By H. S. Munroe

The native copper of Lake Superior occurs in the form of fine grains and scales, disseminated in small percentage through the copper-bearing rock ; and in large and small masses, from a few pounds to several hundred tons in weight. Formerly the bulk of the copper came from the mines of Ontonagon and Keweenaw counties, producing mass copper. At present these mines furnish less than one-tenth of the total product, and fully one-half of this is from a single mine. The masses are usually found irregularly distributed in nearly vertical fissure veins, and require much dead work; in sinking, drifting, and stoping for their development. The risk and expense attending the working of these mines have made them, with few exceptions, anything but profitable.

Jan 1, 1880

P. E. McKinney,* Washington, D. C.-Observation made after examination of a number of defective gun forgings, together with a history of their manufacture, has strongly suggested that so-called "flakes" and woody or fibrous fractures are not necessarily analogous and are often caused by entirely different conditions. While some flaked bars may show fibrous areas in the fracture, it does not necessarily follow that the conditions causing these areas are the same as cause the fibrous, or so-called laminated, structures so commonly met in gun forgings subject to transverse tensile test; the fibrous structure formed in some flaky bars are merely incidental to the conditions causing the flakes. It is believed that the so-called flakes, or bright silvery spots, are mainly due to inherent physical defects in the steel, which existed at the very origin of the steel, rather than metallographic defects caused by subsequent irregularities in mechanical or thermal treatment. While great care in forging and treatment may, in a measure, tend to overcome the evil effect of the defects, with many heats of ingots, no such precautionary measures are needed to produce perfect forgings- and with such heats of steel it would be impossible, no matter how carelessly handled, to produce intentionally a forging containing the defects commonly known as flakes. It has been found possible, on several occasions, to actually predict flaky forgings from an inspection f the ingot after it had solidified, and in such cases no amount of careful forging or heat treatment would prevent the occurrence of such defects in the forging. The inspection of the physical condition of the ingot, and especially the character of the shrinkage on. the top of the ingot, has been given too little thought and study in this connection.

Jan 5, 1919

By John C. Branner

Stratigraphic Position of the Deposits.—During the progress of the geological survey of Arkansas, in the northern part of that State, it was found that the interval between recognizable Lower Silurian rocks below and recognizable Lower Carboniferous rocks above contains no representatives, or but poor representatives, of the whole Upper Silurian and Devonian series. In some places one passes in the space of a foot from Lower Silurian rocks to the Lower Carboniferous—the Boone chert of the Arkansas survey, or the " Burlington " beds; at other places this interval is 3 or 4 feet thick, but it is generally concealed by the ready decay of the black shale—the Eureka shale—which fills it, so that for a long time it was passed over undetected. It was only after considerable work in the region lying north of the Boston mountains, and by the valuable palzeontologic work of Dr. Henry S. Williams, of Yale University, who kindly accompanied me on a trip through this part of the State, that the importance of this interval came to be recognized, and the thin beds occupying it to be critically studied. It then appeared that this interval was occupied, for the most part, either by a greenish or black shale or by a sandstone; and eventually the sandstone was found to have a maximum thickness of 40 feet on South Sylamore creek in 15 N. 11 W., Section 21. It was, therefore, called Sylamore sandstone. The shale of this interval is generally from 3 to 10 feet thick; it is a constant feature of the geology through Carroll county, and is well exposed in the streets and cuts in and about Eureka Springe, and was for this reason named the Eureka shale. Its maximum thickness is 50 feet in the northwestern part of Benton county. The relations to each other of the Sylamore sandstone and the Eureka shale I have never determined satisfactorily; for

Jan 1, 1897

By W. A. Backofen, D. Lee

Titanium of commercial purity (RC-70) and two all-a (hcp) alloys (4Al-1/4O2 and 5Al-2.5Sn) were tested in sheet form under conditions of combined-stress loading. Plane-strain compression and plane -strain tension together with uniaxial compression and tension provided information for constructing the tension-tension and compression-compression quadvants of the plane-stress yield locus. Coordinate values were obtained from yield-strength measurements; the slope at each point was based on a plastic-strain ratio. The materials represented a wide range of plastic anisotropy, which was reflected in correspondingly varied departures of the yield locus from that for iso-tropy. The tension-tension and compression-compression quadrants were not identical. If the uniaxial yield strength is insensitive to direction and the sign of the applied stress, the Mises or perhaps the Tresca criterion is adequate for predicting the onset of yielding under combined-stress loading. The prediction is not so straightforward in plastically anisotropic material. Depending upon details of texture, combined-stress yielding resistance may be substantially different from that indicated by the usual criteria.' However. a continuum theory of yielding under such conditions is available for reasonably direct application.2,3 Whether or not it can be used successfully must, of course, depend upon how closely the conditions of the theory are satisfied in the material in question. In its present form the theory contains no provision for Bauschinger-type effects, nor does it allow for the consequences that might grow out of deformation by more than one mechanism, e.g., by slip and twinning.4 With those limitations, more importance must be attached to experimental information about the yield surface for anisotropic materials. Studies of the yield surface have generally been confined to states of plane stress (tension-tension and tension-compression) established in thin-wall tubes by externally applied forces and internal pressure. That approach would be entirely suitable for anisotropic materials if they were available in tube form or in sufficient bulk to be machined into test specimens. 6-9 It would not serve for the textured and anisotropic sheets of much current engineering interest, unless sheet could be formed into high-pressure tubing without structural change. Since there would seem to be little chance of the latter, practical alternatives are needed. One such alternative is the subject of this paper. It involves the use of a few selected but relatively simple uniaxial loading tests on sheet specimens. The underlying idea is presented here with some details relating to application and a few results bearing on how well it has worked. THE BASIS OF TESTING Conventional Measurements. Yielding for a general case of anisotropy is described by the plane-stress locus in Fig. 1. Reference directions in the sheet specimen are related to the stress coordinates as shown with the insert: x is the rolling direction, y the transverse direction, and z the through-thickness direction. The four reference-direction yield strengths (t, tension; c, compression), Xt, Xc, Yt, and Yc, are all different. Nine paths that can be followed in uniaxial loading experiments are identified. Paths 1, 2, 3, and 4 represent conventional tension and compression testing to establish Xt, Yt,.Xc, and Yc. Useful information also comes from the ratio of the transverse plastic-strain components associated with yielding and flow in conventional tension or compression. A condition to be satisfied in locus construction is that the plastic-strain vector be everywhere normal to the locus.10 The projection of the vector which would

Jan 1, 1967

By L. F. Mondolfo, B. E. Sundquist

The undercooling associated with the nucleation of the secondary phase from the liquid by the solid primary phase was studied in sixty binary alloys by means of a hot-stage microscope. It was found that in a system of a and ß, a usually nucleates ß at low undercoolings, but ß does not nucleate a, except possibly at undercoolings approaching homogeneous nucleation. This behavior can be explained in terms of relative interfacial energies and shows that crystallographic disregistry is only a minor factor in heterogeneous nucleation from metallic liquids. PREVIOUS experimental work1-6 on nucleation of solids from liquids has shown that normally nucleation is heterogeneous, and that small solid particles present in the liquid are responsible for the nucleation. These experiments and the theory that has evolved from them have made apparent that there is a "characteristic undercooling" associated with the nucleation of the solid from a given liquid by a given impurity. Little is known, however, about the chemical and structural relationships between the nucleating agent and nucleated solid that control the effectiveness of the nucleating agent in catalyzing the nucleation, as measured by the required undercooling. A review of the literature has yielded seventeen undercoolingsL-6 for the nucleation of solid from liquid metals by "known" nucleating agents. All values come from experiments in which the metal studied was divided into a number of particles (10 to 300 pin diam.) much larger than the number of extraneous impurity particles so as to obtain a large number of particles free of foreign nucleating catalysts. Known nucleating agents are then introduced by coating the droplets with particles or a thin film of the catalyst. Six of the seventeen undercooling values referred to cases where, for various reasons, the identity of the nucleating species was not at all certain. Another six cases involved nucleating agents with a crystal structure that was not known. Four other cases involved undercoolings listed as greater than or equal to undercoolings which were very likely those for homogeneous nucleation. One investigation3 involved adding to droplets powdered oxides, carbides, and so forth that were doubtlessly covered with adsorbed oxide or nitride films. The highly variable nature of these films resulted in highly variable undercooling (as was also found in preliminary work in this investigation). It is apparent that the information on heterogeneous nucleation in liquid metals is too limited to give rise to any definite conclusions on the nature of the catalytic process. With these problems in mind a new method was

Jan 1, 1962

By N. J. Grant, H. Brunner

This paber is concerned with the determination of equations relating elongation to the amount of shear taking place both along grain boundaries and in slip planes of poly crystalline aggregates during creep. Certain discrepancies with previously used equations are pointed out. Grain boundaries were observed to become serrated during creep, but it is shown that this does not necessarily prevent further grain boundary sliding. Direct obser-vations of subgrain boundary ingration lead to the conclusion that this migration facilitates sliding along serrated grain boundaries. It is bointed out that the state of stress at triple boints is still unknown. MOST of the mechanisms of deformation contributing to elongation are shear processes, such as slip, kinking, grain boundary sliding, and twinning. For quantitative investigations of individual deformation mechanism it is necessary to know the equation which permits the calculation of speci-tnen elongation from measured amounts of shear. This calculated elongation must then be compared with the observed total elongation. The authors' special interest concerned grain boundary sliding during creep. Although this subject has already been investigated quantitatively by McLean,' Rachinger,' and Fazan, Sherby, and Dorn, calculations indicated that none of the equations used thus far to relate shear with elongation were sufficiently well founded. A basic study of this relationship was thus made and the results of this study (which do not entirely agree with those previously used) are presented. Most of the ideas set forth apply not only to grain boundary sliding but to other mechanisms of shear as well. THE SPEAR-ELONGATION RELATIONSHIP Basic Models—The relationship between shear and elongation is trivial in the simplest case of shear, which is shown in Fig. l(a). The vector A; designates the displacement across the shear interface, and Au, and Aut are its components parallel and normal to the tensile direction, respectively. It is evident that the specimen elongation due to shear is equal to the longitudinal component of the shear vector, and it should be noted that the normal component does not contribute to the elongation of the specimen (there are, of course, two normal components in a three-dimensional model). The model shown in Fig. l(b) may be applied to mechanical twinning and to subgrain boundary tnigration. In this case the width (h) of an already existing shear band increases by the migration of an interface, but the shear angle y (angle of mis-orientation in the case of a subgrain boundary) remains constant. The geometrical relationships indicated in Fig. l(b) permit this case to be reduced to the one shown in Fig. l(a). For the resulting elongation A6 we find: where AV/V = fraction of the volume of the specimen swept by migrating interfaces , and 1 = length of specimen. Thus, assuming for example that the angle of mis-orientation is 1 deg, and that P = 45 deg, we find that the specimen elongates 0.87 pct of its length if the entire volume of the specimen is swept once by such a subgrain boundary. An example of deformation by migration of subgrain boundaries is shown in Fig. 2. The specimen shown was repolished after 9.8 pct creep strain and the test then continued for another \ pct. Since the shear vector has, in general, a component normal to the surface, subgrain boundary migration results in the formation of an inclined band delineating the region swept by the subgrain boundary. These inclined bands become clearly visible when observed with oblique illumina-

Jan 1, 1960

By D. W. Levinson, L. F. Mondolfo, N. A. Gjostein

MANY investigations are reported in the literature on the age hardening of Al-Mg-Zn alloys but most of them are concerned mainly with mechanical property changes. The present investigation was started to determine the structural changes in an AlMgZn alloy. The alloy composition was chosen in the existing phase diagram" so as to lie on the quasi-binary section Al-(AlZn)Mg Actually, it was found that the diagram as published was inexact at the lower temperatures and that the phase in equilibrium with aluminum at the lower temperatures is not the ternary compound. Technique The alloy used for the investigation was prepared from high purity materials and the resulting composition as determined by chemical and spectro-graphic analysis was: Zn, 6.17 pct; Mg, 2.13 pct; CU, 0.03 pct; Si, 0.009 pct; Fe, 0.005 pct; and the remainder, aluminum. An ingot -in. thick was cast, homogenized, hot and cold-rolled to strip 0.064-in. thick for dilato-metric and powder work, and to foil 0.005-in. thick for single crystal work. Solution treatment temperature for all specimens was 475°±5°C for periods of at least 1 hr, either in air furnaces or lead baths. Aging was done in oil or Pb-Bi baths controlled to within ±3°C. The aging was investigated at the following temperatures: room (30°), 130°, ZOO0, 260°, and 300°C. For the dilatometric study, the length changes were measured continuously, at temperature, using strips of alloy 10 in. long, shaped as channels to eliminate undesirable deflection due to bending. To compensate for thermal expansion and contraction due to the variations in the temperature of the aging baths, the dilatometers were built of the same alloy as the one being tested, with the same shape and size, but with material fully annealed. Gages on which 0.0005 in. could be read and 0.0001 in. estimated were used to measure the dilation. Length changes were also measured at room temperature. Strips approximately 10 in. long were solution-treated, quenched, and measured in a supermicrome-ter in which 0.0001 in. could be read and 0.00001 in. estimated. The specimens were immediately aged for a given time, remeasured, and then the cycle was repeated, including the solution treatment. The error of measurement with this technique was somewhat larger, but the results confirmed those obtained by continuous measurements. The sheet used for the dilatometric work was checked to determine grain orientation. Both X-rays and etching methods revealed a rather coarse grain size but only a negligible amount of preferred orientation. Thus, volume changes calculated from length changes are not invalidated by preferential orientation effects. Pieces of the sheet used for the dilatometric work were also used for the metal -lographic work. Filings for the powder X-ray study were produced from a homogenized piece of sheet. These filings were magnetically purged of iron, screened to 200 mesh, sealed in a Pyrex tube containing an argon atmosphere, and solution-treated. When quenching, the glass tube was broken, so that the powder dropped directly into cold water. After drying with alcohol, the powder was sealed into capillary tubes containing an argon atmosphere and then aged for the required times. In spite of all these precautions the three strongest lines of a( Al2o) appeared in all patterns, and were used as internal standards. By the use of these standards, accurate corrections for film shrinkage were obtained. For the back reflection patterns, annealed nickel powder was mixed with the specimen to act as internal standard. A preliminary investigation was made in small (57.3 mm diam) powder cameras. From these patterns the changes which took place in the solid-

Jan 1, 1957

By L. R. Raymond, J. L. Hudson

This paper proposes a comparatively short-term (8 to 10 hours) well test for detecting and characterizing well-bore damage and for measuring mean formation permeability. The proposed test is made by injecting fluid at constant pressure, recording injection rate as a function of injection time. After one to four hours of injection, the well is shut in and fall-off of bottom-hole pressure is obtained as a function of shut-in time. Formation permeability is estimated by an iterative technique. First, a value of formation permeability is assumed. Then, a plot of the recorded injection rate as a function of dimensionless time is made, using the assumed pertneability value. From the slope of the injection-rate curve. a new value of formation permeability is calculated. If the new value agrees with the original assumed value, the assumption was the correct formation permeability. If the values do not agree, the process is repeated using the new permeability value in the calculation. Convergence is rapid, and a reliable permeability value results. Pressure fall-off data are used to check the result. Graphs of pressure and injection rate us functions of time given in the paper show that changes in permeability of the formation in the neighborhood of the wellbore are disclosed by this technique. Thus, the short-term test can he used to detect formation damage. Also, a rough measure of the radial extent of damage can be inferred, which is helpful in designing stimulation treatments. The mathematical model used for this work was a single-zone, horizontal reservoir with a damaged zone in which permeability decreased continuously as radial distance to the wellbore decreased. This model is more realistic than the usual two-zone, discontinuous permeability model used in published works; calculations indicate the realistic model is valid. Vertical variations in horizontal permeability were studied with this model, and results indicate that the permeability measured by the short-term test is the mean horizontal permeability for the vertical interval tested. The proposed short-term test thus should be useful in detecting and characterizing formation damage and in measuring formation permeability needed in calculating reservoir transmissibility. INTRODUCTION To plan the most efficient production or injection schedule for a well and to design or evaluate the optimal stimu- lation treatment, it is necessary to know the properties of the reservoir adjacent to the well, particularly the reservoir transmissibility and characteristics of a damaged zone, if one exists. Several techniques for determining reservoir transmissi-bility from well tests have been presented in the literature. 1,2,3,4 All these techniques rely on conducting constant-rate well tests that often are difficult to execute. A constant-pressure well test is generally easier to carry Out. and this paper contains the first available method for the analysis of constant-pressure well tests. Determination of wellbore damage from transient well tests has been the subject of several papers."" From these studies it is apparent that information necessary for determination of the characteristics of a damaged zone is available shortly after the transient well test is initiated. Consequently, it may not be necessary to carry out an extensive well test (for example, a pressure build-up test) if the primary purpose of the test is to detect the existence of wellbore damage. All previous studies of well testing to determine wellbore damage have been based on the two-zone perrneability model. In this model the damaged zone has a permeability k,, extending to a radius r,,, and the formation permeability k obtains from r, to the drainage radius r,.. Consequently, there is a discontinuity in permeability at r = r,,. This discontinuity can be eliminated by assuming a continuous variation in permeability through the damaged zone. The effect of this assumption on transient well tests is discussed in following sections of this paper. In addition, all formations have within them vertical permeability variations associated with lithology changes throughout the zone of interest. This paper also considers the effect of these variations on transient well tests. ANALYSIS OF CONSTANT-PRESSURE WELL TESTS The mathematical analysis associated with the injection of fluid at constant wellbore pressure into a single-zone, horizontal reservoir completely filled with a fluid of small and constant compressibility and constant viscosity is given in Appendix A. In this analysis it is assumed that the well is located at the center of an undamaged, circular drainage area. From this analysis, the formation permeability can be obtained as follows. 1, Estimate a value for the formation permeability k. 2. Prepare a plot of injection rate q vs

Jan 1, 1967

By H. Conrad, E. Stofel

The fracture behavior of 60-deg-oriented sapphire crystals was investigated for both tension and compression. Plastic flow on the basal plane was found to be a factor in reducing the tensile stress required to produce fracture in the temperature RECENT experiments1-' have shown that single crystals of a alumina (sapphire) can deform plastically, particularly at temperatures greater than 1000°C. The effect of this plastic flow on the fracture behavior of sapphire was not established, but range 1100º to 1500ºC. Mechanical twins, both (0001) and (0111) types, were produced by compression in the temperature range 1100" to 1300°C. Cracks propagated more readily along the twin boundaries than in the nontwinned crystal. experiments with other ceramic crystals4'5 have shown that plastic flow can initiate cracks that lead to catastrophic failure. This suggests by analogy that plastic flow might also be an important factor in the fracture of sapphire crystals. A recent experimental investigationS undertaken to determine the mechanism of plastic flow in sapphire provided an opportunity to study the type of fracture produced after various amounts of plastic shear strain. The results of this study of fracture are reported in the present paper. During the course of

Jan 1, 1963

By J. W. Mitchell

Season cracking of 70-30 cartridge brass cases of small arms and artillery ammunition has been under investigation at the Frankford Arsenal for many years. The nature of this stress-corrosion failure has been found to be intergranular. Much of this work, however, has been directed toward improvements in method of manufacturing the cases so as to reduce the tendency to season crack and little progress had been made toward finding the source of the chemical agent producing the inter- granular corrosion. Ammonia has been shown to produce season cracking in brass and is known to be present in certain atmospheres, particularly industrial, in sufficient concentration to cause cracking. However, in the case of small arms ammunition, the hypothesis that atmospheric ammonia is the cause will not hold, since small arms ammunition is hermetically sealed during storage and yet occasional lots are found to have cracked after 3 to 5 yr. storage. Much of the early study of season cracking in small arms ammunition was done by Nicholas H. Murdza of the Frank- ford Arsenal. In 1936, he suggested that the corrosive agent might be one of the decomposition products of smokeless powder and mentioned nitrogen oxides specifically. Then in 1937, Murdza suggested that the breakdown of smokeless powder in storage resulted in the formation not only of nitrogen oxides but also ammonia

Jan 1, 1945

By G. C. Hancock

The operating plant of The Broken Hill Associated Smelters Pty. Ltd. is situated at Port Pirie in South Australia and it treats to finality the whole output of lead concentrates from the mines of The Zinc Corporation Ltd., North Broken Hill Ltd., and aroken Hill South Ltd. at Broken Hill, New South Wales. Lead bearing ores from other sources are also purchased for treatment and lead scrap and residues are treated on a toll charge basis. The present output of the plant is approximately 200000 tonnes of refined lead per annum and there is a substantial production of by-products including refined silver, gold, cadmium, antimonial lead alloys, copper matte and sulphuric acid. Recently the Company commenced the production of zinc by slag fuming and electrolysis from a six million ton dump of lead blast furnace slag, which has been accumulating at Port Pirie for over fifty years. The slag fuming plant contains two furnaces of conventional design, but features a high degree of pre-heat for the blast air and this is obtained by the use of all-metal recuperators. The raw zinc oxide fume produced by the plant is roasted in a rotary kiln prior to treatment in the leaching and electrolysis sections, which follow conventional practice for nigh current density plants. Present output is approximately 36000 tonnes of electrolytic zinc per annum.

Jan 1, 1970

By Harlowe Hardinge

The sound made by ball, pebble and rod mills has long been used by the operator as the "telltale" of their operation. The nature of this sound depends upon local conditions and the type of mill used. By experience an operator can tell whether the mill is running properly or not. Some operators are able to detect the difference in sound much better than others and get better results running the same mill under the same conditions. The automatic operation of a mill using sound as the fundamental means for maintaining control presents many problems. The satisfactory solution of these problems requires, for given operating conditions, a greater average output, with improved product for subsequent processing, than can be obtained by manual control. Relation of Sound to Useful Grinding Energy Experience has taught us that there is a difference in character as well as in intensity of sound between a mill grinding wet and one grinding dry, in open or closed circuit, to obtain a coarse or fine product, on the same material, to say nothing of the effect with a variety of different materials. Broadly speaking, a wet-grinding mill operates best at a lower sound level than the same mill grinding dry, with other conditions the same. Several reasons for this variation in sound intensity under these conditions can be advanced, but the important point is that there is a difference, based upon practical results. Since these reasons may be more or less involved, and may be subject, to much discussion, only one will be considered here. It is apparent that two balls hitting together or a ball striking the lining, if there is no intervening material, will produce the maximum sound. If a complete cushion of material is placed between the balls or ball and liner, so that the energy is dissipated without doing useful work, the balls will be unable to create enough pressure or force to fracture the particles, and the sound will be at a minimum. At some point in between—that is, where there is sufficient material between the balls or ball and liner so that the ball will fracture the particles without mashing them unduly—the sound

Jan 1, 1939

By G. A. Moore, D. W. Williams, C. E. Sims

During the past several years, the steel casting industry has made studies of heavy castings in which the test bar has been taken from heavy sections rather than from attached or separately cast coupons. It has been noted that the ductility properties of these heavy sections are often lower than those normally expected. Such lowered ductility is usually accompanied by a spotty test bar fracture, and the ductility values can often be greatly improved if a low-temperature aging treatment is given to the casting. A loss of ductility of this type is considered "abnormal," since it is not accompanied by an increase of tensile strength or hardness, and "temporary" when the ductility can be restored by aging. The cure of such an abnormal condition represents a real improvement in the quality of the steel. Several types of abnormal loss of duetility can be distinguished, of which those caused by excessive amounts of inclusions of undesirable type and those caused by unsuitable grain size and inget structure are well known. The particular type of abnormal lowered ductility currently under consideration may be distinguished by the fact that the low-temperature aging treatment necessary for its relief is insufficient to cause any visible change in the micro-structure as ordinarily observed. As this aging will in fact eventually occur at room temperature, the phenomenon of present interest may be given the symptomatic definition, ''Temporary Abnormal Low Ductility." Some hundreds of previous investigations, largely qualitative in nature, have established, beyond reasonable doubt, that hydrogen is normally present in newly manufactured steel and that this gas, in small amounts, can cause a temporary abnormal loss of ductility. The commonly observed association of high gas content and low ductility has given strong evidence for the presumption that hydrogen, possibly assisted by other gases, is the primary cause of the low ductility observed. Accordingly, The Steel Founders' Society of America has, since Nov. 1, 1944, sponsored investigations at Battelle Memorial Institute whose primary objective is to obtain quantitative information on the relation of the amount of hydrogen and nitrogen in steel, together with associated methods of steelmaking and treatment, to low-duetility effects and porosity. The interest of this investigation thus extends to permanent abnormal losses of ductility, such as are caused by the inclusions which sometimes result from special deoxidizing practices and possibly from metallic nitrides, but as these can he distinguished from the temporary effect of hydrogen, they have been excluded from the work reported here except when they

Jan 1, 1949

By E. O. Jones

DURING the heating of cold-worked nickel silver, the tendency of the material to crack is well known. The present research deals with this question, and may conveniently be divided into the following sections: Changes in these alloys during heating and cooling, determination of the temperature at which cracking occurs, effect of grain size, quenching cracks, methods of overcoming annealing cracking. The work is far from complete, in particular the influence of impurities on this tendency has not been investigated, but the results so far obtained lead to certain definite conclusions, which are of theoretical and practical importance. CHANGES IN ALLOYS DURING HEATING AND COOLING During the annealing of many metals at a temperature just below that at which recrystallization sets in, there is evidence of some change, the effect of which is to harden and embrittle the material. This effect has been most clearly demonstrated in the cases of aluminum, copper, brass, and nickel silver, and appears to be a common property of cold-worked metals and alloys, or, at any rate, the non-ferrous ones. The effect would obviously offer an explanation for certain types of annealing cracking, but the trouble is so much more common in the nickel silvers than in the other alloys that some special cause should be looked for. There is, however, fairly good reason for believing that similar cracking may occur in some of the brasses; D. Bunting suggests that the a brasses toward the saturation limit are subject to a transformation closely allied in nature to that known to occur in the nickel silvers at around 320° C. Although the existence of this critical temperature range was known, it did not necessarily follow that this transformation was responsible for the trouble under investigation, so the first portion of this paper deals with the attempts made to determine whether other critical changes might not occur in these alloys. There were already reasons for the belief that such would prove to be the case, as the mechanical properties of the nickel

Jan 7, 1925

By L. S. Darken

It has been known for sometime that in an ionic lattice, such as that of Ag,S or FeO, the migration velocity of the anion may differ markedly from that of the cation, the cation being usually the more mobile. It has been shown, for example, that during the formation of silver sulphide tarnish on silver, the tarnish layer grows principally by the motion of silver cations through an essentially stationary silver sulphide lattice. Similarly, the growth of wüstite scale on iron proceeds principally by motion of iron ions, this being accomplished with the aid of vacant iron lattice sites into which the iron may readily move. Likewise investigations of solid solutions of various salts show that there is usually considerable difference in the mobility of the different cations. Measurements of the mobility of various metals in liquid mercury indicate that the various metals move at different rates relative to the mercury. In view of the foregoing it seems reasonable to suppose that when any single phase solution is acted upon by a field, the atoms of different elements respond in different ways; in particular, that the force arising from a particular concentration gradient in a binary alloy would cause the atoms of one component to move with a drift velocity which is in general different from that of the atoms of the other component. The recent experiments of Smigelskas and Kirkendall' support this viewpoint, since they found, in essence, that during diffusion in alpha brass zinc moves appreciably faster than copper. This was evidenced by the relative motion of inert molybdenum wires. Such a phenomenon is incompatible with the place interchange theory of diffdsion proposed by several authors, most recently by Bir-chenall and Mehl.2 This theory has, however, also been questioned3v4 for other reasons, principally because of the high energy required for direct atomic interchange. The rather large difference between self-diffusivity, as determined by tracer technique, and mutual diffusivity, as determined with the aid of another element at low concentration, might also be interpreted as favoring the above idea; however. Birchenall and Mehl have pointed out that there is another possible interpretation of this difference; this is discussed later. A rather interesting and pertinent observation was made by Schwartz, who noticed that tungsten lamp filaments, heated by direct current, commonly fail by necking down in the region at the temperature gradient near the positive end, with a concomitant swelling at the corresponding position near the negative end. He introduces considerable auxiliary evidence to show that this phenomenon is occasioned by the motion of tungsten cations which migrate in the high temperature region from the positive end toward the negative end. The mechanism of this migration is not clearly understood. If, however, this experimental evidence be accepted, we are forced to conclude that alloying elements in the tungsten may migrate by the same or a Similar mechanism, whatever it may be, at a greater Or lesser rate, thus giving rise

Jan 1, 1949

By L. S. Darken

It has been known for sometime that in an ionic lattice, such as that of Ag,S or FeO, the migration velocity of the anion may differ markedly from that of the cation, the cation being usually the more mobile. It has been shown, for example, that during the formation of silver sulphide tarnish on silver, the tarnish layer grows principally by the motion of silver cations through an essentially stationary silver sulphide lattice. Similarly, the growth of wüstite scale on iron proceeds principally by motion of iron ions, this being accomplished with the aid of vacant iron lattice sites into which the iron may readily move. Likewise investigations of solid solutions of various salts show that there is usually considerable difference in the mobility of the different cations. Measurements of the mobility of various metals in liquid mercury indicate that the various metals move at different rates relative to the mercury. In view of the foregoing it seems reasonable to suppose that when any single phase solution is acted upon by a field, the atoms of different elements respond in different ways; in particular, that the force arising from a particular concentration gradient in a binary alloy would cause the atoms of one component to move with a drift velocity which is in general different from that of the atoms of the other component. The recent experiments of Smigelskas and Kirkendall' support this viewpoint, since they found, in essence, that during diffusion in alpha brass zinc moves appreciably faster than copper. This was evidenced by the relative motion of inert molybdenum wires. Such a phenomenon is incompatible with the place interchange theory of diffdsion proposed by several authors, most recently by Bir-chenall and Mehl.2 This theory has, however, also been questioned3v4 for other reasons, principally because of the high energy required for direct atomic interchange. The rather large difference between self-diffusivity, as determined by tracer technique, and mutual diffusivity, as determined with the aid of another element at low concentration, might also be interpreted as favoring the above idea; however. Birchenall and Mehl have pointed out that there is another possible interpretation of this difference; this is discussed later. A rather interesting and pertinent observation was made by Schwartz, who noticed that tungsten lamp filaments, heated by direct current, commonly fail by necking down in the region at the temperature gradient near the positive end, with a concomitant swelling at the corresponding position near the negative end. He introduces considerable auxiliary evidence to show that this phenomenon is occasioned by the motion of tungsten cations which migrate in the high temperature region from the positive end toward the negative end. The mechanism of this migration is not clearly understood. If, however, this experimental evidence be accepted, we are forced to conclude that alloying elements in the tungsten may migrate by the same or a Similar mechanism, whatever it may be, at a greater Or lesser rate, thus giving rise

Jan 1, 1949

By C. A. Heiland W. E. Pugh

The principle underlying the majority of magnetic intensity variometers is a comparison of the force to be measured with another force of known magnitude. The known force may be (a) of a magnetic nature, such as magnetic fields produced by magnets or coils, or (b) of a mechanical nature, such as (1) the elastic forces of wires, or (2) the force of gravity, such as employed in bifilar magnetometers and magnetic balances. In instruments of such type, usually a magnetic system is employed, free to move about either a horizontal or vertical axis, on some sort of a suspension. If the earth's magnetic field alone were present, such a system would adjust itself into the direction of the field or that of its components. Owing to the simultaneous action of the comparison force, however, the magnetic needle assumes a position that differs from the direction of the magnetic force; for all such instruments, the angle of deflection is given by tan = FIX, where F is the known and X the unknown earth magnetic force component. In other words, the magnetic system merely serves as an "indicator" for the position of balance of the two forces. Considering the matter from this point of view, it is not immediately obvious why the temperature of such a magnetic system should modify the results. In magnetic instruments, we may distinguish two different effects of temperature: (1) a magnetic effect and (2) a mechanical effect. The first is due to the fact that the magnetic moment of a magnet drops with an increase in temperature. This drop is characterized by the temperature coefficient of the magnetic moment (see equation 1). The second effect is due to the change in the torsion of suspension wires with temperature or to the expansion of lever arms of masses acting on magnetic balances.

Jan 1, 1934

By J. R. Cain

In every process for making steel there are one or more stages where the metal is exposed to gas of one kind or another. Thus, in the open-hearth furnace, the carbon dioxide and water vapor in the products of combustion are oxidizing toward the ferrous and manganous oxides in the slag, tending to convert these to higher oxides; the higher oxides then , oxidize the steel, so that indirectly the products of combustion are oxidizing toward the steel. In the Bessemer process, there is direct contact of air and steel; also, the water vapor in the air blown into the converter is continually decomposed by the molten steel, yielding hydrogen and ferrous oxide, both of which are in part taken up by the metal. In the electric-furnace processes, there is always more or less air in contact with the slag covering the metal, and this air and the gaseous reaction products from it are dissolved in the slag to some extent and thus transmitted in part to the steel. In the crucible processes, there is always entrapped air in the charges and the crucibles are more or less permeable to the gaseous products of combustion from the furnace. In all the processes of manufacture, the molten metal is exposed to air while tapping into ladles and ingot molds and has an opportunity to saturate itself with air or with gaseous or solid products generated by chemical reactions between air and steel. Sievertsl has shown that molten metals requirc but a few seconds to saturate themselves with a surrounding gas. No one familiar with the operations at a steel plant needs to be reminded of the important role that gases play at all stages. The familiar "boil" of open-hearth furnaces, due to evolution of carbon monoxide when iron ore is added to the molten steel; the spectacular operation of the Bessemer converter brought about entirely by a gaseous reagent; the almost magic effect of small quantities of silicon, manganese, or aluminum added to the molten metal in ladle or furnace in quickly preventing bubbling and evolution of gases; the unwelcome phenomena of blowholes in ingots that have not been properly manufactured—these

Jan 1, 1920

By G. H. Clevenger

(Continuing the discussion of the paper of James Johnston, presented at the New York meeting, February, 1914, and printed in Bulletin No. 85, January, 1914, pp. 107 to 133.) This paper cannot fail of being of great interest and value to all who are interested in the cyanide process, on account of the important developments which it records. Mr. Johnston is to be commended for the large amount of detail which he gives, and the company and its management for permitting the publication of data of this character, which while of great value to others could well be considered private property. It might be discussed from a number of standpoints: First, as an example of recent practice in mill and cyanide plant construction; second, the mill practice; third, the cyanide practice; and fourth, the new features in cyanide treatment involved. Perhaps a more vivid way of expressing it would be : First, the equipment or tools with which the various operations are carried on, are they the best and most efficient which could have been selected for their respective uses; and, second, is the best use in every case made of these tools? It may be well inquired is the highest possible recovery of silver made at the lowest cost per ounce recovered? For after all, the making of the greatest ultimate profit is inseparably associated with successful metallurgical practice; there must therefore be at all times a careful balance maintained between recovery and cost of obtaining it. I wish to call attention in a very general way to the equipment used and to an anticipation of questions which are bound to arise in this connection. However, the. bulk of my discussion will be confined to the presentation of certain additional data, together with a more or less general discussion showing the line of development which leads up to the present practice and .the applicability of certain features of it to similar problems elsewhere. There are a number of vital points of broad general interest involved in Nipissing low-grade practice upon which metallurgists will by no means be agreed to which I wish to call particular attention in the hope that it will lead to the presentation of data y others of practice in other districts which will' assist in reconciling this divergence of opinion.

Jan 7, 1914

By S. F. Emmons

IT was said by many who discussed Professor Posepny's admirable paper on the " Genesis of Ore-Deposits," read at the Chicago meeting of the Institute, in 1893, that its most valuable feature was the clear distinction which it drew between the influence upon ore-deposits of the "vadose " circulation of waters descending directly from the surface, and that of the deep underground circulation of waters generally coming from the depths, and assumed by the author to be ascending through more or less open spaces under the influence of heat. A little later the effect of the oxidizing action of the vadose circulation upon ore-deposits was ably and exhaustively treated by Prof. R. A. F. Penrose, in a paper on " The Superficial Alteration of Ore-Deposits "f-the only one, so far as I know, which has been exclusively devoted to this important subject. My own first detailed study of ore-deposits was made at Leadville, in 1880, at a time when almost the only minerals visible in those deposits were in oxidized forms. That this form was the result of the alteration of earlier sulphides by surface-waters had to be proved at the time by induction or analogy, the general correctness of which was, however, abundantly confirmed by subsequent developments. Thus I was early impressed with the importance of distinguishing, in the study of an ore-deposit, the alteration-products, resulting from the action of oxidizing waters descending from the present surface, from the earlier-formed sulphides; and, assuming that the latter were primary or original, I called the former secondary. I also went so far as to say$ with regard to oxidized ores passing into sulphides in depth "So generally is this accepted as a rule in ore-deposits that it would require special demonstration to prove beyond a doubt that the native metals or their

Jan 1, 1902