By P. G. Winchell, J. K. Jackson

The strtcture of body-centered Fe-Ni-C alloys (0 to 16.5 wt pct Ni) containing less than 0.015 wt pct C was investigated by measuring the carbon-diffusion peak at low frequencies with a torsion pendulurrr. By determining the Snoek damping in ferrite and in quenched alloys of identical composition, the effects of nickel content and heat treatment were separated, and the existence of a structure in which Snoek damping is greatly reduced was revealed in the quenched ternary alloys. The relative amount of this structure increases with increased nickel content and cooling rate. It is proposed that this structure may be highly imperfect or tetragonal. In Fe-Ni-C alloys containing only ferrite the addition of nickel (0 to 5.1 wt pet) decreases tke area of the carbon-diffusion peak and shifts its position to lower temperatures but broadens the peak only slightljl. The decrease in peak area with increasing nickel implies that short-range interactions with the nickel atoms prevent some of the carbon atoms from participating in the relaxation process. The shift in the peak position indicates a long-range effect of nickel on the movement of carbon atoms so that at 300°K the diffisivity of carbon in -ferrite is increased by about 35 pct by the addition of 5.1 tut pct Ni. The results are presented as distributions of relaxation strength 072 the activation energy under the assumption that the frequency factor is invariant. BODY-CENTERED iron-base solid solutions dissolve carbon interstitially in the octahedral sites. The occupation of an octahedral site produces a tetragonal distortion of the surrounding lattice. These sites fall into three sets according to the orientation of the tegragonal distortion associated with each and may be identified by their lattice coordinates as: type 1/2 0 0, type 0 1/2 0, type 0 0 1/2. At low carbon levels in cubic ferrite the carbon atoms are distributed at random1 among these sites. In high-carbon body-centered iron-base solid solutions, which are unstable with respect to several two-phase mixtures, a tetragonal structure occurs as the product of the diffusionless transformation of austenite. This transformation is commonly accompanied by appreciable microstrain and its product is called martensite. The tetragonality of martensite, a supersaturated solution of carbon in a iron, is maintained prior to decomposition even though local diffusion of carbon occurs as evidenced by carbide precipitation. The tetragonality is taken as evidence that one set of octahedral sites is preferentially occupied by carbon. (This preferential occupation is called ordering below.) Support for this view is presented by the absence of strain-induced carbon-atom diffusion in high-carbon solid solutions (martensite). Such diffusion occurs in ferrite and produces the 40°C internal-friction peak observed at 1 cps frequencies.' Thus, there appears to be qualitative evidence favoring the view that at sufficiently high carbon levels tetragonality arises spontaneously as a result of the ordering of the carbon atoms; however, no experimental evidence exists concerning an equilibrium between cubic and tetragonal body-centered solid solutions. Moreover, attempts to estimate the energy of ordering7-' predict a value too low to maintain the tetragonality observed at medium carbon levels, 0.3 to 0.6 wt pct C. In the present work an attempt using internal-friction measurements is made to establish the presence or absence of tetragonality in low-carbon body-centered solid solutions formed by quenching austenite. Fe-Ni alloys containing about 0.01 wt pct and 0 to 15 wt pct Ni were selected for the study. While the work was in progress Gilbert and Owen10 reported that the transformation which occurs in these alloys during quenching at rates up to 5000°C per sec is not martensitic but is more properly categorized as massive. Thus, the solid solution

Jan 1, 1964

By A. W. Fletcher

A nickel-copper sulphide concentrate was treated in a pilot plant at Warren Spring Laboratory during 1961, by a hydrometallurgical roast-leach- solvent extraction process devised to cleanly separate the metal values, and produce acid sulphate liquors containing the metals. It is shown that 86 percent of the nickel and 95 percent of the copper could be leached from the calcine, after a sulphatizing roast on finely ground flotation concentrate. Iron was removed from the leach liquor by limestone neutralization with a small loss of values. Copper and nickel were separated by solvent extraction with naphthenic acid in kerosene after partial neutralization of the iron-free liquors with ammonium hydroxide. Hydrogen sulphide and chlorine were used to remove zinc (and residual copper) and cobalt impurities respectively. The recovery of pure copper and pure nickel, by electrowinning, from the acidic solvent extract strip liquors finally produced, appears technically feasible.

Jan 1, 1964

By George R. Huebner

The White Pine Copper Company, subsidiary of Copper Range Company, is located in the Upper Peninsula of Michigan. The offices, plant, and mine are six miles south of Lake Superior in Ontonagon County. Employing 1700 people, White Pine is the largest single industry in the Upper Peninsula. 970 underground employees produce 16, 700, tons of ore daily. From this tonnage 363,400 pounds of refined Lake Copper are produced in various shapes as specified by the customer. The following paper explains the geology of the ore body and briefly outlines present mining methods. It enumerates the reasons for considering longwall mining of a hardrock* ore body and the preliminary investigations leading to the decision to undertake the initial test panel. Selection of the initial test panel location is covered in detail. Equipment choice and reasons for that choice are described as well as selection and training of personnel.

Jan 1, 1964

The methods employed for the addition of uranium to steels and cast iron in the Physical Metallurgy Division are outlined. It has been found that the segregation of? uranium is a major problem in aluminum and/or silicon killed steels and that the cooling rate is important in al-lowing the segregate to settle to one area, which can subsequently be discarded. The unsegregated areas were found to be extremely low in total oxygen, acid insoluble aluminum (AizOg) and, in some cases, slightly lower in nitrogen. Uranium recoveries, based on analyses of the unsegregated areas, were quite constant, at about 45 per cent, regardless of the type of uranium master alloy used for the addition. No segregation of carbon, manganese, silicon, sulphur, phosphorous, chromium or copper was observed in these steels. In commercial heats, the recoveries ranged from 7 to? 29 per cent for ladle additions to oxygen converted steel. When the steel was fully deoxidized prior to the uranium addition, recoveries ranged from 49 to 66 per cent, regardless of the steelmaking process.

Jan 1, 1964

By Sidney Fischler

Large striation-free single crystals of bismuth have been grown from the melt by rapid freezing. Zone-refined bismuth, together with doping impurities if desired, is placed in a shallow flat-bottomed graphite boat and melted in air with a propane hand torch. The torch is then withdrawn in a manner which causes the melt to freeze direction-ally. Crystallization, which resuires only a few minutes, usually results in the formation of a single crystal even when a seed crystal is not used. Crys -tals of any desired orientation may be grown by using oriented seeds. Undoped crystals grown by this method have residual resistivity ratios greater than 200. THE growth of large single crystals of bismuth by either the Czochralski or horizontal zoning technique is not entirely satisfactory. Specifically, difficulties are encountered in producing single crystals of the required dimensions in all desired orientations, and striations caused by low-angle polysynthetic twins are frequently present in the crystals. In addition, both methods are time-consuming and require special apparatus of some complexity. A simpler method has now been developed for growing large striation-free bismuth single crystals of desired orientation in a short time. Fig. 1 shows a typical setup consisting of a rectangular graphite boat which contains zone-refined bismuth, a 1/8-in.-thick flat quartz plate which covers the entire inner bottom of the boat, and three additional quartz plates about 1/4 in. thick which are used to separate the bismuth from the graphite everywhere except at a small area at the left of the boat. The graphite boat is 1 in. high, and its sides and bottom are about 1/8 in. thick. The quartz plates should be smooth and clean. The graphite boat is heated from the right with a propane torch, as shown in Fig. 1, until the bismuth is completely melted. The melt has the shape of a triangle with a narrow neck at the apex farthest from the torch. The melt is frozen direc-tionally by gradually moving the torch toward the right, away from the boat. The bismuth in contact with the graphite, at the left end of the neck, freezes first. The freezing interface then moves down the neck into the main bulk of material, where it develops a convex shape ideal for the continuation of single-crystal growth. The interface continues to move through the melt until the entire bulk is solid. The entire procedure may be completed, in air, in a matter of minutes. The technique described almost always yields a single crystal whose basal plane is nearly perpendi,cular to the bottom of the graphite boat. In earlier experiments, in which the bottom of the melt was in direct contact with the graphite boat, single crystals were grown with basal planes parallel, perpendicular, or at some intermediate angle to the bottom of the boat. At times the orientation of the bulk of the material differed from the orientation of the material in the narrow neck. In these cases, a nucleation site initiated the growth of a differently oriented crystal, and the thermal conditions favored the new orientation over the initial one. The thermal conditions depend on a number of factors, including the heating technique, the placement, shape, and thickness of the quartz plates, the thickness of the walls and bottom of the graphite boat, and the quantity of bulk bismuth employed. All of these factors, plus the initial orientation and the presence and effectiveness of nucleation sites, will determine the orientation of the final large single-crystal slab. When a crystal of specific orientation is desired, an oriented section of a rapid-freeze crystal is shaped by spark cutting and grinding for use as a seed. To grow a doped crystal, the desired impurity is placed in the graphite boat together with the bismuth chunks and seed. Crystals doped with mercury, cadmium, lead, and selenium have been grown. The rate of freezing is so great that the distribution coefficient of any impurity approximates unity. On a gross scale, therefore, impurities should be more homogeneously distributed in rapid-freeze crystals than in Czochralski or zoned crystals. Because of the possibility of constitutional supercooling, however, it is quite possible that impurities are not homogeneously distributed on a microscopic scale in the rapid-freeze crystals. Generally the single crystal slabs which have been prepared are initially 5 to 7 mm thick. Thicker crystals may be obtained by using one of these slabs as a seed. The slab is placed in a graphite boat resting on a large aluminum block, either air- or

Jan 1, 1964

By F. L. Klinger

CRUDE OIL refining continued to be the foremost industry of Bahrain in 1963. This island, the largest of a group 30 kilometers off the Saudi Arabian coast, is the site of the first petroleum discovery in the Persian Gulf and in the Arabian peninsular region. The island's only oilfield was discovered in 1932; exports of crude began in 1934 and the refinery was built in 1936. Although its crude oil has been less than 1 percent of annual Middle East output in recent years, Bahrain has been an important refining center for many years, processing a substantial portion of Saudi Arabian petroleum as well as all local production. The Bahrain refinery annually accounts for 17 percent 0 the petroleum products produced in the Middle East and 25 percent of the exports. Bahrain's mineral resources consist of oil, gas, and basic construction materials. Petroleum production and refining are the important mineral industries and contribute most of the national income by payments for taxes, wages, and local services including construction and material supply. The petroleum industry has supported a large share of local business and extensive indirect employment, and its early establishment also helped Bahrain to strengthen its position as a trading center in the Persian Gulf. The country's entrepôt trade produces about 20 percent of Government revenue, and Bahrain is somewhat less dependent on the petroleum industry than are the neighboring States to the west.

Jan 1, 1964

This paper states how alloy and welding advances have made possible the rapid development of the use of aluminum in the construction of equipment for earth moving and off -highway rock hauling. The main details are given regarding the construction and field testing carried out on an aluminum prototype body. The test results of strain gauge readings are analysed, and a description is given of how these have been applied in subsequent designs. The increase in the number of aluminum units put into the various types of service in Canada, as well as the problems encountered, is described, and the experience gained from five years of field service is discussed in some detail. An assessment is also made of the durability of the e units. The economics of using aluminum, together with the current development position, are reviewed, and predictions are made for considerable future increases in the use of aluminum units in open-pit and off-highway operations.

Jan 1, 1964

By Walter Kawa

Bureau of Mines research on the hydrogenation of coal has been concerned with developing processes that could be used to supplement the Nation's petroleum and natural gas resources. Motor fuel was produced in a subsidized coal hydrogenation industry in Europe prior to 1945, but the process used is still not economical and other methods of producing liquid and gaseous fuels from coal are being investigated. As an aid to the planning of coal hydrogenation research, a literature survey was made of processes or methods of hydrogenating coal that differ from the subsidized or conventional process. This report contains a bibliography of unconventional methods of hydrogenating coal and a brief discussion of the economics of the conventional method. A general discussion of unconventional methods is included, and the advantages and disadvantages are pointed out where possible. The survey supplements a previous Bureau of Mines survey3 and a comprehensive review published in 1930.4

Jan 1, 1964

By J. F. Breedis

The morphology and crystallography of marten -site formed during quenclzing were examined by transmission electron microscopy in alloys whose compositions lie between Fe-19 wt pct Cr-11 wt pet Ni and Fe-33 wt pet Ni. Depending upon composition, four types of transformation products were observed in this portion of the Fe-Cr-Ni system. Three of these products are denoted as lath, plate, and surface martensite. The hcp structure found in association with martensite it? certain higlz-clzromium stairzless steels does not influence the transformation crystallogyaphy and cannot he Considered to act as a transitional structure in the transformation from austenite to martensite. DISTINCT changes in the characteristics of mar-tensitic transformations are produced by the partial replacement of nickel by chromium in austenitic iron alloys. Large, discrete martensite plates form in Fe-30 pct Ni, while aggregates of small crystals form in sheets parallel with (111)A austenite planes in stainless steels containing in the vicinity of 18 pct Cr and 8 pct Ni. These transformation structures are termed plate and lath martensite, respectively. In addition, an hcp structure (E) has been observed in certain high-chromium stainless steels in association with martensite. It has been suggested that the E structure acts as an intermediate step in the nucleation of martensitel-' and influences the morphology and crystallography of the final transformation product. However, this structure may be the consequence of the deformation of austenite arising from the shape distortion accompanying the transformation to bcc martensite.' An hcp stacking of atoms is produced in an fcc lattice by the introduction of an intrinsic stacking fault on alternate (111)A planes. At present, the arguments behind each explanation for the E structure are based on circumstantial evidence. This investigation seeks to determine the importance of the hcp structure to the martensitic transformation, and to examine the crystallography and morphology of the structures produced in bulk samples by quenching in alloys whose compositions lie between Fe-19 wt pct Cr-11 wt pct Ni and Fe-33 wt pct Ni. These aspects of the martensitic transformations occurring in these alloys have been studied by electron metallography and selected-area diffraction of foils examined in transmission in the electron microscope. EXPERIMENTAL METHODS The alloys have been prepared from thoroughly mixed powders of pure iron (99.6+ pct, 0.06 max pct C, 0.15 max pct N), chromium (99.9+ pct), and nickel (99.9+ pct). After sintering in an Ar-H2 atmosphere, the mixtures were melted by induction heating in recrystallized alumina boats under purified argon. The ingots were cold-rolled to 0.4-mm sheets (100 pct reduction in thickness) after the removal of at least 1.5 mm from their surfaces by grinding. Three-millimeter discs were punched from the cold-rolled sheet and annealed at 1150°C for approximately 24 hr in evacuated quartz capsules. The average grain size was 40 µ Thin foils for examination in transmission in the electron microscope were prepared from discs quenched to liquid-nitrogen temperature. A depression was first jet-machined into the center of a disc and a thin area (less than approximately 3000A in thickness) was produced at the base of the depression by electropolishing. Electron-microscope studies utilized the RCA EMU-3 and the Philips EM-100B microscopes operating at 100 kv. X-ray examination of the polycrystalline alloys was performed either in a diffractometer or in a

Jan 1, 1964

By F. F. Netzeband

This report relates to the sulfur industry of seven States--Arkansas, Kansas, Louisiana, Mississippi, Missouri, Oklahoma, and Texas--and is part of a national study of the sulfur industry by the Bureau of Mines. Markets as used 1n this report are divided into two components for individual analysis--(1) supplier markets which include regional Frasch and byproduct sulfur producers and (2) consumer markets which include processors and manufacturers requiring sulfur in their operations. The term sulfur as used in this report includes brimstone, native sulfur, elemental sulfur, or sulfur equivalents.

Jan 1, 1964

By C. R. Hubbard

The Bureau of Mines investigated the mineral resources of the Upper Missouri River Basin as a part of a comprehensive water and related land resources study by six Bureaus of the Department of the Interior, coordinated by the Department's Missouri River Basin Field Committee. The mineral resource study covers an area of about 18,000 square miles within the Great Plains physiographic province of central Montana. Exposed Formations in the plains are chiefly flat-lying Cretaceous sediments. Plutonic rocks crop out in the central parts of the mountain uplifts, with steeply tilted Paleozoic sediments exposed around the margins. Oil and gas have been produced from several fields in the study area; total value exceeds $45 million. Coal-bearing formations of Upper Jurassic and Cretaceous age cover approximately 45 percent of the study area. Total production of coal since 1880 has been between 40 and 50 million tons, exceeding $75 million in value. Total metal production has been about $52.5 million. Industrial mineral production from 1925 through 1960, is valued at $24 million.

Jan 1, 1964

By C. E. Silverblatt, D. A. Dahlstrom

Previous bench-scale studies demonstrated that a substantial moisture reduction can be obtained by the application of steam to coal filter-cakes, particularly to those containing a limited amount of minus 200-mesh material. Consequently, U.S. Steel's Applied Research Laboratory conducted a study to determine the feasibility of steam filtration of 1/4 in. by 0 coal on a continuous pilot-scale installation in which an Eimco extractor is used. The test results showed that the moisture content of this coal could be reduced to 5.5% at a steam loading of about 175 lb of steam per ton of dry cake. In terms of steam consumption, this loading is calculated to be 1-1/2 lb of steam per lb of water removed. In some tests, only 1 lb of steam per lb of water removed was required. These levels of steam consumption are significantly less than the actual heat requirements of conventional thermal dryers. The satisfactory moisture reductions were obtained at filtration rates of 125 to 186 lb of dry solids per sq ft per hour. However, the proper design of commercial filters should improve the potential rates that can be attained. These results indicate that steam filtration has considerable economic potential for drying 1/4 in. by 0 coals and also has additional advantages over the conventional thermal drying of coal. The results of the previous bench-scale studies and those published by Burton' demonstrated that a substantial moisture-content reduction can be effected by the application of slightly superheated steam to coal filter-cakes, particularly to those containing a limited amount of minus 200-mesh material. Consequently, US Steel's Applied Research Laboratory conducted a study to determine the feasibility of steam filtration of 1/4 in. by 0 coal on a continuous basis. In the continuous process, the dewatering operation on the filter is conducted in stages. In the first, the bulk of the water in the feed slurry is removed by conventional mechanical dewatering on a portion of the filter before the steam is applied. In the second stage, steam is applied to the cake. The steam condenses and releases its latent heat, thereby reducing the viscosity of the remaining cake water; this reduced viscosity then facilitates further drainage and produces a cake of lower moisture content. Because of the availability of feed coal on a continuous basis and since steam was readily available from a low-pressure boiler, the Applied Research Laboratory selected for the test site a coal-preparation plant that cleans Pittsburgh Seam coal. A slurry of table and flotation coal in percentages as they occur normally was used as feed stock. Typical analyses of this slurry are shown in Table I. DESCRIPTION OF FILTER AND EXPERIMENTAL PROCEDURES An Eimco Extractor was selected for the evaluation of steam filtration in a continuous process. This unit was chosen because of its availability and its design features that permit relatively simple hood construction, instrumentation, and operation. A photograph of the Extractor is shown in Fig. 1. In the filter a cloth medium is used that travels horizontally and continuously with a grooved, rubber drainage belt. The total effective filter area was 12.5 sq ft. As the feed slurry flows by gravity from the feed box onto the medium,

Jan 1, 1964

By W. Rostoker, H. Nichols

It has been demonstrated in previous work1'2 that wetting of aluminum alloys by liquid mercury can cause fracture to occur with substantial suppression of prior plastic flow. This has been interpreted as the action of a critical liquid species in reducing the cohesive strength of a stressed solid at sites of potential crack nucleation. In this way the critical transverse stress for fracture nucleation is reached at much lower stresses than is normally the case. The stresses for both fracture nucleation and fracture propagation are depressed by the same mechanism. In so doing the plastic-energy component of fracture energy is reduced to a level which is of the same order of magnitude as the surface, interfacial, or cleavage energy. Recent work2 has illustrated the influence of dispersed precipitates, cold work, and combinations of these on brittle fracture associated with plastic strains of the microyield order of magnitude. This has been rationalized in terms of the contribution of internal microstress fields to the stress magnifications at points of obstruction of active slip bands in a stressed metal. The presently reported studies on an Al-4-1/2 pct Mg alloy amplify this subject by introducing thermal-mechanical conditions which can produce strain aging. As amply demonstrated by Phillips, Swain, and borall, the tensile behavior of aluminum alloys containing magnesium reveals a yield-point elongation and successive discontinuous elongations over the whole plastic-strain range. This gives a stepped or serrated character to the stress-strain diagram. The yield-point elongation is not temperature-dependent. On the other hand, the discontinuous extensions in the plastic-strain range are gradually suppressed by lower temperatures of testing. At -78"C, only the yield-point elongation persists. The yield-point elongation itself can be suppressed by rapid quenching to room temperature from an annealing temperature of 500°C. The argument presented by Phillips et 1. and Cottre114 is that the yield-point elongation derives from surmounting at a critical stress the restraint to slip by grain boundaries which have been reinforced by appreciable magnesium-atom segregation. The serrated character of the plastic-strain range is the result of rapid strain aging during the test. This is made possible by the inevitable proximity of magnesium atoms to any dislocation line. In the Al-4-1/2 pct Mg alloy there is one magnesium atom for every twenty-two aluminum atoms and, with a coordination number of 12, a magnesium atom is on the average only about two atomic distances from any given lattice site. Rapid strain aging is therefore a reasonable expectation. A study of mercury embrittlement of the Al-4-1/2 pct Mg alloy (commercial designation 5083) provides an opportunity to relate the interplay of grain size, grain boundary restraint to slip and strain aging in the brittle-fracture process. One lot of commercial sheet material of 0.125-in. thickness was used for all of the tests. The specimen shape and test procedures used were the same as those described in a previous publication.2 A range of grain sizes between 0.0057 and 0.0125 mm was produced by various combinations of plastic prestrain and annealing. The coarsest grain was somewhat elongated in shape. In this case the measurement was taken in the direction transverse to the axis of tension as more meaningful to a brittle-fracture process. In the annealed condition, specimens wetted with mercury failed with zero permanent elongation at stresses slightly below the normal yield point, i.e., stresses at 0.05 to 0.2 pct strain. Since this occurs before yield-point elongation can begin, fracture derives from slip contained within individual grains and restrained from propagating across grain boundaries. No significant difference in wetted fracture stress was observed between specimens which had been water-quenched or furnace-cooled from the annealing temperatures. This signifies that the degree of magnesium segregation at grain boundaries

Jan 1, 1964

An intensely sheared and mineralized zone occurs in the quartz dolerite greenstone (or younger greenstone) mass on the western limb of the Kalgoorlie syncline. This zone comprises the western part of the Golden Mile and has produced the greater part of the 33,000,000 oz of gold produced to date from the main mining belts. A study of the general geological and structural features suggests that the lode shear system will continue southward on a pitch similar to that of the main syncline. Although payable ore has been found recently further to the south, the expectation of large quantities extending southward from the present mining areas is problematical.INTRODUCTIONUntil the late 1930's the principal mining activities in the western lode system were centred on three major ore-shoots formed on the No. 4, No. 3 and to a lesser extent on the No. 2 lode shears (Fig. 1). With the gradual reduction of grade in depth on these main ore shoots, increasing attention was paid to the "Minor Lode" system of lode shears known to exist in the same area. A large quantity of payable ore was found on these "Minor Lodes" particularly in the central part of the mining area. In recent years more attention has been given to exploration in a southerly direction.ROCK TYPES AND STRUCTURESThe western system occurs on the western flank of a dragfolded, south pitching syncline. The rock succession consists of Black Flag sediments overlying the younger greenstone horizon which overlies the fine grained older greenstone horizon. The axis of the syncline is regarded as a tight infold of the overlying Black Flag sediments. This infold has been faulted and intruded by albite porphyry resulting in the formation of a composite body of slates...

Jan 1, 1964

By L. F. Coffin

Monotonic tension and controlled cyclic-strain tests have been conducted on an annealed steel at various strain rates and temperatures in the weep range. Evidence of a strain-induced precipitate reaction abozle 500°C was determined from pronounced cyclic-hardening effects, increase inflow stress, inter granular fracture, drastic decrease in low-cycle fatigue resistance, and loss in tensile fracture ductility, as well as through electron-microscopy examination. It was found that strain rate as well as temperature had a pronounced effect on these observations. A parameter of the form P = T(7.95 - log ip) was determined, which was directly related to the ductility, defined either as the true strain at fracture in the case of simple tension, or as 2N 1/2 ? E p in the case of cyclic plastic strain. A highly satisfactory comparison of the cyclic life as measured and as computed from the ductility predicted by this parameter was obtained for a range of temperatures from 400° to 650°C and for crosshead speeds of 0.002 to 0.2 in. per min. MANY metals subjected to sustained loading at elevated temperatures derive resistance to creep from solid-state reactions of various alloying constituents. These reactions can be many and varied, and occur as a consequence of time and temperature according to reaction-rate principles. Strong evidence exists that many of these reactions are influenced by plastic strain, the argument being put forth that dislocations act as sites for nucleation and growth for the new phase.' Many examples can be cited where plastic strain during transformation influences the structure, and as a consequence affects the properties.2 The low-alloy steels serve as particularly good examples for investigating the effect which aging reactions have on resulting properties. Alloying elements such as carbon and nitrogen, and carbide formers such as manganese, chromium, molybdenum, and so forth, can, by the particular aging reaction which occurs, produce strengthening effects at various temperatures, and so endow strength to the alloy over a broad range of temperatures. These effects have been systematically studied by Glen both during creep3 and for constant strain-rate tension testing.4,5 The work of Glen is of considerable interest in connection with the present study, particularly in regard to the effect of various alloying additions on the true stress-strain curve and on fracture ductility at various elevated temperatures. He has shown that strain-age hardening occurred during plastic straining, which was quite specific both to the temperature of the test and to the alloying element involved. When strain-age hardening was noted at a particular temperature, a .minimum in reduction of area was also obtained. Provided the temperature for the minimum reduction of area exceeded 300°C, all minimum ductility fractures were found to be inter-crystalline in nature. For carbon steels containing molybdenum, two minima in reduction of area were noted, one occurring at 200° to 250°C, the precise temperature depending on the percentage of molyb-

Jan 1, 1964

By N. Arbiter

If two fluid phases are brought into contact with a solid, one fluid may completely wet the surface to the exclusion of the other, or both may wet it, forming a three-phase line of contact. These relative wetting tendencies are quantified by the contact angle 0 which is related by Young's equation (1,2) [12 cos? = 13 ? 23] [to the three interfacial tensions (3). No contact angle for the first fluid, indicating that it does not wet the solid in the presence of the second, means that the difference between the two solid-fluid fluid surface tensions, - 8 is greater than (or just 13 -23 equal to) the fluid-fluid tension 12; a finite angle indicates that the difference is less.*]

Jan 1, 1964

By George Mah, Charles Wert

Internal-friction peaks caused by diffusion of oxygen and nitrogen have been observed in ytterbium. They are thought to be caused by the redistribution, under stress, of strain dipoles around an interstitial oxygen or nitrogen and a neighboring substitutional impurity. With the use of a simple geometrical model, diffusion coefficients for oxygen and nitrogen between special interstitial sites have been calculated. a) APPLICATION OF INTERNAL FRICTION TO MEASUREMENT OF DIFFUSION RATES IN DISSOLVED INTERSTITIAL ATOMS In bcc metals, the interstitial atoms occupy the centers of cube faces (0, 1/2, 1/2), or their equivalents, the center of the cube edges (0, 0, 1/2). An interstitial atom in this position causes an aniso-tropic distortion in the lattice. When stress is applied, mechanical relaxation can take place by the movements of the interstitial atoms. This relaxation has been used to obtain information concerning the movements of the interstitial atoms in the bcc metals. Data for these alloys have been compiled by Stanley and Wert. Other researchers have extended the investigation of interstitial diffusion to the close-packed metals. Gupta and weinig2 found an oxygen peak in a titanium, the height of which is linearly dependent on the oxygen concentration. They assumed, therefore, that they were dealing with movement of atomic ally dispersed oxygen in titanium. KG and wang3 determined that the diffusion coefficients of carbon in fcc steels and in nickel obtained by internal-friction methods were consistent with those obtained by macrodiffusion methods at much higher temperatures. Bisogni found oxygen and nitrogen peaks in hafnium by use of which he deduced the diffusion coefficient of these gases in hafnium. He observed further that the half-widths of these peaks corresponded almost exactly with those of a single-relaxation process; he assumed it to be caused by movement of atomically dispersed oxygen and nitrogen. From these studies, the deduction can be drawn that, in general, diffusion data can also be obtained for the interstitial diffusion in close-packed metals (or more precisely, in slightly impure close-packed metals). One group of such metals for which little data exist for the diffusion of dissolved oxygen and nitrogen is the rare earths. They have great affinity for gases, which enter solution interstitially. In this investigation results were obtained for the Yb-O and Yb-N interstitial solid solutions with traces of substitutional impurities; these solid solutions are of fcc structure. b) MECHANISM OF THE RELAXATION IN FCC CRYSTALS In the fcc structure, an interstitial gas atom is usually situated in the octahedral position (1/2, 1/2,

Jan 1, 1964

By E. S. Cheney

The sandstone-type uranium deposits of the Gas Hills occur in the arkosic, lower Eocene Wind River formation on the southern edge of the Wind River Basin. The d S34 values of pyrite cement associated with uranium mineralization are-significantly lighter than values for syngenetic-diagenetic pyrite nodules, therefore the H2S responsible for the precipitation of the epigenetic pyrite and uraninite was produced [t]epigenetically. These values are much lighter than the values of H2S from neighboring oil fields. The presence of biogenic pyrite in meta-igneous Precambrian cobbles indicates that these cobbles are not remnants of former; vein-type uranium deposits.

Jan 1, 1964

By Rex B. McLellan

A simple model for dilute interslitial solid solutions is set up which enables a solubility equation for the equilibrium between the solid solution and the gaseous solute to be deduced. This solubility equation is used to estimate the partial thermody -namic functions of Ag-O and Fe-N dilute interstitial solid solutions from the measured equilibrium between these solutions and the gas phase. It is shown that the partial excess entropy of the solute atom in solution is a vibrational entropy which is due Principally to the oscillation of the interstitial atom and does not arise from electronic or elastic interaction between the solute atoms and solvent matrix. In this work measurements of the equilibrium between dilute solid interstitial solutions and a gaseous phase are used to deduce the important thermody-namic functions of the solid solution with the aid of a theoretical solubility equation formulated from a knowledge of the thermodynamic functions of the gas and a simple model for the solid solution. The quantity of principal interest which is deduced from the equilibrium data is the change in vibrational entropy occurring when a solute atom (u) is placed in an interstial site in the solvent (u) lattice. This paper forms part of a more general study in which the properties of condensed phases are deduced from measurements of the equilibrium between the condensed phase and a gas. Previous investigations have dealt with the equilibrium between krypton and liquid metals,' a pure metal and its vapor,' and dilute substitutional alloys and the vapor,3 and the subject has been popularly reviewed by McLellan.4 In the latter investigation3 the vapor pressures of very dilute Cu-Ag and Cu-Au alloys were measured with a Knudsen cell technique over a large range of temperatures and the analysis of the vapor-pressure data showed that the relative partial excess entropies were large and positive [ds= -Sudk = 30 for Au-Ag alloys and 150 for Cu-Au alloys; these values should be compared to unity, the value assumed for these exponentials in the quasi-chemical theory of solutions]. For many interstitial solutions experimental data is available for the equilibrium between the solution and a gaseous phase, and this can be used to deduce the vibrational entropies of the solute atoms in solution. The general method employed is to calculate the chemical potential of the solute atoms in the gas and equate this to pi, the chemical potential of solute atoms in the solid, which is deduced from a simple model set up for the dilute interstitial solution (in which the solute atoms act as bound oscillators in interstitial sites). This enables a theoretical solubility equation to be set up. In the case of Ag-O and Fe-N solid solutions the solubility c, is found to vary with temperature according to a relation of the type, where PU2 is the pressure of the O2 or Np molecules. Essentially, the theoretical solubility equation enables the parameter A(T), which gives the vibration entropy, and the parameter AH, which gives the energy of solution of a solute atom, to be estimated from the measured variation of solubility with temperature. The solutions treated are dilute enough to enable solute-solute interactions to be neglected so that the partial energy and excess entropy of solution E, and GS are not functions of composition and the configurational entropy is that of a random solution. Large positive values have been found for sxSu this quantity has not been given sufficient consideration in recent work on interstitial solutions and it is felt that the partial thermodynamic quantities of very dilute solutions should be understood before the thermodynamics of concentrated solutions can be fully appreciated. EXPERIMENTAL DATA 1) The Silver-Oxygen System. The measurements of Steacie and Johnson,= using silver foils, indicate that there is a pronounced minimum in the solubility vs temperature curve for O-Ag solutions. Eichenauer and Miiller6 have recently redetermined the solubility of oxygen in silver using a method developed in the investigation of metal-hydrogen systems.7 The solubility determinations were carried out on compact specimens of differing shapes and sizes and the results indicate a much lower solubility than was obtained by Steacie and Johnson with no minimum at 400°C. Subsidiary experiments showed that the erroneous results of Steacie and

Jan 1, 1964

By L. U. Spellman

Atlantic Cement Company's new multimillion dollar, 10,000,000 barrel per year cement plant went into full operation in February, 1962, bringing into reality a new concept in the distribution of Portland cement. The Cerro and Newmont Mining Corporations, well established in the mineral extraction and dressing industry, backed the venture. To take advantage of the, economics inherent in single production units of large capacity, it was necessary to first find a market' capable of absorbing such large quantities. Cement can be economically shipped by rail and truck about 200 miles. Beyond' that radius from the producing facility the freight costs become prohibitive. No single marker area within that radius exists which could absorb such a large volume of cement. However, water transportation provides a relatively inexpensive method of transporting bulk products many times over such a distance. Thus, it was decided to locate the producing facility near a deep water port which had ready access both to the Atlantic Ocean and, just as important, a good source of raw material. An extensive feasibility study was made and the site at Ravena, New York on the Hudson River near Albany was chosen. Here, vast quantities of limestone in the foothills of the Catskill Mountains are found within a short distance of-the deep-water Hudson River.

Jan 1, 1964