By C. G. Dunn, F. W. Daniels, M. J. Bolton

IN recent investigations1. a data on relative grain boundary energies in silicon iron have been obtained. The present investigation is a continuation of this work along similar lines for the purpose of obtaining additional information on boundary energies. One aim has been to extend the data for a (110) series, which was formerly studied,' to small differences in orientation, since a recent theory3,4 based on a dislocation model of grain boundaries predicts a E. ? (A-ln ? )* form of energy curve for small differences in orientation. Another aim has been to provide data for a (100) series—all grains having (100) planes parallel with the surface of sheet speci-mens—and to compare the results with the predicted form of energy curve. Finally, information on the nature of approach to equilibrium conditions was to be obtained through observations on the movements of grain boundaries. Recently published papers2,3,5 have treated the mathematical problem of expressing equilibrium conditions for grain boundaries for the general case when boundary energy depends upon boundary orientation. The equilibrium equations, which relate equilibrium angles and grain boundary -free energies, contain additional terms that express the variation of energy with boundary rotation. It has been necessary in the present investigation, however, to neglect these additional terms since no data for their evaluation were available. Dropping the additional terms leads to the following approximate equations which were used: E12/sin ?3 = E18/sin?2 =E28/sin?1 or those of the form: E28 + E13 cos ?3 + E12 cos ?2 = 0 Experimental Procedure Except for sample F1, all specimens were made from two lots of silicon iron called C and L respectively. The compositions of these are listed in table I. In the preparation of 12 three-grain specimens for the present investigation, a controlled grain growth technique, which has been described previously,' was used. After preparation, the specimens were notched at the boundaries to shorten them as a means of providing more rapid approach to equilibrium in the anneals. Initial grain boundary angles were determined from micrographs taken at X500. Seven anneals, totaling about two days at 1300°C and two to four days at 1400°C, were run in an atmosphere of pure dry argon as described in a previous paper.' Boundary changes generally could be followed without metallographic surface preparation, because thermal etching occurred during the anneals. These observations indicated angle changes of as much as 35" in some instances, with the major changes occurring during the first anneal. Annealing was discontinued when the angles reached stationary values. Fig. 1 gives a schematic diagram for purposes of defining crystallographic and boundary directions for three grains with common plane parallel with the sheet. Differences in orientations (expressed by A) are the angles between [00l] directions. They can be calculated with the aid of the ?'s. The grain boundary angles can be calculated from the w'S. Results Results are given in table 11. Types of crystal-lographic planes refer to those parallel with the sheet. Orientations are given in terms of [00l] direc-tions as shown in fig. 1. Except for grain 3 of specimen H6, which was unintentionally tilted 7" out of a (100) plane, all grains generally were within 1" or 2" of the plane specified. The directions of boundaries were measured generally to within 1" on both upper and lower surfaces, and the average direc- tions were determined for use in calculating the grain boundary angles. Variations in grain boundary directions refer to deviations from average directions. Boundaries near the junction point for all specimens generally were very close to perpendicu-

Jan 1, 1951

By A. Gittens

In two recent papers stevens13,14 has compared the methods used by various investigators to calculate the contribution of grain boundary sliding to the total creep strain. In previous work Gittins15 has shown that the strain due to grain boundary sliding Egb may be estimated from the lateral, d, and vertical, v, displacements of a longitudinal marker line as it crosses a grain boundary. He obtained the formula, where nL is the number of grains per unit length measured on the specimens before creep, and \p and ?2 are, respectively, the angle between the grain boundary and the stress axis in the plane of the surface and normal to the surface (see Ref. 13, Fig. 1). The subscript L indicates that observations are made in a longitudinal direction parallel to the stress axis. It was generally found more convenient to measure the grain size of a specimen before creep; this was necessary to characterize the specimen. Stevens13,14 however prefers to define Egb in terms of NL, the number of grains per unit length after creep. Since nL - NL(l + €1) where cr is the total strain, Eq. 1 11 becomes The quantities d and ?, can be determined directly from the marker lines, while v and ?2 are found by sectioning normal to the surface. In the interior when symmetry considerations suggest that v = d and ?1 - ?2 the strain due to grain boundary sliding may be estimated from a suitable internal longitudinal marker line by the equation To determine cgb at the surface using either Eqs. |1| or [2] requires a large number of observations, particularly if many estimates of cgb are required, and also it is impossible to determine the variation of cgh with creep strain on the same specimen because the specimen must be sectioned to determine ?2. Gittins15 found that for a number of materials the sliding vectors d and v were related to each other so that provided one was measured the other could be estimated. Also during creep, grain boundaries tend to migrate to meet the surface at angles close to 90 deg,16 so that the term nL(v/tan?2)L was comparatively small when 4,- 90 deg. By determining the frequency distributions of ?2 on control specimens this term can be estimated without sectioning the creep specimen. In this way an empirical equation based on Eqs. |1| and |2| enables cgb to be determined with reasonable accuracy with fewer observations of the angles and sliding components. For B brass, the relationship between the sliding vectors indicated that ceb = 0.85nLVL . In Table I of Stevens paper this equation is stated to be incorrectly derived. However it should be pointed out that this is an empirical equation derived from Eq. |1|, based on a knowledge of the relationship between d and v and on the frequency distributions of ?1 and ?2 for a particular material under given experimental conditions. It was used only when these relationships were known, to reduce the number of observations required to estimate cb. Therefore the comment "derivation incorrect does not apply. Gittins did in fact make use of Eqs. |1| and 131. Author's Reply I must apologize to Dr. Gittins for the inadvertent misrepresentation of his work. Other slight errors in Table I have been pointed out to me. Langdon (No. 12 Table I), Gifkins (No. 7, Table I), and possibly other workers did not measure the number of boundaries per unit length after creep (A') but the corresponding quantity bejove creep (n). As Dr. Gittins points out, a completely analogous set of equations to those given in the paper can be derived by the same method: using the number of boundaries per unit length before instead of after creep. The basic equations corresponding to Eqs. [2] and 171 of the paper, from which all the others can be derived, are

Jan 1, 1968

By T. L. Loucks, E. T. Guerrero

Pressure drop characteristics in a system composed of two adjacent concentric regions of different permeability were studied. The differential equations for continuity of mass flow in the two regions were solved using the Laplace transformation and the necessary boundary conditions to give the pressure distribution in the composite reservoir, the resulting equation for pressure drop at the inner boundary was evaluated for a variety of composite reservoirs and compared with the results for a uniform reservoir. From this study it was found that under certain conditions the permeability in both zones, as well as the size of the inner zone, can be determined from the pressure drop curve. INTRODUCTION The theory for the pressure distribution and pressure build-up behavior of a well producing a single, slightly compressible fluid from infinite and finite homogeneous reservoirs was presented by Hornerl and Miller, Dyes and Hutchinson.2 Extensions on this original work to provide improved and extended interpretations and better agreement between theory and observed results have been made by Matthews, et a1,3 van Everdingen,4 Gladfelter, et al5 Stegemeierand Matthews,6 Hurst and Guerrero,7 and Perrine.8 More recently Lefkovits, et al,9 studied pressure build-up behavior in bounded reservoirs composed of stratified layers. Houpeurtl0 has suggested various approaches to the general problem of variable permeability and porosity but presented no analytic solutions for particular permeability variations. Albert, Jaisson and Marionll studied the finite composite reservoir and presented numerical solutions to the unsteady-state case and an analytical solution valid only for large times. They also studied the so-called pseudo-steady state for several examples of radial permeability variations. Very similar examples have been treated in the unsteady state with application to pressure build-up by Loucks in an unpublished manuscript. More recently Hurst12 has presented the complete point-sink solution (valid for all times) for the infinite composite reservoir. He applied these solutions to interference between oil fields along with an even more elegant application of his explicit solution to the material-balance equation including water influx. Mortada 13 approaches the same application by avoiding the point-source limitation but gives the solution for the aquifer region which is valid only for large times. Hopkinson, Natanson and Temple14 have treated both the finite and infinite composite reservoir obtaining the pressure distribution for the inner zone valid for large times. This paper presents a theoretical study of the pressure distribution in an infinite composite reservoir composed of two adjacent concentric regions of different permeability. The object was to determine the manner in which pressure drop at the inner boundary of a composite reservoir depends upon time, the permeability of each zone and the size of the inner zone. Expressions for the pressure distribution in both zones are developed which take into account the radius of the sink and are valid for small times as well as large times. It was felt that an understanding of the pressure drop behavior in various composite reservoirs would be of assistance in the interpretation of some pressure build-up curves which do not behave according to the theory derived for uniform systems. Often the region surrounding the wellbore is either more permeable or less permeable than the reservoir because of the various drilling and completion practices. The effects of reduced permeability due to drilling-fluid invasion and of increased permeability due to fracturing or acidizing need to be more carefully defined. Therefore, an equation for the pressure drop in a composite reservoir was developed, and the effects of both the permeability in each zone and the size of the inner zone were studied. STATEMENT AND SOLUTION OF PROBLEM BOUNDARY CONDITIONS AND ASSUMPTIONS The physical system studied was a composite

By B. B. Wood, M. J. Rzasa, E. W. Hough

An apparatus for the determination of fluid-fluid interfacial tension by the pendant drop method has been constructed. The apparatus is refined beyond those previously described in that the samples are introduced into an evacuated windowed cell without contacting air or mercury. Interfacial tension data are reported for the water-methane system between 74 and 280°F and 15 and 15,000 psi. The variation of wettability of the stainless-steel dropper tip with pressure and temperature was observed incidentally to the measurements. INTRODUCTION The most refined previous apparatus --for the determination of fluid-fluid interfacial tension at reservoir conditions was built by Hauser and Michaels.' These authors used the pendant drop method, previously investigated by Andreas, Hauser, and Tucker.' Recently, Fordham3 has made the pendant drop method an absolute one by numerical integration of the differential equation of drop shape. It is necessary to know the difference in density of the two fluids and the acceleration due to gravity in order to evaluate the interfacial tension from measurements of drop dimensions. Contact angle is not involved in the measurements by this method. Some precise tests of the method have been made at atmospheric pressure and 77°F by Douglas," who found agreement with established values to within about 0.1 per cent for water and air, cyclohexane and air, benzene and air, and benzene and water. No values of interfacial tension from the recent pendant drop apparatusJ have been published by Hauser and Michaels. However, values for the water-benzene and water-decane systems are given in Michaels' thesis5 or Dressures from 15 .to 10,000 psi and temperatures from 73 to 268ºF. Some determinations on gas-oil and gas-water systems in the range of 15 to 4,000 psi and 78 to 178°F have been made by Hozott,' by the drop-volume method. The capillary rise method has been used to investigate the interfacial tension in gas-oil systems at 88°F to several thousand psi by Swartz.7 Other determinations in gas-oil systems at pressures under 1,000 psia have been made by Jones: and Beecher and Parkhurst.9 The scarcity of data for pressures above 5.000 psi is apparent. APPARATUS An assembly drawing of the working section of the interfacial tenqion apparatus is given in Fig. 2. 'The endanant drop (A) is housed in a pressure chamber having glass windows (B). An agitator (6) is provided. The metal parts of the apparatus coming into contact with the sample are made of AISI: Type 316 steel. Drain grooves are provided around the whdows so that the sample in contact with the O-rings is not returned to the working section when the pressure is reduced. A schematic arrangement of the apparatus is given in Fig. 3. The working section containing the pendant drop (A) is filled by samples from bombs (B) with the aid of the vacuum system (C). The O-ring sealed pistons (D) used to separate the sample from the hydraulic fluid are shown together with the pressure production and measurement system (E). A front view of the apparatus is shown in Fig. 1. Most of the hydraulic system is at the top of the panel. The pump and displacement piston are at the lower right. The Variacs for the air bath heaters. the camera. and the vacuum gauge are a1so visible on the panel. The working section together with a window closure and a drop-forming tip closure are shown in Fig. 9. The carbon arc light source with filter is visible in the upper part of the picture. Two sides of the air bath with the impeller and a part of the convection shield can also be seen. The assembled air bath is shown in Fig. 10.

Jan 1, 1951

By H. D. Kessler, R. J. Van Thyne

Phase diagrams of the titanium-rich portion of the ternary systems from 0 to 10 wt pct Al and 0 to 1 wt pct 0, N, and C were determined. Micrographic analysis of annealed high purity arc melted alloys was the principal method of investigation and was supplemented by X-ray diffraction. TITANIUM-ALUMINUM alloys exhibit excellent properties, particularly for elevated temperature use. For this reason, the Materials Laboratory, Wright Air Development Center, sponsored an investigation of the effect of the interstitially soluble contaminants, oxygen! nitrogen, and carbon, on the Ti-A1 system. Using high purity arc melted alloys and micrographic analysis of annealed samples as the chief method of investigation, titanium-rich partial phase diagrams were determined for the ternary systems. Experimental Procedure Materials: The titanium used in the preparation of the alloys was iodide crystal bar (99.9+ pct pure) produced by the New Jersey Zinc Co. and Foote Mineral Co. The aluminum was obtained from the Aluminum Co. of America in the form of sheet. The given analysis was: Si, 0.0006 pct; Fe, 0.0005; Cu, 0.0022; Mg, 0.0003; Ca, <0.0006; Na, <0.0005; and Al, 99.99. High purity titanium dioxide purchased from the National Lead Co. was used in the preparation of the oxygen-bearing alloys. The spectrographic analysis of this material was as follows: SiO,, 0.07 pct; Fe,O,,, 0.002; A1,0,, <0.001; Sb,O,, <0.002; SnO,,, <0.001; Mg, <::0.001; Cb, <0.01; Cu, 0.0004; Pb, 0.002; Mn, <0.00005; W, <0.01; V, <0.002; Cr, <0.002; Ni, <0.001; and Mo, <0.002. Special spectroscopic graphite rod purchased from the National Carbon Co. was used in the preparation of the Ti-A1-C alloys. Alloy Preparation: Alloy ingots weighing 10 grams were melted in a nonconsumable tungsten electrode arc melting furnace using water-cooled copper hearths and a helium atmosphere. The arc was struck on a tungsten stud in the copper block to minimize contamination from the electrode. Details of the techniques have been reported.&apos;, &apos; Each ingot was inverted and remelted a minimum of four times to insure homogeneity, without opening the furnace. Remelting small control ingots of iodide titanium under similar conditions resulted in no measurable hardness increase, indicating contamination-free melting conditions were used. The alloy charges and resultant ingots were weighed to the nearest milligram. Only small weight losses were obtained upon melting, indicating that the actual compositions were very close to the nominal compositions. Check analyses substantiated this. Oxygen and nitrogen were added during ingot preparation as master alloys. An oxygen master alloy containing 25 wt pct 0 was prepared by melting iodide titanium and pressed titanium dioxide (40 pct 0) powder. The Ti-25 pct 0 alloy is more easily handled during weighing and charging than the pressed TiO, powder. Chemical analysis indicated that titanium-nitride received from an outside source contained large amounts of impurities (2.7 pct Ca). Therefore, a master alloy containing approximately 12 pct N was prepared by melting nitrided sponge titanium. As the sponge melted with difficulty, the alloy was diluted by addition of titanium to lower the melting point. The chemical analysis of the final alloy was 6.69 pct N. Both master alloys are friable and were used as —8 +16 mesh lumps resulting from crushing the ingots. NIelting the Ti-A1-0 and Ti-A1-N compositions five times produced homogeneous ingots. The preparation of homogeneous carbon-bearing alloys caused considerable difficulty. Alloys containing less than 1 pct C were prepared using spectrographic graphite rod, 1/8 in. diameter by 1/8 in. long. However, the graphite did not dissolve even with long melting times and many remelts. The ?/s in. pieces of graphite were used rather than powder because the low density powder is troublesome in arc melting.

Jan 1, 1955

By E. W. Hough, B. B. Wood, M. J. Rzasa

An apparatus for the determination of fluid-fluid interfacial tension by the pendant drop method has been constructed. The apparatus is refined beyond those previously described in that the samples are introduced into an evacuated windowed cell without contacting air or mercury. Interfacial tension data are reported for the water-methane system between 74 and 280°F and 15 and 15,000 psi. The variation of wettability of the stainless-steel dropper tip with pressure and temperature was observed incidentally to the measurements. INTRODUCTION The most refined previous apparatus --for the determination of fluid-fluid interfacial tension at reservoir conditions was built by Hauser and Michaels.&apos; These authors used the pendant drop method, previously investigated by Andreas, Hauser, and Tucker.&apos; Recently, Fordham3 has made the pendant drop method an absolute one by numerical integration of the differential equation of drop shape. It is necessary to know the difference in density of the two fluids and the acceleration due to gravity in order to evaluate the interfacial tension from measurements of drop dimensions. Contact angle is not involved in the measurements by this method. Some precise tests of the method have been made at atmospheric pressure and 77°F by Douglas," who found agreement with established values to within about 0.1 per cent for water and air, cyclohexane and air, benzene and air, and benzene and water. No values of interfacial tension from the recent pendant drop apparatusJ have been published by Hauser and Michaels. However, values for the water-benzene and water-decane systems are given in Michaels&apos; thesis5 or Dressures from 15 .to 10,000 psi and temperatures from 73 to 268ºF. Some determinations on gas-oil and gas-water systems in the range of 15 to 4,000 psi and 78 to 178°F have been made by Hozott,&apos; by the drop-volume method. The capillary rise method has been used to investigate the interfacial tension in gas-oil systems at 88°F to several thousand psi by Swartz.7 Other determinations in gas-oil systems at pressures under 1,000 psia have been made by Jones: and Beecher and Parkhurst.9 The scarcity of data for pressures above 5.000 psi is apparent. APPARATUS An assembly drawing of the working section of the interfacial tenqion apparatus is given in Fig. 2. &apos;The endanant drop (A) is housed in a pressure chamber having glass windows (B). An agitator (6) is provided. The metal parts of the apparatus coming into contact with the sample are made of AISI: Type 316 steel. Drain grooves are provided around the whdows so that the sample in contact with the O-rings is not returned to the working section when the pressure is reduced. A schematic arrangement of the apparatus is given in Fig. 3. The working section containing the pendant drop (A) is filled by samples from bombs (B) with the aid of the vacuum system (C). The O-ring sealed pistons (D) used to separate the sample from the hydraulic fluid are shown together with the pressure production and measurement system (E). A front view of the apparatus is shown in Fig. 1. Most of the hydraulic system is at the top of the panel. The pump and displacement piston are at the lower right. The Variacs for the air bath heaters. the camera. and the vacuum gauge are a1so visible on the panel. The working section together with a window closure and a drop-forming tip closure are shown in Fig. 9. The carbon arc light source with filter is visible in the upper part of the picture. Two sides of the air bath with the impeller and a part of the convection shield can also be seen. The assembled air bath is shown in Fig. 10.

Jan 1, 1951

By F. W. Jessen, H. Kazemi

A washing technique has been developed to form a spherical cavity in massive salt. The technique is, basically, a process of controlling the fluid motion in the cavity, the concentration distribution of brine, the rate of dissolution at the walls of the cavity, and the particular settings of the wash pipe, or pipes (inlet and outlet pipe) employed. For a particular arrangement of tubing and casing, fresh water enters from the casing annulus at a position above the bottom of the tubing, and the dissolved material leaves the cavity through the tubing near the bottom of the projected hole. The initial configuration of the cavity is cylindrical, representing the drilled hole situated at the axis of the projected cavity. As washing progresses the original hole is enlarged radially (any direction perpendicular to the axis of the hole). An inert fluid (generally a hydrocarbon, natural gas, or air) which serves as a blanket is injected through the annular space between the original hole and the casing. The controlled downward motion of this blanket maintains the upper edge of the brine region that is expanding on the surface of the projected sphere. A large spherical glass container and a radial model were used to investigate the flow patterns and the concentration distribution of brine occurring during the progress of solution of the salt. Aluminum flakes and dye were injected and flow patterns were observed and recorded on motion picture film. Based on the results of these model studies and other work carried out in this laboratory, the controlled washing technique was formulated. INTRODUCTION Underground cavities leached in salt beds and salt domes have been used extensively for storing hydrocarbons. Little attention has been focused on the shape of the cavities as long as large volumes were obtained and the cavities were structurally stable. The general process involves circulating fresh water and removing brine. Two distinctly different circulating systems can be employed, each of which yields characteristically different shapes. By far the most generally accepted method of washing storage caverns in salt domes is the direct circulation system. Water is introduced through the innermost pipe of a concentric pipe system, and brine is withdrawn through the annulus. In the reverse-circulation method, water enters through the annulus and is discharged through the smallesc tubing string. The size of the operation, and hence the size of tubing and casing used, depends on such factors as cavity volume, length of hole, availability of water, disposal of brine and power requirements. Underground caverns are from 100 to 1,000 ft or more in length, and when completed vary from 40 to 100 ft in diameter, providing storage of 100,000 bbl or more. The volumes of water required per volume of salt removed vary from 6 to 7 for the reverse circulation method to 10 to 11 for the direct circulation method. Up to 80,000 BWPD are often circulated. In the direct circulation method, because water enters near the bottom of the projected cavity, solution of salt is greatest at this point, particularly in view of the fact that when the washing is begun turbulent flow undoubtedly exists in the immediate vicinity of the discharge of the inlet water. As the diameter of the hole increases, flow rates also are increased, so perhaps the condition of fluid turbulence is maintained for some time. During the later stages of leaching, when capacity of equipment may be the limiting factor in maintaining flow rates, there may still exist some turbulence adjacent to the point of influx; however, for the most part laminar flow conditions prevail. There appears, therefore, rather good evidence to indicate that the state of fluid motion is responsible for the typically shaped cavity which results from such washing — namely a cylindrical form, generally somewhat larger at the bottom than at the top. Depending on the number of so-called stages which might be employed, the walls or surfaces of the salt diminish rather uniformly from bottom to

Jan 1, 1965

By J. A. Stachura

Continuous mining machinery provides the coal industry with one way to compete for a larger share of the total energy market. Various types of machines are discussed and some of the problems with continuous miners, encountered by operators, are reviewed. Equipment manufacturers are working with mine personnel to provide solutions for problems that arise. While coal production over the past 25 or 30 years has been on a horizontal plane, coal&apos;s share of the total energy market has declined. To participate more effectively in this total energy market, it is necessary to produce coal more efficiently. It is the obligation of all management, employes, and mining departments to gear the deep mining industry to the rapid progress and changing of today&apos;s modern industry. This can be accomplished in the near future with the selection of the proper type of continuous miner best suited to each operator&apos;s individual situation. In most mining operations there is tremendous incentive to undertake the continuous mining program. It can reduce the size of the mine greatly by permitting a minimum of working places; it makes pillar recovery work more efficient from the standpoint of overall cost, amount of coal recovered, and safety. The work force can be reduced materially permitting closer and more efficient supervision. It simplifies maintenance because equipment can be more readily standardized. The trend of the coal market favors the use of continuous mining machines. Although there appears to be a general feeling that continuous mining is still a relatively new program and will be slow in replacing conventional mechanical equipment, the fact is that tremendous strides have been made since the first machines were installed in 1948. This program is advancing at approximately the same rate that mobile loading machines replaced hand loading. From 1948 to 1955 there were approximately 450 continuous mining machines in service. In October 1959, a survey revealed that there were more than 700 continuous mining machines in service. Many operators have expressed a desire to undertake this program, but they feel that they could not do so at this time because of one or more of the following reasons: 1) the thickness of their coal seams, 2) seam characteristics, 3) soft bottoms, 4) bad roof conditions, 5) size consist, 6) insufficient flexibility in machines, 7) difficult ventilation problems, and 8) high maintenance costs. With the realization on coal about the same today as it was in 1948, or slightly less and since coal is still failing to participate to a greater degree in the total energy market, it is not surprising that the coal industry is desperately exploring more economical methods for deep mining. The manufacturers are aware that the coal industry is willing to invest in continuous miners if the equipment is built for maximum flexibility, will produce higher tons per man, and assure long life between overhaul programs. CONTINUOUS MINING MACHINES Before discussing details regarding the selection of a continuous miner, let us have a preview of some of the continuous mining machines which are available to the coal industry today. Jeffrey Manufacturing Co.: The machine shown is the Jeffrey 76 A.M. Colmol. This is their most widely used miner, and has been particularly successful in central Pennsylvania and in high-wall mining in western Kentucky. One of the outstanding features of this auger-type miner is its portability. The entire mining range can be changed from its lowest point to the maximum height without stopping the mining operation. Jeffrey 76 B.M. Colmol: This machine is similar to the 76 A.M. model; however, it is built bigger and stronger for a mining range of 50 1/2 to 72 in. This is the model that is now available (Fig. 2). Jeffrey has added two arms to the top row, omitted the odd arm in the bottom row, thus permitting a 50 pct larger throat opening. This eliminates one

Jan 1, 1961

By J. S. Brown, A. G. Guy

With the exception of the work of Tammann and Hartmann,1 no published information has been found on the structural changes produced in eutectic structures as the result of heating following plastic deformation. In part this lack of information may be due to the fact that many eutectic structures contain an intermetallic compound as a prominent phase, and as a consequence have been considered to be unworkable. For example, Tammann and Hartmann were able to obtain useful data only on those alloys that they could greatly reduce in thickness by cold rolling. This restriction placed on the investigation of alloys containing intermetallic compounds has been largely removed by the work of Savitskii2 which showed that large deformations of such alloys can be produced by relatively slow compression at temperatures near the melting range. It was possible, therefore, to carry out the present work on a range of binary eutectics including one composed of two intermetallic compounds. The essential results obtained on the alloy systems studied are illustrated by the Pb-Mg eutectic containing 33.2 pct Mg, Fig 1. The cast structure, Fig la, was obtained by melting together magnesium of 99.8 pct purity and chemically pure test lead, casting into a heated, small steel mold, and furnace cooling in the mold from about the eutectic temperature. The fairly coarse eutectic structure thus obtained was too brittle to work at room temperature without cracking. Fig 16 shows the worked structure obtained by compressing a 1/2-in. cube 70 pct in about 15 sec at 550°F and then water quenching. The pronounced changes in the distribution of the two phases produced by heating the worked alloy at 850°F for 1 hr are shown in Fig lc. Recrystallization of both phases appears to have taken place, and the mechanical properties of the cast alloy must have been significantly changed by the working and heat treatment. Similar results were obtained with the Mg-59.5 pet Bi, Mg-36.4 pet Sn, Mg-65.4 pet Cu, and Bi-40 pet Cd eutectics, only the last of which could be worked at room temperature. Tammann and Hartmann reported a thickening and shortening of the needles of the eutectics which they heated about 10°C below the melting range for 1 hr after drastic cold rolling. They found the following eutectics, given the indicated amounts of reduc- tion, to have a granular structure after heat treatment: Sn-9 pet Zn (98 pet); Cd-82.5 pet Pb (60 pet); and Bi-43.5 pet Pb (90 pet). On the other hand the alloy Al-11.7 pet Si (60 pet) showed no change after heating. Tammann and Hartmann observed a distinct shrinking of the needles in unworked eutectics subjected to heat-treatment. In the present work inappreciable change in the eutectic structure was found on heating undeformed alloys. In summary, it appears that eutectic structures can be recrystallized into a "spheroidized" condition by heating near the eutectic temperature after severe deformation. If the eutectic contains one or more brittle phases the necessary deformation can be accomplished by pressing at high temperatures. It is reasonable to expect that this tendency towards equiaxed grains from the plate- or needle-like eutectic structure should be general since the energy relations and mode of growth in recrystallization are so different from those that hold for eutectic crystallization. References 1. G. Tammann and H. Hartmann: Ztsch. Melallkunde (1937) 29, 141-144. 2. E. M. Savitskii: Doklady Akad. Nauk S.S.S.R. (1940) 62, 349-351. Abstr. in Melal Prog. (July, 1949) 56, 126, 128.

Jan 1, 1950

By J. L. Carne

ORE control is a matter of planning and supervision based on a foreknowledge of the content and distribution of ore. The Inspiration orebody is predominately a copper-sulphide blanket, overlain by an oxidized zone of copper silicates, copper carbonates, and barren capping. Most of the ore is treated by leaching, and the optimum requirement of this method is the goal toward which the mining schedule is aimed. Both open-pit operations and underground mining are used. The problems of ore control at Inspiration are: 1-maintenance of metallurgical balance, 2-conservation of oxide ore, and 3-mining out of the orebody at an average grade which parallels that of the reserve figure. Prior to the fall of 1926 all of the Inspiration division ores were treated by flotation, but the mixed ores of the Live Oak-Keystone section carried too large a proportion of copper in the form of chrysocolla for satisfactory flotation. For this type of mixed ore the leaching process now in use had been worked out, and the plant was put into operation in the fall of 1926. The process is known as the ferric sulphate leach, and the leaching solvents contain both ferric sulphate and free sulphuric acid. Sulphide copper in the form of chalcocite is leached by the ferric sulphate, and the oxidized copper minerals are dissolved by the sulphuric acid. From the beginning of operations to the present time the plant has treated some 67 thousand tons of ore having an average copper content of 1.142 pet, of which 0.605 pct has been in the form of oxidized copper minerals. The plant is currently being operated at the rate of 11,500 tons per day, 7 days per week. However, this tonnage is produced in 6 days of mine operation. The average current grade is approximately 1 pct copper, of which about 50 pct is present as oxidized or acid-soluble copper. Close control of metallurgical procedures is a vital factor in operation of the plant and is in turn dependent upon careful regulation of feed. An excess of sulphide copper requires the presence of more ferric sulphate in the leaching solvents. On the other hand, an excess of ferric sulphate in the presence of a low sulphide feed seriously reduces the efficiency of electrolytic precipitation in tank house operations. This condition must be avoided at all costs. An additional factor must be considered. It is known that the sulphide content is predominant in the ore which remains in the reserve. To maintain the necessary sulphide-oxide proportion, so that the entire reserve will mine out at both a grade and a sulphide-oxide ratio that will be permissible throughout the remaining life of the property, it is obvious that the oxide reserve must be currently preserved to as great an extent as possible. Fortunately much of the oxide reserve is found in the open-pit operation. This happy circumstance adds flexibility to the procedure and makes it possible to maintain the close regulation necessary to insure best overall results, both mining and metallurgical. The two ore streams from the pit and underground operations join at the coarse-crushing plant, and proper control must be exercised before the ore reaches this point. The open pit is currently providing about 55 pet of the ore and underground operations the balance of production. Both operations are under a single superintendent so that the closely interrelated problems may be more readily controlled. The least flexible of the two producing units is the underground mine, where the mining method is block caving. Although a block of ground may be undercut and developed, characteristics of the material determine its caving action. The ore in the chutes must be drawn. The area currently mined from underground is in a zone predominately sulphide and is generally

Jan 1, 1952

By S. S. Lisnyak, B. D. Lichter

An important question in the study of the "hot corrosion" phenomenon (i.e., accelerated oxidation of Ni-Cr-base and Co-Cr-base "superalloys" in the presence of sulfur) is the condition of formation and physico-chemical properties of different sulfides in the system Ni-Co-Cr-S. seyboltl has observed the presence of ((chromium-rich" sulfides of compositions M3S4, and M2S3 in the scales of superalloys after hot corrosion; however, as he points out, much confusion exists as to the identity of sulfides found on Ni-Cr and Co-Cr alloys. According to the literature,&apos; ternary sulfides, e.g., NiCr2S4, (monoclinic structure) and CoCr2S4 (spinel structure) exist in these systems. Therefore, it is likely that these compounds are found in the scale of alloys undergoing hot corrosion. At present this possibility has not been discussed in the literature. Accordingly, we have begun investigation on the properties of ternary sulfides and their mutual interaction. The magnetic and electrical properties of pure NiCr2S4 and pure CoCr2S2 have been previously determined."-&apos; In the present work we have studied the interaction between these sulfides at high temperatures by means of X-ray diffraction and magnetic susceptibility. The measurements were carried out at room temperature after appropriate thermai treatment of samples at high temperatures. For alloys containing the three elements nickel, chromium, and cobalt this interaction may be of importance in the study of the hot corrosion phenomenon. The compounds NiCr2S4 and CoCr2S4 were prepared from stoichiometric amounts of the elements and CoS in the case of CoCr2S4. Samples were mixed and sealed in evacuated silica tubes, slowly heated to 900&apos; to 100O°C, and held at temperature for a total of 120 hr (NiCr2S4) or 80 hr (CoCr2S4) with intermediate re-grinding~. X-ray diffraction showed a pure spinel structure for CoCr2S4 and a monoclinic structure for NiCr2S4. Samples of mixtures of the two ternary sulfides were prepared with different compositions, see Table I. Samples were heated for a total of 80 hr at 900&apos;C in evacuated silica tubes, with one intermediate regrind-ing. The capsules were slow-cooled to room temperature in the furnace. Samples for X-ray diffraction were prepared by placing powder on a glass slide with vaseline. Dif- fractometer traces were obtained on a G.E. XRD-5 diffractometer using a chromium tube and vanadium filter (40 kv and 31 ma). The size of the spinel unit cell was determined from the eight highest angle peaks (80 deg < 2b < 160 deg). Calculated lattice parameters were plotted vs cos B . ctn 0 and extrapolated to 6 = 90 deg. Measurements of the magnetic susceptibility were carried out at room temperature using the Faraday method in a magnetic field of 3000 G and using a Cahn RG automatic microbalance. The system was calibrated from the well-established susceptibilities of platinum and palladium: (Xpt = 0.968 x 10-6 g-1 and Xpd 7 5.04 x 10~6 g-1). The weight of samples were approximately 0.200 g. X-ray diffraction patterns for unsintered mixtures showed Bragg peaks from both the spinel (CoCr2S4) and monoclinic (NiCr2S4) structures. After sintering no monoclinic peaks were observed in samples containing up to 40 mol pct NiCr2S4. However, the spinel peaks were displaced to higher angles with increasing

Jan 1, 1970

By E. S. Machlin, C. W. Chen

RECENTLY Chen and Machlin&apos; proposed a mechanism for intercrystalline cracking in metals during high-temperature stressing. According to this mechanism the formation of voids at grain boundaries is primarily responsible for intercrystalline cracking. A model has been provided to demonstrate the initiation of submicroscopic cracks and voids at jogs of grain boundaries where grain boundary sliding is inhibited. Submicroscopic cracks can grow as a result of either further grain boundary sliding or localized tensile stress. In the former case, it is believed that grain boundary sliding produces more voids which link together to produce macroscopic cracks and which may lead to the eventual failure of the metal. Concurrently, Nield and Quarrell2 reported their interesting results obtained in a systematic investigation of intercrystalline cracking in two aluminum alloys under various creep conditions. Their observations are generally in agreement with the above mechanism, especially the conclusion that voids are formed as a direct consequence of grain boundary sliding. On the basis of the volume fraction occupied by voids, they could find no confirmation of vacancy condensation as the mechanism for void growth. Furthermore, an important feature of intercrystalline cracking has been likewise pointed out by them that the majority of cracks are not formed at grain corners. Nield and Quarrel1 meanwhile emphasized the importance of grain boundary migration by designating it as one of two main processes operative in the mechanism of crack formation during creep. The designation seems unnecessary because overemphasis of grain boundary migration only complicates the mechanism of void formation. There are two reasons which militate against the inclusion of grain boundary migration in the mechanism of void formation. In the first place, the formation of intercrystalline voids per se does not require grain boundary migration. Secondly, in addition to grain boundary migration, void formation may be minimized by any other process such as plastic deformation which is capable of relieving localized stresses around jogs. Chang and Grant3 have shown that intercrystalline cracking is prevented in aluminum by lattice bending in high stress regions. The influential role played by grain boundary migration in creep has also been realized in our studies. In several cases, voids did not appear at all in grain boundaries whenever grain boundary migration took place prominently during creep. The purpose of this paper is to discuss the effect of grain boundary migration on the formation of intercrystalline voids and other related rupture properties. Experimental evidence indicates that in an unstable grain structure void formation may be markedly modified by structural changes. The abnormally high ductility and the transcrystalline mode of fracture observed in copper at elevated temperatures reveals that effective grain boundary migration minimizes void formation. Grain boundary migration has long been known as a common high-temperature phenomenon in metals with the grain configuration in a nonequilibrium state. Its effect on ductility and mode of fracture has not been recognized until recently.4 Since the introduction of the term "Equicohesive Temperature," the conventional belief has been that below the equicohesive temperature the ductility of metals increases moderately with decreasing temperature until the ductile-to-brittle transition temperature of fracture is reached. In this temperature range, metals fracture in a ductile mode with a "cup-and-cone" fracture surface. Above the equicohesive temperature, ductility remains invariably low and decreases slightly with increasing temperature. The mode of fracture is strictly brittle and intercrystalline. Typical examples have been shown for a brass and copper in Fig. 1 and 9, respectively, in the paper by Greenwood, Miller, and Suiter.5 The observation in the upper temperature range that ductility of metals is low and insensitive to temperature may be explained in terms of void formation at grain boundaries. It is also in accordance with the findings of McLean6 and Fazen, Sherby, and Dorn7

Jan 1, 1961

By R. S. Wagner, H. Brown

Criteria for nucleation with the aid of twin planes during crystal growth from the melt are discussed. It is shown experimentally that bismuth crystals can grow from a subercooled melt in a twinned bismdtic form. A mechanism of growth based on the presence of at least me twin plane is proposed. It is well known that faceted growth can be observed in crystals grown from the vapor phase, dilute solutions, or from the melt. Faceted growth, in which the crystal is bounded by its slowest growing faces, will occur if the growth rate is strongly orientation dependent. The addition of atom layers on a facet plane can only occur by two-dimensional surface nucleation or with the aid of an imperfection. Nucleation with the aid of dislocations was proposed by rank&apos; and observed to be of particular importance in crystal growth from the vapor phase. Nucleation with the aid of two-dimensional imperfections, notably twin planes, was suggested by stranski2,3 and Frank.4 A twin plane, terminating at the growth interface, can form a reentrant step at which nucleation can occur at a much smaller super-saturation (or supercooling) than required for two-dimensional surface nucleation. Nucleation by a twin plane usually results in a fast growth rate along a crystallographic direction parallel to the twin plane. Such a nucleation mechanism, based on the presence of a twin plane, has been used by Dawson5 to explain the growth and morphology of sheet-like crystals of paraffin n-hectane. In recent years more evidence was found that nucleation by twin planes occurs frequently in crystal growth from the vapor phase and from dilute solutions, for example, in cadmium,&apos; barium titanate,7 silver,8 silicon9 and gallium arsenide.10 In crystal growth from a supercooled melt, however, nucleation by twin planes has so far only been observed in materials with the diamond or zinc blende structure. Bennett and Longini11 were the first to recognize the important role a single twin plane plays in the growth of germanium dendrites. Subsequently, it was found that a prerequisite for continued propagation of germanium dendrites is the presence of two parallel twin planes which form a self-perpetuating system of nucleation sites.12 Sili- con and some III-V compounds such as InSb also grow dendritically by twin plane nucleation. It appears that the following criteria must be satisfied in order that nucleation with the aid of twin planes can occur: A) The growth form of the material must be faceted." B) The formation of twin boundaries, by a fault in layer sequence during growth, by plastic deformation, or by an accidental meeting of properly oriented crystals, must be possible. C) Twinning must form a reentrant step where the twin boundary terminates at the faceted growth interface. D) These three conditions are necessary, but in certain cases not sufficient for continued crystal growth with the aid of a twin plane. Depending on interface morphology, a combination of more twin planes is sometimes required to form a self-perpetuating system of nucleation sites. This investigation was carried out with the idea in mind that nucleation with the aid of twin planes is a more general phenomenon and should occur in those materials, grown from a supercooled melt, which satisfy the criteria outlined above. It has been found that crystals of high-purity bismuth grown from a supercooled melt can grow by the aid of a twin plane. In the first two sections the faceted growth form and the twinning elements of bismuth are discussed. In the last section prismatic crystals of bismuth, which appear to grow with the aid of a deformation twin are discussed.

Jan 1, 1962

By R. J. Sherman, M. R. Achter

Creep rates have been measured for nickel at 1200°F in air and in vacuum, and related to the depth of surface cracks in the specimens tested in the two environments. The surface cracks were observed to grow faster in air than in vacuum in both short-time and long-time tests. Crack depths, however, could be correlated with creep rates only in the short-time tests. Although no cracks were observed in a relatively brittle Ni-Cr-A1 alloy creep tested at 1300°F, the appearance of alloy specimens fractured after interruption in creep indicated that there was a decrease of intergranular cohesion resulting from the diffusion of atmospheric gases into grain boundaries. PREVIOUS investigations1-3 have demonstrated that the effect of atmosphere on the high-temperature strength of nickel and nickel-base alloys may be reversed by changes in the stress or temperature of the test. At high stress and low temperature the creep-rupture life is longer in vacuum than in air, while at high temperature and low stress the relative strengths are reversed. A mechanism to explain this behavior was proposed based on two competing processes. Oxidation hardens and strengthens a metal, but adsorption of gas, by lowering surface energy, reduces the work required to propagate an intergranular crack. The controlling process is determined by temperature and stress. Basic to this mechanism is the concept that environment determines the ease of propagation of intergranular cracks and thus affects creep rate and rupture life. To explore the mechanism in greater detail, this investigation was undertaken to determine the effect of atmosphere on crack initiation and propagation rates in nickel1 and a relatively brittle Ni-Cr-A1 alloy.3 EXPERIMENTAL PROCEDURE The materials were the same as used previously. Nickel of 99.8 pct purity had the following impurity content: 0.02 pct Co, 0.03 pct Fe, 0.02 pct Mg, 0.03 pct Si, and 0.008 pct C. Rods were cold swaged from 1/2 in. to 3/8 in. in diam and machined into speci- mens with gage sections 1/4 in. in diam by 1-1/4 in. long. They were annealed in vacuum at 1600" F for 1 hr to achieve a grain size of 0.07 mm. The alloy was composed of 19.1 pct Cr, 3.6 pct Al, 1.7 pct Si, 0.57 pct Fe, 0.10 pct Mg, 0.027 pct C, 0.004 pct S, and the balance Ni. Sheet specimens of 0.500-in. width and 1.25-in. gage length were machined from 0.033-in.-thick strip and annealed in vacuum at 2000° F for 2 hr, resulting in a grain size of 0.036 mm. Large amounts of an intergranular phase were introduced as a result of the anneal. Creep tests on both materials, using equipment previously described by Shahinian; were conducted in air and in a vacuum of 1 x 10-5 mm Hg. They were continued to rupture and interrupted at various stages of the test. Although extensions were measured from dial gage readings of movement of the lever arm, it is considered that valid comparisons of creep rate may be made in this manner.l Two parameters were measured metallograph-ically* on longitudinal sections of nickel specimens interrupted during creep—the mean depth of surface cracks 2, and the density n as the number of cracks per unit length of surface. They were combined into one parameter by the relation p = n-d [1] As used here, p is equal to the total of crack depths per unit length of surface. RESULTS Nickel. It is well known that the incidence of intergranular cracking is increased with increasing rupture life. Indeed, it is evident in Tables I and I1

Jan 1, 1962

By P. T. Carter, A. B. Murad, H. B. Bell

The distribution of manganese and oxygen between molten iron and FeO-MnO-SiO2 slags not saturated with SiO2 has been determined and used to calculate activities of MnO and SiO2 in MnO-SiO2 slags. These were found to be intermediate between the corresponding activities in FeO-SiO2 and CaO-SiO2 slags. THE equilibrium constant for the reaction between molten iron containing manganese and slags containing FeO and MnO, namely: FeO(slag) + Mn = MnO (slag) + Fe(1iquid) is most conveniently represented by: (MnO) Kmn== (FeOHMn] [Fe] is omitted, since for dilute solutions of manganese in iron, afe is approximately constant. When activities are used for (MnO), (FeO) and [Mn], Kmn is a true equilibrium constant and will apply to all types of slags, but when weight percentages are used, the values obtained for Kmn for different slags vary considerably. The equilibrium between iron containing manganese and relatively pure FeO-MnO slags has been investigated by several workers;1-4 the most recent investigation reported is that of Chipman, Gero, and Winkler.4 Their results, corresponding to slags containing up to 4 pct SiO2, were represented by the equation: 6440 log KMn = +2.95 In this case both slag and metal may be assumed to be ideal solutions, therefore the values of Kmn so derived represent the true constant for the manganese reaction. As the molecular weights of MnO and FeO are almost equal, weight concentration of these oxides may also be used in the above expression. Acidic oxides such as SiO2 and P2O5 affect the activities of FeO and MnO differently, so that when total concentrations by weight of FeO and MnO are used in the above expression for Kmn the values obtained are no longer constant. These will be denoted by K&apos;mn. Körber and Oelsen5 investigated the manganese reaction using silica-saturated iron-manganese-silicate slags and found: 7940 logK&apos;mn =3.172 This corresponds to Kmn values much higher than those obtained for pure oxide slags. The results of Körber and Oelsen, and Chipman, Gero, and Winkler are summarized in Table I. In the present investigation it was decided to study the manganese reaction using iron-manganese-silicate slags not saturated with silica, and which fell mainly between the orthosilicate join 2FeO . SiO2 - 2MnO.SiO2 and the FeO-MnO side of the ternary system FeO-MnO-SiO2. It has been shown" that the phases present in solidified slags of this part of the diagram are (FeO, MnO) and (2Fe0.Si02, 2Mn0-SiO,) solid solutions. Such an investigation would be of interest in deoxidation and also gives information on activities in liquid slags. This equilibrium has not as yet been investigated successfully. Hilty and Crafts7 attempted to examine this reaction in a rotating crucible furnace, but were unable to obtain suitable slag samples. In the present investigation one series of experiments was carried out in a rotating crucible furnace, because the success of Taylor and Chipman8 with such a furnace in their study of oxygen distribution between molten iron and (CaO, MgO) — FeO-Si0, slags suggested that it would minimize contamination of the slag by the crucible material. A second series was carried out using a wire-wound resistance furnace. Rotating Crucible Furnace Experiments In all cases the metallic charge consisted of 800 to 1000 g Armco iron containing 0.02 pct C, 0.03 pct Mn, and traces of Si. Manganese and silicon additions consisted of electrolytic manganese (99.9 pct)

Jan 1, 1953

By C. R. King

Most of the acid volcanic glasses such as obsidian, perlite, pitchstone, pumice, and pumicite (volcanic ash) are susceptible to some expansion if suddenly subjected to a suitably high temperature in a properly designed furnace, and subsequently suddenly cooled. Expansion results from the action of chemically combined or dissolved water expanding as a vapor within the softened heated rock particles. This expansion forms countless minute bubbles within the pasty mass of the natural glass particles. If the particles are cooled before these bubbles can escape, the resulting products are cellular, more or less spherulitized glass froths or hollow glass spheres of many types. Chemically, they are essentially aluminum silicates containing about 70 to 75 pct silica, 10 to 16 pct alumina, and 2 to 7 pct sodium plus potassium oxides. They are relatively resistant to attack by acids or alkalies, are resistant to heat up to over 1000°F, and are completely inert to insect or fungus attack. These products are of great potential value in many branches of industry as insulation materials, aggregates, fillers, abrasives, and additives. By proper selection of the perlite rock type and control of processing conditions, expanded perlite of a bulk density varying from about 2 to 20 Ib per cu ft can be • made. The physical properties of the particles comprising a product of a given bulk density also may be varied within wide limits of porosity, water absorption, and crushing strength. In general, crushing strength of expanded perlite increases in direct relation to increase in bulk density, but insulating value varies in inverse ratio to bulk density. The selection of a particular grade of expanded perlite for a given use as an aggregate is therefore always a compromise between insulating value, lightness, and friability. If porosity and water absorption are factors affecting the use of the material, factors other than bulk density are important. Some types of perlite rock tend to decrepitate excessively during expansion, resulting in a highly porous or even hygroscopic product of high friability relative to the bulk density of material produced. In general, treatment of any good perlite rock below the temperature necessary for maximum expansion, or insufficient time in the hot zone of the furnace for effective heat penetration to the core of the rock particles will result in some decrepitation and high porosity in the expanded product. On the other hand, exposure of the material to the temperature required for optimum expansion for a period of time slightly longer than that necessary for proper heat absorption will result in a slightly heavier product of extremely low porosity, i. e., a glazed surface. It is beyond the scope of this paper to describe in detail the rock types and processing methods used to produce the many types of expanded perlite in present use, or that may be produced to fill the present and future needs of industry. A few phases of the economics involved in processing and selling products made from this abundant and cheap mineral raw material, plentifully distributed in large and relatively accessible deposits in most western states and in other areas within economic shipping distance of large centers of consumption, will be treated with particular reference to the Los Angeles area. Relation of Balk Density to Use and Cost of Production Perlite differs from most other lightweight aggregates and fillers in that the raw material (perlite rock) may be quarried much as rock arid sand is mined, and then shipped into consuming areas as crude rock in open gondola cars at correspondingly low freight rates and handling costs. At processing plants in or near large consuming areas the rock is converted into relatively fragile, very bulky products which in most cases are used within a short haul of the processing plant or enter into a manufactured product made at the site of the perlite processing plant.

Jan 1, 1950

By D. L. Martin

THAT small amounts of impurities have a harm-J- ful effect on the malleability of metals and alloys is well-known. One common type of em-brittlement involves the formation of a small quantity of eutectic at the grain boundaries, and is typified by sulfur embrittlement of nickel. Another example of eutectic embrittlement—sulfur embrittlement of cobalt—is described in this report. In the preparation of specimens for a study of Co-Pt alloys, it was observed that the hot swagabil-ity of the alloys appeared to be influenced by the grade of cobalt used as melting stock. The cause of the hot-shortness was not traced to any particular impurity, although sulfur was suspected.&apos; The damaging action of sulfur on the malleability of cobalt has not been generally recognized,&apos;; in spite of the fact that the Co-S phase diagram8 eveals the same basic conditions—low solubility and eutectic formation—responsible for sulfur embrittlement of iron and nickel.7, 8 Apparently sulfur embrittlement has not been a serious problem in the fabrication of cobalt alloys. One related factor is likely the limited commercial experience with high cobalt alloys, since the predominant use of cobalt has been in alloys containing less than 75 pet Co. A series of Co-S alloys was prepared and studied to establish the effect of sulfur on the hot working characteristics of cobalt. Specimens, 5/8 in. diam by 4 in. long, were prepared by vacuum melting in magnesium oxide crucibles and casting in a copper mold. Two grades of low sulfur electrolytic cobalt were used as the basic material for the study, one from Johnson, Matthey and Co. and the other from the International Nickel Co. Each contained about 99.5 pet Co and had a nominal sulfur content under 0.005 pet. The sulfur was added initially as cobalt sulfide powder. Later, some low sulfur alloys were prepared by diluting the high sulfur alloys with cobalt. Trouble was experienced in controlling the sulfur content. Apparently much of the cobalt sulfide powder was lost during melting, as most of the samples contained a lower sulfur content than was added. The alloys were evaluated for hot brittleness by heating to 1000°C in a hydrogen furnace and swaging in air. The results of these tests are summarized in Table I. All the alloys containing less than 0.008 pet S were successfully hot swaged to 1/4 in. diam. The bars containing more than 0.015 pet S could not be swaged because of the formation of intercrystal-line cracks similar to those illustrated in Fig. 1. Examination of the microstructure of the cast bars revealed cobalt sulfide eutectic at the grain boundaries, Fig. 2. The sulfide was not always continuous at grain boundaries in bars that were hot embrittled but, in general, the particles did form a network that could account for the brittleness above the eutectic temperature, 880°C. There is no question about the brittle nature of a specimen exhibiting a continuous sulfide network such as is shown in Fig. 2b, though a sulfide distribution similar to that in Fig. 2a is marginal. This particular bar cracked when hot-swaged. However, other bars with lower sulfur content but with some sulfide phase at grain boundaries were successfully worked. The reduction of area of a hot tensile test specimen was also found to be a sensitive indicator of sulfur embrittlement. The variation of reduction of area with sulfur content is shown in Fig. 3 for specimens fractured at 900°C in an evacuated capsule. The ductility of cobalt is greatly reduced when the sulfur content exceeds 0.005 pet. Similar results were obtained for alloys tested at 800°C, below the eutectic temperature. The upper sulfur embrittlement limit of 0.015 pet, Table I, agrees with the observation of Kalmus8 hat

Jan 1, 1957

By T. S. Spice, H. L. Lovell, R. W. Utley

With the increased demand for lightweight aggregate, such materials have been manufactured from slags, clays, slates and, to a minor extent, the refuse of coal preparation processes. The latter source is attractive due to current interest in eliminating air pollution and improving the unsightly appearance of refuse piles as well as potential economic advantages, if a satisfactory product can be manufactured. A study has been made relating the composition of coal refuse, expressed as washability data, and the properties of a resulting aggregate. Three different refuse samples (bituminous and anthracite) were separated at gravities ranging from 1.4 to 2.96. Their chemical composition was determined. Aggregates were prepared in the laboratory from these fractions before and after ashing, at temperatures between 1250&apos; and 1350°C. The specific gravity, expansion and compressive strength of the products were measured. The response of the refuse to bloat is related to the chemical composition of the ash to yield a glass of desirable viscosity and to the presence of a material which will form a gas in the appropriate temperature range. Carbonaceous material within the particle is a negative factor since after the glassy phase forms, oxygen cannot enter the mass thus inhibiting bloating. Precombustion of the refuse is also detrimental since it removes substances of gas-forming capability. The fraction sinking at 2.60 yielded an aggregate which had the lowest specific gravity, greatest expansion and greatest compressive strength. The purpose of this study was to seek and evaluate possible relationships between the composition of coal refuse, as expressed by washability data and factors affecting the production of a lightweight aggregate from refuse by bloating. The study was related to an intense program in the Department of Mineral Preparation at the Pennsyl- vania State University to study the possible elimination of air pollution from coal refuse fires by producing a low-carbon secondary refuse. Another phase of this program is considering possible uses of such a secondary refuse. Thus one study was to determine if a lightweight aggregate could be produced from this new refuse material and what effect the nature of refuse beneficiation would have upon the characteristics of a commercial aggregate product. It was hoped that these studies would assist in the design of a process and in establishing the optimum specific gravities at which refuse separation could be made in respect to the production of a low grade fuel from the float product and a raw material for lightweight aggregate from the sink product. The combination of producing a saleable low grade fuel and a lightweight aggregate, while at the same time minimizing disposal costs and air pollution contributions would be attractive to the coal mining industry. MECHANISM OF BLOATING Austin, Nunes and Sullivan,1 Ehlers,3 Everhart, 4 Riley7 and others, have stated that bloating is an expansion process in which two essential conditions exist simultaneously. These are: the development of a glassy phase over a relatively wide temperature range (the viscosity of this glassy phase plays a major role in the retention of the evolved gases) and the evolution of gases (SO2, SO3, CO2 and O2) from mineral decomposition in sufficient quantities at appropriate temperatures to form a cellular structure in the mass. Unless these two "type" reactions take place at the same time or in overlapping ranges of time and temperature, cellulation will not occur. In this event, the gas will escape or the melt will be too fluid to retain it; or if retained, the cells may be too large or the walls too thin for good strength in the product. The stages that occur when clays and shales are heated in an oxidizing atmosphere may be summarized as follows: 1) Drying and removal of free water to 200°C. 2) Absorbed water dehydration period (200 to 480°C). 3) Chemically-combined water dehydration period (480 to 700°C).

Jan 1, 1965

By R. W. Heckel, H. W. Paxton

The growth of grain boundary films and Widmanstiitten plates of proeutectoid cementite in hypereutectoid steels ulas considered quantitatively in three plain carbon steels and one "pure" iron-carbon alloy. Growth was found to take place at a slower rate than would be predicted on the basis of a model invoking rate control by long range diffusion of carbon. The films in the pure alloy grew faster than those in the plain carbon steels. A possible explanation is suggested. In 1904, Nernsst&apos; and Brunner2 postulated that ionic crystals growing in supersaturated aqueous solutions grew at rates determined by diffusion through the solution to the growing crystal interface. The gradient down which the diffusion took place was assumed to be fixed by the supersaturated bulk solution concentration, the concentration dt the crystal surface and some arbitrary distance. The flux of material to the crystal was described as Flux where D is the diffusion coefficient, A the crystal surface area, Ci the bulk solution concentration, Co the saturated solution concentration, and 6 the thickness of the diffusion zone. It is obvious that the expression is an adaptation of F+ick&apos;s3 first law of diffusion (steady state). This was the initial formulation of what will be defined here as "diffusion controlled growth," i.e., growth limited by the long range diffusion of a component either to or from the advancing interface assuming both phases at the interface to be in equilibrium. This idea of equilibrium interface concentration implies an infinite reaction rate at the interface. Volmer, Zener,&apos; and 11schner6 have derived expressions for the diffusion controlled growth of spherical precipitates in metallic systems. These analyses agree that the growth in a given direction should be parabolic with time. Brown and Hawkes7 observed that graphite, formed both from the decomposition of cementite and from the decomposition of eutectoid austenite in cast irons, grew according to a parabolic relationship and, therefore, concluded that the laws of diffusion controlled growth, as defined above, were obeyed. They, among others, failed to consider, however, that parabolic growth is a necessary, but not sufficient, condition for diffusion controlled growth. Mehl and Dube"&apos; have pointed out that equilibrium may not be realized because the concentration at the interface cannot change instantaneously from that of the bulk to the saturation value. Furthermore, they propose that an equilibrium solute concentration in the parent phase adjacent to the precipitate would remove the thermodynamic activity gradient across the interface and, thus, stop the growth process. Frisch" has also emphasized the importance of interface concentrations that vary throughout the growth of a new phase. The variation in activity across an interface, as discussed by Onol&apos; and Cahn and Hilliard,12 is of fundamental importance to this question. Ham13 considered the data of Turnbull14 on the growth of barium sulfate in aqueous solutions. He concluded that the data could be analyzed in terms of a radiation-type boundary condition. Flux across interface = K (c, - C,) [21 where C, is the concentration in the solution at the interface, Co the saturated solution concentration, and K the proportionality constant. The edgewise growth of Widmanstlitten plates, frequently referred to as the rate of lengthening, was first considered by Zener.&apos;&apos; Basing a mathematical analysis on steady-state (constant velocity) growth he concluded that where G is the growth rate, D the solute diffusivity, Ci the concentration in the bulk, Co the equilibrium interface concentration, C, the concentration in the precipitate, a a constant, Y the radius of curvature of the edge of the plate, and rC the critical radius, i.e., the radius which would increase the activity of solute at the interface at equilibrium under the influence of capillarity to that of the bulk. Zener1&apos;

Jan 1, 1961

By B. F. Decker, J. H. Keeler, W. R. Hibbard

Textures of hot-rolled, of cold-rolled, and of cold-rolled and annealed zirconium sheets were determined by use of an X-ray spectrogoniometer. All textures showed a tilt of the basal planes 240" from the rolling plane about the rolling direction. Deformation textures showed the [1010] direction to be approximately in the rolling direction. After recrystalliza-tion, the 111201 direction was approximately in the rolling direction. This texture was sharpened by annealing above the allotropic transformation. Textures of sheet produced by alternately cold rolling and then annealing were less strongly oriented than sheets that underwent severe deformation without intermediate anneals. THIS study of the deformation and annealing textures of high purity zirconium was carried out to supplement an investigation of zirconium and zirconium-base alloys. The spectrogoniometer method of pole figure determination was used and yielded more detailed and precise information than the photographic techniques used by previous investigators. Earlier investigations of the rolling textures of hexagonal metals titanium,1,2 beryllium," and zirconiumL having a c/a ratio slightly less than 1.6 disclosed a rotation of the basal planes from the rolling plane about the rolling direction so that the basal poles were inclined toward the transverse direction, and with one exception,& the [1010] direction was found parallel to the rolling direction. Similarly, hot rolling produced a spread of the basal poles in the transverse direction,2,3,5 With the [1010] direction parallel to the rolling direction. The textures of these metals after recrystallization differ somewhat from each other although still exhibiting the transverse rotation of the basal poles about the rolling direction. Zirconium" was found to have the [1120] direction in the rolling direction, beryllium" continued to have the [1010] direction in the rolling direction, and titanium&apos; was shown to have the [1010] direction in the rolling direction (the cold-rolling texture) when annealed at 1000°F, changing to the [1120] direction in the rolling direction when annealed at 1500°F. It was suggested2 that the titanium retains the deformation texture after re-crystallization, and preferred grain growth at higher temperatures produces the second texture. Annealing above the allotropic transformation temperature did not appreciably change the high temperature recrystallization texture for titanium.&apos; Coarsegrained zirconium showed more spread" in the transformation texture than in the recrystallization texture. The material used in this investigation was crystal-bar zirconium prepared by the iodide process. The major impurity was hafnium which was less than 0.3 pct. The composition obtained by spectro-graphic analysis is given in Table I. The hot-rolled specimen was prepared from a 50-g button of zirconium arc-melted in a water-cooled crucible under an argon atmosphere. This button was enclosed in a welded sheath of soft iron and the ensemble was rolled at 825°C. After each pass the sheath was put back into the furnace to allow it to return to the desired temperature. The zirconium ingot was reduced in this manner to a thickness of about 0.035 in., a reduction of approximately 90 pct. The sheet after removal from the sheath was alternately polished and etched to a thickness of 0.001 in. Cold-rolled specimens were prepared from crystal bar by a series of reductions of approximately 0.010 in. until the sheet reached a thickness of 0.010 in. after which it was cold-rolled to 0.001 in. thickness between sheets of alloy steel. The total cold reduction amounted to about 99.8 pct. Specimens were annealed in an evacuated Vycor or quartz tube. The transmission pole figures were obtained by the quantitative method of Decker, Asp, and Harker6 modified by Geisler7 using an X-ray spectrogoniometer with Cu Ka radiation. Unless otherwise specified all four quadrants were examined with 5" increments along the radius of the pole figure. Absorption corrections were made for changes in length of the X-ray path through the sample as inclination of the

Jan 1, 1954