Search Documents

By L. T. Leyson, U. C. Tainton

Some time ago, at ameeting of the Institute Prof. J. W. Richards1 said, "I take exception to the statement that all the factors in the production of electrolytic zinc were known long ago.... There is possible in my opinion an improvement of perhaps 50 per cent. in the new electrolytic processes." An examination of the literature of the subject will show the justness of Professor Richards' contention. The work of the earlier investigators was carried on in the shadow of difficulties that, today, are hardly more than memories. We seldom hear now of zinc sponge, that bête noir of the electrolytic-zinc pioneers. Zinc sponge was the name given to a peculiar, soft, black, non-adherent form of zinc deposit that was utterly useless for melting into ingot form. At the big plant at Cockle Creek, New South Wales, in 1897, Edgar Ashcroft2 said that the solution in the plant would suddenly, and without ascertainable cause, go' "bad" and begin to deposit spongy zinc. The most delicate, even spectroscopic, methods of analysis were unable to detect any difference between "good" solution and "bad" solution; either form might change to the other on being kept for a while. When it is added that an outbreak of this insidious disease (which appeared to be infectious, or at least contagious) could be dealt with only by discarding the solution and washing out all tanks and pipe lines, some idea may be gathered of the troubles of the zinc electrometallurgist in what may be spoken of as the "sponge age" of electrolytic zinc. Thanks to the efforts of a number of investigators, we are today able to diagnose with considerable certitude the nature of the malady that puzzled Ashcroft and his co-workers. The researches of Mylius and

Jan 1, 1924

By HUBERT O. De

IN December, 1936, several drilling tests were made at the Hubert O. De Beck feldspar mine at Green Mountain, N. C., to determine the most efficient type of hammier-drill bit and drilling method for use at this particular property. This mine is well recognized as having the hardest rock in the Burnsville - Spruce Pine feldspar district and drilling costs always have been high. Local structural deformation has greatly distorted and warped the normal crystalline structure of the feldspar so the rock is much tougher than usual. In studying drilling methods and bit types, available literature was re¬viewed but little specific data could be found on the direct comparison of four-point and six-point drill bits so the following results may be of some interest.

Jan 1, 1937

A comprehensive, systematically structured mineral evaluation system is a prime requirement for objectively assessing mineral supply impacts on the economy. The Minerals Availability System developed by the US Bureau of Mines is a step in the right direction-a well-organized unraveling of the mineral supply network, structured in format to allow quick retrieval for rapid listing, supply analysis, and other uses.

Jan 9, 1977

By Frank J. Tolonen, Nicholas H. Manderfield, Paul Jasberg

EARLY in the study of the low grade iron formations of Michigan, wide variations in their structure and texture became evident. Because of these variations no simple method of concentration is possible, and those portions of the formations that can be exploited profitably under a given stage of metallurgical progress and existing economic conditions must be searched for carefully. Both structure and texture of the formations have an important bearing on their amenability to beneficiation. By structure is meant the banding planes of easy fracture, the porosity, and the degree of leaching. Texture, which includes grain sizes, shapes, and degree of interlocking, determines the amount of grinding necessary to liberate the mineral grains. Structure determines the liberation of portions richer in one mineral. Structure and texture may be termed the gross features of the formation

Jan 11, 1957

By David A. Thomas, John F. Peck

Fibrous microstructures and their development have been studied by metallography and by hardness and quantitative metallographic measurements. Thin, curved grains were observed in transverse sections of commercial tungsten wire and were developed in laboratory-drawn iron wire at reductions greater than about 70 pct. The unusual grain shapes are attributed to the nonuniform mode of deformation of the grains associated with the characteristic [I101 preferred orientation that develops in bcc metals during drawing. Transverse sections of heavily swaged iron wire showed a ospiral nebulao structure that appears to result from the elliptical shape of the cross section of the swaging dies and their rotary motion. Hardness and quantitative metallographic results show unusual trends that parallel the changes in microstructure. Other phenomena are considwed in light of the results, including the strength of fine wires of bcc metals, ocylindricalo textures, and the ductility of fibrous tungsten. 1 HE microstructure of tungsten wire in a longitudinal section shows grains highly elongated in the working direction, giving the appearance of a bundle of parallel fibers, Fig. l(a). Wires of tungsten and other bcc metals show a pronounced preferred orientation in which a [I101 direction is parallel to the wire axis.l The microstructure and texture of tungsten develop during warm working (working above room temperature but below the recrystallization temperature) into wire by swaging and drawing. Fibrous tungsten so produced has limited but useful room-temperature ductility, whereas annealed tungsten is brittle at room temperature. During an investigation of the effect of recovery annealing on the substructure of commerical 0.030 in. diam tungsten wire, it was found that transverse sections of the as-received material showed thin, curved grains, Fig. 1(b), instead of the expected equiaxed grains. The fact that Figs. l(a) and (b) show different sections of the same material at the same magnification is at first disconcerting, because the long dimension of the curved grains in the transverse section is several times the average fiber width in the longitudinal section. However, a longitudinal section cuts most of the curved grains across their narrow dimension, giving the appearance of a multitude of narrow fibers. On the other hand, the plane of a longitudinal section occasionally includes a long dimension of a curved grain, resulting in a broad ofibero, such as A in Fig. l(a). EXPERIMENTS AND RESULTS To investigate the origin of fibrous microstructures and particularly the unusual transverse-section structure of tungsten, rods of iron (also bcc) were drawn and swaged in the laboratory. One rod of annealed Ferrovac E was drawn in six steps to a total reduction in area of 87 pct (0.10 to 0.036 in. diam), and a second rod was swaged to the same reduction, using approximately the same reduction steps. Longitudinal and transverse sections of the swaged and drawn iron wires are shown in Fig. 2, for reductions in area of 39, 73, and 87 pct. A fibrous microstructure in longitudinal section is first evident at 73 pct reduction, and it is further developed at 87 pct reduction. The grains in transverse section remain equiaxed until about 73 pct reduction, when they become somewhat elongated and curved. At 87 pct reduction, the drawn wire shows thin, curved grains in the transverse section, similar to those observed in tungsten. The transverse sections of the iron wires swaged 83 and 87 pct reduction in area show the striking ospiral nebulao structure in Fig. 2(d). This struc-

Jan 1, 1962

By John Howe Hall

One's first thought, upon being chosen to deliver the Henry Mario Howe lecture, is of pride at being selected for this post of honor, but ther succeeds immediately a deep sense of the Obligation thereby incurre to give of one's very best in order to make a contribution worthy of hir in whose memory these lectures are given. One who had the goo fortune to be associated with Henry ill. Howe, upon sitting down t prepare such a paper as this, irnrnediately falls to musing upon thc day when his face and his footfall were familiar from constant association, an recalls with singular vividness his active figure, his mobile, alert face, an his keenness in penetrating to thc corc of the subject under discussior Like Dr. Mathews, I was a young man when I first worked under hi direction, now nearly a quarter of a century ago, and in those early day he oft,en seemed a hard taskmaster—a man whose standards it woul never be possible for me to meet. I well recall his insisting upon m proving for the third time the truth of a conclusion which I had brc unwilling to submit to him until it had been confirmed by two carefull planned experiments. To my impatient protest that thc third .demor stration he asked for was but a repetition of the second, with differer samples, he replied, "Yes, that is true, but the inherent improbability ( your conclusions is so evident that I can not accept them until you prov your case again." "Shall I ever do a thing well enough to suit him? I thought. Looking back today upon many similar incidents, 1 suspect that h never expected me to attain the excellence he preached, and held up t me and to himself as a model, but knew out of the fullness of his experienc. that in no other way could he so impress upon me the necessity in researc of the patient, never-failing attention to detail and to accuracy tha distinguished his own work. How painstaking he was in the preparation of his many books an professional papers, as well as in his experimcntal work, was ncvcr s

Jan 1, 1929

By R. F. Mehl, B. Lustman

The formation of intermediate phase layers in cementation processes has been subjected to extensive qualitative investigation though to relatively little quantitative study; this work has recently been fully summarized by F. N. Rhines.' It is necessary here only to cnumerate the general conclusions drawn concerning the kinetic laws governing the growth of intermediate layers and to state what is known concerning the structural changes accompanying the generation of phase layers. I. When the intermediate phase is protective in type—i.e., when its density is less than that of the base metal, so that a continuous coating is formed and maintained—the isothermal growth of the phase follows a simple parabolic equation: X2 = kt [i] where X is the thickness of the alloy layer, k thc reaction rate constant, and t the time. The applicability of this equation to diffusion processes is tested by plotting the square of the thickness versus time, or by plotting the thickness versus the square root of time; the resultant achievement of a straight line in such a plot has been considered sufficient proof of the validity of this equation. Exceptions have been found where liquid phases are involved in the reaction, where the diffusion layer is cracked,2 and where thin semimetallic oxide and sulphide coatings are formed on metals.$ In the first two cases the thickness increases linearly with time, and in the latter it is a logarithmic function of time. 2. The rate of thickening varics with temperature according to the Arrhenius equation: k = Ae-Q/RT [2] where k is the parabolic rate constant of Eq. I, or some other rate-descriptive function, A is the action constant, e the base of natural logarithms, Q the heat of activation, R the gas constant, and T absolute temperature. This equation has been found to be generally valid except when transformations occur during reaction in either the base metal or in the reaction layer; in such instances Eq. 2 is still applicable with different values for the constants A and Q above and below the transformation temperature. 3. Ali phases that are stable at the temperature at which diffusion occurs will appear in the interdiffusion of two components. In some cases certain of the phases may be too thin to be observed and identified easily. Nonequilibrium phases have never been noted in thick reaction layers; i.e., layers of a thickness that may be discerned microscopically. The relative thickness of each phase in a diffusion layer is proportional to the concentration gradient and to the rate of diffusion in that phase.4 The reaction layers tend to have a

Jan 1, 1942

By R. F. Mehl, B. Lustman

The formation of intermediate phase layers in cementation processes has been subjected to extensive qualitative investigation though to relatively little quantitative study; this work has recently been fully summarized by F. N. Rhines.' It is necessary here only to cnumerate the general conclusions drawn concerning the kinetic laws governing the growth of intermediate layers and to state what is known concerning the structural changes accompanying the generation of phase layers. I. When the intermediate phase is protective in type—i.e., when its density is less than that of the base metal, so that a continuous coating is formed and maintained—the isothermal growth of the phase follows a simple parabolic equation: X2 = kt [i] where X is the thickness of the alloy layer, k thc reaction rate constant, and t the time. The applicability of this equation to diffusion processes is tested by plotting the square of the thickness versus time, or by plotting the thickness versus the square root of time; the resultant achievement of a straight line in such a plot has been considered sufficient proof of the validity of this equation. Exceptions have been found where liquid phases are involved in the reaction, where the diffusion layer is cracked,2 and where thin semimetallic oxide and sulphide coatings are formed on metals.$ In the first two cases the thickness increases linearly with time, and in the latter it is a logarithmic function of time. 2. The rate of thickening varics with temperature according to the Arrhenius equation: k = Ae-Q/RT [2] where k is the parabolic rate constant of Eq. I, or some other rate-descriptive function, A is the action constant, e the base of natural logarithms, Q the heat of activation, R the gas constant, and T absolute temperature. This equation has been found to be generally valid except when transformations occur during reaction in either the base metal or in the reaction layer; in such instances Eq. 2 is still applicable with different values for the constants A and Q above and below the transformation temperature. 3. Ali phases that are stable at the temperature at which diffusion occurs will appear in the interdiffusion of two components. In some cases certain of the phases may be too thin to be observed and identified easily. Nonequilibrium phases have never been noted in thick reaction layers; i.e., layers of a thickness that may be discerned microscopically. The relative thickness of each phase in a diffusion layer is proportional to the concentration gradient and to the rate of diffusion in that phase.4 The reaction layers tend to have a

Jan 1, 1942

By B. H. Caudle, L. G. Davies, I. H. Silberberg

This paper presents a method of predicting the recovery and performance of a five-spot steam injection project, in which a realistic approach to pattern sweepout efficiencies is made. Published methods for radial systems were modified for the five-spot pattern by approximating the stream lines with straight lines radiating from the injection well and then converging to the producing well. In each radial segment, the position of the steam front and the temperature profile ahead of the steam front were determined by heat balance equations, which included an estimation of heat losses to surrounding formations. The location of the saturations behind the cold water front was determined from a Buckley-Leverett solution to the material balance equation. Results from this program show steamflood recovery in a five-spot pattern to be considerably less than that predicted for true linear or radial flow systems. For a specific reservoir containing 900-cp oil, a steamflood in a purely radial flow system was predicted to recover more than 75 percent of the original oil in place when 2 PV of water had been injected as steam. A five-spot steamflood with otherwise identical properties was predicted to recover 10 percent of the original oil in place when 0.15 PV of water had been injected as steam and to recover almost no oil thereafter. A cold water five-spot flood in this system was predicted to recover approximately W percent of the oil in place with I PV of water injected. For a five-spot pattern in an example reservoir with 10-cp oil, steam injection similarly showed lower ultimate recovery than water injection but no improvement in recovery rule. Introduction The thermal recovery method considered in this study is steam injection in a five-spot pattern. Pattern steam injection has been given little attention in the past, possibly because of some rather obvious disadvantages. Unless steam temperature is maintained throughout the entire swept area, the process will revert to simple waterflood with all heat being lost prior to reaching the oil bank. Also, the oil viscosity reduction takes place near the steam front and not around the producing wellbore, so that low producing rates must still be endured. This is the reason for the success of the steam stimulation, or cyclic injection, in which the fluids are produced from the same well used for injection. On the other hand, steamflooding can offer some advantages. Oil displacement is by four methods: (1) mechanical displacement by the condensed water, (2) viscosity reduction of the crude oil, (3) swelling of the crude oil, and (4) distillation of the crude oil in the steam zone. Although dependent upon the crude, laboratory experiments have shown displacements up to 80 percent by steamflooding. In addition, steam is a good heat transport medium, since it is cheap and has a high heat content. Previous Investigations Previous publications have reported methods for predicting recovery in a steamflood for linear and radial systems. Since no pattern sweep efficiency is taken into consideration, the recovery even from a radial system must be greater than from more realistic geometries such as the very common five-spot patterns. Probably the broadest coverage is given by Willman who reported experimental results and offered a method of predicting recovery for a radial flow system. They concluded that both hot water and steam injection recover more oil than an ordinary waterflood, and that steam injection could yield recoveries "as much as 100 percent greater than by water flood." They also concluded that both the heat requirements for a reservoir and the residual oil remaining in the reservoir after steam injection were independent of the amount of oil originally in place, that short exploitation times were desirable, and that a high percentage of net sand in the reservoir with a high initial oil saturation was desirable. The method assumes that the flood occurs in three concentric cylindrical zones: (1) an inner steam zone, (2) a central hot water zone, and (3) an outer cold waterflood zone. Displacement in the steam zone is based on laboratory-determined residual oil saturations while the hot water and cold water zones use the conventional Buckley-Leverett equations. Although the results shown by Willman et al. are for a radial system flowing out from the well to an assumed external circular boundary, their equations did

Jan 1, 1969

By Peter Greenfield, Paul A. Beck

Thirty binary systems of vanadium and chromium group transition elements with second and third long period transition elements were explored in regard to the intermediate phases formed. It was found that the phases predominating in these systems are s, AB type with ordered a-tungsten or C8 structure, close-packed-hexagonal with small unit cell dimensions and, finally, phases isomorphous with 1-manganese. IN recent years, considerable information has become available concerning the intermediate phases in binary systems of the transition elements. Thus, the s phase has been found to occur in most of the binary systems of vanadium, chromium, and molybdenum with the group of elements manganese, iron, cobalt, and nickel.' It was observed that, while the rr phases formed by chromium with manganese, iron, or cobalt possess a considerable temperature range of stability, particularly in the Cr-Co system, the corresponding s phases with molybdenum are limited to a temperature range of less than 400" above about 1200°C. Goldschmidt' reported v phases of tungsten with iron and cobalt, and these are apparently stable only at (and above?) 1400°C." Exploratory work in this laboratory with Fe-W and Co-W alloys of approximately 60 atomic pct W annealed at 1300°C did not produce X-ray patterns suggesting the presence of a phase. It appears then that the phases of iron and cobalt with the chromium group elements decrease in stability as the two components are chosen from long periods further removed from each other. From the available information, it might be concluded that the controlling factor is the increasing difference in atomic radii between the components. In contrast to the a phase, the phases formed by iron and cobalt with chromium group elements' are stable only when the latter have large atomic radii (molybdenum and tungsten); the corresponding phases with chromium do not occur. When the difference in atomic size becomes still larger (r,/r,, approaching the ideal value of 1.225), the u and p phases are replaced by Laves phases (AB,), as in the alloys of iron and cobalt with columbium," tantalum." and titanium."-" However, atomic size certainly cannot be the sole determining factor, since, for instance, in contrast to the very stable (Mo, Co)p phase, no such phase occurs in the Mo-Ni system even though the atomic diameters of cobalt and nickel are nearly the same. Similarly, chromium and cobalt form a a phase in a wide temperature range," but the corresponding s phase in the Cr-Ni system is missing. It has been shown that the composition of the u phase in various binary and ternary systems of transition elements in the first long period may be correlated in a fairly quantitative manner with the number of electron vacancies. The influence of electronic structure is probably present also in binary and ternary phases' and to some extent, apparently, even in Laves phases." " Although the absence of phases in the Cr-Ni and Mo-Ni systems has not as yet been explained on the basis of electronic structure, it appears reasonable to suspect a connection. One of the great difficulties in arriving at well founded rules in regard to the alloying behavior of transition elements lies in the lack of reliable information concerning the details of their electronic structure in the metallic and alloy form. The theoretical penetration of this field appears to be beset by very considerable difficulties, even when the complications due to alloy formation are disregarded. Another great source of uncertainty is the scarcity of phase diagram information even for binary systems of the transition elements so that only a very limited basis is provided for generalizations as to the occurrence of intermediate phases. For instance, very few binary phase diagrams of second and third long period transition element systems have so far been published. The present work was undertaken in order to survey the various types of intermediate phases occurring in 30 binary systems of elements of the group vanadium, columbium, tantalum, chromium, molybdenum, and tungsten with the elements rhenium, ruthenium, rhodium, palladium, and platinum. For most of these binary systems phase diagrams are very incompletely or not at all known, as will be further reviewed.*

Jan 1, 1957

By RUSSELL C. FLEMING

GILSONITE is a brilliant black, tarry-like bitumen, classed technically with glance pitch and graharnite as an asphaltite. As found it is brittle, breaking much like ice, and has a conchoidal fracture. Purest forms are used in the manufacture of paints, varnishes, electrical irisulatiorl, and inks for rotogravure; molded articles such as switch handles, telephone mouthpieces, and but- tons are made from the intermediate grades, and the poorer grades are used for the saturation of felt. According to the U. S. Bureau of Mines figures, production grew from about 4000 tons mined in 1904 to 55,000 tons in 1929. This asphaltic substance is found only in the Uintah basin in northeastern Utah, in veins over a wide area. Veins in the vicinity of Fort nuchesne were first discovered about 18G2, on what was then the Uintah Indian reservation, and the vein matter was originally called Uintaite because of that fact, In the early days, S. H. Gilson. of Salt Lake City, was so persistent and zealous in his efforts to develop the deposits and find a market that the name gilsonite was given to the material. Later, the wider and more renowned wins near Wayson and Dragon, in extreme eastern Utah, became the main supply.

Jan 1, 1932

INTRODUCTION The International Finance Corporation (IFC) is affiliated with the International Bank for Reconstruction and Development (World Bank) but operates with a separate staff and funding. It supplements the activities of the Bank by providing, to private business, equity and loans without government guarantees in whatever form and combination most suited to the project. IFC frequently complements the Bank's activities by utilizing, for example, the Bank's public sector infrastructure activities to support IFC's private sector projects. In the case of local financial institutions especially, IFC collaborates with the Bank by providing technical and financial assistance. IFC is the world's largest multilateral organization which finances private sector business in developing countries. IFC's fundamental purpose is to promote the economic development of its developing member countries through the support of the private sector. Of the 124 member countries of IFC, more than 100 are developing countries. Since it began operations in 1956, IFC has been associated with more than 2,000 companies and financial institutions in supporting over 700 business ventures in more than 80 countries. The total capital costs of these projects exceeds $26,000 million. In the 1984 fiscal year, IFC approved 62 projects in 37 countries with a total project cost of $2,473 million. IFC will make investments only if sufficient capital cannot be obtained on reasonable terms from other sources. IFC often serves as the catalyst for a project by encouraging other investors--from inside and outside the host country--to make their own equity investments along with the local sponsor for a particular project. IFC'S SPECIAL ROLE The significance of IFC's role extends beyond just its financing and technical assistance: IFC's capability to raise investor confidence in a project and to help all the participants to arrive at mutually satisfactory investment arrangements is its distinctive character. Direct Investments IFC invests in all types of projects both large and small. Heavy industrial ventures not only supply essential materials and equipment for other domestic enterprises, but also earn foreign exchange through exports. In recent years, increased emphasis has been placed on agriculture and agribusiness products, aquaculture, food and food processing, and other renewable and nonrenewable resources such as metals and energy. [ ] An overall objective of IFC is to assist entrepreneurs and others in the private sector raise the needed capital for business ventures. IFC does not compete with, nor seek to replace private initiative and capital. Rather, IFC helps to raise funds in order to undertake projects that would otherwise be held back by the lack of adequate funding. IFC can do this in several ways: IFC can invest in equity and make loans for its own account. But beyond that, IFC can reach out into the international capital markets in search of additional capital. Because of IFC's 25 years experience and record, outside investors who might otherwise be

Jan 1, 1985

By A. B., Sabin

THERE are many who know The Lucky Tiger and will remember the 35-mile road from Esqueda, a station on The Nacozari Railroad in northern Sonora, Mexico. They will remember the box canyons of the Agua Caliente Mountains which are scarcely wide enough for two cars to pass; the Bavispe River which one hour may be a lazy trickle and the next a sweeping torrent, and the tortuous road up Tigre and Espuela canyons, now following the wash, now hugging some gigantic red cliff. It is still the same. From camp the view of the distant blue-gray mountains is the same. But one thing a visitor of a former day might miss: The hundreds of pack mules and burros, loaded with concentrates from the mill, which used to take most of the road and show up at the most inopportune places, have almost disappeared, replaced of course by the auto truck.

Jan 1, 1929

By J. Burns Read, S. Tour

It is the purpose of this paper to summarize, as far as possible, the metallurgical information and experience gained by the Ordnancc Department, during the war, in the manufacture of artillery cartridge cases, to describe the tests to which artillery cartridge cases were put, and to summarize the knowledge and experience gained in this testing. The authors wish to acknowledge the aid given by manufacturers, army officers, and civilian employees of the Department in obtaining data. Artillery cartridge cases are cold drawn from circular disks punched from strips of rolled brass. The rnanufacture involves from 25 to 30 main operations, which are done almost entirely on a punch press. Descriptions of the operations have appeared in various periodical:: and, therefore, will not he given here. After each cupping, or drawing, operation, except the last, the cases are annealed at from 540" to 650" C. (1000" to 1200°F.), to remove all the hardening stresses set up in the metal and to allow complete recrystallization. After each annealing, the cases are pickled in niter cake or sulfuric-acid solution and then washed in water to remove all traces of acid. In some instances, the cases arc then immersed in a cyanide-salt solution, and afterwards rinsed in water, to remove the thin layer of copper that forms on the surface of the cases during the acid pickle. The last cold-drawing operation is followcd by the heading operation which, by flattening the head of the case on the outside, causes the metal to flow on the inside to approximately the proper finished dimensions. The mouth, or open end, is then annealed at 430" to 450" ('. 1800" to 900" F.) by immersion in a salt bath or by gas flames. After being washed, the eases are tapered, when they arc ready for machining, inspection, and testing. Cartridge-case Disks Good disks of proper composition and physical properties are essential to the production of good cartridge cases. The Ordnance Department

Jan 1, 1923

By J. Burns Read, S. Tour

It is the purpose of this paper to summarize, as far as possible, the metallurgical information and experience gained by the Ordnancc Department, during the war, in the manufacture of artillery cartridge cases, to describe the tests to which artillery cartridge cases were put, and to summarize the knowledge and experience gained in this testing. The authors wish to acknowledge the aid given by manufacturers, army officers, and civilian employees of the Department in obtaining data. Artillery cartridge cases are cold drawn from circular disks punched from strips of rolled brass. The rnanufacture involves from 25 to 30 main operations, which are done almost entirely on a punch press. Descriptions of the operations have appeared in various periodical:: and, therefore, will not he given here. After each cupping, or drawing, operation, except the last, the cases are annealed at from 540" to 650" C. (1000" to 1200°F.), to remove all the hardening stresses set up in the metal and to allow complete recrystallization. After each annealing, the cases are pickled in niter cake or sulfuric-acid solution and then washed in water to remove all traces of acid. In some instances, the cases arc then immersed in a cyanide-salt solution, and afterwards rinsed in water, to remove the thin layer of copper that forms on the surface of the cases during the acid pickle. The last cold-drawing operation is followcd by the heading operation which, by flattening the head of the case on the outside, causes the metal to flow on the inside to approximately the proper finished dimensions. The mouth, or open end, is then annealed at 430" to 450" ('. 1800" to 900" F.) by immersion in a salt bath or by gas flames. After being washed, the eases are tapered, when they arc ready for machining, inspection, and testing. Cartridge-case Disks Good disks of proper composition and physical properties are essential to the production of good cartridge cases. The Ordnance Department

Jan 1, 1923

By Herluf P. Nielsen, Robert I. Jaffee

IN recent years much attention has been given to high-melting alloy systems, It has been of interest in this respect to investigate the alloys of platinum and tungsten, which were known from the literature to have very high melting points up to about 50 pct tungsten, but about which little had been published on the high-tungsten side of the system. Powder metallurgical methods were used throughout this investigation for the preparation of the alloys, utilizing electrical sintering techniques such as are used for tungsten and molybdenum. In the course of the work it was found desirable to determine fusion temperatures of the alloys, and it was possible from these and other data to draw a tentative constitutional diagram (solidus, mostly) applicable to the high-temperature part of the system. No attempt was made to determine solid solubility vs. temperature data, nor to investigate the lower temperature transformations in the solid state. Data on the microstructure, hardness, and a note on oxidation resistance of the sintered alloys were obtained. PAST WORK Müller1 determined liquidus temperatures of platinum-rich alloys to 50 pct tungsten, using a radiation method employing a photoelectric cell, and found that the melting points increased progressively from 1771°C for platinum to 2350°C for the 50 pct alloy. Microscopic evidence by Müller that complete solid solutions exist to 50 pct tungsten was not checked by Kremer2 who, according to Vines and Wise,3 found that "although the 8 pct tungsten alloy was a solid solution, the 26 pct tungsten alloy contained a eutectic or an intermediate phase." Hultgren and jaffee4 using X ray methods found continuous solid solutions to at least 33.6 pct tungsten (35 at. pct) after annealing in vacuum for 6 days at 1000°C. Vines and Wise3 report work communicated to them by E. C. Rhodes on wrought alloys to 7 pct tungsten, which showed that tungsten hardened platinum extremely rapidly, and was one of the most potent hardeners of the binary additions to platinum. Considerable quantities of 4 pct tungsten platinum wire have been produced for grids in radar tubes and for aircraft spark plugs. Some of the alloy for the latter application is made by sintering, the remainder by smelting and casting. MATERIALS The platinum powder used in this work was kindly supplied by the research and Development Laboratory of the Owens-Corning Fiberglas Corp., Newark, Ohio, It was prepared from scrap platinum. After dissolving in aqua regia and evaporating almost to dryness, the solution was worked up several times with concentrated HCI. the resultant platinic chloride was diluted considerably, and metallic zinc was added, which precipitated the platinum in a very finely divided form. After dissolving the

Jan 1, 1948

CONTENTS PAGE Rae, Colin C.-A Possible Origin of Oil. Discussed by S. Linker, Colin C. Rae... 2 Cottingham, Kenneth.-Subsurface Conditions on Portion of Arches Fork Anticline. Discussed by David B. Reger 6 Moyer, W. Irwin.-Time to Pay Out as a Basis for Valuation of Oil Properties. Discussed by H. J. Smith 9 Pogue, Joseph E.-Future Demands on Oil Industry of United States. Discussed by James O. Lewis 11 J. J. Walsh.-Coa-lmine Ventilation. Discussed by W. B. Daly, J. J. Walsh, R. R. Sayers, H. H. Stock, George S. Rice, James W. Paul, D. Harrington, T. D. Thomas 15 Longyear, Robert Davis.-Diamond-drill Sampling Methods. Discussed by Ira B. Joralemon, J. J. Rutledge, E. C. Harder 19 Joralemon, Ira B.-Sampling and Estimating Disseminated Copper Deposits. Discussed by J. Parke Channing, John E. Hodge, E.E. Hunner, B. B. Gottsberger, W. Y. Westervelt, W. O. Hotchkiss 20 Boericke, W. F.-Sampling and Estimating Zinc and Lead Orebodies in Mississippi Valley. Discussed by J. Parke Channing, Arthur Thacher 24 Daly, W. B. and Linforth, F. A.-Organization of Mine Sampling at Anaconda. Discussed by George A. Packard, W. B. Daly, B. B. Gottsberger 25 Norris, E. M. and Rahilly, H. J.-Mine Fires. Discussed by R. Dawson Hall, W. B. Daly, Frank Haas, D. Harrington, Robert E. Tally 26 Raymond, R. M.-Safety Practice for Hoisting Ropes. Discussed by B. F. Tillson, Graham Bright, Rudolph Kudlich, J. F. Howe, Robert Peele, H. G. Davis. 30 Howe, J. F.-Use of Wire Rope in Mining Operations. Discussed by Horace F. Lunt, J. F. Howe, B. F. Tillson 36 Tanner, W. N., and Jaccard, F. C.-Wire Rope and Safety in Hoisting at Butte Mines. Discussed by Horace F. Lunt, W. B. Daly, C. L. Colburn, William Kelly, Robert Peele, B. F. Tillson, Graham Bright, Charles E. Locke 38 Richardson, A. S.-Ventilation of Butte Mines of Anaconda Copper Mining Co. Discussed by D. Harrington, Chas. A. Mitke 42 Stuart, Charles E.-Storage-battery Locomotive as Applied to Mine Haulage. Discussed by Howard N. Eavenson, Charles E. Stuart, William Kelly, Arthur Thacher, W. H. Patton, Graham Bright 45 Woodward, C. D.-Electric Haulage Systems in Butte Mines. Discussed by William Kelly, Graham Bright, Howard N. Eavenson, C. E. Arnold, Gerard B. Rosenblatt, K. A. Pauly 47 Harrington, D.-Efficient Ventilation of Metal Mines. Discussed by R. E. Simpson 52 Otagawa, Masayuki.-Mining Methods at the Ashio Copper Mine. Discussed by Horace V. Winchell, D. W. Brunton 52 Stoek, H. H. and Clagett, Thomas H.-Coal Mining Methods. Discussed by P. D. Browning, G. L. Cox, Erskine Ramsay, Frank Haas, George S. Rice.

Jan 6, 1922

By H. l. Burghoff, J. S. Porter

THIS paper presents the results of an investigation of the effect of cold-working and annealing treatments upon the occurrence of preferred orientation in annealed brass wire. The subject has received less consideration than has the same phenomenon in annealed brass sheet or strip, and perhaps very properly so in view of the obvious and undesired results obtained in the forming or drawing of strip having preferred orientation, which results are in contrast with the lack of any spectacular visual evidence in wire. The factors of cold-working and annealing that control preferredness in strip are naturally expected to function similarly in wire. Indeed, one might expect the condition to be commoner in annealed wire, because the severity of the cold-working between anneals in commercial practice is usually much greater for wire than for strip. For example, a wire that is to be finished in the annealed condition on a diameter of 0.040 in. is commonly subjected to a final reduction of 96 per cent between the last two anneals, the large reduction being accomplished in the successive drafts of a multiple-die machine. Wire for rivets, for instance, on 0.125-in. diameter, although given a slight reduction of about 10 per cent after the final anneal, may have been given a prior reduction of 75 to 80 per cent. Barrett1 states the fiber axis of annealed 70-30 brass wire to be [111] with some indication of [100] as a secondary fiber axis. Croft and Sachs2 have reported briefly on some differences in brass wire with random and with preferred orientations. They showed statistical plots of the twin-band angles with respect to the wire axis or direction of drawing as observed on an axial plane. They also pointed out that the resistance of the wire to corrosion-cracking when externally stressed and exposed to a mercurous nitrate solution decreased as the degree of the preferred orientation increased. MATERIAL AND PROCEDURE All the wire for the investigation was processed from one. portion as cut for extrusion from a cast billet of the following analysis: 70.13 per cent copper; 0.01 lead; 0.01 iron; 0.02 nickel; 29.83 zinc (by difference). The billet section, 8 in. in diameter, was extruded hot to 3/4 -in. diameter, after which it was processed by alternate cold-drawing and annealing treatments as indicated in Fig. I. The earliest anneals in process were at about 1100°F. and the next to the last reductions by drawing were 58 per cent. The diameter of the finally annealed wire was 0.132 in. Semifinal anneals were at 800°F., 950°F. and 1100°F. and reductions of 47.5, 74, 83.5 and 89.5 per cent were employed in drawing to 0.132 in. The final anneals were at 875°F., 1050°F. and 1250°F. and were

Jan 1, 1944

By CHARLES W. BENTON

THE following paragraphs comprise such information as the Secretary has been able to obtain concerning the members and associates whose deaths have been reported. Further particulars or corrections of errors, and biographical data concerning deceased members or associates not already noticed in this way, are solicited. Charles IV. Benton was born at Kezar Falls, Maine, Nov. 12, 1843. We have no accurate knowledge concerning the early part of his career. In 1871 he engaged with the N. Y. Honduras Rosario Mining Co., at San Juancinto, Honduras, C. A., and later was employed at the Monserrat mine at Yuscaran, and at Santa Lucia, Honduras, with the Tenero Mining Milling Co. of Pennsylvania. In 1897 he became a member of the Institute. At the time he was stricken with his last sickness he was employed at the Paymaster mine at Tucson, Ariz. He died at Fairmount, Denver, Colo., Sept. 9, 1907. William R. Boggs, Jr.-The notice in the Bulletin for January was incorrect in saying that the murder of Mr. Boggs occurred while he was employed as metallurgical. manager by Mr. W. B. A. Dingwall, at La Maroma, San Luis Potosi, Mex. Mr. Dingwall writes that in March, 1907, Mr. Boggs left him, to return to his home at Winston, N. C., whence he. subsequently went to Durango, Mex., to take, with the Topia Mining Co., a position which he occupied at the tine of his death, Nov. 17, 1907. Mr. Dingwall says that, while in his service, Mr. Boggs never had any trouble with the workmen, but was esteemed and liked by them, as by all who knew him ; and adds, injustice to the State of San Luis Potosi, that the population, even in the mining-camps of that State, is orderly and law-abiding, and that the authorities are vigilant and just. Our

Mar 1, 1908

By John Wulff, Richard P. Seelig

The importance of the pressing operation in the forming of articles by powder metallurgy depends to a great extent on the type of product to be made. While in some few cases the pressing is merely a means of compacting loose powder particles into a solid mass preliminary to a sintering treatment, in most applications it constitutes a molding operation with the purpose of shaping the raw material in powder form into a certain predetermined, accurately defined part not altered in shape by subsequent sintering. In still other cases, no pressing at all but sintering in molds gives useful articles. A limited number of products are made by the simultaneous application of pressure and heat. The factors that control the product of the pressing operation are raw material, lubricant, type, size and shape of die and compact, magnitude and time of application of pressure, as well as temperature of pressing. All such factors need to be controlled; yet, depending on the function of the pressing operation, greater emphasis may be placed on processing factors other than the pressing operation. In any complete discussion of pressing, subsequent sintering cannot be disregarded. For the sake of brevity, the present paper has been limited to the mechanics of pressing and only occasionally refers to sintering. For the same reason, hot-pressing has been omitted as beyond the scope of this paper In any survey of the literature on the pressing of metal powders, the 1938 paper of Balshinl on the theory of the process of pressing deserves mention. The first attempts at an interpretation of pressing phenomena were made by Balshin' and RakovskL2 The experimental results of both are of great interest. Since the experimental results are not described, the work was repeated, using our own interpretation of the possible techniques, and is reported in the following pages. The basic theory of Balshin,' based on a hydro-dynamic analogy, however, leads to hut another way of plotting density and pres- , sure against height of a pressed compact. Since it does not give any new insight into the phenomena, nor account for the influence of side-wall friction, a discussion of the theory has been omitted from this paper. Density Gradients in Compacts The process of pressing metal powders in a die (disregarding for this consideration the powder filling and ejection operations) may be divided into three phases: (I) packing, (2) elastic and plastic deformation, (3) cold-working with or without fragmentation. It must be emphasized that these three steps do not follow each other in sequence; on the contrary, in practice

Jan 1, 1946