By J. F. Butler, H. W. Paxton

The vapor pressures of manganese in equilibrium with several alloys in the iron-manganese-carbon system between 1200° and 1275°K have been measured using the Knudsen effusion technique in conjunction with a vacuum microbalance. The effect of orifice area of the effusion cell upon the measured pressure has been determined. The binary iron-manganese system shows small negative departures from ideality, and the system of mixed carbides, (Fe, Mn)7C3, in equilibrium with graphite behaves ideally. THIS work is a continuation of the investigations in which the Knudsen effusion method has been used to determine thermodynamic activities in systems and at temperatures of interest to metallurgists. In a previous publication,' the free energy of formation of Mn7C3 was determined and some preliminary work on the solution behavior of this carbide with the hypothetical "Fe7C3" was reported. The present work deals with this latter topic and also includes data on the binary ir-on-manganese system. EXPERIMENTAL METHOD The Knudsen effusion method was used to measure the vapor pressure of manganese in both the alloy and carbide sections of this investigation. This dynamic method of vapor pressure measurement presents a problem when studying solid alloy systems in which one of the components has a much larger vapor pressure than the others. Over-all depletion of the alloy in the most volatile component will occur during evaporation so that the pressure of that component will decrease. Even more serious than the over-all concentration change is the surface depletion of volatile component in the alloy brought about by the slow rate of diffusion of this component from the interior to the surface of the solid particle. Since knowledge of this surface composition is necessary in order to relate it to the activity determined through the measurements, changes in surface composition from the analyzed bulk composition are to be avoided in dynamic vapor pressure studies of solid alloys. The system under investigation in this study presents the problem of surface depletion of manganese since its pressure at 1230°K is 105greater than iron and 1020 greater than carbon. Since the existence of a volatile manganese carbide had been ruled out previously,' the high manganese pressure relative to iron and carbon insured that the only species leaving the effusion cell was manganese. Therefore, the effusing species required no analysis so that the manganese pressure was determined directly from the weight loss of the effusion cell. In order to detect small weight losses near the beginning of effusion, a vacuum microbalance was used to weigh the cell continually. These initial weight loss data allowed the rate of manganese effusion to be determined before the surface of the alloy became depleted in manganese. The apparatus used in this investigation is shown in Fig. 1. Temperature was measured using chro-

Jan 1, 1962

Jan 1, 1900

By Jerome F. Kuzmick

Condusions. From the work on aluminum powder, the following general con clusions can bc drawn: I. The physical properties of aluminum compacts, such as density. strength and ductility, increase with increasing pressure, up to the practicable pressure limits. 2. Good properties ill aluminum con pacts can be secured only by the use of high pressures, because it is neccssary to rupture the refractory oxide film on aluminum powder. 3. Considerable softening of the specimens occurs upon sintering. regardlers of the pressure used. General Conclusions 1. For relatively short-time sintering. molding pressure is a very important factor in the final physical properties of the sintered specimens. 2. The effect of pressure. is difierent for each metal, so that few general rules can be drawn that would apply to all metals. 3. In many cases, fur a particular metal powder and sintering temperature there is a critical pressure at which the best physical properties can be obtained. 4. The principles of cold work and in nealing and their effect on grain structure applied to massive metal also holds true for sintered metals. 5. Particle size, at least for electrolytic iron powder, does not have a. great effect on ultimate grain six. DISCUSSION [E. E, Schumacher presiding V.. V. Crane. *—I was particularly impressed with Dr. Kuzmick's work on tin IF not the illustration, particularly the Second one. a very good illustraition of hot preessing. in that

Jan 1, 1945

By J. D. Rice, S. C. Pitzer, C. E. Thomas

Interpretation of pressure build-up data obtained in the conventional manner has often been difficult because of the deviation from theoretical behavior. Major causes of this deviation have been attributed to damage and afterflow, and to fluid redistribution in the wellbore which, in extreme cases, can result in a pressure hump in the early portion of the build-up curve. Theoretical investigations show that bottom-hole pressure is definitely influenced by phase redistribution in the tubing column during surface shut-in tests, and that the magnitude of the effect is sensitive to the producing gas-oil ratio and stabilized rate of flow in the well. For field experiments a wire-line tubing packer, which can be run in the tubing against a stabilized flow rate, was developed for bottom-hole shut-in tests. By use of this bottom-hole .shut-in method, pressure humps previously observed in surface shut-in tests were completely eliminated and the effects of afterflow minimized. Analog and digital computer studies have been made to obtain theoretical curves for comparison with field curves, and remarkable agreement between the results of bottom-hole shut-in tests and theoretical curves has been obtained. INTRODUCTION Pressure build-up data from shut-in wells have been used by the petroleum industry to determine the permeability of the formation, to estimate wellbore damage, to evaluate the static reservoir pressure and to speculate reservoir volume. Calculation of these factors is based on methods of analysis developed for theoretical systems whose build-up curves have a charac- teristic shape when the wells are shut-in at the sand faCe.1,2,3,5,8,10 However, field curves obtained by conventional surface shut-in methods do not always exhibit this characteristic. Such factors as stratification, rock heterogeneities and irregular reservoir geometry can cause the character of a build-up curve to deviate from that predicted by theory for a simple system. In addition, all field build-up data are affected by the methods utilized in obtaining the measurements. Conventional surface shut-in techniques allow two effects to occur which contribute directly to the manner in which pressure builds up at the sand face. The first, afterflow, has been recognized for some time and methods are available for estimating the magnitude of its effect and for correcting its influence.' The second, phase segregation in the tubing column after shut-in, has been reported only recently and appears to exert a considerable influence on the character of field build-up curves.!' In extreme cases, phase segregation can produce "pressure humps" in the early portion of the build-up curve. Such curves have been considered anomalous and have defied analysis. It is the purpose of this paper to discuss the effect of phase segregation in the tubing string during build-up and to present a bottom-hole shut-in technique for obtaining field build-up data which minimizes the influence of afterflow and eliminates phase segregation effects. It will be shown that reliable reservoir information can be calculated from build-up measurements obtained using this method, even though conventional surface shut-in tests on the same wells yield anomalous data. DISCUSSION OF PHASE REDISTRIBUTION EFFECTS Some of the effects of phase redistribution on pressure build-up curves have been described previously by Matthews and Stegemeier" who have presented evidence that phase segregation is responsible for the pres-

By R. E. Old

Through the use of pressure and production records, formation properties and bottom-hole sample data, the performance of an oil reservoir may be studied analytically to define and evaluate the natural forces acting on and within the reservoir. Use is made of material-halance methods and the equations for natural water encroachment. to estimate reserves. Methods for calculation of pressures are given. A study of the Jones sand, Schuler field, Arkansas, has been made and is given here to illustrate the value of the methods discussed. Introduction With the decreasing rate of discovery of new oil reserves, attention is necessarily focused on the efficient development, evaluation, and production of existing reserves. From the nation's viewpoint, the necessity of conserving resources is obvious. From the operator's viewpoint, the problem is to lengthen the period of profitable operation, in an attempt to increase the return on his investment. To do this the operator must take advantage of the natural forces acting on and within the reservoir. Natural water encroachment, the nemesis of profitable operation in the past, can be and is being harnessed to produce a greater oil recovery during the stage of flowing production. Proper evaluation of water encroachment rates and a fuller under- standing of reservoir behavior dictate the appropriate production procedures. Complacency in hit and miss production is obsolete. Oil production must and will approach the efficiency of other businesses, such as manufacturing. A manufacturer will not place an article on the market until he has fully investigated the processes involved, additional investment in equipment, costs of production, and expected profits. These may be modified by actual experience at a later date, but at least he begins with an idea of expected return. It is just as logical that an oil operator should investigate these same factors during the development and the early period of production of an oil reserve. The complexity of the problems existing in oil reservoirs should not be underestimated. Conversely, they should not be regarded as insoluble. Many completely defy solution, but there are others that can be solved completely or attacked intelligently to yield approximate results. The petroleum engineer has many tools, both figuratively and literally, at his disposal. Physical data such as core analyses, electrical logs, bottom-hole sample analyses, and bottom-hole pressures are accumulated extensively. Advances in the analytics of fluid flow have kept pace with the advances in measurement of physical data. It is the purpose of this paper to show how some of these records may be analyzed to define certain phases of reservoir behavior.

Jan 1, 1943

By R. E. Old

Through the use of pressure and production records, formation properties and bottom-hole sample data, the performance of an oil reservoir may be studied analytically to define and evaluate the natural forces acting on and within the reservoir. Use is made of material-halance methods and the equations for natural water encroachment. to estimate reserves. Methods for calculation of pressures are given. A study of the Jones sand, Schuler field, Arkansas, has been made and is given here to illustrate the value of the methods discussed. Introduction With the decreasing rate of discovery of new oil reserves, attention is necessarily focused on the efficient development, evaluation, and production of existing reserves. From the nation's viewpoint, the necessity of conserving resources is obvious. From the operator's viewpoint, the problem is to lengthen the period of profitable operation, in an attempt to increase the return on his investment. To do this the operator must take advantage of the natural forces acting on and within the reservoir. Natural water encroachment, the nemesis of profitable operation in the past, can be and is being harnessed to produce a greater oil recovery during the stage of flowing production. Proper evaluation of water encroachment rates and a fuller under- standing of reservoir behavior dictate the appropriate production procedures. Complacency in hit and miss production is obsolete. Oil production must and will approach the efficiency of other businesses, such as manufacturing. A manufacturer will not place an article on the market until he has fully investigated the processes involved, additional investment in equipment, costs of production, and expected profits. These may be modified by actual experience at a later date, but at least he begins with an idea of expected return. It is just as logical that an oil operator should investigate these same factors during the development and the early period of production of an oil reserve. The complexity of the problems existing in oil reservoirs should not be underestimated. Conversely, they should not be regarded as insoluble. Many completely defy solution, but there are others that can be solved completely or attacked intelligently to yield approximate results. The petroleum engineer has many tools, both figuratively and literally, at his disposal. Physical data such as core analyses, electrical logs, bottom-hole sample analyses, and bottom-hole pressures are accumulated extensively. Advances in the analytics of fluid flow have kept pace with the advances in measurement of physical data. It is the purpose of this paper to show how some of these records may be analyzed to define certain phases of reservoir behavior.

Jan 1, 1943

By Ling Yang, John Henderson

Self-diffusion coefficients of copper in molten copper have been measured by the capillary reservoir method in the temperature range 1140o to 1260°C. The results can be represented by the equation D = [(1.46 * 0.01) x 10-3) exp [(-9710 * 710)/RT] cm2/sec. The energy of activation agrees within the limit of experimental uncertainty with that for viscous flow. The relationship between the diffusivity and coefficient of viscosity is best described by the equation D = kT/4pnr cm2/sec. MEASUREMENT was made of the self-diffusion coefficient of copper in molten copper in the temperature range 1413º to 1533ºK, using the capillary reservoir technique and CU64 as the radioactive tracer.The procedures for filling the capillaries, making the diffusion run and evaluating Dcu from the counting results were the same as described previously.1,2 All experimental operations involving the melt were carried out in a purified argon atmosphere. A graphite crucible, enclosed in a McDanel tube, was used as a container for the melt because of its satisfactory nature as a refractory material and the low solubility of carbon in copper. Graphite was also used for the capillary material. A McDanel thermocouple sheath, to which graphite radiation shields were affixed, was used to hold the capillaries. By moving this sheath through a rubber seal at the top of the McDanel tube, the capillaries could be lowered into or raised out of the melt. A Globar furnace with a constant temperature zone (± 2°C) of 2 in. was used to heat the assembly. The temperature of the furnace was the equilibrium value corresponding to a given setting of the transformer. Temperature was measured with a Pt-10 pct Rh/Pt thermocouple and varied during a run

Jan 1, 1962

Discussion of the paper of Robert Henry Lee, presented at the New York Meeting, October, 1913, and printed in Bulletin No. 82, October, 1913, pp. 2515 to 2522. J. E. JOHNSON, JR., New York, N. Y.:-This subject is of great and increasing importance, as the exhaustion of the deposits of ore of ideal character compels the iron industry to turn more and more to those which are less desirable on account of physical structure as well as analysis. Thus there has come about the use of the Mesabi ores in this country and also of the Minette ores in Europe, which produce far greater percentages of flue dust than did the lumpy ores first used. It is a matter of common knowledge that the utilization of this flue dust, containing commonly 50 per. cent. or more of metallic iron, has been a problem very difficult and tedious of solution. The number and variety of the solutions now offered is a sufficient proof of this. . I have no intention of going into the merits or demerits of any of these processes as such, but there are certain considerations concerning the effect of their product on the operation and fuel economy of the blast furnace which I believe to be new and which I desire to bring out. There are two methods, so different as almost to be direct opposites of each other, whereby an ore may exercise an unfavorable effect on the economy of the blast furnace. The first of these is well known and results from the ore being refractory and highly resistant to the action of the reducing gases of the blast furnace. This results in its being incompletely reduced when it reaches the zone of fusion and in the reduction being finished by the direct action of carbon in the lower portion of the furnace. This is so well understood as to need little elaboration or comment. There is, however, another action which may be equally as fatal to the economy of the furnace as the foregoing, and as this point is, to the best of my knowledge, not generally appreciated, it is one upon which I desire to lay particular stress. This consists in the ore being, in a sense, too reducible.

Jan 12, 1913

By John C. Calhoun, Frank T. Bethel

The application of a method for analyzing pressure build-up curves to determine the effective permeability in the Spraberry is presented. Sixteen upper Spraberry wells of the Driver area arc analyzed and show variations in the in-place effective permeability of 2 to 183 md. Since these value- are much larger than the .5 md. or less reported for the matrix rock. a large part of the vertical fractures noted in Spraberry cores- must be considered native to the formation. The effectiveness of the well fracture treatment in connecting the well bore to the native fracture system is analyzed by comparison of the effective permeability as determined from the PI test to that obtained from a pressure build-up curve. These results show that the fracture treatment is sufficiently effective in connecting tile well bore to the native fractrure system to yield a flow capacity within about 50 per cent of that dictated by the native fracture system About two-thirds of the wells show some degree of local blockage. INTRODUCTION Fractured reservoirs have been known in the past.' However, during the past two years the Spraberry formation has directed the attention of the petroleum industry to a study of the performance of a fractured reservoir. The large variation in the number of fractures noted in Spraberry cores rile large variation in the producing ability of offset well.. the dramatic effect of well treatment on well ,productivity. the unknown quantity of oil stored in the fractures and matrix rock. and the unknown oil to be recovered were part of the initial Spraberry puzzle. In this type reservoir where the well treatment is an important factor in determining the productivity. it i- particularly desirable to determine the in-place flow capacity of the drainage area at distance* far removed from the well bore. This value. when compared to the flow capacity obtained from a PI measurement, will show the effectiveness of the well treatment (completion. fracture treatment, acidization. etc. in establishing a flow capacity in the vicinity of the well bore equal to that in the more remote region. The object of this paper i.; to show the application of a method of pressure build-up analysis for this purpose in studying the Upper Spraberry formation in the Driver area. STATEMENT OF THEORY The theoretical basis for the application of a pressure buildup curve to show the effective permeability of the rock at distances far removed from the well bore has been presented in detail in earlier publications.', in the previous development it was shown that pressure build-up behavior of all wells could be reduced to the same dimensionless build-up curve of Fig. 1. This mean.; that the bottom hole pressure of a well after hut-in will rise in such a manner that a plot of pressure against the logaritllm of time yields a straight line. The slope of this linp can be rlzed to calculate the effective permeability as expressed by the following equation: where: effective oil permeability md oil production rate prior to shnt in. STB/I) In practice the flow which occurs into the well bore after shut in and the variation in flow capacity in the immediate vicinity of the well bore usually cause the early part of the build-up curve to be unsatisfactory in the determination of permeability. In general the effect of these factors on the straight line section will become negligible after a time when the of the following equation is equal to 0.1. and the preferred section Of the curve for use in defining the slope lie-

Jan 1, 1953

By F. W. Schaller

TETRAGONALITY is an important aspect of the models of transformation, strengthening, and tempering of ferrous martensite. When the c/a

Jan 1, 1963

By Edward J. Felten

THE oxidation resistance of chromium and Fe-Cr alloys is increased by small additions of yttrium or other rare earth metals.1,2 In addition, the presence of the additives increases the resistance of these alloys to spalling of the external oxide above 1000°C. This ability to prevent spalling appears to be related to the formation of an internal oxide in alloys containing yttrium or the other rare earth metals. The internal oxide is found in the form of a filamentary growth concentrated in the grain boundaries of the unoxidized metal. In alloys containing yttrium this internal oxide was found to be either Y2O3 Or YCrO3.' In an earlier report,' the growth of the external oxide was found to be controlled by diffusion through the oxide layer. Thermal balance studies were used to establish the kinetics of external oxide formation. In this related study the rate of growth of the internal filamentary oxide has also been studied. The results obtained indicate that the growth of the internal oxide is also diffusion controlled. Internal oxidation appears to occur in at least two ways. Using copper alloys containing small amounts of silicon, Rhines 3 found that between 600" and 1000oC a subscale was formed which consisted of particles of silica dispersed in the metallic matrix. The conditions requisite to internal oxidation as suggested by Rhines are: 1) a solubility of oxygen in the alloy, 2) the ability of oxygen to diffuse at an appreciable rate into the alloy, 3) the possibility of the formation by the alloying element of an oxide more stable than the oxide of the host metal, and 4) a relatively low solubility of this oxide in the metal. These conditions are fulfilled for a number of other copper alloys.3-5 Furthermore, the relationship between the depth to which the internal oxide is formed and the oxidation time follows the simple parabolic law.6 The activation energy for copper containing small amounts of silicon, germanium, iron, or manganese as calculated from Rhines data6 is about 48 kcal per mole. In some cases the internal oxide is found segregated at the grain boundaries, especially near the the surface. Observations of this type of oxide formation have been reported by stead,7 Rhines,* and Lustman. Evans" cites these cases as examples of the simultaneous movement of anions and cations during oxidation. Furthermore, Evans states that the presence of a minor constituent with a high

Jan 1, 1962

By B. M. Larsen, J. W. Campbell

Several articles have recently been published discussing the conditions necessary for accurate measurements of temperatures in the open-hearth steel furnace. In the course of a study of refractories service conditions in steel furnaces, the present writers have taken temperatures in several open-hearth shops in the Pittsburgh district. The conclusions, as to conditions necessary for accurate measurements of temperature, are somewhat at variance with those of other investigators. The subject is closely connected both with the close control of steel-making and the prevention of overheating of the silica refractories used in roofs and walls. It is becoming more and more important to obtain furnace temperatures of fairly definitely known accuracy. At present, the most useful instrument for such measurements is the disappearing-filament type of optical pyrometer. This method of measurement has formed the basis of most other discussions on the subject and was also used by the writers. Previous Investigations In 1916, Burgess' made perhaps the first systematic series of measurements in steel furnaces. The emissivity figures of 0.40 for liquid steel and of 0.53 to 0.65 for liquid slags had been determined by the Bureau of Standards and were used by Burgess in this work. These correction factors are still being used and are regarded as fairly accurate, so that the tapping and teeming temperatures on metal streams given by Burgess should be very nearly correct. Most of his temperatures of furnace roofs and slag surfaces were taken while flames were present in the furnaces and include a few roof temperatures above 1700' C. (3100' F.).

Jan 1, 1927

By Paul H. Lu

Methods and results of measuring three basic parameters for ground stability control, ground pressure, strata movement, and geomechanical properties of mine rock are presented in this paper. It is found that these parameters can be measured in situ by simple and practical techniques with nonsophisticated and inexpensive instruments. Specifically, a drillhole dilation technique employing a cylindrical hydraulic borehole pressure cell (CPC) was used to determine the modulus of rigidity. Premining ground pressures were determined by pressure convergence tests with a combination of one CPC and two pre-encapsulated flat hydraulic borehole pressure cells (BPC) installed in a single drillhole. Abutment pressures and pillar loading were monitored with BPC's. Differential strata movements and bed separations were measured with self-recording 10-anchor-point extensometers. Roof-to-floor convergence was measured with self-recording convergence meters. Some applications of these in-situ-determined parameters to mine design and ground stability control are also discussed.

Jan 1, 1984

By R. E. Hummel, J. W. Koger

IT is generally accepted that the martensitic start temperature (Ms) can be determined by resistivity measurements and is that temperature where the resistivity vs temperature curve on cooling first deviates from a straight line.1-4 Both Titchener and ever' and pops5 have used resistivity measurements to follow the martensitic transformation in b1 Cu-Zn and ternary Cu-Zn-based b-phase alloys, respectively. Actually because of the nature of their measurements the temperature of minimum resistivity (M) was used by these authors to determine "Ms" . Also, due to experimental difficulties in detecting M, with resistivity measurements, Pops and Massalski 8 determined M, by optical microscopy. The present communication is concerned with high-precision, low-temperature resistivity measurements which reveal a definite M, temperature which differs from the temperature of minimum resistivity (M). It is also shown that M is merely the result of the geometry of the percent-transformation curve and the temperature coefficient of resistivity of the alloy. In other words, it will be demonstrated that M has no apparent significance (except that it denotes a temperature at which some percent of martensite can be detected in a given alloy). Alloy specimens were made by melting 99.999 pct Cu and 99.9999 pct Zn in sealed and evacuated quartz tubes and homogenizing them at 601PC for 300 hr. After the alloy was cold-rolled into foils suitable for resistivity measurements, it was quenched in ice water from 871PC. The chemical analysis showed a zinc content of 38.8 wt pct. The cooling rate during the martensite transformation was 1°C per min and was controlled with a thermistor. Electrical resistivity measurements were made using a K-3 type potentiometer; the reproducibility of the resistivity values was better than 0.03 pct. Temperatures were measured with a thermocouple to an accuracy of better than 0.2° C. Fig. 1 shows the resistivity vs temperature curves of the martensitic transformation in B1 Cu-Zn for both cooling and heating. The starting point of the martensitic transformation (M,) was taken as that

Jan 1, 1968

By Frederic Benard

PRIOR to 1936, the Ontario Refining Co. received all incoming blister copper from The International Nickel Company's smelter in the usual form of 460-lb. cakes, or slabs. These were received in open cars in lots of 250 pieces. At the refinery the cakes were unloaded onto narrow-gauge cars, for convenient handling and pickup by charging cranes. In March 1936, an investigation was started on the feasibility of transferring converter copper in the molten state from the smelter to the refinery anode furnaces, a distance of 1 ¼ miles. Although common in steel practice, the transportation of blister copper in this form had not previously been attempted and a preliminary study of the various factors involved was therefore necessary. For this purpose, a series of experiments was made in which molten copper, removed at different stages during the furnace cycle, was held in a small portable holding furnace. This vessel was essentially a refractory-lined steel cylinder provided with ports for filling and emptying, heated by an oil burner. Dimensions of the steel shell were 3 ft. 10 in. diameter by 7 ft. 3 in. long, and thickness of refractories depended on the design and combination used for the particular experiment. The vessel was filled with approximately 2 ½ tons of copper at a predetermined temperature, the lining having been preheated to a definite point by means of an oil burner. All openings were well luted and temperature readings were made every 15 min. by means of an immersion-type thermocouple. In this manner the rate of heat loss resulting with different refractory design could be developed. The ratio of exterior surface to weight of metal was taken into consideration in comparing the experimental results with what might be expected for a full-sized unit, and observations were also made on type and degree of slag accretion. It was not possible to get as much information on this latter point as desirable, but all evidence showed that the problem would be control of slag build-up rather than attack on refractories. From the information derived, and in consultation with the engineering staff of the supplying company, an order was placed for the first

Jan 1, 1938

By H. W. Gillett

UNLIKE most previous Howe lecturers, I had not the good fortune to be associated with Henry Marion Howe, nor to be directly one of his students. Yet, through his writings, he has been my teacher, as he has of all American metallurgists. Instructive as his writings are-I use the present tense because Howe thought so keenly and reasoned so surely, seeing clearly, as if by intuition, what was hazy to lesser minds, that his writings are still vital-it is not, those books and papers, nor even the minds he trained in his classes, that were his most outstanding service. It was the spirit of Howe in his: approach to the problems of metallurgy, his broad-mindedness and fair-ness, his recognition of the need for theories and hypotheses to explain metallurgical phenomena, his willingness to use them as servants, as well as his questioning attitude-his refusal to accept them as masters-that comprise his greatest service. This most thoroughly warrants the honor the Institute pays each year to his memory. These traits I so respect and honor in any man that I glory in this opportunity to do reverence to him in whom they were so notably united.

Jan 1, 1939

[ ]

Jan 1, 1907

By James M. Link

Slurry transport of industrial minerals has proven to be practical, economical, and efficient. Industrial minerals currently being pumped for long distances include cement, clay, phosphate, sand, and various waste product from industrial mineral processing operations. This paper will touch upon the basic theory of hydraulic transport of solids and then consider the economic and engineering considerations upon which construction and operation of such a line would be based. Where possible, actual cost data will be presented.

Jan 1, 1974

By C. F., Christopher

The purpose of any steel-making process is to convert the two raw materials iron and scrap into steel. The chemical analysis of the steel is set within certain limits which involve the physical proper- ties desired by the consumer. In addition to tensile properties a large number of other properties are at the present time desired, such as impact resistance, grain size regulation, specific degrees of hardenability, resistance to creep at high temperatures, resistance to expansion on heat treatment, the ability of the product to undergo extreme amounts of cold deformation without failure, and many other properties which are not directly related to the specified chemical analysis. Variations in many of the properties of plain-carbon steels are due to elements and compounds not included in the ordinary "five element"§ composition. Such variations result primarily from variations in oxidation of the metal in the furnace and from the deoxidation method employed. The steel-making problem therefore resolves itself into two distinct sections: (I) the elimination of certain elements from the charge (the iron and scrap entering the furnace) and the addition of materials to meet the chemical specifications for the heat; (2) the manipulation of the slag and metal and the process of deoxidation to give certain desired properties in the steel entirely apart from the chemical analysis specified. Each of 'these two ends must be attained

Jan 1, 1957

By William B. Plank

IN this paper are presented the results of a complete statistical survey of the enrolment, courses and degrees, and the employment situation of recent graduates in all of the 46 institutions in the United States, including Alaska, and four of the six schools in Canada that grant degrees in mineral technology. The data were collected by the writer by means of a questionnaire in December, 1933, to which all the institutions, except one, replied. Included also are data of a similar study made by the writer in May, 1933, for the S. P. E. E. summer session of mining and metallurgical teachers at the University of Wisconsin and published in the Journal of Engineering Education for December. 1933. Some of the data of a paper of the writer's entitled, "The Trend of Mineral Engineering Student Enrolment in the United States," read at the A. I. M. E. meeting on Feb. 16. 1931, are given for comparison. Acknowledgment is made to all the administrative officers of the institutions who took the time from their busy lives to supply the in- formation asked for. Their fine cooperation has alone made possible these two surveys with a completeness of detail never before attempted

Jan 1, 1934