Jan 1, 1902

By A. W. Fahrenwald

PRACTICALLY all fine grinding is done in a ball mill or some modification of a ball mill. Millions of tons of material are ground each year. The cost varies from, say, a minimum of 10 c. to a maximum of 35 c. per ton. It is thus obvious that even small improvements, which may result in increased grinding efficiency, would be welcomed by mill operators. A review of literature shows that various phases of the subject have been studied independently by many investigators. Also, it is now a subject of investigation at various laboratories in the United States and in foreign countries. Notwithstanding this extensive investigation, ball milling still remains a subject of some speculation. This paper presents the results of an experimental study of some of the factors entering into ball mill grinding.

Jan 1, 1931

By L. C. Graton

I. INTRODUCTION. The Relations of Scale in Geologic Work. MANY features of human accomplishment rest upon the possibility of representing natural objects on a scale of different magnitude from the actual one. Most drawings, for example, are of very different scale from that of the object depicted, and indeed are useful mainly on this account. More important than the question of mere convenience, however, is that of meeting the physical limitations of vision.1 Thus, a mural

Jan 5, 1913

G. R. GOHN. l-1n Table I11 of The Sager, Brown, and Mears paper, which was presented on the screen, data were given showing the results of accelerated corrosion tests of certain magnesium alloys. Mention was made that these were carried to a certain time which was used as a measure of failure but no mention was made as to the period of time. I would like enlightenment on that. G. F. SAGER (Author).-In reply to Mr. Gohn's question regarding the times of exposure for the accelerated stress-corrosion tests referred to in Table I11 of our paper, which shows the correlation between accelerated and atmospheric stress-corrosion tests on magnesium alloys, I can say that we usually run the accelerated tests on such alloys for at least 500 hr. We feel that this is long enough to reveal any marked susceptibility to stress-corrosion cracking. In the case of the atmospheric tests on such alloys, we have not yet decided how long we should expose the specimens. Most of them are being exposed for indefinite periods and a good many of our specimens have now been exposed for several years. We may want to continue some of the tests for five or ten years. The period of six months mentioned in connection with the times of exposure for the atmospheric specimens was a rather arbitrarily selected minimum time for which specimens had to be exposed before we counted them with those that had not failed. A fairly large number of magnesium- alloy specimens have been exposed in the atmospheric stress-corrosion tests at var-

Jan 1, 1945

By T. F. Baily

DURING the period of the War, in both this country and Canada, a number of attempts were made to make pig iron from steel scrap in the FIG. 1.-EXPERIMENTAL FURNACE. 5000 KW. CAPACITY: 150 TONS 2 PER CENT. SILICON PIG IRON PER DAY. electric furnace, and a considerable tonnage of white pig iron was produced, the silicon and manganese additions being made with ferroalloys; but it is believed that the experiments conducted at Canton, Ohio, in

Jan 1, 1930

By L. H. Dushak

DURING the war period of quicksilver activity there were a number of departures from what may be termed the classical quicksilver metallurgy. Attempts were made to beneficiate low-grade ores by gravity concentration and flotation; mechanical furnaces began to replace the Scott furnace and the vertical coarse-ore furnaces, and condensers of sewer tile and redwood tanks were used in place of the older brick and stone condensing chambers. Other developments that have occurred during the current period of quicksilver, activity are mainly in the nature of improvement and further refinement of those started during the war period. Each period of quicksilver activity has been accompanied by the proposal of various new processes, including wet methods for the treatment of quicksilver ores and innovations in furnaces, retorts and condenser equipment. As far as the author knows, nothing of economic significance in the way of "new processes" has been developed. There is in fact no real need for any essentially new process for the treatment of quicksilver ores; the direct furnace treatment is simple and inexpensive. Moreover, with fare exceptions, the quicksilver industry has no complex or refractory ore problems corresponding to those which are receiving more and more attention from metallurgists in other branches of the nonferrous field. Under these conditions improvements in quicksilver metallurgy must be looked for through the adaptation of current developments in engineering and metallurgy generally to the particular needs of quicksilver practice rather than through the invention of new processes.

Jan 1, 1930

By R. R. Sayers

SILICOSIS is a term known to almost everyone today. Yet, in spite of a great deal of study, much is still to be learned regarding the disease. Government organizations are still continuing their investigations, begun near Joplin, Mo., 25 years ago. Work is also being done in several universities, as Harvard, Pennsylvania, Rochester, and Toronto, and at least two private organizations, the Air Hygiene Foundation of America, Inc., and the Saranac Laboratories for the Study of Tuberculosis, devote most of their time to this subject. Similar studies have been and are being made in many other countries.

Jan 1, 1939

By M. Baeyertr

Since 1915 many papers and books have covered industrial applications of X-rays from various angles. Two of the more recent are a paper by Fink and Archer, which describes in detail the technique of radiography, and a paper by Clark2, which embraces the whole field of X-ray metallogmphy. This paper, therefore, is confined to work of the X-ray Laboratory of the Western Electric Co., which naturally divides into two categories: radiography and diffraction patterns of various types. Radiography Radiography is the field in which the application of X-rays has had most general appeal among the industries which produce or use metals and alloys. Equipment permitting the examination of heavy sections of metals less permeable than aluminum or other light alloys requires apparatus capable of generating hard X-rays over a considerable period of time. The equipment used in the work presented in this paper is practically identical with that described by Fink and Archer in their paper on radiography in industry and is easily capable of penetrating 1/8 in. of lead. Radiography is used in two major groups of problems: (1) in the development of cquipment and tools and (2) in studies of materials. So far there has been no instance in which the use of radiography for routine inspection is justified. This is partly due to the fact that the manufacture of telephone apparatus involves the production of many identical parts by standardized procedures and equipment that has had development and trial before being put on a regular production basis. It is during this stage of development of equipment and tools that radiography has been used to particular advantage.

Jan 1, 1931

By W. Rall, A. J. Birkle

The effect of fast-neutron irradiation on the micvo strcture of a common reactor pressure-vessel steel, A212 Grade B, was studied using thin-foil transmission electron microscopy. The dislocation density of the irradiated material is considerably greater than that of the nonirradiated control material. Annealing studies indicated that dislocations and hardness ill the irradiated material annealed out—as docs the radiation-induced embrittlement according to other- investigators— at temperatures STEELS in nuclear reactors are affected by neutron irradiation. In the American Society for Testing Materials (ASTM) A302B and A212B steels commonly specified by designers for reactor vessels, between 650° and 800°F. However, the dislocations and hardness in control samples cold-worked to 9 and 70 pct did not anneal out readily, and a high dis -location density was observed, even after a 1-hr anneal at 850°F. Based on the hypothesis that cllrster defects, rather than the increased dislocation density, are primarily responsible for mdicltiotz-iudziced e)nbriftlen7ent, reconzmendations are made for reducing the susceptibility to such ernbrittlement. exposures at a temperature of 550°F or lower to neutron dosages encountered during a 20- to 30-year life (-3 X 10'' nvt, >1 mev) may increase the nil-ductility transition temperature (NDT) as much as 300" or 400".'9 Therefore, to prevent brittle failures in reactor structures, extreme caution is required to reduce thermally induced stresses during all reactor shutdowns and startups when the temperature is below the NDT of the pressure vessel.

Jan 1, 1964

By W. H. Bassett

Beads of metal frequently appear at the ends of cast-copper wire bars and on the sides of wedge cakes near the top. These are richer in cuprous-oxide than the rest of the casting. A micrographical study of these exudations has been made. It is suggested that the material is forced through the surface while the copper is solidifying. If not eliminated in process of manufacture, it shows on the finished polished sheet copper in patches differing in color from the main body of the sheet. FIGURES 1 to 4 show the copper exudations, at different magnifications, as they appear on the ends of cast wire bars, and on the sides, usually near the top, of wedge cakes. Sometimes the exudations are in fine "drops;" at other times, large masses of the material are found. Microscopic examination of the copper exudation indicates that it is high in oxide and of eutectic proportions. Because of the difficulty of securing a suitable sample, the protuberances have not been analyzed chemically; but the spectroscope shows no indication that there are any more metallic impurities present than in the balance of the copper. The lowest copper plus silver content of the coppers studied for this? paper was 99.914 per cent.; the highest, 99.966 per cent.; so the oxygen content of the whole casting would be well under 0.07 per cent.

Jan 2, 1926

New Jersey Zinc Co. - The Mines Franklin-Sterling Friedensville Development Austinville Ivanhoe Development Eagle Mine Hanover

Jan 12, 1953

By Henry N. McCarl

[The Construction Materials section contains the following Chapters: Aggregates Cement and Cement Raw Materials Crushed Stone Dimension and Cut Stone Lightweight Aggregates Gypsum and Anhydrite Sand and Gravel Insulating Materials-Thermal and Sound Slag Roofing Granules] Mineral aggregates are those natural and manufactured industrial mineral and rock materials that provide bulk and strength in portland cement concrete, bituminous concrete mixes, and plaster or stucco surfaces. They may also provide special characteristics such as thermal and acoustical insulation, weight, surface textures, abrasion resistance, and impermeability to various concrete products and mixes. Most aggregates are relatively inexpensive materials, but despite their low unit value, the tonnages consumed each year in the United States and throughout the" world make mineral aggregates by far the leading industrial mineral and rock materials both in terms of volume (tonnage) produced and value consumed. The major use of mineral aggregates is in concrete. The low cost, high bulk aggregates tend to keep concrete construction costs at levels competitive with other building materials. Other major uses of aggregates include highway and railroad base or ballast materials, graded fill, and various industrial uses such as metallurgical and chemical fluxes and raw materials-these latter uses are often considered nonaggregate uses of mineral aggregate materials. The per-ton value of mineral aggregate materials at the production plant in 1980 and 1981 varied from $2 to $5 for most sand and gravel and crushed stone, $3 to $6 for air-cooled slag, $7 to $20 for expanded slag and expanded clay or shale aggregate, to as much as $165 to $320 for expanded perlite or vermiculite. The expanded lightweight aggregates have been dramatically affected by increasing fuel costs. It is ironic that the specialized aggregates used as insulating materials to conserve energy cost so much more to produce due to the high proportion of energy consumed in their production. The first four parts of "Construction Materials" deal with the utilization of four major mineral aggregate types: Crushed Stone, Lightweight Aggregates, Sand and Gravel, and Slag. While the focus will be on the use of these industrial minerals and rocks, there will also be some coverage of sources, mining and production, especially in those cases where they are not discussed in the Commodity section of this book.

Jan 1, 1983

K. T. Aust and J. W. Rutter (General Electric Research Laboratory)—We find it difficult to reconcile the activation energies determined by Gifkins with his general conclusion that "migration during both creep and grain growth can thus be treated on the basis of the same model" (that of Lucke and Detert). Gifkins finds the activation energy for grain boundary migration during creep to be 24.5 kcal per rnol and that for grain boundary migration during grain growth to be 7.5 kcal per mol. The calculation carried out by Gifkins of the activation energy for grain boundary migration during grain growth, using the Lucke and Detert model, gives a value of 20 to 24.5 kcal per mol, rather than his experimental value of 7.5 kcal per mol. The theory of Lucke and Detert was developed to account for the rates of migration of grain boundaries in the presence of impurities during grain growth. The theory does not take into account the effect on the boundary migration of another, simultaneous process such as creep deformation and would be expected, therefore, to be applicable only to migration during grain growth. The fact that Gifkins measured a different activation energy for boundary migration during grain growth (7.5 kcal per mol) from that during creep (24.5 kcal per mol), although the specimens were of the same composition, shows clearly that such an effect exists under his experimental conditions; the presence of a simultaneous creep deformation markedly affects the boundary migration process in comparison with what would be observed under the same conditions but without the creep deformation. The failure of McLean's equation (Eq. [4] of Gifkins' paper) to give a satisfactory dislocation density difference for boundary migration during creep is not surprising, since the activation energy which must be used in this equation refers only to the elementary atom transfer process of grain boundary migration. This activation energy value is approximately 6 kcal per mol for zone-refined lead, as determined in both the grain boundary migration experiments of Aust and Rutter31, 32 and the grain growth experiments of Bolling and Winegard.33 Using this activation energy value, McLean's equation gives reasonable agreement with observed migration rates for grain boundaries moving free of the influence of impurities.31, 32 The value of 24.5 kcal per mol is probably associated with the presence of impurity atoms, as Gifkins suggests. It should be noted, however, that this value was obtained using lead of only one composition and measurements at only two temperatures. The work of Aust and Rutter3"' on the effects of tin, silver, and gold on grain boundary migration in zone-refined lead in the temperature range from 320" to 200°C, as well as the work of Bolling and Winegard34 on the effect of silver and gold on grain growth in zone-refined lead, shows that the measured activation energy is markedly dependent upon the kind and amount of solute present. Gifkins' work does not permit evaluation of the effect of the 8 ppm of impurities other than oxygen present in his specimens. One incidental point: the symbols used to designate the experimental points of Fig. 6 appear to be in incorrect order in the figure caption. As the caption is printed, it would indicate that larger grain sizes were obtained after annealing at 47°C than at 100°C, which does not agree with the text (point M, p. 1019). Finally, it seems clear from Gifkins' results that any serious attempt to determine whether grain boundary migration and grain boundary sliding during creep occur with the same activation energy, as Gifkins suggests and McLean rejects, must take into account the effects of impurities on these two processes, Although the work of Weinberg35 indicated that adding small amounts of copper, iron and silicon to aluminum did not affect the grain boundary shear behavior, it should be noted that his starting material contained approximately 60 ppm of impurities. Gifkins' results indicate impurity effects at an impurity level of 8 ppm, suggesting strongly that the most significant impurity range to be investigated lies substantially below that value. R. C. Gifkins (author's reply) — As Drs. Aust and Rutter suggest, the results under discussion may have to be reinterpreted in the light of their own work on grain boundary migration, which was not available to me when the paper was written. Because of their work, Aust and Rutter attach more importance than I did to the activation energy for grain boundary migration during annealing (7.5 kcal per mol) obtained from a "direct" plot of log-rate against the reciprocal of absolute temperature. At the time it was obtained, this value seemed rather low, although it was similar to the value obtained by Bolling and Winegard.36 It was then, and still is, difficult to accept this value because of the low value of the index in the power law for grain growth, which seemed to indicate the influence of impurities. It was also concluded that the low value of the activation energy might have arisen from the manner of selecting rates of grain growth which were truly comparable at the two temperatures. There were many other indications in these experiments and those on recrystallization during creep3? that an impurity, probably oxygen, was of importance. The model for grain-boundary migration which Lucke and Detert had proposed was an obvious possibility and its use yielded an activation energy for boundary migration during annealing of 20 to 25 kcal per mol.

Jan 1, 1961

By H. C. Jennison

Two distinct types of defects occur at times in copper wire as a result of the use of dies of improper design or undesirable wire-drawing practice. The conditions under which these defects may be produced, as well as precautions to be taken in order to prevent them, have been known to The American Brass Co. for many years. The quality of the copper wire bars and rods has too often and unjustly been held responsible for these particular defects and it is to correct any such belief that this paper is presented. An extremely high quality of electrolytic copper has been supplied to the trade by all refineries for the last 20 years at least. The purity of the copper would average well above 99.900 per cent. The casting of the wire bars has been handled in a generally satisfactory manner. The bars have been cast sound, with a flat to slightly crowning set and have been free from sloppy edges, cold sets, etc. In other words, the wire bars have met A. S. T. M. specifications and have been generally satisfactory. For the most part, they have been everything that could be desired from a quality standpoint yet most of the wire mills in this country and in Europe have at times held the quality of the copper responsible for the two types of defects described in this paper. As a matter of fact, these defects are produced entirely in the wire mills. The author has visited many of the large wire mills in the United States and in Europe to investigate these defects. In some cases the trouble has been so serious that the wire mill has ceased operations. At times the wire mills are reluctant to believe that they are responsible for the defective product. The effect of die design, wire-drawing practice, etc., upon the quality of copper wire has received' little study on the part of wire mills, particularly those that have commenced operations in the last few years.

Jan 1, 1930

By Nathaniel Arbiter, Norman L. Weiss

Factors now accelerating the trend to larger concentrators and larger equipment units are reviewed. After almost 40 years of stability with unit sizes less than 100 cu ft, 200 and 300-cu-ft flotation-cell units are now operating and a 500-cu-ft machine is being built. The design of these cells is considered, as is the design and operation of flotation circuits against the background of the need to achieve greater process efficiency while holding down operating and investment costs. Particular attention is paid to the scale-up problem. With the newer cells having five to ten times higher unit capacities, the advantages resulting from this in sampling, mill operation nnd control, testing and plant layout are indicated, as well as the broad direction for changes in the overall design of 50,000 to 100,000-tpd concentrators. A comparison is given of the available larger cells of U.S. manufacture with analysis of differences and similarities. After almost 60 years of application in this country, froth flotation is still by far the most important process for concentrating metallic ores as well as a number of nonmetallic ores including fluorspar, phosphate rock, and potash. Its use on iron ores and coal is increasing. In the metals groups, the largest plants and the greatest progress are found in copper and molybdenum mills, and the section of this paper that deals with applications will be found most pertinent to that field. During its long reign, the flotation process has passed through several phases of evolution and has achieved progress in economy, efficiency. and simplicity of operation. Much of today's success in the flotation of low-grade ores can be attributed to that progress. Even more important to us than our ability to cope with today's conditions are tomorrow's problems, which we can contemplate with some prescience and confidence. Our annual production of copper, lead, zinc, and molybdenum—to mention only the most important metals occurring in the U.S. as sulfides- must be held at a high level in the face of a declining grade of ore. It is probable that the tonnage of such ores mined and processed will double in this country before the turn of the century. Not only will many of the existing flotation mills be enlarged again and again, but larger mills will be built here and abroad to meet our needs. At this moment, in fact, there are at least three proposed new foreign mills or expansions that envision 100,000-tpd milling rate on copper ores. Table 1' shows the trend in copper ore grades in U.S. in recent years. Table 2' shows the projected annual growth rate of consumption 1966-1985. A study by one of the authors 25 years ago showed that of 32 copper mills in North America with more than 100-tpd capacity, only eight had capacities exceeding 10,000 tpd. The average for these eight was 25,000 tpd. These included the three giants of that day, Magna, Arthur, and Morenci; the other five averaged a little over 10,000 tpd. Today instead of the eight mills with capacities exceeding 10,000-tpd capacity we have 25, and the mill with less than 1000-tpd capacity is fast becoming extinct. Much less range is found in lead and zinc mills, which are still generally small except for the few with over 1000-tpd capacity in Missouri, Utah, and Idaho, and a few zinc ore mills in the same size category. Molybdenum and potash operations are the fastest growers in North America today, but when one considers the projected increase in consumption of copper together with the projected decrease in grade of ore (3% annually), he can foresee that copper ore milling will soon lead the list. Technological improvements to meet the challenge of lower-grade ores have taken the wholly predictable path toward bigger equipment. In mining, shovels, draglines, scrapers, and trucks have led the way; in ore processing, we have seen a rapid increase in size of grinding mills, flotation cells, and pumps. Twenty-five years ago, for example, the 10-ft-diam ball mills treating 2000 tpd at Morenci were considered the giants, but today some grinding mills in similar service have five times that capacity. The specific matters to be dealt with in this paper are 1) the underlying principles that affect flotation-machine design, and the conditions required to produce

Jan 1, 1971

By Hjalmar W. Johnson

It has long been accepted that blastfurnace practice varies to some degree with the coke used. While the qualities desirablc in iron have been known for some time, the qualities in coke that produce such iron have not been established. There are no objective standards for blast-furnace coke, which is usually described in general terms, as good or bad. Many experienced operators believe that coke cannot be measured objectively except by using it in the furnace, noting the result, and labeling the coke according to furnace operations. This is admittedly unscientific, and besides is useless for the two main purposes for which a measure of coke quality is needed: (I) to produce the best possible coke from the coals and equipment on hand; (2) to test new coals and determine their value for blast-furnace coke. In seeking such an objective measure, much work has been done on tumbler tests, shatter tests, sizes of coke, porosity, specific gravity, reactivity or combustibility and other tests, but as yet very little has been published in which conclusive correlations have been established between such objective measures and furnace operation. In our study of the problem during the past 8 years we have developed no new measures of coke quality, but we have collected data that are presented here in the hope that they may assist in further work, so that at some future time there may be developed such positive measures. The purpose of this paper is to show that there are variations in coke and that such variations do influence the operation of blast furnaces. At the same time we must remember that there are variations in blastfurnace operation and it may be the blast furnace that is at fault. This correlation of coke properties with blast-furnace operation will be worked out in the following steps: . Discussion of a period when a change in the coke resulted in an increase in efficiency on one furnace and a decrease in efficiency on another. 2. Adaptation of the inefficient furnace to the available coke so that normal efficiency was restored. 3. The use of radial distribution: a discussion of the effect of size of ore layer in adapting blast-furnace operation to the coke. 4. An example of a change in size of coke and the detrimental influence on the pro duction of one furnace. 5. An example of a change in size of coke, together with manufacturing data, to show why it changed, the conclusion being that coke is a product with an optimum value. 6. Illustration of the fact that coke has different optimum values on two furnaces, with discussion on adaptation of operation so the optimum values will be the same. 7. Limitations of the use of screen tests as an objective measure of coke quality. 8. Importance of uniformity in coke. Functions of Coke and Qualities Required to Perform These Functions Coke has three important functions in a blast furnace: (I) to furnish most of the

Jan 1, 1942

By Hjalmar W. Johnson

It has long been accepted that blastfurnace practice varies to some degree with the coke used. While the qualities desirablc in iron have been known for some time, the qualities in coke that produce such iron have not been established. There are no objective standards for blast-furnace coke, which is usually described in general terms, as good or bad. Many experienced operators believe that coke cannot be measured objectively except by using it in the furnace, noting the result, and labeling the coke according to furnace operations. This is admittedly unscientific, and besides is useless for the two main purposes for which a measure of coke quality is needed: (I) to produce the best possible coke from the coals and equipment on hand; (2) to test new coals and determine their value for blast-furnace coke. In seeking such an objective measure, much work has been done on tumbler tests, shatter tests, sizes of coke, porosity, specific gravity, reactivity or combustibility and other tests, but as yet very little has been published in which conclusive correlations have been established between such objective measures and furnace operation. In our study of the problem during the past 8 years we have developed no new measures of coke quality, but we have collected data that are presented here in the hope that they may assist in further work, so that at some future time there may be developed such positive measures. The purpose of this paper is to show that there are variations in coke and that such variations do influence the operation of blast furnaces. At the same time we must remember that there are variations in blastfurnace operation and it may be the blast furnace that is at fault. This correlation of coke properties with blast-furnace operation will be worked out in the following steps: . Discussion of a period when a change in the coke resulted in an increase in efficiency on one furnace and a decrease in efficiency on another. 2. Adaptation of the inefficient furnace to the available coke so that normal efficiency was restored. 3. The use of radial distribution: a discussion of the effect of size of ore layer in adapting blast-furnace operation to the coke. 4. An example of a change in size of coke and the detrimental influence on the pro duction of one furnace. 5. An example of a change in size of coke, together with manufacturing data, to show why it changed, the conclusion being that coke is a product with an optimum value. 6. Illustration of the fact that coke has different optimum values on two furnaces, with discussion on adaptation of operation so the optimum values will be the same. 7. Limitations of the use of screen tests as an objective measure of coke quality. 8. Importance of uniformity in coke. Functions of Coke and Qualities Required to Perform These Functions Coke has three important functions in a blast furnace: (I) to furnish most of the

Jan 1, 1942

By Gary E. Melickian

Last year's review was characterized as a year of politics and began an era of legislation. The 1972 review can be similarly characterized, with even more rigid health and safety regulations and environmental legislation. The mining industry should be aware of what's happening in the nuclear power and other fields as a result of the National Environmental Policy Act (NEPA) of 1969, where the environmental impact of most major construction activities are already under close scrutiny. Section 102 of NEPA requires that all federal agencies include a detailed statement on specified environmental conditions as part of every report on proposed actions significantly affecting the quality of the human environment. All such environmental reports must consider the same general conditions: • The environmental impact of the proposed action. • Any adverse environmental effects which cannot be avoided should the proposal be implemented. • Alternatives to the proposed action. • The relationship between local short-term uses of man's environment and the maintenance and enhancement of long-term productivity. • Any irreversible and irretrievable commitments of resources which would be involved in the proposed action should it be implemented.

Jan 2, 1973

By T. E. Scott, R. P. Zerwekh

The charactevistics of the deformatiotz of fcc thorium were examined between 78 and 473 K. Activation energy, actiuation volume, and the temperature dependence of the flow stress were determined and conlpared uith several theories for the rate-controlling mechnnistn of the tempemture-dependent component of the flou~ stress. It was established that the Cottrell-Stokes law does not hold, even approximately, for thorium. Through consideration of the above factors and other parameters, it was concluded that the vandom solute barrier theory proposed by Friedel demonstrates the best agreement with experimental observations of the deformation of thorium below ambient temperature. THORIUM, the first metal in the actinide series of rare-earth elements, is interesting and important from two points of view. In the more practical vein, it is a potential reactor fuel. As such, it is important to know its properties. Of specific interest here are the mechanical properties of thorium. Second, no detailed information concerning the deformation characteristics of the actinide elements has been gathered to date. In view of the interesting physical and chemical properties of these metals, their mechanical behavior might reveal characteristics which could improve our understanding of the mechanisms controlling deformation of the more common metals. For example, it has been shown1 that thorium exhibits a yield point which is greatly enhanced by interstitial solute elements such as carbon. This is not a normal occurrence in fcc metals. The goal of this investigation, therefore, was to characterize the deformation of polycrystalline thorium. MATERIAL AND PROCEDURES Thorium, made by the magnesium intermediate alloy process described by Peterson et al.,2 was rolled and swaged to 0.065-in.-diam wire. The metal analysis is given in Table I. After preparation, the oxygen and nitrogen contents had risen to 308 and 60 ppm, respectively. The 0.065-in.-diam wires were cut into 2-in. lengths and annealed in a vacuum of lo-' Torr at 750°C for 1 hr, producing a grain size of 2735 grains per sq mm. The ends of the 2-in. sections were masked off so that a 1-in. gage length could be electropolished. Specimens were polished at 35 v in a solution of 6 pct perchloric acid in methanol which was maintained at 0°C . The gage diameters after polishing were about 0.0625 in. The tests were run on a screw-driven tensile machine at a constant crosshead speed corresponding to a strain rate of 0.005 min-'. The strain rate was changed rapidly after each 0.01-in. extension between 0.005 min-' and one of three higher strain rates which were selected in order to achieve strain-rate ratios of 5, 10, and 20. Tests were run at several temperatures from 78" to 473°K; most were tested at 423", 300°, 215", and 78°K. EXPERIMENTAL RESULTS Flow Stress vs Strain and Temperature. Typical true stress-true strain curves for thorium are shown in Fig. 1 for several temperatures over the range 473" to 78°K. The curves for 78", 215", 300") and 423°K were obtained from strain-rate change tests using the lower (0.005 min-') or base strain-rate values of stress. Additional tests, using the same base strain rate at different strain-rate ratios, gave curves which virtually superposed on those shown, indicating that strain-rate changes did not materially influence the work-hardening characteristics at the base strain rate. The curves for 273") 373") and 473°K were standard tensile tests at 0.005 min-'. The behavior of the flow stress with temperature is

Jan 1, 1968

ASHBEL WELCH, Lambertville, N. J.: Dr. Dudley has given the wear of steel rails under four different conditions. He arrives at the conclusion that the softer rails, or those that from their composition ought to be softer, wear better than the harder. But there is another condition which has an important bearing on the subject, and should not be overlooked,—the weight on a wheel. With the lighter weights of the past, the softer rails may have worn best; with the heavier weights of the future, the harder may wear best. Weights will probably be increased up to the capacity of steel to bear; then doubtless the harder steel will wear best. A leaden rail with ten pounds on a wheel might carry millions of tons, but with one hundred pounds on a wheel, it would be destfoyed by a few thousand tons. So in the days of iron rails, my experience was that the softer rails under light machinery stood better than some of the harder; but under heavy machinery the softer were muqh the most rapidly destroyed. It is doubtless the same with steel. The pounding motion of the wheels loosens or spreads the particles of a thin film of steel; the pull lengthwise on the rail de-

Jan 1, 1881