By James H. Bechtold

The yield strength of annealed tungsten was found to have a strain rate exponent 12 times as great as that of low carbon steel. The effects of temperature and strain rate could be correlated through the Zener-Hollomon parameter with a heat of activation associated with yielding of 32,000 cal per g-atom. This heat of activation is independent of strain although both the temperature and strain rate dependence of the yield strength vary with strain. MOST metals have mechanical properties that are relatively insensitive to strain rate, especially at temperatures below that at which creep is important. In iron and molybdenum," however, relatively large strain rate effects are observed in the temperature range where the rapid increase in yield strength occurs which leads to the ductile to brittle transition. In this temperature range Zener and Hollomon' have suggested that the effects of strain rate and temperature T on the yield strength could be correlated through a single parameter, P, in the following manner where Q is a heat of activation characteristic of the metal and associated with some unspecified relaxation process. They also observed that if the temperature is restricted to a relatively narrow range— below room temperature for steel—that the logarithm of the yield strength could be expressed as a linear function of the logarithm of P. From this relation the logarithm of stress should be a linear function of the logarithm of the strain rate at constant temperature: where r will be referred to herein as the strain rate exponent. At a constant strain rate the logarithm of stress should be a linear function of l/T, ay(e = C) ~ eT [4] where q = Qr [5] and is referred to herein as the temperature exponent. These equations have been found to relate the effects of temperature and strain rate on the yield strength of molybdenum in the temperature range wherein the ductile to brittle transition occurs, —75° to +150°C.2 Bechtold and Shewmon3 have shown recently that the ductile to brittle transition in annealed tungsten occurs in the temperature range +150° to +350°C. In this temperature range the yield strength in-

Jan 1, 1957

By T. A. Read, H. K. Birnbaum

Deformation of AuCd alloys having the 8 (orthorhombic) and (3" (tetragonal) structures occurs by the stress induced motion of twin boutdaries. A restoring force acts on displaced twin boutdaries as a result of internal energy increases in the volume through which the boundaries are displaced. The phenomonology of the twin boundary motion is described and a mechanism for twin boundary motion and the restoring force is proposed. A time-dependent stabilization behavior of the twin boundaries, which is observed after the twins are formed by the diffusionless phase transformations, is described. THE AuCd 8 phase (ordered bcc structure) exhibits a transformation to a phase having an orthorhombic structure, 8' (space group D'), for compositions in the vicinity of 47.5 at. pct Cd and to a phase having a tetragonal structure, 8" (point group 4/m, m,m), for compositions in the vicinity 50.0 at. pct Cd. Both transformations are diffusionless, occur on cooling at 60" and 30OC, respectively, and are crystallo-graphically reversible.' They are accompanied by an inhomogeneous deformation which was observed to be twinning in the low-temperature phase. 3'4 The transformations may occur by a "single interface" or by "multiple interfaces."5'6 In the "single interface" transformation, the twinned product phase consisted of two twin orientations as shown in Fig. 1. In the multiple interface transformation the product phase contained "domains" each of which contained two twin orientations, Fig. 2. Deformation of specimens containing transformation twins was achieved by motion of the twin boundaries. Releasing the applied stress resulted in the displaced twin boundaries returning towards their initial positions. This "pseudo-elastic" behavior of the boundaries varied with time after the formation of the twin boundaries by the transformation.

Jan 1, 1961

By R. H. Hiltz

Three titanium alloys, known to provide a mechanically unstable p structure after quenching, were selected as material for a study of the Origin and nature of stress-induced transformation. Data from hardness and tensile tests were used to study the initiation of marten site and the effect of the transfornation and transformation products on the mechanical properties of B titanium, particularly the stress-strain relationships. With the exception that the materials investigated showed a natural aging reaction in the P condition, their behavior is analogous to that of' stress-transforming stainless steels. The transformation starts after initial yielding and is essentially complete just prior to .maximum loading. Once initiated, the martensite itself is capable of propagating the transformation. The deforn-ing materials show low strength, high ductility, and a high strain-hardening exponent. In metallic systems which undergo a diffusionless transformation on cooling, it is possible to produce a similar transformatiorl by plastic deformation under special conditions. Dewez' in delineating Ms temperatures for the titanium-rich end of most titanium binary systems:, established the point of intersection of Ms with room temperature for those particular alloys. Alloy compositions which would quench to mechanically unstable p were established from these data. The first investigation into the possibility of stress-induced transformation occurring in titanium met with little success. It was concluded that such a transformation in titanium was possible only under very special conditions. Continued effort in this direction, however, showed certain Ti-Mo binaries to be highly susceptible to this phenomenon. This fact was utilized by Liu to study the habit planes of martensite and by Machlin and wenig5 to study the effects of stress and plastic deformation on the P to a prime transformation in titanium alloys. The first investigation of the mechanical properties of these alloys was conducted by Holden and his coworkers at Battelle Memorial Institute.' The potentiality of the alloys i3s sheet-forming material was recognized, and the data reappeared in a survey of this type of titanium material.? The initial optimism was tempered by the difficulties in obtaining homogeneous 2i-Mo alloys in commercial-size ingots. The increasing need for good sheet-forming material kept investigation in this direction active, resulting in the development of a commercial alloy of this type.' This study was undertaken to obtain a clearer picture of the mechanism of stress-induced transformation in titanium. MATERIALS AND TEST PROCEDURE Three alloys were selected for this investigation: one a Ti-Mo alloy; another a Ti-Cr-Mo alloy, known to deform martensitically; and the third, a Ti-V alloy with an Ms below room temperature and an Md above room temperature, but known to contain w phase in the quenched condition. The compositions of these alloys are given in Table I. These alloys were cast as 5-lb experimental ingots, employing skull melting. The ingots were hot-forged into 1-in.-round bars. Two 72-in.-thick slices were cut from each bar for hardness testing; the remainder was cut into 0.252-in. tensile blanks. The tensile blanks and one hardness disc from each bar were heated in salt to a temperature 100°F above the 0 transus, held 2/2 hr, and brine quenched. X-ray analysis showed the pieces to be 100 pct 8.* *Omega cannot be distinguished from p by the technique employed. Tensile blanks were machined to size after this treatment. TO prevent transformation due to machining stresses, the shoulders and gage length were ground. True stress-true strain curves were

Jan 1, 1960

By Robert Bakish, William D. Robertson

AFTER more than fifty years of investigation and continuing failure in service, a satisfactory mechanism to explain stress corrosion cracking in homogeneous alloys is still lacking. The relative chemical activity of grain boundaries and adjacent grains, inferred from the boundary structure, has been used to explain intergranular cracking in a brass.' This concept is probably correct as a general hypothesis, but it requires much more extensive development in order to explain satisfactorily the observed phenomena. For example, the specific function of the solute in an alloy must be considered, because intergranular failure does not occur in pure metals,' which are structurally similar to homogeneous alloys. Also, in this connection, an inter crystalline fracture path in binary copper alloys can be changed to a transcrystalline path by relatively small ternary additions.' The fracture path in ß brass is predominantly transcrystalline,' in contrast with an inter crystalline path in a brass. Whether the two different fracture paths are the result of a difference in composition, crystal structure, or the state of long range order is unknown and cannot be determined with ß brass, because only the ordered state can be obtained at room temperature. The study of chemical activity at structural sites in the Cu-Zn system is restricted by the formation of opaque films in an ammonia environment in which stress corrosion cracking is generally observed. Furthermore, both components of the alloy are chemically active and the interpretation of observations is therefore relatively complicated. The Cu-Au system is a better choice for the purpose of studying structural factors. In particular, CuAu is very susceptible to cracking in ferric chloride and opaque films are not formed in this solution; it may be obtained in different states of long and short range order; and, finally, only copper is oxidized in dilute ferric chloride, which considerably simplifies the chemical problem. To provide information necessary for a more general explanation of stress corrosion cracking in homogeneous solid solutions, the following structural factors have been investigated in a Cu-Au alloy having a composition corresponding to Cu,Au: 1) the effect of long and short range order; 2) the structural sites from which copper is removed from the annealed and cold worked polycrystalline alloy; and 3) the effect of annealing time and temperature on structural reactions in the cold worked alloy. Experimental Procedure A Cu-Au alloy of nominal Cu3Au composition was cast from cathode copper and high purity gold and fabricated into sheet and wire. Chemical analysis for copper and gold indicated 48.92 wt pct Cu and 51.01 pct Au. Quantitative spectrographic analysis indicated 0.01 pct Ag, 0.002 pct Pd, 0.001 pct Pb, and 0.002 pct Fe, with traces of magnesium, silicon, and zinc. Presumably most of the remaining 0.055 pct corresponds to the limits of analytical precision. Heat treatments of wire and sheet were conducted in argon or vacuum. Wire specimens, 0.064 in. diam, were heated for 1 hr at 850 °C to establish a definite

Jan 1, 1957

By G. K. Manning, A. R. Elsea, C. R. Simcoe

Boron increases the hardenability of hypoeutectoid steels by decreasing the nucleation rate of ferrite and bainite. It is postulated that concentrations of lattice imperfections, such as exist at the grain boundaries, furnish the necessary energy for nucleus formation. Boron, because of its atomic diameter, will concentrate at lattice imperfections where sites of suitable size are present. Boron will decrease the energy of these local areas by occupying these sites. This mechanism accounts for the large increase in hardenability observed with small amounts of boron. The loss of the boron hardenability effect and the boron precipitate formation are explained on the basis of increased concentration of boron at the grain boundaries either with increasing boron content of the material or with increasing temperature. COMMON alloying elements affect both the nucleation and growth rates of the austenite decomposition reactions.' This effect is largely a result of the slow diffusion rates of these elements. Although a small addition of boron markedly increases the hardenability of steel, the diffusion rate of boron, which is of the same order of magnitude as that of carbon, can hardly account for this effect. An addition of boron in the range of 0.001 to 0.003 pct is about as effective as an addition of 0.30 pct Mo, 0.40 pct Cr, or 1.25 pct Ni in increasing the hardenability of a 0.40 pct C steel;' however, increasing the carbon content of the steel decreases the effectiveness of the boron addition."' The difficulty in understanding why so small an addition of boron can replace much larger quantities of the more strategic alloys, together with the erratic behavior sometimes encountered in boron-treated steels, has interfered with their general acceptance by industry. In the belief that an understanding of the mechanism by which boron increases the hardenability of steel should lead to a more general acceptance of boron-treated steels, a research investigation to determine this mechanism was undertaken at Battelle Memorial Institute under sponsorship of Wright Air Development Center. Experimental Work In order to study the effect of boron on the transformation of austenite to ferrite and bainite, a group of steels was made with a basic composition similar to that of the SAE 8600 series. This base composition was chosen because it has sufficient hardenability to permit accurate measurement of the times required for transformation to start at various temperatures. The chemical analyses of the steels used in the first part of this investigation are listed in Table I. These steels were made as 200 lb heats in an induction furnace. The furnace charge was Armco ingot iron with the alloying elements added as ferroalloys. After the alloy additions were made, the heat was deoxidized with 0.125 pct Al. A 100 lb ingot was cast and an addition of 0.003 pct B, as ferroboron, was made to the metal remaining in the furnace. This metal was cast into a second 100 lb ingot. The ingots were forged to 11/4 in. diam bar stock from which end-quench hardenability specimens were obtained. Part of this material was further reduced by hot rolling to lx¼ in. bar stock from which specimens were obtained for isothermal transformation studies. Studies of Nucleation and Growth: End-quench hardenability tests were performed on these steels, using an austenitizing temperature of 1600°F. The hardenability curves, shown in Fig. 1, indicate that boron treatment resulted in considerable increase in hardenability of the steels. Any such change in hardenability must result from a change in the transformation rate of the austenite, and these rate changes can be established readily by isothermal transformation studies. Isothermal transformation studies were conducted on these steels as follows: specimens were austeni-tized at 1600°F for 15 min, transferred to a lead bath operating at a constant subcritical or intercritical temperature, held for various lengths of time, and water quenched. The specimens were sectioned for metallographic examination to determine the amount and the type of transformation products present. In order to determine the effect of boron on the formation rate of ferrite, isothermal transformation tests were made on the 0.20 pct C steel in both the boron-treated and boron-free condition at an intercritical temperature of 1375°F where ferrite is the only decomposition product of this low carbon austenite. The results of these tests are shown in Fig. 2, where the percentage of ferrite formed is plotted as a function of time at temperature. It is apparent that boron markedly decreased the transformation rate of austenite to ferrite at this temperature.

Jan 1, 1956

By D. A. Thomas, M. F. Comerford

Poly crystalline wires of Fe-3.2 wt pct Si were cold-drawn to 31, 66, and 87 pct reductions of area. Mechanical properties and tnicrostructures were studied after recovery and re crystallization. An initial increase in strength during recovery was ascribed to strain aging, and subsequent softening was largely due to polygonization rather than re-crystallization. No unique actioation energies could be determined for the recovery process. Rather, activation energies ranged from 60,600 cal per mole at 10 pct recovery to 83,200 cal per mole when recovery was 50 pct complete. Sites for the nucleation of recrystallization were found to depend on time and temperature. In the early stages of re-crystallization, nucleation occurred in deformation hands. Later, or at high temperatures, recrystal-lized grains were nucleated primarily al grain boundaries. Polygonized structures did not seem to be preferred sites for nucleation. MUCH of the research on deformation, recovery, and recrystallization processes in bcc materials has been performed on single crystals or lightly worked polycrystals. Little study has been devoted to the relation of mechanical properties to micro-structure in polycrystals after severe deformation and subsequent annealing. This paper presents the results of a study of the tensile properties and microstructures of Fe-Si wires drawn varying amounts and annealed at a series of temperatures. EXPERIMENTAL PROCEDURE The experiments were carried out on an alloy of the following composition: 3.2 wt pct Si, 0.08 Mn, 0.016 C, 0.005 0, 0.0002 N, 0.0001 H, 0.008 P, 0.034 S. The material was received as l-in.-sq bars cut longitudinally from a hot-rolled slab provided by the Armco Steel Corp. The bars were forged to 3/8-in. rounds, centerless-ground to 0.250 in., and swaged to '0.108 in. All subsequent reductions were performed by room-temperature wire drawing at the rate of 2 in. per min. Each preliminary draft gave approximately 30 pct reduction of area and was followed by a l-hr anneal at 1010°C in dry hydrogen. Three lots of wire were made with ultimate cold reductions of 31, 66, and 87 pct reduc-

Jan 1, 1965

By Craig R. Barrett, Jack L. Lytton, Oleg D. Sherby

The types of substructures developed during high-temperature creep of (110)[001]-oriented polycrys-talline Fe-3.1 pct Si were examined by electroetching of dislocation sites. Edge dislocations were observed to accumulate adjacent to grain boundaries and poly-gonize perpendicular to their glide planes to form a "Pile-up" of nearly parallel tilt boundaries. The dislocation density developed within the grains during steady-state creep was found to increase with increasing stress. The formation of periodically spaced groups of edge dislocations along grain boundaries was observed, and it was proposed that these formed to relive bending stresses at grain boundary shear .faults. Grain boundary serrations developed at these faults, and it was suggested that this was a result of localized grain boundary migration at the polygonized groups. THE authors have conducted a series of high-temperature creep tests on (110)[001]-oriented poly-crystalline Fe-3.1 pct Si sheet. The creep specimens were examined at various stages of creep by means of electrolytic etching of dislocation sites using the chrome-acetic acid solution developed by Morris.' Hibbard and Dunn2 have demonstrated that the etch pits produced with this technique correspond to single dislocations. It is the purpose of this paper to present and discuss the dislocation substructures which were formed during high-temperature creep at constant stress. EXPERIMENTAL PROCEDURES The polycrystalline Fe-3.1 pct Si sheet employed in this study contained a (110)[001] texture. This texture was quite strong, and the elastic properties of the sheet closely approached those of a single crystal of iron.3,4 A typical analysis in weight percent for this material is 3.1 Si, 0.1 Mn, 0.003 C,

Jan 1, 1965

By R. W. Powers, M. V. Doyle

ThE solution of a diatomic gas such as 0, or N2 in a metal usually follows Sieverts' law; i. e., Here C is the solute concentration at equilibrium and P, the gas pressure. The proportionality constant Ks is also the equilibrium constant for the reaction 1/2 02 (at pressure, P) - 0 (in solution at [21 concentration., C). to use oxygen as an illustrative gas. Sieverts' law is therefore interpreted to indicate that diatomic gases go into metallic solution atomically and that the solute "gas" atoms interact negligibly with each other. Of course, this interpretation is strictly valid only over the temperature interval in which the reaction indicated in [Z] can be investigated. At temperatures several hundreds of degrees below this interval, the possibility of interactions between solute atoms is conceivable. Indeed, from internal-friction measurements some evidence for the existence of groupings of oxygen atoms in tantalum solid solutions was presented a few years ago.1,2 Over a range of solute concentration, the experimental oxygen internal-friction peak in tantalum, measured as a function of temperature at constant frequency of vibration, can be described as the sum of two elemental peaks, each corresponding to a separate relaxation process. At 0.7 cps, the height of the elemental peak found at 137°C is proportional to the oxygen content, whereas the height of the one at 162°C varies as the square of the oxygen concentration. The 137°C peak was presumed to arise from the stress-induced ordering of oxygen atoms among various classes of octahedral sites in the manner proposed by Snoek.3 The 162°C peak was attributed to a somewhat similar stress-induced ordering process, in which each oxygen atom was interacting with a neighboring oxygen atom. Similarly, the experimental peak due to nitrogen in tantalum can also be described as the sum of two peaks. The height of one varies as the nitrogen concentration and the other as the square of this quantity. In fact, some evidence of solute interactions exist for all oxygen and nitrogen solid solutions of Group V transition metals. However, the interaction energy was not obtained previously for any alloy. The determination of this quantity, as a part of a more intensive study of the interaction between oxygen atoms in solid solution in tantalum, is reported in this paper. PRINCIPLE OF THE EXPERIMENT Consider an equilibrium in a solid solution of tantalum between oxygen atoms which are bound together pairwise and those solute oxygen atoms which are not so associated. 20 (Ta) - O2 (Ta) [3]

Jan 1, 1960

By R. E. Ogilvie, N. L. Peterson

DURING the past few years there has been considerable effort devoted to the understanding of radiation effects on materials. The concept of the Frenkel defect and other lattice defects suggests that radiation may alter the rate of many metallurgical phenomena, especially those which are diffusion controlled. In 1953 R. R. Coltman and T. H. ~lewitt' found an appreciable effect on the ordering rate of Cu,Au due to fast neutron bombardment. Since then several rather comprehensive theories have been proposed on radiation enhanced diffusion in solids.2"4 If the energy of the radiation is above the threshold energy for the removal of atoms from their lattice sites, Frenkel defects will be produced. These defects can be produced uniformly throughout a relatively thick specimen by high-energy X-rays permitting bulk property studies without the limitation of sample dimensions. In this work high-purity arsenic containing 30 ppm of impurities was allowed to diffuse from the gase- ous phase at 700°C into single crystals of p-type germanium containing 0.1 ppm of indium. As the arsenic diffuses into the P-type germanium, an n-type layer will form in the diffusion zone. At the p-n junction the concentration ratio of the arsenic to the indium is constant. Experimental Procedures—The germanium specimens, 10 mm by 10 mm by 5 mm, were polished and etched to a mirror finish. The specimens were then sealed off in a vycor glass capsule at 3 x 10"5 mm Hg pressure with a sufficient amount of arsenic powder to produce a one-half atm pressure of arsenic at 700°C. Specimens were annealed at 700°C without radiation. The diffusion coefficient determined from these samples agrees within 8 pct of previous work done by Fuller.' Three specimens were given diffusion anneals at 700°C in a small tube furnace centered beneath the target of a 2-mev Van de Graaff generator. The specimens when in the furnace were 10 cm directly below the target of the generator. These specimens were irradiated continuously during the diffusion run with the Van de Graaff operating at 2 mev with a tube current of 225 to 250 pamp. The intensity of the x-radiation at the surface of the specimen inside the furnace was approximately 4.5 x l05 roentgens per hr. The temperature was controlled within m2°C by a chromel-alumel thermocouple throughout this work with no observed temperature change due to the radiation. By careful lapping, the samples were polished at an angle of 5 deg to the diffusion zone, giving a XI0 increase in the visible diffusion zone. The location

Jan 1, 1960

By D. I. Bardos, A. M. Bardos, Paul A. Beck

The approximate effective silicon radii in ternary Laves phase alloys with transition elements and silicon were found to range between 1.16 and 1.21A, i.e., considerably smaller than the atomic radius calculated for elemental silicon. The atomic radii were found to increase with the size of the transition element atoms in the structure. It has been noted by Aronsson1 that silicon in solid solution in iron, cobalt, and nickel has an effective CN 12 atomic radius of approximately 1.20Å, a value very much smaller than the CN 12 radius of 1.34Å derived from the interatomic distances in elemental silicon.7 The unusually short metal-silicon interatomic distances in transition element monosilicides and disilicides have been also pointed out by various investigators.1 A similar tendency was observed by Nevitt in Cr3O type silicides.2 Recent work on Laves phases in ternary systems of silicon with transition elements4"8 suggested that extensive Laves phase fields may occur in such systems.8 It has been pointed out by Laves7 that the MgCu2 and MgZn2 type structures lend themselves particularly well for the determination of the effective radii of the component atoms. In these AB2 phases the B atoms are arranged in close packed straight lines, and their distances are related in a simple manner to the lattice parameters.8 The present work was undertaken in order to find out whether or not the B transition element in such AB2 Laves phases can be replaced to an appreciable extent by silicon. In cases where extensive substitution proves to be possible, the "average atomic radius for the B site" at various silicon contents was to be determined, and the effective atomic radius of silicon calculated by extrapolation to complete replacement of the B component by silicon. The following ternary systems were studied: Ti-Mn-Si, Ti-Fe-Si, V-Co-Si, V-Ni-Si, Nb-Fe-Si, Nb-Co-Si, Ta-Fe-Si, Ta-Co-Si, and Mo-Fe-Si. In all of these alloy systems, the Laves phase solid solutions were found to extend over a considerable range of silicon content. As previously reported,4"8 in the V-Co-Si, V-Ni-Si, and Mo-Fe-Si ternary systems Laves phases do occur, even though there are no corresponding binary Laves phases. In stabilizing the Laves phase, silicon acts as if it were decreasing the effective electron concentration of the alloy.8 A more detailed study of the boundaries of the Laves phases in the V-Co-Si and V-Ni-Si systems has been made and will be published elsewhere. In both cases, the elongated Laves phase fields extend parallel to the B-Si side of the composition triangle, clearly showing that silicon is substituting for cobalt, respectively, nickel over a wide range of compositions. The binary Laves phases NbCo2 and TaCo2 have the cubic MgCu2-type structure. It was found that, in both ternary systems with silicon, again the MgZn2-type hexagonal Laves phase is stabilized and that this phase extends to high-silicon contents. In each ternary system at least three Laves phase alloys of the composition A(B1_xSix)2 were used, x here denoting the fractional substitution of the B-transition element atoms by silicon. The alloys, listed in Table I, were prepared by arc melting in argon. Each specimen was water quenched after a homogenizing anneal of 3 days at 110(FC, except for the Mo-Fe-Si alloys, which were annealed at 1200°C. Metallographic examination showed that most of the homogenized alloys consisted of a single phase, although some had minor amounts of a second phase, as shown in Table I. X-ray diffraction patterns were prepared using an asymmetrical focusing camera of large resolution and Fe Ka radiation. The patterns were indexed, and the lattice parameters of the hexagonal Laves phases were determined from the available diffraction lines of highest indices: (213), (205), and (313). The lat-

Jan 1, 1963

By Harry A. Lipsitt, Douglas Y. Wang

A fatigue study in completely reversed axial tension-compression has been perforried on high-purity titanium and on three high-purity alloys of titanium. The alloys each contain approxi7nately 0.75 at. pct of a single interstitial element; carbon, nitrogen, and oxygen, respectivley. The results corroborate a previously published theory which proposed that strain aging under alternating stress was responsible for the fatigue limit behavior of certain alloys. The present data indicate that in these alloys an increasing strain-talline aging effect under alternating stress is provided by oxygen, carbon, and nitrogen, respectively. CURRENT research on the nature of the fatigue limit in metals suggests that the presence of a fatigue limit in metallic materials is a manifestation of strain aging that occurs under alternating stress.lm5 A comprehensive theoretical model based on the above hypothesis has been developed to explain the existence of a fatigue limit.' This model also provides increased insight into several other fatigue phenomena as under stressing, overstressing, and coaxing effects. The theory, as well, provides equal understanding for those cases where no real fatigue limit is observed. Briefly, this theory assumes that the S-N curve for a pure metal is a smooth function of the applied stress, and the effect of adding an element that is soluble (or forms a precipitate) in the pure metal is simply to shift the S-N curve to the right. If the added element confers the power to strain age, the result is a further shift of the S-N curve, this time upward and to the right. Since strain aging is not expected to be a strong function of stress, and since damage per cycle is known to be quite stress dependent, it is to be expected that there will be some limiting lower stress at which the strengthening due to strain aging will balance the damage due to crack propagation. This stress is the fatigue limit. The position of the fatigue-limit knee was thought to be a function of the magnitude of the strain-aging effect on both the finite and infinite life portions of the S-N curve. Although the strain aging hypothesis seems to be reasonably valid for bcc materials,2'6 it needed to be tested for both fcc and cph metals. This report is the first of a series concerning the fatigue-limit behavior of titanium with varying amounts of the interstitial solutes (C, N,, and 4) that are known to cause static strain aging in titanium. Yield-point effects have been reported for polycrys-talline high-purity titanium alloys containing either carbon, nitrogen, or oxygen.7'9 These effects were observed at testing temperatures in the range 100 to 300'. In addition yield-point and strain-aging effects have been reported for single crystals of titanium containing 0.1 wt pct C plus N.' These yield points were observed over a wide temperature range, but no room-temperature aging occurred. Aging at 180' was required to cause the return of the yield point. The magnitude of the yield phenomena in titanium containing interstitials is not expected to be as large as is observed in bcc metals because of several factors. Titanium has a very high chemical affinity for oxygen and nitrogen. The thermodynamic stability of solutions of oxygen or nitrogen in titanium is recognized. Lattice parameter measurements of titanium containing arbon, oxygen,1° or nitrogen" show that the "c" parameter is expanded more than the "a" parameter, but that up to about 2 wt pct this results in an insignificant change of the axial ratio 'c/a." Ehrlich" has shown that the sites occupied by interstitial atoms in titanium are spherically symmetrical and therefore a lattice expansion, at a constant c/a ratio, results in a simple dilation of the interstitial site. Such a dilation involving no shear has been shown to react only with edge components of dislocations.13 This causes only a weak pinning action. Shear stresses would be anticipated locally when only one of the two interstitial positions was occupied. The carbon atom will cause a symmetrical distortion of the lattice whereas the oxygen and nitrogen atoms have, in addition, the previously mentioned chemical affinity of titanium for these elements. These factors will result in a considerably smaller reduction of free energy upon the association of interstitial atoms with dislocations, and therefore a much weaker pinning than has been observed for the bcc metals. These considerations would lead to the hypothesis that of the interstitial elements considered here carbon would cause the strongest pinning effect in titanium where the amount of interstitial in solution is constant. This hypothesis will be borne out in the analysis of the present results.

Jan 1, 1962

By A. A. Bauer

The ?-to-? transformation has been studied in zirconium alloys containing 22 to 70 wt pct U. In this range of compositions the ? phase can be retained by quenching. Transformation to ? occurs by a nucleation-and-growth process. The diffusion of atoms to preferred lattice sites to yield a partially ordered structure apparently controls the rate of reaction. Alpha uranium and a zirconium precipitate from the supersaturated E phase initially formed in alloys outside the equilibrium E phase composition limits. ZIRCONIUM-Uranium alloys have long been of interest for reactor-fuel applications because of the low thermal-neutron cross section of zirconium. Considerable information is available on the various properties and behavior of these alloys1 although there had been a number of areas where information was incomplete. As part of a program to provide more detailed knowledge in these areas, the presently reported investigation was undertaken. The constitutional diagram of the zirconium-uranium system is shown in Fig. 1.' The system is distinguished by a region of complete solid solubility between the body-centered cubic ß-zirconium and ? uranium phases and the existence of an intermediate phase in the vicinity of 50 wt pct U. This intermediate phase, designated as E, is reported3 to have a primitive hexagonal structure with a = 5.03 and c = 3.08A. The structure is partially ordered with zirconium atoms at the 0, 0, 0 position and zirconium and uranium atoms located randomly at the 1/3, 2/3, 1/2, and 2/3, 1/3, 1/2 positions. While the E phase may be nominally designated as of UZr2 stoichio-metry, the random distribution of uranium and zirconium atoms permit a considerable range in composition. Of interest in the research performed were alloys in the range from 20 wt pct (10 at. pct) to 70 wt pct (47 at. pct) U. In this range of compositions the body-centered-cubic ? phase can be retained either completely or partially on quenching. The nature and kinetics of transformation of the ? phase were the subject of study. Proceeding concurrently with the presently reported work was an investigation by Kearns4 which has since been reported. Kearns studied alloys containing 50 to 60 wt pct U prepared from sponge zirconium. While the work reported here is for alloys prepared from crystal-bar zirconium and the techniques of study are to some extent dissimilar to those employed by Kearns, general agreement so far as results and interpretation can be reported. Experimental Techniques—Alloys were prepared and the transformation of the ? phase studied during interrupted-quench and quench-and-temper isothermal heat treatments by means of hardness measurements and X-ray diffraction and metallographic techniques. The isothermal transformation of the ? phase on quenching and tempering was investigated further employing dynamic-modulus measurements. Electrical resistivity and limited Hall coefficient measurements were also obtained as part of the study. Alloy Preparation and Heat Treatment— Alloys containing 15, 20, 22, 30, 40, 45, 50, 55, 60, and 70 wt pct U were prepared from as-reduced uranium and crystal-bar zirconium. The alloys were double arc melted by consumable-electrode are-melting techniques. The final ingots were forged and rolled at temperatures between 790" and 840oC to 1/4-in. rod and 1/8-in. sheet. Chemical analyses of the fabricated alloys were

Jan 1, 1961

By S. Weinig, J. Winter

The grain boundary adsorption of solutes as a function of bulk concentration and solution temperature was studied using internal-frictimz techniques. From the variation of the cor-responding energy of activation for the Phenomenon, the inter-actior2 energy between a solute atom and a high-angle boundary was calculated. Interaction energies in the range of 0.3 ev were obtained, and were used to obtain the actual concentration of solute at the grain boundary. In corroboralory creel, studies the direct grain boundary contribution to the total creep strain was measured. It was found that the interface creep varied with the type and magnitude of the solute adsorbed. Subscribing to the theory of their being energetically favorable sites at the grain boundary for solutes of both Positive and negative size deviations, ternaries were investigated in Which solutes of both types were present. A marked increase in the resistance to grain boundary creep was manifested. THE major difficulty which has been encountered in investigations of the grain boundary segregation of solutes has been the lack of a sufficiently sensitive method of measuring the amount of adsorbed solute at the boundary. For the general case of a high-angle boundary, no direct method of measuring the adsorption at the boundary has been found to date. Internal friction has been used in several studies of grain boundary adsorption1-3 and although it is somewhat indirect, it was demonstrated to have the necessary sensitivity. In this investigation the authors have used internal-friction techniques in conjunction with a study of the grain boundary contribution to the total creep strain. As both parts of the investigation were performed on the same specimens it was possible to combine a highly sensitive technique with a somewhat more direct method in order to obtain information about the adsorption phenomenon. From internal-friction studies the rate of increase of the activation energy was observed to be a function of the difference in size between the solute and solvent atoms. It was proposed that if Gibbs' adsorption isotherm is considered, i.e., where r is the excess solute at the boundary, c is the bulk concentration, and ay/ac is the change in grain boundary energy with bulk concentration, then AH b/ac must vary in the same way as ay/ac and therefore In this way a relative measure of the grain boundary adsorption of solutes is directly obtainable from in-ternal-friction studies. If the previous work in the field of grain boundary adsorption of solutes is examined, certain apparent information is desirable if the phenomenon is to be understood. The most important questions that must be asked are as follows: 1) Is the adsorption of solutes at the grain boundary an equilibrium process? 2) Can the Mott model of the grain boundary be used as a basis of setting up an elastic interaction between the grain boundary and solute atoms? 3) Is it possible to obtain an exact measure of the excess solute at the grain boundary as a function of temperature and bulk concentration rather than merely a relative measure of the adsorption 4) Are the conclusions obtained from an indirect method such as internal-friction studies meaningful in considering gross grain boundary effects such as creep? EXPERIMENTAL PROCEDURE The material used in this investigation was Bureau of Mines "superpurity" titanium (79 Bhn—1500 kg

Jan 1, 1960

By A. E. Nehrenberg

THE mechanism by which austenite forms in steels has received a great deal of attention in the literature in past years.'-'* Our present knowledge concerning this mechanism has been recently summarized quite concisely by Bain and Vilella,1 while a few years ago the literature was carefully reviewed by Roberts and Mehl.² The consensus is that any ferrite-carbide interface is a potential site for the nucleation of austenite during heating above the Acl temperature, and that the new austenite generally grows freely to produce approximately equiaxed grains, whether the carbides are initially present in the lamellar or the spheroidal form. In the case of eutectoid steels, growth of the new grains of austenite continues until contact is established with other grains. Then growth stops and an initial austenite grain size is established which does not change until the heating is continued to some high temperature at which grain coarsening begins. In the case of pearlitic steels which are not of eutectoid composition, the proeutectoid ferrite or carbide may interfere with the growth of the austenite if the temperature is not above that designated the A63 or the Acm, respectively. Although a large amount of work has been done to establish the mechanism of austenite formation in steels, it became clear to the present author while he was studying the transformation characteristics of a new 0.25 C Mn-Si-Ni-Mo hypoeutectoid steel" that the manner in which austenite grows in steels depends upon some factor, or factors, not previously considered. This was indicated by the fact that when this steel in the spheroidized condition was heated above the Ae1 temperature the new austenite which was formed did not envelop the carbides and grow in an equiaxed manner as described by Bain³ or spheroidized steels. Instead, in this steel, the austenite was observed to grow much more readily in certain directions than in others with the result that at temperatures within the Ac1-Ac³ ransformation range the austenite grains were acicular in shape. The excess ferrite was also found to be acicular with the distribution of these phases being such that a lamellar pattern was developed. This unusual directional growth of austenite in this new steel initially in the spheroidized condition is illustrated by fig. 1. A search of the literature revealed that this type of growth was not necessarily peculiar to this steel for similar microstructures had been observed by other investigators.4-8 However, the full significance of these microstructures does not appear to have been appreciated, and no work has been done to determine the conditions responsible for this directional growth of austenite or to arrive at an understanding of it. It was for this purpose that the work described in the present paper was carried out. Material: During the course of this investigation a total of 15 steels was studied. They consisted of hypoeutectoid, eutectoid and hypereutectoid carbon steels, and hypoeutectoid and hypereutectoid alloy steels, all of which were obtained in the annealed condition from commercial warehouse stock. As received, the carbon and alloy hypereutectoid steels had microstructures which consisted of spheroidal carbides in ferrite, whereas the eutectoid steel and the hypoeutectoid steels were pearlitic. The grades of steel represented were 1050, 1080, 10110, 3310, 4140, 4340, 4615, 6145, 8620, 9260, 9442,

Jan 1, 1951

By J. W. Faust, H. F. John

Generalized conditions for rod or ribbon growth by the twin plane re-entrant edge mechanism are given. It was shown that this mechanism can result in growth of twinned platelets from dilute metal solutions. The platelrts 01 the fee metals are faceted by (111) planes and contain two or more twin planes. Microsegregation traces were revealed in silver grown from a thallium solution. VOGEL has already set down conditions for dendritic growth;1 however, this was the normal single-crystal dendritic growth experienced during solidification. In this work it is desired to set down the crystallographic conditions that will lead to rod or ribbon growth with smooth facets. These are as follows. a) The growth must be crystallographically limited (i.e., faceted growth). b) In order to have directed growth, some mechanism must allow easier nucleation than two-dimensional nucleation. That mechanism is afforded by the re-entrant edges at twin planes.213 Thus there must be twin planes present in the rods or ribbons. c) The growth direction must lie in the twin plane. If not, the twin plane will grow to the face or side of the ribbon and the site of easy nucleation will be lost. d) The growth direction must be parallel to at least one plane of the faceting planes, and no set of the faceting planes can be perpendicular to the growth direction. A corollary to these conditions involves the number of twin planes necessary to maintain the indestructible re-entrant edge. The number depends on the crystal structure of the material. An analysis of the data available shows that a material whose faceting planes form an open figure requires at least one twin plane while materials whose faceting planes form a closed figure require at least two twin planes in order to form the indestructible re-entrant edges for extended growth. The conditions and an assessment of the possibility of rod or ribbon growth are given in Table I for several crystal systems. As can be seen the fee, diamond and zinc blende, or-thorhombic, rhombohedral, and one form of the hexagonal lattice systems can yield this type of growth, but not the bcc metals nor the hexagonal

Jan 1, 1965

By T. H. Courtney, G. W. Pearsall, J. Wulff

The mechanism, of the decrease in transition temperature of Nb3Sn was studied. Presintered Nb3Sn powder compacts were heated in a dynamic vacuum at elevated temperatures. Loss of tin resulted from these heat treatments and transition temperature as a function of tin loss was discontinuous at a critical value of tin loss. In general, decreases in transition temperature were correlated with deviations from AS a class, the A15 structure-type (also known as Cr3O or ß W) compounds have the highest superconducting transition temperatures.' In this class are stoichiometry and presence of vacancies in niobium sites. The effect of vacancy distribution on the physical properties of Nh3Sn is considered. It is concluded that the close-packed atomic A chain in the A3B A15 structure must be preserved both in coutinuity and direction if good superconducting properties are to he obtained. tempting to associate these high transition temperatures with the most unique crystallographic feature of the A3B structure: the three close-packed, orthogonal chains of A atoms.'0"' There are at least three principal mechanisms by which the perfection of these "A-atom chains" could be interrupted: changing stoichiometry, inducing disorder, or introducing vacancies. Departures from stoichiometry in either direction in V3Ga lower the transition temperature.7'8 In niobium-

Jan 1, 1965

By J. O. Brittain, E. P. Lautenschlager, D. A. Kiewit

Compression tests were run in the temperature range of 700° to 900°C ox 0' phase NiAl intermetal-lic alloys of several grain sizes. At these temperatures the minimum strengths were observed at the stoichiometric composition. While significant increases in strength occurved in both the low-nickel (vacancy) and high-nickel (substitutional) regions, the highest strengths were found in the high-nickel region. During deformation serrated flow was sometimes observed in the low-nickel alloys. After deformation transgranular cvacking and deformation striations were observed in all compositions tested. AS part of a general investigation of the properties of NiAl inter metallic compounds, a preliminary study of the role of point defects upon plasticity was made by high-temperature compression tests on ß' NiAl specimens of several grain sizes and compositions. ß' NiAl is an intermetallic compound having a CsCl structure and a rather wide range of composition from A1-45 at. pct to 60 at. pct Ni.1 According to Bradley and Taylor2 and to cooper,' it possesses a defect lattice in which departures from stoichiometry in the direction of decreased nickel content lead to the presence of vacant nickel sites (although Cooper's work indicates that a small amount of substitution also occurs) whereas departures on the high-nickel side lead to substitution of nickel on aluminum sites. NiAl forms congru-ently from the melt at approximately 1650°C,1 and thus has a higher melting point than either of its component elements. Up to this time, although this and other high-melting intermetallic compounds have been suggested for elevated-temperature usage,4 only the hardness4 and a few tensile-strength measurements5 have been reported for NiAl at high temperatures. In the present investigation the effects of composition upon the compressive-strength properties in a range of 700° to 900°C have been measured for NiAl of several grain sizes. EXPERIMENTAL PROCEDURES The alloys were made as described elsewhere6 from an A1-46.8 at. pct Ni master alloy furnished by the International Nickel Co. with additions of high-purity nickel and aluminum. The charges were vacuum-induction-melted in A12O3 crucibles with small amounts of helium added to the atmosphere to suppress vaporization. They were cooled slowly from the melting temperature to achieve uniform grain size. In order to refine the as-grown grain size a special rolling technique was developed. Alloys were packed into 0.10-in. wall-type 302 stainless-steel tubes which were partially filled with magnesium oxide to prevent bonding between the alloy and the steel jacket. The ends of the tubes were closed by hot forging, and the packets were then hot-rolled. The alloys with greater than 50 at. pct Ni were rolled at 1100°C, but it was found necessary to increase the temperature to 1350° C before alloys with less than 50 at. pct Ni would roll without cracking. With these temperatures, reductions as high as 48 pct were achieved in a single pass. The rolled alloys will hereafter be referred to as "fine grained" whereas the as-grown material will be designated "coarse-grained''. The compression specimens were made by cutting square cross-sectional pieces, approximately 3/16 by 3/16 by 1/2 in., with a water-cooled diamond cut-off wheel from the as-grown or the rolled alloys. Specimens were ground to their final dimensions by polishing through 3/0 grit silicon carbide papers. The final shape was a rectangular parallelepiped of square cross section having a height-to-width ratio of 3:1. Compression testing was carried out in a compression rig of our own design mounted on an In-stron Floor Model. The specimen chamber could be heated to 1000°C and was controlled within ±2°C. The compression rig was enclosed within a bell jar and was maintained at a 50 µ of mercury vacuum throughout the duration of the test. The test cham -ber was heated from room to test temperature within 15 min. Specimens were then held at the test temperature 30 min prior to testing. Previous experiments indicated that no grain growth would occur within this time. An Instron Variable Crosshead speed unit was used to adjust for small variations in specimen lengths in order to have a constant initial strain rate, €, for all specimens of a group. For the fine-grained specimens the strain rate was changed rapidly at constant temperature by a factor of 10 with the speed lever on the Instron. For a given € the compression data was analyzed in terms of true plastic strain (E) and true compressive stress (0).

Jan 1, 1965

By J. O. Brittain, E. Lautenschlager

An investigation was conducted on fine grained airon wire to measure the influence of the temperature of deformation on strain aging near room temperature. Specimens were deformed various amounts at 77°, 195°, or 273°K and aged. The strain aging was followed by either internal friction or return of the yield-point measurements. The results show that strain aging occurs in three stages. During the first stage there is small, almost immediate return of the yield point. The solute carbon concentration, as mesured by internal friction, remains constant in stage I but is lower than the concentration in the unstrained condition. In the second stage, the solute concentration decreases while the magnitude of the yield point increases. In the third stage, the solute atoms continue to drain from the solution, the yield point approaches a maximum, and the strain-hardening coefficient and flow curve increase. The kinetics of the strain aging reaction are not the same for the two sets of measurements since the internal friction results lag behind the yield-point measurements. However, the strain-aging kinetics measured at 44° and 64°C showed no effect due to the difference in initial deformation temperature; nor were the strain aging kinetics influenced by low-temperature anneals at 77°, 195°, and 273°K. 1 HE object of this investigation was to measure the effect of initial deformation temperature on the strain aging of a-iron by tensile tests (i.e., return of the yield point) and internal friction methods, to correlate the results of the two measuring methods, and to measure the effect of low-temperature annealing (<273°K) after low-temperature deformation upon strain aging. The experiments were performed on fine-grained a-iron wire containing 0.02 wt pct c.l According to Thomas and Leak,&apos; return of the yield point and internal friction are similar measures of strain aging since both are dependent on solute atoms leaving the solid solution. The decrease in internal friction as a function of aging time is indicative of the removal of solute atoms from the solid solution, while the return of the yield point as a function of the aging time gives the rate of arrival of solute atoms at the dislocations. According to Cottrell and Bilby,3 during aging the solute atoms create an "atmosphere" which locks the dislocations and causes a return of the yield point on subsequent testing. It has been shown that after low-temperature neutron bombardment, a-iron goes through a stage of recovery at low temperatures which can be attributed to the annealing of iron interstitials&apos; and/or vacancies.4 If, after low-temperature deformation, there is an interaction during a low-temperature anneal between mobile point defects and the solute atoms (i.e., carbon atom interaction with vacancy or iron interstitial), it is possible that some solute atoms will be found at defect sites other than dislocations. Such changes in the sinks for the carbon atoms might be expected to alter the strain-aging kinetics sufficiently to be detected by either inter-

Jan 1, 1962

By M. Cohen, D. J. Blickwede

Quantitative observations concerning the carbide phases in high speed steel are of importance for two general reasons: (1) the carbides, being inevitable constituents of the final structure, exert a direct influence on the properties of the steel; and (2) a substantial proportion of the total alloy content is tied-up in the carbides, and hence the extent of their solution on austenitizing governs the composition of the steel matrix. The latter relationship has a vital bearing on the response of the steel to tempering as well as on its performance in subsequent service. Accordingly, in the course of a long-term study of the behavior of high speed steels, the authors were confronted with the problem of securing quantitative data on the carbide phases. The obvious method for acquiring such information is to isolate the car-bides from the steel and subject them to chemical, X ray diffraction and other measurements. There are well-known extraction techniques which involve the chemical or electrolytic solution of the less noble matrix (ferrite, marten-site or austenite), thus leaving a residue of the carbide phases. However, the results obtained must be scrutinized carefully1,2 since the carbides may be affected by the chemical or electrolytic action. It is the purpose of the present paper to describe the experiments leading to an electrolytic-extraction technique for quantitatively isolating the carbides from both I and hardened high speed steel. Particular attention is paid to the amount, as well as the composition, of the carbides so that the matrix analysis becomes ascertainable by subtraction from the overall steel composition. Illustrative results are given for the M-2 grade of tungsten-molybdenum steel. Review of the Literature The chemical method of dissolving the matrix selectively with respect to the carbides makes use of dilute non- oxidizing reagents such as hydrochloric or sulphuric acid. Although this simple procedure has led to the determination of the cementite composition,3,4 it achieved only limited success because of the interaction between the acid and the carbide residue. Some of the carbides may not only be destroyed in this way, but the hydrogen released is likely to remove part of their carbon as hydrocarbon gases. The electrolytic technique of isolating carbides has the advantage of rapidly dissolving the specimen (anode) in the presence of less reactive solutions than are practicable with the chemical method. This reduces the possibility of chemical attack on the carbides, and furthermore, the hydrogen evolved during the electrolysis is released at the cathode which is not in close proximity to the carbides. The common electrolytes adopted for this purpose are hydrochloric and sulphuric acids.5-l1 Aqueous solutions of ferrous salts have also been used.12,13 A considerable advance in experimental technique was introduced by Treje and Benedicks14 who developed a double-compartment cell for electrolytic extraction, the anode and cathode chambers being separated by a porous diaphragm. A solution of 15 pct sodium citrate, 2 pct potassium bromide and 1 pct potassium iodide was selected for the anolyte, while the catholyte consisted of a 10 pct solution of copper sulphate, with copper serving as the cathode. This type of cell has a number of desirable characteristics: 1. The anolyte has a pH value close to 7, at least at the beginning of the run. 2. The iron that dissolves from the anode-specimen forms a water-soluble complex ion with the citrate, thereby preventing the precipitation of iron hydroxide (which would contaminate the carbide residue) despite the neutrality of the solution. 3. Copper deposition instead of hydrogen evolution occurs at the cathode, and this avoids an increasing concentration of hy-droxyl ions which (in an otherwise neutral solution) might cause the precipitation of insoluble hydroxides. 4. Contamination of the anode chamber by copper sulphate is inhibited by the porous diaphragm. Houdremont and coworkers15 applied the above method (with the further refinement of excluding oxygen during the electrolysis, washing and drying) to the extraction of carbides from a series of plain carbon steels after various heat treatments. They had quantitative success only with specimens in the annealed condition, and concluded that the size and shape of the carbide particles play an important role in the isolation process, with large spheroids exhibiting the least tendency to decompose during the electrolysis. Up to the present time, the citrate double-cell has not been used to any extent for isolating the carbides of high alloy steels, apparently on the grounds that the complex carbides are more resistant than cementite to attack in the simpler acid electrolytes. In particular, Bain and Grossmann7 and Gulyaev10.10a have employed the hydrochloric acid cell for their investigations of the carbides in high speed steel.* It will be demonstrated here that this type of cell is capable of yielding quantitative results in the case of high speed steel, and actually has certain advantages over the more complicated double cell. However, in order to provide a rigorous test of the quanti-tativeness of electrolytic procedures for the problem at hand, both methods were studied in considerable detail.

Jan 1, 1950

By W. D. Robertson, A. S. Tetelman

The technique of decorating dislocations was employed to investigate deformation and fracture resulting from Precipitation of hydrogen in Fe-3 pet Si single crystals. It is shown that cracks are produced on (100) planes inside crystals, as a consequence of the precipitation of hydrogen gas, either when crystals are quenched from a hydrogen atmosphere at elevated temperatures or cathodically charged with hydrogen at room temperature. Plastic deformation in the vicinity of cracks, observed as arrays of decorated dislocations, is in conformity with the calculated stress distribution about a crack containing an internal pressure, and the observations provide information permitting a detailed analysis of the mechanics of crack growth. The fracture characteristics of crystals containing internal cracks were evaluated at 25o and -196°C and the results are related to the mechanism of hydrogen embrittlement in terms of the growth of preexisting cracks. HYDROGEN in bee iron or steel produces two characteristic changes in mechanical properties: I), a decrease in ductility (macroscopic strain at fracture) that depends on temperature and strain rate, and 2), spontaneous fracture under static load that depends on time and apparent stress. Resolution of these phenomena into the microscopic processes that combine to produce the macroscopic effects is especially difficult in the Fe-H system in which the active component cannot be directly observed and only maintained in equilibrium with great difficulty in the temperature and pressure range in which embrittlement phenomena appear. As a result of these complications, verification of the numerous hypotheses&apos;-5 that have been proposed to explain the microscopic mechanism of embrittlement depends on self-consistency with measured changes in macroscopic properties that are averaged over the volume of a specimen. It is obviously important to obtain a more direct evaluation of the microscopic processes that combine to produce embrittlement. Accordingly, the present investigation was designed to identify and observe, as directly as possible, the microscopic effects of introducting hydrogen into a bee crystal. It was concluded from a previous investigation6 of X-ray line broadening, produced by introducing hydrogen into pure iron at room temperature, that the only effect that could be associated with the introduction of hydrogen was plastic deformation; in particular, dilation of the lattice was not observed, within ± 0.01 pet, and no evidence was found that could be interpreted to support the idea7&apos;* that hydrogen occupies tetrahedral interstitial sites in the iron lattice. The absence of lattice dilation is consistent with the extremely small solubility of hydrogen in bee iron9,10 (0.015 at. pet at 900oC and 1 atm pressure), and the evidence of plastic deformation is consistent with the fact that hydrogen, introduced by cathodic charging, eliminates the carbon yield point.11-13 Following this investigation, the immediate problem was to devise a method by which plastic deformation could be observed directly. The technique employed by Hibbard and Dunn14 to observe the movement of dislocations during bending and subsequent polygonization of Fe-3 pet Si single crystals was adopted and modified for the present purpose to include the observation of dislocation arrays in the volume of the crystal, and their association with the fracture process. EXPERIMENTAL PROCEDURE Single crystals of a high purity Fe-3 pet Si alloy, containing 0.007 pet C, were grown in vacuum by

Jan 1, 1962