fibers could be broken during mixing cycle of the processing. Consolidation techniques could also be the cause for fiber breakdown. Attaining of the uniform dispersion of fibers into the metal matrix is not an easy process. The chemical reactions at elevated temperature exposures in the interface between the matrix material and fiber reinforcement cause product formations leading to poor mechanical properties."

Jan 1, 1998

By Manjie Li, Mingrui Yang, Haijun Peng, Shuxing Qiu, Wei Liu, Shengfu Zhang

It is important to produce and utilize highly reactive coke in order to reduce the energy consumption and CO2 emissions through improving shaft efficiency in blast furnace. The present study aimed to investigate the transformation of iron minerals and properties of iron coke (the coke mixed iron ore fines). Along with the increase of iron ore fines, cold strength displayed a slight downtrend and the pore structure wasn’t inferred to be a major factor affected the properties of iron coke. During carbonization, the majority of mixed iron oxides were reduced to metallic iron by CO and H2 and the degree of metallization achieved to approximately 75%. Nevertheless, produced metallic iron was oxidized by pure CO2 during gasification. Iron coke reactivity index (ICRI) was obviously enhanced and the iron coke strength after reaction (ICSR) drastically decreases, which were also significantly influenced by crystal structure of carbon.

Jan 1, 2015

By George S. Dulikravich

An advanced semi-stochastic algorithm for constrained multi-objective optimization has been adapted and combined with experimental testing and verification to determine optimum concentrations of alloying elements in heat-resistant and corrosion-resistant H-Series austenitic stainless steel alloys. The objective was to simultaneously maximize a number of alloy's mechanical properties. This research will result in a rigorous tool for the design of high-strength H-Series steels and other types of alloys unattainable by any means existing at the present time. Such a material-by-design tool will also be able to reduce or minimize the need for the addition of expensive elements such as Cr, Ni, Co, Nb, Ti, V, etc. and still obtain the optimum properties of an alloy.

Jan 1, 2003

By George S. Dulikravich

An advanced semi-stochastic algorithm for constrained multi-objective optimization has been adapted and combined with experimental testing and verification to determine optimum concentrations of aJ10ying elements in heat-resistant and corrosion-resistant H-Series austenitic stainless steel alloys. The objective was to simultaneously maximize a number of alloy's mechanical properties. This research will result in a rigorous tool for the design of high-strength H-Series steels and other types of alloys unattainable by any means existing at the present time. Such a material-by-design tool will also be able to reduce or minimize the need for the addition of expensive elements such as Cr, Ni, Co, Nb, Ti, V, etc. and still obtain the optimum properties of an aJ1oy.

Jan 1, 2003

By O. C. Gaspar

The mineralogical and textural characteristics of the volcanogenic massive sulphide ores from the Aljustrel and Neves-Corvo deposits have been studied by ore microscopy techniques since 1977. Several ore types have been recognized, and the ore paragenesis, ore textures, and behaviours of different ore types during grinding and concentration processes, have been determined. An ore classification was established for use in metallogenetic studies, ore reserve calculations, selectivity during mining, and control of the ore beneficiation processes. In addition, an empirical method was developed for supplying, on time, the qualitative and semi-quantitative information needed for processing the Aljustrel ores and for optimizing the Neves-. Corvo copper and tin concentrators.

Jan 1, 1991

By Tang Chaoho

Laboratory research on the reducing and matte smelting of Jamesonite concentrate has been carried out. The influence of the process conditions such as the smelting temperature, the amount of pyrite cinder (the agent of fixed sulfur) and the amount of additives on the smelting process have been studied. Under the optimum condition the direct recovery ratios of antimony and lead are 83.26% and 68.50% respectively. The ratio of fixed sulfur is 98.97% but more than 15% lead and 30% silver remained in the ferrous matte. The key problem to be solved of this new process is how economical and effective is the recovery of silver and lead in ferrous matte.

Jan 1, 2003

By Józef Czemecki

Polish copper concentrates are characterized by high levels of impurities, particularly Pb and As. Two technologies are being used for copper concentrate smelting at KGHM Polska Meidz S.A., namely the shaft furnace process (Legnica Copper Smelter, Glogów I Copper Smelter) and a single-stage process for direct to blister concentrate smelting in a flash furnace (Glogów II Copper Smelter). Both technologies are used at different physical and chemical conditions which results, in different impurities behavior. The paper presents flow sheets for copper production in a plant using the shaft furnace process and in another in which a single stage flash process is used. The metals distribution in particular semi-products is given as well as a method for elimination of impurities from the copper production cycle. Methods are also discussed for alloy and matte converting and copper refining to obtain low Pb and As concentrations in anode copper (0.3% Pb and 1500 ppm As maximum) that are being used in the KGHM Polska Meidz plants. Useful co-operation between the plants using different technologies, aimed at the limiting the effect of undesired impurities on the quality of blister copper produced, is also described.

Jan 1, 1998

By Tang Chaoho

Laboratory research on the reducing and matte smelting of Jamesonite concentrate has been carried out. The influence of the process conditions such as the smelting temperature, the amount of pyrite cinder (the agent of fixed sulfur) and the amount of additives on the smelting process have been studied. Under the optimum condition the direct recovery ratios of antimony and lead are 83.26% and 68.50% respectively. The ratio of fixed sulfur is 98.97% but more than 15% lead and 30% silver remained in the ferrous matte. The key problem to be solved of this new process is how economical and effective is the recovery of silver and lead in ferrous matte.

Jan 1, 2003

By Mehmet Bu daycı, Onuralp Yücel, Ahmet Turan, Murat Alkan

In this study, iron based alloys (Fe, Fe-Cr-Ni-Mo, etc.) were produced by using metallothermic methods starting from Mill Scales obtained continuous casting processes. During the process, the combustion was realized by ignition and the produced wave propagates throughout the reactant mixture yielding the desired product. In this work, Mill scale used as an iron source, which includes +2, +3 values iron oxides. Aluminum, Magnesium and Silicon were used as reductants. In these metallothermic experiments, different ratios of reductants were examined, and their effects on the metal recovery and alloy compositions were investigated. The samples were characterized by using chemical analysis (AAS), XRD and XRF techniques.

Jan 1, 2016

By Tina Maniatis

Applied Biosciences has developed a biological technology for removal of arsenic, nitrate, selenium, and other metals from mining and industrial waste waters.The ABMet® technology was implemented at a closed gold mine site in Canada for removing arsenic from tailings pond water. The system included six bioreactors that began treating water in the spring of 2004. Design criteria incorporated a maximum flow of 567 L/min (150 gallons per minute) and water temperatures ranging from 10°C to 15°C. Influent arsenic concentrations range from 0.5 mg/L to 1.5 mg/L. The ABMet® technology consistently removes arsenic to below detection limits (0.02 mg/L). Data from the full scale system will be presented, as well as regulatory requirements and site specific challenges. Keywords: Arsenic, Sulfate Reduction, Metal Sulfide Precipitate, Biological Water Treatment

Jan 1, 2005

By W. K. Connor, O&apos

Thermal Treatment Technology Division Albany Research Center, U.S. Dept. of Energy Oregon. This evaluation included a characterization study and direct smelting tests conducted in a bench-scale electric arc furnace (EAF). In contrast to other thermal treatment technologies considered for these wastes (i.e., fluidized bed combustion), direct smelting in the EAF can process 100% of the wastes without prior beneficiation, and utilizes solid oxidant additions (in this case iron ore) rather than air to oxidize the carbon. This solid oxidant addition is advantageous because it results in the production of several value-added furnace products. These products include cast iron resulting from the reduction of the iron oxides, baghouse dust containing virtually all of the zinc from the residues, and a clean (nonhazardous) slag product suitable for recycle as concrete aggregate or construction fill. Offgas from the smelting furnace also holds potential as fuel gas for cogeneration. The direct smelting tests conducted thus far were successful at producing the desired furnace products, exhibiting the potential for complete recycle of the waste pile. A cast iron product of comparable quality to conventional cast irons was produced, at nearly 80% iron recovery to the metal. The slag product was determined to be nonhazardous, based on the EPA TCLP. Lead and zinc partitioning to the dust product was greater than 99%. The material balance over the furnace indicates that for every ton of feed processed, 540 lb. of cast iron, 600 lb. of slag, and 150 lb. of dust would be produced. Energy consumption was roughly 1.10 kWxh/lb of feed material. Prior experience suggests that these figures measured in the bench-scale furnace would translate to 0040 to 0.50 kWxh/lb at the industrial-scale.

Jan 1, 2000

By Xie Zhang, Jiang Diao, Xin Qiu, Lu Jiang, Bing Xie, Hong-Yi Li

"Duplex converter process, in which the first converter is used for removing phosphorus from hot metal (De-P), is an important way to produce low P-content and ultra-low P-content steels. In order to improve phosphorization removal and formation of slag with high basicity at relatively low temperature during dephosphorization converter process, effects of temperature, silicon content in hot metal and varied compositions of the De-P converter slag on phosphorus distribution between the slag and hot metal were investigated with thermodynamic calculations and by laboratory scale experiments in present work. Results showed that phosphorus distribution ratio between slag and metal was varied in 10.6~26.6 when basicity of the slag was in the range of 1.5~2.1 at 1370, and the distribution ratio was increased with increasing basicity and Fe10 content in the slag.IntroductionIt is known that phosphorus exists in steel in the form of solid solution, which can significantly improve strength and hardness of steel at room temperature. However, the plasticity and toughness of steel, especially the low temperature plasticity is sharply reduced and leads to high ductile-brittle transition temperature. This phenomenon is commonly known as cold brittleness of steel [1~3]. Hence, phosphorus should be removed as much as possible in the steelmaking process, because it is generally harmful to the iron and steel products."

Jan 1, 2013

By Eleazar Salinas R., Miguel Perez L., J. Cesar Juarez T., Martin Reyes P., Eduardo Cerecedo S., Isauro Rivera L., Francisco Patino C., Juan Hernández A.

"A complete characterization of burrows from Mining district of Pachuca - Real del Monte, in Hidalgo state Mexico, was done. These kind of residues had not been formally characterized, founding an average chemical composition of 70.43 % wt. of Si02, 7.032 % wt. of Ah03, 2.69 % wt. of Fe20 3, 0.70 % wt. of Mn, 3.98 % wt. ofK20, 3.34 % wt. of CaO, 2.50 % wt. ofNa20, 1.01 % wt. of MgO, 0.26 % wt. of Ti02, 0.04 % wt. of Zn, 0.026 % wt. of Pb, 56 g/ton of Ag and 0.6 g/ton of Au; In the same way, the residues present as majority mineralogical phases the following: Quartz, Berlinite, Orthoclase, Feldspar, Anorthoclase and Calcite. By the other hand, joint with the big volume that present these residues and the chemical and mineralogical characteristics, these materials or sub - products can be used for production of ceramics, into mixes forming some materials for architecture (bricks, blocks, and tiles), refractory bricks, in the production of cement and to get some metallic values such as gold and silver involved in these residues.IntroductionActually the mining residues in Hidalgo State, Mexico are the result of more tan 500 years of mining, leading so a great volume of deposits, which we can classify in different types, among the most communes we have: Acid Mining Waters, Waters of solid transport and elements in the form of radicals, deposits of abandoned minerals without processing, and mining wastes of processed minerals known as burrows or dumps, being these the most abundant in the Hidalgo State [1-4].Form the metallurgical point of view, it is known that a characterization study if fundamental to find the viability of reuse of these kind of residues, leading so an additional use and the opportunity of get an alternative use into several industrial processes, due to its contents of oxides of silicon, iron, aluminum, calcium, sodium and potassium, principally, besides of its mineralogy and distribution of chemical elements into its primary and secondary phases [ 1-2, 5- 6]."

Jan 1, 2011

By Noel A. Warner

Modern steelmaking is based on direct use of oxygen in high intensity batch reactors. A totally new approach is proposed in this paper, based on the view that pursuit of high intensity is unlikely to lead to successful coal-based continuous steelmaking. By substituting carbon dioxide and water vapor as the oxidants rather than using oxygen directly, the intensity is greatly reduced. Accordingly. subsurface formation of carbon monoxide bubbles can be avoided by careful manipulation of the three participating rate processes, gaseous diffusion, interfacial chemical kinetics and liquid phase mass transfer. Steelmaking can then be carried out without explosive ejection of molten droplets and the generation of micro-spray but rather in a controlled and fumeless fashion. The vital component is the introduction of generic melt circulation technology. Three melt circulation loops in series are envisaged. Starting with a composite feed of iron ore fines, pulverized coal and lime flux, a metallized solid raft floating on molten iron is propelled out of the ironmaking loop onto the first of two downstream steelmaking loops. In the first, a liquid slag is formed, primary decarburization is undertaken not with oxygen but rather with CO2 and H2O and the melt is desulfurized. The semi-product stream enters the third melt circulation loop, where open-channel decarburization is effected along with dephosphorization to yield a low carbon steel product. Alternatively, the melt leaves the last loop to irrigate a packed tower countercurrent to argon at around 100 mbar to continuously produce ultra-low carbon (ULC) steel.

Jan 1, 2003

By Fumito Tanaka

The Mitsubishi process is the sole pyrometallurgical process for the continuous production of blister copper from copper concentrates and has been successfully operated around the world. The development of calcium ferrite slag (CaO-FeOx-Cu20), the so-called "C-slag", has enabled continuous converting from matte to blister copper in the commercial scale operations. Commercial interests in the slag led to many papers over the CaO-FeOx slag. However, CU2O- bearing slag has not been studied well due to experimental difficulties. The authors have quantified the thermodynamic properties ofthe CaO-FeOx-Cu2O system. The results have been utilized to analyze various issues related to the converting furnace, such as the magnetite precipitation from the slag or from blister copper and to develop better controlling criteria for the continuous converting operation.

Jan 1, 2003

By R. J. Wesely

The paper describes the various methods which are currently being used or considered to refine gold and silver. These methods are then compared on a technical and economic basis. Conclusions are drawn on the factors which might influence the choice of process for different feed stocks and economic constraints

Jan 1, 1990