Search Documents

By A. William Johnson

It was pointed out in an earlier paper1 that our understanding of the atomic mechanism by which diffusion occurs in metallic alloys is scarcely in an advanced state. This unsatisfactory condition is the result not of any lack of interest, but of the difficulty of designing experiments that .will yield suitable data. The diffusion coefficient of an alloy, measured in the usual way, is simply a number specifying the rate of homogenization of a nonhomo-geneous metal; this number, of itself, can furnish neither the rate at which the individual atoms move nor information as to the mechanism by which they move. It does not necessarily follow, however, that such information cannot be obtained, even if the path to be followed is still not clear. Much success has been attained in the study of diffusion in ionic crystals. A number of experiments, for which there are few counterparts in connection with metals, yield information often indicating a detailed mechanism by which diffusion probably occurs. From such work, quite acceptable theories of lattice imperfections have been developed by Wagner, Schottky, Frenkel, Jost and others.2 It is postulated that real crystals of stoichiometric composition contain, in equilibrium, certain imperfections of which the most importarlt types are: (I) vacant cation sites, with an equal number of interstitial ions; (2) vacant anion sites, with an equal number of interstitial ions; (3) equal numbers of anions and cations in interstitial positions; (4) equal numbers of vacant anion and cation sites. The classification of a particular crystal according to this scheme then follows from studies of the variation of electrical conductivity with pressure of the electronegative component surrounding the crystal, with ion size, and with temperature; other physical phenomena, such as the Hall effect, have aided in establishing the classification. The relative mobility of the anion and cation may be determined by chemical analysis of the salt at the electrodes following electrolysis. With such information, and knowing that one ion never occupies the lattice site normally belonging to an ion of opposite sign, it is usually possible to ascertain the diffusion mechanism. It is clear that the same experiments are not applicable to metal crystals, and substitute experiments that yield as much information have not yet been devised. Much can be learned, however, about the mobilities of the two* kinds of atoms in alloys by the use of radioactive metals as indicators. Only one such experiment has been performed in the past. In 1933, Seith and Keil,3 in an effort to explain the great difference between the rate of diffusion of gold in lead and of lead in lead, measured the rate of diffusion of radioactive lead in 3 gold-lead

Jan 1, 1942

By Dean, R. S.

THE numerous theories of hardening which have been advanced in recent years are all satisfactory in accounting for some of the phenomena observed in hardening metals, but none so far presented account for all of the facts observed. Some years ago one of the authors, R. S. Dean,' presented a theory to account for some of the properties accompanying work hardening. The present paper develops this theory further in the light of recent experimental work and extends it to other forms of hardening. Many of the ideas included have come from the writings and personally communicated thoughts of others. We have attempted to give proper credit in every case, but it is possible that we have not always done so. As an historical basis it is desirable here to review very briefly the hardening theories which have been current. The first comprehensive theory of work-hardening phenomena was due to Sir George Beilby.2 He contributed the idea that with cold work part of the structure of the metal was rendered amorphous and that-it was to this amorphous material that the cold-worked metal owed its difference in properties. According to Beilby's theory this amorphous material was a supercooled liquid and, therefore, had the characteristics of a vitreous material. That such a theory is not capable of explaining the property changes in metals has been repeatedly pointed out. This theory also allowed a slip to take place only once on a given plane, which, as has been pointed out by Jeffries and Archer13 is not consistent with the observed length of an, individual slip and the amount of elongation which can be obtained by wire drawing. The modifications, which have been proposed to this hypothesis to make it coincide with the experimental facts, have to a considerable extent robbed the theory of its clean-cut characteristics. The commonest of these modifications replaces the amorphous phase with an

Jan 1, 1927

By W. C. Meyer

In an effort to conserve and extend oil resources, the use of powdered coal-in-oil mixtures (COM) as an alternate fuel in oil-fired boilers is receiving increasing attention. For the approach to be successful, some degree of stability of the suspension against settling is needed. The variety of means available to achieve stability of this nonaqueous slurry is reviewed along with some of the physical and chemical concepts which underlie each method.

Jan 1, 1983

By William E. Bruce

In recent investigation of drilling processes, the U.S. Bureau of Mines measured the operating characteristics of two percussive drills. Basically, this entailed measuring maximum piston velocities while drilling. The maximum piston velocity is not necessarily the same as the striking velocity. The latter is usually somewhat lower1 because most commonly used drills provide an air cushion which slows the piston just before it comes in contact with the drill rod. Penetration rates for the two drills were determined in nine rock types, and the physical properties of the same nine rocks were measured and tabulated. Then the penetration rates were plotted against the individual properties to determine the general relationships on which methods for predicting drilling rates could be based.2

Jan 1, 1970

By S. L. Hoyt

ABOUT three years ago eight standard steels were prepared for the cooperative investigation of methods for oxygen analysis, sponsored by the Iron and Steel Division of the American Institute of Mining and Metallurgical Engineers and by the National Bureau of Standards. A preliminary report of the results was made at the annual meeting of the A.I.M.E. in February, 1936. ? This report showed the reliability of vacuum-fusion methods and further brought out certain advantages of the fractional vacuum-fusion method. The results obtained by the authors with the latter method will be discussed here, with some com-ments on the procedure for those who are interested in determinations of gases in steel. Some additional comments are offered on the use of the polarizing microscope for identifying the inclusions in the steel to check and amplify the findings of the fractional vacuum-fusion analysis. For details of the fractional method, see the paper by L. Reeve1.

Jan 1, 1937

By William H. Spice

Drilling activities in South Central Texas for the year 1945 continued the steady increase over the past two years, while new fields discovered for the year included four new gas fields and one field extension. In the 30 counties included in this area, which comprises district No. 1, Oil and Gas Division, Railroad Commission of Texas, 141 exploratory wells were completed, compared with 61 drilled in 1944 and 29 drilled in 1943. Of these 141 tests, 55 were field well and 86 were wildcats; 38 were completed as oil wells, S as gas and gas-distillate producers, and 95 were abandoned as dry. Atascosa and McMullen Counties were the most active in the district, accounting for 73 of the wells drilled.

Jan 1, 1946

By Paul B. Crawford, Melvin B. Burton

A procedure is given which describes how the gelatin model may be-used to study the effect of mobility ratio on areas swept before and after breakthrough in fluid injection programs. Differences in mobility ratio are achieved through the proper selection of electrolytes for the invading and displaced fluids. The progress of the front is followed visually and photographed or traced onto plates (it desirrd positions before and after breakthrough. Example applications to standard flooding pattrrrls, vertically and horizontally fractured reservoirs and the in-situ combustion recovery process ore presentrtl. INTRODUCTION In water flooding, gas cycling and other fluid injection programs, the sweep efficiencies and swept areas after breakthrough are known to depend on the mobility ratio. Previous investigators have described the application of the X-ray technique, stepwise use of the poten-tiometric model and numerical procedures for studying these problems.1,3,4,6 Others have described the application of the electrolytic and gelatin models for studying sweep efficiencies at a mobility ratio near one.2,5,7,8,9 It is a purpose of this paper to describe a procedure for using the gelatin model to study swept areas at mobility ratios other than one. PROCEDURE The technique developed for gelatin model studies is composed of four phases: the construction of the model, the selection and preparation of electrolytes, the running procedure, and the recording of the swept areas. Each phase is discussed independently in order that the over-all procedure will not be confused. Construction of the Model Since some of the advantages of the gelatin model are its economy, and speed, it is desirable to have as small a model as is possihle without creating error through the inability to follow visually the progress of the colored front. For this work, it was found that a distance of 4 to 6 cm between salt bridges is convenient to use. Since the size is relatively small, it follows that the gelatin layer must be thin. For this study, 1/8 in. was used as the gelatin thickness in each case. The model was constructed on a flat 1/2-in. plastic (Lucite) base with boundaries constructed from 1/8-in. plastic strips. The well pattern to be studied was outlined with the 1/8-in. plastic strips on the base with narrow apertures (- - 2 mm) in the boundary to represent the wells. Behind each well opening, a rectangular area of some 8 to 12 sq cm was outlined by additional plastic strips. The plastic strips were fastened to the base by any suitable non-conducting cement so that the boundary system was liquid tight. The electrodes were constructed from sheet copper in a fashion that would allow easy removal. In this work, it was found that by simply forming a large U-shaped clip from a strip of the copper that would slip over the boundary was satisfactory and easily removed. The electrodes should be as wide as one of the sides of the rectangular area behind the well opening. If a fractured pattern is studied, fractures inside the well pattern may be represented by strips of copper of the desired shape mounted in some easily removable fashion. The reason that apertures (or salt bridges) were used for wells instead of metallic electrodes is that the plating of the electroactive ion at the cathode and the introduction of an electroactive ion at the anode has a detrimental effect on the swept area outline if these operations \rere permitted to be carried on within the well pattern itself. The anode may be used within the well pattern

Jan 1, 1957

By L. Mair

A STUDY by J. R. Low, Jr.1 on the effect of quench aging on the Charpy-impact specimens of semikilled 1020 steel disclosed that a decrease in cooling rate from 1275°F raised the transition temperature. This was demonstrated in his investigation by controlling the cooling rate of impact specimens to duplicate that of a heavier plate and com- paring the properties with air-cooled specimens and quenched specimens. The transition temperature of the samples that had been cooled at a rate estimated to be similar to that of an air-cooled 3/4 in. plate was approximately 45ºF higher than the quenched samples. The transition temperature of the air-cooled series was between that of the slow-cooled and the quenched series. On the basis of this work, it appeared that the cooling rate of plates after rolling in a hot mill would have a bearing on the brittle fracture of the

Jan 1, 1955

By R. J. Teitel

FOUR or five years ago an investigation was initiated to study and develop basic information on llquid metal fuels for future power nuclear reactors. The objective was to find fluid forms of uranium (solutions or dispersions) in low melting alloys. A summary of the different fuels was presented in a recent article by Teitel, Gurinsky, and Bryner.' The combination of uranium and bismuth, with its low thermal neutron cross section and low melting point, is of basic interest to the development of these fuels. Most of the previous effort on the U-Bi phase diagram was done under security regulation. Ahmann and Baldwin' reported their findings on the U-Bi system in 1945. Their results indicated that the phase diagram had at least two compounds and possibly one more. UBi, and UBi were established by chemical analyses of residues after high temperature centrifugation of alloys. UBi, decomposed peritectically at1980°C and there were signs of another reaction above that. UBi melted at a very high temperature, and there were also signs of a monotectic at high temperatures in high uranium alloys. The solubility of uranium in liquid bismuth has received attention by three groups of authors: Bareis,X ayes and Gordon,' and Ahmann and Baldwin.' The latest and most widely accepted data is that of Bareis, and it is included in Fig. 1 along with new data at higher temperatures. Brewer et al." and Ferro"'' have used X-ray diffraction to determine the number and crystal structure of the compounds. Brewer identified the structure of UBi to be a simple NaCl cubic structure having a cell edge of 6.364A. The density of the compound was calculated to be 11.52 g per cu cm. Two other unindexed patterns were presented as possibly belonging to two other compounds. Ferro agreed with Brewer on the crystal structure of UBi and identified the structure of UBi, and U,Bi,. The intermetallic compound UBi, has a tetragonal cell with a = 4.445A and c = 8.908A. The density of the compound was determined and the number of atoms per cell (six atoms) was calculated. The X-ray density reported was 12.35 g per cu cm. The compound UsBir was treated in a similar way and it was reported to have a cubic structure 9.35A on an edge and to contain 28 atoms per cell. The density was given as 12.59 g per cu cm. Teitel reported that there was a compound UaBi, and no UBi, compound. (The difference in the compositions is 3.3 pct U.) This conclusion was based upon the extrapolation of some 20 tie lines in the

Jan 1, 1958

By V. A. Phillips, M. Safdar Ali

The tensile properties of Cu-0.20 pct Al, Cu-0.45 pct Mg, Cu-0.27 pct Cr, and Cu-0.22 pct Be solid-solution alloys were studied at -196°, 18°, 2509 and 500°C on wires internally oxidized at 900°and 1000°C. Internal oxidation produced marked increases in yield strength relative to pure copper, particularly at low temperature. The yield strength decreased with increase in temperature to a much greater extent than predicted by current theories of dispersion hardening. The strengthening effect of internal oxidation persisted throughout the entire stress-strain curve, but since a marked loss of ductility occurred at all test temperatures, only modest increases in tensile strength were realized. INTERNAL oxidation involves the preferential oxidation of a baser solute in a relatively noble solvent by diffusion of oxygen into the solid. Since the process is diffusion controlled, it is expedient to carry it out at a high temperature often approaching the melting point. The amount of solute is limited and the oxidation conditions adjusted so that oxygen diffuses inwards to meet the solute causing reaction to progress inwards and form subscale instead of only sur face scale. The reaction can be made to occur throughout the thickness of thin material producing a fine dispersion of oxide inside the metal. C. S. Smith1"3 appears to have been the first to recognize the true nature of the process of internal oxidation. Although extensive kinetic and metal-lographic studies followed by Rhines and coworkers,4-5 Chaston7 andMeijering and Druyvesteyn8 working independently were the first to report hardening effects due to internal oxidation. These results prompted detailed studies of the effects of internal oxidation on the hardness, tensile, creep, and fatigue properties of a number of alloys by G. C. Smith and coworkers9-12 in England, on hardness by Gottardi13 in Italy, and on hardness and tensile properties by wood14 in the U.S.A. Publications dealing with other aspects of internal oxidation will not be reviewed here. Internal oxidation of solutes having a high affinity for oxygen provides a means of obtaining very fine dispersions stable in a suitable atmosphere at temperatures well above those at which most age harden ing precipitates coalesce. The process therefore offers a method of producing thin sheet and wire of possibly outstanding creep resistance. The size limitation might be overcome by internally oxidizing porous powder compacts made from alloy powder before final sintering. PREPARATION OF ALLOYS The alloy ingots, which were approximately 5 1/2 in. long by 1 in. diam, were made up in a high-frequency furnace, using as raw materials OFHC copper, 99.99 + pct Al, high-purity magnesium, and master alloys of Cu-4.19 pct Be and Cu-10 pct Cr. The alloys containing aluminum and magnesium were melted ii closed high-purity graphite crucibles and solidified in the crucible which was lowered partly Out of the coil to give a hot-top effect. The alloys containing beryllium and chromium were made by melting in vacuo in alumina-lined sillimanite crucibles. The magnesium, chromium, and beryllium

Jan 1, 1960

By W. L. McMorris, Shiou-Chuan Sun

The Convertol process was first described in Ger- many by Muschenborn1 in 1952. In the U. S. Fraser2 reported this new process in 1953, and Brisse and McMorris-resented the results of a Convertol pilot plant at the Alpheus preparation plant in Gary, W. Va., illustrating the mechanics of the process by a series of sketches. The purpose of the present investigation was threefold: 1) to determine the relative effectiveness of various oils and hydrocarbons for recovering coal by the Convertol process, 2) to ascertain the behavior of coal pulps in this process under various operational conditions, and 3) to compare Convertol with flotation in the recovery of fine coals.

Jan 11, 1959

By AIME

The Taconites Are Ready, the editorial appearing on P. 933 of the September issue, has provoked comment from several informed engineers to the effect that the indicated profit margin was considerably exaggerated. The cost figures in the editorial, taken from the Congressional Record, were characterized as inaccurate by some correspondents. The theme of the story was, however, substantiated in the announcement (P. 1023, October) that Republic and Armco had joined forces in a $160 million project for taconite development. Chief among the dissenters was E. W. Davis, , Director of the Mines Experiment Station at the University of Minnesota. Mr. Davis has worked up the following set of cost figures:

Jan 1, 1950

By G. E. Pellissier, P. H. Salmon Cox, B. G. Reisdorf

Banding that occurred in plates rolled from the early production heats of 18Ni(250) maraging steel is described and related to the segvegation of certain alloying elements (nickel, molybdenum, titanium), the extent of which was quantitatively evaluated by means of electron-microprobe analysis. The effect of banding on mechanical properties is discussed, with particular reference to observed directional differences in plane-strain fracture toughness of plates. It is shown that banding originates as interdendritic segvegation during ingot solidification and persists in some degree through normal soaking and hot reduction to plate. The results of the study showed that heating sections of small laboratory-cast ingots at 2200°F for 4 hr was sufficient to markedly reduce microsegregation and to considerably improve mechanical properties. Hot rolling of 7-in.-thick ingot sections to 1/2-in.-thick plate effected a similar reduction of microsegregation, but resulted in even greater increases in ductility and toughness than that obtained by homogenization treatment alone. DURING the past few years, considerable attention has been directed towards the low-carbon, high-alloy maraging steels and in particular towards the 18Ni-8Co-5Mo-0.4Ti alloy. The steels of this group, having an excellent combination of high strength and toughness, have a number of advantages over their more conventional medium-carbon low-alloy, quenched-and-tempered counterparts. In the annealed condition, the maraging steels are in the form of a ductile marten-site; aging at a relatively low temperature, typically 900°F for 3 hr, increases greatly the strength through the precipitation of intermetallic compounds. One problem in the early production heats of maraging steel was that the finished plate frequently displayed a banded structure. Previous work on other steels1-' had established that banding in wrought products is either a direct or an indirect consequence of chemical segregation, which occurs during solidification and persists to some extent through normal thermal and mechanical treatments. For example, Smith and others: in a study of low-alloy steel, were able to correlate the severity of banding in the wrought product with the degree of interdendritic segregation of nickel and chromium in the as-cast ingot. The effect of banding on the mechanical properties of steels is usually considered to be detrimental, although there is only limited evidence to suggest that a marked improvement in properties can be obtained with less heterogeneous structures. Comparison of the longitudinal and transverse tensile properties of banded and of homogenized 4340 steel showed that only the transverse ductility was improved by homogenization, but even then the improvement was not commercially significant.' Conversely, homogenization of through-the-thickness tension specimens of quenched-and-tempered steel plate, containing 1.47 pct Mn, increased the strength by as much as 10 pct and the tensile ductility by at least a factor of twos5 This improvement was related to the elimination of manganese-rich bands, which also are one of the factors responsible for cold cracking in the heat-affected zone of metal-arc welds.7 In the present study the nature and severity of banding in early commercial 18Ni(250) maraging steel plate and in laboratory-melted 18Ni(250) maraging steel plate was determined. The effects of banding on plane-strain fracture toughness and the effects of thermal homogenization treatments on the strength, tensile ductility, and toughness of 18Ni(250) maraging-steel as-cast ingots and rolled plate were evaluated. In addition, the effects of hot deformation by rolling on the mechanical properties of ingots were determined. 1) STUDIES OF BANDING IN EARLY PRODUCTION PLATE The chemical composition of the steel (A) used in this part of the investigation is shown in Table I. Banding was not clearly evident in either as-rolled or annealed* plate, but annealed and agedc** plate had a banded structure. The typical banded condition, Fig. 1, consists of layers of unetched austenite (white) and dark-etching martensite in a light-etching martensitic matrix. X-ray diffraction measurements showed that this steel contained more than 6 pct austenite. An electron-probe X-ray microanalyzer (using a focused beam of electrons) was used to determine the composition of the bands and of the material between the bands with respect to the main alloying elements— nickel, molybdenum, titanium, and cobalt. The recorded X-ray intensities were converted to concentration values with the use of a standard of similar composition. To facilitate probe positioning, all analyses were conducted on specimens that had been given a light etch. The influence of this etching on the analytical results was negligible; analyses made on the identical area before and after etching yielded essentially the same concentration values. The results of the electron-microprobe analyses at selected points revealed that the layers of austenite and adjacent dark-etching martensite contained greater amounts of nickel, molybdenum, and titanium than did the surrounding matrix, Table 11. The austenite layers

Jan 1, 1968

By RALPH HAYES SWEETSER

ONE per cent. of ash in a ton of coal has been so little considered that in many circles it has been positively ignored. Even P. T. Barnum had never heard of it, or he would have had one on exhibition alongside the Cardiff Giant and the White Elephant. One per cent. of ash is closely related by both those freaks of Barnum in that it is "stone" and, in its aggregate, it is the greatest "White Elephant" that the American public now supports. Some of you may have paid Mr. Barnum for a look at the "petrified man" (named the Cardiff Giant by the gullible wise men of the early seventies); but it is certain that everyone of you is now paying for the support of the great White Elephant that is being constantly carried by our railroads all over the country-at the public's expense. " One per cent. of ash in a ton of coal" requires 120,000 open-top railroad cars each year to transport this use- less stone giant from its native bed in the coal seams of the bituminous regions to the coal bins of the consuming public.

Jan 1, 1924

By J. K. Stanley

Knowledge of the diffusivity of carbon in the low temperature form of iron (alpha iron existing below 910°C) is at the moment of considerable interest in the study of the decomposition of austenite and martensite, the elastic after-effect,123 the magnetic after-effect4 and the decarburization of steel below 910°C. Information on the solubility of carbon in iron, and to a lesser extent its diffusion, is also important in consideration of such phenomena as blue-brittleness, temper-brittleness, "magnetic" aging, quench-aging, strain-aging, and possibly the yield point. In order to obtain more information on these subjects more fundamental knowledge is necessary. It is the purpose of this work to present data on the diffusion and solubility of carbon in the alpha iron. The high temperature form of iron (gamma; face-centered cubic) existing above 910°C is capable of dissolving relatively large amounts of carbon, up to 1.7 pet at 1130°C, while the low temperature form (alpha, body-centered cubic) existing below 910° dissolves only a limited maximum amount of less than 0.02 pet carbon at 725°C, according to data obtained here. Since the solubility of carbon in the face-centered or gamma iron is large, relatively speaking, no great analytical difficulties have been encountered in the determination of the solubility lines5 or of the diffusion of carbon.0 The limited solubility of carbon in alpha iron offers difficulties because experimental procedures and analytical methods for low carbon contents below say 0.01 pet have to be more refined than techniques used for work with gamma iron. Because of the difficulties of applying conventional methods to the determination of the diffusion of carbon in alpha iron, virtually no work has been done on this subject. However, by proper refinement of the analytical method for small amounts of carbon, the determination of the diffusion coefficient can be made readily using modified procedures. The solubility of carbon in alpha iron has been determined over a temperature range by various investigators, but the agreement among them is poor. The present investigation establishes the limits quite accurately. Information of this kind is useful in establishing the correctness of equilibrium diagrams but, more significantly, such information on maximum solubilities, especially when extended to alloyed ferrites, should be extremely important in the study of aging and related phenomena. Literature The literature existing on the diffusion, in particular, and on the solubility of carbon in alpha iron is not extensive. The data which exist are not of a high order of accuracy, much of them being in the realm of conjecture. THE DIFFUSION OF CARBON IN ALPHA IRON Whiteley7 made the qualitative ob- servation, using metallographic techniques, that the rate of diffusion of carbon at the A1 (725°C) point was very rapid and that its diffusion was still rapid at 550°C. Snoek,4 studying the magnetic aftereffect in high purity iron, arrived at the conclusion that the after-effect could be explained by the presence of small amounts of carbon diffusing under the influence of magnetostrictive strain (lattice distortion due to magnetic interaction). In later work, Snoek8 made an estimate of the ratio of carbon diffusion in alpha to its diffusion in gamma iron, and concluded that for a temperature of 910°C the ratio of Da/D? was 2600. Polder,9 basing his calculations of D on relaxation phenomena in the elastic after-effect, estimated that Da is about 1/3 of D? at 910°C (1183°K) and is about 1/12 of Dy at 727°C (1000°K). Polder's equation for the diffusion of carbon in alpha iron was calculated to be 18000 D = 5.2 X 10-4 e-RT cm2 per sec Ham10 obtained data for the diffusion and solid solubility of carbon in alpha iron at two temperatures by using one technique similar to that employed in this study. He found a D of 8.0 X 10-7 cm2 per sec at 702°C and of 2.7 X 10-7 at 648°C. THE SOLUBILITY OF CARBON IN ALPHA IRON Although pearlite is absent in steels containing 0.06 pet,11 0.05 pet,12 or 0.045 pet C,13 it appears that the carbon in these steels cannot be in solution in ferrite. The solubility of carbon at the A1 (725°C) point was first determined by Scott14 on the basis of cooling curves, and was found to be between 0.03 and 0.04 pet C. Tamura15 by interpolating between the solubility of carbon in delta iron at 1400°C and in alpha at room temperature (assuming zero solubility) ar-

Jan 1, 1950

By L. S. Darken, H. A. Wriedt

An investigation has been made of nitrogen absorption by the lattice defects in a low-carbon steel afte~ Plastic deformation. Specimens in which defects were distributed by various combinations of cold rolling and vacuum heat treatment were equilibrated with controlled ammonia + hydrogen mixtures at 300° to 450°C to study the relation between the solubility and the thermodynamic activity of nitrogen. The results are interpreted in terms of nitrogen being absorbed upon two different types of defect sites, called A sites and B sites. The concentrations of these sites are calculated for specimens with various histories of straining and annealing; and the thermodynamic relations descrihing the equilibrium distribution of nitrogen among the A, B, and ordinary interstitial sites in ferrite are evaluated as follows: THE generalization that the solute atoms in a solid solution interact with imperfections in the solvent lattice is now universally recognized and the subject of an extensive literature. All types of imperfections—point, line, or surface—exhibit these interactions, but the relative importance of each type depends upon its concentration, the strength of its interaction with the particular solute atom, and whether the interaction is attractive or repulsive. The strength and sign of the interaction vary with the vectorial displacement of the solute atom from the imperfection in the crystal. The concentration of lattice defects increases during plastic deformation and the effect of the imperfections upon the solute atoms is usually perceived only after cold work or irradiation. Two experimental methods have previously been used to observe the effects of interaction between nitrogen atoms and lattice imperfections in a iron. Internal friction, which was first used for this purpose by Dijkstra,1 has been applied more often than the electrical-resistivity method of Cottrell and Churchman.2 The method of the present investigation has not been used before.* Uniform specimens of steel with a metastable defect structure are produced by cold rolling and subsequent heat treatment below the recrystallization temperature. Variations in the defect structure are obtained by varying the amount of strain and the heat-treatment conditions. The specimens are then saturated with nitrogen at moderately elevated temperatures in ammonia + hydrogen mixtures having various thermodynamic activities of nitrogen below saturation with Fe4N. From the nitrogen contents of analyzed samples, the metastable equilibria of interactions between the defects and nitrogen can be established and the concentration of sites for nitrogen atoms in the lattice defects calculated. A steel was used in the present experiments instead of purified iron or iron alloys because the amount of nitrogen absorbed at defects is larger in the steel over a much wider range of experimental conditions and could therefore be measured more accurately. The effect of alloy composition is discussed in Part II of this paper; it is sufficient to say here that impurities and phase heterogeneity in ferritic alloys favor the generation and/or retention of larger defect concentrations during plastic deformation and annealing at 300° to 500°C. MATERIALS AND EXPERIMENTAL PROCEDURE The experimental specimens were prepared from stock of a low-carbon steel, which will be called "X steel" here, with the composition: C, 0.12 pct; Mn, 0.43 pct; P, 0.010 pct; S, 0.034 pct; Si, 0.007 pct; As, 0.086 pct; Cu, 0.022 pct; Ni, 0.009 pct; Cr, 0.003 pct. The stock was all from a single ingot made by the basic open-hearth process, which was hot-rolled to strip 0.080 in. thick.. This hot-rolled strip, given the code designation "XH", was the starting material for preparing a series of cold-rolled sheets. The latter are designated "XC27",

Jan 1, 1965

By P. W. Bridgman

DURING the war, the Navy undertook the construction, under my direction, of an experimental gun embodying features designed to lessen the cost and time of production. These experiments were initiated after representations as to their, desirability had been offered by myself, by the Naval Consulting Board, and by the National Research Council. The first drawings were made in June, 1917, and the experiment was completed in November, 1918. For the sake of clearness it will pay to recapitulate briefly the fundamental idea of gun construction. It is well known that if a hollow cylinder is subjected to internal fluid pressure, the maximum stress occurs in the inside layers, the outer parts carrying much less than their due share of the stress. This inequality of stress is more pronounced the thicker the walls of the cylinder. If such a cylinder is pushed to the elastic limit, failure in elasticity will take place long before the outer layers have reached the limit of their capacity. Economical use of the material would demand, however, that all parts of the cylinder reach the limits of their capacity simultaneously. This may be brought about, at least in cylinders of not too great thickness, by producing in. the inner layers an initial compression, and in the outer layers an initial tension. The effect of internal pressure is at, first to relieve the compression of the inside layers, while increasing the tension of the outside layers. If the initial stresses are properly distributed, all parts of the cylinder will reach their elastic limits simultaneously, thus giving a cylinder of maximum strength for its weight. In gun construction as hitherto practiced, this initial distribution of stress is produced either by winding the inner tube with wire, a common English practice, or by shrinking hoops over the inner tube, which has been the standard American practice. Either process is long and expensive, particularly with the larger guns, 12- or 14-in., which require

Jan 2, 1920

By AIME AIME

HONORARY COMMITTEE. HON. C. D. WALCOTT (Chairman.), Director U. S. Geological Surrey. HON. FREDERICK I. ALLEN, Commissioner of Patents. DR. FRANK BAKER, Superintendent National Zoological Park. MR. CHARLES A. BELL, President American Security and Trust Co. MAJOR JOHN BIDDLE, Engineer Commissioner of District of Columbia. ADMIRAL C. M. CHESTER, Superintendent U.S. Naval Observatory. GENERAL WILLIAM CROZIER, Chief of Ordnance, U. S. A. ADMIRAL GEORGE DEWEY, Admiral of the Navy. COLONEL CLARENCE R. EDWARDS, Chief Bureau. of Insular Affairs. MR. WILLIAM C. FOX, Director Bureau of American Republics. MR. CHARLES C. GLOVER, President The Riggs National Bank. GENERAL A. W. GREELY, Chief Signal Officer, U. S. A. MR. BERNARD R. GREEN, Superintendent Library Building. GEN. G. H. HARRIES, Vice-President Washington Electric Railway Co. HON. E. A. HITCHCOCK, Secretary of the Interior. COMMANDER H. M. HODGES, Chief Hydrographer, U. S. N. PROF. W. H. HOLMES, Chief Bureau of American. Ethnology. PROF. S. P. LANGLEY, Secretary Smithsonian Institution. GENERAL ALEXANDER MACKENZIE, Chief of Engineers, U. S. A. ADMIRAL N. E. MASON, Chief Bureau of Ordnance, U. S. HON. WM. M. MEREDITH, Director Bureau of Engraving and Printing. HON. V. H. METCALF, Secretary Department of Commerce and Labor. HON. WILLIS L. MOORE, Chief -U. S. Weather Bureau. HON. PAUL MORTON, Secretary of the Navy. MR. F. H. NEWELL, Chief Reclamation Service, U. S. Geological Survey. HON. S. N. D. NORTH, Director Census Office. CAPT. E. C. PENDLETON, Superintendent Naval Gun Factory. MR. GIFFORD PINCHOT, Chief Forester, Department of Agriculture. MR. HERBERT PUTNAM, Librarian of Congress. ADMIRAL CHAS. W. RAE, Chief Bureau of Steam Engineering, U. S. A: MR. RICHARD RATHBUN, Assistant Secretary Smithsonian. Institution. HON. W. T. RICHARDS, Commissioner General Land Office.

Jul 1, 1905

J. E. JOHNSON, JR., New York, N. Y. (communication to the Secretary*).-The discussion of Mr. Henrich's paper took place at a meeting from which I had the misfortune to be absent, and has just come to my attention. I do not wish to let the subject pass without contributing to it a little information which has come into my possession. In 1912, I published a brief note in the Transactions on The Effect of Alumina in Blast-Furnace Slags, giving in tabular form three typical slags used in iron blast-furnace practice, one of them the high alumina slag of, which Professor Richards speaks. That table is reproduced herewith. TABLE 1.-Composition of Slays. 1 3 3 4 5 6 7 CaO by Neutral Ratio Ratio Ratio Al2z03, SiO2, Differ- Substan- Cat Ca0 a A1203 Ratio Per Per ence, ces, CaO Cent. Cent. Per Per Al2O3 + Sioz Sit: SiO2 Cecil_ Cent. Virginia practice 6.5 36.0 54.0 3.5 1.27 1.6S 1.50 Lake-ore practice 13.5 33.0 50.0 3.5 1.08 1.92 1.51 Special experiment... 36.0 24.7 36.8 3.5 0.59 2.90 1.44 It supplies what seems to me convincing evidence that, for the purposes of the iron blast furnace, alumina can be regarded only as a neutral substance, dissolving in the slag and materially altering its viscosity, but not affecting its chemical activity. In subsequent experience with charcoal furnaces, I found the same rule to hold; that the chemical effect of alumina could be disregarded, providing the ratio of the lime and magnesia to the silica were kept constant. This is exactly the experience which Messrs. Dwight and Mathewson had in copper- and' lead-smelting furnaces. I have never seen any evidence or argument adequate to support the contention of Professor Richards-that the alumina acted as a base in the charcoal iron furnace and as an acid in the coke furnace, and that the function of alumina in iron-furnace slags is inherently different from that in copper- and lead-furnace slags-and I am compelled to differ absolutely with his conclusions in that respect.

Jan 9, 1917

Prof. H. O. Hofman, Massachusetts Institute of Technology, Boston, Mass. (communication to the Secretary): When Mr. Stetefeldt quotes me as saying that " silver-assays are uniformly made by scorification," he has evidently not understood that I was referring solely to the practice of silver-lead smelting-works. Everybody knows that silver-mills do not employ the scorification-assay for regular work ; and it is equally certain that in very few, if any, silver-lead smelting-works will the crucible-assay be found in use for determining silver. The second part of the quotation, "as it is adapted to all kinds of ores and gives excellent results unless organic matter is present," although, of course, also intended in a restricted sense, might very well be extended to a general one. Mr. Furman, in his Manual of Practical Assaying,* says, on page 123: "We believe that the Colorado practice is preferable, as most ores will yield higher silver-results by scorification." The fact that the scorification-assay is the accepted one in Colorado is strong presumptive evidence for its accuracy, as exactness would nowhere else be more jealously demanded. Mr. Stetefeldt cites Albert Arents- as a supporter of his preference for the crucible-assay, although I had already done so in favor of scorification. Looking up again the reference, I find that I was justified in quoting him, as, while Mr. Arents advocates the crucibleassay for low-grade gold ores, not on account of the greater accuracy of its results, but because it is quicker and less expensive, he condemns it§ for the assay of silver-ores, and prefers the scorifier for rich goldores, and for coppery ores, and in general for ores containing both silver and gold. As I, like Mr. Stetefeldt, have kept no detailed

Jan 1, 1895