By R. G. Davies, R. H. Richman

Several techniques, X-ray diffraction, transmission electron microscopy, conventional, metallography, and mechanical property measurements are combined to investigate decomposition in the suPersaturated solid solution Fe-27 at. pct Be. The following sequence of structures for aging temperatures below 400°C is established: massive short-range order, pseudo-FeBe (L2o) order, Fe3Be (DU3) order, sinusoidal modulation of composition, general or continuous precipitation, and discontinuous or cellular precipitation. In addition to this sequence itself, several features of the individual stages are noteworthy; for example, when coherent modulations occur, their development is parallel to (100) everywhere in the specimen apparently without incubation, and both the wavelength and the composition amplitude of the modulations increase with aging time. Two types of discontinuous reaction are observed, depending upon the aging temperature. At low temperatures (<550°C) the boundary-nucleated variety of discontinuous precipitate predominates; but at higher temperatures (>600°C) the crystallographic variety occurs instead. Hardness and flow-stress measurements clearly reflect the quoted structure sequence. Some qualitative aspects of the structure changes and of the relationship between mechanical properties and structure are discussed. BERYLLIUM in solid solution markedly strengthens iron.&apos;" A recent study demonstrated that not only were supersaturated single crystals of Fe-27 at. pct Be very strong, but they deformed primarily by mechanical twinning.3 Such behavior, coupled with the decrease in solid solubility of beryllium in a Fe from about 33 at. pct at 1165°C to about 10 at. pct at 500°C4 as shown in Fig. 1, leads naturally to questions about property changes with aging in this system. In 1929 roll,1 and later Seljesater and Rogers,5 reported that useful increases in strength could be obtained by aging quenched Fe-Be alloys, but it was not until quite recently that any of the details of precipitation in these alloys were studied. Richman6 observed that both an Fe3Be superlattice (with a DO3 crystal structure the same as Fe3A1, illustrated in Fig. 2) and a modulated structure preceded the appearance of a discrete second phase in the 20 at. pct Be composition. Here, a modulated structure refers to a periodic composition fluctuation within one crystal, while its lattice remains coherent. Subsequent work on a Fe-Be alloys by Heubner7 and von Heimendahl and Heubner8 confirmed the existence of the modulated structure, although only an FeBe (L20) ordered structure was detected (also shown in Fig. 2). Both Rich-man and Heubner corroborated the large increases in hardness during aging reported earlier, but other mechanical properties were not examined. Since modulated systems are encountered relatively infrequently, the influence of coherent modulation upon mechanical properties is not well-known. With the accumulation of information about age-hardening systems, it has become clear that many precipitation reactions cannot always be described by the concept of heterogeneous nucleation at some lattice discontinuity followed by diffusional growth. Rather, complex sequences involving prior "preparation" of the matrix are quite common; that is, a transition structure occurs in the parent phase, instead of in some "nucleus" form. Delineation of such subtle sequences appears to be a worthwhile step toward the understanding of solid-state precipitation. Since not many structural progressions of comparable nature have been reported, the objectives of the present survey are to identify and elucidate the various

Jan 1, 1967

By M. E. V. Plummer, F. E. Beamish, J. C. Hole, J. M. Kavanagh

Prior researches have shown that the iron-copper-nickel content of platinum concentrates may be reduced by carbon to form a collecting alloy for the platinum metals in a manner exactly analogous to the formation of the lead fire assay button. The nature of the iron-copper-nickel alloys with the platinum metals has been investigated. Palladium and probably some of the other platinum metals form solid solutions with this alloy. ONE of the greatest known reserves of the platinum metals is to be found in the nickel, copper, iron sulphide deposits of Northern Ontario. The very large tonnage of copper-nickel ore processed makes the Sudbury district a significant world source of the platinum metals, the latter being recovered as byproducts in the electrolytic refining process for copper and nickel. Chalcopyrite, pentlandite, and pyrrhotite are carriers of the platinum metals;&apos; these minerals contain from 0.03 to 2.0 ppm of the noble metals. The analysis of the above ores for the platinum metals necessitates an initial concentration of the minute quantities present in the ore. The method usually employed involves the extraction of the noble metals by molten lead with or without small proportions of silver. The lead is then separated from the precious metals by cupellation, a process which involves absorption by the cupel and volatilization of lead oxide, leaving the precious metals collected in a silver bead on the surface of the cupel. The collection by lead is probably achieved by a process of dissolution followed by some degree of segregation in the lead alloy since the cold button is seldom uniform in composition. With silver-lead alloys this process of liquation has been used to re- cover pure lead since, during the cooling period, crystals of pure lead separate and silver becomes concentrated toward the center of the solid.&apos; Platinum and gold liquate in a manner similar to silver which may account for the successful recovery of platinum by fire assay even though it is considered insoluble in a solid lead medium. 3 In the case of iridium the liquation process may be a disadvantage in that the iridium may appear in the outer areas of the button and thus be lost mechanically during the handling processes. In any case the deficient alloying characteristics of lead for the platinum metals encouraged attempts to find an improved collecting alloy, and by analogy with aqueous extractions, preferably one in which solid solutions would be readily formed. Since, beyond a certain minimum solute to solvent ratio, the formation of a solid solution is accompanied by a lattice distortion, one would expect some relationship between the atomic diameters of any two metals and their tendency to form a solid solution. In one survey5 the hypothesis was put forward that when the atomic diameter of the solute differs by more than about 15 pct from the solvent, the "size factor" is unfavorable and the formation of a solid solution is restricted. On the other hand, when the atomic diameters are within this limit the size factor is favorable and solid solutions are readily formed, e.g. the transition metals of Group VIII having similar radii form solid solutions over wide ranges of composition.6 Even with a favorable size factor, elements having different crystal structures cannot form a continuous series of solid solutions. Cell dimensions alter as the concentration of the solute increases, causing a

Jan 1, 1962

By A. T. Chatas

A description of the geometrical characteristics of spherical reservoir systems, a discussion of unsteady-state flow of such systems and examples of engineering applications are presented as backgmund material. The fundamental differential equation, a description of average spherical permeability and the introduction of the Laplace transformation serve as theoretical foundations. Engineering concepts are investigated to indicate particular solutions of interest, which are analytically obtained with the aid of the Laplace transform. These are numerically evaluated by computer, and presented in tabular form. INTRODUCTION A tractable mathematical analysis of unsteady fluid flow through porous media generally requires incorporation of a geometrical symmetry. The simplest forms include the linear, cylindrical (radial) and spherical. Most analytical endeavors have concentrated on cylindrical symmetry because it occurs more often in petroleum reservoirs. Nevertheless, some reservoir systems do exist that are better approximated by spherical geometry. Review of technical literature revealed but a single reference to unsteady spherical flow in petroleum reservoirs.l The motive and purpose of the present work was to remove this gap in technical information, and to provide the practicing engineer with some useful analytical tools. The mathematical details associated with the particular solutions of interest involved use of the Laplace transformation. Hurst and van Everdingen previously demonstrated the efficacy of this operational technique, and in many respects the present treatment was patterned after their earlier work.2 PRELIMINARY CONSIDERATIONS GEOMETRICAL CHARACTERISTICS Geometrically, a spherical reservoir system is defined at any instant of time by two concentric hemispheres whose physical properties of interest vary only with the radial distance. Every physical property is thus restricted to be a space function of only one variable: the distance along a radius vector emanating from the center. Such a system is composed of an outer region and an inner region, separated by a defined internal boundary. The inner region simply extends inward from this boundary, whereas the outer region extends outward from it to an external boundary. The position of the internal boundary is presumed fixed, so that the size of the inner region remains constant. On the other hand, the position of the external boundary at any given instant of time is determined by the distance into the system that a sensible pressure reaction has occurred, Thus, the external boundary may change position with time. It initially emerges from the inner region and advances outward to its ultimate position. When this ultimate position coincides with a geometric limit, the reservoir system is said to be limited. When it coincides with points subject to pressure gradients furthest removed from the internal boundary, yet short of a geometric limit, the system is said to be unlimited. In this investigation two different boundary conditions are imposed at the ultimate boundaries of limited systems. The first requires that no fluid flow occur across this boundary; the second that the pressure remain fixed at this boundary.3-5 UNSTEADY-STATE FLOW In a strict sense virtually all flow phenomena associated with a reservoir system are unsteady-state. The transient behavior of these phenomena requires accounting, however, only when time must be introduced as an explicit variable. Otherwise, steady-state mechanics may be used. Analytically, steady-state conditions prevail in a reservoir system only over that portion of its history when this relation is satisfied:

Jan 1, 1967

By B. Ramaswami, U. F. Kocks, B. Chalmers

This paper describes the tempetrature, solute (gold), and orientalion dependence of the plastic rleforlirnlion of silver single crystals. The virgin flow stress, To, and its temperatutre dependence incrense with increase in solute concentration. el decreases with decrease in temperature below room teiirperature and with increase in solute coucentralion. The dependence of 011 on temperature arid solute sontenl is due to the dependence of Ts on the two variables. An increase in ts, due to either the temperature or the solute conlent, results in a decrease of e11 in crystals of single-slip orientation and an increase of 011 in crystals of&apos; (100) find (111) orientation. is orientation-dependent and at all the temperatures and in all the materials studied. The Leveling off of the engineering stress-strain curve in crystals of (100) 07-ientotion at a stress tl, is associated with extensive cross slib. The temperature and strain -rate dependence of tl are similar to those of indicating that a rate process is the cause 01 this phenomenon. The plastic deformation of silrer crystals of (110) orientation is multiple to that of crystals of single-slip orientation. THE work hardening of fcc crystals has been the subject of intensive investigations in the past 15 years. The effect of orientation, deformation temperature, solutes, second phase or precipitates, strain rate, etc., has been studied in a number of fcc metals.&apos;-5 In spite of the considerable amount of work reported on the dependence of work hardening on the orientation, temperature, and solute concentration, certain aspects of the plastic deformation of fcc crystals have not been clarified. For instance, with the exception of a few investigations,6-8 where crystals of multiple-slip orientations have been studied, almost all the studies have been on crystals of single-slip orientations. Hence, a major portion of this study has been devoted to the dependence of plastic deformation on the multiplicity of slip systems and the enhanced possibility of dislocation interactions resulting from such multiplicity. Further, the abnormally low rate of work hardening observed at large strains at certain temperatures in crystals of the (100) orienta-tion 6-8has not been explained satisfactorily. It is the aim of this study to clarify this aspect of the orientation and temperature dependence of the plastic deformation of fcc single crystals. The work-hardening characteristics of single crystals of aluminum of ( 110) orientation have been studied at room temperatur "&apos;12 and above." They have not been studied at temperatures where the virgin flow stress is dependent on temperature or where, in Seeger&apos;s terminology is important. The work hardening of single crystals of (110) orientation is of interest for another reason. As shown in Table I, the dislocation reactions that are possible in the (110) orientation are similar in certain respects to those that are possible in the (100) orientation. Hence, the deformation of single crystals of silver of (110) orientation was studied in the temperature range 100° to 900°K at intervals of 200°K. The effect of solute concentration on the plastic deformation of fcc single crystals of single-slip orientation has been studied by several investiaators.> In all of these investigations—with the exception of Ref. 20—single crystals of identical orientation have not been used, with the result that the orientation dependence of plastic deformation is superimposed on the effect of the solute. In addition, the effect of the solute on the work-hardening characteristics of single crystals of multiple-slip orientations has not been studied by the previous

Jan 1, 1965

By A. L. Labbe, J. J. Donoso

Hard-won experience in the operation of smelting plants has pointed the way to the most efficient design and economical operation of a baghouse system for recovery of metallurgical fumes. This paper treats of the principles governing bag filtration and the factors most directly affecting bag life. Methods for temperature conditioning of smoke previous to filtering are described and the evolution of bag shaking mechanisms is brought up to date. THE history of the bag filter process, as applied to the recovery of metallurgical fumes, goes back to 1876, when the Lone Elms Works of Joplin, Missouri, erected a two-section baghouse for filtering fumes from Scotch Hearth lead smelting furnaces. By modern standards this installation was crude, but the basic operating principles remain essentially the same today. Great progress, however, has been made in the mechanization of the process by the use of devices for mechanically and automatically cleaning bags of adhering fumes, in the use of instruments for recording and controlling the variables affecting baghouse operation, and in the conditioning of the smoke previous to filtering. The principles governing bag filtration of fumes were investigated in 1929 by A. J. Seitz of American Smelting and Refining Co., and he arrived at the following conclusions: 1. Pressure on Bags at Constant Volume: The rate at which the pressure builds up in a bag with constant volume is directly proportional to the time, with the same kind of smoke and dust burden (fig. 1). 2. Pressure on Bags for Change in Volume: With equivalent smoke and dust burden, the bag pressure increases with the square of the increase in volume. The rapid increase in pressure is due to (1) increase in volume, (2) increase in amount of dust on the bag, and (3) more intense packing of the dust at higher velocity (fig. 2). 3. Effect of Intensive Filtering on Pressure: Since the pressure builds up directly as the square of the volume, with the same smoke and dust burden, it is necessary to shake the bags in that increased ratio, and vigorously, to keep the pores of the bag open and pressure down. This increases the wear on the bags and the dust losses. 4. Effect of Shaking on Dust Losses: The losses are in direct proportion to the frequency of shaking because the loss takes place immediately after shaking, before the bag seals itself. Tests show that with hand shaking the last 20 pct of the removable dust requires seven times more shaking per unit weight of dust than the first 80 pct. 5. Effect of Fineness of Dust on Losses: The fineness of the dust particle increases the loss in two ways: (1) When the bag is clean a greater percentage of it will pass through before the bag seals itself; (2) fine material penetrates farther into the bag pores, building up pressure faster and necessitating more shaking, thereby increasing the loss. The physical principle of operation of the bag filter is simply the separation of solids from a gaseous carrier through a porous medium, and is analogous to the filtration of solids from liquid carriers. Basically, the mechanics of the process are as follows: Fume-laden gases drawn from the operating fur-

Jan 1, 1951

By Allen F. Agnew

Detailed stratigraphic studies in the Wisconsin-Illinois-Iowa district have made it possible to map the folds and faults that controlled the deposition of the zinc-lead ore. Prospecting on the basis of this mapping and prospecting in lower zones that are potentially ore-bearing have led to discoveries of ore. GEOLOGIC studies for the Federal and State governments in the Wisconsin-Illinois-Iowa zinc-lead district were begun in 1835, and subsequent surveys were made in the three states at intervals until 1916, see Table I. The current study of the district, Fig. 1, by the U. S. Geological Survey was begun in 1942 in the hope that a systematic investigation would help increase production of zinc and lead, then in extremely short supply. Major emphasis of the USGS program was on detailed mapping of the geologic structure and ore deposits. Preliminary maps and reports covering localities of intensive mining activity have been published during the course of this study, Fig. 2. By 1950 the objectives of the study by the USGS were revised; 71/2-min quadrangles of relatively unprospected localities as well as intensively mined localities are now being mapped in Wisconsin. Since 1945 the investigation in Wisconsin has been made in cooperation with the Wisconsin Geological and Natural History Survey, and since 1951 the geologic mapping of areas of particular interest in Iowa has been performed in cooperation with the Iowa Geological Survey. At intervals since 1943 the Illinois State Geological Survey has mapped the geologic structure and ore deposits of localities in the Illinois part of the mining district, see Fig. 2. Geology was applied by mining company personnel as early as 1853, but only sporadically, with periods of greater application between 1890 and 1925. Much of the so-called geologic work was in reality mining engineering. Since 1946 the major mining companies in the district have employed geologists who have successfully applied geologic techniques in the search for ore. History of Mining Occurrence of galena in the district was known as early as 1658 or 1659, when French explorers heard of lead mines that were apparently in the vicinity of Dubuque, Iowa. In 1690 a trading post was established near Dubuque to obtain galena. The first significant attempt at mining by white men took place in 1788 when the Indians granted to Julien Dubuque mining rights for 20 miles along the west side of the Mississippi River, including the vicinity of Dubuque, Iowa. By 1805 lead was being mined near Galena, Ill. In 1819 permanent settlement of the region was begun, and most of the important lead-producing areas had been found by 1830, see Fig. 3. Lead production in the Wisconsin-Illinois-Iowa district between 1830 and 1871 far exceeded that of any other district in the U. S.&apos; Smithsonite was first mined in 1859, and sphalerite was mined as early as 1867. After 1873 the production of sphalerite exceeded that of smithsonite. In 1873 annual zinc production from the district first equaled lead production, and from then until 1893 production of zinc and lead was roughly the same. Since 1893 the ratio of zinc to lead mined has generally ranged between 5:l and 20:l. In 1942 the Wisconsin-Illinois-Iowa zinc-lead district ranked 14th among zinc-producing districts of the U. S. From 1946 until February 1953 the dis-

Jan 1, 1956

By William R. Barton

Iron and steel slag represent man&apos;s most successful attempt to date to profitably utilize a solid waste. Its consumption represents a solution to a solid waste problem and also represents tonnage of natural aggregates that will not have to be mined with concomitant disturbance of the land. Slag has been produced as long as iron has been made; but until a little more than 50 years ago, it was mostly a waste product to be disposed of with as little effort and cost as possible. Huge piles of waste slag were generated over the years of iron and steelmaking. Sporadic use was found for small amounts starting with slag (from Catalan forges) used for road bases by the Roman Empire. The first recorded sustained commercial use was, as is often the case in man&apos;s history, for making war. Some profit- conscious munitions maker in the 16th century realized that he could make cannon balls of slag instead of the more precious iron. Other small-volume uses gradually developed: cast building blocks, slag-lime mortars and cements, slag wool, ballast, road base, and, finally, in concrete. But it was not until after World War II that the true potential of blast-furnace slag as a construction aggregate was really recognized. Now nearly all blast-furnace slag produced is used, and much of the earlier stock- piles in the U. S. have been reduced or entirely consumed. Steel slag for aggregate use has been in commerce for only the past 10 years, and use has increased rapidly (10-50% per year) during the past 5 years as blast-furnace slag supplies became depleted. However, much remains to be accomplished in determining character and optimum conditions of use for various types of steel slags before such slags will realize their full use potential. Although slag represents only 2% of construction aggregate materials used in the U.S., its production involves certain features that make its production record far more important than national tonnage figures would indicate. Its source is in iron and steel production and concomitantly slag availability is restricted to those areas where iron or steel is produced. In such areas, it often represents one of the principal aggregates marketed and, because of special properties that make slag a selected aggregate for certain uses, the tonnage imbalance may be overcome by the importance of its contribution to quality or special characteristics of end products. The location and number (Fig. 1) of slag plants handling this annual production is governed by the geographic makeup of the iron producing industry. Prior to the period marked by World War 11, most blast furnaces were in the Great Lakes area-Pittsburgh, Cleveland, Chicago, Gary, Buffalo, Detroit, Youngstown, and Toledo, with exceptions at Baltimore, Bethlehem, and Birmingham. Since that time, iron and steel facilities have been established in Texas, Utah, and California. Today 85 slag plants in 15 states provide employment for almost 2000 persons. The slag plants also recover almost 4 million tons of slag-encrusted iron each year for return to the blast furnaces. Much of the success in developing uses for slag can be attributed to the efforts of the National Slag Association founded in 1918. Since then, it has conducted numerous field and laboratory investigations to demonstrate the properties and uses for slag and slag products. These investigations have resulted in total recognition of blast-furnace slag as a construction material of consequence. The American Society for Testing & Materials Designation C125 recognizes blast-furnace slag as "the nonmetallic product consisting essentially of silicates and aluminosilicates of

Jan 1, 1975

By E. Hein, R. A. Dodd

The fatigue softening of prior strain-hardened poly crystalline copper has been determined by measuring changes inflow stress resulting from fatigue treatments. Tensile fatigue does not soften the metal, while the softening due to reversed stress fatigue depends on the extent to which fully reversed stressing is approached. True tensile fatigue is shown to be possible only in the case of long wire specimens. Annealing following fatiguing of strain-hardened metal shows that tensile fatigue is very effective in modifying normal recovery and recrys-tallization. OBSERVATIONS by Ludwik and Scheu,&apos; Kenyon,&apos; Polakowski and Palchoudhuri, Kemsley, and Broom and Ham,596 have shown beyond doubt that strain-hardened metals are softened by reversed-stress fatigue. To some extent the softening might be associated with a rearrangement of dislocations, but the results of Broom and Ham5 on the temperature dependency of the fatigue hardening of annealed copper, and those of McCammon and Rosenberg7 on the partial recovery at 100&apos;C of fatigue-hardened copper suggest that point defects may be involved. Since lattice vacancies are the only species of point defect present in appreciable quantities in thermody-namic equilibrium, most attention has been accorded them in the various theories advanced to explain hardening and softening effects resulting from fatigue. Precise mechanisms remain uncertain, and while some effects may be due to single vacancies, defects arising from vacancy clusters may also contribute to the changes in properties. All types of plastic deformation result in point-defect formation, one frequently invoked formation mechanism involving the nonconservative motion of jogs formed by the intersection of, for example, mixed dislocations. But since fatigue deformation is thought to be a particularly effective way of forming point defects, additional mechanisms peculiar to fatigue must be sought. One possibility is that jogged loops contract during the unloading cycle to give rows of vacancies. A local high-vacancy concentration could conceivably promote polygonization and recovery by climb, and, therefore, could explain the fatigue softening of strain-hardened metals under appropriate conditions of temperature. Conversely, the experiments by Broom and Ham6 on the fatigue hardening of copper single crystals involving subsequent tensile testing of previously fatigued specimens, resulted in the observation of distinctly lowered yield points. This could be due to vacancy atmospheres associated with dislocations, possibly augmented by jogs on dislocations. In addition to the yield-point phenomenon, a post-yield hardening was observed, with a temperature-dependence resembling the friction-hardening of irradiated metals,9 this again suggesting a point-defect mechanism. An important development in this field has been the observation,10 by transmission electron microscopy, of high concentrations of prismatic loops in fatigued aluminum. By analogy with quenched aluminum filmso11 it seems certain that these loops originate in the collapse of vacancy clusters formed during deformation. Metals, such as copper, having a relatively low-stacking fault energy would tend to produce Frank sessile loops (in practice tetrahedral defects with stacking faults on all (111) planes) rather than the glissile prismatic loops observed in aluminum. The manner in which these various defects affect the different aspects of fatigue behavior has not yet been fully investigated. The present work was designed principally to indicate whether tensile fatigue gives rise to hardening and softening effects similar to those associated with reversed stress fatigue, and with the hope of providing additional information on the contribution of point defects to fatigue deformation. Despite the uncertain ty often associated with the interpretation of resistivity data, i.e., the relative contribution of stacking faults and other defects, such measurements are conveniently employed to study point defect pheno-

Jan 1, 1962

By D. L. Albright, R. W. Kraft

Solidification experiments were conducted with the objective of testing the theory of eutectic colony formation. Appropriate control of variables in tests on a series of high-purity aluminum-copper specimens of eutectic composition resulted in the observation of three types of eutectic microstructures, these being a unique structure consisting of lamellae essentially parallel to one another, a banded structure, and the colony structure. Lamellar faults, which are morphologically similar in many respects to edge dislocation models in crystals, produced a complex substructure in these specimens. SOLUTE rejection at the advancing solid-liquid interface of a unidirectionally solidified single-phase metal can cause the liquid immediately in front of the interface to become constitutionally super-cooled below the equilibrium liquidus temperature. Constitutional super-cooling occurs if the solidification rate, R, is too rapid, or if the thermal gradient in the liquid at the interface, G, is too low. 1 This constitutionally supercooled layer in turn stabilizes a cellular rather than a planar interface.&apos; A similar cellular interface has been observed when lamellar and other types of eutectics were unidirectionally solidified, and it has been shown that the cellular interface led to the formation of eutectic colonies.&apos; The lamellar structure is fan-shaped at the edges of colonies (which correspond to valleys or grooves in the cellular interface) because the lamellae grow normal to the local interface. One of the possible mechanisms which might cause the formation of the cellular interface, in the case of solidifying eutectic alloys, is constitutional supercooling of the liquid with respect to a third component rejected by both phases of the eutectic.3,4 On the basis of the analogy between the solidification of single-phase metals and binary eutectics, a eutectic alloy should solidify with a planar interface if the ratio of G/R is sufficiently high to compensate for any impurity which might be present and causing constitutional supercooling. The fan-like microstruc-ture of eutectic colonies should not occur under these conditions and the lamellae should be parallel to one another and to the solidification direction for extended distances. The experiments conducted in this investigation were designed to test these ideas. Following a resume of the experimental procedure, the various microstructures observed during the study are described, and their relationship to the growth conditions which produced them is discussed. EXPERIMENTAL PROCEDURE The eutectic between an aluminum solid solution and 0 phase (approximate composition CuA12) was chosen for this work for the following reasons: it was known that a lamellar structure forms, the eutectic temperature is low enough to facilitate experimental work, and the components can be procured commercially in a very pure form. High-purity copper (est. 99.999 pct Cu, obtained from National Research Corp.) and spectrographic aluminum rods, having impurities other than copper estimated to be Zn-15 ppm, Mg-10 ppm, Fe-3 ppm, Na-2 ppm, Cd-1 ppm, and Mn < 1 ppm, were melted in a stabilized zirconia crucible in a vacuum induction furnace at a pressure of 10 pof Hg. The melt was superheated to about 1000°C to assure mixing, cooled to 780°C and cast into an investment mold which yielded sixteen cylindrical specimen blanks 1/2 in. in diam and 5 1/2 in. long. The casting was allowed to solidify under vacuum. This master heat had an analysis of 32.6 wt pct Cu and 67.4 wt pct A1 by difference. The cylindrical specimen blanks were remelted and solidified unidirectionally in an apparatus illustrated schematically in Fig. 1. An RF induction coil heated

Jan 1, 1962

By M. E. Wadsworth, J. R. Lewis, J. M. Quets

Samples of snythetic magnetite were reduced in hydrogen at various partial pressures and temperatures. The reaction mas found to be surface controlled and directly proportional to hydrogen partial pressure over the temperature range studied (400° to 1000°C). A transition in the mechanism occurred at approxirnately 590°C. This has been attributed to a change in the slow step of the reduction reaction resulting from the presence of stable wüstite at higher temperatures. Below 590°C the heat of activation for the reduction was found to be 14,700 cal per mole and it was 3,200 cal per mole above 590°C. THE reduction of the oxides of iron has been a subject of study and interest for many years. Edstrom1 has reviewed the work up to 1953 and his findings provide much basic information concerning details of the reduction of hematite (Fe2O3 ) and magnetite (Fe3O4) with both H2 and CO. He concluded that below 600°C the reduction of both hematite and magnetite was essentially identical, since the rate was controlled by a surface reaction at a magnetite gas interface and the iron formed was very porous. The decrease in the reduction rate for both hematite and magnetite immediately above 600°C was attributed to the formation of a stable wüstite phase across which diffusion was very slow. The wide difference in reduction kinetics for hematite and magnetite above 600°C was explained in terms of the character of the wüstite formed. The rate of magnetite reduction increased slowly with temperature beyond the minimum immediately above 600°C and rates equivalent to those observed at 550°C were not obtained until the temperature was increased beyond 850oC. Edstrom and Bitsianes2 studied the solid-state reduction of magnetite, the reaction of which can be written (4x-3)Fe + Fe3O4—4 FexO [1] where x is between 0.83 and 0.95. The rate was found to be controlled by the kinetics of transport of iron ions through the wüstite phase. Bogdandy and Riecke3 studied the kinetics of reduction of small grains of iron oxide in hydrogen and qualitatively attributed the slow step in the reduction process to the diffusion of hydrogen and water vapor through pores. McKewan4 has analysed the data of Joseph,5 Stalhane and Malmburg,6 and Lewis7 and has demonstrated that the kinetics of reduction of both hematite and magnetite are controlled by surface reactions and also that the variation in surface area during reduction must be accounted for. McKewan was able to correlate the reduction data by the equation rodo[1-(1-R)1/3] = Kt [2] where ro is the initial particle radius, do is the density of the iron oxide, R is the fraction reduced at time t, and K is a rate constant. The applicability of Eq. [2] for temperatures above 600°C where a stable wüstite phase is present, indicates the slow step in the over-all kinetics does not result from diffusion unless diffusion occurs laterally along the oxide metal interface or through a wüstite layer of constant thickness. Diffusional control through a layer of wüstite is unlikely, however, in view of the pressure effects demonstrated by Tenenbaum and Joseph,&apos; Diepschlag,9 McKewan,10 and the results of the present study. McKewan has demonstrated a linear rate dependence on the hydrogen partial pressure over the temperature range 400" to 1050°C for the reduction of hematite.

Jan 1, 1961

By Joseph L. Gillson

BRAZIL has had an industry based on ocean beach deposits of heavy minerals containing monazite, zircon, rutile, and ilmenite for well over 40 years, but except at the very earliest period, prior to 1906, and again during World War 11, has this industry been at all comparable in size with similar operations in other countries. Limiting factors have been neither a lack of reserves nor lack of markets (except for zircon). Although poor local transportation and shipping facilities have handicapped the development in Brazil, these conditions were perhaps equally bad (when mining operations started) in the Indian State of Travancore, and in New South Wales and Queensland, Australia, in which states the principal production of beach deposits of heavy minerals has occurred. The outstanding restraints on the Brazilian industry have been the lower quality of the Brazilian minerals, the relative small size of individual deposits that were known until recently, the lack of interest of Brazilian investors in mining ventures, and the unfavorable climate for investment of foreign capital under Brazilian mining law. The lower quality of the minerals is indicated by the fact that the Brazilian monazite carries only 5 to 6 pct Tho2*, and the ilmenite 561/2 pct TiO2, whereas the corresponding Travancore minerals carry 9 pct Tho, and 60 pct TiO, respectively. The Brazilian zircon is a dirty brown color (which can be removed readily) as compared with the gleaming whiteness of the Australian zircon. An inadequate market for the abundant zircon that will be available in any operation in Brazil is certainly a heavy restraint, since otherwise it could be an important byproduct. The oxide of zirconia, baddeleyite, that has come from Brazil is from other sources.&apos; Since the Brazilian beach sands carry only a little rutile, that mineral has not been available as a valuable byproduct to help finance the operations. Substantial tonnages of rutile have been exported from Brazil. The sources of this mineral are stream placers and residual deposits over gneisses in the States of Goyaz, Minas Geraes, Ceara, etc. (Leonardos,&apos; and Chambers". With these handicaps, Brazilian production from beach sands has been marginal, and there has been only one consistent producer. This is a company, originally French, which was called Companie de Franco-BrazilliCne, but, with the downfall of France in 1940, became Brazilian under the name Monazita e Ilmenita do Brasil ("Mibra"). This company has operated several deposits in the vicinity of Guara-pary, in the State of Espirito Santo. Its office and plant has been at Guarapary. Recently a company called, "Fomil" (Fomento Monazita-Ilmenita) started operations. This company was organized by the Foote Mineral Co. of Philadelphia, and such share as a foreign company can hold under Brazilian law has now been acquired by the Lindsay Light and Chemical Co. of Chicago. When the writer went to Brazil in the fall of 1940, he found that no general survey of the beaches had been made except for a thorough study of part of the area by Abreu.4 The paper by Miranda6 had not then been written. The federal Geological Survey and Department of Mines knew only of the existence of the deposits in Espirito Santo south of Vitoria, and had a hazy idea that others might be found north of Vitoria. One deposit in Bala was known in Rio, but the larger one at Guaratiba was not known, although a Frenchman had prospected

Jan 1, 1951

By Joseph L. Gillson

BRAZIL has had an industry based on ocean beach deposits of heavy minerals containing monazite, zircon, rutile, and ilmenite for well over 40 years, but except at the very earliest period, prior to 1906, and again during World War 11, has this industry been at all comparable in size with similar operations in other countries. Limiting factors have been neither a lack of reserves nor lack of markets (except for zircon). Although poor local transportation and shipping facilities have handicapped the development in Brazil, these conditions were perhaps equally bad (when mining operations started) in the Indian State of Travancore, and in New South Wales and Queensland, Australia, in which states the principal production of beach deposits of heavy minerals has occurred. The outstanding restraints on the Brazilian industry have been the lower quality of the Brazilian minerals, the relative small size of individual deposits that were known until recently, the lack of interest of Brazilian investors in mining ventures, and the unfavorable climate for investment of foreign capital under Brazilian mining law. The lower quality of the minerals is indicated by the fact that the Brazilian monazite carries only 5 to 6 pct Tho2*, and the ilmenite 561/2 pct TiO2, whereas the corresponding Travancore minerals carry 9 pct Tho, and 60 pct TiO, respectively. The Brazilian zircon is a dirty brown color (which can be removed readily) as compared with the gleaming whiteness of the Australian zircon. An inadequate market for the abundant zircon that will be available in any operation in Brazil is certainly a heavy restraint, since otherwise it could be an important byproduct. The oxide of zirconia, baddeleyite, that has come from Brazil is from other sources.&apos; Since the Brazilian beach sands carry only a little rutile, that mineral has not been available as a valuable byproduct to help finance the operations. Substantial tonnages of rutile have been exported from Brazil. The sources of this mineral are stream placers and residual deposits over gneisses in the States of Goyaz, Minas Geraes, Ceara, etc. (Leonardos,&apos; and Chambers". With these handicaps, Brazilian production from beach sands has been marginal, and there has been only one consistent producer. This is a company, originally French, which was called Companie de Franco-BrazilliCne, but, with the downfall of France in 1940, became Brazilian under the name Monazita e Ilmenita do Brasil ("Mibra"). This company has operated several deposits in the vicinity of Guara-pary, in the State of Espirito Santo. Its office and plant has been at Guarapary. Recently a company called, "Fomil" (Fomento Monazita-Ilmenita) started operations. This company was organized by the Foote Mineral Co. of Philadelphia, and such share as a foreign company can hold under Brazilian law has now been acquired by the Lindsay Light and Chemical Co. of Chicago. When the writer went to Brazil in the fall of 1940, he found that no general survey of the beaches had been made except for a thorough study of part of the area by Abreu.4 The paper by Miranda6 had not then been written. The federal Geological Survey and Department of Mines knew only of the existence of the deposits in Espirito Santo south of Vitoria, and had a hazy idea that others might be found north of Vitoria. One deposit in Bala was known in Rio, but the larger one at Guaratiba was not known, although a Frenchman had prospected

Jan 1, 1951

By W. D. Robertson, A. S. Tetelman

The technique of decorating dislocations was employed to investigate deformation and fracture resulting from Precipitation of hydrogen in Fe-3 pet Si single crystals. It is shown that cracks are produced on (100) planes inside crystals, as a consequence of the precipitation of hydrogen gas, either when crystals are quenched from a hydrogen atmosphere at elevated temperatures or cathodically charged with hydrogen at room temperature. Plastic deformation in the vicinity of cracks, observed as arrays of decorated dislocations, is in conformity with the calculated stress distribution about a crack containing an internal pressure, and the observations provide information permitting a detailed analysis of the mechanics of crack growth. The fracture characteristics of crystals containing internal cracks were evaluated at 25o and -196°C and the results are related to the mechanism of hydrogen embrittlement in terms of the growth of preexisting cracks. HYDROGEN in bee iron or steel produces two characteristic changes in mechanical properties: I), a decrease in ductility (macroscopic strain at fracture) that depends on temperature and strain rate, and 2), spontaneous fracture under static load that depends on time and apparent stress. Resolution of these phenomena into the microscopic processes that combine to produce the macroscopic effects is especially difficult in the Fe-H system in which the active component cannot be directly observed and only maintained in equilibrium with great difficulty in the temperature and pressure range in which embrittlement phenomena appear. As a result of these complications, verification of the numerous hypotheses&apos;-5 that have been proposed to explain the microscopic mechanism of embrittlement depends on self-consistency with measured changes in macroscopic properties that are averaged over the volume of a specimen. It is obviously important to obtain a more direct evaluation of the microscopic processes that combine to produce embrittlement. Accordingly, the present investigation was designed to identify and observe, as directly as possible, the microscopic effects of introducting hydrogen into a bee crystal. It was concluded from a previous investigation6 of X-ray line broadening, produced by introducing hydrogen into pure iron at room temperature, that the only effect that could be associated with the introduction of hydrogen was plastic deformation; in particular, dilation of the lattice was not observed, within ± 0.01 pet, and no evidence was found that could be interpreted to support the idea7&apos;* that hydrogen occupies tetrahedral interstitial sites in the iron lattice. The absence of lattice dilation is consistent with the extremely small solubility of hydrogen in bee iron9,10 (0.015 at. pet at 900oC and 1 atm pressure), and the evidence of plastic deformation is consistent with the fact that hydrogen, introduced by cathodic charging, eliminates the carbon yield point.11-13 Following this investigation, the immediate problem was to devise a method by which plastic deformation could be observed directly. The technique employed by Hibbard and Dunn14 to observe the movement of dislocations during bending and subsequent polygonization of Fe-3 pet Si single crystals was adopted and modified for the present purpose to include the observation of dislocation arrays in the volume of the crystal, and their association with the fracture process. EXPERIMENTAL PROCEDURE Single crystals of a high purity Fe-3 pet Si alloy, containing 0.007 pet C, were grown in vacuum by

Jan 1, 1962

By John R. Keith

Lead and zinc contents of elm, maple, and oak trees and of soils in which the trees grew were determined in samples from the Upper Mississippi Valley mining district, and from an area outside but contiguous to the district. The lead and zinc analyses of plant materials served to differentiate the mineralized and nonminer-alized areas. Stems contained about two times as much lead and about two to five times as much zinc as did leaves taken from the same stems. Lead and zinc analyses of all soil horizons could be used to differentiate between the two areas. Soils at most sample sites in the mineralized district seemed to be more reliable than plants for geochemical prospecting and are a more practical sampling medium. Soil samples from areas with thick loess cover, however, failed to indicate the presence of mineralized bodies whereas tree samples from the same sites contained anomalous amounts of lead and zinc. It is suggested that in areas of thick loess cover, plant samples could be used in prospecting for lead and zinc. The important part that plants play in the cycling of elements through the soil horizons is well-known. The concentration of elements in the upper soil horizons by the action of plants has been called the Goldschmidt enrichment principle.&apos; The fact that plant species vary greatly in their ability to concentrate particular elements in their tissues is also well-known.&apos; Agricultural literature has dealt extensively with relationships of the major nutritive elements in soils and plants3 The extent, however, to which plant actions cycle the minor nutritive and the nonmetabolic elements in the soil has not been adequately investigated. Lead is non-nutritive and toxic to plants, whereas zinc is a micronutrient in low, but toxic in high, concentrations.4 This report presents the results of a biogeochemical study concerned with the amounts of lead and zinc in some plants and soils that occurred both within and adjacent to the Upper Mississippi Valley lead-zinc district. Field work for this study was done in the summers of 1961 and 1962. SAMPLE TARGETS AND CHEMICAL ANALYSES Geologic and physiographic descriptions of&apos; the district have been made by Heyl 5 and several other authors in a series of U.S. Geological Survey (USGS) reports and quadrangle maps.6-I Sedimentary rocks, mostly dolomite, limestone, shale, and sandstone, of Cambrian, Ordovician, and Silurian age predominate in the area. Mineral deposits are of the vein and cavity-fill type; the principal ore minerals are galena and sphalerite. Vegetation of the area was characterized by Curtis1 6 as southern hardwood forest interspersed with patches of oak savanna and prairie. Plant genera typical of the eastern United States Temperate Zone, including ash, cherry, dogwood, elm, hackberry, hickory, maple, oak, and other woody and herbaceous genera, are present. The natural vegetation has been greatly modified by agricultural, logging, and mining operations. The species of the original flora are present, but not in their former relative abundance. Soils of this district belong, for the most part, to the Brunizem and Gray-Brown Podzolic great soil groups. The Brunizems are the soils developed under prairie vegetation.&apos;&apos; The Gray-Brown Podzolics are the soils developed under deciduous forests,18 They are derived from both bedrock and from loess parent materials, and

Jan 1, 1970

By B. L. Averbach, Morris Cohen, S. A. Kulin

The martensitic transformation can be initiated by elastic stresses at temperatures above M. in a steel containing 20 pct Ni and 0.5 pct C. Shear strains and normal tensile strains acting on a potential habit plane promote the transformation but compressive strains oppose it. THE strain sensitivity of the martensitic transformation has long been recognized. It is now well known that martensite formation can be induced by plastic deformation at temperatures below, and not too far above, the M, point.&apos; However, the exact role of elastic vs. plastic strains and of the concomitant stresses has proved to be a very elusive matter. Many investigators2-&apos; of the steel hardening reaction have made use of the stresses resulting from volume changes to account for such observations as the existence of retained austenite and its variation across the section of a bar, the change in the amount of retained austenite with quenching rate, and the self-stopping nature of the transformation when the cooling is stopped. The effect of applied strain as an independent variable has been studied in 70 pct Fe-30 pct Ni alloys by Scheil7 and McReynolds.8 Some data are also available for lithium and Li-Mg alloys,9 Cu-Zn,10 Cu-Sn and Cu-A1 alloys," and aus-tenitic stainless steels."-" It has been found that martensite formation can be induced isothermally, even at temperatures above M,, by mechanical deformation of the parent phase. The competitive nature of plastic yielding by slip and by the martensitic reaction has been depicted by Scheil.7 Basically, Scheil postulated that: 1—at temperatures not too far above M, (where austenite is less stable than martensite), a critical resolved shear stress (within the elastic range) is required to promote the transformation to martensite; 2—at and below M,, the austenite lattice becomes mechanically, as well as thermodynamically, unstable and shears over spontaneously into martensite without the application of external stress; and 3—at temperatures sufficiently far above M8, the critical resolved shear stress for martensite formation increases to a level above that required for slip, and plastic flow then supersedes the transformation when external stress is applied. Scheil&apos;s concepts were tested by McReyno1ds8 ho found no change in the elastic moduli (measured both statically and dynamically) of 71 pct Fe-29 pct Ni alloys in the vicinity of the M, temperature. Since the moduli did not approach zero or become negative on cooling to M,, it was concluded that the austenite lattice does not become mechanically unstable at M2, as postulated by Scheil. McReynolds also reported that M, is not raised by elastic stresses. Accordingly, plastic deformation was considered to stimulate the transformation by generating martensite nuclei in the distorted regions of the parent phase. The above issues with regard to the role of applied stress require clarification, if a basic understanding of the martensitic transformation is to be obtained. For example, in the reaction-path theory,&apos;"," it is postulated that strain embryos exist in the austenite that provide part of the activation energy for the nucleation process. These embryos are visualized to be regions of localized strain in which the atoms in the austenite lattice are displaced part way along the path to their ultimate positions in the martensite. Consequently, it would

Jan 1, 1953

By W. M. McKewan, R. G. Olsson

In order to improve the understanding of the iron oxide reduction mechanism, the rate of equal molar diffusion of hydrogen and water vapor was measured through disks of porous iron and alumina. The measuretneizts were made at atmospheric pressure at 800°, 900- , and 1000°C. It is shown tint the reduction of dense hematite pellets with hydrogen at these temperatures and at atmospheric pressure is to a great extent limited by gaseous diffusion between the bulk-gas phase and the iron-wustile interface. THE investigation of the reduction of iron oxides with hydrogen has been the subject of numerous papers. Although the effects of temperature, pressure, and gas composition on the rate of iron oxide reduction have been studied, the actual mechanism of the reduction process has not been definitely determined. As a means of improving the understanding of the mechanism, the rate of equal molar counterdiffusion of hydrogen and water vapor was measured through porous iron and porous alumina disks at reduction temperatures. The alumina was used as a basis of compari-son because its pore structure is homogeneous and independent of temperature. The porous iron was prepared by the reduction of dense hematite disks with hydrogen at the temperature of the subsequent diffusion experiment. The hematite disks were made from pellets that were identical to those used by McKewan1,2 in his study of iron oxide reduction with hydrogen. In these investigations the weight loss and rate of movement of the various interfaces were measured as a function of the reduction temperature and gas composition. With these reduction data and the presently reported diffusion data it is possible to determine the importance of H2-H2O transport between the bulk-gas phase and the Fe/FeO interface to the reduction of dense hematite. APPARATUS AND PROCEDURE A porous iron or alumina sample was held in the base plate of a sealed canister containing porous granular wustite, as illustrated schematically in Fig. 1. The canister was suspended from an automatic recording balance in a vertical tube furnace through which flowed hydrogen and water-vapor mixtures of known composition at atmospheric pressure (0.96 atm). Hydrogen from the gas stream diffused through the porous sample, reducing the wustite in the interior of the canister. The water vapor that was formed diffused back to the gas stream. The rate of diffusion was determined from the recorded weightloss data. The furnace, automatic balance, and gas-metering equipment have been described previously.2 The main body of the canister and the tubing extension were made of stainless steel while the base plate was made of high-purity iron. The main body of the canister was % in. in diam. It held approximately 6 g of porous granular wustite that was prepared by reducing 0.1- to 0.2-cm-diam specular hematite particles at 900°C with an H2-H2O mixture of a composition near the iron-wustite equilibrium value. The upper end of the 1/8-in.-diam tubing extension was sealed with a segment of plastic tubing and a tubing clamp. The temperature at the top of the furnace was sufficiently high so that no water vapor condensed inside the extension. In the experiments with porous iron, iron oxide samples were prepared from reagent-grade hematite that was pressed and sintered in a manner previously described.&apos; The resulting pellets had a density of 5.15 ± 0.05 g per cu cm. Each pellet was centerless-ground

Jan 1, 1967

By R. E. Miner, J. K. Jackson, D. F. Gibbons

Internal-friction measurements were made during isothermal aging treatments of 18 pct Ni maraging-steel wires between 420° and 612°C. A sharp initial drop in the internal-friction level was interpreted in terms of a rapid dislocation recovery reaction. The rate of the recovery was found to be independent of temperature. Truncation of the recovery reaction was apparent in those systems that exhibited the rapid age-hardening characteristics of the maraging steels. It is proposed that this initial hardening response is the result of a low activation energy preprecipitation reaction involving molybdenum. A gradual rise in the internal-friction level at longer aging times was associated with the precipitation of a molybdenum-containing precipitate. CONSIDERABLE research effort has recently been devoted to the mechanisms responsible for the high strength and toughness of 18 pct Ni maraging steels. These bcc martensitic alloys are found to harden during aging at temperatures between 400° and 600°C. The aging response is very rapid with more than half the total hardness increase occurring within the first few minutes of aging, Fig. 1. Precipitate particles have been observed in the later stages of aging by a number of investigators.&apos;-&apos; While the identity of the precipitates remains the subject of some controversy, one or more of the intermetallic compounds, Ni3Mo, Ni3Ti, and Fe2Mo, are almost certainly involved. Heterogeneous nucleation of precipitates at dislocations has been noted8 and cobalt is believed to enhance the formation of fine, homogeneously distributed particles by lowering the solubility of the alloying elements in the martensitic matrix.3,7 Transmission electron microscopy studies of the initial hardening behavior have not been fruitful. Strengthening mechanisms based on atomic ordering have not been generally supported by X-ray and neutron-diffraction experiments.9 In the present investigation, the aging reaction was studied using isothermal-aging internal-friction measurements. The marked sensitivity of internal friction to short-range diffusion and precipitation processes has provided a convenient tool for the elucidation of the strengthening mechanisms operative in the maraging steels. EXPERIMENTAL PROCEDURE An upright torsion pendulum was used to measure the internal friction of several maraging steels during isothermal aging. The pendulum was placed in an atmosphere of helium at a pressure slightly less than atmospheric. To permit measurement of internal friction during the first minutes of aging, the specimens were rapidly heated by passing a current through them in a manner similar to that described by Ang and Wert.10 Thermal gradients in the specimen were largely eliminated by using specially designed specimen grips11 which produced temperature variations of less than 1 pct over 90 pct of the specimen length and less than 3 pct over the entire length at aging temperatures up to 620°C. A proportioning strip-chart program controller was employed to maintain constant specimen temperature during treatments of up to 36 hr duration. A number of vacuum-melted laboratory heats having compositions near that of a typical commercial 18Ni-7Co-5Mo-0.4Ti alloy were investigated. The amount of cobalt was varied from 0 to 7 wt pct in five of the heats. Either molybdenum or titanium was omitted in the remaining two heats. The alloy desig-

Jan 1, 1967

By Richard P. Hight

Abrasives include the substances, natural or artificial, that are used to grind, polish, abrade, scour, clean, or otherwise remove solid material, usually by rubbing action but also by impact (pressure blasting for example). They do not include abrasive tools, for instance, lathe tools and files-or polishing agents such as waxes, which act by filling pores. Detergents and cleaners whose action is chemical rather than physical are omitted although some chemical-action polishes and cleaners may also contain solid abrasives, for example, many automobile and metal polishes. General Considerations The most important physical properties of materials that qualify them for use as abrasives are hardness, toughness (or brittleness), grain shape and size, character of fracture or cleavage, purity or uniformity. For making bonded abrasive products such as grinding wheels, additional important factors are stability under high heat and bonding characteristics of grain surfaces. The economic factors of cost and availability are always important. No one single property is paramount for any use. For some uses extreme hardness and toughness are needed, as in diamonds for drill bits; for others, the factors of greatest importance are hardness and ability to break down slowly under use, to develop fresh cutting edges when grains become worn-for example: in garnet for sandpaper neither highly cleavable or friable grains nor extremely tough grains are wanted. For still other uses, great hardness is objectionable; for example, abrasives for dentifrices and for glass-cleaning soaps. For the most efficient use in the more critical applications, the different types of abrasives are rarely completely interchangeable; thus, while crushed quartz and garnet are both used in sandpaper, the papers are not at all interchangeable in their use applications. In the last analysis, the choice of a high grade abrasive depends upon the quality and quantity of work done by the abrasive per unit of cost. Initial cost of an artificial abrasive may be much greater than that of a natural abrasive but the artificial abrasive may do so much better work than the natural one, and do it so much faster that the ultimate cost will be less. It is for this reason that artificial abrasives have largely replaced natural abrasives. Abrasive Value Mineralogical hardness or "scratch" hardness as expressed in Mohs&apos; scale is an important property in evaluating abrasive materials, but, as noted before, it is only one of several essential properties. The mineral hardness of pure crystal almandite garnet is about 7.5, but if the crystal is crossed by incipient fracture planes, or if it contains inclusions of other minerals, the apparent or useful hardness may be much lower. While the quartz grains in a sandstone have a hardness of 7, the bond holding the grains together may be so weak that the stone is valueless as a commercial abrasive. In artificially bonded wheels and stones, the hardness, strength, and character of the bond are fully as important as the hardness of the abrasive grains. Thus, in an overall consideration of abrasive hardness of loose abrasive grains, both "scratch" hardness and toughness must be considered. In naturally or artificially bonded abrasive stones, bond characteristics are a third factor, which is most important. The problem of abrasive hardness is further complicated by the inadequacies of methods of testing hardness and of expressing relative values. The Mohs&apos; scale is inadequate both because the methods of testing are very crude and

Jan 1, 1983

By J. T. Dewan

An experimental setup is described whereby the responses of Neutron logging instruments have been determined opposite formations of different porosities and under various borehole conditions. The results of these tests are presented in several charts which show how the Neutron log is affected by the following factors: hole diameter, casing, cement, salinity and weight of drilling mud, and position of logging tool with respect to the wall of the hole. The responses in the case of empty holes are also shown. A chart is furthermore presented which shows the shapes of the Neutron log, as a function of logging speed and time constant, at the boundaries between two formations with different porosities. These were derived mathematically using as a basis laboratory determination of the shape of the curve under static conditions, i.e. at very low logging speed. Corrections for the readings made opposite thin beds are given by these computations. The correction is found negligible under usual logging conditions for beds thicker than about 4 ft. INTRODUCTION The Neutron log is used in borehole surveys both for the delineation of porous formations and for the quantitative estimation of their porosities.1,2,3,4,5 It is common practice to calibrate the response of the Neutron log in terms of porosity values for each given geological unit by means of empirical comparisons between the deflections of the neutron curve and the porosity values given by the core analysis in a sufficient number of wells. Usually, the plots of the porosity values vs Neutron log deflections show a definite trend. It is therefore possible to trace an average line across the plotted points. This average line constitutes a calibration curve which can be used to evaluate the porosities from the Neutron logs in the other wells drilled in the same region. Futhermore, when the porosity values are plotted on a logarithmic scale and the Neutron log deflections on a linear scale, the calibration curve is practically a straight line. Accordingly the calibration curves are often determined by simply tracing a straight line between two points corresponding to two widely different porosities. Different choices are made for these two points, depending on local conditions. For example, one point will be defined by plotting the deflection of the Neutron curve opposite a formation known to be very tight, for which an average porosity value of 1 or 2 per cent is assumed. The other point may correspond to shale sections, to which a porosity of around 40 per cent is ascribed. The information provided by the eletrical logs — in particular the Laterolog, Limestone log or Micro-Latero-log — is also very often a help in the calibration of the Neutron logs. Empirical approaches such as these make possible the derivation of fairly reliable porosity values from the Neutron logs in many cases, at least in open holes and in essentially clean formations. There are, however, several causes of uncertainty which may sometimes entail appreciable errors. On the one hand, the Neutron log readings are influenced by the borehole conditions: hole diameter, presence or absence of casing and cement, presence or absence of drilling mud, characteristics of the mud, and position of the logging instrument with respect to the wall of the hole. The amplitudes of the curves opposite thin beds are furthermore atfected by the bed thickness,

Jan 1, 1957

By M. Kaufman, A. E. Palty

The phase structure and aging characteristics of two nickel-base alloys, Inconel 718 and 702, were investigated. Wrought and cast Inconel 718 showed ArisCb as the major hardening phase, as well as ture was positively identified. Inconel 702 had Ni3Al as the major hardening phase, as well as Cr7C3-of the phase amounts with temperature was determined. 1 HE value of phase structure and aging rate information in the utilization of alloys has been well established. As part of a continuing program, the results obtained on two nickel-base alloys, hconel 718 and Inconel 702, are presented here. Inconel 718 is a relatively new alloy considered for application in both sheet and cast form. Its novelty lies in the use of high columbium tantalum levels in a Ni-Cr-Fe base. No previous work on this type of alloy has been reported in the literature. Inconel 702 is being used now as an oxidation-resistant sheet alloy. Occasional fabrication problems spurred work on its basic structural behavior. The composition of 702 is essentially nichrome plus aluminum and titanium for strengthening and added oxidation resistance. This puts it in the basic class of other nickel-base alloys which have already been studied. The two alloys will be treated separately. INCONEL 718 Phase Study Methods. The phases present after the various conditions investigated were determined by X-ray diffraction analysis of two different elec-trolytically extracted residues and microscopic examination. The extraction methods, using 10 pct HC1 in alcohol and 10 pct H3PO, in water and the X-ray technique have been described previously.&apos; The effect of temperature on the phase behavior was studied on sheet material using the following heat treatments: 2250°F, 2 hr, ice brine quench 1300 100 hr, water quench 2250°F, 2 hr, ice brine quench 1400°, 100 hr, water quench 2250°F, 2 hr, ice brine quench 1500°F, 100 hr, water quench 2250o 2 hr, ice brine quench 1700°F, 48 hr, water quench 2250°F, 2 hr, ice brine quench 1850°, 24 hr, water quench 2250°, 2 hr, ice brine quench 2000°F, 6 hr, water quench The high solution temperature was an attempt to dissolve as many phases as possible without causing melting. Aging exposures were made longer than normal heat treating times in order to approach equilibrium conditions more closely. Cast material was examined only in the as-cast condition and with the normal heat treatment (1700°F, 1 hr, air cool 1325oF, 16 hr,air cool). Materials. The full phase study was performed on sheet specimens approximately 1/2 in. by 2 in. by 1/16 in. The cast pieces were cut from the gating system of a vacuum-cast test piece. An all weld-metal specimen was made by running many weld beads on the sheet using filler made from the sheared edges of the sheet. All external contamination was removed by belt-sanding followed by an electro-polishing treatment. The typical composition of wrought Inco 718 is as follows: The alloy is air-melted. Cast hco 718 may have higher molybdenum. Due to the expectation of finding a Ni-Cb phase (Ni, Cb) for which no X-ray diffraction pattern was available in the ASTM Index, a special 5 Ib heat to the stoichiometric composition of this intermetallic

Jan 1, 1962