By M. B. Bever, A. B. Michael

The solidification of aluminum-rich aluminum-copper alloys was investigated for different solidification rates. The measured amounts of nonequilibrium eutectic were compared with the amounts calculated on the assumption of no diffusion in the solid. The morphology of the eutectic was studied and dendritic spacings were measured. Compositions of the cored primary solid solutions were determined by quantitative autoradiography after activation of the solute copper by neutron irradiation. CONSIDERABLE progress has been made in recent years toward an understanding of the solidification of metals. This is especially true for the factors involved in nucleation, the controlled growth of metal crystals from melts, and various aspects of the freezing of ingots and castings. Many features of the solidification process, however, are not understood adequately and much further work is required. In the research reported here the solidification of a series of aluminum-rich aluminum-copper alloys was investigated. Different degrees of deviation from the idealized case of equilibrium solidification were attained by varying the rate of solidification. Thermal analysis and microscopic examination were supplemented by lineal analysis and autoradiography. The latter required the use of radioactive tracers and was adapted to the quantitative determination on a microscale of concentrations of copper dissolved in aluminum. The tracers were produced in situ by activating the copper with neutrons. These techniques permitted a correlated interpretation of the temperature-time history, the amounts of nonequilibrium eutectic and the general morphology of the alloys, and yielded quantitative data on microsegregation. Nonequilibrium Solidification In the general case of the solidification of a solid solution in accordance with the phase diagram, the composition of the coexisting liquid and solid must change continuously. This change requires diffusion, which at best remains incomplete in the solid during solidification. The resulting inhomogeneity of the solid solution crystals is well-known as coring, dendritic segregation, or microsegregation. The generally accepted analysis of coring assumes that, 1—no diffusion occurs in the solid, 2—diffusion is complete in the liquid, and 3—the composition of the solid formed on cooling through any infinitesimal temperature interval is given by the solidus of the phase diagram. On this basis, In this equation m designates mass, x designates the concentration of solute and the subscripts L and S refer to the liquid and solid phases, respectively; the subscript o indicates the initial state, in which the liquid is identical with the entire system. Eq. 1 or its equivalent has been derived repeatedly'-7 and an analogous equation, known as Rayleigh's equation, has been used for distillation. The assumptions on which Eq. 1 is based do not include an infinitely fast cooling rate as sometimes stated. In fact, Olsen and Hultgren %ave shown by experiment that very high solidification rates suppress coring, presumably by preventing diffusion in the liquid and by the effect undercooling has on the composition of the nucleus. Coring thus occurs at rates of cooling which are too fast for a close approach to equilibrium in the solid and too slow to suppress diffusion in the liquid and to cause marked undercooling. If the liquidus and solidus approximate straight lines, Eq. 1 simplifies to The fraction of liquid present at any temperature during nonequilibrium solidification can be calculated from Eqs. 1 or 2. By the lever relation it is

Jan 1, 1955

By J. G. Y. Chow, S. B. McRickard

The tensi1e properties of Ferrovac iron have been studied from 4° to 300°K. The stress required for macroscopic yielding was found to he constant below approximately 50°K. The effect of mechanical twinning on this low -temperature stress plateau was investigated. The onset of twinning occurs in this iron between 130° and 150°K and depending on its previous thermal history the twinning-stress curue may drop below or remain above the vield-stress curves as the temperature is lowered. Twinning has been shown to initiate slip in quenclzed iron at low temperatures. In no instances, however, did the onset of twinning alter the continuity of the yield stress -tempwature curve. Our data shows that carbon inhibits twinning and slip at low tem-peratures. This observation nay be used to explain the ductile-to-brittle transition in iron. The effect of fast neutron irradiation on yielding and embrittlement in iron and Fe-C alloys is offered as supporting evidence for this viewpoint. THE mode of yielding in iron at low temperatures was studied in an attempt to find an expression based on a single mechanism to describe the thermal dependence of the yield stress of iron. There are two types of inflections observed in the variation of the yield stress with temperature in iron and Fe-C alloys. The first is associated with ductile behavior and consists of a region extending 50" to 100°K above absolute zero in which the yield stress is independent of temperature. The second is observed in more brittle materials such as Fe-C alloys and irradiated iron and consists of an abrupt discontinuity in the yield curve as the temperature is lowered through a ductile-to-brittle transition point. The temperature dependence of the yield stress for iron with four grain diameters as found in this study is shown in Fig. 1. To varying degrees all the curves appear to flatten or approach an asymptotic value as the temperature is lowered below 50°K. Several other investigators1,2 have observed a plateau in the yield stress of iron and steel at low temperatures and in 1956 Louat3 presented a theory which contained an explanation for this behavior. In a subsequent exchange with Erickson and Low4'5 who attributed the plateau to the onset of mechanical twinning Louat8 showed that twinning first occurs in iron and steel tested in tension at temperatures as high as 140°K which is well above the observed plateau in yield stress. Furthermore he pointed out that both twinning and slip are basically dislocation processes and that with modified parameters his original theory still applied when deformation is initiated by twinning. Variables which affect the ductile-to-brittle transition in iron are test temperature, strain rate, composition and grain size.7 LOW,8 Hahn et al.,9 and Hull10 have provided evidence which links brittle fracture at a given temperature with the specimen grain size and the onset of twinning. In fact, Hull equates the brittle fracture stress to the twinning stress. On the other hand brittle fracture has been observed in the absence of twinning and priestnerl1 has given a fracture criterion which is valid whether or not fracture is preceded by extensive twinning. The data presented here clarify the role of twinning in the low-temperature deformation of iron. Strong evidence is given that the amount and distribution of interstitial impurities such as carbon are of

Jan 1, 1965

By R. A. Burton, J. T. Hansford, D. A. T. Donohue

Substantial evidence indicates that many petroleum producing horizons contain naturally occurring, ordered fracture systems and that within a particular geologic zone, vertical fractures induced in wellbores often will be directed along a particular compass direction. Both conditions will seriously alter the fluid displacement behavior within reservoirs. In this study the effect of induced fracture orientation and length on sweep efficiency is determined for a five-spot pattern. In general, it is assumed that all wells are fractured and directed along the same compass direction. Using the electrical analog to steady state, two-dimensional fluid flow in porous media, boundary conditions are obtained from which flood fronts are tracked numerically. The numerical computations require a particle tracking routine for approximating flood front histories. It is shown that recovery is sensitive to the length and orientation of fractures for the pattern studied. with the proper design of fracture-pattern systems, recovery can be enhanced considerably. INTRODUCTION Hydraulic fracturing introduced in 1949l gave the industry a rather inexpensive means of increasing the fluid injection or production capacity of wells. It has been used with particular success to increase the production rate of wells completed in tight formations, such as in western pennsylvania2 where producers have fractured in depleted or near-depleted fields and observed economic responses. Once the natural energy declines in such a reservoir where all wells have been fractured, waterflooding is generally suggested as means of further increasing recovery. Of the dual objective sought in waterflooding — high injectivity and high breakthrough sweep efficiency — the former condition can be obtained if all wells in the flood pattern are fractured; the latter condition should depend on the nature of the fracture system. Considerable theoretical work has been published on the nature of fractures induced in boreholes.3-5 Although discussion persists concerning the possibility of forming a horizontal fracture at a given point within the wellbore, it is generally conceded that only vertical fractures will develop below a given depth, i.e., where the fracturing Pressure is less than the overburden load. Given the fact that fractures will be vertical in most cases of interest, it is also important to know whether there is order to fracture orientations within a given geological region. Kehle has suggested that in tectonically relaxed areas of uncomplicated geology, the stresses are fairly uniform and all fractures in the region should be parallel.5 Dunlap arrived at a similar conclusion in a theoretical investigation of localized stress conditions surrounding the borehole.6 He concluded that most vertical fractures are propagated in a preferred azimuthal direction. Fraser and Pettitt, in extending these theoretical suggestions to a specific field case, used an impression packer to record both a vertical fracture and the orientation of this fracture in the wellbore of a well in the Howard Glasscock field, Tex.7 Use of this information enhanced the waterflood recovery of the field. Anderson and Stahl also used impression packers on three fractured wells in the Allegheny field. N. Y.. and found that the fractures were oriented more or less along the same compass direction.8 Orientation of the fractures in this manner depends on the stress condition within the formation during fracturing. Elkins and Skov have demonstrated that a natural, oriented, vertical fracture system exists within the Spraberry field? Heck suggests

Jan 1, 1969

By F. E. Streigert, J. H. Mallery, A. H. Geisler

The existing data on precipitation in Cu-Be alloys have been reconciled with some new data to present a more complete and rational analysis of the atomic rearrangements involved in the process. Two different coherent precipitates were proposed. Each is responsible for a type of diffuse X-ray diffraction effect. THE nature of the atomic rearrangement involved in the precipitation of the compound y-Cu-Be from supersaturated solid solutions of the copper-base alloys has been the subject of two extensive investigations.'-" he precipitate in this alloy system has a rather simple structure; at equilibrium it has a body-centered cubic unit cell with copper atoms on the corner sites and beryllium atoms on the center site. While a simple mechanism would be expected to obtain for the precipitation process, those which have been proposed do not adequately explain all of the reported data. The purpose of the present report is to rationalize some of the previous observations and to contribute new data on the subject obtained by the usual techniques of structure analyses. The Cu-Be system of alloys represents one of the most extensively investigated precipitation systems, so a detailed review of the pertinent literature on structure is in order. Striations: Since one of the important features of the mechanism—the habit plane—is determined by microscopic examination, microstructural features that have been observed should be considered at this time in order to assess their role in the precipitation process in Cu-Be alloys. One of the most prominent features appears as regularly oriented markings or stripings (ripples or striations) across the crystals on a suitably polished and etched sample of the aged alloy. These have been observed and interpreted by many workers. Masing and Dah14 observed striations in both the a and /3 phases of a 2.5 pct Be alloy, and attributed them to the beginning of the precipitation of very fine y crystals along favored planes of the a matrix and to the local decomposition of the £ crystals into a plus y. These markings were apparent in both the a and /3 phases of the micrographs given by Smith5 for a 2.75 pct Be alloy, while Moore" detected them in the a matrix phase using polarized light. Desch7 attributed the markings to fine precipitate particles lined up on a family of matrix planes like Masing and Dahl had done, and he identified the planes as those of the (111) family, the slip planes of the matrix. The striations were presumably the structure which Northcott- eferred to as "martensitic." He found that this structure was present in samples that had been aged under widely different conditions with hardness values ranging from 160 to 400 VHN. Later Guinier and Jacquet' also found striations in both the a matrix and secondary /3 phase. Their analyses showed that the striations were along (110) planes of the matrix phase, apparently in contradiction of the results of Desch. They found that the striations were developed during aging on the surface of a specimen that had been polished prior to aging.' On this basis they concluded that the striations represented mechanical deformation by slip along (110) planes of the matrix resulting from precipitation stresses.'" Similar but fainter striations were observed in the same manner on an A1-Cu alloy sample, in which the change in volume was much less than for Cu-Be alloys and

Jan 1, 1953

By Mark J. Klein, A. H. Clauer

The Snoek peak induced by solute nitrogen in chromium was studied. A rapid quenching rate is required to maintain nitvogen in solution in sufficient concentrations to be detectable by internal-friction techniques. An expression for the tertninal solubility, c, of nitrogen in weight pevcent is log,,c = -4130/T + 1.05. The diffusion of nitrogen in zhromium determined by internal friction is SNOEK&apos;S theory1 of the stress-induced ordering of interstitial solute elements in the bcc lattice has been used to deduce information on the behavior of interstitials in a number of bcc metals. Under the proper conditions, internal-friction studies of "Snoek peaks" permit a determination of diffu-sivities, solubilities, and precipitation kinetics of interstitial elements. Internal-friction studies of this type have been reviewed by Nowick,&apos; Wert,= Powers and Doyle,4 and others. The behavior of interstitial atoms in Group V-A metals and iron has been rather extensively studied in this way, and results are reasonably self-consistent. However, the study of interstitial elements using internal friction in the Group VI-A metals—tungsten, molybdenum, and chromium—is much less clear. Thus far, internal-friction studies have revealed a peak in tungsten tentatively attributed to carbon5 and a peak in chromium associated with nitrogen. In chromium, Bungardt and Preisendanz6 observed a peak at 180°C for a frequency of -1 cps which they associated with nitrogen. More recently, de Morton7 determined the diffusivity of nitrogen in chromium from studies of a nitrogen peak at 160°c for a frequency of -1 cps and from elastic aftereffect measurements. The objective of this investigation was to study the nitrogen peak in greater detail, to obtain information on the behavior of nitrogen in chromium. This information is of interest because nitrogen is known to have an embrittling effect on chromium. However, efforts to deduce the role played by nitrogen in influencing the mechanical behavior of chromium are handicapped by lack of information on its behavior and distribution in chromium. EXPERIMENTAL PROCEDURES The chromium wires used in these studies were drawn from arc-melted iodide-chromium stock that had been extruded, swaged, and centerless-ground to 0.25 in.-diameter rods. Internal-friction measurements were made in an evacuated torsional pendulum similar to the one described by Kê,8 utilizing wires 0.048 to 0.030 in. in diameter. A series of analyses of the fabricated wires showed that the major impurities were approximately 100 ppm Fe and a combined interstitial content of 50 to 100 ppm C, O, N, and H. A typical interstitial analysis of the wires after processing is 15 ppm C, 2 ppm H, 50 ppm O, and < 5 ppm N. Interstitial concentrations were determined by vacuum-fusion, combustion-conductimetric, and micro-Kjeldahl analyses. In general, vacuum-fusion analysis yielded a lower nitrogen concentration than did micro-Kjeldahl analysis. For consistency, the nitrogen concentrations reported in this investigation were determined by the former method. Heat treatments were carried out by encapsulating the specimens in quartz tubes containing argon. The fabricated wires were annealed at 1150°C for 1 hr to produce uniform recrystallized grain size of about 0.015 mm. Nitrogen and carbon were added to the fabricated wires by encapsulating them in a quartz tube containing ammonia or methane, and annealing them at 1150°C for 48 hr. In some instances, carbon was also introduced by coating the wires with carbon black prior to annealing.

Jan 1, 1965

By H. R. Brannon, R. J. Robinson, G. W. Kattawar

Accurate prediction of storm wave characteristics are needed for design of offshore structures. Statistical methods of random noise analysis provide techniques for predicting required wave properties. These techniques have been used to analyze and characterize storm wave profiles from Gulf of Mexico recording installations in 34, 65 and .98 ft of water. Correlations based on the results can be used to predict wave crest probabilities and wave shapes for a range of Gulf water depths and storm conditions. Example predictions of wave crest probability as a function of water depth for a particular set of storm conditions are given. INTRODUCTION Accurate predictions of wave crests and wave shapes are needed for design of offshore structures. With predictions of wave crests, platform deck elevations giving adequate protection from exposure to storm waves can be selected. Use of hydro-dynamic wave theories with the wave crest and wave shape predictions permits an estimate of the wave forces an offshore structure must withstand. Observation of ocean waves suggests use of statistical analysis for studying wave characteristics for water depths beyond the breaking wave zone; recent wave generation theories lend support to this approach. l-3 One of the most powerful methods of statistically analyzing wave profiles was introduced by Cartwright and Longuet-Higgins; most of the basic relations used were developed by Rice5.6 in studies of random noise theory. This method predicts wave crest elevation probabilities from two parameters characterizing a wave profile. The statistical approach also provides a means for predicting wave shapes. In the random noise model of a wave profile, surface elevation is represented as an infinite sum of sine waves with closely spaced frequencies and random phase angles. Power density is proportional to the sum of the squares of the amplitudes of sine waves having frequencies within a narrow band, and the distribution of power density as a function of frequency is called the power density spectrum, or power spectrum. The power spectrum characterizes an irregular sea, and hence finds use in motion studies of ships, barges and semisubmersible drilling platforms. From the power spectrum, a wave profile of any duration of time can, in principle, be calculated; this long wave profile depicts the many wave shapes to which a structure may be exposed. Thus, the statistical methods of wave analysis provide an approach to selecting wave shapes as well as wave crest elevations needed for design of offshore structures. For practical application of these techniques, power spectra and related quantities must be predicted from storm properties. Barber and Tucker 7 have reviewed correlations of wave properties and storm conditions. Their review summarizes work of Darbyshire,8 among others, in which a correlation of power spectra with wind intensity of the North Atlantic was developed. These results, plus more recent work by Pierson and Moskowitz and Kitaigorodskii,10 establish feasibility of correlation, but there is no theoretical basis for modifications extending the relations to other areas as remote as the Gulf of Mexico. Hence, to predict characteristics of Gulf of Mexico waves, a study of local observations is needed. This paper presents (1) a practical approach to computing wave profiles hat depict shapes of waves for use in force calculations, (2) a summary of relations for predicting probabilities of wave crest elevations, (3) correlations of parameters needed to apply these methods in the Gulf of Mexico and (4) examples of application of the techniques. THEORETICAL BACKGROUND The following sections summarize relations needed to calculate wave profiles and to estimate wave crest probabilities. These relations also identify quantities that must be related to storm

By C. W. Phillips, D. N. Frey

A commercial Ti-Fe-Cr alloy, Ti-150, exhibits a martensitic transformation on cooling and two nucleation and growth reactions, one above and one below the Mg-Mf region, on isothermal holding below the single-phase ß temperature range. The reactions were followed by metallographic, X-ray diffraction, and microhardness methods. THE rapidly expanding engineering application of titanium and its alloys makes increasingly urgent an adequate knowledge of the effect of heat treatment on this material. The work herein reported is an attempt to determine certain aspects of the behavior of a commercially available alloy, Ti-150, during heat treatment. The alloy, with a nominal composition of 2.7 pct Cr, 1.3 pct Fe, 0.25 pct 0, 0.02 pct N, and 0.02 pct C, was received in the as-rolled condition as a 3/4 in. round. Slugs 0.11 to 0.12 in. thick were cut under a coolant using a silicon carbide wheel. Preliminary work established that the alloy consists of two phases, a (hexagonal close-packed) and /3 (body-centered cubic), at temperatures below 1750" to 1775"F, and of only /3 phase at higher temperatures. The slugs were heated for 1 hr in air at 1800°F to form a single-phase /3 matrix, then transferred to molten tin (1250° to 1650°F) or lead (1150°F and below) for isothermal holding. Holding temperatures ranged from 700° to 1650°F, times from 0.001 to 23 hr. The treated slugs were then sectioned, one part for metallographic examination and diamond pyramid hardness, the other, after deep etching to remove the high oxygen surface,&apos; for comparative lattice parameter determination and X-ray phase identification. Hardness measurements were taken on the lightly etched surfaces of the metallographic specimens; a 1000 g load on a 136° diamond pyramid was used. Five impressions on each sample were made and the average of the hardness calculated. The use of microhardness measurements to follow the course of an isothermal transformation reaction is undesirable because of the possibility of wide differences in microconstituent hardness.&apos; They were used in this case, however, because of the small amount of material available. At the higher transformation temperatures, where the above-mentioned objection was apparent, the readings were proportioned to correspond to the estimated ratio of transformed and untransformed constituents present. At lower temperatures, resulting in much finer microconstituents, the microhardness measurements were more uniform. The standard deviation of the mean of five impressions calculated from these latter values was 4.2 DPH. Employing 2a limits (probability 0.95) the experimental error of the hardness measurements averages was 8.4 DPH. The etchant used was composed of one part glyc-erol and one part 48 pct hydrofluoric acid." Of a number of etches tried, this one appeared most satisfactory. All micrographs were taken at 500X magnification and with oblique lighting to permit easier identification of the acicular structure resulting from rapid cooling. No advantage was gained by using polarized light for metallographic examination. Phase identification and lattice parameter measurements were made with a North American Philips high angle spectrometer in conjunction with a recording potentiometer. Considerable difficulty was encountered with some of the lattice parameter measurements because of the extreme broadness of the few diffraction lines obtained from samples consisting mainly of strained, untempered, quenched structures.

Jan 1, 1953

By C. L. Sollenberger, Will Mitchell, Ford F. Miskell

Heat treatment of ore prior to comminution reduces power requirements for grinding, reduces grinding media wear, and improves recovery of iron values from a typical Minnesota magnetic taconite. Test data demonstrating this, as well as an analysis of the economics of commercial application of the technique, are presented. THE taconites in general are hard, tough ores, difficult to grind. Liberation of iron mineral constituents usually is accomplished by grinding the ore through at least 100 mesh, and often it has been found necessary to grind substantially through 325 mesh to achieve satisfactory recovery and grade in the concentration process. Because of the fineness of grind required and the enormous tonnages of material contemplated for treatment in the future, costs resulting from grinding media wear and power consumption, together with capital investment required for comminution, approach astronomical figures. Economy in any one of these elements per ton of material ground could very well reflect a considerable saving to the ferrous industry in yearly costs. With this in mind, the Research Laboratories of Allis-Chalmers Manufacturing Co. have launched a program to discover means of effecting this economy. The initial phase of the work as described here deals with a heat treatment of crushed raw ore, followed by thermal shock in cooling, for the preparation of rod mill feed. Several investigators1-" ave noted an improvement in the grindabilities of ores treated in this manner. One investigator2 subjected low grade iron ores to heat treatment in an electric furnace. Basing his conclusions on screen analyses of crushed products, he observed that treated ore was more easily crushed than the untreated. He reported that observation of the treated and untreated ore through a microscope revealed cracks following the grain boundaries in treated ore, whereas no cracks were present in untreated ore. However, few if any have quantified the improvement in terms of total hp hours saved, reduction of wear of grinding media, or reduction of capital costs of grinding equipment involved. By means of Bond rod mill and ball mill grindabilitiesh nd by comparative wear tests, the conditions maintained during this investigation have been definitely evaluated. Heat treatment experiments have been made on a batch scale in a muffle furnace, followed by continuous scale experiments in a rotary kiln under various conditions of temperature, atmosphere, retention time, and quenching to determine the combination that would give the greatest improvement in the grindability of a taconite without affecting adversely the magnetic susceptibility of the magnetite. From these data, relative costs have been calculated for grinding both untreated and heat- treated ore on a basis of plant capacity of 120 tons per hour. Heat requirements for a rotary kiln, as well as the kiln capacity required for the treatment, have been estimated. For these tests 50 tons of ore were obtained from the Aurora mine of the Erie Mining Co., Hibbing, Minn. The ore was reported7 to have been selected from the magnetic portion of the lower chert horizons. An average chemical analysis of&apos; this portion is shown in Table I and an approximate mineralogi-cal analysis is shown in Table 11. No attempt was made to differentiate between the various silicates because the compositions vary widely on the different horizons and depend on the degree of oxidation. Minnesotite, however, is the predominant silicate. The siderite grains were dispersed throughout the ore but were essentially associated with the rock-forming minerals. In a series of preliminary tests in which batches of —6 mesh ore were heat-treated in a muffle fur-

Jan 1, 1953

By Will Mitchell, Ford F. Miskell, C. L. Sollenberger

Heat treatment of ore prior to comminution reduces power requirements for grinding, reduces grinding media wear, and improves recovery of iron values from a typical Minnesota magnetic taconite. Test data demonstrating this, as well as an analysis of the economics of commercial application of the technique, are presented. THE taconites in general are hard, tough ores, difficult to grind. Liberation of iron mineral constituents usually is accomplished by grinding the ore through at least 100 mesh, and often it has been found necessary to grind substantially through 325 mesh to achieve satisfactory recovery and grade in the concentration process. Because of the fineness of grind required and the enormous tonnages of material contemplated for treatment in the future, costs resulting from grinding media wear and power consumption, together with capital investment required for comminution, approach astronomical figures. Economy in any one of these elements per ton of material ground could very well reflect a considerable saving to the ferrous industry in yearly costs. With this in mind, the Research Laboratories of Allis-Chalmers Manufacturing Co. have launched a program to discover means of effecting this economy. The initial phase of the work as described here deals with a heat treatment of crushed raw ore, followed by thermal shock in cooling, for the preparation of rod mill feed. Several investigators1-" ave noted an improvement in the grindabilities of ores treated in this manner. One investigator2 subjected low grade iron ores to heat treatment in an electric furnace. Basing his conclusions on screen analyses of crushed products, he observed that treated ore was more easily crushed than the untreated. He reported that observation of the treated and untreated ore through a microscope revealed cracks following the grain boundaries in treated ore, whereas no cracks were present in untreated ore. However, few if any have quantified the improvement in terms of total hp hours saved, reduction of wear of grinding media, or reduction of capital costs of grinding equipment involved. By means of Bond rod mill and ball mill grindabilitiesh nd by comparative wear tests, the conditions maintained during this investigation have been definitely evaluated. Heat treatment experiments have been made on a batch scale in a muffle furnace, followed by continuous scale experiments in a rotary kiln under various conditions of temperature, atmosphere, retention time, and quenching to determine the combination that would give the greatest improvement in the grindability of a taconite without affecting adversely the magnetic susceptibility of the magnetite. From these data, relative costs have been calculated for grinding both untreated and heat- treated ore on a basis of plant capacity of 120 tons per hour. Heat requirements for a rotary kiln, as well as the kiln capacity required for the treatment, have been estimated. For these tests 50 tons of ore were obtained from the Aurora mine of the Erie Mining Co., Hibbing, Minn. The ore was reported7 to have been selected from the magnetic portion of the lower chert horizons. An average chemical analysis of&apos; this portion is shown in Table I and an approximate mineralogi-cal analysis is shown in Table 11. No attempt was made to differentiate between the various silicates because the compositions vary widely on the different horizons and depend on the degree of oxidation. Minnesotite, however, is the predominant silicate. The siderite grains were dispersed throughout the ore but were essentially associated with the rock-forming minerals. In a series of preliminary tests in which batches of —6 mesh ore were heat-treated in a muffle fur-

Jan 1, 1953

By J. L. Huitt, IM. L. Slusser, E. E. Glenn, M. L. Slusser

This paper is concerned with: (1) an analysis and interpretation of the filtration characteristics of drilling muds on filter paper, and (2) an interpretation of early stage "filtration" on consolidated synthetic porous media, herein referred to as the "surge loss" period. It is shown that water-loss data can be plotted so as to disclose the existence of a surge period, a non-uni-form cake thickness period, and a constant pressure filtration period. The same periods occur during exposure of consolidated porous media to muds. The data on consolidated porous media indicate that: (1) mud particles bridge pores inside porous media during the surge period, and (2) "filter cake" build-up inside porous media occurs during subsequent filtration. The data also show that the surge loss increases with sample permeability and with pressure differential. INTRODUCTION The phenomenon of mud filtrate invasion into porous sands of a drilling well has been recognized for many years.1,2,3,4 Part of API Code 29 is concerned with the filtration testing of a drilling mud to yield data on this subject. In a number of investigations "plastering properties" of muds were studied,5,6,7,8 "plastering" apparently meaning cake forming properties. In such studies the characteristics (thickness, permeability, and toughness) of the cake and the rate at which the liquid phase of the mud was separated from the solids (filtration rate through the cake, commonly referred to as water loss) were measured or at least considered. From the standpoint of its effect on well productivity, filtrate invasion into "clean" water-wet pay sands (i.e., those containing no clay minerals) may not necessarily be a serious problem. An increase in water saturation in the zone immediately around the wellbore would cause loss of oil permeability. However, in such a system, much of this water may be removed by oil production. If filtration occurs into "dirty" sands (i.e., those containing appreciable clay minerals), clay swelling or other mechanisms may cause losses in oil permeability which cannot be overcome by oil production.&apos;.&apos; The phenomenon of mud particle invasion into the pay sand of a drilling well was considered to be a possible serious factor in the early days of rotary drilling. Opinions varied as to whether drilling fluids "mudded up" and "sealed" oil sands. In 1932 Rubel,9 Gill,10 and Parsons," in separate papers, presented differences of opinion together with some laboratory and field data concerning loss of oil production caused by drilling fluid invasion into pay zones. These papers, and the discussions, furnish a large background on this subject and indicate the very clear thinking of many men at a time when petroleum production technology was in its infancy. Jones and Babson,6 and Silent,&apos; experimentally found that the depth to which mud particles invaded water-saturated sand packs was small (no greater than 1/16 in). Arn-quist12 in 1937 observed loss of water permeability due to invasion of mud particles into water-saturated, consolidated, sandstone samples. Williams and Cannon5 studied the filtra-tion properties of drilling muds and mentioned "sludge" which penetrated a short distance into the water-saturated filtering medium (sand pack). Byck5 concluded that formation permeability had no effect on the plas-

Jan 1, 1958

By R. R. Goddard

By use of the frequency response method with a radioactive tracer, it was possible to determine fluid dispersion and distribution in a natural consolidated and an unconsolidated medium. Measurements were made in a linear flow system at oleic saturations of 69 per cent in the consolidated medium, and 100 per cent in both media. Dispersion and distribution were obtained by measuring the amplitude attenuation and the phase velocity of sinusoidal waves with a dual monitor apparatus. The gamma ray emissions permitted in situ measurements at any distance along the porous samples. One result of importance was that the effective diffusivity increased as the wave length increased. As a consequence, a dispersion coefficient appropriate for the injection of large slugs might exceed the value measured by use of small slugs. Since flow models based solely on fluid velocity and an effective diffusivity coefficient imply that the diffusivity should be independent of frequency, such representations were not adequate for the data of this study. A comparison was made with a capacitance model of porous media with deadend PVs, but even this model was not completely adequate. By using attenuation and phase velocity data, fluid dispersion can be predicted without postulating a differential equation satisfied by the tracer concentration, thereby eliminating the need of a complicated model to represent dispersion. INTRODUCTION The flow of similar miscible fluids through a porous medium can be fairly adequately described by two parameters: the average fluid velocity and the effective diffusivity.1-3 It has been pointed out recently, however, that significant discrepancies exist between this representation and the experimental data.4-7 An improved agreement can be obtained by introducing additional parameters based on the concept of dead-end pores. The purpose of the present investigation was to find out whether the frequency response method could be used to measure the relevant parameters. The method was used in the following form. A stream of fluid was flowed at a constant rate through a sample of porous material and the concentration of a radioactive tracer in the fluid was varied sinusoidally at a fixed frequency. The effects of flow through a porous medium are a decrease in the amplitude of the concentration wave and an increase in the velocity of the peaks of the waves above the average velocity. Attenuation and phase veIocity of the waves were measured as a function of frequency and fluid velocity. The simple two-parameter model implies that the diffusivity should be independent of frequency. Data reported in this paper show that the diffusivity decreases as the frequency increases. Hence, as shown also by many others, the two-parameter model is not completely adequate. Coats and Smith 5 used two additional parameters in their model: the volume of the dead-end pores and the rate of mass transfer between dead-end pores and the flowing stream. Their capacitance model of a porous medium containing some stagnant fluid, to which transfer occurs by molecular diffusion, did not explain the dispersion results of either the present study or of theirs. Instead, the capacitance effect can be better described as the result of extreme velocity variations within the pores of the medium, with transfer between the velocity zones by convection. EXPERIMENTAL PREPARATION OF POROUS MEDIA Data reported here were obtained with a natural Berea sandstone, and with two packings of 20/25 mesh sand. Pertinent information about these media is listed in Table 1. The sandstone core was first sealed with a non-

Jan 1, 1967

By A. E. Powers

YEARS of experience and research have shown that molybdenum, tungsten, and vanadium are among the most useful and effective elements in augmenting the high-temperature strength of heat-treatable, ferritic steels. Grün, for example, in conducting an early survey of the strengthening effects of various elements in annealed, low-carbon steel at 750° and 930°F (400° and 500°C), found molybdenum and vanadium to be the most effective.&apos; Holtmann comprehensively studied the strengthening effects of molybdenum and vanadium in quenched and tempered steels at 930°F as a function of microstructure and carbon content.&apos; He found creep strength to be related to the saturation of the austenite at the austenitizing temperature, such that strength is increased by alloying until the y loop is reached—the terminus of complete austenitization. Beyond this degree of alloying, the inability to heat treat will result in lower strength, at least for low and moderate creep temperatures. Tungsten, owing to higher cost than molybdenum, has been little used in ferritic high-temperature steels. As a result, very few investigations have been made of its high-temperature strengthening ability, and reliable data on its effectiveness are not available. Grün rated tungsten far less effective than molybdenum at 930°F (500°C) on a weight-percentage basis.&apos; However, Tammann has found that tungsten is as effective as molybdenum in raising the recrystallization temperature of iron. For this reason Smith, in a review of the subject, has advocated a re-examination of the influence of tungsten on the high-temperature strength of steel.&apos; In any study of the effects of alloying additions on high-temperature properties, recognition must be made of the many variables involved, some of which can be controlled but have been ignored in innumerable investigations of the past, and some of which are difficult or even impossible to control. One cannot, for example, assign a definite strengthening index to any one alloying element, for this will be dependent upon the microstructure (heat treatment and mechanical treatment), testing con- ditions (temperature, time, and stress), and the complete composition of the steel (accompanying alloying elements, impurities, etc.). One ever-appear ing variable, hardness or tensile strength at room temperature, may be eliminated by heat treating all of the alloys to a single hardness level. An attempt may be made to control the variable of primary quenched structure by oil or water quenching the test specimen. The control of such variables may not be possible in cases of widely varying compositions, but at least such deviations should be recognized. Material and Procedure The alloys, made as 30-lb ingots in an induction furnace, all had the same base composition of about 0.18 pct C, 0.85 pct Mn, and 0.48 pct Si. They were grouped as follows: Mo Group—Containing up to 5.2 pct Mo. W Group-Containing up to 6.0 pct W. V Group—Containing up to 3.3 pct V. Mo-V Group—Containing up to 2.7 pct Mo and up to 1.4 pct V. Mo-W Group—Containing up to 2.5 pct Mo and up to 2.5 pct W. The steels, listed in Table I, were forged to ¾ in. sq bars and the material for the high-temperature, rupture-test specimens was further swaged to %-in. round bars.

Jan 1, 1957

By Fritz Wald, Martin Weinstein, Herbert E. Bates

ONE of the methods for preparing a fiber-reinforced composite is that of directional solidification of a eutectic melt. Its major drawback lies in the fact that the matrix in this case is a pure constituent (or a terminal solid solution of fixed concentration) and the ratio of fiber to matrix volume is fixed. Only very few, if any, pure metal matrices possess technically useful properties, and the necessity for alloying is the inevitable consequence of this fact. Nevertheless, structures similar to binary eutectic ones can be obtained in higher-order systems by pseudoeutectic reactions of a type where crystallites and a solid-solution matrix are simultaneously precipitated from a liquid.1"3 Trials to solidify such alloys directionally—the matrix consisting of a solid solution of chromium, nickel, and silicon and the reinforcing phase being Cr3C2— will be reported elsewhere.4 This note describes constitutional studies carried out primarily to determine -the position of the pseudoeutectic and further to insure that no undesirable reactions between the reinforcing phase and components of the matrix occur in the solid state at elevated temperatures. In the investigation it was specifically desired to reinforce a matrix which is as close as possible to the 80/20 Nichrome composition with Cr3C2 to insure good oxidation resistance and improve the strength at high temperatures. No konstitutional information on the quaternary C-Cr-Ni-Si svstem in the range of interest was found in the literature. Nevertheless, the two most important ternaries c-cr-Ni5 and have been completely investigated. On C-Cr-Si some investigations have been conducted,7"9 and C-Ni-Si was studied with a few alloys in the course of the present investination 9 Eight alloys were prepared to investigate the changes in the constitution of the ternary C-Cr3Ce-yNi eutectic5 with silicon contents up to 10 wt pct. Five alloys were made with varying chromium and carbon contents around compositions containing -60 to 70 wt pct Ni and 5 to 6 wt pct Si. The latter alloys were designed to locate the y(Ni-Cr-Si-C)-Cr3C2 pseudoeutectic reaction and to determine the maximum chromium content in solid solution compatible with a two-phase equilibrium between y and Cr3C2 only. The alloys were prepared from electrolyte nickel, semiconductor-grade silicon, high-purity chromium (99.999 pct pellets), and semiconductor-grade graphite. They were melted inductively in high-purity alumina crucibles under flowing argon. Twenty-gram charges were prepared and investigated by optical microscopy (including hot-stage investigations), X-ray powder methods, and electronmicroprobe analysis. The alloys were studied in the as-cast condition and also after a homogenization annealing treatment of 48 days at 900°C in evacuated quartz ampoules. The structures of all alloys based on the ternary eutectic plus silicon in the as-cast state consisted generally of an inhomogeneous solid solution and at least two other phases. Annealing of the alloys showed that the solid solution was homogenized but that an incomplete solid-state reaction had taken place in all alloys with silicon contents over 5 wt pct. This reaction is clearly visible in Fig. 1 around the large Cr3C2 crystals (gray areas). Below this concentration, the alloys consisted of a homogeneous matrix and precipitates of Cr3C2 plus graphite, Fig. 2. The Cr3C2 was entirely unreacted here. From these observations and subsequent X-ray and microprobe investigations, it was deduced that the

Jan 1, 1969

By C. J. Ramsburg

THE construction and operation of by-product coke-oven plants in America are essential to strong national defense and of the greatest importance to many widely diversified undertakings as well as to safety and health. CARBONIZATION PROCESS Coal used under a boiler or in a locomotive is consumed by combustion. Coal used in a by-product oven is distilled or carbonized, meaning that heat is applied to the coal, out of contact with air, causing a distillation that removes the volatile matter in the coal in the form of gas and vapor, leaving coke as a final product. From the gas and vapor distilled from the coal, many valuable substances can be secured, known as by-products. Hence the name "by-product oven." The simplest example of this principle can be shown by means of an ordinary clay pipe. If powdered coal is placed in the bowl of the pipe, the opening of the bowl is plugged with clay, and the bowl placed in a flame, the bowl will become hot, transferring the heat through the wall of the bowl to the coal within. When this coal attains a temperature of about 950°F., gas will begin to pour out of the pipe stem, and this gas may be lighted. A black liquid also will exude from the stem of the pipe. This is tar mixed with certain other products. What remains in the bowl after distillation is coke. A coke oven corresponds to the bowl of the pipe. A modern oven of the latest type is a refractory brick chamber approximately 42 ft. long and 14 ft. high, averaging 18 in. in width. The oven is filled with coal through closable charging holes in the oven top. Each end of the oven consists entirely of a self-sealing door, the removal of which permits the finished coke to be discharged by means of a power-operated pusher machine. The ovens are built in batteries, and the heating is effected by gas burned in vertical flues in the oven walls, each set of flues heating the walls of two adjacent ovens. Such ovens carbonize a charge of approximately 18 tons of coal in 18 hr., or have a daily throughput of 24 tons per oven, producing about I 7 tons of coke. In times of need, the output may be increased by raising the temperature of flues, thus shortening the coking time. There is one great essential difference in principle between distillation in a clay pipe and in a coke oven. In the 18-in. oven, the distillation proceeds from two parallel walls held at a high temperature (over 2000°F.) and instead of all the coal being heated at once, the distillation is a progressive one creeping inward. The average travel of this heating is 1/2 in. per hour from each vertical wall, and as the volatile products are formed progressively they must push away from the interior toward the wall through the previously formed hot coke, then up the walls and over the top of the coal charge, finally escaping through the outlet pipe. This results in a cracking of the components into many different and valuable substances not formed when the carbonizing temperature is low.

Jan 1, 1942

By A. D. Schwope, L. R. Jackson, A. M. Hall

IN the course of an extensive investigation of the comparative properties of several types of copper, data were obtained on the cold working and subsequent recovery and recrystallization of the copper. In this paper, relations between the degree of cold work and the course of recrystallization are developed. In particular, it is shown that the course of recrystallization over long periods of time and at low temperatures can be predicted with reasonable accuracy from short-time high-temperature recrystallization data. MATERIALS USED IN THE INVESTIGATION Three types of copper were used in this investigation; these were tough pitch, OFHC, and OFHC copper with 15 oz per ton of silver added identified herein as Lots C, D, and F, respectively. The material was supplied by the American Metal Co. Ltd., and processed by the Rome Cable Co. The analyses of the three types of copper are given in Table 1. Originally, it started as wire bars 4 X 4 X 54 in. These bars were heated to 871°C in air and hot rolled to 3/8 in. rod. This rod was cold drawn to 0.204 in. rod (70 pct reduction) in three passes and annealed at 427°C for 4 hrs. A portion of the 3/8 in. rod was saved for more detailed cold-drawing experiments. Starting with the annealed 0.204 in. rod, hard-drawn wires were produced by cold drawing to 0.081 in. wire in 7 passes (84.4 pct reduction in area). Half-hard wires were made by cold drawing the 0.204 in. rod to 0.102 in. wire, (75 pct reduction) in 6 passes and annealing at 427°C for 4 hrs. This annealed wire was then drawn to 0.081 in. wire, (37.1 pct reduction) in 2 passes. Square rod was made by hot rolling wire bars to 9/16 in, rod in 8 passes. This rod was then cold drawn to 0.445 in.-diam rod and annealed for 3 1/2 hrs at 538°C. It was then cold drawn to 0.325 in. rod and again annealed at 538°C for 3 1/2 hrs. Hard square rods were then made by cold rolling this material to 0.257 X 0.257 in. rod, a reduction in area of 20.5 pct. Half-hard square rods were made by cold rolling to 0.268 X 0.268 in. square, annealing for 332 hrs at 538°C and cold rolling to 0.257 X 0.257 in., a reduction of 8.5 pct. Soft wire or rod was made from all types of copper by annealing the hard-drawn material at 343°C for 3 hrs in steam. The grain size of the annealed 0.081 in. wire varied slightly among the three lots: from 0.015-0.025 mm in the silver-bearing OFHC to 0.035-0.045 mm in the OFHC copper. The annealed 0.257 in. wires were more uniform in grain size, averaging about 0.035-0.045 mm. Representative structures are shown in Fig I. EFFECT OF COLD DRAWING AND TENSILE STRAIN ON STRENGTH OF COPPER Conventional tensile tests were performed on the three types of copper in the various degrees of hardness described above. Results of these tests are tabulated in Table 2. The results in Table 2 are

Jan 1, 1947

By M. Kaufman, A. E. Palty

The phase structure and aging characteristics of two nickel-base alloys, Inconel 718 and 702, were investigated. Wrought and cast Inconel 718 showed ArisCb as the major hardening phase, as well as ture was positively identified. Inconel 702 had Ni3Al as the major hardening phase, as well as Cr7C3-of the phase amounts with temperature was determined. 1 HE value of phase structure and aging rate information in the utilization of alloys has been well established. As part of a continuing program, the results obtained on two nickel-base alloys, hconel 718 and Inconel 702, are presented here. Inconel 718 is a relatively new alloy considered for application in both sheet and cast form. Its novelty lies in the use of high columbium tantalum levels in a Ni-Cr-Fe base. No previous work on this type of alloy has been reported in the literature. Inconel 702 is being used now as an oxidation-resistant sheet alloy. Occasional fabrication problems spurred work on its basic structural behavior. The composition of 702 is essentially nichrome plus aluminum and titanium for strengthening and added oxidation resistance. This puts it in the basic class of other nickel-base alloys which have already been studied. The two alloys will be treated separately. INCONEL 718 Phase Study Methods. The phases present after the various conditions investigated were determined by X-ray diffraction analysis of two different elec-trolytically extracted residues and microscopic examination. The extraction methods, using 10 pct HC1 in alcohol and 10 pct H3PO, in water and the X-ray technique have been described previously.&apos; The effect of temperature on the phase behavior was studied on sheet material using the following heat treatments: 2250°F, 2 hr, ice brine quench 1300 100 hr, water quench 2250°F, 2 hr, ice brine quench 1400°, 100 hr, water quench 2250°F, 2 hr, ice brine quench 1500°F, 100 hr, water quench 2250o 2 hr, ice brine quench 1700°F, 48 hr, water quench 2250°F, 2 hr, ice brine quench 1850°, 24 hr, water quench 2250°, 2 hr, ice brine quench 2000°F, 6 hr, water quench The high solution temperature was an attempt to dissolve as many phases as possible without causing melting. Aging exposures were made longer than normal heat treating times in order to approach equilibrium conditions more closely. Cast material was examined only in the as-cast condition and with the normal heat treatment (1700°F, 1 hr, air cool 1325oF, 16 hr,air cool). Materials. The full phase study was performed on sheet specimens approximately 1/2 in. by 2 in. by 1/16 in. The cast pieces were cut from the gating system of a vacuum-cast test piece. An all weld-metal specimen was made by running many weld beads on the sheet using filler made from the sheared edges of the sheet. All external contamination was removed by belt-sanding followed by an electro-polishing treatment. The typical composition of wrought Inco 718 is as follows: The alloy is air-melted. Cast hco 718 may have higher molybdenum. Due to the expectation of finding a Ni-Cb phase (Ni, Cb) for which no X-ray diffraction pattern was available in the ASTM Index, a special 5 Ib heat to the stoichiometric composition of this intermetallic

Jan 1, 1962

By T. Vasilos, J. T. Smith

THE mechanism of pressure sintering, or hot pressing, for ceramic materials, has been investigated by several researchers.1-8 Plastic flow has been suggested as the rate-determining mech-anism1,2 while grain boundary sliding3,4 and fragmentation processess have been found controlling in other studies. Vasilos and Spriggs5,6 have reported that pressure sintering occurs by a diffusion-controlled mechanism. For the pressure sintering of metals, investigations with lead7 and with tin6 have not identified the operative mechanism during consolidation of these powders. This note reports the results of a pressure sintering study initiated to determine the mechanism controlling the densification of spherical copper powder. Temperatures of 300°, 400°, 500°, and 600°C at 2500, 5000, 7500, and 10,000 psi pressures were investigated. The copper powder for this study was obtained from Metals Disintegrating Co., Elizabeth, N.J. The minimum purity was reported to be 99.9 pct. The powder size was -325 mesh and a lineal analysis showed the average size to be less than 1 p. An alumina die body and punches were employed. Graphite spacers were placed between the copper powder and the punches before pressing. It was expected that the graphite would form carbon monoxide with any entrapped air and form a reducing atmosphere within the die cavity. This condition was generally realized during pressing although a minor amount of oxidation occurred at 500" and 600°C. The oxide particles were located randomly in the pressed samples and were not considered to influence the densification process. Calibration tests showed the temperature of the copper pellet to be about 20°C less than the die wall temperature, probably resulting from heat losses through the punches. This difference was compensated during the experimental pressing operations. The hot pressing equipment employed for this work has been described by Spriggs et a1.9 and was calibrated with a Baldwin-Lima-Hamilton load cell. Travel of the punches was monitored with a dial indicator showing increments of travel to 0.0005 in. Relative density was calculated at selected time intervals for a known copper weight, punch travel, and die diameter. The accuracy of this calculation was *1 pct. Average grain size after hot pressing was obtained by lineal analysis. Typical densification curves are presented in Fig. 1 and Fig. 2 where relative density is plotted vs log time as a function of applied pressure for the 300" and 600°C pressure sintering temperatures, respectively. The curves for 400" and 500°C were similar to those at 300°C and consequently are not shown. The curves at 300°C as well as 400" and 500°C do not show an end-point or limiting density for a particular applied pressure. At 600°C, a density in excess of 95 pct of theoretical has been reached such that further densification is extremely slow for the 5000, 7500, and 10,000 psi pressures. It is suggested that further densification at these pressure levels may be retarded or prevented by discontinuous grain growth, by entrapped gases, and by other microstructural limitations as described by Cob1e.10 The curve for 2500 psi hot pressing pressure is a straight line over the time interval although a slight change in slope may be occurring at the last time intervals. The plastic flow models,1,2 derived for hot pressing, predict the existence of an end-point (or limiting) density dependent on the yield point of the material at the temperature of interest. The yield stress of copper at a 0.005 strain level has been

Jan 1, 1965

By K. P. Gupta

The Cb-rich boundary of the (Cb,Al) a phase field at 1250OC is near 41 pct Al. The Al atoms tend to occupy the C. N. 12 sites in this structure. A homologous (Ta,Al)a phase was identified. No a phase was found in the Mo-Al system at 1200°C. The first binary o-phase with a non-transition element as a major component was found1,2 in the Cb-Al system. The composition of this phase was reported2 as approximately 34 at. pct Al, based on X-ray diffraction patterns taken of alloys in the as-cast condition. Further study of the composition of this o-phase, therefore, appeared desirable. Since Si was previously found3,4 to occupy preferentially the lowest C.N. sites (I and IV) in the a phase, and preliminary resultsa indicated that Al may show similar ordering, one of the aims of the present work was to obtain more complete information on ordering in (Cb, Al) o. Among the binary systems of Al with Ti-, V-, and Cr-group elements, the Ti-Al, Zr-Al, V-Al, and Cr-Al systems are known to comprise no o-phase. In the present work a Ta-Al and a Mo-Al alloy were studied in an effort to find additional o phases with Al as a major component. EXPERIMENTAL PROCEDURES AND RESULTS An alloy with the intended composition of Ta + 40 at. pct Al was prepared by arc melting in He atmosphere. In both the as-cast condition and after annealing for 10 days at 1250°C and quenching in cold water this alloy consisted of two phases, as seen in the X-ray pattern and the microstructure. One of these phases was identified as the o-phase; the observed and calculated d-spacings are shown in Table I. The lattice parameters of this o-phase are a = 9.972 A, c = 5.214 A and c/a =0.5228, as determined from a Debye-Scherrer pattern using Fe K a radiation. The d-spacings for the unknown second phase are given in Table 11. The alloy contained approximately 25 pct of the unknown phase after annealing, as estimated on the basis of microscopic examination. A Mo-Al alloy was prepared by arc melting, with an intended Al-content of 35 at. pct. The alloy button was annealed for 7 days at 1200°C and water quenched. The X-ray pattern of the alloy in both the as-cast and the annealed state showed the reflections of Mo3Al (Cr30 type structure) and an unknown phase different from a. Six Cb-Al alloys were prepared in the composition range 30 to 50 pct Al. All alloys were arc melted in He atmosphere. After annealing for three days at 1175oC in evacuated silica capsules and quenching in water, the alloys with 30 to 40 pct Al contained three phases, namely the o-phase, Cb3Al (Cr3O-type structure) and an unknown phase. The alloys with more than 40 pct Al contained two phases, namely, what appeared metallographically, the o-phase and the same unknown phase. In the alloys containing less that 38 pct Al, the unknown phase was not present after annealing for 4 days at 1250°c,

Jan 1, 1962

By E. H. Rennhack, J. F. Libsch

Definite transition behavior was found in unalloyed titanium at 0.13 pct 0 equivalent. The addition of 0.5 Sn, 1.0 Al, 0.5 Al, and 1.0 Sn lowers the tvansition temperature of titanium at oxygen equivalents exceeding 0.22, 0.29, 0.40, and 0.51, respectively. Metallographic evidence indicates that progressive amounts of oxygen restrict deformation at low temperatures resulting eventually in brittle fracture. The presence of tin or aluminum is thought to alter the atomic distribution of oxygen within the titanium lattice in such a manner as to facilitate some degree of slip and twinning. 1 ITANIUM-like iron and zinc experiences a transition from ductile to brittle fracture with decreasing temperature. The presence of sufficient quantities of the interstitial elements, carbon, oxygen, and nitrogen in solid solution, has been shown to progressively lower the room-temperature impact resistance of titanium with increasing interstitial content.1"1 Ogden,et al,2 reported finding no transition from ductile to brittle fracture with decreasing temperature in iodide titanium. However, a definite transition was found to occur at 0.36 pct 0 equivalent in an alloy containing 0.47 pct carbon in solid solution. The oxygen equivalent in this case was obtained by assuming the effects of carbon, oxygen, and nitrogen in combination on the impact properties of titanium to be additive on the same basis as their separate effects on tensile strength, namely: Oe = 2/3 (pct C) + pet 0 + 2 (pet N) They concluded that the tendency toward transition behavior is dependent on the total interstitial content in solid solution and not on any one particular interstitial element. Rennhack,4 however, recently found transition behavior in iodide titanium at an oxygen equivalent of 0.17 pct. Ogden, etal3, reported that the strengthening effects of carbon, oxygen, and nitrogen in titanium decrease with the addition of tin. They showed that tin additions increase the tolerance of titanium for the interstitials, that is, 10 pct Sn permitted individual additions of up to 0.4 wt pct of the interstitial elements without any significant loss in ductility. Aluminum tends to decrease ductility and impact strength of titanium for a given interstitial ~ontent.3 Van Thyne and Kessler5 found that the solid solubility of carbon in titanium doubled in the presence of 10 pct Al. The precise effects of tin and aluminum in the nrespncp of rorvfen nn the impact properties of titanium had previously not been determined. The high oxygen tolerance of titanium containing tin may provide a suitable means for improving the impact properties of titanium containing the interstitial elements, particularly oxygen. Unlike tin, however, aluminum has a high affinity for oxygen and will reduce rutile titanium dioxide (TiO2)by a thermit-type reaction.6 Thus, the atomic distribution of oxygen in titanium might be different in the presence of aluminum. The present work was undertaken to: 1) Determine the effect of oxygen on the transition behavior of unalloyed iodide titanium. 2) Determine the effect of small amounts of tin and aluminum on the transition behavior of iodide titanium in the presence of oxygen and other interstitial~. EXPERIMENTAL Three different lots of iodide titanium were employed to prepare the alloys studied in the present work. Their chemical composition is presented in Table I. The compositions of the tin and aluminum used for alloying are shown in Table 11. Oxygen additions were made using calcined rutile titanium dioxide (TiO2)of 99.7 pct purity. Alloy Preparation—Four titanium-base alloys containing separate additions of 0.5 and 1.0 pct each

Jan 1, 1960

By O. N. Carlson, W. M. Paulson

A phase diagram is proposed for the Y-C system based on the vesults of thermal analyses, microscopic obsevvations, and X-ray diffraction studies. Three intermediate phases occur in the system: a congru-ently melting fcc phase with a wide range of homogeneity about the composition Y2C, an intermediate solid-solution region between 55 and 58 at. pct C, and a bct dicarbide melting congruently at 2415°C. All three compounds undergo a phase transformation at elezlated temperatures. A continuous serzes of solzd solutions exists between the fcc phase and the high-temperature form of YC2 with a maximum in the solidus at 2000°C and 30 at. pct C and a minimum at 1805°C and 54 at. pct C. THIS investigation of the Y-C system was undertaken as part of a nuclear materials development program. Yttrium-base alloys are of interest as possible containers for liquid metals, and carbides are currently receiving increased attention as high-temperature materials for advanced reactors and other applications. Previous work on this system was limited in scope, and the results were somewhat inconclusive and at times contradictory. Spedding et al.&apos; reported the existence of a triyttrium carbide having an fcc structure with a wide range of homogeneity and Dean et a1.2 reported the existence of a rhombohedra1 phase having the stoichiometry of Y2C. Bachella et a1.3 observed that the latter was the result of ordering of carbon atoms in the fcc solid solution. The ordering range was placed at 800" to 1000°C. Vickery et a1.4 reported a high-melting compound which they identified as yttrium dicarbide, and Spedding and coworkers1 determined the structure of this phase as bct with lattice parameters a = 3.66 and c = 6.17A. Samsonov et al.5 reported the melting point of YC2 as 2300" * 50°C. Recently Bowman et a1.6 found a transformation in the dicarbide from the tetragonal to an fcc form at 1320 20°C. Samsonov and coworkers7 reported a monocarbide of yttrium melting at 1950" * 20°C and also a sesqui-carbide melting at 1800" * 50°C. The existence of the latter has also been indicated by others,1&apos;8 but neither compound has been definitely established. The Y-C phase diagram shown in Fig. 1 was proposed by Chubb and Keller8 in 1964 based on the data available at that time. The tentative nature of this diagram together with the uncertain status of the compounds indicated that additional work on this system was needed. EXPERIMENTAL PROCEDURE Yttrium metal of 99.9 pct purity was prepared for use in this study by the reduction of YCl, with calcium to form a sponge product.9 The major impurities in this material were as follows: 100 ppm C, 150 pprn H, 20 ppm N, 300 to 1000 ppm O, <20 ppm Ca, <100 ppm Cr, <80 ppm Cu, 150 ppm Fe, <30 pprn Mg, <400 ppm Ta, and <100 ppm Ti. Alloys were prepared by arc melting yttrium sponge together with pieces of high-purity graphite rod in a purified argon atmosphere. Homogeneity was insured by repeated melting, inverting the ingot between melts.

Jan 1, 1969