By CARLE R. HAYWARDC

BEFORE discussing this subject it is necessary to define somewhat the meaning of the tern metallurgical.. When I was a student at M. I. T. ore-dressing was not thought of as metallurgy in any sense of the word, but it was considered as more closely allied to mining, enabling the miner to market an otherwise unmarketable product, or at least to market it to better advantage. Progress in ore-dressing has gradually allied it more closely with smelting, for at present the raw material received by the smelter is predominantly concentrates and smelting practice has been profoundly affected by the products of the concentrating mill. It is not surprising therefore that in many schools ore-dressing is frankly considered as metallurgy and although there may be some dissenting opinions it will be considered as such in this discussion. Twenty-five years ago at M. I. T. metallography was taught in a few optional lectures. This subject has developed rapidly and been expanded into the new and increasingly important field of physical metallurgy. To many metallurgists the -term metallurgy means only physical metallurgy. They know little or nothing about smelting and leaching and even less about ore-dressing. Having then broadened the scope of the term metal¬lurgy to cover ore-dressing, smelting, leaching and phys-

Jan 1, 1930

By S. H. Ash

Safety records in the mineral industry for 1954 will do well to hold their own as compared with 1953, because of the poorer rate in the coalmining branches, even without the recent mine explosion at the No. 9 mine of the Jamison Coal & Coke Co., Farmington, W. Va., that killed 16 persons. .The cause of that disaster has not yet been ascertained. The metal-mining branch appears to have improved its record over the last year, however. Health Diesel equipment continues to be favored in non-coal mines. Equipment includes locomotives, trucks, tractors, and muckers. Of major concern and interest is the establishment of a new threshold limit for oxides of nitrogen-5 ppm as compared with 25 ppm. This gas is the most harmful component of diesel-engine exhaust gas

Jan 3, 1955

Jan 1, 1916

By F. E. Bachman

Although it has been apparent to me for a long time that too great weight was currently given to the silicon-contents of foundry-iron, and that the theory of the control by silicon of the carbon-contents of cast-iron is unsound, or that, at best, the influence of silicon is too small to be of much practical value as a guide in foundry-work, it never seemed to me desirable to enter the lists against either the " silicon-fad " or the theory, for the reason that I had neither the time nor the facilities to prove my position, nor any better theory to offer. But since Mr. Summers has taken the step, it seems but right that I should give such facts as are at hand in support of his contention. At the same time I do not think these are enough to prove the case if the contrary proposition were not itself, as it seems to me, based on insufficient evidence. Both Keep's and Turner's conclusions seem to be drawn from irons carrying less than the normal amount of carbon; Turner's " base " being, moreover, a steel rather than a pig-iron, and both the white base and the ferro-silicon of Keep being so low in carbon that compounds of them would not give a material approaching the carbon-contents of a normal casting, and having, therefore, little value as showing the effects of silicon on foundry-irons, even if his samples were treated under the same conditions as those to which pig-metal is subjected in making castings.

Jan 1, 1899

By L. A. Panek

Using an approach based on the theory of similitude, the author develops a general equation and related concepts that provide new insights to an old problem. The load-bearing capacity (strength) of a square, rectangular, or cylindrical prism of a brittle material such as rock, coal, or concrete is expressed as the mathematical product of a size effect, a shape effect, and a function of the mechanical properties (deformability, cleat/joint spacing, and friction) of the pillar, roof, and floor materials. Through an application of multivariate statistical analysis, the results of assorted tests (laboratory and in situ) and observations of failed pillars can be combined into a fundamental scaling equation, which provides a unified, consistent approach to the estimation of mine pillar strength. The form of the equation is sufficiently general to be able to incorporate refinements in the characterization of the structural parameters, as they become available through future analysis and experimentation. Analysis of the published test data suggests that pillar compressive strength (per unit of area) is proportional to the cube root of the pillar width, and that the height effect can be described as the superimposing of a variable size effect (characteristic of the material) on the constant width effect.

Jan 1, 1981

By Walter Harvey Weed

The Republic of Mexico is traversed by many mountain ranges, and presents a great diversity of climates, soils and geographical features, yet its grander geographic provinces are few and peculiarly well defined. The Gulf plain, the Cen tral plateau, the Sierra Madre, and the lowland or Tierra Cali ente of the western coast are the main features of the geogra phy of the Republic, and in the northern half these provinces are particularly well defined. The Sierra Madre separates the Republic into eastern and western parts, and from the City of Mexico north to the Texas line presents an almost impassable barrier to east and west travel. On the north, the first wagon road pass from east to west is at El Paso del Norte, the site of the Texan city of El Paso. Southward for many hundreds of miles the Sierra Madre, traversed by well-worn trails, over which all travel from the west coast to the interior must pass, is a stupendous barrier to social and commercial intercourse. The Sierra Madre is commonly described as a range or con geries of mountain ranges. In fact, it is, in Chihuahua at least, a great plateau, fringed by mountains on the east, trenched by deep canons in its center, and bordered by a wild and rugged complex of mountains carved out of the plateau on the west. Professional duties took me across this region from Parral westward to the Gulf of California via Guadalupe y Calvo. As it includes some of the great ore-deposits of Mexico, and its geological features have never, so far as I am aware, been described, I have prepared a diagrammatic section made from my observations on a horseback trip across the Sierra, and added such notes as seem to be of general interest.

Jan 1, 1902

By C. B. Alcock, M. G. Hocking

The kinetics of the growth of sulfate layers on blocks of Cu20 has been studied between 688" and 800°C. At 788c the over-all weight increases followed the parabolic rate law, with k = 216 30 sq mg per cm4 min, using a 1:1 entering gas mixture of SO2:02. At 757 after an initial linear period the parabolic rate law was followed, with k = 57.8 10 sq mg per cm4 min. The gas mixture required a platinum catalyst to produce the maximum SOs pressure. The sulfation rate at 757' and 788c was high until all the CUZO had changed into a core of CuO, when it became very much lower. At 757°C marker experiments showed that the sulfates (CuO. CuS04 and CuSO4) grow outwards from the oxide surface, but CuO. CuS04 mixed with CuO was found beneath the markers. At 688 markers were found at the CuO. CuS04/CuS04 interface. Visual observations at 757 showed a liquid eutectic moving beneath the sulfate surface. causing very rapid sulfation and extruding to solidify as thick 'needles" up to 8 mm long. Marker experiments have shown conclusi.cely that CuO grows on Cu20 in air by the outward migration of copper. ThermODYNAMIC measurements on the sulfate and basic sulfate of copper, reported recently,' are followed here by measurements of the rates of formation of these sulfates on cuprous oxide, in order to provide a background for the understanding of roasting processes. peretti2 and McCabe and Morgan3 have shown that the phase Cu20 lies next to Cu2S when the sulfide is roasted under conditions where sulfates will be formed. Since this would present too complex a system for kinetic study, the present work4 has been based on the kinetics of sulfation of the oxide phase. The results of a study of the kinetics and mechanism of the sulfation of cobaltous oxide have recently been reported.4,5 Results on the sulfation of cuprous oxide have also appeared,6 but are at variance with those to be reported here. This seems to be because the previous workers6 did not obtain constant SO3 pressures from the SO2/O2 sulfating gas mixtures used, as will be discussed later. Wadsworth, Leiter, Porter, and Lewis found that the sulfates produced when SO2/O2 mixtures are passed over Cu20 at red heats are CuS04 and the basic sulfate CuO.CuSO4. When the decomposition of CuS04 was followed' by differential thermal analysis, a stage corresponding to CuO .CuS04 was reached before decomposition into the oxide occurred. APPARATUS The vertical furnace used for quantitative studies was a conventional resistance-heated and propor- tionately controlled furnace with an even zone (1 deg) which was 4 cm long. The gas mixtures of SO2 and 02 were made by mixing measured flows from capillary flowmeters and drying over phosphorous pentoxide before passing them into the Pyrex top-piece of the furnace assembly. A mullite tube of bore 2% cm was used as reaction vessel and at the bottom of this tube was a trap for SO3, which condensed as a colorless liquid. The residual gas was led into a fume cupboard for ventilation to the atmosphere. The furnace used for visual observations of needle growth and other phenomena consisted of a transparent silica reaction tube of bore 3 cm, having an optically flat silica window sealed into its wall. The reaction tube was clamped vertically, inside a mullite tube of bore 4 cm and length 42 cm which was heated by Kanthal windings. The window in the silica reaction tube was arranged opposite a hole 3 cm wide and 2 cm tall which had been cut in the wall of the mullite winding tube 19 cm from its top end. A binocular microscope was used to look through the window, illumination being provided by a focusing microscope-lamp offset sideways and downwards. The oxide block to be sulfated was suspended from the removable Pyrex top-piece to the reaction tube, by means of which it was inserted at the start of the experiment, and through which entered the S02/02 gas mixture. The variation of the temperature inside the reaction tube with horizontal and vertical displacement from the window was investigated, and, while it can be said that the temperature was constant 1 deg, its value at a given position was known only to 12 deg. In both furnaces, the oxide block to be sulfated was suspended from a small silica hook immediately downstream from a platinum thimble used as catalyst, which was held on a long silica rod from a Pyrex spring attached to the removable Pyrex top-piece of the furnace. The spring was only included in the quantitative sulfating furnace; its sensitivity was 1.4 cm per g and it was found to be free from creep in a 16-hr test when carrying the working load. The extensions were followed by a cathetometer which could be read to 0.001 cm, corresponding to i0.7 mg. Extensions of the spring were measured on adding weights between 5 and 500 mg to the working load (thimble + oxide block), and Hooke's law was closely obeyed. SAMPLES Cuprous oxide blocks were prepared by oxidizing Johnson Matthey "Specpure" copper sheet of 1 mm thickness (impurities: iron at 3 ppm, silver at 2 ppm, lead, nickel, sodium, and silicon each at 1 ppm, calcium, chromium, magnesium, and manganese each at less than 1 ppm) for 6 days in air at 1000°C in a re-crystallized alumina boat. It has been reported7 that when Cu20 is prepared by heating copper sheet for 1 day the central plane of the blocks produced consists

Jan 1, 1967

By G. M. Ault, G. C. Deutsch

The paper reviews the efforts made to utilize powder metallurgy to solve problems encountered when using alloys at high temperatures. The following subjects are discussed: comparison of wrought and sintered super alloys, sintered aluminum powder, porous materials for transpiration cooling, molybdenum, and cermets. TODAY, powder-metallurgy techniques are be-JL coming increasingly important, producing materials which at the present time cannot be made by any other method. Among these materials are high melting-point metals such as tantalum and tungsten, porous metals for filters and lubricant-containing bearings, electrical contacts and electrodes (i.e., tungsten-copper), cutting tools of the cemented carbides, and magnet alloys. In addition, the powder-metallurgy industry has grown because, through the application of its methods, shaped parts, such as gears, can be produced at tremendous rates with a low scrap loss in comparison with manufacture by casting or forging and machining. In the past few years, by utilizing powder metallurgy, several approaches to the problem of high temperature materials have been investigated. In this paper the authors will review some of the studies on application of materials having properties above 1350°F. Since their experience lies in the aeronautical field, possible uses of powder-metallurgy techniques in the production of aircraft en- gines will be emphasized. A large portion of the work is classified, but such a restriction has not eliminated any field from discussion, although limiting the amount of detail it is possible to present. The development of high temperature alloys from powders and porous metals for cooling will be discussed as well as research done on molybdenum and molybdenum alloys, cermets, and intermetallics. Some studies on the utilization of cermets will be considered along with special problems that have been revealed through these investigations. Special interest in certain factors of sintered aluminum powder (SAP) makes it desirable to discuss this material although its use temperature is below the 1350°F limitation set for this paper. High Temperature Alloys from Powders In general, components made from powders for room-temperature application have been investigated with the primary purpose of taking advantage of the high production rates and economies made possible by powder metallurgy. From the standpoint of properties, the ojective of the powder metallurgist has been to obtain a product comparable to the cast or wrought product that is to be replaced. Comparisons of the properties of alloys made by powder-metallurgy methods with those of similar compositions made by casting and forging are reported in the literature.12 In many cases equivalent

Jan 1, 1955

By D. Kuhlmann-Wilsdorf

A new theory of work hardening is developed which rests on only a few simple principles and is applicable to a wide variety of materials and dislocation structures. It explains, qualitatively, the general characteristics of the three-stage shear stress-shear strain curve of fcc metals, as well as the most important features connected with easy glide. The value of, the work-hardening coefficient in stage 11, is derived quantitatively, from first principles, and is shown to be insensitive to many changes in detailed dislocation behavior. The low rate at which energy is stored during mechanical working in stage 11, the dependence of slip line length on stress, and the so-called Cottrell-Stokes law are explained. Although the theory is primarily developed for fcc metals and alloys, it is largely applicable also to some other materiuls, and in particular apparently to poly crystalline simple steels in theh linear range of hardening. FOR pure fcc metals and alloys, after many different pretreatments and under a great variety of testing conditions, the well-known three-stage work-hardening curve is commonly observed. Moreover, the work-hardening coefficient in stage 11, 011, bears an almost constant relationship to G, the modulus of rigidity, such that K = G/Brr" = 300, within a factor of about 2 either way. The very fact that the three-stage curve and the value of K are so very persistent, can hardly be understood except on the assumption that some quite simple phenomena are responsible. In this light all available theories of work hardening must be judged unsatisfactory: Each of them is based on some quite specific dislocation model, while it is known that metals with similar values of K may have widely different dislocation structures, for example, dislocation tangles in the case of pure fcc metals, and piled-up groups of dislocations in a-brasstype alloys. Thus, while a particular theory might conceivably represent a special case with a reasonable degree of accuracy, it cannot possibly have illuminated the underlying principle. Another severe criticism applying to the presently most widely discussed theories is that they employ empirical or even quite unexplained parameters in order to arrive at a numerical value of K. This indicates that some vital aspect of the work-hardening process has remained unexplained. In the present paper, a new theory of work-hardening is developed which does not suffer from the above shortcomings. It is derived from first principles, and is founded on the realization that the underlying causes for the three-stage work-harden- ing curve and for the persistence of the numerical value of O,, must be few and simple. As a first step it is shown herein that the experimental oklservations on "easy glide" can be explained on the assumption that in this stage dislocations multiply, beginning in a number of restricted area:;, and from there penetrate into crystal regions still substantially free of glide dislocations until a quasi-uniform dislocation distribution has been established. During "easy glide", the resistance to the movement of the foremost dislocations, advancing into still largely a dislocation-free regions, is believed to control the flow stress. This resistance is determined by various factors, among them the reaction of the dislocations against bowing-out into loops, which is due to their line tension. Without such bowing-out no dislocation multiplication would occur, but the corresponding contribution to the flow stress stays practically constant all through stage I. According to the present theory, stage TI begins as soon as there are no more areas left into which newly formed dislocations have not yet penetrated, i.e., as soon :is a quasi-uniform dislocation density has been attaned. Regardless of how, in detail, the dislocations should happen to be arranged at the end of "easy glide", whether in pileups or tangles, on one glide system or on several, the stress necessary to overcome the line tension of the segments must now increase, because the dislocation density increiises while the average free dislocation length decreases. It is argued that all other contributions to the flow stress stay at about the same level as in stage I, and that the said increase in the stress necessary to bow out dislocation segments into loops is responsible for the major part of work hardening in stage 11. Stage TII of the stress-strain curve is explained by largely follouing the ideas of Seeger and his co-workers; however, it is pointed out that the start of stage m may on occasion indicate the onset of "conservative climb" instead of cross slip. Indirect evidence indicates that linear work hardening persists even under the profuse action of cross slip, but at a lower rate. Only when, in addition to cross slip, climb operates extensively, does the work-hardening rat,. drop sharply, ultimately down to zero. BRIEF SURVEY OF EXPERIMENTAL EVIDENCE The stress-strain curve of crystals of many different substances are qualitatively similar. No significant permanent plastic deformation takes place below the so-called "critical resolved shear stress". As the applied stress is raised beyond this level. yielding occurs with little or no work hardening and

Jan 1, 1962

By John Chipman, Carl F. Floe

The system molten copper-oxygen-sulphur is of interest from both the practical and theoretical standpoints; practically, because oxygen and sulphur play an important role in the commercial production of copper, and theoretically because it offers a chance to study the reaction between an oxide gas, SO2, and a molten metal. Reactions of this type, such as that between CO or CO2 and molten iron, are important in many metallurgical operations. Again, the determination of any gas-metal equilibrium is of theoretical interest and value insofar as it contributes to the general development of the laws for solution of gases in metals. This problem is being given an increasing amount of attention in modern metallurgy. This paper is the first of a series and presents the results of a determination of the solubility of sulphur dioxide in molten copper at temperatures from 1100" to 1500ºC., and pressures from about 20 mm. of mercury to somewhat above atmospheric. Review of Previous Work The solubility of gases in most liquids has been found to obey Henry's law, which states that for a fixed temperature the amount of gas dissolved is directly proportional to the pressure. However this law does not hold for liquid metals. Instead, it appears that for many gases, particularly the simple diatomic ones such as O2, N2 and H2, the amount dissolved in liquid metals is directly proportional to the square root of the pressure. This is known as Sieverts' law. It may be recognized as a special case of Henry's law, which applies when the solute gas is dissociated into atoms or when it reacts with the solvent metal to form solute molecules containing single atoms of the gaseous elements, as, for example: 2M+G2=2MG K=(MG)2 /M2 X PG2 [I] which, if the solubility is not too high and the concentration of metal therefore nearly constant, can be simplified to: MG = K1 vPG2 [2 Following the same reasoning, it would be expected that the solubility of SO2 in copper would be proportional to the cube root of the pressure, the reaction being as follows: 6Cu + SO2 = Cu2S + 2Cu2O [3] K= Cu2S X (Cu2O)2 i - (Cu)6(Pso2) [4] or, neglecting the change in metal concentration and considering that the concentrations of sulphur and oxygen are both proportional to the volume V of gas absorbed: K1 =V3SO2 /Pso2 or

Jan 1, 1941

By Carl F. Floe, John Chipman

The system molten copper-oxygen-sulphur is of interest from both the practical and theoretical standpoints; practically, because oxygen and sulphur play an important role in the commercial production of copper, and theoretically because it offers a chance to study the reaction between an oxide gas, SO2, and a molten metal. Reactions of this type, such as that between CO or CO2 and molten iron, are important in many metallurgical operations. Again, the determination of any gas-metal equilibrium is of theoretical interest and value insofar as it contributes to the general development of the laws for solution of gases in metals. This problem is being given an increasing amount of attention in modern metallurgy. This paper is the first of a series and presents the results of a determination of the solubility of sulphur dioxide in molten copper at temperatures from 1100" to 1500ºC., and pressures from about 20 mm. of mercury to somewhat above atmospheric. Review of Previous Work The solubility of gases in most liquids has been found to obey Henry's law, which states that for a fixed temperature the amount of gas dissolved is directly proportional to the pressure. However this law does not hold for liquid metals. Instead, it appears that for many gases, particularly the simple diatomic ones such as O2, N2 and H2, the amount dissolved in liquid metals is directly proportional to the square root of the pressure. This is known as Sieverts' law. It may be recognized as a special case of Henry's law, which applies when the solute gas is dissociated into atoms or when it reacts with the solvent metal to form solute molecules containing single atoms of the gaseous elements, as, for example: 2M+G2=2MG K=(MG)2 /M2 X PG2 [I] which, if the solubility is not too high and the concentration of metal therefore nearly constant, can be simplified to: MG = K1 vPG2 [2 Following the same reasoning, it would be expected that the solubility of SO2 in copper would be proportional to the cube root of the pressure, the reaction being as follows: 6Cu + SO2 = Cu2S + 2Cu2O [3] K= Cu2S X (Cu2O)2 i - (Cu)6(Pso2) [4] or, neglecting the change in metal concentration and considering that the concentrations of sulphur and oxygen are both proportional to the volume V of gas absorbed: K1 =V3SO2 /Pso2 or

Jan 1, 1941

By V. Apraxine, J. Lakaye, J. J. Saquet, P. Troch

Union Minière du Haut-Katanga owns concessions for extracting copper and associated metals in the high plateau region of Katanga. The concession is about 188 miles long by 44 miles wide and has three principal areas: Southern area-The Prince Leopold mine is an underground operation from which a copper-zinc sulfide ore is extracted. The mine and associated concentrator are at Kipushi. Copper concentrates are smelted and converted to blister copper at the Lubumbashi smelter at Elizabethville.

Jan 12, 1962

In late May, at its final session in Nairobi, Kenya, the UN Conference on Trade and Development (UNCTAD) narrowly rejected the US proposal for a new International Resources Bank suggested by Secretary of State Henry Kissinger. The proposal was defeated by a roll-call vote of 33 to 31, with most of the nay votes cast by communist countries, and with 89 of the less-developed countries abstaining or absent.

Jan 7, 1976

By Fred C. Bond

SIZE of grinding media is one of the principal factors affecting efficiency and capacity of tumbling-type grinding mills. It is best determined for any particular installation by lengthy plant tests with carefully kept records. However, a method of calculating the proper sizes, based on correct theoretical principles and tested by experience, can be very helpful, both for new installations and for guiding existing operations. As a general principle, the proper size of the make-up grinding balls added to an operating mill is the size that will just break the largest feed particles. If the balls are too large the number of breaking contacts will be reduced and grinding capacity will suffer. Moreover, the amount of extreme fines produced by each contact will be increased, and size distribution of the ground product may be adversely affected.

Jan 5, 1958

By George Burrell

INTRODUCTION THE senior author of this paper, while in Colorado on other official business, made a trip to the Cripple Creek gold-mining district to get more data than are at present available regarding the composition of the gas that issues from the rock into the mines of the district. This was done at the suggestion of George S. Rice, Chief Mining Engineer of the Bureau of Mines. There are many questions of interest and importance in connection with the ventilation of the mines in the Cripple Creek district, such as the menace to life and mining of a suffocating gas entering the mines from the rock, the danger due to powder smoke (from blasting operations), and danger of continued inhalation of rock dust by the miners. This report confines itself to the first problem, the gas from the rock, and principally to one phase of this question, the composition of the gas and its effects on men and lights. A more thorough study of this and other ventilation problems is planned. That the, rock gas is a real menace is shown by the fact that miners (variously estimated from 25 to 50 by different persons interviewed) have been killed by it in the 25 years that mining has been vigorously carried on at Cripple Creek. Many men have had narrow escapes from death, some of them having been incapacitated for days. In addition, much loss of time results because at certain periods of the year or on certain days it is impossible to enter some workings. At a few mines fans force air into the workings, thus supplementing the natural ventila-

Jan 5, 1916

By Leonard Obert

The structural stability of any mine or under- ground opening in rock is dependent on the stress field, that is, the state of stress in rock before mining, the stress distribution in the rock created by the opening, and the in situ strength of the rock. In the past mine design problems have been considered by assuming that the stress field is due only to the weight of the overlying rock, the stress around the opening can be calculated from elastic theory using laboratory-determined elastic constants, and the in situ strength of the rock can be determined from laboratory tests on small specimens. Solutions to hypothetical problems using this procedure are given in a report by Obert, Duvall, and Merrill.' Because of the uncertainties of these assumptions, this method can give only a rough approximation to the solution of actual structural problems. Obviously, this approach to determining the stability of underground openings would be greatly improved if the rock stress could be measured in situ, and it is undoubtedly for this reason that in recent years many investigators have spent considerable effort on the development of procedures for measuring rock stress. In this report a method is described for determining in situ the absolute stress in rock. The method requires the measurement of the deformation of a borehole before and after the rock is stress-relieved. The magnitude and direction of the applied stresses are calculated from the borehole deformation and modulus of elasticity of the rock. Also, the results of absolute stress determination made in the walls and pillars of underground openings in five rock types are presented. From these results a number of conclusions are drawn regarding the accuracy and limitations of this method and the problem of stress measurements in general.

Jan 8, 1962

By S. Gstalder, J. Raynal

Consideration was given to simple tests which could be performed on rocks to give a measure of rock drillability. Various methods of breaking rocks were considered and the hardness test developed by Schreiner was selected for this study. The test involves application of an increasing load on the rock face through a flat-faced cylindrical punch until rupture occurs. Test results show that hardness is a good measure of the breaking strength of rocks. Useful relationships are shown to exist between hardness and other physical quantities such as specific disintegration, Young's modulus and sonic velocity. Specific disintegration (volume of rock broken per unit of work input) provides a possible means of comparing the effectiveness of other methods of rock breakage. The relationship between hardness and sonic velocity may be very significant for it may be possible to deduce rock drillability from sonic log data. provided that a mineralogical factor is taken into account. TO test further the results of the work, laboratory drilling tests were performed which closely simulated down-hole pressure conditions. Correlations of drilling results with rock hardness measurements were quite good. It was concluded that rock hardness, as measured in the laboratory or as deduced from sonic logs, could be used in relations for predicting rock drilling performance. INTRODUCTION Drillability of rocks cannot be defined in an absolute manner by a single quantity or measured by a single test. Resistance of rock to drilling depends to a large extent upon the means used for rock destruction. This complicates drillability classification of rocks for there may be as many classifications as there are methods of rock breakage without known functional relations between them. The objective of this work was to develop. in terms of rock destruction behavior, means of selecting the best drilling method for a given rock or the conditions for optimum output from a given drilling method. ANALYSIS OF ROCK DESTRUCTION TESTS Gauthier and Baron' have reviewed the many test methods which have been developed for determining the resistance of rocks to breakage. These include drilling tests, punch tests, scratch tests, resistance to shock, wear tests, etc. A standard drilling test might be to determine the time required to drill a standard depth (1/16 in.) in a rock using a bi-cone microbit (1 1/4-in. diameter) when a standard load (417 Ib) is applied at a standard speed of bit rotation (110 rpm). From the standpoint of similarity, the results of microbit drilling tests would seem to be most representative of the several methods suggested above. However, evaluation of drilling performance by this method is only qualitative and cannot be applied directly to actual drilling conditions. Punch tests basically measure rock hardness. Punches of various shapes and sizes, including small cones for Vickers' and Knoop's tests, the wedge for Epstein's test and the right circular cylinder for Schreiner's test, have been used. Results of these tests lead to a quantitative hardness classification which would seem to be related to the resistance of rock to bit-tooth penetration. Scratch tests are related to the resistance of rocks to abrasion such as would be encountered in drilling with diamonds. Either the width of the scratch obtained at a fixed load or the load required to give a scratch of a fixed width may be used to evaluate surface hardness of the rock. This should be related to the resistance of the rock to wear. The above tests, and probably many others. give relative measurements of the breakage or destruction characteristics of rocks. There is no direct relation between results of these tests and the drillability of rocks. Also, the tests each measure different quantities which have different dimensions and they do not permit direct comparison of numerical values. As one step in rectifying the above difficulties. it is proposed that the results of all test methods be expressed in terms of volume of rock destroyed per unit of work required; this is referred to as "specific disintegration". Test results may then be reported in a form which shows both a classification of rocks in regard to each method and a comparison of methods with regard to each rock. The disadvantage in using specific disintegration is the difficulty of measuring this quantity with accuracy. The volume of rock damage is difficult to measure. as is the true value of work input. Rock heterogeneity adds to the

Jan 1, 1967

By Charles Will Wright

FRANCE will be given a large portion of the Marshall Plan funds for relief, reconstruction, and industrial development in France and in her colonial possessions. At present that country is not in position to export any large tonnages of the mineral products needed in the United States. However, if, through Marshall Plan aid and private capital investment, production of these products can be largely increased, agreement should be made by which the United States is to get a substantial portion of such increased output in part payment for the material and technical aid they receive. France issued a decree, published in the "Official Gazette" on Feb. 3, 1948, which permits conversion into dollars of dividends derived from dollar investment in Government-approved projects and will agree to a scale of capital amortization to be determined in each individual case. This decree is to encourage private capital to cooperate with local capital in industrial undertakings. The French Colonial Ministry has prepared an extensive program for aid to the mining industries in overseas possessions to be undertaken by

Jan 1, 1948

Technical graduate wanted for metallurgical. work in experimental laboratory of large New England manufacturing concern. A knowledge of metallography of steel is essential. Practical experience is desirable but not required. No. 305. Man familiar with precipitating with the diamond drill core to act as foreman. No. 311. Competent mining man to develop and take charge of mines in Peru. Property to be developed from start and equipped with thoroughly modern appliances to meet the increased production. Applicant must possess considerable mechanical ability and experience. No. 312. Engineers and assistant engineers in forest production for National Defense work for the duration of war. Laboratory work conducted primarily by experimental and research methods, embracing principally investigations of mechanical and physical properties of wood, processes for the preservation of wood against decay and other destructive agents, practical problems of pulp and paper industry, and other industries utilizing wood by chemical means or otherwise. Assistance in this department of Government is urgently required in order to obtain maximum benefits from the investigation. Salary $1860 to $3000 for engineers; $1200 to $1800 for assistant engineers. No. 313.

Jan 6, 1918

SPEAKING generally, it may be said that leaching is the simplest method of recovering copper from its ores. Likewise it is perhaps the oldest method of treatment used by copper metallurgists of the modern era. Reliable records indicate that as early as 1752 cupriferous pyrite was leached in the famous Rio Tinto region in Spain. Though the manipulation was quite different from that in use today at Chuquicamata, New Cornelia, Inspiration, and Andes, it resembled that employed by Phelps Dodge at Bisbee, as described in Chapter XIV. Leaching consists of subjecting ore to the action of a liquid solvent or menstruum (usually an aqueous solution) which dissolves the major part of the soluble copper minerals. The resulting pregnant solution is drained off or otherwise separated from the residual ore; and the copper in the solution is then recovered by some appropriate means of precipitation. When sulphuric acid is the lixiviant, as is usual, the simplest procedure is to pass the copper-bearing solution through large troughs containing scrap iron. The iron displaces the copper in the solution, precipitating it as a slime coating the iron and varying in color -from bright copper to a dull black. This may be washed off at intervals, collected as a sludge, dried, and melted with a little fluxing material to produce reasonably pure copper. Usually, of course, the mud is sent to a smelter where most often its destination is the converter or reverberatory furnace. Modern practice uses precipitation on iron only as a complemental process to electrolytic precipitation or deposition, wherein the pregnant copper-bearing solution, acting as the electrolyte in a cell having insoluble anodes and copper cathodes, is depleted of the copper it contains. Cathode copper, 99.5 per cent pure, is produced ready for the market as refined copper, or for a simple process of melting, fire-refining, and casting in

Jan 1, 1933