By Eugene F. Broome, Hugh A. Walls

Self-diffusion coefficients were measured using the modified shear cell technique over a temperature range from 31" to 401°C. These data agree within experimental error with those of Petit and Nachtrieb, which were determined from 30°to 99°C. LIQUID self-diffusion behavior in gallium has been studied previously by Petit and Nachtrieb&apos; using their shear cell technique.&apos; Data were obtained in that investigation over temperatures ranging from 30.6 to 98.7"C, and these comprise the only published data for liquid gallium. In the work reported here, diffusion data were obtained from 30.8 to 400-9.Cusing a shear cell technique different from that of Petit and Nachtrieb. This modified shear cell method and the mathematical analysis for diffusion in a finite capillary geometry have been previously described.3 PROCEDURES AND ANALYSIS The segments of the modified shear cell were fabricated from types 304 and 316 stainless steel. No corrosion problems with gallium were encountered until attempts were made to obtain data at 500°C. The diffusion capillary diameter was 1.59 mm and capillary lengths for the four sets of cell segments used are given in Table I. Gallium with a purity of 99.999 wt pct was obtained from Var-Lac-Oid Chemical Co. The gallium-72 isotope used to measure the self-diffusion coefficients was produced from this inert gallium by irradiation in The University of Texas Reactor Facility, and was checked for radiochemical purity. Following a period of isothermal diffusion controlled to within 0.0l°C, the contents of each capillary section were emptied into a counting planchet, weighed to assure that gallium had not been lost during handling, and the radioactivity determined by windowless gas-flow proportional counting. Great care was taken to obtain a reproducible counting geometry for the samples. Diffusion coefficients were obtained from the solu-tion3 to the diffusion equation for the modified shear cell problem, viz.: in which B2= C2(t)Li + L2)- CSL1-COL2 P* (C0-Cs)(L1+ L2) and L, and L2 are the capillary segment lengths. The step-function initial concentration distribution was expressed as C(x,O) = C, for -L1 = x < 0 and C(x,O) = Co for 0 < x 5 L?. Also, C2(0 = ^- fcix,t)dx Computation of the diffusion coefficients was done numerically as described in our earlier paper.3 Because of the short half-life of gallium-72 (14.1 hr) and the relatively long counting times taken to give a precise value of the diffusion coefficient, it was necessary to account for the radioactive decay both during the actual count and between counts for different samples (before and after diffusion). Thus, the average count rate Cz(t) for a second sample counted from times t3 to t4 can be made consistent with the average rate Co determined for a first sample counted from times t1 to t2 by the relationship: N(e-»i-e-M») , , C2(f) " &-«,)(*-«.-«-»«) [21 in which N is the total number of counts taken and is the decay constant. RESULTS AND DISCUSSION The self-diffusion coefficients determined in this investigation are listed in Table 11. Values of the parameters used to calculate the coefficients are given in the table, as are values of the random counting error &apos; for the concentration ratio pz and the corresponding expected random variation AD in the diffusion coefficient. The quantity is calculable from: &apos;Cg — C2(t)} , „ ,2 .-„¦, M co-csl(ACs)J W in which AC is the error in the individual count rate. The mean values of the diffusion coefficients within each temperature group are also given in Table 11. Such temperature groupings of data are reasonable because of the small variations between the temperature~.~

Jan 1, 1970

By Donald A. Corrigan, John Chipman

It is shown that the heat of solution of nitrogen in liquid-iron alloys is Proportional to the interaction coefficient. This proportionality forms the basis for a method of predicting nilrogen solubility at any temperature when the interaction coefficient is knoun at 1600°C ov when the solubility is known at some one temperature. A method for predicting the solubility of nitrogen in liquid steels, including alloy steels, was proposed some years ago by Langenberg.&apos; Since the data available at that time were restricted to temperatures of about 1600°C, his predictions were similarly restricted. More recently, Nelssonz devised an approximate method for estimating nitrogen solubilities at higher temperatures. It is the purpose of the present paper to present a method by which the solubility of nitrogen at any temperature within the steelmaking range may be predicted from the known interaction coefficients at 1600°C. Nitrogen in iron and in all of the alloys to be considered here is known to obey Sieverts&apos; Law; hence the activity of nitrogen in an alloy of fixed composition is proportional to its concentration, here expressed in weight percent. The activity of nitrogen is defined as equal to its weight percent in the binary Fe-N solution at any temperature. Its activity coefficient in any alloy is the comparison being made at equal values of T and PN2. In all alloys the activity coefficient changes with composition, log fN being a linear function of the percent of alloying element at low concentrations. In the following calculations the alloy compositions are restricted to those in which this linear relation is exhibited. For most systems this is a fairly wide range, for example up to 5 pct V and to 10 pct Cr or Ni. For this composition range. complex alloy is the same as that in the Fe-N-j ternary solution. Langenberg&apos;s method of prediction was based on Eq. [3], the values of log fN for various additions being taken from a graph. Instead of using the simple addition indicated in Eq. [3], he used a more complex method suggested for Fe-S-j alloys by Morris and Buehl.3 For the composition ranges in which Eq. [2] is valid the two methods are equivalent. Nelson extended the prediction to other temperatures on the assumption that logfN is inversely proportional to absolute temperature. It may be shown that inverse proportionality would result if the partial molal entropy of nitrogen were unaffected by addition of the alloy element, an assumption which Nelson designated as a "regular" solution. It has been shown recently by the authors4 that this assumption is not a good approximation. The heat of solution of nitrogen (N2) in an alloy may be obtained if the solubility is known as a function of temperature. Measurements of this nature have been reported recently by Beer5 for Fe-Mn alloys, by Nelsson2 for Fe-C, by El Tayeb and parlee6 for Fe-V, and by Pehlke and Elliott7 for many alloys embracing a wide range of compositions. In connection with the work of the last named authors it is noted that their Fig. 22 gives the heat effect per half mole rather than per mole of N2. In using their data we have shifted some of their values slightly by using the best straight line in preference to their curve. Their data, supplemented by others from the literature, are summarized in Table I. In Fig. 1 the heat of solution of nitrogen is shown as a function of composition for the several alloy systems. The difference between the heat effect in the alloy. AH; and that in pure

Jan 1, 1965

By Orville R. Lyons

DISCUSSION Judson S. Hubbard (The Humphreys Investment Co., Denver)—In this very interesting paper several brief references are made to the Humphreys spiral, a device used for cleaning fine coal. In Table I, Plants 76 and 77, data are given on spiral performance treating Raton and Trinidad coal. The fine coal, as fed to the spiral in these instances, is actually a table middling, hence the more easily treated material was previously removed and a large number of particles were present which were difficult to clean. Mr. W. M. Bertholf of the Colorado Fuel and Iron Co. presented a paper in February, 1946, Cleaning Table Middlings from a Coal Washery with the Humphreys Spiral Concentrator, from which I quote: "In considering the results of our tests it should be noted that the feed was our table middling, and that any real separation is a &apos;moral victory&apos; as there is little material that could properly be called coal and practically no heavy rock, the consequences being that previous attempts to clean the middling have not at all been successful." Referring again to Table I, Plants 72, 73, 74, and 75, these data were obtained by Yancey and Geer and others and presented at the February 1950 Meeting, AIME, in a paper entitled Laboratory Performance Tests of the Humphreys Spiral as a Cleaner of Fine Coal. Results shown for those tests involve all particles from 8 mesh through the colloids, which admittedly is not an ideal situation for spiral feed if much refuse is contained in the —80 mesh or —100 mesh size range. As an illustration of the effect of treating too broad a size range, let us consider Plant No. 75, Kentucky No. 9 seam. Spiral feed was 8 mesh x 0. Now had this been 8x100 mesh the percentage of misplaced material would have been 8.0 pct instead of the reported 15.26 pct. Similar comparisons can be made on the other data presented with respect to the spiral. Other types of equipment show a similar trend in that whenever too fine a size is treated in a given unit process the percentage of misplaced material increases. Since the spiral is working near the finer end of the size range, it will sometimes be advantageous to treat the entire range of —8 mesh material rather than to deslime and make a fair showing on, say, the +80 or + I00 mesh. Desliming is subsequently done in any case in the dewatering or thickening operation. Results obtained by spiraling any given coal depend on factors too numerous and complex to discuss here, but there are strong indications that proper preparation of feed to the spiral can improve results obtained on some of the raw coals tested. This is clearly pointed out at the end of the aforementioned paper by Yancey and Geer. "The spiral is an extremely simple device which involves no moving parts and is constructed almost entirely of unmachined castings. Since it is such an uncomplicated mechanism, operation is simple and virtually foolproof. These characteristics, which go far toward insuring low cost operation, are attractive attributes in any coal cleaning unit." Certain equipment used in conjunction with the spiral has resulted in a decrease in the percentage of misplaced material, notably in actual practice the launder screen which is used to remove objectionable high ash fines from a spiral-washed coal product. Private correspondence with the U. S. Bureau of Mines has intimated that an additional yield of coal is possible by flotation of the spiral middling. Possible future improvements and developments may result from other methods now under consideration. Finally, some compromise must be made between the best metallurgical performance and the best practical or economical results. Mr. Lyons emphasizes in his summary this objective of overall economy in selection of equipment. G. B. Walker (American Cyanamid Co., Stamford, Conn.)—I had the pleasure of reviewing the draft of this paper and my curiosity was aroused by the data given for Tromp plants, in that all of the examples shown appeared to be 2-product separations, whereas all the Tromp plants with which I am familiar have been 3-product units. The data given for plants No. 101 and 102 appear to be taken from Tromp&apos;s brochure on his process and represent the results obtained at the Dominale plant in Holland which was operated for many years by Mr. Tromp. The plant, which was designed to treat 58 tons per hr, was sampled while treating 35 tons per hr of 3Y4x-in. coal. Example 101 appears to conform to what would result if the middling product were calculated into the refuse product, while Example 102 represents the calculation of the middling into the coal product. It is believed that Examples 103 and 104 represent the operation of the Willem-Sophie Mine in Holland recalculated on the same basis. In checking the English examples given by numbers 14, 15, 16, and 17, the same procedure seems to have been followed. These results have, apparently, been taken from an article in Colliery Engineering in August 1941, describing the initial operation of the Williamthorpe Colliery of the Hardwick Colliery Co. Two vessels are employed in this plant, one to treat soft coal and one to treat hard coal. Example No. 14 presents the results that could be obtained from the soft coal bath if the middling were calculated into the refuse, and Example 15 the results when the middling is calculated into the coal. Examples 16 and 17 represent the same expedient in the case of the hard coal bath. Of interest to this discussion is the fact that during the past year the Simon-Carves Engineering Co. in England has installed in the Williamthorpe plant their new "Sim-Car" medium cleaning system which is based on magnetic extraction and control and which is licensed under the Heavy-Media Separation Processes patents by the American Zinc, Lead and Smelting Co. This system has been described in the December 1951, issue of Colliery Engineering. It is reported that since the Williamthorpe Colliery was changed from the Tromp system of medium cleaning to the Magneto-Motive method of medium control the opera-

Jan 1, 1953

By Orville R. Lyons

DISCUSSION Judson S. Hubbard (The Humphreys Investment Co., Denver)—In this very interesting paper several brief references are made to the Humphreys spiral, a device used for cleaning fine coal. In Table I, Plants 76 and 77, data are given on spiral performance treating Raton and Trinidad coal. The fine coal, as fed to the spiral in these instances, is actually a table middling, hence the more easily treated material was previously removed and a large number of particles were present which were difficult to clean. Mr. W. M. Bertholf of the Colorado Fuel and Iron Co. presented a paper in February, 1946, Cleaning Table Middlings from a Coal Washery with the Humphreys Spiral Concentrator, from which I quote: "In considering the results of our tests it should be noted that the feed was our table middling, and that any real separation is a &apos;moral victory&apos; as there is little material that could properly be called coal and practically no heavy rock, the consequences being that previous attempts to clean the middling have not at all been successful." Referring again to Table I, Plants 72, 73, 74, and 75, these data were obtained by Yancey and Geer and others and presented at the February 1950 Meeting, AIME, in a paper entitled Laboratory Performance Tests of the Humphreys Spiral as a Cleaner of Fine Coal. Results shown for those tests involve all particles from 8 mesh through the colloids, which admittedly is not an ideal situation for spiral feed if much refuse is contained in the —80 mesh or —100 mesh size range. As an illustration of the effect of treating too broad a size range, let us consider Plant No. 75, Kentucky No. 9 seam. Spiral feed was 8 mesh x 0. Now had this been 8x100 mesh the percentage of misplaced material would have been 8.0 pct instead of the reported 15.26 pct. Similar comparisons can be made on the other data presented with respect to the spiral. Other types of equipment show a similar trend in that whenever too fine a size is treated in a given unit process the percentage of misplaced material increases. Since the spiral is working near the finer end of the size range, it will sometimes be advantageous to treat the entire range of —8 mesh material rather than to deslime and make a fair showing on, say, the +80 or + I00 mesh. Desliming is subsequently done in any case in the dewatering or thickening operation. Results obtained by spiraling any given coal depend on factors too numerous and complex to discuss here, but there are strong indications that proper preparation of feed to the spiral can improve results obtained on some of the raw coals tested. This is clearly pointed out at the end of the aforementioned paper by Yancey and Geer. "The spiral is an extremely simple device which involves no moving parts and is constructed almost entirely of unmachined castings. Since it is such an uncomplicated mechanism, operation is simple and virtually foolproof. These characteristics, which go far toward insuring low cost operation, are attractive attributes in any coal cleaning unit." Certain equipment used in conjunction with the spiral has resulted in a decrease in the percentage of misplaced material, notably in actual practice the launder screen which is used to remove objectionable high ash fines from a spiral-washed coal product. Private correspondence with the U. S. Bureau of Mines has intimated that an additional yield of coal is possible by flotation of the spiral middling. Possible future improvements and developments may result from other methods now under consideration. Finally, some compromise must be made between the best metallurgical performance and the best practical or economical results. Mr. Lyons emphasizes in his summary this objective of overall economy in selection of equipment. G. B. Walker (American Cyanamid Co., Stamford, Conn.)—I had the pleasure of reviewing the draft of this paper and my curiosity was aroused by the data given for Tromp plants, in that all of the examples shown appeared to be 2-product separations, whereas all the Tromp plants with which I am familiar have been 3-product units. The data given for plants No. 101 and 102 appear to be taken from Tromp&apos;s brochure on his process and represent the results obtained at the Dominale plant in Holland which was operated for many years by Mr. Tromp. The plant, which was designed to treat 58 tons per hr, was sampled while treating 35 tons per hr of 3Y4x-in. coal. Example 101 appears to conform to what would result if the middling product were calculated into the refuse product, while Example 102 represents the calculation of the middling into the coal product. It is believed that Examples 103 and 104 represent the operation of the Willem-Sophie Mine in Holland recalculated on the same basis. In checking the English examples given by numbers 14, 15, 16, and 17, the same procedure seems to have been followed. These results have, apparently, been taken from an article in Colliery Engineering in August 1941, describing the initial operation of the Williamthorpe Colliery of the Hardwick Colliery Co. Two vessels are employed in this plant, one to treat soft coal and one to treat hard coal. Example No. 14 presents the results that could be obtained from the soft coal bath if the middling were calculated into the refuse, and Example 15 the results when the middling is calculated into the coal. Examples 16 and 17 represent the same expedient in the case of the hard coal bath. Of interest to this discussion is the fact that during the past year the Simon-Carves Engineering Co. in England has installed in the Williamthorpe plant their new "Sim-Car" medium cleaning system which is based on magnetic extraction and control and which is licensed under the Heavy-Media Separation Processes patents by the American Zinc, Lead and Smelting Co. This system has been described in the December 1951, issue of Colliery Engineering. It is reported that since the Williamthorpe Colliery was changed from the Tromp system of medium cleaning to the Magneto-Motive method of medium control the opera-

Jan 1, 1953

By J. W. Spretnak, G. Sachs

The: iron-rich iron-nickel alloys have attracted considerable academic interest in recent years. The carbon-free alloys are of minor practical importance, but they are the base of many alloys with various outstanding properties. The iron-nickel alloys, therefore, have been investigated extensively regarding both their structures and their properties. The researches on these alloys up to 1938 have been collected and critically reviewed by J. S. Marsh,l and will be discussed in some detail in the sections of this paper dealing with specific subjects. These numerous investigations have not succeeded in establishing the equilibrium conditions in this system. Alloys containing more than a certain amount of nickel (8 to 10 per cent Ni) undergo the allotropic transformation extremely sluggishly, both on heating and cooling, showing a large hysteresis," which is not dependent upon the rate of cooling and persists even with very slow rates of cooling.3 Honda4 and Merica4 have therefore resigned themselves to proposing a diagram (Fig. I) for practical use, illustrating the structural relations under commercial conditions instead of attempting to establish the true equilibrium diagram. Marsh is less pessimistic and suggests an equilibrium diagram (Fig. 2) which conforms approximately to the facts known about this system. Recent X-ray investigations by Owen-Sully5 and Bradley-Gold-schmidt6 on powdered alloys indicate that the previous work on the iron-nickel system yielded very incomplete results. These investigators agree (Figs. 3 and ,+) that alloys in the powdered form containing more than 8 per cent and up to about 35 per cent Ni decompose into a stable heterogeneous mix-

Jan 1, 1941

By G. Sachs, J. W. Spretnak

The: iron-rich iron-nickel alloys have attracted considerable academic interest in recent years. The carbon-free alloys are of minor practical importance, but they are the base of many alloys with various outstanding properties. The iron-nickel alloys, therefore, have been investigated extensively regarding both their structures and their properties. The researches on these alloys up to 1938 have been collected and critically reviewed by J. S. Marsh,l and will be discussed in some detail in the sections of this paper dealing with specific subjects. These numerous investigations have not succeeded in establishing the equilibrium conditions in this system. Alloys containing more than a certain amount of nickel (8 to 10 per cent Ni) undergo the allotropic transformation extremely sluggishly, both on heating and cooling, showing a large hysteresis," which is not dependent upon the rate of cooling and persists even with very slow rates of cooling.3 Honda4 and Merica4 have therefore resigned themselves to proposing a diagram (Fig. I) for practical use, illustrating the structural relations under commercial conditions instead of attempting to establish the true equilibrium diagram. Marsh is less pessimistic and suggests an equilibrium diagram (Fig. 2) which conforms approximately to the facts known about this system. Recent X-ray investigations by Owen-Sully5 and Bradley-Gold-schmidt6 on powdered alloys indicate that the previous work on the iron-nickel system yielded very incomplete results. These investigators agree (Figs. 3 and ,+) that alloys in the powdered form containing more than 8 per cent and up to about 35 per cent Ni decompose into a stable heterogeneous mix-

Jan 1, 1941

By George S. Rice

THE A.I.M.E. Ground Movement and Subsidence Committee, pro- posed in 1920, held its first technical meeting in February 1923, under the able chairmanship of Mr. H. G. Moulton. The following list of papers and discussions, indicating the scope of the problems and relation to various conditions and method of mining, were given at that meeting by the distinguished mining engineers: J. Parke Channing, on Subsidence at Miami, Arizona; Howard N. Eavenson, on Mining an Upper Bituminous Seam after a Lower Seam Has Been Extracted; J. J. Rutledge, on Subsidence in Two Oklahoma Coal Mines; Benjamin F. Tillson, on Caving Cracks at the Franklin Mine, New Jersey; Dr. F. W. McNair, on the Dome Theory; William Kelly, on disadvantageous effects in Mining and Back-filling Working Upward a Steep-Pitching Iron-ore Bed; Eli T. Conner, on the good results of Back-Filling by Hydraulic Means in Preventing Destructive Subsidence in the Anthracite District; Thomas H. Claggett, on the merit of Systematic Pillar Drawing in Preventing Cracks in an Upper Seam; Henry H. Otto, successful results in the anthracite district in Mining Lower Seams before Upper Seams; Douglas Bunting, on Leading Factors Incident to Successful Mining of an Overlying Seam; Edwin Ludlow, on there being "less damage to buildings when there was complete removal of coal with complete packing than when room and pillar is used without extracting the pillars"; Edward O&apos;Toole on "bumps" in eastern Kentucky mines, which he thought were the result of geologic stresses: H. A. Buehler, on Upheaval of Surface in an Illinois Case in Advance of the Face; and R. Dawson Hall, on The Mechanics of Subsidence from Mining. The author of this paper discussed various kinds of problems of ground movement and subsidence in both metal mining and coal mining; the production of great landslides by workings near an outcrop, as at Turtle Mountain, Alberta, Canada; and general

Jan 1, 1939

By Garth M. Crosby

Hugh E. McKinstry (Professor of Geology, Laboratory of Mining Geology, Harvard University, Cambridge, Mass.) Pre-Cambrian age for the Coeur d&apos;Alene mineralization, as indicated by isotope studies and recently discussed by Silverman, Long, and Kulp&apos; would explain some features of the mineralogy of the district that have long been a puzzle. In the Silver Belt, especially in the Sunshine mine, lead-zinc min erali zation passes downward into tetrahedrite ore. Although commercially speaking this is a rich silver zone, the silver is, quantitatively, a mere impurity amounting to a small fraction of 1 pct. In effect the zonal change is from lead-zinc down into copper mineralization—-the usual zonal change that occurs in many districts. In the Burke-Mullan portion of the district, on the other hand, lead-zinc ore does not pass downward into copper mineralization of the Sunshine type. Instead, pyrrhotite appears in depth while the tenor in lead and zinc declines. The change occurs at increasingly greater depth away from the Gem stocks, deepening irregularly by some 3000 ft within two to four miles. As noted by Crosby, biotite, grunerite, and garnet appear in the deep zone. The marked difference between this apparent zonal change and the more nomal change to a copper zone is quite explainable if already existing pre-Cambrian veins have been locally metamorphosed by a Tertiary intrusive. The chief obstacle to this explanation is the evidence that mineralization cuts Laramide intrusives, but evidence on this point is conflicting as indicated by Crosby&apos;s observations and summary. This is not the first instance of a problem in determining the time-relationship of mineralization to a spatially associated intrusive. At the Noranda mine veins of chalcopyrite extend into a diabase dike which apparently cuts the ore, although Price2 concludes that the ore is later. However, at the Normetal mine diabase of a similar dike is thought3 to intrude the orebody but is cut by stringers of chalcopyrite. In the Sullivan Mine, B. C.,4 galena follows a fracture in a larnprophyre dike which, itself, cuts the main orebody. In the Sudbury district dikes of olivine diabase are clearly younger than the nickel ore, yet where they cut the Creighton orebody they contain stringers of chalcopyrite. In the laboratory, Hawley5 has developed veinlets of sulfide (chalcopyrite) it] silicate gangue by heating specimens of ore in a stream of H2S at 410 °C. From this and other evidernce. it seems clear that sulfides can be transferred from one site to another — at least through short distances — at temperatures well below their melting points. It would seem then that even if sulfide Mineralization in the Gem stocks can be shown unequ ivocably to be later than the intrusive the possibility of "remobiliza tion" need not be more than local. Thus the zonal relationships are quite in accord with a pre-Cambrian age for original deposition of the lead, zinc, copper, silver, and uranium in the Coeur d&apos;Alene district. REFERENCES 1. A. Silverman, A. Long, and J. L. Kulp: Discussion of: The Gem Stocks and Adjacent Orebodies, Coeur d&apos;Alene District, Idaho. Mining Engineering, May 1960, pp. 470-471; AME Trans., 1960, vol. 217, p. 117. 2. Peter Price: Geol. & O. D. at the Home Mine, Noranda, Quebec. Can. Inst. M & M Bull 263, 1934, p. 108; also,Trans. CIMM 1939, pp. 108-140. 3. w. L. Brown Nometal Mine in structural Geology of Canadian Ore Deposits, Montreal, 1948, p. 690. 4. C. O. Swanson and H. C. Gunning: Geology of the Sullivan Mine. Can. Inst. Mining & Met. Trans. vol. 48, 1945, p. 653. 5. J. E. Hawley: Heat Effects on Sulphides and Possible Applications. Univ. Toronto Studies, Geol. Ser. No. 46, 1941, p. 34.

Jan 1, 1961

By George S. Rice

The A.I.M.E. Ground Movement and Subsidence Committee, proposed in 1920, held its first technical meeting in February 1923, under the able chairmanship of Mr. H. G. Moulton. The following list of papers and discussions, indicating the scope of the problems and relation to various conditions and method of mining, were given at that meeting by the distinguished mining engineers: J. Parke Channing, on Subsidence at Miami, Arizona; Howard N. Eavenson, on Mining an Upper Bituminous Seam after a Lower Seam Has Been Extracted; J. J. Rutledge, on Subsidence in Two Oklahoma Coal Mines; Benjamin F. Tillson, on Caving Cracks at the Franklin Mine, New Jersey; Dr. F. W. McNair, on the Dome Theory; William Kelly, on disadvantageous effects in Mining and Back-filling Working Upward a Steep-Pitching Iron-ore Bed; Eli T. Conner, on the good results of Back-Filling by Hydraulic Means in Preventing Destructive Subsidence in the Anthracite District; Thomas H. Claggett, on the merit of Systematic Pillar Drawing in Preventing Cracks in an Upper Seam; Henry H. Otto, successful results in the anthracite district in Mining Lower Seams before Upper Seams; Douglas Bunting, on Leading Factors Incident to Successful Mining of an Overlying Seam; Edwin Ludlow, on there being "less damage to buildings when there was complete removal of coal with complete packing than when room and pillar is used without extracting the pillars"; Edward O&apos;Toole on "bumps" in eastern Kentucky mines, which he thought were the result of geologic stresses: H. A. Buehler, on Upheaval of Surface in an Illinois Case in Advance of the Face; and R. Dawson Hall, on The Mechanics of Subsidence from Mining. The author of this paper discussed various kinds of problems of ground movement and subsidence in both metal mining and coal mining; the production of great landslides by workings near an outcrop, as at Turtle Mountain, Alberta, Canada; and general

Jan 1, 1940

By George S. Rice

The A.I.M.E. Ground Movement and Subsidence Committee, proposed in 1920, held its first technical meeting in February 1923, under the able chairmanship of Mr. H. G. Moulton. The following list of papers and discussions, indicating the scope of the problems and relation to various conditions and method of mining, were given at that meeting by the distinguished mining engineers: J. Parke Channing, on Subsidence at Miami, Arizona; Howard N. Eavenson, on Mining an Upper Bituminous Seam after a Lower Seam Has Been Extracted; J. J. Rutledge, on Subsidence in Two Oklahoma Coal Mines; Benjamin F. Tillson, on Caving Cracks at the Franklin Mine, New Jersey; Dr. F. W. McNair, on the Dome Theory; William Kelly, on disadvantageous effects in Mining and Back-filling Working Upward a Steep-Pitching Iron-ore Bed; Eli T. Conner, on the good results of Back-Filling by Hydraulic Means in Preventing Destructive Subsidence in the Anthracite District; Thomas H. Claggett, on the merit of Systematic Pillar Drawing in Preventing Cracks in an Upper Seam; Henry H. Otto, successful results in the anthracite district in Mining Lower Seams before Upper Seams; Douglas Bunting, on Leading Factors Incident to Successful Mining of an Overlying Seam; Edwin Ludlow, on there being "less damage to buildings when there was complete removal of coal with complete packing than when room and pillar is used without extracting the pillars"; Edward O&apos;Toole on "bumps" in eastern Kentucky mines, which he thought were the result of geologic stresses: H. A. Buehler, on Upheaval of Surface in an Illinois Case in Advance of the Face; and R. Dawson Hall, on The Mechanics of Subsidence from Mining. The author of this paper discussed various kinds of problems of ground movement and subsidence in both metal mining and coal mining; the production of great landslides by workings near an outcrop, as at Turtle Mountain, Alberta, Canada; and general

Jan 1, 1940

President MRS. HARRISON SOUDER south Paramus Road Ridgewood, N. J. First Vice-president MRS. ROBERT HURSH New York N. Y. Second Vice-president MRS. RICHARD LLEWELLYN LLOYD Great Neck, L. I&apos;. N. Y. Third Vice-president MRS. PERCY E. BARBOUR New York N. Y. Fourth Vice-president MRS. E. P. MATHEWSON Tucson Ariz.

Jan 1, 1937

By Glenn Keep

THIS paper is not an announcement of the successful conclusion of the Cerro de Pasco Copper Corporation&apos;s pacos-pyrite problems, but merely a description of the commercial-scale, intermittent-roasting operations conducted by the writer, J. H. Lucas and others of the staff. It was prepared by request, for presentation at the February meeting of the Institute. The results obtained in Peru confirm the 1-ton-a-day experiments completed about three years ago at Kearny, N. J. by C. C. Gordon and Mr. Lucas, where it was first demonstrated that a mixture of about 80 per cent. pacos ore with 10 per cent. pyrite ore and 10 per cent. salt could be roasted intermittently in a small 1-ton-a-day Holt-Dern furnace without extraneous fuel, producing porous calcine that could be leached rapidly. Mr. Keep and his staff, by successfully introducing improvements in the construction of the commercial furnace and in their handling of material, have established beyond doubt a low cost for roasting. The other steps in the process of treating pacos and pyrite ores have not as yet been demonstrated as sufficiently conclusive to warrant their acceptance for a permanent plant.

Jan 1, 1929

By W. M. Raynor

LARGE quantities of "midnight oil" have been consumed by researchers in attempting to develop a process to produce cold ductile zirconium at low cost. The tantalizing facts that zirconium is a bright, silvery, tarnish-proof metal and is 2 1/2 times as abundant in the earth&apos;s crust as copper, and thirteen times as plentiful as lead have resulted in much speculation on uses, ranging from automobile radiator grills to kitchen sinks. but unfortunately no low-cost process of producing it has so far been found. In the case of zirconium, we cannot say that "virtue is its own reward" for the principal virtues of the metal, namely, corrosion resistance at ordinary temperatures and ability to absorb gases at high temperature, are the very characteristics that defeat all of the usual recovery methods such as sintering, plating, or direct chemical reduction. The only method giving a pure metal sufficiently low in oxides, nitrides, etc. to be truly cold-malleable is the one developed by Van Arkel and DeBoer in 1925. This process involves decomposition of zirconium tetraiodide in contact with a hot filament and pre

Jan 1, 1947

By Donald B. Evans, Robert D. Pehlke

The solubility of nilrogen in liquid binary alloys of iron with Litanium. zivconium, columbium, vanndiurn, and tantalum was measured for alloy composiLions up to the solalbility limils of lhe alloy nitrides. All five alloying agents were found to decrease markedly the activity coefficient of nitrogen in liquid ivon. The metal/nitvogen mole ralios in the alloy nitrides formed were generally .found to be slighlly greater than 1.0, but in no case greater than 1.5. From the experimental data, the standard free energies of fortmation of titanium and zir-conium nitrides have been calculated for the Lemperaluve range 1550° to 1750 C. The solublily Products for columbium, tantalum, and vanadium nitrides are also reported. A number of research investigations have examined the effect of refractory metals on the solubility of nitrogen in liquid iron. Although data on zirconium are not available, investigators are in agreement that titanium, vanadium, columbium, and tantalum markedly increase the solubility of nitrogen in liquid iron. This fact alone makes desirable the acquisition of thermodynamic data for these elements in liquid iron. Since refractory metals are known to be stable nitride formers, they have been suggested as steel denitrifying agents, and some of their nitrides have recently been considered as containment materials for liquid iron and iron alloys. Most available thermodynamic data for these metals relate to their dilute concentrations, but effective thermodynamic treatment of these applications requires data at concentrations near the solubility limit of the alloy nitride. Although some work has been done at relatively high alloy concentrations in liquid iron (particularly for vanadium 2,3 and titanium 2,4), the results have been somewhat contradictory. Disagreement may be partly attributed to the fact that the compositions of most refractory metal nitrides have been shown to be nonstoichiometric, and to vary 2,5-8 depending on the temperature and nitrogen gas pressure with which the solid nitride phase is in equilibrium. One purpose of this study consequently has been to determine the compositions of the refractory metal nitrides precipitated from a liquid iron solution. EXPERIMENTAL PROCEDURE Rao and Parlee2 and Evans and Pehlke 9 have discussed the technique for measuring the solubility product of an alloy nitride phase in liquid iron by finding the point of departure of the nitrogen solubility from Sieverts&apos; law. The method consists of measuring the solubility of nitrogen in a melt of iron containing a known concentration of a second metal as a function of the nitrogen gas pressure over the melt. In this study the second metal was one of the refractory metals titanium, zirconium, columbium, vanadium, or tantalum. When the nitrogen pressure at which the refractory nitride forms is reached, a deviation of the measured solubility of nitrogen in the melt from Sieverts&apos; law is observed in the form of a "pressure halt." The concentration of nitrogen in the melt associated with this breakpoint in the nitrogen-absorption curve is then used to calculate the nitride solubility. The Sieverts method was used to measure nitrogen solubility as a function of nitrogen pressure and temperature. The experimental equipment for this technique has been previously described in detail. 1,9 Charge materials used were vacuum-melted high-purity iron (Ferrovac-E) and the best commercial grades of the refractory metals obtainable (in all cases at least 99.8+ pct pure). Recrystallized alumina crucibles were used to hold all melts except those containing zirconium, for which zirconia crucibles were necessary. Temperatures were measured by a disappearing-filament type optical pyrometer sighted vertically downward on the melt surface through a 1/4-in.-diameter sight hole in the crucible lid. By means of a technique previously described, 9 in which the refractory-metal nitride was precipitated at one temperature then redis-solved by raising the temperature 50°C and precipitated again at a higher temperature, it was possible to obtain data over a temperature range of up to 200°C on a single melt. It was found that this technique could not be used with melts containing zir-

Jan 1, 1965

By Benjamin Smith Lyman

The question of the original extent of the anthracite-beds of Pennsylvania has often been raised; and even discussed with reference to the probability of their present existence under the New Red, a matter of immense practical importance. So high an authority as my revered master, J. P. Lesley, Honorary

Jan 1, 1903

By Earl Bardwell

(Butte Meeting, August, 1913.) THE structural relations existing between cuprous oxide and copper were first systematically studied by Heyn1, who suggested that a study of the microstructure of refined copper might be substituted for the analytical methods in vogue for determining the oxygen content of copper coming .;from the refining furnace. Hofman, Green and Yerxa,2 in their paper A Laboratory Study of the Stages in the Refining of Copper, working along the lines suggested by Heyn, showed that a study off the microstructure could be made to yield a correct estimate of the oxygen content of the specimen of refined copper under examination. In order to determine the oxygen content of the specimen of refined copper under examination a photomicrograph was first made. From the relative areas of copper and eutectic, the percentage of cuprous oxide and the corresponding percentage of oxygen were then readily calculated. It was found that the values for oxygen thus obtained corresponded closely with the analytical results. With the idea of utilizing, this method of determining the oxygen content of each charge dipped from the refining furnaces at the Boston & Montana Reduction Plant, the physical testing laboratory was equipped with suitable apparatus for carrying out the work. It may be of interest to describe certain of the methods which have been worked out in, this connection and give such data as have been obtained bearing on the effect of the oxygen content of refined copper upon its conductivity.

Jan 7, 1913

By T. A. Rickard

The question of the original extent of the anthracite-beds of Pennsylvania has often been raised; and even discussed with reference to the probability of their present existence under the New Red, a matter of immense practical importance. So high an authority as my revered master, J. P. Lesley, Honorary

Jan 1, 1903

By Eugene Coste

Although some of the observers who first paid especial attention to the occurrences of oil and gas in the strata (such as Hunt in 1859, Andrews in 1861; Winchell in 1865, Mendelejeff in 1876, Höfer in 1876, Minshall in 1881, and I. C. White in 1883) seem to have been impressed with the fact that oil and gas deposits were connected with the disturbances in the rocks caused by their upheavalll yet, with the exception of Mendelejeff, and possibly Andrews, these observers do not appear to have understood what is really the one essential factor in the occurrence of oil and gas in the strata: viz., the faulting, uplifting, fracturing, fis-suring, and jointing always accompanying even slight rock disturbances, and in certain districts (petroliferous provinces)2 allowing solfataric hydrocarbon emanations to force their way up from the interior and to reach and impregnate the porous portions of sediments subjected to the disturbances. Instead of this simple explanation to account -for the observed connection between petroleum deposits and rock disturbances, most of the observers mentioned above, and many others who have foliowed them on the same lines since, have entirely reversed the problem. To them, instead of the dissemination of gases from fissures into the sediments, it presented the accumulation and concentration, according to anticlinal or other geologic structures, of oil and gas originally present throughout the whole mass of the strata where they were produced by the decomposition or distillation of organic remains. Whether this important problem involves accumulation from sources within the strata themselves, or infiltration and dissemination from outside sources, may be easily determined if all preconceived ideas are put aside and the established facts only are considered. Physical Facts Sedimentary strata are composed of alternate beds of shales, sandstones, and limestones, most of which are sufficiently close-grained to

Jan 1, 1915

By Charles A. Chase

This paper, descriptive of a single mine, is presented in the belief that it may furnish useful suggestions to mine-managers encountering similar problems; and it includes the details which will enable them to estimate the value of the methods employed—especially where these depart from common practice. Tt should be added, however, that this mine is not typical of the San Juan district, but differs markedly from neighboring mines in physical conditions and metallurgical requirements. The Liberty Bell mine is situated in San Miguel county, Colo., on the west front of the San Juan mountains, 2 miles north of Telluride. The vein was discovered in 1876 by Wm. L. Cornett, who, with subsequeilt locators, took up claims along the apex. A few hundred feet of development-work was accomplished, and a few? tons of ore were smelted or milled; but profitable working proved impossible under existing

Jan 1, 1912

By S. W. Nabbs, W. D. Bachman, A. W. Last

A study has been made of wet, autogenous grinding of disseminated copper ores, including testing of a large number of samples from. Kennecott Copper Corp.&apos;s Chino mine. The grindability of the various samples was found to vary over an extremely wide range, even among samples taken from diflerent locations within the same ore body. These variations in grindability can be qualitatively correlated with the composition of the rock and the fracturing and alteration that had occurred. Because of the large-scale nonhomogeneity of disseminated copper ore bodies, extensive and careful testing of autogenous grinding is needed. An accurate correlation of the grinding data from various samples with the geology of the ore body and with mining plans will indicate if variations in grinding mill throughput can be avoided in practice by mixing or blending of mill feed and if, therefore, autogenous grinding can be applied successfully. In the past 15 years, comminution by primary autogenous grinding has been investigated and applied economically in the minerals industry, particularly in iron-ore processing. Successful application of primary grinding is described by A. A. Dor,l.&apos; P. B. Dettmer,334 R. R. Turner, and W. F. McDermott." other authors describing the advantages of primary grinding include H. Hardinge,&apos; R. T. Hukki,&apos; D. S. Coyle" and F. C. Bond,"," to mention only a few. For the past several years, Kennecott Copper Corp.&apos;s Metal Mining Div. Research Center has been investigating primary grinding of disseminated copper ores. Both fully autogenous and semi-autogenous grinding has been explored. Ores from three of Kennecott&apos;s western operating properties and from several development properties have been tested. Host rocks include diabase, schist, silicated and argillaceous limestones, shale, granite porphyry, quartzite, and granodiorite. The object of this paper is to supplement the general knowledge in the field of primary grinding by presenting information gained from the studies with the various disseminated copper ores. Data are presented which show that carefully considered test programs are required to determine the practicality of applying autogenous grinding to a specific mining-beneficiation operation. Particularly this is so if more than one rock type occurs within an ore body or if there are wide variations in the degree of rock alteration within a deposit. Extensive sampling and subsequent testing of the ores within a mine are required if serious pitfalls are to be avoided and good engineering data acquired. We hope that this presentation will stimulate studies to increase the understanding of the fracturing process applicable to large pieces of rock, a factor which is important in autogenous grinding. Test Facilities and Procedures Both pilot-scale and full-scale test facilities were used to investigate primary grinding characteristics of the disseminated copper ores. A 6-ft Hardinge Cascade mill, a 24-ft Hardinge Cascade mill, and a 5-ft Aerofall mill were used in the studies. The Cascade mills were operated wet, while the Aerofall mill was operated both wet and dry. The Cascade mills were operated both for fully autogenous and for semi-autogenous grinding; the Aerofall mill was operated only semi-autogenously. Fully autogenous grinding, as the term is used in this presentation, is defined as the direct grinding of coarsely crushed rock by the action of the rock mass. Semi-autogenous grinding is defined as the grinding of coarsely crushed rock with the rock mass supplemented by a steel ball charge. Most of the test work was done using the 6-ft Cascade mill, operated under fully autogenous grinding conditions. Only limited testing was conducted with the 5-ft Aerofall mill and only one ore was tested using the 24-ft Cascade mill. This presentation is concerned, therefore, primarily with fully autogenous, pilot-scale grinding in the Cascade mill. Fig. 1 presents a diagram of the test facilities used with the 6-ft Cascade mill. Principal test equipment consists of a 6-ft Cascade mill, an 18-in. spiral classifier, an elevator, a 2 x 9-ft belt feeder, a conventional integrating kilowatt-hour meter, and a recording wattmeter. In testing, feed charges, adjusted as to weight, were deposited as evenly as possible on the belt feeder every 15 min. The weight of each charge was adjusted to maintain a mill charge of 27 to 30% of mill volume. The classifier was adjusted to obtain the desired size-consist of the final product, generally at 20% + 100 mesh. After equilibrium was established in the circuit, the feed, mill discharge, classifier sand, and classifier overflow were sampled and their size distributions determined. During the sampling periods, the power drawn by the mill was measured to determine the energy consumed in the reduction of the size consist of the ore solids. Fully Autogenous Pilot Grinding Tests on Various Kennecott Ores Typical test results obtained in the 6-ft Cascade mill with samples from Kennecott&apos;s Ray Mines Div., Chino Mines Div., Utah Copper Div., and a development property designated as Mine A are presented in Table 1. As shown, the ores that were ground most easily in the pilot-scale mill were composite mine samples obtained

Jan 1, 1971