This is a sampling of the papers presented at the conference, the proceedings can be bought from the SAIMM The technique reported here involves measuring the air pressures generated within sealed boreholes located behind blasts. Results from twelve free face blasts in competent rock environments a represented. There were no instances of high pressure gas penetration, even at distances corresponding to less than one blast burden. Rapidly generated underpressures were measured in most holes, with the magnitudes of the peak pressures decreasing with distance behind the blasts. It has been proposed that the under pressures are the result of new volume created due to crack formation and overall rock mass dilation. The experimental evidence is consistent with this, including a correspondence of the onset times of the peak underpressures with the nominal firing times of the nearest blastholes. New post-blast cracks were observed when using borehole video cameras in the monitoring holes. A calculation of new volume produced within the monitoring holes is proposed as an indicator of damage. While the data exhibit considerable scatter, there is a power function dependence on scaled distance, which resembles that of typical vibration data. The data also lie within the normally quoted vibration regimes for rock damage and are consistent with measured extents of damage. It is concluded that this technique may provide an inexpensive and practical comparative measure of near-field rock damage due to blasting. It is further concluded that gas penetration is not a common phenomenon. Damage appears to be mainly attributable to the nearest blastholes and the control of charge mass in perimeter blastholes is emphasized for damage minimization.

Jan 1, 2000

By C. Lemire, A. Biscaro

Ferro-alloys are sold according to the size grading specifications of users. Fines are produced during crushing and the amount produced depends on the crushing process and the physical characteristics of the ferro-alloy. The market value of fines has declined. Market demand is very weak and in some extreme cases is nonexistent. An induction furnace melt process has been developed to solve this problem. The process feasibility has been demonstrated on a small scale with charges of approximately 2.5 kg. The piloting was carried out using a 100 kW furnace with a metal liquid capacity of 140 kg. The operating parameters were determined during the pilot process. The procedures were defined and the equipment required for melting fines produced at the client's site was sized. With the production of ingots, the client can now recover the full value of ferro-alloy fines.

Jan 1, 2004

Application of Gy?s formula is appropriate for calculation of the Fundamental Error (FE) prior to samples being collected at any stage of the minerals process, provided that sampling parameters K and a (alpha) have been determined by calibration of the ores. Two types of calibration procedure are well established in the industry, the Hetrogeneity test and the 32-piece sampling tree experiment. The sampling tree experiment uses the variance and average grade of metal analyses from four series of samples at different nominal fragment size, as the basic input data. Pierre Gy suggested the cube as an appropriate exponent of the nominal fragment size for use in his equation. More recent work suggests that this exponent is variable and characteristic of specific ores and therefore requires calibration. The method described here explains the experimental procedure of the calibration. It is then possible to calculate a sampling nomogram using the sampling parameters K and a. This allows the sampler to determine a suitable protocol for the sampling event that will ensure that the FE does not exceed a predetermined precision at any point in the sampling procedure.

Jan 1, 2007

By J. N. Van der Merwe

The principal goal of the research described in the paper was to determine, by measurement of pillar scaling on pillars that have not failed, whether the pillar life prediction method developed by van der Merwe (2003) was valid as it stood or whether adjustments were necessary to the rates indirectly derived from observation of failed pillars. To this end, measurements were taken on over 350 pillars at 13sites on 6 mines. The project was done as a collaborative effort between the University of Pretoria, the Nancy School of Mines and CSIR Miningtek. During the course of the investigation, it was found that the majority of pillars display maximum scaling at mid height, that there was no clear preferential direction of pillar scaling, and that pillar corners do not scale significantly more than the mid pillar areas. The most important conclusion was that the scaling rates found by measurement agreed with the inferred rates found in the previous work. The previously developed procedure for the prediction of pillar life spans consequently requires no adjustment, although the error span is in the region of 20%. It is recommended to do further research into the effect of sealing of panels and, possible chemical changes taking place in the pillars as they age on the scaling rate.

Jan 1, 2004

By R. D. Hull

Paper written on project work carried out in partial fulfilment of B.Sc. (Eng.) (Mining) degree As a partial fulfilment for the degree of B.Sc. (Eng) (mining) at the University of the Witwatersrand, a dissertation was to be completed in the mining industry. This was done at Finsch mine, with the purpose of determining the best solution to the required secondary breaking problem. In order to complete the study of the secondary blasting method available for use in the new block 4, cave mining method at Finsch mine the following problem statement was identified and solved ?The methods currently in use, for the secondary breaking of oversize rocks at their source in the current production levels, are to be investigated, and their applicability to the new block 4mining project determined?. To effectively achieve this problem statement above; time was spent researching and investigating, in depth, the methods that are currently in use at both Finsch and Koffiefontein mines; so as to gain practical knowledge of these. The methods were identified and independently evaluated, taking into consideration factors such as costs of the equipment, time to break oversize rocks, advantages, disadvantages, safety and labour requirements, etc. This in turn then allowed for a direct comparison between the methods and the decision as to the best to apply to the new block 4 production level. The methods that were investigated included: ?Concussion blasting, where concussion bombs and lay-on charges are used to break hang-ups and boulders. ?Drill and blast methods, where holes are drilled in large rocks and charged manually with explosives. ?Emulsion secondary blasting, which is a new project in use at Koffiefontein mine from African Explosives Limited. ?The Ro-BustTM breaking system, a hydro-fracturing breaking system. Once all the methods had been evaluated and compared it was found that the Ro-BustTM Breaking system was the most applicable for the breaking of boulders, with, the Emulsion Blasting System being used for hang-ups. Further information and the more in-depth version of this report, is stored in the resource centre at De Beers?Finsch Mineand the School of Mining Engineering WITS University.`

Jan 1, 2002

By F. Bonnet, J. Lehmann, H. Gaye

A review of thermodynamic information and models of slags, including associated software when available, is presented. The pertinence and accuracy of these models is discussed by comparison of their predictions for various slag thermodynamic properties with the available experimental data. Practical industrial applications will be illustrated by a literature review of the dephosphorization process of ferromanganese alloys and by the description of Ti behavior during silico-manganese alloys production. This latter example will show how the thermodynamic models have been used to propose a flotation treatment at low temperature to enhance TiC removal.

Jan 1, 2004

By A. Andrews

Paper written on project work carried out in partial fulfilment of MSc (Eng) degree Solid state sintered silicon carbide ceramics are used in aggressive environments as sealings. There exist data concerning corrosion, but there are only few data concerning their electrocorrosion behaviour. Therefore the electrochemical corrosion of solid state sintered silicon carbide (SSiC) ceramics has been studied at room temperature in acidic and alkaline environments by using potentiodynamic polarization measurements. The investigation showed a pronounced electrochemical corrosion in bases and acids. In HCl andHNO3pseudo-passivity features due to the formation of a thin layer of SiO2on the surface were observed, whereas in NaOH soluble silicate ions were observed, resulting in more pronounced corrosion. The microstructural observations of initial and corroded samples reveal that the residual carbon found in the microstructure do not dissolve preferentially. Keywords: Corrosion; SEM; SSiC; polarization test.

Jan 1, 2006

By A. S. Macfarlane

The introduction of new technology into mining operations is seen as a strategic necessity by many mining companies, in order to improve safety and to improve operational effectiveness. Many attempts have been made in recent years to introduce new technologies into mining operations in southern Africa. Amongst these are noteworthy successes, as well as some disappointing failures. Often, the reason for failure does not lie with the technology itself, but with the work system into which the technology is introduced. Such failures may come with a significant opportunity cost, and have a detrimental effect on future development, simply because the system has not been adequately engineered, and the risks have not been adequately assessed and managed. This paper examines the reasons for such failures, and proposes a methodology to be followed to ensure successful and sustainable implementation of new technologies, such as to reduce technical and financial risk to the company, and to energize the workforce into ensuring the initial objectives of the project are met. The paper also focuses on the application of appropriate technology, and the development of technological applications which are commensurate with the level of development of the work environment into which it is introduced. The paper therefore focuses on the application of risk management, change management, systems engineering and feasibility analysis as being key elements of a successful and holistic technology implementation programme.

Jan 1, 2001

By R. C. D. Phillis

Conventional stoping in hard rock mining is largely considered an operational environment. This paper suggests that stoping falls within the realm of a project management environment typified by uncertainty, variation, and large numbers of interdependencies. Stoping was then equated to a micro-project with many simultaneous activities that had to be executed accurately using finite resources within limited shift durations in order to reach specific goals. Critical chain project management (CCPM) principles were applied to the stoping activities, and the results showed that the number of blasts per panel can be significantly increased by successfully moving the distribution of work as close as possible to the start of shift. Critical chain principles also assisted in facilitating re-focusing and teamwork among stoping crews as well as between day- and night-shift crews. The main recorded success was in managing inherent protective capacities/local contingencies/fat/buffers that are found in all projects. The impact on mine health and safety (MHS) was significant as individual operators and crews became convinced that they could perform all stoping tasks (activities) without compromising accuracy or speed.

Jan 1, 2011

By J. D. Steenkamp

In a paper presented at the Heavy Minerals Conference 2001 a laboratory scale investigation on the beneficiation of an ilmenite containing waste stream by magnetizing roasting was reported1.This waste stream contained a high concentration of ilmenite, which was contaminated by chromite and other gangue minerals. Interpretation of the results of the investigation was based on the assumption that during magnetizing roasting of an ilmenite concentrate, under the oxidizing conditions, the magnetic properties of the chromite would remain constant. In this article the following hypothesis was tested: The magnetic susceptibility of chromite would remain constant during magnetizing roasting of an ilmenite concentrate under the oxidizing conditions reported by Gouws and Van Dyk1. The results of this study indicated that the hypothesis is not true. The increase in the magnetic susceptibility is not significant though and it is expected that it will not influence the final ilmenite quality to a large extent. Based on the assumptions that the bulk magnetic susceptibility of the waste stream samples represents that of the ilmenite in the waste stream, and the bulk magnetic susceptibility of UG1 chromite that of the chromite in the waste stream, the results also served to confirm that the waste stream with a high chromite content should be roasted under oxidizing conditions, in a reactor with a well-defined retention time distribution (i.e. a fluidized bed reactor), at a roasting temperature of 750°C (rather than the higher temperature ranges of 800°C and 850°C).

Jan 1, 2003

By T. Tamura

It is known that the CaO-FetO-P2O5slag system has a wide liquid miscibility gap at steelmaking temperatures and this two-liquid slag phase has many advantages such as high activities of both FetO and CaO and high amount of P2O5. The phosphorus distribution ratio between the two-liquid slag and molten steel was confirmed to be higher than that between CaOsat.-FetO-P2O5slag and molten steel. The two-liquid slag may be useful for dephosphorization of molten steel and reduction of slag volume. Furthermore, the phase equilibrium of two-liquid CaO-FetO-P2O5slagsaturated with MgO was measured to determine the applicability of the two-liquid slag to dephosphorization in steelmaking process. Keywords: slag, refractories, solid solution, two-liquid phase, dephosphorization, steelmaking, phase equilibrium.

Jan 1, 2004

By R. T. Jones

Slags have been produced as by-products from pyrometallurgical processes for thousands of years, and have generally been regarded as waste. Many of these slags are no longer seen as residues merely to be discarded, but as potential economic sources of metals, or as useful by-products in their own right. Slag cleaning can enhance the recovery of valuable metals in existing pyrometallurgical processes, or can produce economic value from recycling old slag dumps. For example, a process has been developed and implemented industrially for recovering cobalt from copper smelting slag in a DC arc furnace. The relatively non-leachable behaviour of glassy slags allows them to be used as a very safe means of disposal of metallurgical waste streams, including many that are classified as hazardous. The high temperatures, reducing conditions, and good mixing that can be achieved in a DC arc furnace enable the effective functioning of this environmentally beneficial means of disposal. Lead blast furnace slag can be rendered safe for disposal by treating it using the Enviroplas process, which strips most of the hazardous lead from the slag (and traps the rest in an insoluble glassy slag) and recovers economic quantities of zinc by absorbing (in a lead splash condenser)the zinc vapour that is fumed off in the furnace. Another example can be seen in the recovery of a chromium- and nickel-containing alloy from stainless steel plant dust, while producing a disposable residual slag. The examples presented here illustrate that it is possible to develop processes that are both economic and environmentally beneficial. Keywords: DC arc furnace, plasma, slag cleaning, cobalt recovery, zinc fuming, Enviroplas, jigging, re-melting fines, environmental, economic

Jan 1, 2004

By K. M. Li, Y. D. Zhang

The selection of stripping dragline is a complicated problem. Several factors, such as the deposit buried conditions, the demand of mine production rate, cast blasting result, the mining/stripping operation method and parameters, etc. may comprehensively influence the optimal selection of technical specifications of the dragline. Under these circumstances, the basic thinking and procedures for dragline selection are put forward as follows. •Step 1—Initially estimate the dragline annual stripping rate and stripping bench height according to the annual coal production rate and advancing speed of mining front. Then the feasible alternatives of dragline sizes can be calculated and selected from the existing dragline series. •Step 2—A computer simulation model is developed to simulate the dragline stripping operation, to obtain a series of working face parameters, then to select the best dragline alternative. This step can be interactively iterated until the satisfactory results are obtained. •Step 3— Sensitivity analysis can be done with the systems simulation model by changing the stripping bench parameters, e.g. stripping bench height and cut width, etc. to verify and modify the selection results if necessary. The mathematical model for dragline stripping simulation has been set up. The flowchart of the model is shown. A case study for a large surface coal mine with annual production rate of 16 Mt/a is followed. The dragline bucket capacity and operation radius, stripping bench height and cut width as well as other parameters are comprehensively optimized and selected. Keywords: Open cast, dragline, specification, selection, cast blasting

Jan 1, 2003

The gold concentration profiles which develop inside the activated carbon particles during the adsorption process were measured, so as to obtain additional direct proof of intra-particle mass transfer rate-control and to determine how individual carbon particles in a population vary in their gold uptake behaviour. The observed gold concentration profiles inside the activated carbon particles were typical of situations where an intra-particle mass transfer mechanism is rate-controlling. Gold di-cyanide penetrated the carbon particles with a wave-like front until it was uniformly distributed throughout the particle. This corresponds with the profiles predicted by the film and surface diffusion model. However, the rate with which gold di-cyanide was transported inside the individual carbon particles varied within the population of carbon particles. This variation was characterized by a lognormal distribution in surface diffusivity. Because the estimated variances of these surface diffusivity distributions were small, the dynamic adsorption behaviour of the carbons used in the present study did not deviate significantly from that predicted by a model based on film mass transfer and a single surface diffusivity. Van Deventer (1984, 1985 and 1986a) reported data that could not be adequately described by a model based on film mass transfer and a single surface diffusivity. In this study a model based on film mass transfer and a wide lognormal distribution of surface diffusivity values was applied to his data. It was shown that a population of carbon particles with a wide distribution in surface diffusivity values could offer an alternative explanation to the mechanism proposed by Van Deventer which was based on film mass transfer, with partitioning of the carbon into micro- and macropores with surface diffusion in the macropores and slow mass transfer into the micropores.

Jan 1, 1997

By S. O. Bada

Fine phosphate feed is considered to be slime and normally disposed of as a discard in settling ponds or dumped as landfill. The purpose of this research was to establish whether commercially acceptable qualities and yields could be obtained from this material using dry separation methods. The results obtained from the electrostatic separation of <105 µm phosphate ore are presented. An existing separator was upgraded in order to improve on product and flotation concentrate recovery, to test different mineral, and to reduce particle residence time between the charging chamber and the separating zone of the separator. The operating conditions were varied according to the charges imparted to the particles in the electric field, and according to other device parameters. Parameters such as splitter position, charge reversal, rotation speed, charging voltage and separating voltage. The <105 µm phosphate feed was concentrated under both triboelectrification and inductive charging. The use of inductive charging and charge reversal resulted in a significant increase in grade for <105 µm phosphate feed, with the P205 grade increasing from about 12 per cent to 20.50 per cent, and a recovery of 26.30 per cent under a single stage of separation. It was found that better separation was achieved at rotation speed of 6000 r/min, -8 kV charging voltage, and 25 kV separating voltage.

Jan 1, 2012

By L. Rademan

The kinetic leaching behaviour of a low-grade surface gold ore and a high-grade reef ore were evaluated to determine the achievable gold recovery from these ores and particularly mixtures of these ores. The reef ore material has a head grade of 13.40 g/t with a relative standard deviation of 3%, and the unprocessed surface ore material a head grade of 0.43 g/t with a relative standard deviation of 15.6%. It is concluded that the kinetic leaching behaviour of these free milling gold ores during cyanidation, is not influenced by mixing of reef and surface ore material. No statistically significant relationship exists between the achievable recovery by direct cyanidation and the head grade of the material fed. No ideal ratio of surface ore to reef ore could be established. It is recommended that these materials should be processed simultaneously to minimize the costs, security risks, and losses incurred in transportation.

Jan 1, 2012

By W. Barthel, B. A. Dippenaar, J. Malan

In its most basic form, the process of sintering is very simple, and has been in use since the turn of the previous century. However, while the basic process is simple, control of the process relies on a number of extremely complex interdependent process parameters and requires a thorough understanding of the effect of these parameters on production capacity and product quality. Further, as with many other processes, the process parameters and hence design details of visually similar installations are highly dependant on the specific feed materials. While the industry trend has been towards an increase of capacity in order to lower unit production cost, typically in Iron ore sintering plants, this approach is not always possible for other commodities because of the scale of operation. This paper seeks firstly to describe some design considerations of sinter plants; secondly, to report on results from testwork performed with a specific series Manganese ore blends; and last, to relate these results to the design of new small-scale Manganese ore sinter plants.

Jan 1, 2004

By S. S. Makgato

In this study, coke oven tar additions over a range of 0?8 wt.% were evaluated as a possible substitute for imported coal fractions. The coke oven tar used was collected from tar decanters in the byproducts section of the coking plant. The moisture content in the tar varied depending on the residence time and water carryover from the coke oven tar separators to the storage tanks. Moisture contents of 1 wt.%, 3 wt.%, and 6 wt.% were investigated in order to evaluate the effect on coal blend, carbonization, and coke properties. At 6 wt.% moisture content with 6 wt.% coke oven tar, although the coke quality improved the yield showed a 4% decrease. On the other hand, 1 wt.% moisture content with coke oven tar of 6 wt.%, increased the yield by 1% and the coke quality improved. However, the latter process was characterized by an excessive increase in wall pressure and pushing energy, both of which are detrimental to the oven walls. The optimum moisture content in coke oven tar was found to be 3 wt.% with a coke oven tar addition of 6 wt.% in the coal blend. With these conditions, the coke properties improved and wall pressure and pushing energy were acceptable. However, a decrease in coke yield of up to 2% was observed. Despite this, coke oven tar addition is considered to be a viable option based upon economic factors of a reduction in the quantity and cost of imported coking coals that is required to achieve the same optimum final coke product. Keywords coal substitution, coke oven tar, tar moisture, coal blend, coke, coke quality.

Nov 1, 2013

By D. N. Ferguson

The separation of certain minerals by electrostatic techniques can be difficult due to their similar electrical conductivity, and any technique to improve this can be useful in certain difficult separation applications. Triboelectric differences between mineral scan result in certain minerals acquiring small positive or negative charges prior to inductive electrostatic separation. By changing the polarity of inductive separation, relative changes in mineral recovery can be observed, which may be beneficial. In this brief study a JKTech mineral liberation analyser (MLA) was used to evaluate the effect of polarity change on selected minerals present in the Richards Bay Minerals deposit, and an approximate triboelectric series based on this behaviour is presented.

Jan 1, 2010

By M. Sibanda

The diffusion of carbon in Co-5% Fe alloy was studied in a belt-type pressure system at temperatures of up to 1330°C and press loads or nominal pressures of 7 020 tons or 42±3 kbar. Under these conditions, this alloy is in the solid state. Discs of graphite and prealloyed Co-5%Fe were used to make up the diffusion couple. The diffusion coefficient increased with increasing press load due to the tendency of the low density graphite to dissolve in the metallic phase reducing the overall volume and increasing the density of the system. Furthermore, inhomogeneous plastic deformation may have promoted diffusion by creating defects in the alloy. Diffusion couples treated at atmospheric pressure exhibited graphite particles in the metal, while those treated at high pressures exhibited carbide in the form of Widmanstatten laths. Carbon analyses indicated increased carbon solubility with increasing pressure. This was confirmed from calculated high-pressure phase diagrams.

Jan 1, 2005