By P. R. Sperry, P. A. Beck, J. Towers

Dahl and Pawlek1 found that electrolytic copper develops extremely coarse grains at 1000°C after about 90 pct reduction by rolling. This coarsening occurs only under conditions of penultimate grain size, deformation, and alloying which lead to the "cube" recrystallization texture.l,2,3,5 The peculiar angular shapes and straight grain boundaries of the coarse grains were noted by several investigator.1,4,5 On the other hand, coarsening in Fe-containing aluminum or in AI-Mn alloys8 does not depend on a "cube" (or any well developed) recrystallization texture. It is true that increasing deformation by rolling, and, therefore, an increasingly well developed re-crystallization texture, are associated with decreasing incubation periods of coarsening.6-7-8 Nevertheless, coarsening readily develops in aluminum even after only 30 pct reduction by rolling, where the recrystallization texture is very weak.6,8 Also, coarsening was observed by Jeffries9 many years ago in sintered thoriated tungsten, which presumably has no preferred orientation. In all these cases coarsening is associated with grain growth inhibition by a dispersed second phase.8,9 The annealing temperature has to be suficiently high to overcome the inhibition at a few locations. But if it is too high, growth starts at many points, and the resulting grain size becomes much smaller.9 Normally, the coarse grains are more or less equiaxed, and the boundaries have a typical ragged appearance.6.8 Cook and Macquarie4 demonstrated that, in addition to the texture-dependent coarsening previously found at 1000°C,l electrolytic tough pitch copper may also coarsen at 800°C after 50 pct reduction by cross rolling. The coarse grains formed under such conditions have rounded shapes and ragged boundaries, like those in aluminum. When the annealing temperature is higher, the tendency for their formation decreases. All these observations suggest that the coarsening at 800°C is associated with inhibition by a second phase. Actually, coarsening at 800°C after 50 pct reduction by cross rolling was observed only in tough pitch copper,4 which contains Cu2O particles. On the other hand, the texture-dependent 1000°C coarsening occurs in both tough pitch and oxygen-free copper;4 it does not appear to depend on the presence of a dispersed second phase. However, the interpretation of the 800°C coarsening in Cu after 50 pct rolling as an inhibition-dependent process, similar to the coarsening in A1-Mn alloys, is somewhat weakened by the fact that this coarsening was reported4 to occur only after cross rolling, and not after straight rolling. It was, therefore, decided to re-examine this question. A 1 in. diam electrolytic tough pitch copper rod, No. 2 hard drawn, was annealed for 20 min at 700°C, rolled to 0.5 in., annealed 10 min at 700°C, and straight rolled to 0.064 in. It was then given a penultimate anneal of 20 min at 500°C and it was cut into four sections, which were given final reductions by straight rolling as follows: A 30 pct reduction of area B 50 pct reduction of area C 70 pct reduction of area D 90 pct reduction of area Specimens cut from the four sections were finally annealed at 800°C in an oxidizing atmosphere. Strip A remained fine grained up to 10 hr, but the specimen annealed 12 hr consisted of only 2 large grains. Strip B had a few scattered large (1/2 to 3/4 mm) grains after 1 min, although the balance of the specimen consisted of fine grains of about 0.02 mm. After 5 min there were several 10 to 15 mm grains present, and after 1 hr strip B was completely coarsened. The coarse grains had the same characteristics (see Fig 1) as those obtained by Cook and Macquarie at 800°C after cross rolling. Strip C had several grains of 0.05 to 1 mm after 1 min, but it was still largely fine grained after 12 hr. After 48 hr it consisted entirely of grains of about 0.5 to 4 mm, with an extraordinarily large number of twin bands. Strip D remained com- pletely fine grained after 4 hr at 800°C. These results indicate that, in the deformation range of 30 to 70 pct reduction, the incubation period for coarsening as well as the rate of growth and the final size of the coarse grains decreases with increasing deformation. Similar

Jan 1, 1950

By C. Norman Cochran, James L. Brandt

ALTHOUGH gas in aluminum and its effect on aluminum products have been the subject of a number of papers, not many quantitative determinations of the hydrogen content of solid aluminum and its alloys have been recorded in the literature. For solid aluminum samples, four investigators have reported hydrogen contents which appear reasonable compared with the hydrogen solubility of 0.7 ml per 100 g, STP, in molten aluminum at 660°C established by Ransley and Neufeld' and verified by Opie and Grant' and Ransley and Talbot. Sloman," who used a vacuum fusion procedure, reported the hydrogen content of some high purity aluminum as 0.66 ml per 100 g, STP. Griffith and Mallett, employing the tin fusion method, reported the internal hydrogen content of six different aluminum alloys as ranging from less than 0.1 ml per 100 g, STP, for 1100 alloy to 0.7 ml per 100 g, STP, for 4043 alloy (previously 43S, a 5 pct Si alloy). Eborall and Ransley," using a solid extraction of the gases at 600°C, reported hydrogen contents ranging from 0.1 ml per 100 g, STP, to 1 ml per 100 g, STP. Ransley and Talbot reported that several thousand analyses on 99.2 pct and higher purity aluminum as well as Duralumin type alloys indicated hydrogen contents ranging from 0.1 ml per 100 g, STP, to 0.5 ml per 100 g, STP.

Jan 1, 1957

By William B. Phillips

The concentration of natural magnetites has been carried on in this country for several years, and more or less information has been collected on the subject. Various inventors, availing themselves of the magnetism which is inherent in such ores, have devised machines for separating the impurities from the ore by means of the electric current; and a greater or less degree of success has rewarded their painstaking and persevering efforts. We are now fairly in position to judge of the value of the process as applied to such material. It is not my purpose to speak of this matter further than may be required by the emergencies of the case. I shall assume that most engineers and metallurgical chemists are already acquainted with what has been done at the Chateaugay mines, at Mineville, at the Benson mines, at the Weldon and Ogdensburgh mines, and at Cranberry; although, at this latter place, there has not been so much done as we could wish. I shall not now speak of the various types of separators. From the time of William Fullarton, to whom was granted an English patent, in 1792, for separating iron-ore by the application of magnetic attraction, down to the present time, a great. many devices have been suggested, and a great many patents taken out for this purpose; but it is not necessary now to enter upon a discussion of their merits. Perhaps, at some future meeting of the Institute, after we shall have experimented further with some of the machines on the market, there may be an opportunity to contribute something to the current knowledge of the efficiency and economy of separating-machines. In this paper I propose to give, as briefly as possible, the results already reached in converting a non-magnetic ore into magnetic ore, and then concentrating it over a magnetic separator of the alternate-polarity type. I am aware of the work

Jan 1, 1896

By Hsun Hu, R. S. Cline

A detailed studj) of texture formation in 2 pet Al-Fe single crystals with initial orientations of approximately (111) [112], (112) [111], and (112) [111] was made by examining the textures developed on the surface and at various interior sections of the crystal after rolling to various amounts. Depending' upon the initial orientation of the crystal, the surface and interior textures may differ only in sharpness, or may differ essentially in orientation. The orientation of the (111) [112] crystal does not change upon rolling up to 70 pet, but after rolling more than 90 pet a distinct component of (001) (110] orientation is developed. The texture formed in the two (112) (1111 type crystals consists of (111) (1121 and (001) (1101 components. The latter, however, is largely confined to the surface layers. The textures formed on both sides of the crystal are identical, and the texture composition profile is approximately symmetrical with respect to the central section of the strip thickness. The formation of these texture components is analyzed. DURING the past seven or eight years, deformation and recrystallization textures in rolled Si-Fe single crystals have been extensively studied by various investigators.1-7 From these studies, much knowledge on texture formation in bee crystals of various initial orientations was obtained. However, these results also raised many questions, regarding particularly the correlation between deformation and recrystallization textures, as well as the deformation texture itself of some particular crystals. To take a (111) [112] type crystal as an example, it was shown by Dunn and Koh2, 3 that this orientation does not change during deformation by rolling. This finding is consistent with the conclusion reached by Barrett and Leven-son8 with respect to iron crystals that (111) [112] is one of the stable end orientations. However, different recrystallization textures were observed by Dunn and Koh3 in (111) [112] type crystals of different initial thickness, which widened differently during rolling even though their deformation textures were identical. Another interesting example, also from the results of Dunn and Koh2'3 is that of texture formation in a (112) [111] crystal. This crystal developed a two-component deformation texture of (111) [112] plus (001) [110]. Its recrystallization texture, however, was found to be predominantly (110) [001], which is related to the (111) [112] component by a simple [110] rotation. This crystal, therefore, behaved as if the other deformation texture component, (001) [110], were not present. There are also discrepancies among the results of different investigators, as well as numerous unexplained fine features of the deformation texture of crystals of various initial orientations. In order to have a better understanding of all of these points, a detailed study of deformation textures is greatly needed. One of the obvious things that has been completely overlooked in previous texture studies is the possible effect of surface texture. All past work on the texture of Si-Fe single crystals was conducted in a rather simple manner, i.e., the rolled crystals were etched to a very thin sheet; then their textures were examined by transmission X-ray techniques. For recrystallization texture studies, unless precautions are taken by etching off a sufficient amount of the surface layer before annealing, the texture developed in the interior may be affected by the surface layer, which may well have a different initial texture and which may have undergone recrystallization earlier than the interior of the specimen. Because of this effect, it is now planned to reexamine the texture of various rolled and annealed single crystals at the surface, and at various sections below the surface by using reflection techniques. In some cases, both surfaces of the rolled crystal will be examined. In one of Dunn's early papers,9 he noted that at an early stage of rolling the crystal seems to divide roughly through the middle to become a sample which in effect consists of two layers having some what different orientations. This effect has never been further explored. The investigation described in the present paper constitutes the beginning of a series of thorough investigations of texture formation in deformed bee single crystals designed to clear up some of the uncertainties which have been discussed. We have chosen a high-purity 2 pet Al-Fe alloy for this investigation. It is known that the allotropic transformation of iron is eliminated by alloying with approximately 1petAl. Such an alloy, being very similar to silicon ferrite, can be heated to the solidus temperature without phase transformation. One reason for choosing A1-Fe instead of Si-Fe for the present investigation is that we have been able to make single crystals of a vacuum-melted high-purity A1-Fe alloy by the strain-anneal method without much difficulty, but were not successful in doing so with a vacuum-melted high-purity Si-Fe alloy. For many research purposes,

Jan 1, 1962

By M. B. Ramachandra Rao

THIS paper records the results of the earth resistivity surveys made in the Godavari river in connection with the Ramapadasagar project. After describing the topographical and geological features of the area, the results of the investigation at the several sites have been mentioned. Further, a detailed account has been given of the resistivity methods adopted, the apparatus used and the interpretation of the curves. The resistivity measurements carried out over the water course have been specially outlined, and a review of the verification of the electrical indications by drilling in a number of cases, has also been presented.

Jan 1, 1947

By J. P. Morris

PREVIOUS investigations1,2 have shown that alloying elements in liquid iron influence the thermodynamic activity of sulphur and thereby affect the partition of sulphur between metal and slag in the desulphurization process. For example, the greater efficiency of desulphurization in the blast furnace as compared to the open hearth can be attributed in part to a higher level of sulphur activity in blast-furnace metal due to the higher concentration of carbon and silicon. In the present investigation, a short study was made of the influence of manganese on the activity of sulphur in liquid iron and iron-carbon alloys. In contrast to carbon and silicon, manganese was found to decrease the activity coefficient of sulphur; and in iron-carbon alloys it counteracts to some extent the influence of carbon. However, at manganese concentrations normally present in the blast furnace or open hearth, the effect of manganese is small. Since manganese sulphide has a limited solubility in iron, manganese can act, under certain conditions as a desulphurizing agent. Considerable data on the manganese-sulphur product in carbon-saturated melts were obtained in the investigation and have been included in this report. The experimental procedure was the same as that used in the earlier investigations on the effect of silicon' and carbon' on sulphur activity. Briefly, the method was as follows: The molten alloy, contained in a graphite or sintered alumina crucible, was brought to equilibrium at a constant temperature with a mixture of hydrogen and hydrogen sulphide of constant composition by bubbling the gas through the metal. Samples of' the melt were taken for analysis at regular intervals by suction through a 2 to 3 mm bore silica tube dipped into the metal. The experiments were run in a graphite spiral resistance furnace with melts weighing 50 to 60 g. The gas bubbling tubes were made of sintered alumina and were 5/16 in. OD, 1/16 in. ID, and 24 in. long. Equilibrium was assumed to have been attained when the sulphur content of the liquid metal reached a constant value. During an experiment there was a rapid loss of manganese from the melt by volatilization. To offset this loss, small additions of manganese were made periodically. The rate of manganese addition needed to maintain a constant manganese concentration was determined in preliminary tests. In all of the experiments, deposits of manganese sulphide formed above the melts in a cooler region of the furnace. Apparently, these deposits resulted from a reaction between manganese vapor and hydrogen sulphide in the gas. To prove that manganese sulphide did not volatilize from the melts to a measurable extent, an experiment was run in which helium was bubbled through liquid iron containing both manganese and sulphur. Although manganese volatilized rapidly in this test, there was no appreciable loss of sulphur. Volatilization of manganese sulphide from a melt would have led to an apparent equilibrium condition in which the sulphur content of the metal was lower than the true equilibrium value. The experimental results are shown in the first seven columns of Table I. The data in the last two columns were obtained from the previous work on the effect of carbon' and show what the results would have been in the absence of manganese but with temperature, gas composition, and carbon content of the metal remaining the same. Comparison of the last four columns show that, in the presence of manganese, the sulphur content of the metal increased at equilibrium and the activity coefficient of sulphur decreased. However, the results show that, for manganese concentrations below 3 pct, the effect of manganese is small. The values for activity coefficient of sulphur given in Table I were calculated from the following relations: S (in liquid metal) + H2 (gas) = H2S (gas) [l] K ph2s/?s X %S X phg = 0.00251 [2] where K is the equilibrium constant for the reaction, PH2S and ph2 are the partial pressures of hydrogen sulphide and hydrogen, respectively, and ?s is the activity coefficient of sulphur. The standard state for sulphur was taken to be a 1 pct solution of sulphur in pure iron. The numerical value for K at 1600°C was determined in the earlier work. For the purpose of showing graphically the results of the tests run at 1600°C, the activity coefficients of sulphur were recalculated so as to correspond to a manganese concentration in the metal of 2 pct in each case. In the calculation it was assumed that the increase in sulphur content of the metal at equilibrium caused by the presence of manganese

Jan 1, 1953

By Larry Kaufman, Joan B. Berkowitz-Mattuck, Edward V. Claugherty

The oxidation characteristics of hafnium and zirconiunr diboride were measured between 1200 and 2200'K by a thermal- conductivity method which continuously ttzeasures the rate of reaction of oxygen with the diboride and by a metallographic air oridation method zuhich provides a measure of the total arr7ount of bovide conuerted to oxide for a given time interval. The oxidized specimens obtained from the tl~eritaal-coi~ductitrity method were also examined by quantitatire metal-lographic procedares. The significant results obtained in this investigation reveal that metal-rich compositions of lzafi~iutil diboride proride the most oxidation-resistatzt material up to 2000°K; hafnium diboride is tmre oxidation- resistant titan zirconium diboride at all tempevatures examined; the morphology of the oxide formed on H/B2 and Llie temperature coefficient qi. the oxidation rate constants change at the temperature of ttze monoclinic to tetragonal phase transition] in HfO2; the oxidation of neither HfB2 nor ZrB2, results iN catastrophic Jazlure at lorc. oxygen pressures; and pvefevetztial gvaLti boundary oxidation was not obsevued for either HfBi or ZYB, A comprehensive study of the high-temperature characteristics of refractory transition-metal di-borides is currently in progress. This program has included investigation of the physical, thermal, and thermodynamic properties of TiB2, ZrB2, HfB2, NbB2, and TaB2. In addition, aspects of the synthesis and fabrication of such materials have been studied. In view of the diverse nature of this research, a number of other laboratories have actively participated and contributed specific capabilities for analysis and characterization of these materials. As a consequence, an extensive description of the relevant properties of these compounds has emerged which is central in evaluating their high-temperature (1200" to 2500°K) performance. To date, information on thermodynamic stability, specific heat, and vaporization characteristics,1 hot hardness and electrical resistivity,1, 3 therma1 expansion:'4 and thermal conductivity 1, 5 has been presented. This information has been generated on materials of the highest purity (98.5 to 99.9 wt pct Me + B) and density currently available. Samples fabricated by zone melting6 and high-pressure hot pressing"3'7 techniques have been used to generate suitable specimens for all of the aforementioned studies. dation characteristics of the most oxidation-resistant of these materials, hafnium and zirconium diboride, is presented and a description of the synthesis and the experimental procedures used to prepare and characterize specimens is given. The high-temperature range under consideration (1200" to 2200°K) and the known dependence of oxidation characteristics on sample chemistry, density, and oxidation conditions required a close coupling of the synthesis, fabrication, and evaluation procedures.8 This was accomplished by continual surveillance of chemical composition of starting materials before and after specimen fabrication and by evaluation of density, phase constitution, and microstructural features prior to and after oxidation exposure. I) PROCUREMENT AND CHARACTERIZATION OF STARTING MATERIALS In view of the current state of the art in fabricating refractory boride materials, the methods used in preparing samples for the present study are given in detail as follows: starting materials were purchased in high-purity powder form and fabricated by high-pressure hot pressing into 0.40 by 1.00 in. bars from which oxidation specimens were obtained. The hafnium diboride used in this study was purchased from Wah Chang Corp.; the zirconium diboride from U.S. Borax and Chemical Co. These powders were routinely characterized by quantitative chemical analyses for metal, boron, carbon, oxygen, nitrogen, and iron, by qualitative emission-spectrographic analysis for trace impurities, by X-ray procedures for extraneous phase identification, and by powder densitometry for comparison with X-ray (theoretical) density. Hafnium and zirconium metal and elemental boron were also purchased as high-purity powders and characterized for impurities by emission-spectrographic analyses. The hafnium diboride was procured in three shipments which were designated as HfBl.g7(1), HfB1.88(2A), and HfB2.12(2). The indicated stoichiometry is based on the atomic ratio of total boron to total hafnium; the number in parentheses identifies the shipment number. Shipment 1 was 5 1b, shipment 2A, 1 1b, and shipment 2, 8 1b. The zirconium diboride was procured as a 20-1b shipment and designated as ZrB1.89(1). A small quantity of purified zirconium diboride was also supplied and designated ZrB1, 9(P). The averaged results for chemical analyses which were generally performed according to the procedures set forth in the compilation by KrieGe9 are presented in Table I. Qualitative spectrographic analyses indicated that Ca, Cr, Ti, Si, Zr (in H~B~), and A1 were present at levels between 0.01 and 0.10 wt pct. Other metallic elements were found to be less than 0.01 wt pct. Since it is virtually impossible to purchase these materials in the desired quantities (5 to 20 lb) as single-phase compounds it is necessary to obtain

Jan 1, 1968

By Thomas J. Crocker, Galen G. Waddell, Eugene H. Skinner

This paper describes a method of measuring initial and long-term deformations which occur in the medium surrounding mine accessways, and discusses the importance of this type of measurement in assessing support-problem areas. Delineated are (1) description of the rock-deformation monitoring equipment, (2) results of two field tests which monitored rock deformation around 4-foot-diameter raise bores, and (3) a numerical-analysis (finite-element) technique to correlate theoretical with experimental results. Instrumentation developed provided the sensitivity and resolution needed to measure rock deformation around a full-scale raise bore during excavation. Results of the tests conducted at the Lucky Friday mine, Mullan, Idaho, show the relationships between (a) de- formation vs. time, and (b) deformation vs. bit progress. Based on theoretical evaluation of the initial deformation, the medium appeared to behave elastically. Using an estimated field stress of 5,500 psi and Poisson's ratio of 0.20, the gross modulus of elasticity of the rock was calculated to range from 3.15 to 6.0 x 106 psi (with one outlier which was determined to be >12 x l06 psi).

Jan 1, 1971

By W. D. Sylwestrowicz

In tests on polycrystalline copper and aluminum, the ratio of the yield stress to modulus of elasticity was found to be strongly dependent on tempemture. Also, it was shown that the change of the yield stress with temperature of a material at a given temperature and deformed to a given yield stress, but not necessarily to the same strain, does not depend on previous mechanical thermal history. Likewise, for a material at a given temperature and deformed to a given yield stress, the rate of work hardening is independent of the temperature of prior stressing. It has been shown by Los and Orowan1 and by Dorn, Goldberg, and Tietz2 that the temperature dependence of the yield stress-strain curves of crystalline materials reflects two effects: not only does the yield stress of a material in a given structural state depend on the temperature, but the structural state (and the corresponding strain hardening) after a given amount of plastic straining also depends on the temperature at which the pre-straining has been carried out. Thus, for instance, if a specimen of a ductile metal has been strained along the stress-strain curve 1 at room temperature to point A, Fig. 1, and then the straining continued in liquid nitrogen along curve NR, the yield stress A' immediately after lowering the temperature is lower than the yield stress A" of a specimen that has been strained by the same amount in liquid nitrogen (along curve 3). AA' represents the effect of the temperature change upon the yield stress of the specimen pre-strained at room temperature; A' A" is the excess strain hardening acquired if the pre-straining has been carried out in liquid nitrogen instead of at room temperature. The dependence of the yield stress (i.e., of the structural state acquired during preceding straining) upon the conditions (speed, temperature) of a pre-straining is the reason for the nonexistence of a so-called "mechanical equation of state" for plastic deformation. A 'mechanical equation of state" is a relationship of the form F(s,E, e, T) = 0, or s = f(E, E, T) [1] It was first suggested by Ludwik3 that plastic deformation might obey such an equation; this, however, was conclusively disproved by experiments of Kochendorfer.4 Additional disproofs were given in

Jan 1, 1959

By Paul Tyler

THE ferroalloying elements are connecting links between the steel industry and the nonferrous metal industries. Although ferroalloys are distinctly nonferrous themselves, they serve the steel industry either in the manufacturing process or in modifying the product-in some cases so that it may compete in the markets with nonferrous metals. Of the 92 elements generally accepted by chemists as constituting the primary building blocks of matter, all but the very rarest have been investigated with a view to employing them in steel manufacture. The surprising thing is that so few have been found commercially acceptable. Despite the relatively small number of elements involved, the employ-ment of alloys in steelmaking is one of the most complicated and probably one of the least well understood of modern industrial enterprises. A great deal has been written regarding the action of individual elements and a profuse and somewhat acrimonious literature covers pretty much the whole field of ferroalloy ore supplies. In the middle ground between the miner and the steelmaker developments are less carefully watched by most observers, and except for an occasional description of the technique of some conversion process or the tariff hearings in Congress, very little is said about them. The purpose of the present paper is to describe in relatively nontechnical terms this highly complex industry and to study its relations to our national progress.

Jan 1, 1933

By G. Howell Clevenger

FORMERLY great divergence of opinion existed in regard to the influence of copper in steel, as affecting its various physical properties. More recently the investigations of Stead,1 Breuil,2 Wigham,3 Burgess and Aston,4 Ball and Wingham,5 Miiller,6 Dillner,7 and others have shown fairly good agreement in the major points. Copper steel has been shown by these investigators to possess special properties which make it valuable for certain uses. The general range of composition of the useful alloys of copper and iron, and of copper, iron, and carbon, has been quite definitely established, for the former by Burgess and Aston,8 and for the latter by Breuil 9 and Stead.10 Stead 11 has removed one difficulty in reconciling certain of the earlier data by calling particular attention to the influence of carbon in copper steels. Another point which caused confusion in the earlier investigations, particularly in regard to " red-shortness," was the presence of sulphur. Failure to note the presence of sulphur often led to attributing " red-shortness " to the presence of small amounts of copper. Turner 12 has called attention to the fact that where copper exists in an iron ore it often occurs as the sulphide, so that the presence of copper in steel made from such ores might also, necessarily, mean the presence of sulphur. It is evident that the effect in this case might be quite different than where pure copper was added.

Jan 10, 1913

By George H. Found

During recent years considerable interest has been focused on the energy-absorption characteristics of metal when it is cyclically stressed in vibration. The most familiar manifestation of this phenomenon, which is called the "damping capacity" or "internal friction" 06 a material, is involved in the dissipation of mechanical energy of vibration, which otherwise would build up to stress levels where the problems of noise and fatigue are involved. In addition to its engineering importance in structures, the damping behavior of metals, particularly at low stress amplitudes, has also been used as a unique metallurgical research tool with which to provide sensitive means for indicating certain structural changes within metals. Important contributions toward understanding the energy-dissipating -mecha-nisms that are responsible for internal friction in metals have been made in the last few years. The information is not yet sufficiently extensive, however, to provide a useful metallurgical concept describing exactly how the structure affects the internal friction, or to encourage more general use of this technique among metallurgists. Three fundamental mechanisms have been proposed, as a result of recent experi- mental investigations, to account for the internal friction in nonferrous metals in low-stress amplitude tests. These include damping due to internal thermal currents that are created and flow in metal because of differential vibratory stress effects,' damping due to localized inelastic stress relaxation at inhomogeneities within the meta1,2,3 and damping related to plastic flow of a localized type for which an explanation has been sought in terms of the dislocation theory.' How each of these mechanisms functions as a result of structural changes in the metal is, in general, not well understood because of insufficient experimental data for which the controlling variables ham been segregated and because of uncertainties in regard to the nature of the structural changes themselves. In several investigations the effects of cold-working on the internal friction of polycrystalline brass and aluminum have been described. As reported by Köster and Rosenthal,5 and by Förster and Breitfield,6 there is an initial large increase in the damping when the metal is worked. The initial high value is not stable, but declines rapidly, at first, in a hyperbolic manner. About Ioo hr. after straining, a stable value is reached of magnitude proportional to the amount of strain.' In Fig. I is shown the relationship found by Zener and his collaborators between the internal friction due to cold-working of alpha brass and the amount of cold-working.8 Several investigators have made internal-friction measurements on worked poly-

Jan 1, 1945

By M. F. Hawkes, R. F. Mehl

The rate of isothermal transformation of austenite to pearlite depends upon the rate of nucleation, N, and the rate of growth, G, of pearlite in austenite. Values of N are given in terms of the number of nuclei forming in unit time per unit grain boundary area of unreacted austenite; values of C are given in terms of the linear rate of radial growth. Variations in the isothermal rate with temperature result from variation of N and G with temperature. Depth of hardening of a steel depends fundamentally upon values of N and G; changes in carbon and alloy content effect changes in N and G and thus affect depth of hardening. Quantitative studies are available on N and G for the formation of pearlite in plain carbon eutectoid steels.3 Systematic studies in this field are necessary if the phenomena are to be well enough known to furnish a proper basis for full rationalization and for theory. Accordingly, the studies are continuing, both with respect to the effect of alloying elements upon the values of N and G in the formation of pearlite and to the values of N and G for the formation of ferrite in hypoeutectoid steels. The present paper is the first relating to the effect of alloying elements upon the values of N and G for pearlite. It offers special interest since cobalt is known to have an anomalous effect upon the rate of formation of pearlite, accelerating it, whereas all other elements retard it.4 It will be shown that cobalt increases both N and G for pearlite and that this effect is inherent in the Fe-Co-C system and not dependent upon factors relating to austenite heterogeneity nor upon any recognizable adventitious factor. Inasmuch as the rate of diffusion of carbon in austenite and the interlamellar spacing of pearlite are variables related to G and possibly to N (in a manner not yet certain), measurements of the effect of cobalt upon them are also reported here. In the course of the work, measurements were made on the effect of cobalt upon the marten-site temperature and these are given. COBALT AS AN ALLOYING ELEMENT IN STEEL Properties of Cobalt Cobalt resembles iron more closely than does any other chemical element. Its atomic number is 27, hence it is the element immediately following iron in the periodic system. The two differ in atomic structure only in the fact that cobalt contains seven electrons instead of six in the third, or transition, level of .the third shell. The next shell, which is the

Jan 1, 1948

By M. F. Hawkes, R. F. Mehl

The rate of isothermal transformation of austenite to pearlite depends upon the rate of nucleation, N, and the rate of growth, G, of pearlite in austenite. Values of N are given in terms of the number of nuclei forming in unit time per unit grain boundary area of unreacted austenite; values of C are given in terms of the linear rate of radial growth. Variations in the isothermal rate with temperature result from variation of N and G with temperature. Depth of hardening of a steel depends fundamentally upon values of N and G; changes in carbon and alloy content effect changes in N and G and thus affect depth of hardening. Quantitative studies are available on N and G for the formation of pearlite in plain carbon eutectoid steels.3 Systematic studies in this field are necessary if the phenomena are to be well enough known to furnish a proper basis for full rationalization and for theory. Accordingly, the studies are continuing, both with respect to the effect of alloying elements upon the values of N and G in the formation of pearlite and to the values of N and G for the formation of ferrite in hypoeutectoid steels. The present paper is the first relating to the effect of alloying elements upon the values of N and G for pearlite. It offers special interest since cobalt is known to have an anomalous effect upon the rate of formation of pearlite, accelerating it, whereas all other elements retard it.4 It will be shown that cobalt increases both N and G for pearlite and that this effect is inherent in the Fe-Co-C system and not dependent upon factors relating to austenite heterogeneity nor upon any recognizable adventitious factor. Inasmuch as the rate of diffusion of carbon in austenite and the interlamellar spacing of pearlite are variables related to G and possibly to N (in a manner not yet certain), measurements of the effect of cobalt upon them are also reported here. In the course of the work, measurements were made on the effect of cobalt upon the marten-site temperature and these are given. COBALT AS AN ALLOYING ELEMENT IN STEEL Properties of Cobalt Cobalt resembles iron more closely than does any other chemical element. Its atomic number is 27, hence it is the element immediately following iron in the periodic system. The two differ in atomic structure only in the fact that cobalt contains seven electrons instead of six in the third, or transition, level of .the third shell. The next shell, which is the

Jan 1, 1948

By T. Gleason

Problems involved in applying wet scrubbers to gas cleaning coal dust from thermal dryers are reviewed. Careful consideration of all the elements going into a modem coal preparation plant is required in view of the increasing difficulty of applying suitable gas cleaning equipment. This problem arises not only from the presence of finer coals to be handled, but also from the pressures applied by both the general population and the plant operators to improve the standard of gas cleaning performance. The Peabody scrubber is presented by the author as a machine designed to help improve this cleaning operation. Wet scrubbing of fine coal from thermal dryers poses a number of problems in adapting the gas cleaning equipment to the fine particulate matter. Among them are: 1) Dust in gases leaving the thermal dryer cyclones is often extremely fine with high percentages of total dust loading less than 1p in size. 2) Flue gas entering the scrubber is corrosive since the coal fired in the thermal dryer furnace is in the range of 0.7% by weight sulfur or higher. Therefore, comparatively high cost stainless steel alloys or corrosion resistant linings are required for a satisfactory service life. 3) Requirements for residual coal loadings leaving the gas scrubber are continually being lowered, while modern coal preparation operation is imposing heavier burdens on the collection system through introduction into the thermal dryer system of very fine coal previously not recovered. The advent of flotation systems in increasing numbers is typical of this trend. 4) Installation of a scrubbing system on thermal dryers is made primarily to reduce air pollution and product recovery value is of little or no value. Therefore, the operating costs of gas pressure drop and water requirements must be held to a minimum. We have, then, the basic situation which calls for comparatively high cost stainless steel alloy wet scrubbers, which must be highly effective in removing coal fines particularly in the 0 to 5-p size range. Further, the standards of scrubber performance are continually being raised towards the level where gas discharged from the scrubbers must be essentially free of any coloration due to residual dust. In view of the highly refractive nature of fine coal dust, residual loadings of 0.01 grains per cu ft or less are required to provide a color free discharge gas. In the present specifications under consideration a residual coal loading of 0.05 grains per cu ft would be considered color free, since the discharge gases are saturated in the range of 150°F. The steam plume acts as a masking agent at the point of discharge, and upon dissipation of the 150° saturated vapor stream, the effluent gas stream could be essentially color free. The specification under consideration calls for residual solids loading of 0.05 or less grains per cu ft, given a coal size distribution shown in the basic data in Table I. It is noted that the dust laden coal stream has a size distribution by weight of 33% in the 2 to 5-p size range and 55% in the 0 to 2-p size range. The particle size distribution given in the specifications does not detail the percent by weight less than 1-p in size, and more important, the size distri-

Jan 1, 1963

Teamwork: The famous first sentence of an essay en- titled Aphorisms, by Hippocrates, is as follows: "Life is short, the Art long, opportunity fleeting, experience treacherous, judgment difficult." The future of science does not depend so much on the number of scientists or the number of colleges, but rather on the individual qualities and the degree of perfection of a limited group of leading scientists and colleges. These are individual factors which require inherent talent which in turn is a condition evolved after generations of culture. Thus, very elaborate higher education for indiscriminate masses of humanity or students may not necessarily show the expected results. In other words, it is possible that higher specialized education should be given only to the few talented individuals, and their capacity and worth should be judged by as highly qualified and talented teachers. Quality is the greatest of all competitive aids. An essential qualification that must be possessed by a quality mineral industries college is a high caliber teaching staff, for the mineral sciences will advance in the coming years only if the leading minds of today are made avail- able as the mental springboards for our scientists of tomorrow. Mineral industries schools are finding it increasingly difficult to maintain a high caliber staff of instructors and administrators in competition with private business and governmental demands for similar

Jan 1, 1950

By Jesse O. Betterton, Y. E. Lebedeff

AS a matter of the most widespread interest to lead-refining metallurgists, the process of desilverizing lead originated by Parkes is the most fundamental step in lead refining. While this basic operation, in addition to effecting a practically complete recovery of gold and silver, is also a great purifying operation and a governor on the purity and uniformity of the final refined lead, it has the important deficiency that no bismuth is removed in the operation. The problem of finding a satisfactory, inexpensive method for removal of bismuth that would fit in with the basic desilverization step has been one of enticing interest for lead-refinery metallurgists for many years. Of late it has become one of imperative interest, and while many attempts and much progress have been made, it is probably fair to say that metallurgical progress thus far is only catching up with commercial requirements. The Pattinson process, an original competitor of the Parkes process for desilverization, has received much attention for its possibilities for bismuth removal. Bismuth concentrations in the Pattinson process fall far short of the silver concentrations and as a result too many operations are required and a crawl in grade in the kettle units is experienced which requires periodic correction. Altogether, it has proved too expensive a remedy, from the cost standpoint of both installation and operation. The Betts electrolytic process is a fully satisfactory remedy but its present status in the field of lead refining is more a matter of bismuth removal than preference as a refining system, except, of course, in instances particularly favorable to the basic requirements of the process. The Betts process, of course, is essentially different from the Parkes process, and very difficult to associate therewith to any economy except in minor ways. Accordingly, where economy dictates the Parkes process, and this is true of far the greater portion of the world's tonnage, the adoption of the Betts process primarily for bismuth removal is apt to prove an expensive remedy on account of its normally higher cost of operation, inelasticity of the equipment for variable tonnages, and high per ton cost of installation.

Jan 1, 1937

By F. L. Wolf

THE catenary system of line construction possesses so many desirable characteristics from the operating standpoint that it has wide application for all types of electric traction. Many steam roads are electrifying sections of their lines, and in most cases are operating both steam and electric locomotives over the same track. This' means that the overhead catenary system is subjected to the severe corrosive action of locomotive smoke, and data concerning the resistance of various alloys to this form of corrosion are very desirable from every point of view. Reliable and specific information and data on the subject of corrosion due to steam and smoke from locomotives are extremely meager and, on this account, extensive service tests, together with accelerated tests, have been made on a number of commercial metals and alloys. The observations and data recorded in this paper are the result of a, preliminary test which was started in 1923 and which has been carried on to the present time. The recognition of the need for even more detailed and accurate data has resulted in the undertaking of another test which has been in progress for about a year. The result of this test will be published in due course. Some years ago The Ohio Brass Co. was asked by one of the large steam railroad companies to furnish data on construction details for a catenary system which it was considering for one of its divisions. The selection of, materials which would give the necessary physical characteristics as well as withstand the severe corrosive action of locomotive gases caused electrical railroad engineers considerable concern. At that time, there were available no specific or authentic data on these important questions: no systematic investigation of the problem appeared to have been made, even though its importance was generally recognized. Such observations as had been made were crude in that they had been limited largely to visual inspection which too frequently is most misleading. However, the scattered information which was collected gave important clues as to how best to start an investigation.

Jan 1, 1930

By D. J. MacKinnon, J. M. Brannen

Smooth, compact, dendrite free 24-h zinc deposits have been electrowon from zinc chloride electrolyte using a diaphragm cell. The cell consisted of sealed anode compartments containing DSA anodes separated from an open cathode compartment by Dynel cloth membranes. Fresh electrolyte was fed to the cathode compartment where zinc deposition onto an aluminum cathode was aided by air sparging. The catholyte passed through the diaphragms into the anode compartments from which chlorine gas and spent anolyte were withdrawn. Standard electrolysis conditions were: 15 g/L Zn, 0.12 M HCI, I5 mg/L tetrabutylammonium chloride (TBACI) as the addition agent, 35°C, and 323 A/m2 (30 ASF) current density. The effect of variations in these conditions on the morpohology orientation, current efficiency, and energy requirement for 24-h zinc deposits was determined. The effect of total chloride ion concentration on the zinc deposit was studied by adding various amounts of NaCl to the electrolyte.

Jan 1, 1983

By S. Leber, R. F. Hehemann

Diffusion coefficients for the Cb-W system were measured using couples prepared from poly crystalline, commercially pure metals. The diffusion coefficients, measured in the temperature range between 1700° and 2300°C, decreased exponentially as the tungsten concentration was increased from 0 to 50 at. pct, then decreased abruptly at higher concentrations. A decrease of two orders of magnitude was observed over the entin? compositional range. The diffusion coefficients were in the range defined by the self-difiusion coefficients of the individual elements, indicating their general validity. An activation energy of 60,500 cal per mole was measured for the 20 pct W composition. Such low values, when compared with energies over 100,000 cal per mole for the pure constituent elements, indicated that transport mechanisnzs more rapid than volume diffusion were contributing substantially to inter dijfusion. Difference should, therefore, be expected between these data and the intrinsic diffusion coefficients. These differences should be significant in the kinetics of 'transport phenomena in practical systems. CONSIDERABLE attention has been devoted in recent years to the mechanical behavior and other properties of the refractory metals and their alloys. The Cb-W system has been of special interest as a base for the development of more complex compositions of commercial interest. In spite of the importance of mass transport to all aspects of elevated-temperature behavior, and especially to the production of alloys by powder-metallurgy techniques, little attention has been paid to diffusion in the Cb-W system. Results from a previous study of this system1 appeared to be anomalously high. The present investigation is, therefore, an attempt to obtain more accurate diffusion coefficients in this system. Intrinsic diffusion coefficients, of primary importance from the theoretical viewpoint, can only be obtained accurately from studies utilizing compositional gradients approaching zero. However, many practical problems involve diffusion under significant concentration gradients. The diffusion coefficients determined in this investigation were, therefore, obtained from couples prepared from elemental metals. The data obtained should be of value in the analysis of problems such as homogenization during powder-metallurgy alloying or reactions between base and clad in coated structures. In this vein, the investigation was conducted on poly crystalline materials of commercial purity. PROCEDURE Diffusion couples were prepared by sandwiching a columbium sheet between two sheets of tungsten. The composite was welded around all edges, the tungsten forming a protective can for the columbium. The composite was soaked for 4 min at 1600°C in a hydrogen-atmosphere furnace, quickly forged to 40 pct reduction in thickness, and then rapidly cooled to room tempera-

Jan 1, 1967