By H. F. Moore

DURING the last six years, there have been many extensive investigations of the fatigue of metals. The major work of 'these investigations has been the determination of constants for fatigue strength of wrought ferrous metals; but during the past year or two there have become available considerable test data on the fatigue strength of certain nonrferrous metals, including copper, brass, bronze, nickel, copper-nickel alloys, aluminum and aluminum alloys, magnesium and magnesium alloys. It is not proposed to give here extensive quantitative tables of test results; for such tables, reference is made to the published data of various laboratories. The following general conclusions, however, seem to be fairly well established: 1. The phenomenon known as "fatigue" of metal really a progressive fracture of metals. A minute (probably submicroscopic) crack is formed in the metal, the internat stress, is intensified at the ends' of the crack, and under successive applications of load the crack spreads like a minute hacksaw cut until there is not enough sound metal left in the cross-section of the piece to stand the load. applied, and then failure occurs suddenly. 2. For wrought ferrous metals, there is .a limiting intensity of stress (as computed by the ordinary formulas of mechanics of materials) below which, a metal is able to withstand an indefinitely large number of repetitions of stress without failure. This limiting stress is known as the "endurance limit or the fatigue limit.? For reversed flexure, the endurance limit for. wrought ferrous metals is usually not far from 50 per cent. of the ultimate tensile strength.

Jan 1, 1925

By R. J. Brison, W. C. Bleimeister

The International Salt Company has long been interested in finding an efficient process for the removal of impurities from rock salt, and particularly from the rock salt produced at the Detroit mine. Methods which have been used previously at the Detroit mine included both hand sorting and differential crushing in a Bradford breaker with rejection of the oversize. Neither of these methods was adequately effective. The development of a new process for removal of impurities from rock salt has been described in the preceding article." Basically, the process consists of exposure of crude rock salt to radiant heating which selectively heats the impure particles. Subsequently the heated particles are removed by adhesion to a heat sensitive-coating on a conveyor belt. This method was found to be effective in improving both the quality and appearance of rock salt by the rejection of the dark, impure particles. The first commercial unit employing the new thermoadhesive method of dry separation of minerals was installed at the Detroit mine of International Salt Company in Detroit, Mich. (Fig. l). This unit was first put into operation in March 1957. The purpose of the Detroit installation was 1) to serve as a pilot plant for evaluating the process on a commercial scale and 2) to produce marketable quantities of rock salt of improved quality and ap- pearance. The design of this plant was based on the results and information obtained from a 1-tph pilot plant at Battelle Memorial Institute. DESCRIPTION OF PLANT Location: The separation plant was installed underground near the crushing and screening plant, for this was the most suitable location from the standpoint of material handling. Furthermore, ample space was availabe at this location. Because the process requires a relatively constant temperature, the uniform year-around temperature of the mine (57°F) gave an added advantage to an underground operation. Feeding: The rock salt is conveyed to a surge bin, from which it is fed to the heating unit by a conveyor. The feed-rate control consists simply of an adjustable gate at the bottom of the surge bin. The plant may be fed either No. 1 grade of rock salt (0.279 to 0.375 in.) or No. 2 grade (0.375 to 0.500 in.) with a maximum input capacity of 500 tons per 15-hour day. Heating Unit: The heating unit (Fig. 2) consists of a panel of infrared lamps suspended inside a low-speed revolving screen. The radiant-heat panel, which is curved for most effective utilization of the heat, holds 240 infrared lamps of standard industrial type, each rated at 500 watts. The position of the panel is adjustable so that it can be placed centrally over and to within 6 in. of the salt bed on the screen. The entire heat panel is suspended by rollers in ¦ R. J. Brison and O. F. Tangel: Development of a Thermo-adhesive Method for Dry Separation of Minerals.

Jan 1, 1961

By AIME

DURING the happy and peaceful years between the Treaty of Versailles and the third New Deal, metallurgy became one of the most cosmopolitan of the sciences. Any metallurgist can name some twenty or thirty scientists whose work, in this country, in England, in Germany, or in France, Sweden, Italy, or Japan was as well known in other parts of the metal-producing and metal using world as it was locally, despite the fact that many of these men never left their native land. One of these metallurgical cosmopolites is Augustus Braun Kinzel, former Chairman of the Iron and Steel Division, A.I.M.E., and now a Director of the Institute. Gus Kinzel, however, is not only a cosmopolite by reputation; he is also a cosmopolite in fact. For many years he commuted at least twice a year between New York and the rest of the world; he is, therefore, not only an expert on the art and science of metallurgy but is equally expert in world travel and can expound with authority on the comparative quality and especially on the cuisine of the great prewar steamship lines; and being a true cosmopolite, he knows, as well as he knows the iron-chromium diagram, the best vintage years in the Gironde, Cote d'Or, and Saone-et-Loire departments in France and along the banks of the Moselle and Rhine in Germany.

Jan 1, 1946

By J. E. Johnson

IT is the purpose of the present paper, while not excluding chemical considerations, to deal more extensively with some of the physical and mechanical aspects of the blast-furnace process, and to point out its dependence in these respects on well-known laws. The quantity and cost of ore and flux required to make a ton of iron being determined by circumstances over which the furnace-man, under given conditions as to quality and quantity of product, has commonly little control; the principal item of cost, apart from the saving of labor, which he can aspire to reduce, is that of fuel. To determine the limits of possibility in this direction is clearly the first step in d practical inquiry; and this step is represented herewith in Fig. 1, a diagram showing the total useful effect obtained from a pound of fuel under various conditions, and thus permitting direct comparison, under any given conditions, between actual results and the maximum possible results. The following statements will explain the basis upon which this diagram has been constructed. One pound of fuel, containing 90 per cent. of fixed carbon (which represents average conditions), is taken as the unit. The degree of oxidation of the carbon is measured by the ratio of the two oxides of carbon contained in the top-gases. It is necessary to remember that a considerable quantity of carbon is brought in as carbon dioxide by the flux, and to take account of it and of its condition. It is here considered that the carbon dioxide liberated by the limestone does not affect the analysis of the toll-gases, and that the ratio of CO to CO., will remain unchanged by the addition of limestone; enough CO, being reduced by the solution

Sep 1, 1905

By E. S. Moore

ALTHOUGH nickel was in use in alloys long before the Christian era, the metal was not discovered until 1751, when Cronstedt recognized it in niccolite from Sweden. The Chinese apparently used a nickel alloy, known as "pahfong" thousands of years ago and Persian coins dating farther back than 200 B.C. consist of a copper-nickel alloy similar to some of those now in use in coins. The pure metal was first prepared about 1775 and the metal was refined for commercial purposes some years later. The nickel industry did not attain much prominence until the ores in New Caledonia were discovered. Exports of ore from that country began in 1875 and since that date there has been an ever-increasing world output of nickel and a great expansion in the uses of the metal except during short periods of commercial and industrial depression. Previous to 1875, for a number of years, Norway was the chief producer, although the metal was mined also in Sweden, Finland, Italy, Germany, Austria, France, China, the United States and other countries. With the dis-covery of nickel deposits in the Sudbury district, Ontario, a new factor was introduced into the nickel industry and Sudbury has since become the overwhelmingly dominant feature in the world's nickel markets. Although nickel was first discovered in Canada as early as 1848 near the north shore of Lake Huron and nickel-copper sulfides were found in 1856 by surveyors working close to the present location of the important mine at Creighton, in the Sudbury field, it was not until 188.3 that any importance was attached to this field. In that year copper sulfide attracted attention where the main line of the Canadian Pacific railroad was being projected across Canada to the Pacific coast. Mining began near this discovery in 1889 but in the meantime operations had begun in 1886 in other parts of the field and by 1890 about 100,000 tons of ore had been raised. In the Sudbury field, as in Norway and at the old Lancaster Gap mine in Pennsylvania, the ore was first mined for its copper content and difficulty in the refining of the copper led to the discovery of the important proportions of nickel in the ore. No. 3 property of the Inter-national Nickel Co., now known as the Frood, the greatest deposit in the

Jan 1, 1932

By HOWARD RICHARDS

THE dollar was, selected as the unit of currency by the Congress of the United States of America on Apr. 2, 1792. This "Dollar" currency is so much more convenient than the older British currency that the Canadian Government, among others, has adopted it with corresponding success. Just as the dollar is the unit of United States currency, so the meter is the international unit for measuring length. The various weights and measures used in - the United States have since Apr. 5,. 1893, been based on the metric standards. These fundamental standards are kept by the International Bureau of Weights and Measures, which is supported by the United States, Great Britain and the, other leading countries. of the world. Copies are held-in Washington and other capitals. (2) As the dollar is divided into 100 cents, so the meter, which is 10 per cent. longer than the yard, is divided into 100 centimeters or cm. And as the cent is divided into 10 mills, so the centimeter is divided into 10 millimeters or mm. In measuring clothing and other articles which do not require great accuracy, the centimeter is most con¬venient, so that such work is done in terms of centi¬meters.. Instead of speaking of a 15;2-in. collar, a 40-centimeter or 40-cm. collar is referred to. Where accuracy is needed, as in mechanical drawing, machineshop work, etc., millimeters are employed. Thus 8 mm., is the convenient equivalent for 5/16 inch.

Jan 1, 1921

By E. S. Moore

Although nickel was in use in alloys long before the Christian era, the metal was not discovered until 1751, when Cronstedt recognized it in niccolite from Sweden. The Chinese apparently used a nickel alloy, known as "pahfong" thousands of years ago and Persian coins dating farther back than 200 B.C. consist of a copper-nickel alloy similar to some of those now in use in coins. The pure metal was first prepared about 1775 and the metal was refined for commercial purposes some years later. The nickel industry did not attain much prominence until the ores in New Caledonia were discovered. Exports of ore from that country began in 1875 and since that date there has been an ever-increasing world output of nickel and a great expansion in the uses of the metal except during short periods of commercial and industrial depression. Previous to 1875, for a number of years, Norway was the chief producer, although the metal was mined also in Sweden, Finland, Italy, Germany, Austria, France, China, the United States and other countries. With the discovery of nickel deposits in the Sudbury district, Ontario, a new factor was introduced into the nickel industry and Sudbury has since become the overwhelmingly dominant feature in the world's nickel markets. Although nickel was first discovered in Canada as early as 1848 near the north shore of Lake Huron and nickel-copper sulfides were found in 1856 by surveyors working close to the present location of the important rnine at Creighton, in the Sudbury field, it was not until 1883 that any importance was attached to this field. In that year copper sulfide attracted attention where the main line of the Canadian Pacific railroad was being projected across Canada to the Pacific coast. Mining began near this discovery in 1889 but in the meantime operations had begun in 1886 in other parts of the field and by 1890 about 100,000 tons of ore had been raised. In the Sudbury field, as in Norway and at the old Lancaster Gap mine in Pennsylvania, the ore was first mined for its copper content and difficully in the refining of the copper led to the discovery of the important proportions of nickel in the ore. No. 3 property of the International Nickel Co., now known as the Frood, the greatest deposit in the

Jan 1, 1932

By Albert Ladd Colby

A GLANCE through the Bibliography appended to this paper will show that the Transactions of this Institute contain what virtually contitutes a history of the development of the manu¬facture of steel rails in this country and abroad. It is, therefore, fitting that this paper, bringing one branch of this important subject down to date, should be here presented, and it is also appropriate to select this joint meeting of our Society with the Iron and Steel Institute to compare the specifications covering the rails produced in these two countries, and to propose a standard specification to govern the manufacture of American rails for export. During the last ten years the production of Bessemer steel rails in the United States and Great Britain has amounted to 32,128,720 gross tons. Nearly 19,000,000 tons have been rolled in the past five years. The next five years will see an even larger output, owing partly to the extension of railway projects in the Orient, in South and Central America, in Mexico, and in Australia and the other British Colonies. Of late years, the American rail-mills have so largely increased their daily output, that trade conditions have often made possible the delivery of American rails to foreign ports. The tenders submitted by American mills, however, have always been accompanied by requests for changes in the foreign specifications, chiefly in the reduction of the amount of testing required; and it has only been natural, especially at first, that the engineer, whose specification had always been accepted without question by British mills, should interpret American tenders 'as an evidence that an inferior rail would be furnished

Sep 1, 1906

By R. C. FLEMING

MINING rock asphalt for use as a paving material is an industry which has grown with the spread of the good roads movement. "Mineral Industry During 1930" reports asphaltic pavements constructed, including maintenance and repair but excluding pavement constructed with road-oil, cut-back or emulsified asphalt, as grown from 23 million square yards in 1911 to a high of 144 million in 1927. In 1930 the same source reports 106 million square yards of such paving laid and, in that year, 664,871 tons of native rock asphalt were so utilized. Many states contain rock asphalt deposits of greater or less importance but in only a few places are the de¬posits being mined commercially. In the year cited Ken¬tucky produced 305,024 tons of bituminous sandstone, Texas 270,138 tons, mostly bituminous limestone, while Alabama, Oklahoma, California and Utah produced 89,709 tons of bituminous rock for road construction. In addition Utah produced 37,906 tons of the purer asphaltic products, gilsonite, wurtzilite and ozokerite, for other uses. Speaking generally, the rock asphalt is a sandstone or limestone naturally impregnated with asphalt to an extent that makes it an ideal road surfacing material without mixing or treatment other than crushing. The asphalt content of the commercial product runs 8 to 12 per cent.

Jan 1, 1933

By W. F. Boericke

WORLD production of silver in 1929 totaled 256 million ounces. In 1928 production was 258 million ounces, and in 1927, 254 million ounces. With an actual decrease in the amount of silver produced last year, as compared with 1928, and an increase over 1927 of less than one per cent, obviously there has been no overproduction of the metal in the popular sense. But the price of silver tells a different story. For 1927, the average quotation was 56.37 cents; it was 58.17 in 1928, and 53.0 in 1929. During the last year it reached a high point of 57 cents in January, and fell steadily, without interruption to the downward trend, to a low of 47 cents in December. Since then it has dropped to an all time low of 43 cents on February 6.

Jan 1, 1930

By E. F. Koppe

The Upper Freeport coal in the Freeport and New Kensington quadrangles, Pennsylvania, varies from a bony streak to a thick coal deposit often exceeding ninety inches, the "Double" or "Thick Freeport". Distinctive basal partings, a central bone layer, and a canneloid top bench may be present. The appearance of a sandstone roof, sandstone rolls, and bony coal at the top of the main coal bench can be anticipated in thin Freeport areas when basal partings are absent. When the two basal partings are present, a shale roof is normal. These effects are correlated with the original topography upon which the coal was deposited. The original depositional high areas tend to coincide with present structural highs. Preliminary data indicate that coal quality, in part, is affected by the deposi-tional setting. In "high" areas, a tendency exists for the main coal bench to contain higher percentages of fusain and mineral matter. Within limits, some-what higher ash fusion temperatures appear to correlate with paleotopographic highs. As a result of these findings, critical examination of the paleotopography and related sediments is indicated in other areas and other coals. The Upper Freeport coal is quite variable both in thickness and composition in the Freeport and New Kensington quadrangles of Pennsylvania (Figure 1). The coal horizon in these quadrangles is marked either by a thin carbonaceous shale bed or by a single bed containing a variable number of partings (binders). The complex coal zone known locally as the "Double" or "Thick Freeport" contains the Upper Freeport Coal Bed at the base; but in addition, it has an overlying bone layer and an upper coal bed occasionally capped with a canneloid layer. The "Thick Freeport" often exceeds 90 inches in thickness, whereas the normal Upper Freeport coal usually varies between 34 and 50 inches.

Jan 1, 1961

By H Haas

H. HAAS, San Francisco, Cal. (communication to the Secretary?). -Fig. 1 plainly shows that the comparison of the steam-turbine and Diesel-engine plants was made on a basis of 6,000 kw. continuous operating load. The tabulation of costs for an 8,000-kw. load is merely done to show the relation of increased output on' the unit power costs. Both plants would sacrifice their reserve capacity, which is to insure continuous operation, if operated to generate 8,000 kw. continuously; unless Mr. Hawkins advocates the operation of one of the turbines at 33.33 per cent. overload, retaining the other as a standby, which, besides overtaxing the turbine, results in a great loss of efficiency. It would he well for Mr. Hawkins to qualify certain of his statements. Thus, under the caption "Diesel Engines, Selection of Units," he says that "two of the largest Diesel-engine builders take the position that, in the present state of the art, they would not attempt to put out units over 1,000 kw.;" he should qualify it by saving that "two of the largest American Diesel-engine builders take the position that, in the present state of the art in the United States, they would not attempt to put out units over 1,000 kw." The reason that American manufacturers restrict themselves at present to units of that size is to be found not so much in a lack of experience in building large units as in a lack of a sufficient, demand for them in the United States to justify the heavy capital outlay connected with the development of such engines. There are relatively few localities in the United States where fuel prices are as high as they are in the Southwest, and regions of high fuel prices are sparsely settled and have a very limited demand for power. Where low fuel prices obtain, steam turbines are active competitors of Diesel engines for large power plants, particularly when the station load factor is low. As most of the American manufacturers of Diesel engines work under license agreements with European manufacturers, which limit their market to the United States and its possessions and Canada, a further limitation is imposed upon them, leaving to European firms practically the entire world as a market.

Jan 5, 1917

By W. W. Krech, T. E. Perkins

As fractures are propagated through rocks, energy is absorbed near the extending crack tip. Apparent surface energies for several rocks have been measured by cleavage under dynamic con-ditions. At nominal crack velocities from 0.5 to 500 in (min, measurements showed that fractures propagated in discrete jumps. Calculated surface energies and moduli were relatively insensitive to nominal rate of cleavage. in another set of experiments, rocks were cleaved under high confining stresses. The rocks were submerged in low leak-off fluids which formed a filter cake on the freshly cleaved surfaces (similar to the hydraulic lracturing process). Apparent surface energies were increased substantially as the surrounding fluid pressure was increased. Moduli in bending increased significantly upon application of the first 1,000 psi but were insensitive to stress level at greater pressures. INTRODUCTION For almost 20 years, hydraulic fracturing processes have been utilized effectively to stimulate oil and gas wells. During this period, some process improvements have resulted from studies of fracture orientation, mechanics of fracturing, areas generated, conductivities of cracks, etc. Yet many questions remain concerning the conditions and pressures needed during fracture propagation. In this paper we will report additional studies of the mechanics of fracture extension. It was shown previously3 that large rock samples could be cleaved under controlled conditions so as to measure the apparent surface energy (that amount of energy absorbed per unit area of new surface created). In this paper we consider the effects of two additional factors on surface energies, viz.: (1) effect of cleavage rate and (2) effect of confining stress level. THEORY Cleavage experiments were conducted on rock samples similar to that illustrated in Fig. 1. Blocks of rock several inches wide, 2- to 3-in. thick, and up to 3 ft in length were grooved longitudinally with shallow guide slots. A crack was initiated and allowed to extend along the web as the top of the rock specimen was pulled (or pushed) apart. Auxiliary equipment permits the measurement of (1) force applied at the top, (2) separation at the top and (3) crack length. (Further experimental details will be given in the next section.) The rock beams created by the crack are considered ton be cantilever beams. The deflection (or separation of the rock beams) at any point is calculated 4,5 by the beam Eq. 1.

Jan 1, 1967

By H. G. HYMER

B ECAUSE of its remote geographical position and inaccessibility, little is generally known of the mining and prospecting in Northern Rhodesia. In this rather new and promising region, the development of mines presents many difficulties. Although many mineral discoveries have been made, progress in .prospecting the huge mining concessions has been handicapped by the lack of roads, communication, transportation, native population and incomplete knowledge of geology.

Jan 1, 1929

By B. W. Roberts, V. A. Phillips

A copper alloy containing- 25.5 at, pct Zn and 19.0 at. pct Ni, which was previously found to show an anoma1old.s hardening effect on quenching- from 600 "C and aging- at 400oc, has now been examined by neutron diffraction. No evidence of long-range order was found. The aged sample showed diffuse scattering- consistent with clustering. The anomalous hardening effect is now attributed to lattice strains caused by clustering rather than (long-range) order hardening. SOLID-solution Cu-Ni-Zn alloys (the commercial 'nickel silvers") have been reported to show anomalies in: change of resistivity on cold working,1-6 temperature coefficient of resistance,2-12 resistivity at low temperatures,13,14 parameter (vs temperature),2"4 calorimetric data,2,4 specific heat,15,16 dilation,2-4 and elastic modulus.17 The structure responsible for the anomalies is produced by annealing typically near 400°C and is rather loosely referred to as the ('K-Zustands" (K state), a term coined by Thomas1' who apparently meant simply that the arrangement of atoms on the sites deviated from that expected statistically. Thomas proposed that the K state occurred in a variety of (solid-solution) alloys such as Cu-Ni-Zn, Ni-Cr, Ni-A1, Ni-Cu, Fe-A1, and Fe-Si and is recognized because its formation is strongly temperature-dependent and results in an increase in electrical resistance which can then be decreased by cold working. Later workers on ('nickel silver" have interpreted the K state variously as short-range order, long-range order. or a combination. The present work was prompted by the discovery by Phillips and Jones19 of a substantial hardening effect when an 18 pct "nickel silver" alloy which is fairly close to the Cu2NiZn composition, was reheated in the range 150" to 450 C after previously quenching from 600°C or, alternatively. was slow-cooled from 600°C or above. The phenomenon was attributed to (long-range) order hardening. Due to the similarity in the atomic scattering factors of copper. nickel, and zinc atoms, the ''nickel silvers" are unfavorable for X-ray diffraction studies aimed at detecting ordering. Nevertheless Bialas et a1.,20 using a powder sample containing 47.96 wt pct Cu, 24.03 wt pct Ni, and 27.98 wt pct Zn, slow-cooled from 400" to 200°C taking 500 hr, observed weak super lattice lines. Further unpublished work" using an anomalous dispersion X-ray technique indicates that zinc atoms are regularly ordered at the corner points of the lattice cell, while the nickel and copper atoms are statistically distributed on the remaining sites. Köster 17 also observed X-ray superlattice lines, for example, in an alloy containing 43.5 wt pct Cu, 28.6 wt pct Ni, and 27.9 wt pct Zn superimposed on the basic fcc cell with a = 3.62 kX. He proposed a Cu3Au-type superlattice with the Ll2 structure in which the A sites were statistically occupied by copper and nickel atoms and the B sites by zinc. He adds that substitution must be possible so that zinc atoms partly occupy A sites. Below about 35 pct Cu, Koster had some evidence for a CuAu-type superlattice with the Llo tetragonal fcc structure with a = 3.82 kX, c/a = 0.88 which could be preserved by quenching. This is suggested17722 to correspond to CuNiZn. While the present work was in progress Hirabaya-shi et a1.23 made an independent comprehensive neutron-diffraction study of a single crystal containing 50.05 at. pct Cu, 26.57 at. pct Ni, 0.25 at. pct Mn, 0.13 at. pct Fe, balance zinc. The presence of manganese and iron is surprising since the crystal was supposedly grown from high-purity metals. The homogenized crystal showed evidence of long-range ordering after an anneal of 5 months at about 300°C. Three possible crystal models were proposed. A curious feature of their results23 is that they could not find any neutron-diffraction evidence of ordering in a powdered polycrystalline near-stoichiometric Cu2NiZn alloy. There appears to be some essential difference between a near-stoichiometric Cu2NiZn alloy and one somewhat further off stoichiometry as used by the present authors. Thus Sato14 was able to reproduce the low-temperature resistivity anomaly reported by one of the authors13 on the present alloy if he used a similar composition, but found the normal behavior of the residual resistivity in a near-stoichiometric alloy. satol2 found that the resistivity of a cold-drawn slightly off-stoichiometric alloy increased to a maximum on isothermally annealing at 300°C and then decreased ("over-aged"). Since he could not explain this on the basis of ordering phenomenon, he proposed that zinc atoms were segregating to stacking faults (Suzuki effect) and found etching bands on the surface by replication which were attributed to the widening of faults. Sato suggested14 that the hardening effect observed by Phillips and Jones19 is partly due to the Suzuki effect. EXPERIMENTAL The starting material was 1/4-in.-diam hard-drawn rod of a commercial 18 pct "nickel silver" alloy identical with that used in a previous study by Phillips

Jan 1, 1967

By M. W. BERNEWITZ

ALL live producers and manufacturers of metals and alloys are investigating new uses for their products. The tin and tin-plate industry is no exception. One-third of all the new tin mined and refined is consumed in making tin plate. Several billions of cans are each year made from tin plate for the preservation of nearly 200 kinds of food. There are more than 500 tin-plate mills or individual stacks in the United States, which country makes more tin plate than all other countries combined and exports large quantities. As much as 1,800,000 tons of till plate has been made in a year in this country, and 28.000 tons of tin has been used in this period for this purpose. In sonic years a third of the till is so consumed; in 1933 it was half of the supply.

Jan 1, 1935

By W. M. Peirce

COAL'S importance in the metallurgy of zinc may be gauged by the fact that approximately a million and a half tons is so employed annually in the United States. This brief paper will show in what way the various steps in the treatment of zinc ores utilize this fuel, either in its primary form or as coke or gas, and to what extent. The first step in zinc metallurgy that requires the use of fuel is roasting the sulphide ore, which is the type of ore in which zinc commonly occurs. Since the roasting is nearly or completely autogenous, however, this use of fuel is too minor to warrant further attention. Concentration of zinc ores is usually carried out by conventional milling methods, but a pyrometallurgical method, the Waelz process, is used to concentrate certain low-grade ores, and to recover the zinc content of certain residues in concentrate form. The Waelz process uses a continuous rotary kiln in which a mixture of coal and zinc-bearing material is heated to a

Jan 1, 1948

By W. T. Malone, J. R. Williams, R. L. Tiner, J. M. Tinsley

Hydraulic fracturing methods for production stimulation have become a common procedure in the oil and gas industry. Fracturing treatments are performed on wells of various potentials to help increase the production rate. In addition to the desire for increased production is the need to predict what increase might be expected. This knowledge is useful in economical treatment planning to accomplish the desired production goals for the well. Theoretical production increases due to horizontal radial fractures may be calculated using equations developed from mathematical analyses and electrical models.1,2,6 It also is possible to predict theoretical production increases due to vertical fractures using curves developed from electrical3 and mathematical models.8 However, these studies assumed that the vertical fracture height and the formation height were equal, which may not be true." In addition, the final fracture height through which fluid is produced may not be equal to the created height. The development of vertical fracture proppant transport relationships has made unrealistic the assumption that propped fracture height is equal to created fracture height. Through the use of published proppant transport equations,4'12 it is possible to calculate the height of a bed of propping agent deposited in a fracture of a given height. Assuming that the fluid flowing in the fracture moves through only the propped portion of that fracture (i.e., that the un-propped part of the fracture heals) it becomes essential to know how production increase varies with the ratio of propped fracture height to formation height. It should be recognized that future investigation may determine that the fracture does not heal completely and that a highly permeable channel exists over the deposited bed of proppant. The effect of this channel was not considered for the present study. The following analysis of experimental data allowed development of curves to determine theoretical production increases considering fracture height as a variable. Discussion In designing a fracturing stimulation treatment a number of variables must be considered. The size of the treatment, type of proppant used, proppant concentration, treatment fluid properties and well conditions are all factors affecting the dimensions and permeability of the fracture. Production increase due to a vertical fracture is affected by propped length, height, width and permeability of the fracture for a given set of formation conditions. Production increase may be defined as the ratio of production rate after fracturing to the production rate before fracturing at the same pressure differential, pe — pw. The producing rate in an

Jan 1, 1970

By W. Lawrence Austin

Jan 1, 1884

By M. E. Steidlitz

FABRICATION of semiconductor devices.requires the formation of electrical contacts, often involving the use of lead, tin, and lead-tin solders. In several recent instances when germanium had been bonded to nickel with lead, a new metallic phase appeared, unattached to either germanium or nickel, but rather suspended as a continuous foil wholly contained within the lead matrix. Since such metallic structures do not form in nickel-lead or lead-germanium systems under identical conditions, a brief study was made of the characteristics and possible formation mechanisms of this material. EXPERIMENTAL Specimens were prepared by placing single crystal, transistor-grade germanium discs, 30-mils in diam by 6-mils thick, into a depression in a graphite boat. =A* nickel washers, 125 mils in diam by 5-mils thick, containing a center hole of 10-mils diam, and coined into a soup bowl shape, were loaded on top of the discs, so that the bottom of the

Jan 1, 1959