By Na Wang, Chao Du, Yao Zhang Shuqiang Jiao, Hongmin Zhu

"Na2NbAlO5 was synthesized using Nb2O5 and NaAlO2 as raw materials in molten NaCl-CaCl2 by a solid reaction. With an addition of sodium into the melts, Na2NbAlO5 was subsequently reduced to form NbAl3 intermetallic compound with a particle size of 50-300nm.IntroductionThe intermetallic compounds of niobium aluminides have been a subject of research interests as high temperature materials because of their properties such as high melting temperature, large specific strength at elevated temperature, good resistance to high temperature oxidation, low density and large ductility [1,2]. They are applicable for turbine blades in aircraft engines and stationary gas turbines [3,4].In recent years, the methods of powder synthesis have been widely discussed. There are many methods to synthesis intermetallic compounds such as conventional melting and solidification [5], powder metallurgy [6,7], reaction sintering [8] and reaction sintering with prior mechanical activation [9,10]. There is a prominent weakness in such methods that they use metal to produce intermetallic compounds by the means of diffusion reaction. Although the metal can diffusion sufficiently, it is still hard to avoid maldistribution of the constituents which impairs the properties of the materials."

Jan 1, 2012

By T. S. Bannos

Section 1417 of the Safe Drinking Water Act Amendments enacted by the O.S. Congress prohibits the use of lead containing solders for potable water systems in new construction or when making repairs. The legislature defines "lead-free" solder as containing less than 0.2% lead. In the development of a new solder it was recognized in addition to the lead free requirement, the alloy should perform as well as the popular 50/50 tin lead solder, both in application and properties. Another objective was to have only nontoxic elements. This led to the development of a 4.0% copper, 0.5% silver and 95.5% tin solder. Review of the merits of other alloy systems and the development of the physical properties along with test data are presented for the lead free tin. rich alloy.

Jan 1, 1990

By Florian Kongoli

The optimal operation of the blast furnace depends considerably on the properties of the sinter fed into the furnace. As a result, the optimization of the sintering processes has a direct effect on the overall effectiveness of the iron making processes. In order to produce a good sinter special care needs to be taken in order to assure it has a good permeability and reducibility and it is able to retain these properties for a certain time. If the sinter starts to melt down early in the upper part of the blast furnace, where its solid state reduction is essential, permeability decreases, the gas channels get blocked, reductibility diminishes and serious problems may also follow. Among the factors that influences the above mentioned sinter properties are the oxygen potential and fluxing components. Nevertheless, their effect on the phase relations during sintering and sinter reduction conditions has not yet entirely clarified and confusion exists in literature. This quantification becomes even more important today where many new minor components such as Al2O3 and MgO enter the sinter through raw materials. This work quantifies the effect of oxygen potential and fluxing components such as alumina and magnesia on the liquidus and phase relations of the sinter primary melts in the iron rich portion of CaO-FeO-Fe2O3-SiO2 system at sintering conditions. This is carried out by the means of new type of industrial diagrams in the form of Fe/CaO vs. SiO2 that can directly help the optimization of the sintering processes.

Jan 1, 2006

By P. T. Velu

Light weight aluminum alloys are the major construction materials for a number of structures in automobile and aerospace industries. Higher cost of production is the key impediment which restricts the usage of these alloys. A new electrochemical process route for the low cost production of aluminum alloys is being investigated, in which alloying elements are obtained from the dissolved compound. In the present investigation, solubility of lithium compound has been determined by measuring the EMF, when it is dissolved in the electrolyte. The solubility of Li2CO3 increased with temperature from 2.95 wt pct at 1063 K to 7.57 wt pct at 1093 K. Activities of the compound in the electrolyte were deduced using Temkin's ideal solution approach.

Jan 1, 1995

By Rafael Colás

Computer visualization can be employed in industry as an aid to the understanding of the complex interactions between variables encountered in production. The examples of ingot casting of rimming steel and that of hot rolling of low carbon steel strip are presented. Both processes are mathematically modeled, and their results are presented in a graphical way. Such models have been proven to be an asset in quality improvements and increase of productivity as the personnel involved get a better understanding of their job.

Jan 1, 1993

By Georgios Kolliopoulos

Water is a critical commodity of our generation and a key compound for the chemical and mining industries. Sustainable industrial development is directly associated with the ability to recover clean water from contaminated sources. Forward Osmosis (FO) is a low-energy footprint membrane process allowing the recovery of clean water from high salinity effluent streams. In FO, water is recovered spontaneously into a concentrated draw solution (CDS). Energy is required to separate the recovered water from the resulting dilute draw solution (DDS). In the current work, the fundamentals of the FO process and the most important aspects affecting its performance are discussed. An energy comparison of FO and conventional water recovery technologies is presented. Finally, the opportunities FO presents in the field of hydrometallurgy are analyzed.

By Arthur E. Morris

Process modeling software is used extensively in process engineering, but there is a notable lack of affordable software for educational uses. This paper describes two educationally oriented software programs for thermochemical modeling of processes involving metals, minerals, and ceramic materials. Both programs run as Excel@ spreadsheet files. The first is FREED, a thermodynamic database program containing datafiles for 2500 species. It contains the entire U. S. Bureau of Mines and most of the U. S. Geological Survey database, plus data for scores of other species drawn from various sources. Several modules are available for manipulating and viewing the data. The second program is THERBAL, for making thermodynamic calculations using FREED data. Equilibrium calculations can be made for systems with non-ideal solutions, for a specified set of pressure, temperature, and input amounts of reactants. An optional heat balance is also calculated. The results are displayed as tables or charts in Excel worksheets. Examples of the use of THERBAL will be given for the reforming of natural gas for DRI production, DRI production, and EAF steelmaking. Some observations will be made on its use in the classroom. The development of FREED and THERBAL was initially carried out at the Department of Metallurgical Engineering, University of Missouri - Rolla as part of a project to preserve and enhance the Bureau of Mines database. The current versions were developed privately by the authors.

Jan 1, 2002

By Akira Yazawa

The continuous converting has attractive advantages, but further experimental studies on the slag are required, when the process is considered thermodynamically. The summarized experimental results, obtained with iron silicate slag and with ferrite slag and results relating to actual operation are described and discussed in this paper. At first, equilibrium relations at controlled oxygen potentials among three melts of silica-saturated iron silicate slag, white metal and copper are investigated. The results obtained for slag agreed with the thermo-dynamical predictions. Namely, to suppress a magnetite separation, the system should be at high temperature; in the case of the S02 gas of 10 kPa, for example, magnetite did not separate from the slag at 1300°C, but at 1250 and 1200°C the slag was saturated with magnetite even at lower SO2 pressure. Copper losses caused by dissolution of its oxide increased with increasing 5O2 pressure, and were slightly lower than those reported in previous papers without the matte phase. When the continuous converting slag does not contain any appreciable amount of silica - in contrast to the conventional smelting slag ferrite slag would form, but there was no published fundamental work on-ferrite slags. Hence, the melting behavior and activities of the system CaO-Cu2O-Fe2O3 have been investigated. The liquidus diagram in nitrogen atmosphere was, constructed using both thermal analysis and quenching method. The low liquidus temperature region without magnetite separation was found in the part of low content of Cu2O in the section Cu2O-CaO-Fe2O3 and Cu2O?Fe2O3¬CaO?Fe2O3. The activity of Cu2O in the system was also measured. Slags, composed-of CaO, Cu2O and Fe2O3, in platinum crucibles were equilibrated at 1250°C and controlled oxygen pressures. After quenching, the-composition of slag and platinum crucible were determined qualitatively. On the thermo-dynamic analysis of the results, iso-activity lines were drawn, and it was shown that the slag in the converting furnace of the Mitsubishi process exists in an adequate region of the composition triangle.

Jan 1, 1976

By F. Mucciardi

With the increasing trend to continuous smelting and converting, granulation of copper matte is gaining prominence as a means of decoupling the smelting and converting operations. Moreover, granulation is also being seen as a possible avenue to using higher grade oxygen in converters. By feeding cold solid matte, the oxygen concentration can be increased to compensate for the lower enthalpy feed. This leads to a higher grade of SO2 in the off gas and a lower total flow rate. Current granulation technology relies on the cooling of a falling matte film by water jets. This technology while effective has several drawbacks including those related to safety. Noranda and McGill University have developed a new process (patent pending) for solidifying copper matte (or slag). It overcomes many of the negatives of current technology. The system is based on an air cooled twin roll caster. This: new system uses no water and instead incorporates heat pipe technology to transfer the heat from the solidifying matte to the cooling air to produce a thin strip of 1 to 2 mm in thickness. Testing of a prototype unit demonstrated its viability. This paper describes this newly developed, twin roll casting system that is completely waterless. The advantages of this process as well as the findings from several tests are also detailed.

Jan 1, 1999

By Christoph Sagadin

Corrosion mechanisms between high melting synthetic ferronickel slags and refractory were investigated. The used slags were prepared by mixing and melting of specific oxides. Substrates of the applied refractory material and specimens of FeNi slags were heated in a hot stage microscope up to 1650 °C. The experiments were performed under a defined gas atmosphere of 60% CO and 40% CO2. A further examination of the formed phases between slag and refractory occurred by scanning electron microscope. The investigations indicate that the slag penetrates between magnesia grains and partly dissolves magnesia. Spot analyses show that iron diffuses into the magnesia grains, which transform to magnesiawustite, meanwhile SiO2 forms different types of olivine like forsterite and monticellite. Thermodynamic calculations confirm the formation of these phases. The combination of practical lab scale experiments and thermodynamic calculations should finally contribute to an improvement of the refractory lifetime and performance.

By A. G. Cecutti

A brief overview of the known significant health effects of both Nickel and Cobalt will be presented. Some time will be given to the current research activities, especially for Nickel. Emphasis will be placed on some of the controversial issues associated with their health effects.

Jan 1, 1988

By Gerald M. Rich

Magma Copper Company, a subsidiary of Newmont Mining Corporation, has initiated many changes in the continuous casting of 5/16 inch diameter copper rod since startup of the San Manuel rod plant in early 1972. With rod production at forty percent over design capacity, many production records have been established including a record cast of 761 tons of salable rod in a twenty-four hour period. The most challenging and rewarding introduction was the continued utilization of an alloyed copper casting wheel in lieu of the conventional steel wheel. With proper cooling and careful control of the mold release agents. as much as 58.000 tons of copper were cast on a single copper wheel. Other advantages are: 1) Fifteen percent increase in available casting time 2) Reject rod from steel inclusions was reduced by nearly one-hundred percent 3) Wheel cost was decreased by ninety-one percent 4) Natural gas consumption dropped approximately fifteen percent 5) Large increase in refractory component life 6) Reduction of manhours/ton. Many other modifications have contributed to excellent rod quality and high operating efficiency. A two-piece launder was replaced with a single castable launder which reduced oxygen pickup and provided better slag removal. Modifications to the bar preparation unit, pickling system, and coiler resulted in considerably higher milling efficiency.

Jan 1, 1976

By Xiao Y. Yan

A fused salt electrochemical process was investigated for the synthesis of non-oxide ceramic powders directly from metal oxides, boric oxide, and carbon powders by electro-deoxidation. Sintered pellets of the mixed powders were designed to act as a composite cathode in the electrolytic cell. Electrolysis was carried out in molten CaCl2-NaCl eutectic at 3.1 V and at 600-900 ºC under argon. The favoured cathodic reaction was the removal of the oxygen from the oxides to produce metal atoms that reacted with either the reduced boron atoms, forming a metal boride, or the carbon initially present in the sintered pellets to produce a metal carbide. The technical viability of the process was demonstrated by the electro-deoxidation of sintered pellets of TiO2/B2O3 and TiO2/C to produce TiB2 and TiC, respectively. Compared to existing carbothermic reduction process, this new electrochemical process may be less energy intensive and may lead to lower production costs. I

Jan 1, 2008

By Philip E. J. Green

Two of the cornerstones of total quality management, the use of statistical and problem solving tools, and the involvement of employees, are directly applicable to environmental protection. The reduction in variation decreases the chances of violations and mishaps. Involving employees in minimizing environmental impacts is critical. One mistake, even with the best technology, and your plant can be shut down, customers lost and fines and penalties imposed - your reputation and the environment damaged. Proven strategies for involving employees in environmental protection, and over-coming the frequently strong differences of opinions about what constitutes environmental protection, will be discussed.

Jan 1, 1992

By E. Fockedey

he destruction of free cyanide on a Co3O4 doped carbon felt was studied. The experiments were done with an eiectrochemical filter press cell on dilute alkaline solutions containing 250 mg/l NaCN. No chloride ions were added to the solutions. The cobalt oxide protects the felt against corrosion and has a catalytic effect on the degradation of the cyanide. This kind of electrode allows working with current density as high as 1200 Aim without any visible degradation of the felt. The most interesting results were obtained with a current density of 400 Aim' at which the cyanide concentration can be lowered to 5 mg/l with a current efficiency of more than 70 % and a specific energy consumption of about 10 kWh/ kg CN.

Jan 1, 1998

By Hong Yong Sohn

A thermodynamic and experimental investigation has been performed to develop a new process for converting sulfur dioxide to elemental sulfur by a cyclic process. The most promising new process is a cyclic reaction scheme involving calcium sulfide and calcium sulfate. In this process, the reaction between sulfur dioxide and calcium sulfide produces elemental sulfur vapor and solid calcium sulfate. The latter is reduced by a suitable reductant such as hydrogen to regenerate calcium sulfide. 'Experimental results showed that up to 60 % of calcium sulfide powder was converted to calcium sulfate in 10 min at 1153 K under a sulfur dioxide partial pressure of 25.8 kPa. More than 95 % of nickel-catalyzed calcium sulfate powder was converted to calcium sulfide in 20 min at 1123 K under a hydrogen partial pressure of 86.1 kPa, water vapor being the only gaseous product. Sulfur dioxide-containing streams from certain new sulfide smelting plants contain much higher partial pressures of SO2. The rate of the first reaction is expected to be accordingly higher than in the test conditions reported in this paper.

Jan 1, 2002

By A. Kiziltas, D. J. Gardner, C. W. Mcllwraith, J. W. Bridge, M. L. Peterson

"Dynamic mechanical thermal analysis (DMTA) tests were conducted on high-oil content, paraffin-based wax used in wax-coated granular composites. These composites make up the surface of synthetic Thoroughbred horse racetracks used in North America. The modulus and damping response from the DMTA tests were correlated with the dynamic triaxial shear strength response of the bulk track material taken at two different operational temperatures and at four strain rates. The purpose of these tests is to understand the mechanisms of shear strengthening of the bulk track material as the wax is heated through the first crystalline solid to liquid nominal transition temperature. Previous work using differential scanning calorimetry confirmed that under common operational surface temperatures, the wax coatings undergo distinct thermal transitions. The resulting increase in triaxial shear strength values affects the consistency of the racetrack which, in turn, can potentially affect Thoroughbred racing performance and safety of the track surface.IntroductionSynthetic granular composite materials are being used in nine Thoroughbred horse racetracks in the United States as well as in other tracks around the world. In one case, their use was mandated by the state of California in 2007 due to testimony that these tracks were significantly safer than traditional dirt tracks [1]. Several synthetic tracks have shown substantial reductions in injuries since switching to synthetics; one California track showed a 75% reduction in catastrophic horse injuries during the first year as compared to the previous year racing on a dirt track [2]. The composition of the tracks in the U.S. generally consist of silica sand (>70%), polymer fibers (<5%), and rubber particles (0-15%) all coated with a paraffin-based, high oil content wax [3, 4]. In a recent study of several synthetic racetracks, to include the track location in this study, the oil content ranged from 34 to over 44% by mass [5]."

Jan 1, 2011

By Adolfo Pillihuaman Zambrano

Fe-Cr-C production is a very high electrical energy consuming process. Decrease up to 10% of this electrical energy is expected when self-reducing agglomerates are used. This research aims to understand how the synergetic effects are when stronger reductant, like Fe-Si, is substituted for coke in self reducing pellets. Brazilian chromites containing 41.2%Cr2O3 were mixed with petroleum coke and agglomerated with cement as the binder. Small amounts of 1%, 2% and 4% of Fe-75%Si were substituted for the equivalent petroleum coke, and pure silica plus hydrated lime were added for adjusting the slag composition. The mixture was pelletized, dried and submitted at 1773K up to complete the reactions. The results showed that the reduction reactions were 1.4 and 2 times faster with 1% and 2%Fe-Si addition, respectively, than with no addition. The microscopic analysis showed that it was formed a liquid phase, but the pellet did not collapse what indicates that the coalescence of the metallic phase depends on the dissolution of the pre-reduced particles of the chromites into slag.

Jan 1, 2008

By T. V. Jayaraman, Kranti Kumar, Paul Praveen J., Dibakar Das, A. R. James

"Lead free piezoelectric ceramics with high piezoelectric coefficients are in great demand for sensor and actuator applications. Synthesis and characterization study of one such lead free system, barium zirconate titanate - barium calcium titanate [xBZT-(1-x)BCT] (x = 0.5), via solgel method have been carried out. X-ray diffraction (XRD) and transmission electron microscopy (TEM) confirmed the formation of single phase BZT-BCT nanoparticles (<50 nm). The as-synthesized powders were calcined at 1000°C and the powders were pressed into cylindrical pellets. Solid-state sintering of the green pellets at 1550°C for 2 hrs resulted in single phase perovskite structure. Hysteresis loops were obtained which indicates the ferroelectric nature ofBZT-BCT. The bulk ceramic samples with the highest sintered density (~93%) were subjected to electrical poling and the piezoelectric properties ( d33, kp, & i:,) were measured. The structure and piezoelectric properties were investigated and correlated for the given composition of the BZT-BCT system.IntroductionPiezoelectric ceramics are widely used in various sensors and actuators and most of the piezoelectric ceramics, which are presently used, are lead based, which contains at least 60% lead (Pb) by weight. The critical disadvantage of these lead based piezoelectric ceramics is their hazardous effect related to the toxicity of lead, which poses a serious environmental concern starting from their processing to the disposal stage[l]. It is well known that a material to be a good piezoelectric it requires a morphotropic phase boundary (MPB) i.e. the composition induced phase transition between any two ferroelectric phases."

Jan 1, 2013

By Dai Yongnian

"The feasibility to vacuum distillation of a crude metal or an alloy was discussed. The equilibrium relationship between vapor phase and liquid phase in A-B system - - - - - PA/PB =BAa*/b has been derived. The separation coefficient, BA = rAPA/(rBPB) is a judgment criterion. By calculation PA/PB, the equilibrium composition diagram of vapor phase and liquid phase was drawn. By use of the equation derived by M. Olette, the relationship among the volatilization amounts of various impurities in a crude metal (yi) was further solved. 1-(X/100)= C =(1-Y1/100)1/02i . From yi value obtained in practice, 2i, Pi and then can be calcu-lated. The correct volatilization order of various impurities was obtained. These results can be applied to determine the practical conditions (temperture, vacuum degree, type of distilla¬tion furnace, times of distillation and control of product composition) in distillation of a crude metal or an alloy.INTRODUCTIONRefining and separation of various impurities from nonferrous crude metals by vacuum distillation have many the advantages of high metal recovery, impurities recovered in metallic state, flowsheet simplified, good enviromental protection, low operation costs and in complex equipment. So in recent years this method has been adopted widely.Vacuum distillation has also been studied and used in separation of various elements from non-ferrous alloys and the area of its application is being extended rapidly.At this situation, some problems have been put up: What kind of impurities can be removed from crude metals? What kind of alloys can be separated by vacuum distillation? In present paper, attemps have been made to answer these problems and combine with practical results to analyse some valuable data obtained from testwork on vacuum distillation of crude tin and Pb-Sn alloy."

Jan 1, 1988