By C. Law McCabe, R. G. Hudson

The Knudsen cell has been employed to determine the free energy of formation of Mn7Cs in the temperature range 800" to 950°C. A value of 66,440 cal was found for hH°o for a-manganese. Measurements of the pressure of manganese over a mixed carbide, (Fe,Mn),C, points to a power relationship between aun7cs and N.4,. RECENTLY Kuo and Perssonl have reported that the carbide of manganese which is in equilibrium with graphite at temperatures up to 1100° C is Mn7Ca. There are no published data on the thermo-dynamic properties of this compound. In order to determine the stability of Mn7Ca, it appeared that, by obtaining the pressure of manganese above 8-manganese and also above Mn,C, in equilibrium with graphite, the free energy of formation of Mn7Ca from 8-manganese and graphite could be obtained. In addition, the vapor pressure of manganese, reported by Kelley From data of Bauer and Brunner,' is subject to some uncertainty and further determinations of the vapor pressure of manganese seemed warranted. In this investigation of the pressure of manganese vapor above pure manganese and also above the carbide of manganese in equilibrium with graphite the apparatus used is the Knudsen orifice cell. The same apparatus, experimental procedure, and method of calculating the pressure was used in this investigation as in one previously reported.~ Care was taken to insure that the cells were at constant weight before using them in a run. The manganese charged in the cell was CP grade powder, carbon free, obtained from the Fisher Scientific Co. A spectroscopic analysis of the manganese after appreciable amounts of it had vaporized from the Knudsen cell showed that no element was present in sufficient quantities to contribute to a weighable weight loss or to decrease the vapor pressure of manganese to any appreciable extent. The spectro-graphic analysis was 0.002 pct Cu, 0.05 pct Fe, 0.002 pct Pb, and 0.002 pct Ni. 8-manganesea is the allo-tropic form of manganese which was present in the cell at temperatures used in this investigation. The manganese carbide, Mn,Ca, was made in the following way: In a closed graphite cell manganese powder was added to graphite powder, which was made from graphite rods for spectrographic use. The manganese powder was the same as that described previously; 5 pct excess graphite was added over that required for the formation of Mn7C,. The mixture was heated in a closed graphite cell for approximately 20 hr at 1350°K under vacuum. X-ray analysis revealed that there was no manganese present after this treatment, but that the lines due to Mn,C, were present. In order to prove that there was no volatile carbide of manganese which was effusing out of the cell, the following experiment was performed: A graphite effusion cell containing graphite power, in excess of that to form Mn,C, of a desired amount, was brought to constant weight on heating at 1228°K. The required amount of manganese was accurately weighed and then added to the graphite effusion cell. The cell was placed in a vacuum at 1228°K for one week, which was the time calculated for the manganese to have effused completely, assuming instantaneous formation of Mn,C8. The cell was then weighed again. This experiment was carried out on two different occasions and both times the weight loss of the cell came within 1 pct of the weight of manganese originally charged minus the weight of manganese left in the cell, as determined by chemical analysis. These data are summarized in Table I. This agreement is considered to be within experimental error and is taken as proof that no carbide of manganese is volatile in this temperature range. It was established, by X-ray analysis, that Mn,C, formed before appreciable amounts of manganese vaporized from the metal powder which was charged. The identification of the carbide of manganese which was present in the Knudsen cell in equilibrium with graphite and manganese vapor was carried out by Kehsin Kuo at the University of Uppsala. He established that the authors' sample, which was submitted to him for analysis, contained the phase

Jan 1, 1958

By P. Ramachandrarao, T. R. Anantharaman

EVER since the technique of quenching metals and alloys from the melt (splat cooling) was perfected a decade ago, it has been recognized that the grain size of products solidified by this technique may be extremely small.' The further observation that fcc metals quenched from the liquid state contain very few dislocations has led to the inference2 that metals are subjected to negligible or no stresses during the rapid solidification characteristic of the "gun" or "piston-and-anvil" technique. Evidence for the incidence of appreciable densities of stacking faults has, however, been obtained in case of some splat-cooled fcc and hcp alloys,3 although not for pure metals. In the light of these earlier observations it was considered desirable to study X-ray line-broadening effects, if any, in fcc metals rapidly cooled from the melt. In the present work pure silver (>99.99 pct), aluminum (>99.99 pct) and lead (>99.9 pct) were quenched from the liquid state from temperatures about 50°C above the melting point by the "gun technique" and the resulting foils were subjected to X-ray examination in a Philips Diffractometer. The quenched foils (up to -10 u thick) did not generally stick to the substrate surface and could be easily transferred to the Diffractometer without introducing any plastic deformation. The profiles of the first five reflections from the foils were recorded in each case with Cu Ka, radiation at the slowest available scanning speed of 1/8 deg per min. To correct for instrumental broadening, profiles were also recorded from the metals annealed in vacuo at suitable temperatures. The integral breadths of the X-ray reflections were arrived at by a procedure described earlier.' There was a distinct suggestion of preferred orientation in the recorded intensities of reflections from aluminum and lead foils. Such an effect was not observed in case of silver. In addition, the integral breadths of X-ray reflections from splat-cooled aluminum and lead were not significantly different from those recorded for the annealed metals. The analysis was therefore continued only for silver where the X-ray line broadening was appreciable. The pure diffraction broadening, B, was evaluated for each X-ray reflection (hkl) from silver from the observed, B, and instrumental, b, breadths with the aid of each of the three equations due to Scherrer,5 Anantharaman and Christian,6 and Warren and Biscoe,7 respectively: Bs= B-b BAC=B- b2/B Table I gives the values of particle size, 71, the lattice strain, E, arrived at by the use of the following well-known relations and on the assumption that all observed diffraction broadening could be attributed to lattice strain or particle size, respectively: E = 1/4 cos ? n= B cos ? where A is the wavelength of X-radiation and 0 is the Bragg angle. As no significant peak shifts or asymmetry could be detected in the profiles from the foils, the possibility of any significant contribution due to twins or stacking faults was ruled out. The absence of faults is by no means surprising since pure silver is known to develop stacking faults only on severe deformation and the stacking fault densities recorded so far for even silver filings have been extremely low.' The very low values for percentage mean deviation from the mean value for the particle size in Table I strongly suggest that all observed broadening in splat-cooled silver can be attributed only to small particle size. This conclusion receives further support from the lowest mean deviation recorded for data computed from the Scherrer equation based on Cauchy profiles that are considered characteristic of particle size broadening. Further analysis for separation of particle size and lattice strain effects was considered unnecessary in view of the very large mean deviations obtained for strain values and also the earlier results suggesting absence of even detectable strain in metals and alloys quenched from the melt. It is to be stressed in this connection that the particles are actually grains and not cells formed by walls of high dislocation density usually encountered in deformed samples. As such, the absence of strains is not surprising. The present results are probably the first to record X-ray line broadening due only to small particle

Jan 1, 1970

By R. C. Buehl, M. B. Royer

High manganese slags of low phosphorus and iron content are produced by air oxidation of high phosphorus spiegeleisen in a basic-lined converter. Control of phosphorus and iron within specification limits for ferromanganese ore feed is obtained by a unique cyclic operating procedure. Various types of slags, or synthetic manganese ore, can be made. AN affiliated paper' describes the production of high phosphorus spiegeleisen containing 14 to 23 pct Mn and up to 4 pct P in an experimental blast furnace from open-hearth slag or manganiferous iron ore. This phosphorus content is too high for use of the spiegel in normal steel-production operations. Consequently, a preferential separation must be effected whereby the manganese is concentrated in a product that is usable in industrial operations. The preferential separation methods being investigated for this phase of the work are confined to pyrometal-lurgical processes for ready incorporation into steel-plant operations. It is fortunate that manganese is more actively oxidizable than iron or phosphorus, and therein lies a preferential separation method for isolating manganese from these two elements. Silicon is more strongly oxidizable than manganese, and its oxidation precedes, or occurs simultaneously, with manganese. Therefore, manganese and silicon are separable into a high manganese oxide slag phase while the phosphorus and iron remain in the molten metallic state. Complete separation of these elements represents an ideal condition which is not generally attainable in actual operations. This pyro-metallurgical method for separating manganese from phosphorus and iron by preferential oxidation was investigated by blowing 500 lb of metal in a basic-lined vessel to obtain preliminary information on the effectiveness of the procedure. Certain conditions of attainment in the separation process are desirable in any method for removing manganese from high phosphorus spiegeleisen, such as: 1—High recovery of manganese in the oxidation product; 2—the product to be of equal or better quality than ferromanganese-grade ore—48 pct Mn minimum, less than 10 pct SiO2, and Mn-P ratio of 300:1; and 3—attainment of the enumerated objectives in a product amenable to industrial handling, such as a slag of high manganese content that will flow from the processing vessel and of sufficient fluidity for ready separation of metallic granules that may have become mixed with the manganese slag phase. Previous Work Recovery of manganese from low grade ores and industrial byproduct slags by smelting to spiegeleisen, with subsequent oxidation to synthetic ferro-manganese-feed ores, has been a subject for periodic investigation during the past four or five decades in the United States and Germany. Joseph' and associates of the Bureau of Mines North Central Experiment Station, Minneapolis, Minn., smelted manganiferous iron ores of the Cuyuna range, Minn., to spiegeleisen and subsequently tried air and ore oxidation procedures for concentrating the manganese into synthetic ferrograde manganese ore. Joseph's results on the operation of a side-blown basic-lined converter for air oxidation of manganese from molten spiegeleisen were so discouraging that the procedure was abandoned after 11 blowing tests. Much slag was thrown from the converter vessel; phosphorus content was four to five times the maximum allowable for ferro ore; and a manganese-iron ratio of only 2 or 3:1 was obtained in the slag instead of the required 8:1. Oxidation of manganese from spiegeleisen with about 0.5 pct P, by adding iron ore to molten spiegel in an experimental open-hearth furnace, proved moderately successful in Joseph's experiments. The main drawback to the operation was the necessity for over-oreing for effective oxidation of the manganese with consequent too high iron oxide residual in the slag. Furthermore, the phosphorus content was proportional to the iron concentration and therefore much too high, so that several hours of reduction by a carbonaceous material were required to adjust the iron and phosphorus to the desired content of high grade ferro feed. A troublesome feature of the slag product of the spiegel oxidation process was its lack of fluidity if the silica content was less than 10 pct, the concentration considered desirable for the synthetic ore. Approximately twice the desired concentration of silica was required to impart enough fluidity for transfer from the vessel by pouring. The acute shortage of manganese in Germany

Jan 1, 1953

By E. S. Anolick, Joseph Singer

The magnetic after-effect, in the form of time decay of permeability (l/µ), has been used to obtain independent data on the solubility of' carbon in pure iron. The results differ slightly from the solubilities obtained through internal -friction experiments. The mechanism of the time decay being the magnetic analogue of internal friction, it appears necessary to explain the observed discrepancies, and some suggestions are made. THE purpose of this work was to establish the reliability of the time decay of permeability as a measure of dissolved interstitial in the body-centered-cubic lattice, and further, to establish techniques suitable for such measurements with samples of a form convenient for various other measurements. This particular sample form was the "epstein" strip, i.e., 25 cm by 3 cm by 0.035 cms. While the general conclusions are not limited by this geometry, there are two aspects of the samples that may be relevant: a) texture, and b) grain size, which ranged generally from 1 to 10 mm. Effects due to these two possible parameters were thought to be small and were not investigated. Calibrating the time decay technique and the other experimental procedures by measuring the solubility of carbon in pure iron suggested itself because of the accumulation of data on this subject through the related technique of the internal friction'; The essentials of this report have been published in a somewhat condensed form.5 Since then some additional data have been taken. It is the purpose of this paper to add these data and to provide more complete description of the experimental techniques than was possible then. The time decay of permeability is a form of the magnetic after-effect.6,7 Permeability is measured immediately after demagnetization (µº) and also long after (µ8). The time decay, ?(l/µ), is the difference 1/µ8 - 1/µ0 and has been considered to be proportional to the concentration of a dissolved interstitial6,8,9,12 The relaxation time! 7, is characteristic of a particular diffusion, and affects the permeability as follows: where he being the activation energy for diffusion of the interstitial. Reference is made to the works of snoek6 and Neel7 for a complete discussion. A brief exposition of the principal ideas may be in order here, as follows. On the basis of the simplest model, resistance against domain wall motion increases with time after demagnetization due to the diffusion of interstitials to preferred sites created by the magnetostrictive tetragonolization under the strong magnetic field. Thus permeability, measured with a small field after the abrupt removal of the large field, will continuously fall with the process of diffusion of the interstitials, and the total "time decay" (or "time decrease") should be proportional to the amount of interstitial in solid solution. In the present report, use is made only of the total time decay rather than of the nature of the progress of the decay; the only problem involved in this approach is the need for assurance that only one interstitial is contributing to the effect as used. It is felt that the special use made here of the total time decay warrants the conclusions. Other work has been going on elsewhere on the detailed study of the nature of the time decay.8'9 EXPERIMENTAL A) Materials—12-lb ingots were made in a vacuum furnace from high-purity iron and by a series of hot and warm reductions were brought down to 14-mil strip. This was cut into 25-cm epsteins. The pure iron was decarburized at 750 °C by hydrogen. The time decay measurement for the decarburized iron (see below) indicated a satisfactorily low starting level of interstitials. Grain growth to grain sizes of 1 to 10 mm was produced in the pure iron by a 700" anneal in hydrogen after a critical reduction of about 7 pct as suggested by previous trials. No measurement of texture in the pure iron was made. The grain size was taken to be large enough to be beyond any sharply critical size regarding solubility. B) Infusion of Carbon—Since the permeability measurement required about two dozen epsteins, a special method of carbon infusion had to be developed to ensure homogeneity of infused carbon. This was accomplished by setting the samples edgewise in a

Jan 1, 1961

By O. R. Morris, G. L. Hawkes

A galvanic cell, using as electrolyte a fused salt solution of calcium carbide and as electrodes carbon and a Fe-C alloy of known composition, has been set up to study the thermodynamics of Fe-C alloys in the temperature rmzge 800" to 1000°C. Time independence and reproducibility of the cell electromotive force were taken as evidence of the reversible behavior of the cell. Carbon was believed to be present in the electrolyte as the so-called acetylide ion, C;-. The plots of the cell electromotive force us temperature for a specific alloy composition were straight lines within the limits of experimental error. The average Partial molar enthalpy of carbon in iron relative to pure carbon was found to be +10,610 i 93 cal per g-atom C. Thermodynamic analysis of the data has led to the following equation for the carbon activity, ac, based upon pure carbon as the standard state: In ac = In Zc + 10,560/RT + (10.02 + 77O/T)ZC - 2.350 where ZC is the lattice ratio [nC/(nF, - nc )] and T is the absolute temperature. This equalion gives carbon activity values generally slightly lower than those from gas equilibration studies reported in the literature. METAL LOGRAPHIC examination of a polished cross section of the steel anode used in the electrolysis studies of fused salt solutions of calcium carbide by Morris and Harry revealed extensive carburization of the steel by the electrodeposited carbon. This carburization was reflected in the variability, with time, of the applied potential to the electrolysis cell, necessary to maintain a constant current density at the electrodes. This observation suggested the setting up of a galvanic cell of the "alloy concentration" type to study the thermodynamics of some metal-carbon alloys. Cells of this general type have been widely used for the study of alloy systems.2 In view of the availability of published data in respect of the austenite phase of the Fe-C system, it was decided to carry out measurements upon these alloys before proceeding to studies of less well documented systems. The galvanic cell may be written: where [C] is carbon dissolved in iron. The electrolyte was a fused salt solution of calcium carbide, containing some 5 to 10 mol pct of carbide. The cell reaction is believed to be: C(s)-[CI [I1 Carbon forms an interstitial solid solution in iron, with the atoms located in the octahedral interstices. In the fcc crystal structure of austenite there is one octahedral interstice per iron atom. Thus, the lattice ratio, ZC, shown by Gurney3 to be the fundamental concentration parameter in the context of interstitial solutions, is given by: where nc and nFe are the number of carbon and iron atoms, respectively. chipman4 has recently shown empirically the advantages of using this concentration parameter instead of the more usual atom ratio or atom fraction. The cell electromotive force, E, assuming reversible behavior, is related to the carbon potential or the partial molar free energy of carbon in the solid solution relative to pure carbon at the same temperature and pressure, GP at the composition ZC, by the equation: where z is the carbide ion valency and F is the Faraday constant. An activity of carbon, ac, in the solution relative to the value of unity assigned to pure carbon, and an activity coefficient, qC , are defined such that: where R is the gas constant and T the absolute temperature. GF is further related to the relative partial molar enthalpy Hm, and the temperature coefficient of the cell electromotive force, (aE/aT)Zc, by the equations: Measurement of the cell electromotive force thus enables calculation of the relative partial molar thermodynamic properties of carbon in iron, if z is known. At E = 0, the solid solution is in equilibrium with pure carbon. More convenient for many purposes is the standard state based upon the infinitely dilute solution, Henry's law. The relationship between the activity coefficient of carbon based upon this standard state, and that based upon the pure carbon standard state, qC , may be obtained by considering the free energy of transfer of carbon from the latter standard state to the former. The relationship is: where +:H is the activity coefficient of carbon in the hypothetical standard state based on a reference of

Jan 1, 1969

By Reynold Q. Shotts

CHEMICAL methods, based on the relative rates of oxidation of fusain, bright coal, and dull coal by nitric acid, have been devised to determine these coal components.1-4 Results obtained by oxidation methods for fusain have been checked against results obtained from microscopic methods5, 6on duplicate samples of the same coals, but to the author's knowledge this has not been done for bright and dull coal components. For this reason it is not certain that the two methods of analysis identify essentially the same chemical or physical units. It would be highly desirable to see results of the application of both methods to duplicate samples, but in the absence of any such data the author has attacked the problem indirectly. From the U. S. Bureau of Mines samples were obtained of three Alabama coals which the USBM had analyzed optically and reported on over the past 30 years. These samples were subjected to analyses by oxidation rate methods. Results of this work, and comparisons with the USBM analyses, have been published." This was the first indirect approach to the problem. The present report attempts a second indirect approach by way of internal validation. By nitric oxidation samples of two whole coals were carefully analyzed for fusain, bright coal, and dull coal. One coal was analyzed in duplicate. Duplicate portions of each of the coals were divided into three density fractions by means of heavy liquids. A duplicate portion of one of the coals was divided by sieving into three size fractions. Each fraction was analyzed by oxidation and its percentage composition calculated in terms of fusain, bright coal, and dull coal. Because the weight percent of each fraction was known, a material balance calculation for the whole coal was also made. The resulting reconstituted analysis of the whole coal could be compared to that determined by direct analysis. In addition, specific reaction rate constants were determined for each component and for each whole coal or fraction. Arbitrary reactivity indexes were calculated by dividing by 100 the sum of the products of the percent of each component in the coal and its specific reaction rate constant. The resulting figure was an average reactivity index for each coal or fraction. Weighting the reactivity indexes for each fraction by the percent of the fraction in the coal gave a reactivity index for each whole coal which could be compared to that calculated directly from the whole coal analysis. If oxidation analyses really delineate definite physical entities within the coal, or even definite groups of similar entities, reconstituted analyses calculated from fraction analyses should check closely those made of the whole coal. It probably is true that optical methods identify and describe a greater variety of components than do chemical methods and that variations are wide in the appearance and quantity of those components identified optically. Chemical methods based upon differences in oxidation reaction rates would of necessity be less discriminating, as between similar components, than would optical methods. The procedures followed for oxidizing the samples, analyzing the residues, plotting and calculating the percentage of each component, and calculating its specific reaction rate constant have been fully described.'-' In brief the method originally proposed by Fuchs et al.1 for the determination of fusain consists of the oxidation of small samples of coal in boiling 8N nitric acid in a condenser-fitted flask. After boiling for periods of 1/2 to 4 hr, the unoxidized residue is filtered and washed. The washed residue is treated with normal sodium hydroxide, diluted, and allowed to stand for several hours. The resulting brown liquor is removed, and the filtered residue dried, weighed, ignited, and weighed again. The ash-free residue is expressed as a percent of original dry, ash-free coal. The percent residue is plotted against time, and the extrapolation of this line to zero time gives the percentage of dry ash-free fusain present in the original sample. The shape of the resulting time plots has been explained' by the assumption that they are the result of two different types of reaction, the first part representing a first order reaction with rate a func-

Jan 1, 1956

By J. F. Pierce, S. M. Enterline

Since January 1959 a zinc refiner of novel design has been in operation at Blackwell, Okla., producing 99.995+ zinc from the output of the Blackwell horizontal retort smelter. The refiner is a continuously operated, pyro-metallurgical unit with principal dimensions horizonhl permitting one floor operation. It is very ruggedly constructed. Furthermore it is not subjected to deterioration from high concentrations of iron in the feed metal because the boiling units are separate from the rectification columns and constructed with silicon carbide brick arches through which the heat is transferred radiantly to the zinc. A zinc refiner of novel design has been in operation since January 1959 at the Blackwell, Okla. plant of the Blackwell Zinc Co., Inc., a wholly owned subsidiary of American Metal Climax, Inc. Developed by the company's technical and operating staffs, the new refiner produces special high-grade zinc (nominally 99.995+ pct Zn) from the prime western1 slab output of the Blackwell horizontal retort smelter. The refiner is a continuously operated, pyromet-allurgical, high-capacity unit employing fractional distillation to separate zinc from its impurities, consisting principally of lead, cadmium, and iron. In prime western slab, these elements may vary in concentration from 0.005 to 1.6 pct. Table I shows the impurities usually encountered in the Blackwell prime western metal fed to the refiner together with their boiling points and vapor pressures at 907oC. The commercial pyrometallurgical smelting processes for extracting zinc from ore include distillation from retorts and a limited degree of refining can be accomplished by redistillation in similar retorts. To achieve special high-grade purity, an impractical number of batch redistillations would be required, however, with an accompanying loss of much metal. A continuously operated and integrated unit is required in which fractional vaporization and condensation can take place in a large number of stages. The first commercial continuously operated unit was developed by the New Jersey Zinc Co.4 In the separation of any two substances the degree of separation is limited if a mixture exists having a constant boiling point. The Zn-cd5 and Zn-pb6 systems contain no constant boiling points and hence these metals may be separated to any degree of purity. Basically, the pyrometallurgical refining of zinc involves three steps: a) iron, copper, and other metals having no appreciable vapor pressures at 907ºC concentrate in the bath when the impure zinc is boiled, b) lead, bismuth, antimony, and other metals having boiling points above but closer to that of zinc are selectively condensed from the vapor boiled from the bath, and c) cadmium and other metals having lower boiling points than zinc are fractionally distilled by reboiling and subsequent condensation of the zinc from the vapor. The boiling and condensation of zinc must be conducted in vessels constructed of materials which are refractory at the temperature involved (907 ºC) and it is highly desirable that they also be resistant to attack by the various metals. This requirement dictates construction from relatively small, simply shaped pieces which limits the pressures which may be employed to avoid leakage through the numerous joints. Stresses induced must be limited essentially to compressive ones and suitable provision must be made to permit thermal expansion of the components in order to minimize these stresses. Where heat is to be added for boiling or removed for condensation, refractory material through which the heat flows must have a high thermal conductivity. Silicon carbide is highly conductive but is subject to attack by iron and is expensive compared to other commonly employed refractories. A hard, dense aluminous fireclay is well suited to contain these metals where high thermal conductivity is not required. Zinc will penetrate the pores of fireclay brick but only to a limited depth in an exterior wall and has little effect other than an increase in weight and conductivity. The design objectives of the Amax refiner were: a) to achieve a long life by heavy, rugged construction and by employing silicon carbide refractories only where required for heat conductivity and not in contact with liquids of high iron concentrations, b) to simplify operation, manning and control by essentially horizontal construction, and c) to obtain high capacity in a single unit. DESCRIPTION Flow of metal through the Amax refiner is shown diagrammatically in Fig. 1 and schematically in Fig. 2.

Jan 1, 1963

By D. R. Wieland, A. N. Barron, A. R. Hendrickson

A definite relationship has been found between the reactivity of flowing hydrochloric acid and its shear rate in a carbonate fracture. Both flow velocity and fracture width affect the acid reaction rate. Laboratory studies were conducted on acid reactivity at different flow velocities through horizontal-linear fractures, using 15 per cent hydrochloric acid at 80' F and approximately 1,100 psi. Fracture width varied from 0.02 to 0.20 in. These data provide a new basis from which the spending time and penetration of the acid can be estimated. Equations were derived expressing the relationship between injection rate, fracture width, acid concentration, time and fracture height, for linear and radial fracture systems. Because the penetration of the acid before spending is closely related to the extent of productivity increase resulting from an acidizing treatment, these data provide a valuable insight into some of the controlling factors that must be taken into consideration during treatment preplanning. INTRODUCTION Acidizing of carbonate reservoirs to improve production characteristics has been widely practiced since 1932. Originally, it was assumed that the acid uniformly penetrated natural formation pores and flow channels, enlarging them and thereby increasing their flow capacity. Little consideration was given to the reaction rate of the acid, or how far it would penetrate away from the wellbore into the formation, before spending. It has been shown recently' that, unless fractures are present in the rock, very little penetration is attained before spending, and the benefits of the acidizing treatment are largely confined to the immediate vicinity of the well-bore. Therefore, acid treatments may be classified into two categories: (1) matrix acidizing, in which the acid flows through multiple: formation pores; and (2) fracture acidizing, in which the bulk of the acid travels through fractures in the rock, whether natural or induced. When acidizing treatments are conducted at pressures of sufficient magnitude to open and extend such fractures, it is often desirable to inject a propping agent to hold the fracture open after the treating pressure has been released, thus providing a highly conductive flow channel through the rock. In some cases where acid attack produces surface irregularities, the resulting flow passages can be sufficient to provide high conductivity without use of a propping agent. During injection, the acid dissolves the carbonate rock with which it comes in contact until it is spent. Deeper penetration of the spent acid into the formation produces no appreciable benefit (if no propping agent is used) because the unetched fracture faces will rejoin when treating pressures are released and the fracture will "heal", with negligible resultant conductivity. The spending time of the acid thus becomes important in determining how far from the wellbore the improved-conductivity zone extends. The spending time of acid after injection into carbonate rock depends on the rate at which the acid reacts with the rock. This in turn is controlled by a number of factors, as previously reported. 2-4 These include temperature, pressure, acid concentration, rock composition, injection rate and the area-volume relationship between the acid solution volume and the surface area of the formation flow channels through which it penetrates. Thus, in matrix acidizing, where an extremely large area is exposed to the acid, spending is rapid. In contrast, spending time is prolonged in open fractures, where the area-volume ratio is much lower. Thus, greatest penetration of the acid before spending will be achieved in acid-fracturing treatments where fractures are held open by hydraulic pressure. Perkins and Kern5 have presented equations for fracture-width determinations which, for hard formations such as limestone or dolomite, indicate that high injection rates and viscous fluids are required to create wide fractures. Increasing the injection rate will, in itself, produce faster reaction rates. Because this type of reaction can be considered to be first-order diffusion-controlled, '-' the rate of movement of fluid past the rock surface affects the thickness of the diffusion layer, in turn affecting the reaction rate. Staudt, et al,10 report the results of tests in which a rotating marble cylinder was immersed in acid, and the weight loss at different speeds determined. Such test conditions, however, are not truly indicative of the situation in a formation during an acid-fracturing treatment. This paper reports reaction-rate data obtained under

By J. T. Norton, Pekka Rautala

The phases and equilibria in the W-Co-C system have been studied by X-ray diffraction methods, metallographic technique, and thermal analysis. In addition to the 7 phase, two double carbides, called 8 and have been revealed. The compositions correspond to CO3 W6C2 and Co3-W10C4. The reactions leading to these phases have been explained and tentative diagrams of stable and metastable equilibria proposed. The basic reactions in sintering cobalt cemented tungsten carbides are discussed. THE W-Co-C system is of fundamental importance in practical carbide manufacturing as well as for the understanding of the sintering mechanism. Surprisingly little is known about this system, for the probable reason that all the important alloys are of two-phase structure and that the diagram Co-WC has been treated as a quasi-binary. This obviously is incorrect, because WC decomposes before melting. One ternary phase, 7, of composition Co3W3C has long been known. It was first studied by Adelskold, Sundelin, and Westgren,1 although the isomorphous iron-tungsten carbide was known earlier. There have been in the literature several reports of two 7 phases.' " Also the 7 phase has been considered unstable by Takeda4 and Westgren.1 The Co-WC diagram has been studied by Wyman and Kelley5 and a quasi-binary diagram has been published by Sandford and Trent.2 Takeda has published a tentative Co-W-C diagram, considering both metastable and stable equilibria. However, the lines of two-fold saturation are shown only partially and it seems impossible to complete the diagram without violating the phase theory. Therefore it seemed desirable to examine the system in more detail. Experimental Procedure The alloys used in the present investigation were made of powders of tungsten, tungsten monocarbide, cobalt, and carbon and were of the grade used in manufacture of commercial cemented carbides. The powders were ground and mixed in small stainless steel ball mills, using balls of the same material. Benzene was used as a dispersing agent. The mixing period was 1 hr, since this was shown to give suffi- ciently good mixing of the powders without too great a contamination from the mill. After ball milling, the specimens were pressed in cylindrical or rectangular dies. No paraffin or other lubricant was used and the small compacts had sufficient green strength to be handled without difficulty. Several sintering furnaces were employed. The most satisfactory arrangement was a vacuum furnace based on the Arsem principle which employed a graphite helix as the resistance heating element. Specimens were placed on graphite stands and there was generally a slight carburization or decarburiza-tion of the specimen surface, depending on the carbon content of the alloy. The evaporation of the cobalt at a sintering temperature of 1400°C was not significant, but became severe at 1500°C and higher. The sintering time was 1 hr at 2000°C and 2 to 4 hr at lower temperatures. It was not possible to quench the specimens, but the cooling rates were rather fast, greater than 300°C in the first minute. In the system under investigation, the reactions are sluggish, and it is believed that the high temperature structures are satisfactorily retained. The principal method of investigating the sintered specimens was X-ray diffraction by the Norelco recording spectrometer. Approximate determinations of the phase boundaries were made by the disappearing phase method. Ternary Phases To study the phase formation in W-Co-C system, a series of specimens was sintered at 1400°C. In this experiment two ternary phases, called here ? and k were formed in addition to the well-known 7 phase. The 7 phase, which has been completely described by Westgren: showed a range of homogeneity from 7 to 20 pct C and from 38 to 48 pct Co. At 1400°C the 7 phase was found to be in equilibrium with monotungsten carbide, 8, tungsten, 8, #?, and liquid. The boundaries toward #? and liquid were difficult to determine and appeared to be very temperature sensitive. The other boundaries are believed to be well fixed. The homogeneity range of 7, as measured in this work, is considerably smaller than the one

Jan 1, 1953

By E. S. Machlin

An extension of the thermodynamic theory has been made for the case of irreversible growth processes occurring by the motion of an interface. The theory is applicable to such diverse phenomena as diffusion, growth in recrystallization, continuous grain growth, growth of carbides, etc., growth of eutectoid products, growth in solidification, recovery, "slipless" flow, etc. THE publication of a recent book1 has served to focus attention on a very powerful means of treating certain irreversible processes. This method which has been formally described as the thermodynamic theory of irreversible processes is applicable to processes which involve an approach to equilibrium and for which the deviations from equilibrium are small. The irreversible processes can be classified into three groups: chemical reactions, transport processes (diffusion, heat and electrical flows), and relaxation phenomena involving a degradation of internal energy to more stable states. The limits of applicability of the theory can be precisely defined1,2 for each type of irreversible process. For example, in a chemical reaction at constant temperature and pressure, the Gibbs free energy released per mol in the process should be less than the thermal energy, RT. Another type of irreversible process, which sometimes involves a combination of the first two of the above-mentioned groups, is treated in this paper. This process is one characterized by the motion of an interface separating two regions having different values of free energy and may be briefly described as a growth process. Prigogine2 and Herring3 have treated special cases of this type of process. Previous conscious applications of the theory in metallurgy have been limited to the field of diffusion, one of the transport processes. Darken,4 Bardeen,5 Prigogine2 and others have made significant contributions in this respect. Some other applications of the theory are described in this paper. The Theory The thermodynamic theory of irreversible processes is based on the work of Onsager,6 DeDonder,7 Prigogine2 and others. A resume of the theory has been given by Prigogine2 and DeGroot.1 A brief description of the theory follows, although for a complete understanding the reader is urged to read the references. It is first assumed that the change in entropy, even for a system removed from equilibrium, is given by dS = [dU + pdV - Si µi, dn, - Sk Pk dxk]T-1 Using this expression, the irreversible entropy production in the system is calculated by subtracting the contribution to the change in entropy of the system by transfer of heat, work, or matter from the surroundings. Thus, for example, the irreversible entropy production of a system at constant temperature and pressure is given by dtS = — — dG (DeDonder7) Now it has been shown by Prigogine,2 DeDonder,7 and DeGroot1 that the rate of irreversible entropy production diS/dt, when calculated in the manner suggested, can be written as a sum of products of conjugate forces XK and fluxes Jk, i.e., d,s/ = Sk Jk Xk [I-1] dt The assumption is next made that a linear relation exists between a given flux and the forces, obtained from Eq. I-1, i.e., Ji = Sk Lik Xk (i = 1, 2, . . . n) [I-2] Generally, there is a degree of freedom in choice of the fluxes and forces. However, for all the choices consistent with Eq. I-1 the Onsager8 relations, based on the principle of microscopic reversibility, namely, Lik = Lki, are valid. The coefficients Lik, depending upon the choice of the conjugate fluxes and forces, may be more or less dependent upon the parameters defining the state of the system. In general, the proper choice of fluxes and forces utilizing Eq. I-1, makes the coefficients Lik independent of time. Also, because many of the three classes of irreversible phenomena have already been treated,1,2 a proper choice can be made by analogy. In any case, the validity of Eq. 1-2, from whatever choice made using Eq. I-1, must be tested by experimentation. The theory, thus, comprises the following steps: 1—The irreversible entropy production is calculated to yield Eq. I-1. 2—The terms in Eq. I-1 are grouped

Jan 1, 1954

By G. G. Hancock, H. H. Johnson

Hydrogen gas at atmospheric pressure is shown to cause substantial embrittlement in a martettsitic high-stretzgth steel. Subcritical crack growth is observed at very lom stresses and with high growth rates. It is suggested that an adsorbed layer of hydrogen atoms at the crack-tip surface provides the damaging hydrogen. Oxygen in small quantity, as little as O.7 pct by volume, is shown to eliminate subcritical crack growth in gas environments caused by hydrogen or water vapor. However, dissolved oxygen in water has little or no influence upon crack-growth rates. Oxygen-stopped cracks may be restarted by water, or by hydvogen or water vapor if oxygen is removed from the environment. These observations are interpreted in terms of preferential adsorption of oxygen at the crack tip and the formation of an oxide barrier. RECENT investigations1-3 have demonstrated that environmental factors are frequently responsible for delayed failure in martensitic high-strength steels. The environment causes crack initiation from preexisting cracklike flaws at unexpectedly low stresses, often far below the uniaxial yield strength. The crack then propagates at a rate controlled by the environment and the crack-tip stress-field intensity; during this period crack propagation will cease if either the stress or the aggressive environment is removed, and this may be considered a definition of subcritical crack growth. Fracture occurs when the crack has grown to a critical length, such that the fracture toughness of the steel is exceeded. Several liquids are known to cause delayed failure, but water and water vapor are the most severely damaging of the environments investigated to date.'-3 It has been suggested that hydrogen produced during corrosion reactions may be the actual embrittling agent2 The severe embrittlement caused by water vapor inevitably raises the question as to whether other gas environments are damaging. Previous work4'5 has demonstrated that high-pressure hydrogen (2250 psi or greater) is an effective embrittling medium, as measured by such criteria as reduction in area, notch tensile strength, and time to failure. Moreover, the embrittlement was eliminated by the addition of small quantities of air or oxygen to the high-pressure hydrogen, but it was not influenced by additions of nitrogen or argon.4 In the present study attention is focused upon gas environments at atmospheric pressure, in particular hydrogen and oxygen. The influence of these constituents upon the initiation and growth of a crack from a pre-existing cracklike flaw in a high-strength steel was determined directly by the electric-potential method of monitoring crack growth. MATERIALS AND PROCEDURE The H-11 steel was supplied by the U.S. Naval Research Laboratory as 3 by 12 by 0.065 in. sheet specimens with 1-in. transverse center slots. The slot tips were finished by Elox machining to a radius of 0.001 in. or less. The yield strength was 230,000 psi; chemical composition and heat-treatment schedule are given in Table I. The experimental apparatus, precracking procedure, and incremental loading sequence have been described previously.3 In the only significant change, precracking was sometimes carried out by a hydrogen embrittlement and baking technique. All experiments were conducted at room temperature; the hydrogen gas environment was purified by a commercial palladium purifier. Crack initiation and propagation were followed by the electric-potential method,'-3 using a calibration that has been recently dicussed. Stress-field intensities at the crack tip were computed by the conventional Irwin frmula; the plasticity correction was negligible and therefore not included. EXPERIMENTAL RESULTS A striking brittleness associated with molecular hydrogen at atmospheric pressure is demonstrated by the data in Table I1 and Fig. 1, which indicate that subcritical cracks in hydrogen initiate at lower stress-field intensities and propagate more rapidly than in fully humid argon. Ki and Kf are the crack-tip stress-field intensities at initiation and termination of subcritical crack growth, respectively. Termination, of course, corresponds to fracture. In both hydrogen and humid argon Ki is less than Kf

Jan 1, 1967

By Nicholas J. Grant, A. W. Mullendore

Measurements of grain boundary sliding were made on polycrystal and bicrystal tensile creep specimens of Al-2 pct Mg at 500oand 700oF. Grain and pain boundary orientation factors were studied with respect to their effect on the magnitude and direction of grain boundary sliding. It was concluded that a large part of the observed sliding may be caused by the operation of slip crossing the grain boundaries. Supporting evidence for this model from other investigations is also given. GRAIN boundary sliding in metals during elevated temperature deformation has frequently been thought of as an independent mechanism with its own characteristic stress, temperature, and structure dependence. Further, it is common to regard the grain boundary as the weak link during creep deformation since: 1) the strength of apolycrystallinemetal, as meas-sured by creep rate or rupture life, decreases at\a more rapid rate when sliding comes into action, and 2) grain boundary sliding, as revealed by "boundary darkening" and fold formation is often the first visible deformation. On the other hand, more quantitative observations, in both polycrystals and bicrystals, have shown boundary deformation to be closely related to the over-all deformation of the specimen. The curve of grain boundary contribution to elongation vs time takes a shape similar to that of the total creep curve,',' and the apparent activation energy for sliding appears in most cases to have the same value as that for total creep.3 In order to reconcile these observations, one is left with these possibilities: 1) The grain boundary and grain deformation rates are both controlled by the same rate limiting processes. 2) The rate of sliding is limited by accommodation deformation in the grains. 3) Sliding is the consequence of grain deformation. 4) Grain deformation is dependent on prior grain boundary deformation. Alternatives 2) and 3) would view grain boundary sliding as occurring in series with another deformation process which could be rate controlling. McLean prefers item 3) as the sliding basis,4 where subgrain rotation results from dislocation accumulation in the substructure at the grain boundary. Crussard and Friedel's5 treatment of grain boundary migration considers that dislocations are forced into the grain boundary and are dissociated into dislocations with Burgers' vectors nearly parallel to the grain boundary. The movement of these partial grain boundary dislocations then produces the sliding. The results of this investigation have indicated alternative 3) to be the most appropriate and it is this aspect of grain boundary sliding which will be analyzed. EXPERIMENTAL PROCEDURE Three types of tensile creep tests were employed in this study: (I) A constant load test of one very coarsegrained polycrystalline specimen at 500° F, 3600 psi, 1 pct per/hr strain rate to examine the grain and grain boundary orientation factors in grain boundary sliding. (II) Constant strain rate tests of polycrystalline specimens at 510o and 715o F, 2 pct per/hr strain rate to determine the grain boundary contribution to elongation at very low total strains. (m) Constant strain rate tests of bicrystals of various grain and grain boundary orientations at 500°F, 2 pct per/hr strain rate to obtain further information on the orientation effects in grain boundary sliding. The material used in the tests was a high-purity Al-1'.92 mg alloy, kindly furnished by Alcoa. Its composition is given in Table I. The alloy is a solid solution at the test temperatures. The coarse grained polycrystalline specimen for test (I) was prepared by recrystallizingthe machined specimen, straining it about 1pct intension at room temperature and annealing at 900°F for 8hr. The constant strain rate specimens (11), with an 178 in. sq. by 1/2 in. long gage section, were cut from 1/8 in. thick sheet of cold rolled and annealed (8 hr at 1000oF) material. The latter specimens were supported in a special jig during the milling operations to avoid any bending, and the gage section was subsequently heavily electropolished to remove the cold-worked surface layer. The bicrystals (ID) were machined in the same

Jan 1, 1963

By J. H. Jackson, J. G. Kura, M. C. Udy, L. W. Eastwood

The melting and casting of any commercial metal depends upon the success with which the problems attendant to the handling of the specific metal are overcome. Common difficulties encountered in the handling of commercial metals are tendencies to burn or oxidize excessively, low fluidity, entrapment of dross, hot cracking, cold embrittlement, cold shuts, and un-soundness caused by gas evolution. Beryllium is not only subject to these same difficulties but is generally more sensitive to them than are the more common metals, thus necessitating more exact founding precautions. Characteristics of Beryllium Certain characteristics of beryllium which make it particularly difficult to handle in the plant or laboratory are as follows: 1. The melting point of beryllium is about 2400°F and pouring temperatures vary from 2600 to 2900°F, depending upon the degree of fluidity required. The extreme chemical activity, combined with the high temperatures, makes necessary the use of inert atmospheres, slags, or vacuum for protection during melting and pouring. Furthermore, beryllium tends to react with the melting crucibles, tools, and molds, thus requiring the selection of suitable materials and proper maintenance of these items. 2. The very marked absorption of gas by molten beryllium and the subsequent evolution of gas during solidification causes a great deal of difficulty with unsoundness. Beryllium castings may also be subject to unsoundness as a result of gas formation by chemical reaction with the mold surface during solidification. 3. The very marked chemical affinity between molten beryllium and the normal atmosphere causes the formation of dross. On relatively quiescent melts, this dross forms a very tenacious film which, if carried over to the mold, can cause defects such as the formation of skins or dross in the interior or on the surface of the casting; folds or defects similar to cold shuts may also be found. 4. During the pour and attendant turbulence, the dross may be mixed into the metal and then carried to the casting. There it may be entrapped during freezing and cause internal defects, or it may float to the surface and cause severe dross defects on the cope side of the castings. 5. Solid beryllium is very weak at a temperature near the solidus line; brittleness is also a problem at lower temperatures. Thus, hot and cold cracking must be guarded against. Scope of the Experimental Work All of these problems have been given consideration in the work at Battelle. Before the work was started at Battelle, it was customary to melt beryllium in a vacuum furnace or under flux in graphite-lined induction furnaces. Because of the difficulty of preventing gas unsoundness in beryllium castings, an investigation was undertaken primarily to study this particular problem and, secondarily, to devise methods of overcoming the other difficulties encountered in the founding of beryllium. The objectives of the laboratory work were multifold: 1. To devise a practical method of melting, other than vacuum melting, by means of which consistently sound beryllium castings could be produced. 2. To obtain fundamental data which would promote a better understanding of the causes of gas unsoundness in beryllium. 3. To develop a casting technique which would permit low melt temperatures, minimize dross defects and hot cracking, and eliminate reaction with the mold surface. Up to the present time, a considerable amount of progress has been made on the first and third objectives, with the result that it can now be safely stated that consistently sound castings can be made by the open-pot melting method, using argon as a protective atmosphere and a proper casting technique. There has been some progress on the second objective of the project, but it cannot yet be safely stated that the problem is completely understood. Most of the experimental work has been conducted in an enclosed melting and pouring apparatus in which very-close control of melting variables has been effected. Findings based on the results of the work conducted in this small experimental apparatus have been applied to large-scale melts which have been made by techniques suitable for duplication on a commercial scale.

Jan 1, 1950

By E. T. Hayes, A. H. Roberson, M. H. Davies

R. F. Dornagala and D. J. McPherson (Armour Research Foundation, Chicago)—I should like to compliment the authors for a workmanlike job in determining the partial phase diagram of a system comprised of two rnetals which are certainly not easy to work with. We are completing work at Armour Research Foundation on an Atomic Energy Commission-sponsored project for the determination of eight zirconium binary diagrams. Work on the Zr-Cr system has been completed and should be published within the next year. For our work, Westinghouse Grade 3 iodide crystal bar served as the zirconium melting stock. Johnson-Matthey, electrolytic chromium, specially treated for oxygen removal, was employed. The overall constitution of the system determined at Armour Research Foundation is in very good agreement with the present work. We found a eutectic at 18 pct Cr and 1280 °C, somewhat lower than the value reported. This temperature was confirmed by thermal analysis, incipient melting studies, and regular isothermal anneals. The eutectoid was located close to 1 pct Cr and 835°C by metallographic analysis of annealed specimens. Maximum solubility of chromium in /S zirconium was 4.5 pct at the eutectic temperature. Chromium solubility in a zirconium was less than 0.28 pct at all temperatures. We found the compound at 53 pct to melt around 1700°C, with an open maximum, but determined its crystal structure to be hexagonal close-packed (MgZn, type). The lattice parameters were in excellent agreement with those determined by Wallbaum in 1942. The diagrams are in substantial agreement, and .part of the differences are undoubtedly due to the use of different zirconium melting stock. M. K. McQuillan (Birmingham, England)—I read this paper with a great deal of interest, as it covered the same field as some work of my own.' There are a number of points in the present paper on which I would like to comment. First, I should say that I, too, used zirconium prepared by magnesium reduction of the tetrachloride and electrolytically prepared chromium, and melted the alloys in a Kroll-type arc furnace. The purity of my alloys should, therefore, be comparable with the purity of those of the present authors, and any differences in our observations would not be expected to be attributable to this cause. The differences between my observations and theirs concern the presence of the eutectic, the temperature of the eutectoid, and the melting point of the compound. I would be very much interested in any further evidence the authors may have for the occurrence of the eutectic at 1380°C. During the course of my work I noted that a number of my alloys containing 60 to 90 pct Zr melted at about 1400 °C, and for a time assumed that a eutectic occurred at this temperature as described in the paper. On further investigation, however, I found that the structures of the as-melted alloys could not be made to fit in with this interpretation of the system. If a eutectic exists in this region of the system it would be expected that the as-melted alloys would show the usual type of cast structure, i.e., dendrites of the compound plus eutectic. This, however, does not occur, as may be seen from Fig. 9. The compound seen there is not dendritic in form, and the remaining material is by no means certainly eutectic. It may be argued that a compound such as ZrCrl would not form dendrites but would tend to crystallize in geometric shapes. In this case, however, I have evidence to the contrary, as on the chromium side of the compound, where a eutectic occurs at about 1545"C, the compound formed from the liquid takes on a conventional dendritic form, and the eutectic is observed in the interdendritic spaces in the usual way. There is no reason to suppose that the compound would behave differently in an alloy lying on the zirconium side of the compound composition if a eutectic existed there too.

Jan 1, 1953

By D. R. Hay, E. Scala

STUDIES of structure-sensitive properties, especially mechanical behavior, have shown that grain and subgrain structure play an important role. The mechanical properties of tungsten, in particular, are sensitive to the nature of the intergranular structure. Substructure and dislocation networks in single-crystal and polycrystalline tungsten have been studied by Nakayama et al.' Various orders of substructure were observed ranging from a microscopic first order (grain diameter: 2 to 8 mm) to a microscopic second order (grain diameter: 50 to 300 p), and, within the latter, dislocation networks forming an even smaller order of substructure. In their single crystals, grown by arc fusion, the degree of misorientation in each order was small: 16'3OU, -11, and -10" for the first-, second-, and third-order substructure, respectively. To study the properties of polycrystalline tungsten, powder metallurgy tungsten is generally used. However, in a mechanical property investigation, the zone-melted or arc-fusion crystals are more desirable than the powder metallurgy product due to their higher purity and absence of porosity and other defects inherent in consolidation by powder metallurgy. Grain boundaries can also be produced in melted stock by working and recrystallizing. However, material with subgrain mis orientations of the order of several degrees (high-angle substructure) has not been reported previously and is the subject of this communication. Crystals were grown by electron-beam, floating-zone melting. The starting material, Sylvania Pure-tung welding rod, was given one zone pass at a traversal rate of -2 mm per min. Through control of the zone temperature, it was possible to influence the degree of crystal perfection. By maintaining the zone at a high degree of superheat, high-perfection crystals could be grown. However, at temperatures only slightly above the melting point, the zone-melted crystals contained a high-angle substructure. A sensitive control of the zone temperature was not possible due to the difficulty of estimating the temperature of the zone and of providing a constant supply of power to the sample. Therefore, an empirical method, using the shape of the molten zone as a criterion, was adopted as an indication of temperature. At high degrees of superheat, the surface tension of the molten zone decreases and a neck forms at the top of the zone, whereas at low zone temperatures the diameter of the zone remains reasonably uniform. Although it was not possible to obtain a continuous variation of misfit angle, the conditions could be directed toward the growth of either high- or low-angle substructure by maintaining only a slight neck in the zone (sufficient to establish that it was molten) or a well-necked zone, respectively. Mass spectrographic analyses of both types of material revealed no significant differences in the concentrations of their impurities. The degree of misorientation at high angles was obtained by measuring the angular spread of spots corresponding to a single reflection on a Laue back-reflection photograph. Fig. 1 shows a typical Laue back-reflection photograph of a crystal with a 3-deg spread. By measuring the angular deviation of the spots corresponding to a single reflection from the mean center of the spots around which constant angular deviation contours were drawn, an average angular spread of misfit could be calculated. The angular average was weighted by the number of spots observed in each angular interval. At angles greater than 5 to 6 deg the spots from different reflections begin to overlap, and cannot be associated with a particular reflection. Laue back-reflection photographs taken at different locations on samples .with approximately 3-deg spreads showed only a small difference in angular misorientation, less than 8' of arc, within individual specimens. The microstructure was examined using Berg-Barrett X-ray extinction contrast microscopy. Berg-Barrett photographs taken directly on the as-grown surface, Fig. 2, show an essentially equiaxed subgrain structure of -0.1 mm in average grain diameter in both high- and low-angle crystals. Fig. 2(a) is a photograph of a sample with a low misfit angle and Fig.

Jan 1, 1968

By Joseph E. Worthington

The present-day Northumberland gold mine is one of the deposits generally characterized as a Carlin-type occurrence. It lies at the crest of the Toquima Range in Nye County near the center of Nevada. Gold mineralization occurs in two modes, in argillaceous and in silicified limestones, and is generally very fine-grained or micron gold. The Northumberland district has had a history that is typical of many western gold districts: minor production prior to World War II and intermittent exploration thereafter until a combination of geological insight, improved economics, and the advent of heap leach technology created the Northumberland gold mine. Nye County, Nevada, was sparsely populated and little explored in the early years of the settlement of the west; the Northumberland district was not established until 1866. Initial interest was in silver and the district operated as a very small producer for the next seventy years. The disseminated gold occurrences in silicified limestones were recognized and Northumberland Mining Co. was organized to develop the property in the late 1930s. Northumberland Mining Co. actually conducted drilling operations (over 200 drill holes) and mined from small open pits in the silicified limestones. They ultimately produced almost 936 kg (33,000 oz) gold before being shut down by War Production Board Order L-208 in 1942. After World War II gold mining activities were essentially nil for over a decade due to the poor economics of gold production. The property was, however, a known gold producer and attracted recurrent exploration attention. About 45 holes were drilled under the direction of Peter Joralemon for private interests between 1959 and 1963. Next Kerr McGee drilled about 25 holes during 1963 and 1964. Some- what later, in 1968, Homestake drilled 20 holes. The property was then acquired by Idaho Mining Co. which drilled about 30 more holes between 1972 and 1974. By this time the Northumberland mine was becoming somewhat shopworn with over 300 holes drilled. Interest in gold prospects was increasing substantially in Nevada, how- ever, due to rising gold prices in late 1974, and several companies were interested in continuing exploration at Northumberland. In 1975 Cyprus Mines Corp. was successful in obtaining a joint venture arrangement with Idaho Mining Co. for further exploration and development of the property. The overall Cyprus exploration program was under the direction of James G. Hansen, Vice President Exploration. The geologist recommending acquisition of Northumberland was Peter E. Chapman who reported to Joseph E. Worthington, Manager of U.S. Exploration for Cyprus. The basis for selection of the Northumberland mine as an exploration target for Cyprus by Chapman was essentially prior knowledge of regional and 16cal geology and of the mine. Exploration for the next few years was directed by Chapman under the supervision of Worthington. During 1975 and 1976 rotary and check core drilling were conducted that indicated that a substantial Carlin-type or disseminated, low-grade gold deposit occurred in two separate bodies. Drilling was based on geologic mapping and rock chip geochemical sampling. Both ore zones were reflected at the surface as gold and arsenic anomalies in rock chips. Heap leach tests attempted in 1977 were aborted by a flash flood, but were completed in 1978. Engineering studies occupied the next couple of years until the property achieved production in the fall of 1981. It is now producing by open-pit mining with gold recovery by heap leaching and cyanide extraction at a rated capacity of approximately 2722 t/d (3000 stpd) ore. Metal recovery has been projected (probably conservatively) at 5 10 kg/a (18,000 oz per year) gold and 1.6 Mg/a (59,000 oz per year) silver. Reserves are reported to be adequate for ten to fifteen years of production. REFERENCES Anon., 1981, "Gold in Nevada," Span Magazine, Vol. 21, No. 3, Standard Oil Co., pp. 6-9. Koschman, A.H. and Bergendahl, M.H., 1968, "Principal Gold- producing Districts of the United States, Professional Paper 610, US Geological Survey, p. 193. Kral, V.E., 195 1, "Minerals Resources of Nye County, Nevada, Bulletin, Vol. 45, No. 3, Geology and Mining Series 50, Nevada University.

Jan 1, 1985

By J. W. Leomrd, B. A. Donahue

Results of research are presented examining the extent to which the analytical characteristics of the relatively distinct coal bands from a variety of coal seams can be related to each other. This paper dis-cusses an approach for developing a practical coal petrographic quality control program based on conventional analyses, most of which is part of the standard A.S.T.M. procedure. The work is a final follow-up to Part I of this series which was prepared by the authors as an approach to applying conventional coal petrography to single coal seams. Recent published work by the authors entitled Petrography for Coal Mining and Coal Prepration: Part I dealt with interrelating various chemical and physical properties of coal1 measured using conventional analyses made on distinct petrographic bands taken from single coal seams. Since most coal production facilities process coal from a single coal seam or from very closely related coal seams in the same area,2 emphasis on interrelating the properties within a single seam appeared appropriate. The distinct petrographic bands were analyzed on the assumption that such differentiated data would be more representative of a heterogeneous coal seam than the single analytical value commonly used to characterize each property of an entire seam.34 Effort was directed at demonstrating the extent to which the interrelated chemical and physical properties 5,6 could be developed into nomographs or petrographic standardization graphs. Thus, one analysis, determined on a series of petrographic fractions separated from a single sample, was used to estimate numerous other properties in each fraction by referring to the previously established petrographic standardization graphs. This conventional approach to coal petrography was undertaken as a suggested feasible means by which a few coal analyses could be employed to develope a more penetrating knowledge of the properties of coal from any given seam in order to monitor more extensively its performance at the point of utilization. Such procedures can support development of the type of in- formation commonly sought through automated testing and through the use of computers.7 The broad knowledge which can be developed through these procedures is intended for application in the generation of an analytical profile or broad characterization of coal. These estimates were not intended as replacements for individual coal analytical tests. In this expanded second part of the research program, distinct petrographic bands from nine coal seams in the Central Appalachian Region were physically and chemically analyzed to elucidate the extent to which this concept of conventional petrography could be broadened for application to numerous coal seams. In presenting this second phase of work, the relationships developed are presented individually and not in a connecting series of nomographs or petrographic standardization graphs as in the previous work, thus leaving open the combinations of possibilities to individual interpretation and application. MATERIAL AND EXPERIMENTAL WORK Nine coal seams, representing a wide range of rank, from the Central Appalachian coal fields were used in this study. The distinct petrographic bands from the Kittanning, Pond Creek, Jawbone, Tiller, Poca-hontas No. 3, No. 2 Gas, Eagle, Winifrede, and Pittsburgh coal seams were separated by carefully removing a portion of each band at the face of the seam. The following were determined: ash, sulfur, free swelling index, heating value, bulk specific gravity, volatile matter, Hardgrove Grindability Index, and Gieseler Plastometer measurements. Determinations, where procedures were available, were carried out using ASTM standard procedures.8 Bulk specific gravity was determined using a kerosene volume displacement procedure modified from a method applied by Headlee and McClelland of the West Virginia Geological survey,9 Those bands with a bulk specific gravity greater than 1.60, which is generally above the practical specific gravity cleaning range of bituminous coals, were excluded and no analyses were performed. Much of the initial organization of this second phase of work was developed through the extensive use of a computerized statistical monitoring program (see Ref. 4). However, in order to achieve the closest possible interpretation of results, the final organization of data proceeded mainly from exhaustive trial

Jan 1, 1968

By Richard A. Queeney, Lance G. Peterson

ESTIMATES of the stacking fault free energy of copper reported in the literature show an extensive divergence of results. Based on measurements of dislocation node radii, Thornton et al.7 find the lower limit of stacking fault energy to be 60 ergs per sq cm: Jossang and coworkers4 estimate the same value should be less than 40 ergs per sq cm. Assuming stacking fault free energy to be twice the coherent twin boundary free energy, Valenzuela8 reports 72 ergs per cm, while Inman and Khan2 cite a value of 24 ergs per sq cm. which can no doubt be accounted for by almost complete absence of interstitials in solution. However, the minute concentration was sufficient to permit observable recovery of dislocation damping. Assuming a dislocation density of 1010 CM -2 and an average loop length of 0.5 , a concentration of interstitials as low as 0.01 at. ppm is sufficient to reduce dislocation damping by more than a factor of ten. The concentration of interstitial solute atoms in Ferrovac E-0.15 pct Ti was thus estimated at 0.01 at. ppm < (C + N) < 2 at. ppm. The absence at elevated temperature of strengthening due to interstitials, Fig. 1, was therefore anticipated in the titanium alloy. The temperature dependence of the flow stress below 300°K was unaffected by addition of either titanium&apos; or zirconium.&apos; Observed, however, was an initial difference in the absolute value of the flow stress below 320oK, Fig. 1. Grain size may account for the difference; the grain diameter of Ferrovac E was 30 to 45 µ and that of Ferrovac E-0.15 pct Ti 65 to 90 µ. Although second phase particles in the form of titanium carbides and nitrides precipitated in the Ferrovac E-0.15 pct Ti alloy, the spacing was too large to produce any strengthening effect. The mechanical properties measured, therefore, were inherent to the bcc lattice. 1W. C. Leslie and R. J. Sober: Trans. ASm, 1967, vol. 60, pp. 99-111. 2 H. Conrad: Journal of Metals, 1964, vol. 16, pp. 582-88. 3 A. S. Keh and W. C. Leslie: Materials Science Research. H. H. Stadelmaier and W.W.Austin, eds., vol. 1.pp. 208.50, Plenum Press, New York, 1963. 4A. S. Keh, Y. Nakada, and W. C. Leslie: Dislocation Dymmics, Rosenfield, Hahn, Bement, Jr., and Jaffe, eds., pp. 381-406, McCraw-Hill Book Co., New York, 1968. &apos;W. J. Bratina, J. T. McCrath, and H. E. Rosinger: Can. Met. Quart., in press. 6 W. J. Bratina, J. T. McGrath, and D. Mills: Suppl. Trans. Japan Inst. Metals. 1968, vol. 9, pp. 436-43. &apos;H. E. Rosinger and C. B. Craig: Can. Met. Quart., In press. %. Mills. J. T. McGrath. and W. J. Bratina: ScriptaMet,, 1968, vol. 2, pp. 311-13. The purpose of this note is to present the results of a direct measurement of the stacking fault free energy in copper. The present method avoids both the question of interaction forces of nodal dislocations and the assumption that the coherent twin boundary free energy is one-half that of a stacking fault. Fig. 1 shows a transmission electron micrograph of a stacking fault intersecting a high angle grain boundary in copper: Fig. 2 is a schematic representation of the intersecting interfaces. To produce the specimen, pure copper was rolled to 0.002 in. thickness and annealed for several hours at 875°C. These foils were strained in tension to l04 µ in. per in., and rean-nealed to 8 min. Recrystallization and/or grain growth were not observed during the second anneal, indicating that intersections such as Fig. 1 are equilibrium configurations. Many such stacking faults were observed, but few were noted as intersecting grain boundaries in well-illuminated areas. The intersection of Fig. 1 was well away from the specimen edge. Since similar defects have not been observed in fully recrystal-lized and annealed copper, it is felt that this defect is due to the tensile straining. Electron transmission

Jan 1, 1970

By P. E. Busby, C. Wells, M. E. Warga

Fundamental data on the rate of diffusion of boron in austenite and solubility of boron in the a and y phases of iron and steel have been obtained from deboronizing experiments and provide partial explanations for some of the phenomena observed in boron steels. The rate of diffusion of boron is about the same as carbon in austenite. The solubility of boron in austenite at normal heat-treating temperatures is less than 0.001 pct. A partial tentative Fe-B phase diagram in the important low boron concentration ranges and an equation representing the diffusion of boron in austenite are presented. A LTHOUGH a search of the literature revealed ALTHOUGHthat boron diffusion had not been studied quantitatively and systematically prior to 1948, a few qualitative observations which were made by following the diffusion of boron into iron packed in ferro-boron1-3 suggest that boron obeys normal diffusion laws and that the rate of diffusion increases with increasing temperature. The claim of Cornelius and Bollenrath1 that boron does not appear to influence the rate of carbon diffusion has recently been substantiated by Wells, Batz, and Mehl.4 Calculations based on data from the paper by Campbell and Fayv indicated that the diffusion coefficient (D) for boron in iron at 900°C is approximately 3x10 sq cm per sec; a value of 2x10-7 sq cm per sec at 1038°C has been reported by Digges et al in connection with decarburizing experiments on a commercial boron steel containing 0.43 pct C. During the period 1948 to 1950 several diffusivity constant (D) values for the diffusion of boron in the y phase of iron and steel and a number of solubility values for boron in both a and y phases were reported. It was concluded tentatively as a result of Metals Research Laboratory studies that D values for boron in y and a phases are about the same as for carbon in the comparable phasesa and that carbon up to 0.4 pct did not affect the rate of diffusion of boron in y iron above 1000°C within the limits of experimental error. Whether saturation of the y or a phases with carbon would significantly affect rates of diffusion of boron through them was then and still remains in doubt. The best estimate of Q (activation energy) was reported to be about 25,000 cal, somewhat lower than that for carbon in y iron. The solubility of boron in y iron at 1000°C was thought to be higher than 0.004 pct B but not as high as a more recent analysis of available data shows it to be. The solubility of boron in a iron at 700°C was reported to be 0.0004 pct B, but it would not have surprised the authors if the true solubility value is actually lower than this. Breaks in diffusion curves which were not understood when first obtained prior to 1950 have now been recognized as indicating solubility limits, and these are included in the present paper. Experimental Procedure Two methods were employed in an effort to determine diffusion coefficients (D) for boron in austenite. Early experiments involved the use of welded couples prepared in accordance with the procedure of Wells and Mehl,&apos; but when the results of these experiments proved to be unsatisfactory for calculating D values, studies were continued by means of deboronizing experiments. In both cases, boron analyses following the diffusion anneal were carried out spectrographically and all D values were computed using the Grube solution of Fick&apos;s law. The precision of the spectrographic method used proved to be about equal to that reported by Corliss and Scribner" —average deviation from the mean about 5 pct of the amount present when the boron content is 0.003 pct. Concentration-penetration curves obtained from spectrographic analyses of welded couples generally indicated that practically no boron was transported across the weld interface during the diffusion anneal. Furthermore the concentration-penetration

Jan 1, 1954

By E. S. Machlin

The wzodel of Blandin and Diplunt;, generalized to include a phase factor, is applied to the carbon-carbon interaction in iron. Darken&apos;s "energetic" model is generalized to include not only first neighbor interactions but further neighbor interactions as well. On the bases of these generalized models relations are derived for the activity of carbon in both austenite and ferrite in terms of the carbon-carbon Pair interaction energies. A single function then yields the pair interaction energies consistent with the experimental activities of carbon in both ferrite and austenite. Thus, a simple explanation is given for the observation that the nearest-neighbor interaction between carbon is repulsive in austenite and attractive in ferrite. Certain consequences of this approach are explored. OnE object of the present paper is to attempt to take into account the consequences of electrostatic contributions to the carbon-carbon pair interaction energy for carbon as a solute in iron. Friedel&apos; has shown that oscillations in electrostatic potential are to be expected about a solute atom in a metallic solution. Blandin and 6lant6&apos; have shown that such oscillations yield an interaction energy between pairs of solute atoms that obeys the relation: W{ = A cos(2ftFri + 4>)/(kFri)3 [l] where kF = Fermi wave vector, ri = distance between solute atoms comprising the pair7 <p = phase factor dependent only on electronic nature of solute and solvent, A = coefficient dependent only on electronic nature of solute and solvent. Machlin3 found that Eq. [I] accurately described the pair interaction energy derived from short-range order measurements based on field ion microscope observations of dilute alloys of platinum. He also found that the value of the phase factor $ derived from residual resistivity measurements agreed well with that obtained from the analysis of the short-range order data. Harrison and paskin4 were able to predict the long-range ordering energy of 0 brass using Relation [I] and residual resistivity values to predict the value of the phase factor $. Machlin5 has repeated their analysis and applied it to the prediction of the long-range ordering energy in AgZn and AgCd with excellent agreement between prediction and experiment. Both A and $ are independent of the crystal structure. The Fermi wave vector depends uniquely upon the conduction electron concentration per unit volume in the spherical approximation of the Fermi surface. Thus, Eq. [I] is expected to apply to both fer- rite and austenite with only one set of values of A and $. Mossbauer studies6 yield the result that iron has one 4s electron. We shall make an assumption found to hold previously for platinum3&apos;7 and nikel, which is that only the s electrons are involved in shielding the perturbing potential of carbon. With this assumption, kF = 1.35 A-l. Although A and $ may be obtained from certain mdels&apos;&apos;&apos; we shall take A and $ to be empirical constants in the spirit of Kohn and osko.&apos; Thus, Eq. [I] involves two adjustible parameters. Consequently, two independent relations in A and $I are required in order to evaluate them for carbon as a solute in iron. We may use a recent analysis of Aaronson, Domain, and poundg who showed that Darken&apos;s energetic model,1° as well as others, can be used to describe the activity-temperature data for carbon in iron in both the aus-tenitic and ferritic phases. Darken&apos;s model takes into account only first neighbor pair interactions. For our needs, all neighbor pairs need to be taken into account. It is convenient to generalize Darken&apos;s model. The result for the partition function for austenite is: over the temperature range 800" to 1200°C and where the uncertainty corresponds to one standard deviation. Eq. [4] effectively yields only one relation. Another relation is required to obtain unique values for A and $. One property of Eq. [4] is that it is independent of crystal structure. Hence, data for a iron can be used to obtain another relation. To arrive at this relation we must generalize Eqs. [2] and [3] so that they may be applied to the bcc a iron. The result is that:

Jan 1, 1969