By Huimin Lu, Neale R. Neelameggham, Guangzhi Wu

In China’s Inner Mongolia Tuquan County, 1.4 billion tons of reserves of serpentine deposits were found. Because serpentine belongs to magnesium silicate, there is no good reducing agent to reduce magnesium. In the local there is also a large reserves of high-aluminum bituminous coal for thermal power, power plants each year produce a large number of high-aluminum fly ash. The aluminum-silicon alloys obtained from this high-aluminum fly ash as the raw material by carbothermal reduction method can reduce the magnesium from the serpentine. In this paper, first, the feasibility of producing aluminum-silicon alloys by carbothermal reduction of high-alumina fly ash was studied, the hypereutectic aluminum-silicon alloys were obtained; and then the investigation on aluminum-silicon alloy as a reducing agent to reduce of metal magnesium from serpentine was carried out. According to the previous investigation, the optimized technical process for the extraction of metal magnesium from serpentine was proposed.

Mar 1, 2018

By Jian-guang Yang, Lei Jie, Si-yao Peng, Jian-ying Yang

A new membrane electrolysis process for bismuth recovery from bismuthinite concentrate was introduced. Under the conditions of temperature 70 degrees C, acidity 3 mol/L, solid liquid ratio 1:4 and 1.1 times stoichiometry sodium chlorate dosage for 1.5 h oxidation leaching, more than 98.5% bismuth can be leached from bismuthinite concentrate. The resultant leach solution was subjected to membrane electrolysis. Under the conditions of NaCl concentration 300 g/L and pH 7 in anolyte, bismuth ions concentration 80 g/L and HCl concentration 3 mol/L in catholyte, heteropole distance 6 cm, temperature 40 degrees C and current density 200 A/m2, a flat deposited bismuth plate can be obtained after 24 h electrolysis, and the bismuth purity was more than 99%. The current efficiency of cathode was 97.88%. Chemical component analysis results showed that the average convert efficiency of the sodium chlorate was 52.77% and the average oxidizing efficiency of chloride ion was 69.78%, and the resultant anolyte generated in anode compartment could be fully reused as oxidant for leaching bismuthinite concentrate again.

Mar 1, 2017

By Kazuya Koyama

We are studying the hydrometallurgical recycling process of indium from an Indium-Tin-Oxide(ITO) target. For this process, it is necessary to remove Sn(IV) ions from the aqueous hydrochloric acid solutions containing In(III). In this study, the removal of Sn(IV) ions by a potentiostatic electrolysis method was examined. The polarization measurements and potentiostatic electrolyses were carried out under a nitrogen atmosphere. In the Sn(IV) solution, current begins to rise at the cathode potential of -0.26 V vs. SHE, and increases with a reduction in the cathode potential. In the In(III) solution, current begins to rise at a cathode potential of -0.43 V vs. SHE. Metallic tin was electrodeposited without indium electrodeposition at the cathode potentials of -0.30 and -0.40V vs. SHE. More than 98% of the Sn(IV) was removed at the cathode potential of -0.40 V after the electrolysis for 3hrs. Both tin and indium were electrodeposited at the cathode potential of -0.50V vs. SHE.

Jan 1, 2006

By Wenjun Duan, Zongliang Zuo, Qingbo Yu, Qin Qin, Junxiang Liu

Moving bed has been widely used in the field of heat and mass transfer and reaction between solid particles and gas. In order to enhance the heat exchange coefficient, there will be tube banks inserted in the moving bed. In the process of drying ammoniates particles or heat recovery from high-temperature particles with moving bed, the particles flow behavior around the tube banks is significant. In this paper, the particles flow behavior around the tube banks is investigated, and all the results can provide guidance for the design and operation of a moving bed.

Jan 1, 2016

By J. N. Hartley

Samples of ash from the May 18, 1980, eruption of Mt. St. Helens Were collected from several locations in eastern Washington and Montana. The optical microscope and the combined scanning electron microscope with energy dispersive x-ray microprobe were used to determine the composition and mineralogical characteristics of the samples. In addition, a quantitative image analyzer was used to examine the particle size distribution, and x-ray diffraction was used to identify major minerals. Both polished sections and ultra thin sections (less than 5 ~m in thickness) were prepared to study the mineralogical characteristics. The use of ultra thin sections provided access to microstructural detail. Mineralogically, the samples ranged from almost totally glassy to almost totally crystalline. Crystal-line samples were dominated by plagioclase feldspar (andesine) and ortho-pyroxene (hypersthene) with smaller amounts of titaniferous magnetite and hornblende. Nearly all the samples contained from less than 1 to 3 wt% free crystalline silica (quartz, trydimite, or cristobalite).

Jan 1, 1981

By Motang Tang, Chaobo Tang, Shenghai Yang, Lulu Guo, Yun Li, Yongming Chen, Jing He

A new innovative process for one-step and cleaner extraction of lead from spent lead-acid battery by reductive sulfur-fixing smelting was presented. This paper summarized and discussed several potential sulfur-fixing agents and molten salts which can be used in this new technique. Thermodynamic analysis involving reaction mechanism, ΔGT and predominance-area diagrams of different smelting systems were performed, respectively. The results proved the technical feasibility and high-efficiency of this process. Copper oxide ash (CuO), zinc oxide ash (ZnO) and iron oxide bearing residues (FexOy) can be used as sulfur-fixing agent to extract lead through exchange reactions. Sulfur-fixed efficiency of CuO, ZnO and FeO decrease slightly in turn. Sulfur contained in PbSO4 is fixed in form of Cu2S, ZnS and FeS respectively which avoids SO2 emission. The addition of molten salt can significantly decrease temperature of reductive sulfur-fixing reactions. Molten salt can be regenerated and recycled in smelting system after filtering solid residues.

Mar 1, 2017

By Katsunori Yamaguchi

A new technique for the removal of tramp-elements from steel scrap has been required from the viewpoint of saving energy and protection of environment. In order to obtain fundamental information on the removal of copper, tin and zinc from molten iron, the extraction method by using of phase separation in the liquid Fe-Pb-C system was investigated at 1453K A mixture of iron, lead and carbon melted in a carbon crucible separates into two phases of lead and iron containing carbon. The compositions on the miscibility gap in' the Fe-Pb-C system are 95A%Fe-4.5%C-0.l %Pb and 99.9%Pb-0.1 %Fe. The distribution ratios of copper, tin and zinc between the lead and the iron phases, Lx=[masso/uX in molten Pb]/(masso/uX in molten Fe), are 2.2, 2.2 and lA, respectively. Seventy percent of copper and tin from iron scrap can be eliminated with comparable lead addition. Gold, silver and palladium are enriched in the lead rich phase, on the contrary platinum and rhodium are more distributed to the iron rich phase than to the lead phase.

Jan 1, 2003

By G. C. Yao

Iron and silicon impurities can form needle and branch shape intermetallie compounds in molten aluminum when there is no manganese. It is difficult to separate them from molten aluminum by electromagnetic separation. The Fe-Si-AI and Fe-AI intcrmetallic compounds were transformed into Mn-Fe-Si-AI and Mn-Fe-AI compounds by the addition of manganesc into molten aluminum, In molten aluminum the morphology of these intermetallic compound particles is lumpish and spherical. Migration resistance of these impurity particles is small, which is beneficial to separation. FeSiMnAl4 and FeMnAl6 arc paramagnetic. These impurity particles can be moved by magnetic force and can be separated from the molten aluminum.

Jan 1, 2003

By Yuzhe Zhang, Matthew Andriese, Jiann-Yang Hwang, Guanghui Li, Zhiwei Peng, Tao Jiang

The microwave power absorption characteristics of iron oxides, including Fe2O3, Fe3O4 and Fe0.925O, have been studied by determining dielectric loss and magnetic loss distributions in 0.05-m-thick oxide slabs irradiated with 1.2-kW, 2.45-GHz microwaves. The results reveal that the dielectric loss is the main factor contributing to microwave absorption in Fe2O3 and Fe0.925O, while the magnetic loss dominates the power absorption in Fe3O4 below its Curie point. Uneven power distributions are observed in the slabs and this phenomenon becomes even worse at high temperatures at which the permittivity increases significantly. Quantification of power absorption in the oxides is of great importance for efficient and uniform microwave heating

Jan 1, 2015

By D. M. Wyslouzil

The fundamentals of dissolving silver and silver minerals are discussed in the following sections: 1) Basic chemical reactions in the silver system 2) Leaching of pure silver minerals 3) Leaching of silver-bearing ores 4) Description of processes The basic chemical reactions of silver are an important guide to the mineral processor or the extractive metallurgist, particularly for systems in which complex formations are balanced against solubilities. The competition of other cations for free ligands can shift the equilibrium to the detriment of silver. Solubilities of pure silver minerals in specific solvents may not be a good indication of the solubility of silver minerals in ores. The abundance of silver minerals which usually appear in a typical ore precludes the selection of a single method that would result in the best extraction of silver from all minerals in the ore. Frequently, the recovery of silver from host minerals requires a destructive pretreatment such as intensive leaching, oxidation with or without elevated temperature and oxygen pressure, or roasting. The transformation of the host or the silver minerals does not always result in a leachable species? and this requires additional treatment before the precious metal can be recovered.

Jan 1, 1990

By H. Y. Sohn, Joshua E. Ramos, Moo Eob Choi

"A new technology for ironmaking based on direct gaseous reduction of iron ore concentrate is under development. This technology would drastically lower CO2 emission and reduce energy consumption by nearly 38% of the blast furnace requirements. Experiments were performed using iron oxide concentrate at 1150oC in a bench-scale facility, which was the highest temperature that could be reached in the facility. The reduction extent was determined at residence times of 3.5 - 5.5 seconds in which the reduction extent approached 43% with 0% excess H2 and 95% with 860% excess H2. Separate kinetics measurements showed that the rate is much faster at 1200 - 1400 oC. Experiments were also carried out using syngas (mixtures of H2 + CO). About 90% reduction in 3.5 seconds with 860% excess hydrogen contained in the syngas demonstrated sufficiently fast reduction for a suspension process and the feasibility of usingsyngas instead of pure hydrogen.IntroductionDespite the improvements in the modern blast furnace (BF) process, it suffers from many drawbacks. The process requires the feed in the form of sinters or pellets and high-grade coking coal. Thus, BF iron production is projected to decrease gradually [1]. The main factors for this are the environmental regulations [2] and the high capital investment cost.A large number of new ironmaking technologies have been developed or are under development [3]. Most of these processes, however, are not sufficiently intensive to replace the blast furnace because they cannot be operated at high temperatures due to the sticking and fusion of particles. Therefore, a new technology is under development for producing iron directly from fine concentrates by a gas-solid suspension technology, which would reduce energy consumption by about 38% of the amount required by the blast furnace and drastically lower environmental pollution, especially CO2 emission, from the steel industry."

Jan 1, 2009

By Masaru Imaizumi, Hiroyuki Nomura, Mitsuharu Takita

"Cast iron possesses many superior characteristics caused from precipitated graphite structure, for example, castability, wear resistance, solid lubrication, damping capacity. But the more graphite hyper-eutectic cast iron contains, the lower its mechanical strength becomes, because graphite gives a negative effect to strength of cast iron. In addition, primary graphite tends to segregate during solidification, so uniform materials are difficult to be produced.In this study, authors introduced semi-solid processing in developing new and high quality cast iron. A series of semi-solid processing experiments were carried out to clarify the effect of stirring condition; solidification temperature and etc. on microstructures and characteristics of cast iron. In particular much attention is paid to the appearance of ternary eutectic zone at the final stage of solidification. As the results advanced hyper-eutectic cast iron was obtained with high quality of both the mechanical strength and wear resistance. As for the mechanical strength, 300MPa and 0.60% are obtained as the tensile strength and the elongation values, respectively, under the controlled stirring condition. This indicates that semi-solid processed hyper-eutectic cast iron is used prospectively without spheroidization.IntroductionCast iron has various good properties such as wear resistance, solid lubrication, damping capacity and machinability. The characteristics of cast iron are mainly decided by graphite structure, namely graphite shape and its distribution in the matrix. Mechanical strength of cast iron is large in the case of small quantity of graphite particles which are precipitated uniformly, however, it becomes small in the case of large quantity of graphite precipitated flakily."

Jan 1, 2000

By P. A. Metz

The Fairbanks mining district has produced in excess of 7.5 million troy ounces of placer gold and 250,000 troy ounces of lode gold since gold was discovered in the area in 1902. The Fairbanks mining district is in the northwestern part of the Yukon-Tanana Upland Schist Terrane, an area of approximately 240,000 square km that has produced in excess of 21 million troy ounces of placer gold. All lode gold production from the terrane has been from the Fairbanks mining district, and all of this production has come from high-grade gold-quartz polymetallic sulfide veins. Gold grains in the vein systems range in size from several microns to several millimeters. The veins are localized in a complex metamorphic rock assemblage which includes greenstones and felsic metavolcanic and volcaniclastic rocks, meta-exhalatives and metasediments. Gold occurs in the metamorphic host rocks in association with arsenopyrite and arsenic-antimony sulfides which occur in lenses and disseminations within the host rock. Gold grains occurring in the metamorphic host rocks range. in size from sub-micron to a few microns in diameter.

Jan 1, 1987

By Yilin Fang, Alain Bonneville, Timothy. D. Scheibe, Zhijie Xu

"We present a hydro-mechanical model for geological sequestration of carbon dioxide. The model considers the poroelastic effects by taking into account the coupling between the geomechanical response and the fluid flow in greater detail. The simplified hydro-mechanical model includes the geomechanical part that relies on the linear elasticity, while the fluid flow is based on the Darcy's law. Two parts were coupled using the standard linear poroelasticity. Analytical solutions for pressure field were obtained for a typical geological sequestration scenario. The model predicts the temporal and spatial variation of pressure field and effects of permeability and elastic modulus of formation on the fluid pressure distribution.IntroductionIn order to achieve a substantial reduction of CO2 emissions and alleviate the atmospheric carbon problem, massive scale carbon sequestration is required involving millions of tons of carbon dioxide injection over several decades. The geomechanical response is important upon the injection of substantial supercritical carbon dioxide into deep geological formations. Supercritical CO2 is less dense than brine waters and the buoyancy driven flow of CO2 requires the aquifer to be capped by low permeability rock (""caprock"") to prevent the upward migration of C02 (as shown in Fig.1 ). Massive scale injection of C02 changes the overall stress state in the caprock and formation. This change leads to large deformation that can damage the caprock, create fractures, and open new flow paths for supercritical C02. Therefore, a coupled hydromechanical model becomes essential for the caprock integrity analysis."

Jan 1, 2012

By Peter Woodall, Paul Telford, Pengfu Tan

"Arsenic enters the Mount Isa copper circuit in the form of arsenic rich minerals in concentrates from both the Mount Isa and Ernest Henry copper mines. Arsenic is a volatile metal, and will partition in the copper smelter between smelter off gases, slag and anode. Most of the volatile arsenic will report to Isasmelt Electrostatic Precipitator (ESP) or Waste Heat Boiler dusts where it will form a re-circulating load within the smelter. ESP dust is produced at a rate of 15,000 - 20,000 t/y and is currently removed from the precipitator and leached in the new ESP Dust Recovery Plant to separate copper and arsenic from the ESP dust. This paper describes the laboratory test works of ESP dust leaching, neutralisation and cementation processes. The planttrial, commissioning and operation have been presented as well.1. IntroductionThe flue dusts generated in the process of copper smelting contain appreciable amounts of copper and other valuable metals including precious metals. These flue dusts also contain appreciable amounts of arsenic trioxide where arsenic occurs in the ore body. The copper smelters processing concentrates generate residuals, such as ESP dust, containing arsenic trioxide. ESP dust contains impurities such as arsenic and bismuth which are harmful to the copper refining process if they report to anode. These impurities are fumed off in the smelting process and report to the dust as arsenic and bismuth oxides.The content of arsenic in the feed of Mount Isa copper smelter is about 0.1 % to 0.4%. Arsenic is a volatile metal, and will partition in the copper smelter between off gases and anode. Most of the volatile arsenic reports to Electrostatic Precipitator (ESP) and Waste Heat Boiler dusts where it will form a re-circulating load within Mount Isa Copper Smelter. Unless arsenic is bled from the smelter circuit, it will build up to a point where both anode quality and smelter hygiene are adversely impacted."

Jan 1, 2011

By Luane Isquierdo Ferreira Holanda, Lucio Fabio Cassiano Nascimento, Luis Henrique Leme Louro, Sérgio Neves Monteiro, Alaelson Vieira Gomes, Édio Pereira Lima Júnior

In the present study,we used natural fibers malva (Urenalobata, Linn) in 0, 15 and 30 vol.% as reinforcement of epoxy matrix composites to ballistic application. Ballistic efficiency of these composites was assessed by measuring the energy absorbed and residual velocity after impact 9 mm FMJ ammunition projectile, aiming to compare with traditional materials, such as: aramid fabric Kevlar™ used in vests for personal protection. The results showed by visual analysis and scanning electron microscopy (SEM) that the main active failure mechanisms in composites were delamination layers and fiber rupture. In test groups can be seen that the absorbed energy and the residual velocity varies with the fiber percentage used. Compared to aramid there is both a gain in weight and cost of the ballistic armor, which makes the fiber malva a promising material applications involving personal protection against 9 mm caliber ammunition.

Mar 1, 2017

By Sharif Jahanshahi

Calcium ferrite slags are often associated with Professor Yazawa due to his pioneering work on the thermodynamics of this type of melts. Over the past years CSIRO has invested some effort in studying physico-chemical properties of such melts to fill in some gaps in our knowledge and explore opportunities for application of the understanding developed. These investigations cover thermodynamics, transport properties of calcium ferrite based slags, as well as the kinetics of reactions of such slags with refractories. The present paper provides an overview of some of these studies and highlights some of the interesting behavior of such melts. The oxidation state of copper and arsenic in calcium ferrite based slags are predominantly Cu+ and As3+, respectively, at oxygen potentials below 10.1 atm. The concentration ofCu2+ in such slags becomes significant at oxygen potentials of greater than 10'1 atm at 1300 ?C. The activities of CuOo.s and AsOl.S in calcium ferrite slags show strong deviations from the Raoultian Law, while that of CoO is very close to ideal behaviour with respect to pure solid CoO. Addition of Si02 to calcium ferrite slags can have significant effects on the activities of FeO and Fe2O3 and hence the stability of magnetite phase. Transfer of oxygen in calcium ferrite slags is fast with diffusivity of 2xlO?3 cm2/s at 1350 °C and activation energy of 16 kcal/mol Presence of solid phases, such as magnetite, has pronounced effect on the viscosity of calcium ferrite slags. The observed dependence on solid loading and shear rate indicates deviation from Newtonian behaviour. The interfacial tension between copper mattes and calcium ferrite slags is strongly dependent on the matte grade, with the determined values being much lower than the corresponding ones for interfacial tension between similar mattes and iron silicate slags. MgO, Cr2O3 and MgCr2O4 have low solubility in calcium ferrite slags and their solubility increases with increasing copper oxide content of the slag at 1300 °c. The oxidation state of the slag has strong effects on phase transformation, dissolution rate and disintegration of refractories in calcium ferrite slags. Other key factors with major impact on slag-refractory interactions include viscosity and surface tension of slags as well as the contact angle between slag and refractory material.

Jan 1, 2003

By Trevor Saldanha, Nawshad Haque, Will Sikora

This study reported life cycle assessment (LCA) of six copper mines in Australia, Papua New Guinea and Portugal. Inventory data was sourced from published papers, sustainability reports by mining companies, independent technical reports and previous CSIRO studies. Sima Pro software and various databases were used to evaluate life cycle based environmental impacts. The impact indicators were: global warming potential (GWP), acidification potential, water footprint, ecotoxicity potential, ozone depletion potential and human toxicity potential (carcinogenic and non-carcinogenic), abiotic resource depletion potential (minerals and fossil fuels), particulate matter and ionizing radiation. Generally, open pit mines were found to have a GWP of approximately 1.0 t CO2-eq/t Cu concentrate while underground mines had approximately 1.3 to 1.8 t CO2-eq/t Cu concentrate. Environmental impacts varied between mines considerably due to several factors, most notably: ore grade, mining method, flowsheets and ore mineralogy. Energy consumption and sources were significant contributors to most impact categories.

Mar 1, 2018

By Andrea Bernardes

Printed circuit boards (PCBs) of varying compositions have been converted by incineration and following melting into an environmental agreeable slag and a copper-nickel-tin alloy, containing the precious metals. The environmental compatibility of the slag was determined according to the German standard DIN 38414 - Part 4; pollutants' concentration in the lixiviates is smaller than the thresholds of drinking water (CE-Standards). Each experiment the charge were 500g scrap from PCBs and ca. 100g slag forming material. The products were a kind of mullite slag, poor on iron, which was recirculated, and an alloy containing up to 0.3% Gold. With a burner to the retort coal gas, the waste gas was burned without soot, and the produced mixed zinc-lead oxide containing silver was collected in the flue dust.

Jan 1, 1997

By Z. Jing, L. Qihou, C. Jun, L. Hui, Z. Yumeng

Three phases of Bi2O3 were first synthesized by extraction-stripping precipitation and post decomposition from BiCl3 leaching solution. The as-prepared Bi2O3 were characterized by X-ray powder diffraction (XRD), Fourier transform infrared spectra (FT-IR), scanning and transmission electron microscopy (SEM, TEM), UV-vis diffuse reflectance spectroscopy (UV-vis DRS), Brunauer-Emmett-Teller (BET) and X-ray photoelectron spectroscopy (XPS). The photocatalytic performances of the oxides were investigated by decomposing rhodamine B (RB) under visible irradiation. It shows that the Bi2O3 with different crystal structures and morphology were obtained under different decomposition temperature. The band gaps of as-prepared samples were 2.36, 2.41, and 2.78 eV for b-Bi2O3, a-Bi2O3, and d-Bi2O3, respectively, and the photocatalytic activities followed the order: b-Bi2O3 > a-Bi2O3 > d-Bi2O3, which was in good accordance with the photoluminescence spectra measurement results. The b-Bi2O3 exhibited the best photocatalytic performance which can effectively degrade 99.23% RB within 240 min.