By A. M. Gow

The trend in ball milling has been toward mills of larger diameter, but without fundamental laws as a guide. The speeds at which mills are run have been a matter of cut-and-try. This paper deals with both diameter and speed and proposes to show the laws which apply to some laboratory ball mills, ranging in diameter from 18 to 42 in., run at various speeds. The correlation of power, speed and grinding rate of the respective mills will be shown by curves of markedly significant similarity. Before presenting the results some consideration will be given to the mechanics of ball milling. Mechanics and Theory of Ball Milling As early as 1904, Herman Fischerl reported observations on specially constructed ball mills which allowed the paths of balls to be studied. The following conclusions were drawn: 1. Balls do not grind the ore, but crush it by impact. 2. At slow speeds the balls roll down the inclined heap, but at higher speeds the balls close to the wall adhere to it until they reach a certain height, whence they are thrown through an arc to the bottom. 3. The falling balls do not come down in clusters, but in series, the balls of each row keeping to their own line of flight according to their distances from the wall while ascending. 4. A further increase in speed results in the balls adhering during the whole of the circuit to the side of the drum. (This centrifuging speed may be called the "critical" speed and may be taken as a reference basis, since it is a constant function of the diameter.)2

Jan 1, 1930

By J. H. Fletcher

AIR has been cooled, heated, washed; humidified and dehumidified for many purposes and in many industries. At a number of metal mines air is conditioned to reduce the high humidity and unbearable heat found in deep workings, and at some mines air is washed to allay siliceous dust. Steam is introduced into the intake air at many coal mines, particularly in winter, for the purpose of keeping loose coal dust so moistened that the hazard of an explosion is lessened. This paper will describe a further successful application of air conditioning in a coal mine, where, for over three years, all intake air has been cooled to a constant temperature for the sole purpose of preventing roof falls.

Jan 1, 1931

By John L. Schroder

In selecting the best system of mining for a particular operation, many different factors must be considered. The system to be finally selected should be that which provides: 1) The highest possible degree of safety for mine personnel. 2) The lowest cost per ton of product. 3) The maximum coal production per man-shift. 4) The most suitable quality of final product, considering its intended use. 5) The maximum percent recovery of coal per acre of reserve consistent with cost and subsidence rights. 6) Consideration for the ecology of the area. Some of the important factors to be considered when choosing a method of mining are: 1) Amount of cover over the coal seam. 2) Type of the rock in the overburden. 3) Characteristics of the coal seam including: (a) the thickness of the coal seam; (b) the nature and location of any impurities or irregularities; (e) the dip (or pitch) of the coal seam; (d) the nature and direction of any definite cleavage ill the czoa1 seam; (e) the hardness of the coal; (f) the structural strength of the coal; and (g) the presence, anti amount, of explosive gas (methane). 4) Quantity of water likely to be encountered in the mining operation. 5) Nature and strength of the roof (top) over the coal seam. 6) Nature and strength of the floor (bottom) under the coal seam. 7) Any previous or concurrent mining in seams above or below the coal seam to be worked. Information on items 1-7 may be obtained in several ways. Topographical and geological reports and maps of the area are generally available

Jan 1, 1973

By Harmon F. Fisher

In the course of a comprehensive investigation for the development of the electrical process for the dehydration of oil-field emulsions, the writer has had an unusual opportunity to direct and execute a number of related, parallel studies concerning crude oil emulsions and extending over a period of nearly six years. Among these was an investigation utilizing the microscope for studying both the general characteristics of crude oil emulsions, the nature of their electrical charge and the action of an alternating current field in causing coalescence of the finely dispersed, more or less permanently suspended, emulsion particles into larger droplets of such mass that subsequent dehydration would follow by the ordinary process of settling, further agglomeration of the water droplets and, finally, separation into commercially dry, pipe line oil and a clean water discharge. It is not the purpose of this paper to enter into a detailed discussion of the highly specialized subject of microscope technique, nor into a theoretical discussion concerning the origin of the electrical charge on the emulsion particle or concerning the mechanism of the electrical phenomena occurring during the electrical treatment of oil-field emulsions. In a short paper of this character one can hope to touch on only a very limited discussion of the theoretical aspects of crude oil emulsions. The subject of emulsions and colloids is comprised in a comparatively young science in which, however, very rapid progress is being made and consequently it is undergoing many changes; a tentative conclusion valid today may be overthrown tomorrow. Nor would it be a simple science even if it were no longer undergoing this rapid progress; a thorough study of emulsions is based upon a knowledge of such fundamental subjects as molecular structure, ionization and other electrical phenomena, surface chemistry, surface and interfacial tension phenomena, viscosity and other factors too numerous to discuss here and the fundamental theories of which are still undergoing more or less change. Therefore this paper will confine itself largely to a generally descriptive discussion, a sufficiently detailed outline of the microscope technique and a brief comment on

Jan 1, 1931

POSITIONS VACANT (Under this heading will be published notes sent to the Secretary of the Institute by members or other persons.) Position open as assistant superintendent at a steel plant. Practical experience in the manufacture of crucible and open-hearth steel and heat treatment of steel and alloy steels required. This position offers an excellent future. No. 9. A company in Virginia desires a man with experience in Western mines to act as superintendent of its pyrite mine. No. 15. Position open as instructor at a University in Middle West to teach the mechanical side of mining, such as hoisting, haulage, drilling, and mine surveying. Salary, $1,500 to $1,800. No. 16. Experienced amalgamator wanted at a mill in Ivory Coast, Africa. An American speaking French preferred. No. 18.

Jan 5, 1914

By J. T. Crawford

ALTHOUGH nearly 10 pct of the total tonnage of coal produced annually within the United States is handled by bulk freighters on the Great Lakes, very little of the detail connected with it has been published other than occasional newspaper stories and publication of tonnage statistics. Of the total tonnage floated on the Lakes each year some 10,000,000 is stored and distributed from the port of Duluth Superior, at the western end of Lake Superior commonly known as the Head of the Lakes. This port has the largest single area concentration of coal docks in the world. Since this area contains the largest ore docks, the largest movable material handling bridge, the largest and highest grain elevator and the largest coal briquetting plant in the world, it is entirely fitting and proper that here also should be located the largest coal dock and what we believe to be the worlds largest clam shell. Of the sixteen coal docks operated by ten companies, five are owned and operated by the North Western-Hanna Fuel Co. which has two docks on the Superior, Wis. water-front and three docks in Duluth, Minn. It is with these five docks that we are primarily concerned. GENERAL HISTORY In the summer of 1871 a small sailing vessel entered the harbor of Duluth Superior with the first commercial coal cargo. All the coal brought up that first year did not amount to more than 3000 tons. During the year 1877 the first dock equipped for handling coal was built in Duluth. Coal receipts increased to 52,785 tons in 1879 the first year for which an official record was kept. Since then the volume of water-borne coal to the Head of the Lakes steadily increased to a maximum of 12,688,321 tons in the year 1923. This tonnage was nearly equalled in the year 1927 and the next highest tonnage recent year was in 1946 when 10,105,703 tons were unloaded. The average annual bring-up over a ten year period 1938 to 1947 was 8,605,231 tons. Approximately 30 pct of the coal unloaded at the Head of the Lakes is handled over the docks of the North Western-Hanna Fuel Co. Competition of other fuels coupled with expansion of coal fields in the mid-west have held coal receipts for Duluth-Superior at a relatively constant figure during the last eight years although the total tonnage of coal floated on the Great Lakes has more than doubled in the past 25 years. From the shovel and wheelbarrow method of unloading early cargoes to the horsepowered windlass derrick with a wooden tub was but a short step. The first movable coal handling, steam operated,

Jan 1, 1948

By William G. Kranz

Discussion of the paper of WILLIAM G. KRANZ, presented at the San Francisco meeting, September, 1915, and printed in Bulletin. No. 101, May, 1915, pp. 927 to 930. M. PETINOT, Niagara Falls, N. Y. (communication to the Secretary*). -I have read this paper with considerable interest and agree perfectly with Mr. Kranz that steel for castings made in an electric furnace is not necessarily, because of that fact, all good steel, and also that the qualities which he mentions, such as absence of segregation, elimination of `sulphur, great tenacity, etc., can be obtained in an electric furnace if operated under proper metallurgical conditions. An unusually low content of sulphur in steel for castings is not, of course, an absolute necessity and the range of this element usually obtained in steel made in basic open-hearth furnaces is sufficiently low to meet all physical requirements. The main factor in making steel for castings, regardless of the process, is the complete deoxidation of the bath to prevent the formation of

Jan 12, 1915

By Lawrence A. Shepard, Richard H. Krock

A series of ductile, two phase W-Ni-Fe composites, sintered in the presence of a liquid phase, were tested in tension. Identical room temperature stress-strain curves were obtained for specimens containing from 80 to 92 wt pct W (58 to 75 vol pct W particles). The composites exhibited a maximum elongation of 29pct at room temperature, and 10.7 pct at 77 °K. The tungsten particles in the composite elongated by the same amount at these temperatures. Single-phase alloy specimens matching the composition of the composite matrix showed about one half the flow stress of the composites. The test results demonstrated that the mechanical properties of W-Ni-Fe composites are determined by the tungsten particles alone and are independent of matrix volume fraction or mean free path over the composition range studied. A general prediction of the plastic behavior of two-phase alloys or composites from a knowledge of the properties, size, shape, and dispersion of the individual components is not, at present, possible. The excellent theoretical and experimental exposition of the dispersion-strengthening problem applies only to cases where the stronger phase is present as fine particles and in volume fractions of a few percent. Materials in which the stronger phase constitutes a significant fraction of the volume, although of broad engineering interest, have received comparatively little analytical attention. This important group of materials is the concern of the present study. The degree of deformation of each phase during the plastic working of a ductile two-phase alloy has been established by Boas and Honeycombe,1 Clare-brough,2 and Clarebrough and berger.3 These workers empirically correlated the recrystallization temperature of the individual phases with the degree of cold work sustained by each. It was shown that the deformations of both phases are equal and therefore the same as that sustained by the composite whole when the volume fraction of the stronger phase exceeds 35 pct. At yielding, however, deformation begins in the weaker phase. A direct correlation of composite strength, as a function of deformation, with the strength of the individual components cannot be made. In the presence of stronger phase particles, the flow stress of the weaker matrix phase is enhanced by an additional hydrostatic component. The development and potential magnitude of matrix strength promotion upon straining has not even been experimentally established. Quantitative work in this field has been confined to ceramic-metal composites. These materials fracture at strains considerably below 1 pct by cracking of the ceramic particles.4-6 An indication of the potential constrained matrix strength capacity is given by the observation by Nishimatsu and Gur-land4 that the maximum tensile strength of a WC-Co composite is almost double the bulk strength of the cobalt matrix. The relationship between composite strength and geometry is ordinarily expressed in terms of the mean-free matrix path (referred to subsequently as MFP) between the stronger particles.* This factor takes into account both the volume fraction of matrix phase and the average size of the particles. unke17 concluded that composite strength varied directly with the decreasing log MFP, following the Gen-samer8 relationship. However, Gurland and ~radzil~ reported a strength maximum at an MFP of the order of 1 p in WC-Co composites. A ductile two phase metallic composite was chosen for the present investigation of composite mechanical properties with the view of avoiding the difficulties and ambiguities noted above. The W-Ni-Fe heavy alloy of Green, Jones, and pitkin9 contains 80 to 94 wt pct W, and nickel and iron in a weight ratio

Jan 1, 1963

By Noah Fields Drake

During July and August, 1899, the writer took advantage of an opportunity of going to Shansi to gather some information concerning the geology and value of the already famous coalfields of that province. The long journey, mainly on slow river-boats, and the limited time at command, allowed only about ten days of work to be done in the coal-fields around Tsê Chou. The geologic structure and the rock-formations were found to be simple and quite regular, so that in that time the accompanying sketch-map (Pig. 1) was made, and a fairly good idea of the distribution of the coal and general geologic features was obtained. The map was made by measuring a base-line about three-quarters of a mile long, triangulating for principal points over the field, and filling in the details by rapid sketches. The few elevations marked on the map were taken with an aneroid barometer. Only a few of the great number of towns and villages that are within this densely populated area are shown; and the coal-mines indicated are not the only ones within the area, but the ones where most of the following information about the coal was obtained. The value of this coal-field was first clearly set before the scientific and commercial world by Baron von Richthofen,* who made a geologic reconnaissance of Shansi in 1870. Since that time the hostile attitude of the Chinese government and people towards foreigners and their enterprises has kept the coal-fields from being developed. But the last few years of rapid change in the conditions of China have at last apparently opened a way for the exploitation of this coal-field. The Peking syndicate, a joint English-Italian company, now has concessions from

Jan 1, 1901

By Allen L. Hatch

A survey of all phases of the world's lead and zinc production in 1968 from ore through to refined metal was conducted by sending questionnaires to individual companies ad the results of this survey are tabulated at the end of the paper. The paper goes on to review changes in the geographical distribution of the world's lead and zinc mine and metal production and in the trading patterns of raw materials, present and future utilization of metal production capacity, developments in metal smelting and refining processes and the growing importance of marketing, product development and research in the 1950's and 1960's.

Jan 1, 1970

By R. T. Hukki

IT is no great exaggeration to say that present grinding practice and economics are largely determined by lining design. A record of outstanding liner wear can be achieved with any liner surface pattern that will positively lock the outer layer or layers of grinding media. With no slippage, lining wear is bound to be slight. At the same time, popular practice calls for tumbling loads of about 50 pct of mill volume to obtain maximum grinding capacity. Innumerable parallel grinding investigations have verified that optimum speed for such a mill lies within 70 to 85 pct of theoretical critical speed. If the mill is speeded up to 100 pct of critical, little or no grinding can be accomplished. Earlier Work on Supercritical Grinding: First investigations concerning grinding at supercritical speeds seem to be very old. Remarkable work on the subject has been performed by White,1 and his experiments have been described and summarized by Richards1 White's contributions seem to have passed unnoticed by Fahrenwald, 2,3 whose extensive experiments have been well presented, yet apparently very little appreciated. Additional work on grinding at supercritical speed has been reported, e.g., by Lewenson and Tscherny,4 USSR; Anselm5 and Grunder,6 Germany; and Rose and Evans,[6] Great Britain.

Jan 5, 1958

By Willard H. Mutchler, Henry S. Rawdon

As part of the study of the scratch-hardness method for metals and alloys in coöperation with one of the technical committees of the American Society for Testing Materials, the authors devoted considerable time to the study of the changes in hardness of metals when cold rolled. Various seemingly contradictory statements in the technical literature concerning the applicability of the serateh-hardness method to such cold-rolled materials were among the principal reasons for the investigation, the results of which are in part presented here. The effect of cold deformation, at least in moderate degrees, on the hardness as measured by the Brinell aid other common methods is so well known that further reference is unnecessary. Concerning the scratch hardness of cold-worked metals, Martens and Heyn state1 that hardness, whether measured by the ball-pressure rnethod (Kugeldruck) or by the scratch method (Ritzverfahren), will be increased by cold deformation. Jeffries and Archer give a seemingly diametrically opposite view. They state,2 that "the sclerometer (indicating scratch hardness) shows little difference between cold-worked and annealed metals." Portevin3 has shown that the rate at which the Brinell hardness of cold-worked copper and brass increases is very high for relatively slight deformation after which it drops to zero, while Merica and Walten-berg4 have observed that monel metal shows evidence of softening on

Jan 1, 1924

By Jr. Baldwin. William M

WELL known to every metallurgist is the fact that different production schedules will profoundly affect the character of annealed metal strip. Yet the number of conditions [ ] that may be wrought by different combinations of rolling and annealing schedules is so myriad that despite the continual research that is being applied to this subject, the complete picture is not yet known. Copper, like all other metals, during the process of rolling or annealing, develops certain crystallographic configurations which should not be dismissed as being too impractical, for the crystallographic condition existing within the metal is a principal influence upon both the external mechanical properties and the behavior of the material [ ] when it is subjected to such operations as bending, flanging, drawing, and so forth. EFFECT OF ROLLING AND ANNEALING UPON THE CRYSTALLOGRAPHY OF COPPER STRIP The most salient points in the crystallographic reactions of polycrystalline copper to rolling and annealing may be best represented graphically by a "map" such as that given in Fig. I. I. As copper strip is cold-rolled from a randomly oriented structure (pole figure I),

Jan 1, 1942

By C. J. Bier, J. F. O?Keefe

THIS study was carried out with copper because it represents the simplest form of sintering, in that but one metal is involved and all reactions occur in the solid state. [ ] The present work will cover three variables affecting the sintering process; namely, briquetting pressure, sintering temperature and time in hot zone. Although strength and dimensional changes were observed, this is primarily a metallographic study of the sintering process in copper. The term "sintering" should be understood to mean the process by which the metal powder particles of the compact become united into one body. MATERIAL USED The copper powder used was made from reduced copper oxide, and is typical of a grade used for the mass production of parts formed of metal powders. The screen analysis of the powder was as follows: [ ] The minus 325-mesh analysis was made by using a Roller Air Analyzer.1,2 The apparent density is here defined as the weight per cubic centimeter of the [ ] loose, unpacked powder as measured with the Hall flowmeter. The value for the powder used was 2.57 grams per cubic centimeter.

Jan 1, 1944

Gentlemen of the American Institute of Mining Engineers.—As you well know an application is about to be made to Congress, by the American Society of Civil Engineers, for the appointment of a cornmission composed of persons skilled in the production and use of iron, steel, and other structural materials, whose duty it shall be to test the strength, elasticity, and other quatities of such materials ; not simply the substances used as such, but the members of large structures composed of such materials, of the forms and sizes in which they are actually used. As I understand, the papers that will be read here to-night will have for their object to show the necessity for such tests, and therefore the necessity for the commission asked for. As the representative of the Society of Civil Engineers, I have to thank you, gentlemen of the Mining Engineers, for the great zeal with which yon have taken up this subject, and seconded the efforts of the Civil Engineers; or, perhaps I ought rather to say, initiated the efforts to get a suitable commission appointed to obtain most vitally important information which it is admitted on all hands we do not now possess. In drawing up the memorial to Congress, in connection with some of the ablest and best informed of our Society, and in all the discossions on the subject, I have been struck with the emphasis with which the confession is made, that so little is known of the strength of the larger-sized members constantly used in building structures of the magnitude which the present requirements of the country now demand. I presume the remarks made to-night will bring this out very prominently. This is no disgrace, for with the means here-

Jan 1, 1882

By A. E. Outerbridge

I had the honor to present to the American Institute of Mining Engineers at the Pittsburg meeting, February, 1896, a paper having the foregoing title, in which I said : " It has generally been accepted as a fact that cast-iron, under the influence of repeated shocks, becomes brittle, and will finally break under a blow which otherwise it would have withstood. It will probably surprise metallurgists, therefore, to learn that experiment disproves the supposed fact, and establishes exactly its opposite. " The result of about a thousand tests of bars of cast-iron of all grades, from the softest foundry mixtures to the strongest car-wheel metal, enables me to assert with confidence that, within limits, cast-iron is materially strengthened by subjection to repeated shocks or blows." Three tables were appended showing increase of strength

Jan 1, 1905

By A. F. Taggart

This paper describes the result of a series of experiments run in the laboratory of the School of Mines, Columbia University, during the winter of 1927-28. It shows that the several operating adjustments of a pneumatic table produce effects in the action of a given coal that may be grouped into two classes, viz.: stroke length, speed and rocker-arm angle, which affect longitudinal travel; air supply and table slope (transverse and longitudinal), which determine transverse travel. The magnitude of the effect of the different adjustments varies. Some of the adjustments affect stratification of the bed, both as respects size and specific gravity of the bed components, as well as direction of travel. Operation of a pneumatic table is fundamentally different from that of a wet table in that the former exerts, through the air supplied, a force on the particles upward away from the deck which is lacking on the wet table while, on the other hand, it lacks the positive control over cross travel that is supplied by the wash and feed water. Apparatus The pneumatic table used is shown in Fig. 1. Deck A is 20 by 12 in. and consists of nainsook supported on slats that register with the riffles. Fig. 2 is a photomicrograph of the nainsook used. It shows that the cotton threads average about 0.13 mm. dia. and the apertures about 0.17 mm. The deck carries 12 riffles consisting of wooden strips, 3/16 in. wide and 1/4 in. high, laid parallel to the feed side of the table. The riffles terminate along a line starting on the feed side at a point 11 in, from the mechanism end and running to the corner formed by the coal side and slate end. Taper starts from a line that runs parallel to their terminal line through the junction of the upper riffle with the mechanism end. The height at the terminal line is about 1/32 in. The deck with its supporting slats is carried on a framework consisting of rails A, sloping end rails B, and adjustable metal strips C, which latter permit variation in transverse slope. This frame is enclosed at the edges by means of heavy canvas, indicated in the sketch by wavy lines, which makes a flexible conduit between the deck and the stationary air chamber,

Jan 1, 1930

By Donald R. Williamson, Edward R. Mueller

Cyprus Pima Mining Co.'s open pit operation was started in 1957 with the normal assumption that the ore reserve estimate was accurate within an acceptable range of values. Over the years, a number of attempts have been made to refine and polish the ore reserve figures using a variety of established standard procedures. None of these attempts have produced results which are totally satisfactory, particularly when comparisons are made between ore reserve estimates and short to medium range production figures. Statistical studies of operations data revealed relationships which could be used to subdivide ore blocks in much the same way as they are actually mined. Comparisons between these newly developed ore blocks and production data show that the new method of evaluation yields excellent results.

Jan 1, 1978

By G. A. Stamboltzis, N. Arbiter, C. C. Harris

Fracture under low-velocity free-fall and double impact and under slow compression have been investigated. The pattern of breakage and the size distribution of resulting fragments of sand-cement and glass spheres have been determined. Photoelasticity methods were used to simulate the stress distributions in free-fall impact in order to explain the observed patterns of breakage. Oblique fracture planes, occurring only in free-fall impact, develop along lines which coincide with the trajectories of maximum compression as determined by mathematical analysis. Breakage efficiencies for different modes of fracture were compared for both types of spheres. For the same specimen and loading system, static loading and low-velocity dynamic loading induce geometrically similar stress fields resulting in reasonably similar fracture patterns and shapes of fragments. This work had its origin in a desire to understand three fundamental processes involved in autogenous comminution: namely; free-fall impact, double impact, and slow compression. To simplify the investigation, it is preferable to reduce the entire multi-stage fracture process to its most elementary form; that is, to study products resulting from a single-stage operation, such as the breakage of a specimen under single fracture conditions. The goal of this research is to study the energy utilization in the single fracture of brittle specimens and to relate the pattern of breakage and the resultant fragment size distribution with the nature of the material, the specimen size, the manner of load application, and the rate of loading. Published works on single fracture have mainly been concerned with tests on large (> 1-in.) irregular mineral pieces, especially coal and coke. These were mainly friability tests employing a single blow on closely sized pieces. More recently, small mineral specimens in the sieve range and glass spheres have been investigated.5-7 Kick8 has reported free-fall and double impact tests with large large cast-iron, cement, and clay spheres. The establishment of a minimum breaking height independent of size in the free-fall impact tests, and the direct proportionality between the minimum work required for fracture and the volume of the specimen in double impact tests were used by Kick as an experimental proof of his classical law of "Proportional Resistances." In the present work, spherical shapes were chosen because of their simple body geometry and consequent impact and stress field symmetry. Because the study involves several physical principles in connection with brittle-fracture, it may be of interest in fields where the strength of materials is of importance. APPARATUS The equipment for the free-fall impact testing is illustrated in Figs. 1 and 2. This consisted of a massive (17 x 17 x 3-in.) hard steel plate onto which specimens were dropped and a specimen release mechanism which could be set at any desired height up to 10 ft above the plate so that the impact velocity could be varied up to about 25 ft per sec. Double impact breakage is characterized by two points of loading situated at opposite poles. For this mode of breakage the apparatus was modified (Figs. 3, 4 and 5) so that a falling mass provided an impact of predetermined magnitude on a specimen resting on the plate. A spring-loaded device operated immediately after fracture to arrest the falling mass and to record its residual kinetic energy. Precautions were taken to avoid secondary breakage. Slow compression tests were performed on a conventional hydraulic testing machine, the specimen being held between two hardened parallel bearing blocks. In the case of glass spheres, carbide bits were used. Photoelasticity studies were performed on two-dimensional models held in a loading frame equipped with a force gauge (Fig. 6). The models were viewed in a polariscope and isochromatic fringe patterns were recorded photographically. SPECIMENS Sand-Cement Spheres: A series of sand-cement spheres were prepared by molding in spherical glass flasks.

Jan 1, 1970

By Frederic L. Kadey

Diatomite is a siliceous, sedimentary rock consisting principally of the fossilized skeletal remains of the diatom, a unicellular aquatic plant related to the algae. Thus, it has-been formed by the induration of diatomaceous ooze, and consists mainly of diatomaceous silica, a form or variety of opal which is first formed in the cell walls of the living diatom. Diatomaceous silica is not generally regarded as a synonym or the equivalent for diatomite, although it has been so used at various times. Accurately, diatomaceous silica is the preferred name for the principal mineral component of which the rock, diatomite, is composed. The terms diatomaceous earth and kieselguhr are used as synonymous with diatomite. The designations tripoli, tripolite, infusorial earth, etc., were used at one time but are now obsolete. With the changing nomenclature, these terms that were at one time correct when proposed and used for generations would be considered incorrect if used today in the light of current knowledge. The designation diatomite is reserved for those accumulations of diatomaceous silica that are of sufficient quality, size, and minability to be considered of potential commercial value. Processed diatomite possesses an unusual particulate structure and chemical stability that lends itself to applications not filled by any other form of silica. Foremost among these applications is its use as a filter aid, which accounts for over half of its current consumption. Its unique diatom structure, low bulk density, high absorptive capacity, high surface area, and relatively low abrasion are attributes responsible for its utility as a functional filler and as an extender in paint, paper, rubber, and in plastics; and as an anti-caking agent; thermal insulating material; catalyst carrier; and chromatographic support; polish, abrasive, and pesticide extender to name a few representative applications. The United States is the principal producing country, although diatomite is found in numerous other locations.

Jan 1, 1975