By Fernanda Margarido

Recovery of metals contained in the electrode materials of batteries was studied considering an integrated recycling process constituted by physical and chemical operations. The physical treatment included the shredding of the spent batteries, followed by a wet sieving operation of the fragmented material. The physical behavior of Ni-Cd and Zn-Mn based (alkaline and saline) system batteries was studied and compared. In that sense, shredding operation was performed and the sieving of shredded fractions was accomplished to evaluate the efficiency of the separation of electrodes and scrap. For Ni-Cd batteries the loss of electrode material with the supra fraction (scrap) after the shredding operation was lesser than the Zn-Mn batteries. Especially for saline-type batteries, the electrode attached to the scrap was substantial leading to important losses. This difference can be explained by the composition of the case materials and the internal physical constitution of the electrodes. The wet sieving studies carried out allowed optimizing the separation of the electrode fine fractions from the scrap materials through the analysis of selectivity Cd/Fe or Zn/Fe. For Ni-Cd batteries, maximum selectivity was achieved for the granulometry of 1.4 mm, while for alkaline and saline systems best selectivity were obtained at 2.8 mm and 5.6 mm, respectively. This process allowed the recovery of about 70% of electrodes for Ni-Cd and alkaline systems, and 50% for saline batteries, with less than 5% of scrap as contaminant. This physical step can be considered as a pre-treatment of this type of waste material envisaging its valorization by chemical treatment, as improves the concentration of the elements of interest and decreases the iron content.

Jan 1, 2006

By T. T. Chen

Gold in the Twin Creeks ore is primarily associated with arsenian pyrite. During pressure oxidation, the sulphides are solubilized, but part of the dissolved iron reprecipitates as jarosite and as an iron sulphate-arsenate-phosphate phase. The pressure oxidation products are subjected to cyanide leaching. The cyanide leach residues consist of quartz, gypsum, bassanite, anhydrite, small amounts of jarosite, an iron-sulphate-arsenate-phosphate phase, as well as trace amounts of orthoclase, rutile, pyrite, hematite and monazite; all these particles are dispersed in a fine grained matrix of illite-muscovite. The autoclave leach residues contain a small amount of carbonaceous matter. Many gold grains are detected on the surfaces of the carbon particles, and these gold particles are not leached during cyanidation. The gold particles are typically 0.1-0.2/Lm in size and commonly are embedded in the carbon surface or are coated with a K-AI-Si-S-O phase on the surface of the carbon. The gold grains are consistently associated with elevated CI contents (50-300 ppm Cl). The poor gold cyanide leach recoveries, which initially occurred in the Twin Creek developmental circuit under certain operating conditions, are attributed to the presence of chloride in the feed. This results in the formation of soluble gold chlorocomplexes in the autolcave and the subsequent sequestering of the gold on the surfaces of the carbon particles.

Jan 1, 2000

By Bora Derin

The synthesis of titanium diboride (TiB2) by carbothermal reductions of TiO2 and B2O3 was investigated. For this aim, TiO2, B2O3 and carbon black powders were dried, weighed out and mixed in stoichiometric molar proportions (TiO2:B2O3:C = 1:1:5). The experiments were carried out in a graphite resistance furnace in argon media using different range of temperature (1400- 1700 °C) and time (0 and 15 min). The phase analyses observation of the products were examined by using XRD.

Jan 1, 2008

By Hua-qing Li

Electromagnetic stirring process effectively improves the casting quality of metals. In this paper, the physical simulation experiment, in which the molten copper is displaced by mercury, was designed. The factory test parameters were determined according the simulated data. The flow behavior of the mercury to be stirred as well as the relations between the microstructure of plate blanks and the current parameters were analyzed. With an appropriate electromagnetic stirring, the inverse segregation of tin for C51900 alloy plant blank reduces from 15 % ~ 30 % to about 5 %, and the proportion of equiaxed grain rises to larger than 30%.

Jan 1, 2009

By Takaaki Ishikawa

The distribution equilibria of lead, zinc and copper between CaO-Si02-Ah03 melts and liquid copper were measured at 1623K under a controlled H2-C02 atmosphere. The distribution ratios were plotted against the oxygen partial pressure, and reasonable oxide forms dissolved in the melts were estimated from the slopes of the plots. The activity coefficients of zinc oxide (ZnO), lead oxide (PbO) and cuprous oxide (CuO0.5) increased with increasing slag basicity, defined by XCao/Xsio2 The temperature dependence of the activity coefficients was also measured.

Jan 1, 2003

By R. W. McCallum, B. Jensen, K. W. Dennis

"There are substantial challenges in the exploration of magnetic materials in the R-TM-X system (R =rare earth, TM= transition metal, X =stabilizing element) where Xis an element which has high vapor pressure, high reactivity, toxicity, or a refractory nature. This research focuses on discovering new phases with high anisotropy and high magnetization through closed diffusion couples inside high purity Fe crucibles. Either vapor-solid reactions or powder metallurgy techniques are then employed to isolate a stoichiometric sample based on a potentially magnetic phase found in the diffusion couple. For this research, X = F, Ca, Sr, Se, Zn, Bi or Cd, TM= Fe, and R = Nd. New ternary phases have been discovered with WDS and EDS, and magnetic transition temperatures have been measured with a SQUID magnetometer and VSM.IntroductionSince the discovery of the RCo5 compounds in the 1960s, rare earth- transition metal (R-TM) magnets have been the main focus of permanent magnetic research over the last five decades. Iron-based magnetic materials were studied next in attempts to avoid the unstable price of cobalt as well as the high price of Sm, the top performer in the RCos and RzC011 series. This hunt eventually led to the discovery of Nd2Fe14B with a theoretical BHmax of 64 MGOe, nearly double that of the previous samarium based magnets. The next few decades were devoted to enhancing the magnetic properties ofNd2Fe14B by the improvement of processing techniques and the additions of alloying elements. The only complete elemental substitution discovered in this system was R1Fe14C, which did not improve magnetic properties. It is probably safe to say that most ternary R-TM-X systems, where Xis any element that may stabilize a ternary phase, have been investigated if they may be prepared by conventional processes such as arc or induction melting. The present study offers a systematic approach to developing a novel diffusion couple technique in which the volatile, reactive or toxic alloying elements are laser welded inside a high purity Fe crucible. This experimental setup will prevent the oxidation of the rare earth element, as well as contain the volatile X element. As the goal of the research was to find new rare earth permanent magnets, only phases which contained greater than 60 wt% Fe were investigated. 247"

Jan 1, 2012

By R. P. Tavares, M. Isac, R. I. L. Guthrie

"The configuration of the metal delivery system used in twin-roll casting can play a significant role in determining both internal and surface quality of the strips produced by this process.In the present work, a mathematical model for coupled turbulent fluid flow, heat transfer and solidification was developed and used in the study of metal delivery systems for twin-roll casting of low-carbon steels. This study was applied to a pilot twin-roll caster being investigated in Canada, with a roll radius of 0.3 m, producing strips of thicknesses from 4 to 7 mm, at roll speeds ranging between 4 and 12 m/min. Various configurations of metal delivery systems were simulated and their effects on the advance of the interdendritic solidification front and levels of turbulence and temperature within the caster investigated. According to the predictions of the model, an extended nozzle with inlet flow towards the surface of the rolls seems to be the best alternative for feeding liquid steel into twin-roll casters.A full scale water model of a pilot twin-roll caster was also built and used to qualitatively validate the predictions of the mathematical model.Various techniques for fluid flowvisualization were applied. In general, the predictions of the mathematical model were in reasonable agreement with the experiments with the water model."

Jan 1, 1999

By Michael L. Sorokin

The behaviour of cobalt during processing of nickel raw material is analysed within the Ni-Co-Fe-S-O-SiO2 system using the computer model. For this purpose the thermodynamic parameters for "three-suffix" Margules's equations in Co-Fe-S and Co-Fe¬Ni-O-S1O2 systems were computed! Phase and iso-activity diagrams for Co-Fe-S system, and phase diagrams for the systems Co-O, Co-Fe-O, Co-Ni-O, C-oO=SiO2 and Co-Fe-O¬SiO2 are calculated using the developed computer programs and identified parameters. The diagrams are used to analyze cobalt behaviour at smelting and converting.

Jan 1, 1995

By I. S. Blair

The introduction of the 36 MVA smelting furnace at Mufulira, and the experience gained during the first five years of operation have been described previously (6). Based on this experience the furnace was rebuilt in 1977., Details of the modifications made during this rebuild are described. Subsequent to the rebuild, refractory failures, particularly in the electrode ring bricks of the sprung arch roof, continued to cause concern, and repair and improved roof control methods are described. Electrode breakages continued, but developments in casing design and electrode preparation have resulted in significant improvements. Modifications in the electric furnace gas handling system are outlined, together with details of further changes to be implemented in the near future. The systems developed for metallurgical control of the furnace and the thermo-dynamics of the process are discussed. The electric furnace at Mufulira is now operating at above design production levels, and has decisively justified the choice of this technology in situations with inexpensive electric power. The potential for further increases in production capacity from the Mufulira unit, and improvements in design for new units are discussed.

Jan 1, 1983

By Yi Tan, Kazuki Morita, Yaqiong Li

Molten Si-Al alloy, with the addition of Sn, was used for metallurgical grade Si purification by a low-temperature solidification method, with the aim of improving the recovery rate of Si. In this ternary melt, bulk Si was grown with a planar front by a directional solidification process under a well-controlled thermal gradient and growth rate conditions, thereby reducing the contamination of solvent metals. Effects of cooling rate, amount of Sn addition, and temperature gradient on the quality of bulk Si were determined. The criterion for constitutional supercooling for single-phase growth from multicomponent melts was employed to evaluate the growth process.

Jan 1, 2015

By SenYang Qian, ShuangYu Du, Bo Wang, Jieyu Zhang, Jian Zhao

During the solidification process, the flow pattern of the molten steel has significant influence on the formation of solidification microstructure. In present study, the solidification microstructure of 30Cr2Ni4MoV steel ingot under different intensities of mechanical oscillation(forced convection) was simulated by using ProCAST®software. The results showed that the increase of the intensity of oscillation could restrain the development of the columnar grains and refine the grains. As the intensity of oscillation increased, the proportion of columnar grains decreased and the proportion of equiaxed grains increased. When the intensity of oscillation was at a low level, the effect of refining grains could be improved obviously by increasing the intensity. However, as the intensity increased to over 0.833, the effect of refining grains would not be improved.

Jan 1, 2016

By Abbas H. Mirza

Arsenic and selenium are found in low quantities together with other metals in several nonferrous metallurgical process streams such as scrubber blowdown solution, acid plant wastewater, gas cleaning plant water, etc. Normally, the other metals in these streams are present as cations and can be precipitated by conventional lime treatment and sulfide polishing. However, arsenic and selenium are invariably present as anions, AsO33-and AsO43 in the case of arsenic and SeO32 and SeO42 for selenium. Conventional lime treatment removes most of the arsenic, but it does not remove selenium. The present paper reviews the processes and technologies developed to date on the removal of arsenic and selenium from metallurgical process streams.

Jan 1, 1996

By Xie Hao

According to its raw materials orthogonal test scheme is designed and a large number of systemic experiments were carried out in order to study the sintering characteristics of three types of fine ores in Kunming Iron&Steel Co.Ltd(KISC). The effects of carbon mixture ratio and basicity on sintering time, agglomeration ratio, physical properties and utilize coefficient were researched via single factor analysis and range analysis. The experimental results show the best mixture ratio of each fine ore. Analysis found that the influence of the carbon mixture ratio is more significant than which of the basicity on the sintering process except agglomeration ratio of foreign ore.

Jan 1, 2009

By William Petruk

The Kidd Creek base metal deposit near Timmins, Ontario contains around 0.15 wt% Sn, mainly as cassiterite. The cassiterite occurs largely as inclusions in sphalerite, with 85% being in grains smaller than 18.5 micrometres in diameter. Concentrates and tails from the company's Cu, Pb and Zn circuits were studied to determine the liberations and recoveries of cassiterite in the products. The ore had been ground to about 65.% minus 44 micranetres in diameter (-325 mesh); 55% of the cassiterite was liberated. About 92% of the liberated cassiterite and 70% of the unliberated cassiterite were in the concentrator tails, and 20% of the unliberated cassiterite in the zinc concentrate. The company had attempted to recover the cassiterite from the concentrator tails by gravitational methods but recoveries were low. The grain size of the cassiterite in the gravity Sn concentrate was similar to the grain size of the liberated cassiterite in the concentrator tails. Research on flotation of the fine grained cassiterite from Kidd Creek ore has been conducted,

Jan 1, 1990

By Bing Li, Miao Shen, Qiang Wang, Yuqi Chen

Electrochemical methods including cyclic voltammograms, square wave voltammograms, chronopotentiometry are applied to characterize the reduction potentials of Na+ and Li+ ions in LiCl-KCl melts. According to theoretical calculation, the reduction potential for Na+ is slightly more negative than Li+ in NaCl-LiCl-KCl melts at 450℃. However, by electrochemical measurements, the reduction potential of Na+ is slightly more positive than Li+ in the above melt and the potential difference between Na+ and Li+ reaches 0.16-0.2V on an inert W electrode in 1.0-2.0 wt% NaCl-LiCl-KCl melts. An active Pb electrode is used to improve the removal rate of Na+ from LiCl-KCl melts. The reduction potentials for both Na+ ions and Li+ ions on a Pb electrode shift to more positive values and the reduction currents become larger. After 6h electrolysis on a Pb electrode at -3.0V, the practical removal efficiency of Na+ ions reaches 90.12% and the reduced products contain metallic Na and Li with a Na/Li mass ratio of 4.25/1.

Jan 1, 2015

By Daguang Lu

The section of sintering and BF (blast furnace) is very important in iron-making process. In practice, the scheduling is so extensive that three faults unfavorable to continuous product will be easier to happen. This paper introduces the integration Petri Net and GA (genetic algorithm) as suitable tools for simulation and optimization of scheduling to section of sintering- BF under a certain hot iron or-der. The situation of the iron plant Chongqing Iron and Steel Company is researched in approach above mentioned. By analysis, the conclusion is drawn that scheduling with optimized values can maintain continuity of key operations , can satisfy order of hot iron in maximal degree and can keep the best stability of key storages.

Jan 1, 2009

By Jorge Alberto Soares Tenório

Household zinc based batteries contain some heavy metals such as zinc, manganese and mercury. There is a large effort from manufacturers in order to eliminate the last one. As a municipal waste, the disposal of batteries has become an increasing worry. The aim of the present work was to characterize dry batteries scraps, and establish a flowsheet for their processing. This was done using unit operations of mineral processing and parameters and yields of each stage have been defined. Such procedures have been chosen due to their low cost. The operations were hammer mill grinding, size separation, magnetic separation and specific weight separation in water. The characterization step was done through chemical analysis and x-ray difiactometry. After size classification, it was verified that 76.6% of the total amount of zinc was over 1.70mm. This fiaction was constituted basically of zinc and some coarse pieces from the steel body, paper and plastics. This fraction was submitted to magnetic separation followed by specific weight separation in water. A visual examination showed that during the grinding process, graphite was concentrated in the finer fractions. Manganese concentration in the fractions over 6,35mm was less than 2%. This means that there was low contamination by the paste in this fraction. It was due to the entrapment of the paste by steel scraps (from the body) and zinc (from the cup) during grinding.

Jan 1, 1999

By Milton Manrique

The thermal decomposition of zircon concentrates in a non-transferred arc thermal plasma flow reactor was investigated. The plasma torch was operated using argon-helium and argon-nitrogen mixtures as plasma gases. The effect of power, feed rate and zircon particle size was studied. Products were characterized by XRD, SEM, TEM and chemical analytical techniques. The average size of the product was in the submicron range. Free energy minimization plots were used to predict the behavior of the system under different operating conditions. A kinetic model to describe the different stages of the thermal decomposition process is proposed. The results of this investigation showed a significant segregation process where the zirconia-rich product is collected in the reactor while the silica-rich product is collected in the filter. TEM analysis indicated that silica vapor is condensed on the surface of the zirconia particles.

Jan 1, 1996

By Xiaobing Yang, Animesh Jha, Greg Doughty

"Successful use of inert anodes should reduce the CO2 footprint in aluminum production. The search for a “holy grail” inert anode for metal electro-winning from constituent oxides using molten salt bath as an electrolytic medium is continuing. In this article we demonstrate the engineering approaches for the fabrication of intermetallic anodes, based on a quaternary Al-Ti-Cu-M (M:Ni, Fe) system for primary aluminium production. In particular, we examine the microstructural and electrochemical properties of alloys, based on the quaternary compositions. We explain the aspects of phase stability under anodic potential, which leads to the loss of anodic materials in the temperature range of 850-1050oC. The results are analysed in the context of oxidation reaction and formation of oxide layers which readily dissolve in the cryolite melt and prevent passivation. The paper also describes the conditions under which the reduction of aluminium at the graphite cathode occurs which also strongly depends on the molten salt chemistry for the nucleation of molten aluminium at the cathode.1. IntroductionOxygen-evolving inert anodes are an alternative to the conventional consumable carbon anodes for the production of primary aluminium. In this paper the materials selection criteria chosen for the engineering of anode is based on the understanding of the thermodynamic stabilities of aluminide intermetallic phases, some of which are formed and remained stable in fluoride melts. For example, the formation Al3Ti dispersed in aluminium metal via molten-fluoride flux reaction is well known in the context of aluminium casting and grain refining [1-3]. It is for this reason in our research we concentrated on the engineering of stable intermetallic phase mixture in the Al-Ti-Cu ternary system, shown in Figure 1 [4]. In this figure two compositions in the Al3-0.5zTi1-0.5zCuz family are shown with the substitution of 7 atomic % and 11 atomic % copper. However initial investigations showed that these two compositions were unsuitable due to the formation of low-temperature liquid (~540oC) and intermetallic phase, Al2Cu along the Al-Cu binary edge during solidification. The Al2Cu phase segregated along the boundaries of Al3Ti and Al5Ti2Cu, and dissolved away when electrolysis was carried out using these anodes above 800oC. The presence of consequential porosity in the anode material increased the corrosion of the alloy through local heating due to high current density at 0.8 A cm-2. The early tests were carried out with cryolite melts, shown in Figure 2, having 3 weight percent of Al2O3 in the bath at 850oC."

Jan 1, 2010

By Suleyman Tekeli, Serdar Salman, Bulent Aktas

"The effect of La2O3 content up to 15 wt% on phase stability, sintering and microstructure of cubic zirconia (8YSZ) was investigated. XRD results showed that the specimens containing up to 15 wt% La2O3 were composed of only cubic structure. Also, the specimens doped up to 5 wt% La2O3 revealed no La2O3 peaks, indicating that La2O3 was completely solubilized in the cubic structure. However, when> 5 wt% La2O3 was added, the peak of La2Zr2O7 compound emerged, showing that the overdoped La2O3 was not solubilized in the 8YSZ matrix. The lattice parameter of the 8YSZ slightly decreased with the increasing La2O3 content up to 1 wt% but further increase in the La203 amount resulted in an increased lattice parameter. The comparison of grain size of the 8YSZ specimens with various La2O3 content showed that grain size slightly increased with the increasing La2O3 content up to 1 wt% but further increase in the La2O3 amount resulted in a decreased grain size.IntroductionAt atmospheric pressures, three polymorphic forms of Zr02 are stable at different temperatures i.e. monoclinic, tetragonal and cubic. A high-pressure orthorhombic form of Zr02 has also been reported[l]. The successful production of pure Zr02 bodies is not possible all the time due to the large volume expansion associated with the martensitic tetragonal-monoclinic transformation. This fact restricts the applications of zirconia, in spite of its excellent mechanical and thermal properties. However, the stabilization of the high temperature polymorphs at room temperature as stable phases is made possible by addition of suitable dopants. Fully stabilized cubic Zr02 and partially stabilized tetragonal Zr02 show interesting properties and are widely used as ionic conductors, coatings and gas sensors in solid oxide fuel cells and structural applications[2]. Most frequently used dopants include Y203, CaO, MgO and Ce02, although other oxides, such as those of rare earth elements, can also act as stabilizers of the high temperature structures. The incorporation of aliovalent cations to the lattice, forming substitutional solid solutions, allows to control the concentration of anionic vacancies in the structure. This aspect is particularly important in designing ionic conductors[3], and is also determinant in the stabilization process[ 4]. The process of stabilization with larger ionic radii dopants is rationalized by the crystal chemistry model[ 5], that describes the dopant cations as typical stabilizer when they have larger ionic size, lower charged state and higher ionicity than Zr4+ The ionic radius of Zr4+ is 0.84 Å and that for La3+ is 1.016 Å [6]."

Jan 1, 2012