By R. F. Lynch, J. D. Wood

The Al-1.0 pct Mg alloy 565 7 was studied using optical microscopy and electron microprobe X-ray analysis. Constituent particles were found to exist inter-dendritically in the as-cast material in a region of precipitate free a -aluminum. Five phases besides a fine precipitate and a-Al were identified in the cast structure: Fel3, Fe2Al7, Mg2Al3, CUMgAl2, and Cu2FeAl7. Thermal treatments conducted for 100 hr at 1180°, 1130°, 1080°, 1030°, 980°, and 880° F revealed a general dissolution and spheroidization of the in-terdendritic constituent network observed in the cast structure. The principal constituents present in the thermally treated structures were FeAl3 and Fe2Al7 with the relative amount of Fe2A17 to FeAl3 increasing with a decrease in the treatment temperature. The phases Present in the wrought structure were identical to those observed after the thermal treatments, with the constituent particles strung out in the direction of rolling. ALLOY 5657 is a nonheat-treatable commercial purity Al-1.0 pct Mg alloy utilized extensively because of its bright finishing characteristics. This investigation was conducted to determine the constituents present in 5657 alloy, and to study the effect of extended thermal treatments on morphology. Numerous studies have been carried out to establish the equilibrium diagrams for various aluminum systems,1-3 with phase identification based on X-ray analysis, morphology, and the etching response of relatively large particles. Phragmen4 conducted a study of the phases in aluminum eutectic systems and compiled a "corrected" table of etching responses, drawing on his work plus that of Schrader,5 Keller and Wilcox,6 and Mondolfo.7 A review of the original work of Keller and Wilcox, and Mondolfo, which was concerned with the constituents found in commercial alloys, reveals that in numerous cases their etching responses differ from those reported by Phragmen and from each other. These inconsistencies may occur because a specific constituent will react to a given etch in a varying manner depending upon its size, the elements dissolved in the phase, the other constituents surrounding a phase, and the solute content of the matrix. Work with a commercial orientation was conducted on alloys 2024 and 3003 by Sperry8,9 and on alloy 3003 by Barker,10 where the relationship between the phase diagram and the nonequilibrium structure of an alloy was examined. Backerud11 investigated the A1-Fe binary system and found that at high cooling rates the equilibrium eutectic reaction forming a-A1 and FeA13 is replaced by another lower temperature eutectic reaction forming a-A1 and metastable FeAl6, a constituent first identified by Hollingsworth et al.12 Most of the above mentioned studies were conducted on materials having a significantly greater alloy content than 5657 alloy, where the relatively small size and sparse distribution of second phase particles hinders the process of identifying constituents. EXPERIMENTAL PROCEDURE Material with a composition as given in Table I was examined in the as-direct chill cast, hot rolled and cold rolled conditions, and after thermal treatment of the cast structure. Thermal treatments were terminated by a water quench. Microscopic examination was conducted under various lighting conditions following the application of standard etchants as specified in Table 11. A semi-quantitative electron microprobe X-ray analysis was conducted for Al, Mg, Fe, Cu, Si, Zn, and Ti. RESULTS AND DISCUSSION Microstructure of the As-Cast Material. Particles of second phase material were found to exist inter-dendritically, principally in regions of precipitate free a-Al, as illustrated in Fig. 1. Adjacent to the ingot edge was a region of inverse segregation, resulting in an increased amount of second phase material containing large sized particles which aided in phase identification. Phase Identification. Cast Structure. Five phases besides a-Al and a fine precipitate were identified using optical microscopy and electron microprobe X-ray analysis, as presented in Tables II and III, respectively. FeA13 and Fe2A17 are often found with Fe2A17 forming a sheath around the core of FeAl3, resulting from an incomplete peritectoid reaction. These phases have a nearly identical appearance under white light, although they are easily differentiated under crossed polarizers, as characteristically illustrated in Figs. 2(a) and 2(b), respectively. Microprobe analysis con-

Jan 1, 1970

By D. J. Mack, R. E. Reiswig

Six examples of the peritectoid transformation were selected from the literature and studied by the method of isothermal transformation. The kinetics and mechanisms of five of the examples are presented as TTT diagrams and photomicrographs. The exist-enc- of a peritectoid in the sixth case is doubtful. ALTHOUGH the peritectoid transformation per se has been known for many years, no precise published data exist concerning the kinetics or mechanisms involved in transformations of this type, except for the brief treatment by Rhines, et al. 1,10 Bearing in mind the fact that investigations of recent years are uncovering more and more peritectoids and suspected peritectoids, a thorough study of the well-established peritectoids appeared to be in order. It was for this reason that a study of the kinetics and morphological mechanisms of six binary peritectoids was undertaken. The six peritectoids selected from the literature for study were those reported at 7.02 wt pct Al-Ag, 26.0 wt pct Sb-Cu, 30.5 wt pct Sb-Cu, 32.3 wt pct Sn-Cu, 8.35 wt pct Si-Cu, and 21.2 wt pct Al-Cu. These selections were based on availability and purity of components, ease of preparation and heat-treatment, and estimated reliability of the available equilibrium diagrams in the regions of interest. EXPERIMENTAL PROCEDURE The alloys used in this investigation were induction melted in electrode-grade graphite and chill-cast in cast-iron split molds. In all cases, the alloys were so brittle that they could easily be broken into samples weighing 1 or 2 g. Chemical analyses showed that the alloys used were close to the respective peritectoid compositions reported in the literature and that the impurity levels were low in all cases. Metallographic examination showed uniform distributions of phases in all samples, indicating uniformity of composition in the samples studied. Isothermal transformation studies were carried out in fused-salt media, using the familiar inter-rupted-quench method. Uniformity of temperature in the salt baths was maintained by continuous stirring with a stainless-steel agitator. On the basis of actual observations of the temperature fluctuations, the estimated temperature control was + 10C for the Ag-Al and Cu-Sb alloys and ±30C for the Cu-Sn, Cu-Si, and Cu-Al alloys. The accuracy of all temperature measurements was estimated to be ±1°C. It was found necessary to mount metallographic specimens of the Ag-Al alloy in cold-curing methyl methacrylate, since the temperatures encountered in mounting in bakelite or lucite caused an appreciable degree of transformation to the ß phase. For the other alloys, wood-flour-filled bakelite mounts were used to avoid extraneous X-ray diffraction lines during the later examination of the metallographic specimens on a Norelco Geiger-counter d if f r ac tomete r. In the X-ray diffraction procedure, agreement between the published diffraction patterns and those obtained in this study was good. This was particularly important for phase identification, since the literature contained little in the way of micrograph description in some cases. Etching of the silver-aluminum alloy for metallographic examination was done by swabbing with either of the following reagents: 1) 10 g CrO3, 1 g (NH4), SO2, 0.5 g NH4NO3, 100 ml H2O, or 2) 10 ml NH4OH, 1 ml 20 pct KOH, 4 ml 3 pct H2O2, 5 ml H2O. The other alloys were etched with the usual bichromate etchant: 2 g K2Cr2O7, 1.5 g NaC1, 8 ml conc. H2SO4, 100 ml H20 (swabbed vigorously). EXPERIMENTAL RESULTS A) The Ag-Al peritectoid at 7.02 wt pct Al— The phase equilibrium involved in this peritectoid is shown in Fig. I.2 The phase boundaries in the vicinity of the peritectoid were most comprehensively established by Hume-Rothery, et al,3 who placed the equilibrium temperature at 448 °C and the equilibrium compositions of the a ß' and y phases at 6.11, 7.02, and 7.24 wt pct Al, respective The alloy used in this study analyzed4 6.95 wt pct A making it slightly hypoperitectoid according to the accepted equilibrium diagram. The rate of the transformation a+ y — ß' varies rapidly with degree of undercooling below the equilibrium temperature, passing through a maximum in the vicinity of 350°C. Thus the TTT dia-

Jan 1, 1960

By W. J. Kroll

Jan 1, 1960

By D. F. Hewett

CONTENTS PAGE Introduction 1 Geologic features of eastern Oregon 2 Geology of the Sumpter quadrangle 2 Rocks older than the ore deposits 3 Rocks younger than the ore deposits 8 Lodes of the Sumpter quadrangle 8 Areal distribution 8 Geologic distribution 9 Major features of the veins 9 Mineralogy and texture of the veins 13 Ore deposits zonally disposed around the Bald Mountain batholith . . . . 13 Summary of mineralogy and texture 32 Zonal relations 33 Ore deposits zonally disposed around Greenhorn Mountain batholith . . . 36 Zonal relations 37 Relation of textural features to zonal arrangement of veins 37 Summary of zonal relations 38 Comparison with similar districts 39 Outlook for the district 40 INTRODUCTION IN an earlier report on the Sumpter quadrangle1 it was briefly stated that the quartz lodes of that region might be separated into several groups or belts on the basis of the kind and abundance of the minerals of which they are composed, and that these belts were disposed as areal zones around the principal intrusive mass of the region. When the opportunity to revisit the region was offered in 1929, as a result of a cooperative agreement between the State Mining Board of Oregon and the United States Geological Survey, it seemed advisable to pay particular attention to this feature of the lodes, in the hope that if the idea of zonal relations was confirmed it might serve as a guide in exploitation.

Jan 1, 1931

By J. K. Stanley

Knowledge of the diffusivity of carbon in the low temperature form of iron (alpha iron existing below 910°C) is at the moment of considerable interest in the study of the decomposition of austenite and martensite, the elastic after-effect,123 the magnetic after-effect4 and the decarburization of steel below 910°C. Information on the solubility of carbon in iron, and to a lesser extent its diffusion, is also important in consideration of such phenomena as blue-brittleness, temper-brittleness, "magnetic" aging, quench-aging, strain-aging, and possibly the yield point. In order to obtain more information on these subjects more fundamental knowledge is necessary. It is the purpose of this work to present data on the diffusion and solubility of carbon in the alpha iron. The high temperature form of iron (gamma; face-centered cubic) existing above 910°C is capable of dissolving relatively large amounts of carbon, up to 1.7 pet at 1130°C, while the low temperature form (alpha, body-centered cubic) existing below 910° dissolves only a limited maximum amount of less than 0.02 pet carbon at 725°C, according to data obtained here. Since the solubility of carbon in the face-centered or gamma iron is large, relatively speaking, no great analytical difficulties have been encountered in the determination of the solubility lines5 or of the diffusion of carbon.0 The limited solubility of carbon in alpha iron offers difficulties because experimental procedures and analytical methods for low carbon contents below say 0.01 pet have to be more refined than techniques used for work with gamma iron. Because of the difficulties of applying conventional methods to the determination of the diffusion of carbon in alpha iron, virtually no work has been done on this subject. However, by proper refinement of the analytical method for small amounts of carbon, the determination of the diffusion coefficient can be made readily using modified procedures. The solubility of carbon in alpha iron has been determined over a temperature range by various investigators, but the agreement among them is poor. The present investigation establishes the limits quite accurately. Information of this kind is useful in establishing the correctness of equilibrium diagrams but, more significantly, such information on maximum solubilities, especially when extended to alloyed ferrites, should be extremely important in the study of aging and related phenomena. Literature The literature existing on the diffusion, in particular, and on the solubility of carbon in alpha iron is not extensive. The data which exist are not of a high order of accuracy, much of them being in the realm of conjecture. THE DIFFUSION OF CARBON IN ALPHA IRON Whiteley7 made the qualitative ob- servation, using metallographic techniques, that the rate of diffusion of carbon at the A1 (725°C) point was very rapid and that its diffusion was still rapid at 550°C. Snoek,4 studying the magnetic aftereffect in high purity iron, arrived at the conclusion that the after-effect could be explained by the presence of small amounts of carbon diffusing under the influence of magnetostrictive strain (lattice distortion due to magnetic interaction). In later work, Snoek8 made an estimate of the ratio of carbon diffusion in alpha to its diffusion in gamma iron, and concluded that for a temperature of 910°C the ratio of Da/D? was 2600. Polder,9 basing his calculations of D on relaxation phenomena in the elastic after-effect, estimated that Da is about 1/3 of D? at 910°C (1183°K) and is about 1/12 of Dy at 727°C (1000°K). Polder's equation for the diffusion of carbon in alpha iron was calculated to be 18000 D = 5.2 X 10-4 e-RT cm2 per sec Ham10 obtained data for the diffusion and solid solubility of carbon in alpha iron at two temperatures by using one technique similar to that employed in this study. He found a D of 8.0 X 10-7 cm2 per sec at 702°C and of 2.7 X 10-7 at 648°C. THE SOLUBILITY OF CARBON IN ALPHA IRON Although pearlite is absent in steels containing 0.06 pet,11 0.05 pet,12 or 0.045 pet C,13 it appears that the carbon in these steels cannot be in solution in ferrite. The solubility of carbon at the A1 (725°C) point was first determined by Scott14 on the basis of cooling curves, and was found to be between 0.03 and 0.04 pet C. Tamura15 by interpolating between the solubility of carbon in delta iron at 1400°C and in alpha at room temperature (assuming zero solubility) ar-

Jan 1, 1950

By L. F. Mondolfo

An aluminum-copper 4 pct Cu alloy aged at room temperature for times increasing up to 78,000 hr was annealed at 170°C and the hardness and electrolytic potential determined during retrogression and subsequent aging. It was found that there is a change of behavior with increasing time of aging at room temperature which indicates that, given sufficient time, retrogression disappears and the room-temperature aging tends to progress directly into the high-temperature aging. WHEN an age-hardenable alloy is aged at low temperature after proper quench, changes of properties and structure take place. If this material is then heated to a temperature higher than the previous one, but still well below the solution-treatment temperature, the properties and structure changes produced by the low-temperature aging disappear and the material apparently reverts to the as-quenched condition, ready to undergo aging from the start. This phenomenon is termed reversion or retrogression. First discovered by Cayler3l it has been extensively investigated, as shown by the number of publications listed in the bibliography. From all the information available the following facts emerge: 1) All aeg hardenable alloys can be retrogressed.9 13, 19) 24, 33, 41, 42, 44, 47, 53, 54, 61, 63, 64, 66, 73, 78 2) All the properties changes that take place during aging at low temperature can be retrogressed to a smaller or larger extent.4,5,7,12,19,32,49,50,57,58,60,67,75,76 67, 75, 76 3) Retrogression requires that the temperature be well above the preliminary aging temperature. If the difference between the two temperatures is small, Little or no retrogression takes place.7,20,32,33,41,49 57. 65 4) The larger the difference between the preliminary aging and the retrogression temperature, the faster and more complete is the retrogression.20, 33, 41, 48, 65, 67 5) Retrogression can be produced several times in the same alloy.23, 35,41,57,59 6) The amount of retrogression that can be obtained depends on the aging temperature. Alloys aged at the lower temperatures can be retrogressed the most. The higher the preliminary aging temperature the less retrogression can be produced.20,25,33,37,44,49,54,58 7) Appreciable retrogression after aging at elevated temperatures is possible only if the preliminary aging has lasted a short time. After a certain time of aging at high temerature retrogression does not take place any more,:5,6,9,10,11,21,40,58 8) During retrogression the Guinier-Preston zones redissolve and disappear. The other precipitate

Jan 1, 1960

By D. Weinstein, F. C. Holtz

AS a possible method of improving the elevated temperature strength properties of zirconium, an investigation was initiated on the feasibility of producing a dispersion-strengthened material. Because of the high reactivity of zirconium, its high solubility for oxygen, and the stability of the Zr-0 solid solution, the major problem in such a development is choice of a suitable dispersant. Thus, in the present investigation we were concerned primarily with the stability of various dispersants in the zirconium matrix. The experimental procedure consisted of blending powders of zirconium and a dispersant, followed by cold compaction and extrusion. The best available source of -325 mesh zirconium powder contained between 1500 and 3500 ppm Oz; to this material, powders of zirconium carbide (5 p max), vanadium carbide (5 p max), alumina (0.03 p average), lan-thana (0.8 to 2 p), ceria (0.8 to 2 p), yttria (0.8 to 2 p), calcia (44 p rnax), or thoria (0.6 to 0.8 p) were added in amounts of 7 vol pct and compacted at 65 tsi. A cylindrical compact having a density between 70 and 80 pct of theoretical and dimensions of 1 in. diam by 1-114 in. high was thus produced. After canning in copper, these billets could be extruded (5: 1) on a 54-ton capacity, slow-traverse hydraulic press with the billet temperature at 1550°F and the extrusion die at 900°F. However, lack of densifica-tion of some of the extruded billets necessitated ratios of at least 23 :1. Ultimately, all billets were successfully extruded at 1500°F to 0.190 in. diam (32 :I), fully dense rods using a 200-ton capacity press and a ram speed of 90 ipm. The microstructures of as-extruded Zr-7 vol pct LazOS and Zr-7 vol pct Y2Os are shown in Fig. l(a) and (c), respectively. These structures are similar to all the as-extruded materials and consist of an elongated, single-phase zirconium matrix dispersed with oxide or carbide particles. Very little porosity is observed, and the interface between matrix and particles appears satisfactory. The size and distribution of particles, however, are not ideally of the type desired for dispersion strengthening. Since the primary study was of particle stability with respect to zirconium, no attempt was made to overcome agglomeration during powder blending and fabrication. Some areas exhibit fine, well-distributed particles; undoubtedly, a small proportion is submicroscopic and has the

Jan 1, 1963

By J. A. Lund, A. M. Lawson

THE structures of quenched eutectoid and hypereu-tectoid Fe-Cu alloys have been examined by X-ray diffraction and by optical and electron microscopy. The relevant portion of the Fe-Cu phase diagram is given in Fig. 1. Several values have been reported for the solubility of copper in a Fe at the eutectoid temperature, including 1.4 wt pct by orton' and 2.13 wt pct by Wreidt and Darken.2 Alloys containing 4.8 and 7.5 wt pct Cu have been prepared from two batches of Ferrovac E iron (0.005C and 0.013C) and electrolytic tough pitch copper (99.90 Cu). Specimens of dimensions 0.8 by 0.8 by 0.1 in. were cut from hot-rolled material, austenitized, and quenched into brine at 25°C. Similar specimens were also cooled in the furnace, after a short soaking treatment at 1100°C, at a rate estimated to be 10°C per min in the temperature range of 900" to 500°C. X-ray diffractometry was performed on quenched and on furnace-cooled bulk specimens using iron radiation. Only a bcc phase could be detected in all samples. Lattice parameters were calculated from measurements on four lines, made up of two resolved high-angle doublets. Comparisons were made against a silicon standard. Results are shown in Table I. Based on X-ray diffraction studies of a series of alloys of lower copper concentrations, orton' estimated that the tattice constant of a Fe at 25°C increases 0.0014A per wt pct Cu in solution. Extrapolating Norton's data, it may be concluded that all copper was retained in solution in the brine-quenched 4.8 pct Cu alloy, and that approximately 5 pct Cu was also held in solution on quenching the 7.5 pct Cu alloy. Typical microstructures of brine-quenched specimens, as observed by optical microscopy, are shown in Figs. 2 and 3. Precipitation of the E phase (copper-rich) occurred along the y grain boundaries on quenching the 7.5 pct Cu alloy, rendering them readily detectable in the microstructure, Fig. 3. The original boundaries in the 4.8 pct Cu specimens were gener- ally not discernible, however. This indicates that the z phase which was seen in the higher-copper alloy was probably of proeutectoid origin. Thin foils for transmission electron microscopy were obtained from bulk specimens by spark machining to 0.006 in. thickness, followed by electrolytic polishing. Typical transmission electron micrographs

Jan 1, 1967

By George Hulst

PRIOR to 1914, there was little demand for antimony in this country; its use was limited almost entirely to the manufacture of type and bearing metals. Practically no antimony ore was mined here, the market being supplied principally from China, and the alloy was produced by a direct mixing of lead and antimony. The great world war, with its demand for shrapnel in hitherto undreamed of quantities, precipitated a great boom in the price of antimony. Nominally quoted at 6 c. to 7 c. in 1914, the price increased by leaps and bounds to 45 c. in March, 1916. Under the stimulus of high prices many shall mines were opened, for it became profitable to work ores containing as low as 20 percent. antimony. High-grade sulfide ores (stibnite), containing 55 per cent. to 60 per cent. antimony, were received from Bolivia, China, and Alaska. Low-grade sulfide ores, running from 20 per cent. to 45 per cent., were produced in Nevada, California, Idaho, Utah, and Mexico; much of this ore was fairly rich in silver. The principal oxide ores came from Mexico and Oregon. The following analyses are representative of various types of antimony ore: Se Pn Cu Ao Au SIC), Fe S CAO ZN As Oxide Ore 25.09 46.02 0.95 0.40 10.98 0.30 0.22 Sulfide ore 5.5.20. 15.12 1.05 19.87 ? 0.40 0.25 Sulfide Ore 37.16 11.30 0.10 34.0 7.60 0.50 17.05 7.40 0.36 0.10 Sulfide Ore 41.55 15.00 0.20 76.0 0.04 5.60 0.25 18.17 0.85 0.25 0.10 The International Lead Refining Co. fortunately was equipped to handle these ores through residue and blast furnaces. The charge consisted of a variety of sulfide ores containing Sb 20 to 60 per cent. and Si02 6 to 45 per cent., oxide ores containing Sb 20 to 40 per cent. and SiO2 10 to 45 per cent. Secondary materials, such as battery plates, battery mud, lead oxide, paint, etc., together with refinery skims, softener skims, and other refinery byproducts, were treated along with the antimony ore to furnish the lead required. All silver-bearing antimony ores were treated in the residue furnace, the sulfur, iron, and copper forming matte that carried part of the silver, the balance going into lead bullion. The

Jan 9, 1919

By George P. Hulst

Prior to 1914, there was little demand for antimony in this country; its use was limited almost entirely to the manufacture of type and bearing metals. Practically no antimony ore was mined here, the market being supplied principally from China, and the alloy was produced by a direct mixing of lead and antimony. The great world war, with its demand for shrapnel in hitherto undreamed of quantities, precipitated a great boom in the price of antimony. Nominally quoted at 6 c. to 7 c. in 1914, the price increased by leaps and bounds to 45 c. in March, 1916. Under the stimulus of high prices many small mines were opened, for it became profitable to work ores containing as low as 20 per cent. antimony. High-grade sulfide ores (stibnite), containing 55 per cent. to 60 per cent. antimony, were received from Bolivia, China, and Alaska. Low-grade sulfide ores, running from 20 per cent. to 45 per cent., were produced in Nevada, California, Idaho, Utah, and Mexico; much of this ore was fairly rich in silver. The principal oxide ores came from Mexico and Oregon. The following analyses are representative of various types of antimony ore: Sb Pb Cu AG AU SIO2 Be S CaO Zn As Oxide ore.......... 25.09 46.02 0.95 0.40 10.98 0.30 0.22 Sulfide ore......... 55.20 15.12 1.05 19.87 0.40 0.25 Sulfide ore......... 37.16 11.30 0.10 34.0 7.60 0.50 17.05 7.40 0.36 0.10 Sulfide ore......... 41.55 18.00 0.20 76.0 0.04 5.60 0.25 18.17 0.85 0.25 0.10 The International Lead Refining Co. fortunately was equipped to handle these ores through residue and blast furnaces. The charge consisted of a variety of sulfide ores containing Sb 20 to 60 per cent. and SiO2 6 to 45 per cent., oxide ores containing Sb 20 to 40 per cent. and SiO2 10 to 45 per cent. Secondary materials, such as battery plates, battery mud, lead oxide, paint, etc., together with refinery skims, softener skims, and other refinery byproducts, were treated along with the antimony ore to furnish the lead required. All silver-bearing antimony ores were treated in the residue furnace, the sulfur, iron, and copper forming matte that carried part of the silver, the balance going into lead bullion. The antimony slag produced was sufficiently low in silver to warrant being smelted in the blast furnace to antimonial lead.

Jan 1, 1921

By Harrison Everett Ashley

Prof. Hofman's diagrams, Figs. 5 and 7 of his paper, which are reproduced as Figs. 1 and 2 of the present contribution, confessedly fail to show comprehensively the properties of the silicates investigated. Each curve is carefully discussed, and the author has evidently drawn all the conclusions that can be thus reached; but he says :* "The curves do not show, as was hoped, any simple connection between silicate-degree, percentage of lime, and minimum of formation-temperature." There is, therefore, in this case, an excellent opportunity of

Jan 1, 1902

By L. T. Larson, P. M. Basinski

In the northern Reese River Valley uranium is corroded with Middle Pliocene zeolites. These zeolites were diagenetically derived from rhyolitic volcanic glass deposited in a saline- alkaline lake. X-ray diffraction, scanning electron microscopy, and chemical studies reveal clinoptilolite, analcime, and enonite to be pesent and that these minerals can concentrate at least 0.7% uranium from solution. Most anomalous drill cuttings contain zeolite and zeolites are believed to host the uranium. Research suggests the uranium mineralization is conceptually analogous to the Tono mine, Japan.

Jan 1, 1981

By Theron Wasson

During 1936 the state of Michigan produced 11,868,573 bbl. This is approximately 4,000,000 bbl. less than produced in 1935. The principle reason for the decrease in production over the previous year was the rapid decline of the Crystal field, which reached its peak in October 1935. The old producing area—Mt. Pleasant, Porter, Yost-Clark— accounted for over 7,000,000 bbl. during 1936. Crystal produced a total of 2,400,000. Outstanding among the old fields were Vernon and

Jan 1, 1937

By R. D. Nelson, F. E. Bowman

Assumptions are made of ideal mixing and that the density of silver can be obtained by extrapolating reported liquid density-temperature data through the freezing point back to the temperature range of interest. The results of this procedure using liquid silver density data of Kirshenbaum et al.5 are presented in Table I1 where it is observed that agreement is everywhere within <0.1 pct and generally is within 0.05 pct. Because the Sn-Ag alloys are dilute, the assumption of ideal behavior is, therefore, probably justified. In conclusion, the densities of dilute liquid solutions of silver in tin have been determined. Even for concentrations as low as 0.1 pct, the effect of silver on the density of liquid tin is clearly measurable. This work also suggests that for dilute alloys at temperatures far below the freezing point of the solute metal, densities may be accurately calculated by extrapolation of the pure metal data without having recourse to physical measurement on the alloy itself. plutonium having a grain size of about 100 µ. This paper presents data showing that large elongations of fine-grained a Pu can be obtained by using slow deformation rates. Large plasticity, however, of a Pu in compression has been observed.4 Reductions in thickness of 90 pct have been observed with no edge cracking. These large reductions are accompanied by concurrent re-crystallization. The deformation modes, which are quite complex, have been studied extensively by observing the deformation microstructures of polished surfaces that had been deformed in compression.5-7 Although slip apparently is a predominant mode of deformation at room temperature, grain boundary sliding and concurrent recrystallization become more predominant at high a temperatures.4&apos;7 Although recovery occurs,8,9 no grain growth has been reported in a Pu even at temperatures near the a =ß equilibrium temperature (-115oC), which is 0.7 of the calculated melting temperature of a Pu.10 From studies on other materials, it appears that high elongations can be obtained in alloys when the THE purpose of this technical note is to present briefly some data revealing high ductility of a Pu, which is normally considered brittle. The very low ductility of a Pu in tension has been reported by many investigators.&apos;-3 Gardner,1 for example, reported that the total elongation of a Pu at a testing speed of 0.015 ipm is less than 0.1 pct at room temperature and only about 1 pct at 100°C. The only tensile creep studies that have been reported&apos; indicate no large ductility, but they were performed on relatively low purity

Jan 1, 1970

By Arthur L. Christenson, Clarence E. Jackson

In the establishment of the relationship between weldability and hardenability, two methods have been employed in correcting for the grain growth produced in the heat-affected zone: first, the hardenability calculated from chemical composition* may be corrected to the grain size observed in an actual weld? or, second, a hardenability test may be made on the steel quenched from a temperature high enough to produce a grain size comparable to that found in the heat-affected zone.8 In order to obtain grain sizes in the end-quench hardenability bar comparable to those resulting in the base metal from the welding cycle, a quenching temperature of 2Ioo°F. has been used. In studies of the end-quench hardenability specimen quenched from 2Ioo°F. instead of from a lower temperature of I7OO°F., it is impor-TaiiT to ascertain The relative cooling rates for various distances along the bar. It is a question as to whether the cooling occurs at the same rate or whether there is any significant difference from the standard cooling-rate curve published by Jominy and confirmed by others.4,5 This paper reports experimental evidence concerning the effect of quenching temperature on the cooling rates in the end-quench hardenability test. The effect of quenching temperatures on cooling rates has been studied by a number of investigators.6&apos;7 French has considered this effect from both theoretical and experimental aspects. In French&apos;s studies on complete quenching of spheres and rounds, an increase in the quenching temperature caused an increase in the cooling rate at 720°C. at the center of the specimen. The center cooling velocity also has been shown to be dependent upon the surface per unit volume for the type of specimens studied; the velocity of cooling increases with an increase in the surface per unit volume. Three methods of indicating the rapidity of cooling of a body of metal during a quenching operation have been propped: I. The time it takes for the metal to cool from the quenching temperature to a temperature halfway between the quenching temperature and the temperature of the quenching medium (half-temperature time): Grossmann, Asimow and Urban7 justify the use of this criterion by the fact that the half-temperature time includes the temperature and time of incubation as well as the zone of formation of pearlite and, further, the data so derived accord very closely with experimental values. 2. The time interval the metal remains in a given temperature range; for example,

Jan 1, 1944

By Arthur L. Christenson, Clarence E. Jackson

In the establishment of the relationship between weldability and hardenability, two methods have been employed in correcting for the grain growth produced in the heat-affected zone: first, the hardenability calculated from chemical composition* may be corrected to the grain size observed in an actual weld? or, second, a hardenability test may be made on the steel quenched from a temperature high enough to produce a grain size comparable to that found in the heat-affected zone.8 In order to obtain grain sizes in the end-quench hardenability bar comparable to those resulting in the base metal from the welding cycle, a quenching temperature of 2Ioo°F. has been used. In studies of the end-quench hardenability specimen quenched from 2Ioo°F. instead of from a lower temperature of I7OO°F., it is impor-TaiiT to ascertain The relative cooling rates for various distances along the bar. It is a question as to whether the cooling occurs at the same rate or whether there is any significant difference from the standard cooling-rate curve published by Jominy and confirmed by others.4,5 This paper reports experimental evidence concerning the effect of quenching temperature on the cooling rates in the end-quench hardenability test. The effect of quenching temperatures on cooling rates has been studied by a number of investigators.6&apos;7 French has considered this effect from both theoretical and experimental aspects. In French&apos;s studies on complete quenching of spheres and rounds, an increase in the quenching temperature caused an increase in the cooling rate at 720°C. at the center of the specimen. The center cooling velocity also has been shown to be dependent upon the surface per unit volume for the type of specimens studied; the velocity of cooling increases with an increase in the surface per unit volume. Three methods of indicating the rapidity of cooling of a body of metal during a quenching operation have been propped: I. The time it takes for the metal to cool from the quenching temperature to a temperature halfway between the quenching temperature and the temperature of the quenching medium (half-temperature time): Grossmann, Asimow and Urban7 justify the use of this criterion by the fact that the half-temperature time includes the temperature and time of incubation as well as the zone of formation of pearlite and, further, the data so derived accord very closely with experimental values. 2. The time interval the metal remains in a given temperature range; for example,

Jan 1, 1944

By J. P. Zannaras

Referring to the article by R. J. Charles and P. L. de Bruyn, let us assume that W = weight of glass bar; P = weight of hammer; e = total deformation; E = unit of deformation; K = potential stress energy; E = modulus of elasticity; L = length of the bar; 7, = coefficient of inertia; h = height, ft; V = velocity, fps; and a = cross section area. The portion of kinetic energy which is effective in producing stress energy in a fixed bar struck horizontally is given by the formula [ ]

Nov 1, 1956

By T. F. Archbold, W. H. King

THE diffusivities of gold in polycrystalline copper have been determined in the temperature range from 700° to 1000°C by the utilization of the neutron-activation method. Martin, Johnson, and ~saro&apos; used this method for their investigation of the diffusion of gold into copper at 375° and 550°C for 59 days in order to circumvent the experimental difficulties imposed by the 2.7-day half-life of Au-198. They employed the conventional technique of depositing Au-198 on copper specimens for short-time dif-

Jan 1, 1965

By John V. Beall

When a mine has ore averaging 5% lead, 7% zinc, 0.60% copper, 1/4 oz gold, and 6 oz of silver, adequate reserves, power and water, easy access to market, and is situated in beautiful natural surroundings with the advantages of a big city within a few hours drive, there is little left to be desired. Such a mine is the Mayflower mine of the New Park Mining Co. situated 30 miles from Salt Lake City in the Wasatch Mountains near Keetley, Utah.

Jan 1, 1949

By L. M. Yokum

Tremendous strides have been made in front end loaders in the last 15 years. Fifteen years ago a 21/4-cu-yd front end loader was the largest standard machine you could purchase. Today there are two commercially available 15-yd front end loaders and many 10-yd loaders. The estimated total worldwide market for all front end loaders over 1 cu yd has increased to over 30,000 units yearly. The trend for front end loaders, in general, and for the mining market, in particular, is to larger and larger loaders. Today there are 18 and 24-cu-yd front end loaders in prototype form. It is not inconceivable that within another 15 years there will be front end loaders in the 50-cu-yd class with design features quite different from today&apos;s. These larger loaders are being designed at the demand of the mining industry, and the design criteria are being directed at this market area. The costs of these larger loaders may be greater per unit of capacity, but it is the intent of the various manufacturers that they will be more reliable, be easier to service, give greater availability, live longer, and cost less to maintain, than previous loaders. It is also the intent of the manufacturers to compete directly with the large mining shovel as the front end loaders become appropriately larger and more reliable. There has been some trend in this direction in the past with smaller shovels and loaders. In Table 1 are data for U.S. production of front end loaders (5 to 6-cu-yd class and 10-cu-yd class) and U.S. production of cable-operated, crawler-mounted power shovels, draglines, and cranes (11/z to 5-cu-yd class) for the years 1965 and 1970 (Source: Bureau of Census, U.S. Department of Commerce). Many believe that the decline in shovel production, in particular, is due at least in part to the acceptance of the front end loader as a primary production tool. However, the foregoing comparison is for a smaller shovel class than for front end loaders. It has generally been a rule of thumb that a front end loader is competitive on a cost and production basis with a shovel when it is approximately twice as large as the shovel. This same relationship may not hold true with the larger 10 to 15-cu-yd electric shovels, but at some point, direct competition will probably occur. Current Trends There are many trends today that are significant. One major usage trend in large front end loaders involves load and carry operations. This application is defined as "performing the functions of loading, hauling and dumping with one machine over distances within its economical limits." Many people are using front end loaders to transport material as well as load it. It is estimated that nearly half of all 10-cu-yd front end loaders sold in 1970 went into primary load and carry work. Many times, significant savings result from using the load and carry system, instead of small truck and shovel operations, for distances in excess of 1000 ft. Strip mining in coal utilizes great numbers of front end loaders in this manner. In-pit crushing of limestone is developing on an ever-increasing level, especially in Europe, and this stimulates interest in load and carry operations. In Table 2 is a cost example for 10-cu-yd front end loader in a limestone quarry. More than likely, load and carry use will continue to increase over the next few years. While some types of mining do not lend themselves to load and carry in the pit, such areas as surge piles are applicable and should be studied. In the area of machine operating cost reduction, there

Jan 1, 1974