By M. R. Meyer, W. T. Walter

A great deal is known, in a qualitative sense, about the performance of CMI EB-36 centrifuges. The manufacturer can give reliable guidance for the proper operation of its centrifuges and can give general estimates of expected product moisture and recovery. Quantitative estimates of the effects of changes in the various operating parameters are more difficult to find. The engineer faced with designing a preparation plant may be without the specific data needed to make decisions. For example, to obtain optimum product moisture when drying 9.5 mm X 595 µm (0.4 in. x 28 mesh) coal the centrifuge manufacturer recommends having no more than 5% -595 µm (-28 mesh) material in the centrifuge feed. They know that more -595 µm (-28 mesh)material in the feed will cause higher product moistures, but they usually cannot quantify the increased moisture or describe the shape of the product moisture versus -595 µm (-28 mesh) in the feed curve. This study was conceived to provide quantitative information on the EB-36 centrifuges, focusing on product moisture, recovery, and size degradation. All of the centrifuges tested were Model EB-36 dryers from Centrifugal and Mechanical Industries Inc. (CMI), with feeds in the nominal 9.5 mm x 595 pm (0.4 in. x 28 mesh) range. These are typical centrifugal dryers in this application, and many were available for testing.

Jan 1, 1984

By R. W. Bartlett

The rates of oxidation of tungsten have been determined at temperatures between 1320" and 3170°C and oxygen pressures to 1 amn using a surface -recession measurement technique. Above approximately 2000°C and 10-6 atm the rate is independent of temperature and can be calculated from gas collision theory assuming a constant reaction probability, e, of 0.06. Oxygen molecules react at surface sites where oxygen atoms have previously chemisorbed. This provides a direct pressure dependence at low pressures but at high pressures tungsten oxide molecule s form an adjacent gas boundary layer which lowers the PO2 at the tungsten surface. A correction for this effect using free-convection theory fits the rate data over the entire oxygen-pressure range from 10-8 to 1 atrn as well as data using O2-A mixtures. Below 10-6 atrn and above 2000°C, e decreases with increasing temperature because of desorption of oxygen atoms. Below 2000°C the rate decreases with decreasing temperature at all oxygen pressures following an apparent activation energy of 42 kcal per mole and depending on (Po2)n with n varying between 0.55 and 0.80. MOST of the previous tungsten oxidation studies have employed gravimetric methods and have been limited to temperatures below 1000°C where the weight loss associated with evaporation of tungsten oxides is negligible compared with the weight gain from oxidation.' At higher temperatures, oxygen-consumption rates have been determined from pressure measurements, usually at constant flow rates, by Langmuir,2 Eisinger,3 Becker, Becker, and Brandes,4 and Anderson.5 The sensitivity of this method decreases with increasing pressure and, with the exception of Langmuir's work, these investigations were confined to pressures below 10-6 atm. Above approximately 1300°C, depending on the oxygen pressure, the rate of oxide evaporation is greater than the oxide-formation rate and the recession of the tungsten surface can be measured optically without interference from an oxide layer. This was first done by Perkins and crooks6 who heated tungsten rods in air pressures from 1 to 40 torr at temperatures between 1300" and 3000°C. The present investigation of the oxidation kinetics of tungsten at high temperatures emphasizes oxygen pressures from 10-6 to 1 atm. This is the range of interest for earth atmosphere re-entry applications of tungsten for which little data were previously available. APPARATUS The apparatus is a modification of the type used by Perkins and crooks.' Ground tungsten seal rods, 6 in. long by 0.125 in. diam, were mounted vertically between two water-cooled electrodes, one fixed and the other having free vertical travel. The movable counter-weighted electrode is prevented from undergoing horizontal displacement by three sets of runners mounted at 120-deg intervals. Electrical contact is made by means of a water-cooled mercury pool. A 24-in. vacuum bell jar having a volume of approximately 267 liters was used as the reaction chamber with the sample holder mounted in the middle of the chamber. Power was supplied from an 800-amp dc variable power supply. Temperature readings were made by means of a Latronics automatic two-color recording pyrometer. With this instrument, corrections for emissivity are not necessary provided the spectral emissivi-ties at two closely spaced wavelengths are equal. Supporting measurements were made with a micro-optical pyrometer corrected for emissivity of bare tungsten and window absorptivity. The micro-optical pyrometer was calibrated against a National Bureau of Standards calibrated tungsten lamp and both pyrometers were periodically checked against the melting points of tungsten and molybdenum using the oxidation apparatus. Above 10-6 atm, pressures were measured with an Alphatron gage calibrated against a McCleod gage. At 10-6 atm, a hot-filament ionization gage was employed. A magnified image of the self-illuminated tungsten rod was formed using a 360-mm objective lens mounted outside the bell jar. When the experiment exceeded 1 hr, the image was focused on a ground-glass plate about 10 ft from the tungsten rod at about X8 and the recession of the thickness of this image was monitored with a Gaertner cathe-tometer. When faster rates were encountered, a 35-mm time-lapse cinecamera with a telephoto lens and bellows extension was substituted for the ground-glass plate and cathetometer. Diameter recession rates were determined from the photograph image projected on the screen of an analytical film reader. EXPERIMENTAL PROCEDURE After installing the rod in the apparatus and cleaning it with acetone, the system was evacuated to 5 1 x 10-5 torr. Before oxygen was introduced,

Jan 1, 1964

By H. Rush Spedden, A. M. Gaudin

IN the belief that a critical study of its operating problems might be a sound investment, the Cuban American Manganese Corporation initiated an ore-treatment research in cooperation with the Massachusetts Institute of Technology One of the early objectives of this research naturally became the relationship of the microscopy of the Cuban ores of the Corporation to their flotation treatment The operations in Cuba have already been described by F S Norcross, Jr 7 and the laboratory study of manganese oxide flotation goes back a number of years 4 Broadly speaking, the difficulties encountered in the flotation of manganese ores are that the consumption of reagents is extremely high, the concentrate contains more silica than is desirable and the tailing losses are relatively high An appreciable betterment on any of these scores would achieve a definite betterment in costs, quantity of minable ores, and quality of product The microscope study discussed in this paper was made on samples from the Quinto mine, from the Ponupo mine, and from mill products at various stages of passage of the ore through the mill The writers have had access to Company records and in particular to the petrographic studies made on thin sections of ore by the late Professors R J Colony and Philip Krieger, of Columbia University They acknowledge their debt to both of these men for the help derived from the reports Manganese oxides are black, friable, smudging It is therefore, very difficult to judge operations by inspection The mineralogy of manganese compounds seems to be confused, and the authors believe that many more minerals have been described than actually exist Much of this difficulty is due to the prevalence of the structural conditions that will be discussed further in this paper, namely, the porosity and the friability of the ores, and the extremely intimate association of minute manganifeous mineral crystals with impurities of various sorts By all odds the most important manganese mineral in Cuba is the one that in this paper is called "psilomelane " The name "psilomelane" has been used in so many different ways that the choice of it for this ore may not be approved by all However, it seems to be the best under the circumstances This mineral accounts for about 97 per cent of the manganese in the ores of the Quinto and Ponupo mines and in the mill feed The remaining odd 3 per cent consists mostly of pyrolusite together with minor amounts of other manganese oxide minerals DESCRIPTION OF PSILOMELANE Aggregate Structure In grains or lumps, psilomelane has a characteristic fibrous appearance and seems

Jan 1, 1942

By M. J. Duggin

Evidence is produced below to show that the carbide "Mn,C," reported by Kw,and ersson' is really a mixture of two carbides. One is an Fe-Mn carbide which is probably isomorphous with hexagonal Mn15C4, reported by Bouchand and Pruchart.' The othev is a tetragonul Fe-Mn carbide with cell dzmensions close to those reported previously by the author3 for an Fe0.1Mno. carbide. IN a recent investigation several Fe-Mn carbide specimens, each weighing about 5 g, were prepared in a manner previously reported.3 Debye-Scherrer X-ray photographs were taken of at least two samples from different parts of each specimen using a 114.6-mm-diam camera. The exposure time was 2 hr using filtered chromium radiation, a tube voltage of 35 kv and a tube current of 10 ma. In the case of one specimen, which contained nominal weight percentages of iron, manganese, and carbon of 9.40, 84. 6,, and 6.0, respectively, duplicate chemical analyses indicated f1.2 and 5.5 wt pct C to be present in the two samples taken of the specimen: no graphitic carbon was detected. One powder-diffraction pattern of this specimen indicated the presence of the tetragons: carbide reported earlier,3 (a = 6.772A, c = 9.427A), plus cementite (O), plus an unknown structure. The second powder-

Jan 1, 1970

By FRANK COLE

THE territory covered in this discussion includes all the states west of the Mississippi river. Agriculture is expanding each year in this section, but until recent years the application of commercial fertilizers as an aid to crop production was not practised to any great extent. The use of commercial fertilizers has increased somewhat, but is still on a small basis as compared with the tonnages used else- where in the United States. During 1928 these western states used 665,100 tons of all classes of fertilizer as compared 'with 7,933,600 tons used in the whole United States; or this western area, compromising near- ly two-thirds the land area, uses about 5 per cent of the total fertilizer. To show how large a tonnage one state may consume, North Carolina for the year 192s used 1,349,360 tons of commercial fertilizer or about twice the amount used by 22 western states.

Jan 1, 1930

By M. W. BERNEWITZ

IT is 27 years since I last visited Broken Hill, New South Wales, one of the world's greatest lead-silver-zinc districts. Then, the flota¬tion of ores was in its infancy. The Minerals Separation process had its birth as a practicability in the Central Mill, which is still operating and yielding high recoveries. The average Australian knows that Broken Hill is an important mining center in a "corner" of New South Wales, but he does not know what a factor it is in the lead, silver, and zinc production of the world. Nor does he realize that among the ramifications arising from metal production at Broken Hill are the great lead smelter at Port Pirie, South Australia, 254 miles southeast; the electrolytic zinc works at Risdon, and the limestone mine at Davenport, Tasmania; the acid works at Cockle Creek, New

Jan 1, 1935

By L. Bombardieri, H. F. Mills

IRON KING mine, producing gold-silver-lead-zinc ore, is 10 miles east of Prescott, Ariz. At present the 1806 level is being developed. The echelon pattern of ore deposit continues at depth but is less pronounced, and the orebody is now more or less continuous over 2600 ft of strike length. with widths 5 ft to as high as 26 ft where overlapping of lenses occurs in one section of the mine. Better continuity of ore at depth has encouraged systematic mining and improved plant facilities to offset higher operating costs. With favorable persistence of ore at depth. the three-compartment No. 6 hoisting shaft appeared inadequate to handle increased tonnage from greater depths, and in 1952, a four-compartment steel and concrete shaft was started. This is now at a depth of 1906 ft, and shaft pockets and loading cartridges are being installed on the 1806 level. Ore from the new shaft, hoisted in 51/2 -ton Jeto bottom dump skips, is dumped into a 500-ton shaft bin, from which it is fed to a 16x30-in. gyratory crusher and conveyed 415 ft through an undersurface concrete gallery to the secondary crusher and conveying system supplying the 900-ton mill. Lead, zinc, and pyrite concentrates are floated, and the flotation tailings are cyanided after desliming. Waste from the new shaft is dumped into a 250-ton surge bin, fed from this bin to a 24-in. conveyor, and discharged into the glory hole above the block cave. The new shaft is served by a double-drum 400-hp hoist used for ore and waste; the No. 6 shaft conveys men and material To secure a cheap source of waste fill for stoping operations, a block cave area was undercut In the hanging wall near the north end of the mine above the 600 level. Waste from the block cave is drawn from any of three large drawpoints on the 600 level, and a series of hanging wall transfer raises with controls and bypasses on each level provide a fast low-cost material for fill. The block cave is worked vertically through to surface in the form of a steep-sided hole 350x250 ft and several hundred feet deep, the sides of which cave and provide fill material without any blasting. Fill is a mixture of caliche-cemented surface gravel and small particles of hanging wall schist. Level Development: An orebody 300 times as long as it is wide requires a lot of development work. Former practice consisted of driving a haulage drift about 30 ft from the ore in an andesitic footwall, a drift on the ore, and crosscuts from the haulage drift at 100-ft intervals. Crosscuts are about 90 ft long. At present, only the odd numbered levels are so developed, and on the even numbered levels only the haulage drift and crosscuts are driven. Little or no timber is used for this development. This change resulted in 20 pct reduction of development costs and 50 pet reduction of square set stoping required for removal of floor pillars. Elimination of ore drifts on alternate levels leaves

Jan 1, 1957

By Richard J. Borg

The vapor pressure of Cd in equilibrium with CdSb in the presence of excess Sb has been measured using the Knudsen effusion method over the temperature range 276° to 379°C. The free energy of formation of CdSb is given by AF° = -1.58 + 1.53 x l0-4 T, kcal per mole. The enthalpy and entropy are obtained from the temperature coefficient of the .free energy. CADMIUM and antimony have almost imperceptible mutual solid solubility but form a single stable intermediate phase, CdSb. This phase, according to Han-sen,l extends from about 49.5 at. pct to 50 at. pct Cd at 300°C and has the orthorhombic structure. The free energy of formation of CdSb can be calculated from the vapor pressure of Cd for compositions which contain less than 49 at. pct Cd. The appropriate reaction and formulae are given by Eqs. [I] and [2]- CdSb(s, ~ Cd(g)-, +Sb(s) [1] Since Sb is in its standard state, Af - N,,AF'-,, = NcdRT In a,, = NcdRT InP/PO [2] In Eq. [2], P, is the vapor pressure of Cd in equilibrium with the alloy, and Po is the vapor pressure in equilibrium with pure solid Cd. It is implicit in this calculation that the free energy only slightly changes within the narrow limits of the single phase field. Thus, the value obtained from the antimony-rich boundary is truly representative of the stoi-chiometric compound. The results reported herein are obtained from a mixture near the eutectic composition, i.e. 59 at. pct Sb. Only two previous investigations" of the free energy of formation of CdSb have been made. Both relied upon the electromotive force method, and measurements were made over relatively narrow temperature ranges which strongly influences the reliability of the values of AH and aS. EXPERIMENTAL The eutectic composition is prepared by fusing reagent grade Cd and Sb by induction heating in vacuo with the starting materials held in a graphite crucible having a threaded lid. The material obtained from the initial melt is pulverized, sealed under high vacuum in a pyrex capsule, and annealed at 420°C for two weeks. X-ray analysis"gives the following lattize parameters: a = 6.436A, b = 8.230& and c = 8.498A using Cu Ka radiation with A = 1.54056. These values are in fair agreement with the result? previously reported by Al~in:4 i.e. a = 6.471A, b = 8.253A, and c = 8.526A. Vapor pressures are measured using an apparatus which has been described elsewhere,= however, with a single important modification. Knudsen effusion cells are made of pyrex with knife-edged orifices made by grinding the convex surface of the lid on #600 emery paper. Photographs taken at known magnifications using a Leitz metallograph enable the determination of the orifice area. Numerous calibration measurements of the vapor pressure of pure Cd give close agreement with values previously reported5,= thus indicating that no significant error can be ascribed to the substitution of glass cells for metal cells used in previous work. Because the vapor pressure of Cd is reliably established and because it is difficult to obtain Clausing factors for the glass cells, the final values used for the orifice areas are calculated from the calibration measurements of the vapor pressure of pure Cd. Effusion runs are started in an atmosphere of purified helium which is quickly evacuated as soon as the cell attains thermal equilibrium. Less than one minute is necessary to obtain high vacuum after evacuation begins, and the temperature seldom varies by more than 0.5oC from the value obtained prior to pumping out the helium. RESULTS The results of this investigation along with other pertinent data are tabulated in Table I. Fig. 2 is the familiar graph of log P against T-10 K. At least mean squares analysis of the data presented in Table I yields the following equation: log1DJP = 8.790 - 6472 x T"1 [3] The deviations of the individual measurements from the values calculated with Eq. 131 are given in column six of Table I; the average deviation is 4.0% of the calculated value. Although the partial molal properties change significantly with composition within the single phase region, the integral thermodynamic value should remain relatively constant. Hence the results of the following calculations, which use the data obtained for the eutectic composition, are probably representative of the equi-atomic compound. Eq. [4] describes the vapor pressure of pure Cd as a function of temperature and may be combined with Eq. [3] to

Jan 1, 1962

THOSE MARKED THUS * ARE MEMBERS, MARKED THUS ?ARE ASSOCIATES. THESE SIGNS DOUBLED INDICATE LIFE MEMBERS AND ASSOCIATES RESPECTIVELY. THE FIGURES AT THE END OF THE ADDRESS INDICATE THE YEAR OF ELECTION. HEAVY-FACED TYPE SIGNIFIES HONORARY MEMBERSHIP. *AARONS, J. BOYD, Vivian Gold Mining Co., Ltd., Harris, West. Australia. '05 *ABADIE, EMILE R., Cons. and Min. Engr., 214 Union Savings Bank Bldg., Oakland, Cal. '76 ?ABBÉ, MAX F., Prest., Abbé Engineering Co, 220 Broadway, New York, N.Y. '07 ? ABBÉ, PAULO., Secy.,Abbé Engineering Co., 220 Broadway, New York, N.Y. '07 *ABBOTT, AI ARTHUR Morococlia, Peru, So. America. '95 *ABBOTT, CLARENCE Chief EDgr., Iron Mines, Dic Tennessee Caol, Iron & R. R. Co., Bessemer, Ala. '04 *ABBOTT, JAMES W., Min. Engr: Ploche, Lincoln Co., Nev. '94 *ABE, MASAYOSHI, Prof. of Mining, Imperial University Kyoto, Japan. '05 ? ACKER, E. O'C., Supt., Treatment Dept., Bethlehem Steel Co., So. Bethlehem, Pa. '86

Jan 1, 1910

By Henry M. Rowe

Professor Ruff's most illuminating paper' describing his extremely valuable investigation of the carbon-iron equilibrium diagram assigns definite temperatures to certain very important lines in the diagram, viz.: the eutectic temperature EB (Fig. 1) and the " near-eutectic " temperature E'B', but without indicating clearly enough the reasoning which warrants these assignments. These temperatures are of such primary importance that it is well to indicate the apparent gaps in the reasoning, in the hope that they may be filled in. In his diagram, Fig. 1, the point X and the liues B'D'lII represent the experimental results reached by Ruff and Goecke;a AB, AEB, and SE represent the liquidus, the solidus, and the solubility of the carbon in solid austenite in the absence of graphite according to Gutowsky,3 AB being also in accordance with Spiecker's data; S'E' the solubility of carbon in solid austenite in the presence of graphite according to Ruer and Iljin;5 GS the line A3 after Ooerens and Meyer; 6 and EBC the true eutectic line as inferred by Prof. Ruff from Gutowsky's data. B'D' is the carbon content found in cast-iron which had apparently saturated itself with carbon in the presence of the graphite of the enclosing graphite crucibles in which the determinations were made. From its straightiiess and its sharp inflection near 6.67 per cent. of carbon, the carbon content of

Jan 1, 1913

By CHARLES W. BENTON

THE following paragraphs comprise such information as the Secretary has been able to obtain concerning the members and associates whose deaths have been reported. Further particulars or corrections of errors, and biographical data concerning deceased members or associates not already noticed in this way, are solicited. Charles IV. Benton was born at Kezar Falls, Maine, Nov. 12, 1843. We have no accurate knowledge concerning the early part of his career. In 1871 he engaged with the N. Y. Honduras Rosario Mining Co., at San Juancinto, Honduras, C. A., and later was employed at the Monserrat mine at Yuscaran, and at Santa Lucia, Honduras, with the Tenero Mining Milling Co. of Pennsylvania. In 1897 he became a member of the Institute. At the time he was stricken with his last sickness he was employed at the Paymaster mine at Tucson, Ariz. He died at Fairmount, Denver, Colo., Sept. 9, 1907. William R. Boggs, Jr.-The notice in the Bulletin for January was incorrect in saying that the murder of Mr. Boggs occurred while he was employed as metallurgical. manager by Mr. W. B. A. Dingwall, at La Maroma, San Luis Potosi, Mex. Mr. Dingwall writes that in March, 1907, Mr. Boggs left him, to return to his home at Winston, N. C., whence he. subsequently went to Durango, Mex., to take, with the Topia Mining Co., a position which he occupied at the tine of his death, Nov. 17, 1907. Mr. Dingwall says that, while in his service, Mr. Boggs never had any trouble with the workmen, but was esteemed and liked by them, as by all who knew him ; and adds, injustice to the State of San Luis Potosi, that the population, even in the mining-camps of that State, is orderly and law-abiding, and that the authorities are vigilant and just. Our

Mar 1, 1908

By Avnulf Muan, Egil Aukrust

The activity-composition curve for cobalt oxide in (Co,Fe)304 solid solutions with spinel-type stmcture has been determined experimentally by studying the equilibrium between the spinel phase and a coexisting cobaltowüstite phase, "(Co,Fe)O", at 1200°C. A large negative deviation from ideal behavior prevails in the spinel at low cobalt oxide concentrations and a positive deviation at high cobalt oxide concentrations. The activity-composition curve for iron oxide in the solid solution is determined from the above curve by integvation of the Gibbs-Duhem equation along the join Co3O4,-Fe3O4. The standard free energy of formation of cobalt ferrite, CoFe2O4, from the oxide components CoO and Fe2O3 is calculated to be -8.2 kcal. ThERMODYNAMIC properties of (CO,Mn)3O4 solid solutions with spinel-type structure have been presented recently.' The present paper deals with similar relations in another spinel solid-solution phase, that represented by the system Co3O4-Fe3O4. The principles involved in measurements and calculations of thermodynamic properties for the system Co3O4-Fe3O4 are analogous to those used and discussed in detail in the work on (CO,Mn)3O4. A (CO,Fe)3O4 solid solution coexists in equilibrium with a (Co.Fe)Ot solid solution over a considerable Here acOo1.33 and aao are the activities of cobalt oxide in the spinel and the oxide solid solutions, respectively, pO2, is the oxygen pressure of equilibration, and pb, is the oxygen pressure at which CoO and CosO4 coexist in equilibrium in the binary system Co-O at the same temperature. The activity-com position curve for cobalt oxide in the (Co,Fe)O solid solution in contact with metal has been determined in a previous investigation by the present authors.' The system shows a small positive deviation from linear behavior. Because of the large defect concentration in wiistite and in (Co,Fe)O solid solutions, one cannot assume that the activity-composition relations in the oxide phase coexisting with a spinel phase at relatively high oxygen pressures are the same as those prevailing in the oxide solid solution coexisting with metal. However, a Gibbs-Duhem integration over the ternary Co-Fe-0 solution can be used to determine activities of cobalt and iron, and hence of CoO and FeO, from a knowledge of the oxygen potentials. Several papers have dealt with the subject of application of the Gibbs-Duhem equation to multi-component systems. 3-6 In the present case, it was

Jan 1, 1964

Soil Testing for Engineers. By T. W. Lambe. Published by John Wiley & Sons. 165 P. $5.00.-Filling a need for a text for the teaching of soil testing in the laboratory, this book is also of value as a reference for practicing engineers and for personnel in soil laboratories. Following an introductory chapter on general laboratory procedures are chapters devoted to the individual laboratory soil tests which are commonly employed. Apparatus, supplies, recommended procedures, discussion of procedure, calculations results, and numerical examples are provided for each test. Brief derivations of formulas and explanations and discussions of calibration procedures and special techniques are given in the appendix. Mesabi Pioneer. Copyrighted 1951 by the Minnesota Historical Society.- Publication of this book has been made possible by a generous gift to Society from the E. J. Longyear Co. of Minneapolis. This book covers the evolution of the Mesabi Range from a wilderness into the nation's greatest iron producing area. In this book is found the first hand experiences of Edmund J. Longyear who saw the development of the range from its beginnings, and who himself took a notable part in it. In 1890 Edmund J. Longyear sank the first diamond drill hole on the Mesabi. During the next two decades he sank pits and holes- 7133 of them-throughout the length and breadth of the Mesabi Range, exploring for iron ore. He saw roads and railroads built. He watched the range communities--Hibbing, Chisholm, Biwabik, Mountain Iron and the others change from exploration camps to

Jan 11, 1951

By Albert A. Smith

The creep properties of metals have assumed increasing importance in recent years and many investigations have been made on various phases of the problem. In the past year the annual lectures of the Institute of Metals Division1 and the Iron and Steel Division2 were concerned with this subject, and are excellent reviews. For many years the creep properties of lead and lead alloys have been investigated at the Central Research Laboratories of the American Smelting and Refining Co., and it is hoped that the present paper will contribute knowledge of some of the factors that influence creep. Lead, being a metal that recrys-tallizes readily at room temperature, is an excellent material upon which to investigate creep phenomena because of the simplicity of the apparatus needed, and it might be expected that results would apply to some extent to elevated-temperature tests of other metals. Material The creep tests of this investigation were all made on high-purity lead (99.9998+ Pb) in which the only impurity that could be detected by spectrographic and chemical means was approximately 0.0001 per cent Fe. Flat strips, 0.750 in. wide by 0. 100 in. thick, were prepared by extruding 2-in. dia. cast billets at a temperature of 250°C. This gave a material of 2 to 3 mm. average grain size with a tensile strength of j.400 lb. per sq. in. when tested at a straining rate of 5 per cent per minute. With this extremely soft material, great care was necessary in handling the specimens, to avoid distortion and subsequent recrystallization. The creep tests at 30°C. were conducted in a constant-temperature room, specially built for the purpose in the basement of an office building in which there was no moving machinery, and no vibration was detectable under the most severe conditions of shock in the adjacent surroundings. The room was well insulated and heated electrically, control being by means of a de Khotinsky regulator operating a relay. Maximum temperature variation over a period of several years has been ± 1/2°C. Specimens of the extruded strip, 16 in. long, were used for test purposes with no reduced gauge section, thus eliminating any distortion due to machining. The method of clamping and supporting the specimens is shown diagrammatically in Fig. 1. The gauge marker for the measurement of extension consisted of an aluminum strip, 0.050 in. thick by 0.75 in. wide, one end of which was ground and sanded to a precise knife-edge and fastened to the specimen by suitable pins. After the strip was fastened in place a fine scratch was inscribed just below the knife-edge by means of a sharp teasing needle. Just below this gauge scratch a short vertical mark was made so that the same point could be located and read each time. Several hundred specimens have been prepared by this method, and it was found that with experi-

Jan 1, 1941

By Albert A. Smith

The creep properties of metals have assumed increasing importance in recent years and many investigations have been made on various phases of the problem. In the past year the annual lectures of the Institute of Metals Division1 and the Iron and Steel Division2 were concerned with this subject, and are excellent reviews. For many years the creep properties of lead and lead alloys have been investigated at the Central Research Laboratories of the American Smelting and Refining Co., and it is hoped that the present paper will contribute knowledge of some of the factors that influence creep. Lead, being a metal that recrys-tallizes readily at room temperature, is an excellent material upon which to investigate creep phenomena because of the simplicity of the apparatus needed, and it might be expected that results would apply to some extent to elevated-temperature tests of other metals. Material The creep tests of this investigation were all made on high-purity lead (99.9998+ Pb) in which the only impurity that could be detected by spectrographic and chemical means was approximately 0.0001 per cent Fe. Flat strips, 0.750 in. wide by 0. 100 in. thick, were prepared by extruding 2-in. dia. cast billets at a temperature of 250°C. This gave a material of 2 to 3 mm. average grain size with a tensile strength of j.400 lb. per sq. in. when tested at a straining rate of 5 per cent per minute. With this extremely soft material, great care was necessary in handling the specimens, to avoid distortion and subsequent recrystallization. The creep tests at 30°C. were conducted in a constant-temperature room, specially built for the purpose in the basement of an office building in which there was no moving machinery, and no vibration was detectable under the most severe conditions of shock in the adjacent surroundings. The room was well insulated and heated electrically, control being by means of a de Khotinsky regulator operating a relay. Maximum temperature variation over a period of several years has been ± 1/2°C. Specimens of the extruded strip, 16 in. long, were used for test purposes with no reduced gauge section, thus eliminating any distortion due to machining. The method of clamping and supporting the specimens is shown diagrammatically in Fig. 1. The gauge marker for the measurement of extension consisted of an aluminum strip, 0.050 in. thick by 0.75 in. wide, one end of which was ground and sanded to a precise knife-edge and fastened to the specimen by suitable pins. After the strip was fastened in place a fine scratch was inscribed just below the knife-edge by means of a sharp teasing needle. Just below this gauge scratch a short vertical mark was made so that the same point could be located and read each time. Several hundred specimens have been prepared by this method, and it was found that with experi-

Jan 1, 1941

By E. C. Harder, D. F. Hewitt

Since early in 1916, when it became apparent that the steel industry of the United States could not depend for the duration of the war on several important foreign sources of manganese and might have to depend entirely on domestic ores, the U. S. Geological Survey, with the assistance of several cooperating organizations, has made a comprehensive investigation of domestic manganese resources. The work has included field studies in a number of states well as annual, quarterly, and monthly canvasses among operators concerning current and future production. In order that the interested public might have access to the important results of the studies, preliminary reports concerning the field work as well as periodic summaries of production were issued as promptly as possible. Although numerous summaries of production l2, l3, l4 have been prepared from time to time for the use of the several boards and committees responsible for the conduct of the war, it has been thought for some months that those engaged in the industry, as well as others, might be interested in a preliminary summary of the accumulated geologic and production data. The cessation of hostilities, in November, 1918, probably detracts from the usefulness of much of the material that is here presented, but apart from the historic interest in the performance of an important industry in war time, there is a possibility that some of the conclusions may be helpful to those who continue to exploit domestic deposits, as well as to those who wish to measure the country's independence in mineral supplies. Appropriate final geologic reports are being prepared by the geologists who did the field work. The present authors, having done but a small part of the recent field work, acknowledge with great appreciation the use of preliminary and unpublished reports and the cordial informal cooperation of the following geologists in the preparation of this paper: F. L. Ransome, G. W. Stose, F. C. Schrader, J. T. Pardee, E. L. Jones, Jr., H. D. Miser, Laurence LaForge, J. B. Umpleby, Arthur Keith, F. J. Katz, and E. S. Larsen, of the U. S. Geological Survey. Field work in Virginia was carried out in cooperation with the Virginia Geological Survey, T. L. Watson, State Geologist; in Georgia, with the Georgia

Jan 1, 1920

By Webster, Wm. Reuben

THE greatly enlarged demand for small sizes of seamless copper tube which has recently occurred, due particularly to the rapid growth of the electric household-refrigerator industry, has emphasized the superiority of phosphorized to tough pitch copper for the purpose of producing this commodity. In the manufacture of this material exceedingly heavy reductions by cold drawing are employed, customary practice involving as much as 90 per cent. reduction of cross-sectional area in four runs without intermediate annealing. Although this superiority has long been recognized by tube makers, no quantitative expression of it has heretofore been published. It is believed that the data herewith presented mill serve this purpose. Recent investigators are not in agreement as to the relative mechanical properties of copper containing small amounts of oxygen as compared with copper containing sufficient oxygen to produce that condition known as tough pitch. Hanson, Marryat and Ford1 found that "oxygen has a relatively small effect on the properties of copper." Johnson, on the contrary, states "it cannot be denied that it (tough pitch copper) is inferior to deoxidized copper . . . where severe mechanical manipulation is concerned." These authorities in the reports of their investigations, as might be expected from their conclusions, do not present data of a character requisite to a conclusive determination of the question.

Jan 1, 1927

By Auguste J. Rosh

The use of titaniferous ores in the blast-furnace has been the subject of much controversy for many years. Divers objections have been raised against them, and, for one cause or another, the verdict

Jan 1, 1893

By W. G. Frailing, W. P. Sims

The Lakeview Pool of Kern County, California, was discovered in 1910 with the drilling of Lakeview No. 1 which blew out and produced an estimated 8,250,000 bbl of oil in 544 days of uncontrolled flow. The well has since been known as the Lakeview Gusher. Full exploitation of the pool did not take place until about 25 years later. A total of 112 producing wells were completed in the Lakeview sand through April 30, 1949. As of that date, about 30 per cent of the total wells drilled were still producing, with an average pool production rate of approximately 2000 bbl per day. The cumulative oil production was about 41 million bbl of oil, or 55.3 per cent of the tank oil originally in place. The pool is bordered on its down-structure side by a body of inactive edgewater and water production where present has been principally the result of coning. Since the depletion of the greater portion of the gas energy by the Lake-view Gusher, the pool has operated under gravity drive. Relatively high angle dips, good permeabilities and favorable fluid characteristics have made gravity drainage particularly effective. Since January, 1942, the oil recovery -has been relatively constant at about 53,000 bbl per ft drop in fluid level. Correlations between the volume of reservoir space drained and the cumulative oil produced indicate that an ultimate recovery of 63.3 per cent of the tank oil originally in place is attainable. INTRODUCTION The Lakeview Pool is an outstanding example of gravity drainage. It is one of many productive reservoirs of the Midway-Sunset Field, and is located in Kern County, approximately five miles southeast of Taft and two miles north of Maricopa, California. Its position rel- ative to surrounding pools and to the Thirty-Five anticline is shown on Fig. 1. The northern portion of the pool lies in sections 32 and 33, Township 32 South, Range 24 East, Mt. Diablo Base and Meridian, while the southern portion lies in sections 25, 26, 35 and 36, Township 12 North, Range 24 West, San Bernardino Base and Meridian. As no two sections bear the same number, they will hereafter be referred to by section number alone. The purpose of this paper is to review the performance of the Lakeview Pool in an effort to evaluate the effectiveness of gravity drive as a recovery mechanism. REGIONAL STRATIGRAPHY AND STRUCTURE The oustanding structural feature is this area is the Thirty-Five anticline, the axis of which plunges South 75" East through the center of Section 35. As shown on Fig. 2, the following zones are oil and gas bearing in the Thirty-Five anticline area: Pleistocene Basal Tulare Tar Sands Pliocene San Joaquin Mya Sands Top Oil or Scalez Zone Etchegoin Kinsey Sand Wilhelm Zone Gusher Sand Calitroleum Sand Miocene Reef Ridge Lakeview Sand Sub-Lakeview Miocene Sands Monarch Sands or fractured shale equivalent Maricopa Webster Sand or fractured shale equivalent Fractured Shale-Uvigerina Zone C Obispo Sand and fractured shale equivalent Pacific Shale Zone The productive interval of the Lakeview Pool is limited to Upper Miocene and Lower Pliocene deposition. In this general area, the most prevalent type of accumulation results from stratigraphic traps or permeability pinchouts. As is the case of the Lakeview Pool, strati-graphic traps resulting from angular unconformities are present. The structure within the Miocene does not parallel that of the Etchegoin (Pliocene), as the Miocene beds were folded, and in places faulted, and subjected to erosion prior to Pliocene deposition. The Lakeview horizon consists of truncated sands which occur on the northeast flank of the Thirty-Five anticline. The direction of strike is west and northwesterly through sections 25 and 36 and continues northwesterly through sections 26 and 33, to the approximate center of section 32. At this point the strike swings to the northeast and the horizon re-enters section 33. in the northwest corner. The change in strike in section 32 affords synclinal accumulation at that point. The Lake-view sand is truncated updip by the Etchegoin overlap. To the southeast, the sand shales out, while to the northwest, the productive interval appears to be limited by a combination of stratigraphic pinchout and permeability barrier. Structurally, the Lakeview reservoir presents three areas of interest, as shown on Fig. 3. Area I in section 32 is a region in which a productive Sub-Lakeview Miocene sand is present. It occurs from 10 feet to 30 feet below the base of the Lakeview sand and attains a maximum thickness of 25 feet in Well No. 21, section 32. The producing characteristics of the Sub-Lakeview Miocene sand differ radically from those of the Lakeview sand. Water production at high structural locations and abnormally high fluid levels indicate that there was no communication with the Lakeview sand. Wells in Area I penetrated this sand and produced it in conjunction with the Lakeview sand. In Area 11, the Lakeview sand is a

Jan 1, 1950

By I. R. Kramer, L. J. Demer

Aluminum single crystals were pulled in an electrolytic cell allowing surface removal during the deformation. The extent of Stages I and 11 of the stress-st-aitz curve was increased and the slope decreased as the rate of metal removed from the surface was increased. An increase of the strain rate caused a decrease in the effectiveness of the metal removal. The data indicate that the work-hardening coefficient in Stage I is determined primarily by the conditions which exist on the surface of the crystal. In Stages 11 and 111, both surface effects and internal barriers are important. ALTHOUGH numerous investigations have been conducted on the plastic flow characteristics of metals in an attempt to explain the mechanism of work-hardening, relatively few studies have taken into account the influence of the surface. In all current theories of work-hardening it is assumed that the impediments to the movement of dislocations are within the crystal. The barriers due to the surface and the existence of solid and liquid films have been neglected even though it has been demonstrated that the surface exerts a large effect. A number of investigators1-l8 have shown that solid films on the surface of single crystals markedly affect their mechanical behavior. In general, the presence of a solid film tends to increase the yield stress and increase the work-hardening rate. Often, on single crystals, Stage I and, at times, Stage II regions are completely suppressed. Various mechanisms have been offered for the effects of oxide and metal films as well as the influence of electrolytes. Of these, concepts concerned with the locking of surface dislocation sources and the blocking of dislocations at the surface resulting in pileups appear to be actively considered at present. Barrett,11 Takamura,6 Gilman,19 Lipsett and King,20 Shapiro and Read,10 and Weiner and Gensamer21 are among those who have interpreted their results in terms of piled-up dislocations at the surface, while Adams.22 and Chalmers and Davis23 have explained their experimental observations in terms of locking of surface dislocation sources. In general, the change in plastic flow properties due to electrolytes has been explained in terms of the unblocking or unlocking of dislocations by the removal of the oxide films. In considering the two proposed mechanisms, it appears that the locking of sources of surface dislocations by a solid film should exert a primary influence only on the critical resolved shear stress for flow and not on the slopes of Stages I and 11. However, the blocking at the surface of dislocations from internal sources may also affect the critical resolved stress and furthermore exert an influence throughout the whole plastic range. In certain cases it does not seem feasible to explain the results of experimental observations in terms of locking of surface dislocation sources. The abnormal aftereffects found by Barrettll,12 by removing the oxide by an acid treatment are excellent evidence of the blocking of dislocations at the surface. Additional evidence in favor of a blocking due to a pileup of dislocations at the surface may be found from the observations that the critical resolved shear strength continues to increase with the thickness of the oxide layer until very heavy oxide layers are formed. If the locking of surface dislocations sources were the dominant factor, the critical resolved shear stress would not be expected to increase after all of the surface sources were locked by the formation of the oxide. This may be expected to happen after a few atomic layers of the oxide are formed. In spite of the above evidence on the strong influence of the surface on the plastic flow characteristic, this has been ignored in current theories of work-hardening. Seeger24,25 suggested that most of the dislocations may slip out of the crystal only when the specimen axis is within certain areas of the orientation triangle. In other areas the resolved shear stress in other glide systems is large enough to generate dislocations which can form Lomer-Cottrell locks, thereby decreasing the average slip distance in some directions and causing a larger hardening rate. Friede126 assumed that at the beginning of Stage 11, a large number of Lomer-Cottrell dislocations are formed by a catastrophic process which used up all the Frank-Read sources on the secondary slip-planes. In this manner a fixed number of Lomer-Cottrell locks is formed which act as barriers against which the dislocations can pile up. In Stage 111, Seeger24 and Diehl, Mader, and Seeger25 proposed that Lomer-Cottrell barriers are circumvented by the cross slip of extended screw dislocations. Cottrell and Stokes,27 Friedel,26 Cottrell,26 and stroh29 suggest that the Lomer-Cottrell dislocations collapse under the stress field of the dislocation pileup. It is the purpose of this paper to report the changes in Stages I, II,and III of the deformation process in

Jan 1, 1962