By Chengyi Ding, Xuewei Lv, Changyang Ji, Rende Zhang, Xiangwei Zheng

The fraction of liquid phase in sintered ore can be the most important factor to determine the sinter quality and yield in sintering process. The generation ability of liquid phase for mixture of iron ore powders is determined by basicity, roasting time, roasting temperature and chemical composition of iron ores. Five different iron ores were selected in this study and the dried powders of iron ore and CaO reagent (<200 mesh) were homogeneously mixed together at their required proportions, then 15g of the mixture was pressed under a pressure of 20MPa to make a cylindrical sample with a diameter of 20mm. The sintering temperature in this study was kept at 1280℃, the gas phase is air, the holding time was varied with its three levels of 5min,10min and 15min. After that, the sample was cooled under room temperature in the air, and the cooled sample was analyzed by using zeiss optical microscope. The mineral phase compositions were quantitatively determined with an open source image processing software, Image J whicn can calculate the fraction of liquid phase. Besides, the study on how to estimate the sintering behavior of the raw materials in different conditions by the theoretical calculation is of vital importance, and the development of this will greatly improve the sintering production. Factsage will be used to calculate the liquid phases formulation during the sintering. Comparing the experimental results and the theoretical calculation shows that the mass of liquid phase increases with increasing basicity during the sintering, besides, the mass of calcium ferrite increases with increasing basicity. The generation ability of liquid phase of iron ores can be predicted through the experiment verification.

Jan 1, 2015

By Norimasa Yamasaki, Masao Kurosaki

"The effects of plating conditions on the crystal orientation of electrodeposited zinc were investigated by varying elecyrolyte flow rate and current density. Precipitation of the Zn (00 • 2) basal plane is promoted at lower current density and higher flow velocity. Effect of the flow velocity on the mass transport was evaluated based on the polarization measurement in which Cu was used as the tracer. As a result, it has been clarified that the crystal orientation of electrodeposited zinc can be uniquely arranged by the overvoltage (iU0.5) that can be simply calculated by considering -the current density and boundary layer thickness. At the same time, the electrode potential during electrodeposition that can be calculated by using a model based on the competitive reactions of hydrogen reduction 'and zinc reduction exhibits an extremely good correlation with the crystal orientation of electrodeposited zinc.Introduction Electrogalvanized steel sheet has better surface properties than hot-dip galvanized steel sheet, and is used in home electric appliance and automobile applications. Factors such as crystal morphology, crystal orientation and surface roughness have a large influence on its appliance, formability and corrosion resistance [1-3].Electrolysis, condition, bath composition and alloying elements are reported as factors that affect the crystal orientation of the electrogalvanized coating. Factors that can be controlled on time in the production site are electrolysis condition that-is current density and plating solution flow velocity.Some studies[4-6] report that the crystal- orientation of the Zn(00 • 2) plane is increased by promoting, the mass transfer of zinc ions in the plating solution or decreasing the concentration overvoltage, but did not investigate in detail the plating solution flow conditions in the plating cell nor quantitatively determine the effects of both current density and plating solution flow conditions on the crystal orientation of ' electrodeposited zinc."

Jan 1, 2000

By Guan-zhou Qiu, Shui-shi Liu, Yu-feng Guo, Tao Jiang

"The preparation of high-quality synthetic ruitle from electric furnace titanium slag was systematically investigated by activation roasting followed by acid leaching process. The results showed that impurities such as Ca and Mg in titanium slag can be effectively removed and TiO2 grade of the product was markedly improved by the process. High-quality synthetic rutile containing 88.54% TiO2, 0.42% (CaO+MgO) was obtained under the conditions that roasted with 7.5%(wt) H3PO4 at 1000 oC for 2h, followed by two-stage leaching in boiling dilute sulfuric acid for 2h. Mechanism studies showed that anosovite solid solution and silicate minerals were reacted with phosphoric acid in the roasting process. As a result, titanium components in titanium slag turned into rutile (TiO2) and impurities were transformed into acid-soluble phosphate and quartz.IntroductionWith the gradual depletion of natural rutile and the rapid development of titanium industry in China, the natural rutile reserves cannot satisfy the requirement for production of titanium pigment and titanium sponge. Ilmenite is, therefore, becoming main raw material for titanium industry. However, because of its low TiO2 grade, it generally requires preconcentration to titanium-rich material such as titanium slag or synthetic rutile [1-3].Ilmenite resources are extremely rich in Pan-xi area of China, which account for 90.54% of total ilmenite reserves in China [4]. The titanium slag produced by electric smelting of ilmenite concentrate has high contents of Ca and Mg, and is not suitable as a raw material for chloride process and titanium sponge production. Therefore, upgrading titanium slag to prepare raw material suitable for chloride process and titanium sponge production has important significance for the development of China's titanium industry."

Jan 1, 2011

By K. C. Mills, P. N. Quested, A. P. Day, R. F. Brooks

"Methods have been developed to measure the physical properties of molten materials relevant to the fluid flow in high temperature processes. Data for the densities, viscosities and surface tensions of Al-, Ni- and Fe-based alloys are compared with (i) values for the pure metals and (ii) estimated values obtained from models making use of chemical composition of the alloy. Experimental values for metallurgical slags are also given and compared with estimated values.1 IntroductionPhysical property data has proved very useful in improving process control and product quality. For instance, in the continuous casting of steel the viscosity (TJ) of the mould flux is important since it determines (i) the optimum casting conditions, nVc = 2.5±1 dPas (m min-1) where V c is the casting speed and (ii) the level of slag entrapment (which leads to inclusions) in the metal. Thus data for properties like viscosity are exceedingly useful in understanding the process and the problems encountered and the causes of defects and problems.Another interesting development which has helped to increase our knowledge of processes and improve process control and product quality is the development of mathematical models of the fluid and heat flow in the process. These models have been developed to the stage where one of the prime requirements is for good physical property data for the industrial materials involved. Recently, Oxley [1] has shown that the use of reliable, experimental, property values for the commercial alloy in a commercial software package produced a significant improvement in the prediction of casting defects. Thus reliable property data are required for liquid metals but also for (i) liquid slags since many processes involve the use of a slag to refine and protect the metal or to lubricate the mould and (ii) refractories, sand and investment moulds."

Jan 1, 1999

By P. Henry

A novel electrochemical cell has been developed for the recovery of MnO2 from residue of pyrolusite ore leading loaded with Fe, Al Ni, Co and Si impurities, This new process can be considered as an alternative to the traditional methods : S02, H2O2 or bioleaching. It has been observed to proceed fairly rapidly and could prove to be a more economically viable process, as well as being more environmentally acceptable. Electrochemical characterization and kinetic studies have shown that MnO2 is effectively leached by electrogenerated ferrous ions at high current density from a pulp containing less than 5 g8 Fe. The chemical reactions are : Cathode (inox) : 2F23+ + 2e ? 2 Fe2+ Bulk: MnO2 + 2 fe2+ 4H+ ? Mn2+ + 2 Fe3+ + 2 H2O Anode (Pb-Ag) : H2O ? ½ O2 + 2H+ + 2e Global: MnO2 +2H+ Fe2+ = Mn2+ + H2O + 1/2 O2 The catholyte (MnO2 pulp) circulates upward in the expanded mesh cathode separated from the sulfuric acid solution anolyte by a separator which shows high mechanical resistance, low porosity, low potential drop, and reasonable cost. Laboratory and mini-pilot tests have led to the construction of an OT crating pilot plant (100 kg/hr) able to leach more than 95% of Mn, Ni, Co at 1000-1200 A/m2, 50°C with high faradic yield (> 95 %) and low power consumption (3.2 kWh/kg kWh/kg &4D). New applications like the treatment of spent Zn-Mn batteries, polluted soils, spent catalysts and oxide ore (cobalt, nickel) with electrogenerated redox species are now investigated at a laboratory and mini-pilot scale.

Jan 1, 2000

By K. Morsi, S. K. Kassegne, A. El-Desouky, K. S. Moon

"Current Activated Tip-based Sintering (CATS) is a new process for the powder-based fabrication of macro, micro and possibly nano-scale features and shapes. This new and unique process enables selective sintering of powders by localizing electrically activated sintering conditions through a stationary or moving electrically conducting tip. We present preliminary experimental results on the effect of tip size in the CA TS process as well as the effect of initial powder particle size on the sintering behavior of nickel powder.IntroductionSpark Plasma Sintering (SPS) has been the center of attention of numerous researchers due its noticeable advantages over conventional sintering techniques such as rapid heating rates, lower sintering temperature and shorter holding times. Research on SPS has been applied on a wide variety of materials such as pure metals [ 1], ceramics [2], composites [3], nano-materials [ 4], biomaterials [ 5], shape memory alloys [ 6] and many other material systems. However, it has been mostly limited to bulk materials with simple shapes with a few exceptions ofresearch efforts where the effect of electric current was combined with metal forming processes such as spark plasma extrusion [7,8] and electric rolling of powders[9]. In this paper a novel process (Current-Activated Tip-Based Sintering (CATS)) is discussed where electric current and pressure are applied simultaneously through a small conducting tip (stationary or moving) over a conducting powder compact. This process has the potential advantages of sintering complex geometries with minimum energy requirements as unconventionally high current densities can be achieved due to the small contact area between the tip and the powder compact. Furthermore, by controlling the tip size, it can be possible to sinter features on the macro-, micro- and even nanoscales."

Jan 1, 2011

By Renxing Li, Yongyong Gong, Yufeng Cheng, Zhenxing Yin, Xin Cao, Qijie Zhai

"The influence of electric current pulse (ECP) on the solidification structure of SUS430 ferritic stainless steel (FSS) was investigated in the current study. The technology of ECP has been widely used to improve the properties of metals with relatively low cost. The parallel electrodes were inserted into the free melt surface to constitute a current loop. The different influences of three parameters on solidification structure were studied by changing the peak current value, frequency and treating time respectively. The results indicated that the ECP significantly increased the number of equiaxed grains of SUS430 FSS. The as-cast structure without ECP treating was almost wholly columnar, while the number of equiaxed grains of the specimen, which was treated 3min with a peak current of 400kIA, increased to 2698 in the observed surface. To get the best refinement, an optimum range of these three parameters is required and the peak current value plays the most important role.IntroductionFor the lack of nickel resource and the pressure of environment protection, ferritic stainless steel is increasingly adopted to replace the austenite stainless steel because of its low nickel content and good mechanical properties. SUS430 steel is a typical example with excellent performance and relatively low price to replace the application of austenitic stainless steel[1-3]. This type of steel with high thermal conductivity coefficient, low expansion coefficient, good oxidation resistance, excellent stress corrosion resistance and other fantastic characteristics is often used to make components which need to have resistances for atmosphere, water, steam and oxidizing acid corrosion[4]. Since the developing of columnar grains and low toughness at high temperature, its products are easily crinkled and cracked during the subsequent rolling process[5]. The application of ferritic stainless steel is limited by these defects[6-8]."

Jan 1, 2012

By Sarah Beutner Mavrogenes

The mineralogy of three slags from a domestic secondary copper refinery were studied by applied mineralogical techniques to determine the: 1) phases present, 2) phase chemistry, 3) phase abundance, 4) associations, 5) crystalline habit, 6) grain size, 7)microtextures, and 8) causes for certain metallurgical problems, such as metal losses to the slags. The slags were produced by skimming the bath prior to melt-down to allow heat from the flame to reach the bath. The first slag is highly viscous and all three slags contain a large amount of copper. The "first slag", which is skimmed prior to treatment of the bath with fluxes, contains metallic copper, cuprite, delafossite, magnetite, Mg-hercynite, common spinel-chromite solid solution, picrochromite-chromite solid solution, common spinel-picrochromite solid soiution, gahnite, cassiterite, silica-rich glass, and corundum. Its abundant solid refractory phases make the slag difficult to skim. The "soda-rich slag", skimmed after the treatment of the bath with sodium carbonate flux, contains cuprite, delafossite, magnetite, cassiterite, Na-Al-silicate, and Na-Al-Ca-silicate. It contains less metallic copper than the first slag and lacks the refractory minerals. The "phosphorus-rich slag", skimmed after treatment of the bath with a copper phosphide flUX, contains metallic copper, cuprite, delafossite, berlinite, cassiterite, silica, apatite, Cu-Fe-rich apatite, copper phosphate, Cu-Fe-phosphate, and a Pb-phosphate. In contrast to the above three copper-rich slags, recent charges have produced a silver-copper-rich slag. The "silver-rich slag", skimmed after the treatment of the bath with a copper phosphor ide-borax flux, contains, cassiterite, delafossite, cuprite, a Na-Al-silicate, magnetite, metallic copper, MgO, common spinel-chromite solid solution, and wollastonite. Silver ranging from 0.05 to 2.02% was found by atomic absorption and inductively coupled plasma spectrometry analyses in the metallic copper phase.

Jan 1, 1989

By V. Montenegro

Smelting of copper concentrates in Teniente Converter produces highly oxidized slag, containing from 4 to 10 % Cu and from 15 to 25 % of Fe304. Copper recovery requires magnetite reduction at a level of 5%, determining the degree of cuprous oxide co-reduction and the liberation of copper matte inclusions. The rate of slag reduction is controlled by the mass transfer to the reaction interface. Slag stirring affects the rate of reduction and enhances coalescence of mechanically entrained copper matte inclusions. Slag reduction and sedimentation in the AC electric furnace is a commonly used method of slag cleaning. Utilization of DC electric furnace creates beneficial conditions introducing slag electrolysis additionally to chemical reductions with carbon of coke and electrodes. Application of external magnetic field, interacting with a direct current in an electric furnace, induces magnetohydrodynamic phenomena, such as intensive stirring and electromagnetic buoyancy force acting on inclusions. Laboratory scale research in simulated DC electric furnace with a superimposed magnetic field showed a significant acceleration of the rate of slag reduction and copper removal. Continuous measurement of gas flow and composition allowed for determination of the reduction rate along the time. Application of external magnetic field in the reduction of the industrial slag in a crucible simulated DC electric furnace results such as the increase of the reduction rate from 2 to 3 times, compared with the identical conditions in the AC electric furnace. Interaction of non- homogeneous electric field with crossed permanent magnetic field induces vigorous slag stirring, enhance mass transfer and accelerate the rate of the slag reduction. Additional participations of the slag electrolysis in the magnetite and cuprous oxide reduction as well as the acceleration of the settling of the inclusions by the electromagnetic buoyancy force affect the slag cleaning intensification.

Jan 1, 2003

By V. Montenegro

Smelting of copper concentrates in Teniente Converter produces highly oxidized slag, containing from 4 to 10 % Cu and from 15 to 25 % of Fe304. Copper recovery requires magnetite reduction at a level of 5%, determining the degree of cuprous oxide co-reduction and the liberation of copper matte inclusions. The rate of slag reduction is controlled by the mass transfer to the reaction interface. Slag stirring affects the rate of reduction and enhances coalescence of mechanically entrained copper matte inclusions. Slag reduction and sedimentation in the AC electric furnace is a commonly used method of slag cleaning. Utilization of DC electric furnace creates beneficial conditions introducing slag electrolysis additionally to chemical reductions with carbon of coke and electrodes. Application of external magnetic field, interacting with a direct current in an electric furnace, induces magnetohydrodynamic phenomena, such as intensive stirring and electromagnetic buoyancy force acting on inclusions. Laboratory scale research in simulated DC electric furnace with a superimposed magnetic field showed a significant acceleration of the rate of slag reduction and copper removal. Continuous measurement of gas flow and composition allowed for determination of the reduction rate along the time. Application of external magnetic field in the reduction of the industrial slag in a crucible simulated DC electric furnace results such as the increase of the reduction rate from 2 to 3 times, compared with the identical conditions in the AC electric furnace. Interaction of non-homogeneous electric field with crossed permanent magnetic field induces vigorous slag stirring, enhance mass transfer and accelerate the rate of the slag reduction. Additional participations of the slag electrolysis in the magnetite and cuprous oxide reduction as well as the acceleration of the settling of the inclusions by the electromagnetic buoyancy force affect the slag cleaning intensification.

Jan 1, 2003

By D. J. Adams

Cyanide heap leaching is the predominant technology used in processing low-grade gold ores. During closure ora heap leach operation, residual cyanide must be removed from the process and waste solutions, as well as the heap. Biological cyanide oxidation is a proven, economical technology for destroying cyanide in process and waste waters and spent heaps; The use of biological cyanide degradation eliminates the need for toxic or corrosive chemical oxidizers and has- been implemented at full scale at treatment costs usually <$0.50/1,000 gal. The Applied Biosciences biological cyanide destruction (BCND?) process has been demonstrated to effectively treat cyanide, concentrations up to 350 mg/L. Treated process solutions and wastewaters also contained other contaminants such as arsenic, copper, iron, silver. selenium, mercury, nitrate and zinc, much of which was removed in the cyanide degradation process. Under optimal conditions, microorganisms can rapidly oxidize free cyanide in some process solutions from over 250 mg/L down to 0.1 mg/L in 4 to 5 hr. Cyanide is degraded to ammonia and carbon dioxide, with 50%ofthe cyanide carbon liberated as C02. In general, carbon tank based bioreactors degrade cyanide at significantly higher rates than process or wastewater pond configured treatments, which usually degrade cyanide-more rapidly than in heap treatments. Investigation of cell-free enzyme preparations as an alternative to live microbial cyanide degradation shows promise. Advantages of enzymes over live microbes for cyanide degradation include: (I) the ability to tolerate and degrade higher cyanide concentrations (> I ;000 mg/L), (2) nutrients to support live microbial cells are not required, (3) the effects of other toxic contaminants, such as metals, found in mining waters-are eliminated and (4) the potential for greatly increased kinetics.

Jan 1, 1998

By Nathaniel R. Quick

"Nd: YAG, KrF excimer, and Cu-vapor lasers are used in air to synthesize conductors and semiconductors as a second phase in silicon carbide and aluminum nitride. Conductor resistivities as low as 104 O-cm are formed in these substrates; the resistivities for the untreated substrates range from 10 11to 1014 O-cm. The silicon carbide conversion is relatively independent of wavelength while the aluminum nitride conversion shows a dependence on wavelength over the range 248 nm to 1064 nm. Silicon carbide conductors, evaluated over the range 15 K to greater than 300 K, exhibit metal like conductivity; resistivity increases with temperature. Silicon, carbon, and oxygen are identified as the principal chemical species associated with the conductor in SiC substrates while aluminum, nitrogen, and oxygen are identified as the principal chemical species associated with the conductor in aluminum nitride substrates. The silicon carbide system, which has the less complex phase diagram, is evaluated in more depth to explain the synthesis mechanism. Oxygen was principally on the surface and increasing SiC conductivity is associated with decreasing spacing between 5 µm, or less, diameter carbon globules. This technology is proposed as a replacement for metallization in electronic packages, sensors and devices. INTRODUCTIONCeramics are commonly used for multichip module, hybrid and multilayer electronic packaging; semiconductor device and sensor applications because of the insulating, conducting, semiconducting, or superconducting properties that these materials possess (1,2) The majority of ceramics, however, have not been known to exhibit conductive or semi conductive properties when exposed to rapid thermal heat processing. A ceramic and process which through selective conversion can combine two or more of these electrical properties to eliminate the need for metallization is of interest to both the commercial and military sectors."

Jan 1, 1994

By Sepp Härkki

The energy crisis in Finland after World War I1 together with a sharp rise in the price of energy caused Outokumpu Oy to consider replacing the electric furnace smelting of copper concentrates by some other method. The flash smelting method developed under these circumstances offered a considerable saving of fuel through the utilization of the reaction heat of sulphides and yielded a high recovery of sulphur in the form of acid. The pilot plant testing of the new process was carried out in the years 1947 - 1948. The process was adopted for the smelting of copper concentrates (1) (2) (3) on a commercial scale in 1949 and applied successfullv to the smelting of -nickel concentrates&apos; at the Harjavalta Works in 1959 (4) (5) (6). In 1962 Outokumpu adopted another type of flash smelting where elemental sulphur is recovered from the gases after the thermal decomposition of pyrite in the flash smelting furnace (7) (8): In recent years, the copper-nickel flash smelter and pyrite process have been combined to produce elemental sulphur instead of SO2 from the smelter gases (9) (10). The basic idea of the Outokumpu flash smelting process for sulphidic ores is that the conventional methods with separate roasting and smelting operations are replaced by a combined roasting, smelting and part-converting process carried out in one unit. The heat generated from the exothermic reactions can thus be used for smelting the ore so that only a small amount of additional fuel is needed. The characteristic of the method is also that the dried, fine-grained concentrate is smelted in suspension, which offers the best conditions for rapid reactions. The recovery of waste heat from the furnace off-gases had been considered already in the original flash smelting system. A

Jan 1, 1976

By Yuanbo Zhang, Guanghui Li, Zhenyu Fan, Tao Jiang, Xiaohui Fan

"Iron ore sintering process is the main source of SO2 generated in the steel industry, of which the discharge amount of SO2 emission accounts for about 60% of the total. Aiming at the features of sintering flue gases and existing problems during the flue gas desulphurization, a technical route of flue gas circulation sintering (FGCS) for iron ores has been put forward. Under the simulated experimental conditions, effects of FGCS process on the main output and quality indexes and SO2 emission rule are researched using simulating flue gases. Compared the novel FGCS with conventional sintering process, SO2 in the final sintering flue gas is obviously enriched and the total exhaust gases can be reduced evidently. The decreasing of oxygen content in circulating gases has bad effect on the sintering indexes. Increasing the oxygen potential is beneficial to obtain high quality sinters. This investigation shows that the FGCS process is promising.IntroductionSteel is a kind of essential material for modern society, but steel-making process is characterized by high energy-consumption and emission as well as heavy environmental pollution. Chinese steel industry has developed rapidly in the last decade, and the environmental problem caused by ironmaking and steelmaking have also aroused the greatest concern, especially the atmospheric pollution caused by SO2, CO2, etc. Iron ore sintering process is the main source of SO2 generated in the steel industry, of which the discharge amount of SO2 emission accounts for about 60 % of the total. The development of the desulfurization process for sintering flue gases to reduce SO2 emission in sintering process is not only the requirements of sustainable development but also the most important environmental tasks for steel industry [1-5]."

Jan 1, 2011

By K. Murayama, M. Kawakami, T. Takenaka, S. Yokoyama

"Cokes play an important role of spacer in blast furnace. However, they degenerate during Boudouard reaction. Blast furnace cokes are reacted with pure C02 at I 072 to 1673 K. Reaction rate was obtained by the weight change of spherical specimen. The specimen after reaction was examined by microscopic observation. The reaction rate increased with temperature and was expressed by two Arrhenius type lines. The activation energy was 126 KJ/mol at higher temperature than 13 73 K and 202 KJ/mol at lower temperature range. At the higher temperature range, the reaction proceeded from the surface leaving unreacted core, whereas homogeneously whole inside at lower temperature. The porosity increased from the center to surface at higher temperature, whereas it was almost constant at lower temperature.IntroductionThe cokes have the function of fuel, reductant and spacer to keep gas and liquid flow in the blast furnace. Thus, the reaction mechanism of coke with several gas and the strength after the reaction should be important factor to control the blast furnace operation. The reaction mechanism of coke with C02 has been studied extensively. The rate equations were derived by Gadsby[ I], Ergun[2] and Turkdogan and Vinters[3]. They were compared and discussed by Kobayashi and Omori [ 4]. Effect of crystallization degree on the reaction rate was examined by Kashiwaya and Ishii[5]. Catalytic enhancement effect of ash componets have been clarified by Kashiwaya et. al. [6]. Although degradation of coke in blast furnace has been examined recently[7], however, the degradation of coke after the reaction with C02 has not been well clarified yet. In the present work, the metallurgical coke specimen was heated in N2 and C02 and the reaction mechanism and degradation behavior after the reaction was investigated."

Jan 1, 2000

By Riyad N. Ahmad-Bitar, Shadia J. Ikhmayies

"CdS/CdTe solar cells were built by depositing a 200 nm layer of Sn02:F on glass substrates by the spray pyrolysis (SP) technique, a 500 nm CdS:In layer by the same technique and a 1-1.5 µm CdTe layer by vacuum evaporation. The cells were CdCh heat-treated in nitrogen atmosphere for 30 minutes at 350 -.C. The photoluminescence (PL) spectra were measured at the CdS/CdTe interface for two cells with different values of the CdTe layer's thickness at temperature T = 60 K. A deconvolution peak fit was performed from which it is found that the peaks are characteristic of the solid solution CdSxTei-x· The parabolic relation that relates the bandgap energy with the composition was used to estimate x, where xis [S]/([Te]+[S]) and [Te], [S] are the concentrations of Te and S atoms respectively. The results show that the interface is smooth and the change of the bandgap occurs gradually.IntroductionCdS/CdTe heterojunctions represent a combination of materials promising various applications, and for solar energy conversion in the first place [1]. In photovoltaic cells the CdS material acts as a wide bandgap window. Direct bandgap CdTe with high optical absorption coefficient is used as an absorber [1]. Solar cells with efficiencies of 10 to 16% have been obtained with CdTe grown by close space sublimation, electrodeposition, vacuum evaporation and rf sputtering methods [2]. In this work the CdTe layer was prepared by vacuum evaporation because it results with films of minimum impurities, while the Sn02:F and CdS:In layers were deposited by the spray pyrolysis technique because it is a low cost method which enables intentional doping and large area thin films."

Jan 1, 2011

By Hiroaki Kawamura, Takeshi Yoshikawa, Kazuki Morita, Yutaka Yanaba

"To develop an alternative metallurgical process for phosphorus removal in the production of solar-grade silicon (SOG-Si), slag treatment of metallurgical-grade silicon (MG-Si) was conducted, followed by acid leaching. Phosphorus-doped silicon alloy or MG-Si containing certain amounts of phosphorus and calcium was reacted at 1723 K and 1773 K with CaO--CaF2 of several compositions. Phosphorus removal from the molten silicon into the slag phase was confirmed by reduction to phosphide ions, P3-, and phosphate ions, P3-. These ions were separately determined using a wet chemical analysis method developed by ourselves. The highest phosphorus distribution ratio obtained was 2. 7 after reaction for 18 h with 17.5 mass% CaO--CaF2 slag. We then conducted acid leaching of the silicon and achieved removal of a large fraction (over 90 % ) of the phosphorus, which was much higher than that obtained by ordinary oxidizing slag treatment.IntroductionIn recent years, the production of solar cells has been increasing rapidly. Because of this, the demand for solar-grade silicon (SOG-Si) has also been growing rapidly. The development of lower-cost mass production processes is therefore needed to provide silicon feedstock. Phosphorus is one of the impurities in metallurgical-grade silicon (MG-Si). Because of its large segregation coefficient (kp = 0.35) [l ], it is difficult to remove phosphorus using a solidification refining process. Vacuum melting is considered to be a promising method for removing phosphorous from MG-Si [2], but the issues of high cost and large energy consumption have still to be resolved.Slag treatment is often used to remove impurity elements by oxidizing reactions during general oxidation refining processes. For example, phosphorus in molten steel is removed into a slag phase as phosphate ions, PO4 3-l-, by the following reaction:"

Jan 1, 2013

By J. Gartelmann, B. Zaslavsky, Y. Vojta, D. J. Chaiko, W. Mego, A. N. Rollins

"Aqueous biphasic extraction (ABE) processes offer the potential for low-cost, highly selective separations. This countercurrent extraction technique involves selective partitioning of either dissolved solutes or ultrafine particulates between two immiscible aqueous phases. The extraction systems that we have studied are generated by combining an aqueous salt solution with an aqueous polymer solution.We have examined a wide range of applications for ABE, including the treatment of solid and liquid nuclear wastes, decontamination of soils, and processing of mineral ores. We have also conducted fundamental studies of solution microstructure using small angle neutron scattering (SANS). In this chapter we review the physicochemical fundamentals of aqueous biphase formation and discuss the development and scaleup of ABE processes for environmental remediation.IntroductionAqueous biphasic extraction (ABE) is a highly adaptable separation technique that can be used in a wide range of applications. We have been evaluating various types of ABE systems for possible applications in the treatment of solid radioactive wastes (1,2), liquid nuclear wastes (3,4), and contaminated soils (5-7), and in the removal of organics from aqueous salt solutions (8). We have also conducted fundamental studies of the solution microstructure of ABE systems using small angle neutron scattering (SANS) (9).The extraction systems are generated by combining an aqueous salt solution and an aqueous polymer solution. This produces two distinct liquid layers that are as immiscible as oil and water, yet each liquid layer contains at least 70 to 80 wt % water. The biphasic systems that we have been working with consist of immiscible polyethylene glycol (PEG) and salt solutions. Some inorganic salts that promote biphase formation with PEG solutions include the sodium/potassium salts of sulfate, carbonate, phosphate, and hydroxide (10)."

Jan 1, 1996

By R. J. Dippenaar, W. H. Van Niekerk

"An injectable lime-based desulphurization reagent for the treatment of liquid iron was developed. Firstly, selected lime based slags containing small quantities of CaF2 to increase fluidity, and Na20 to increase the basicity, have been evaluated on laboratory scale from a thermodynamic point of view. Subsequently, pilot plant and full scale industrial injection trials were conducted. It was found that lime-based slags, containing Na20 and CaF2, are able to desulphurize liquid iron efficiently. By the injection of a lime based reagent consisting of 60% lime, 25% soda ash and 15% fluorspar at a rate of 7 kg reagent/ton hot metal, the sulphur level in the metal (115kg) was reduced from 0,07% to 0,01 % within 5 minutes. The lime-based reagent developed in this study was successfully injected, both from a metallurgical and from a pneumatic point of view, on an industrial scale. The mathematical model utilised in this study, can be used successfully to predict the course and extent of desulphurization by lime-based slags. IntroductionMainly due to environmental difficulties encountered with pure soda ash, dry slag formation with CaC2 and high cost when Mg are used as desulphurizers, much incentive exists for the development of an inexpensive, environmentally friendlier desulphurization reagent. As a first step in the development of such a reagent, selected lime based slags containing small quantities of CaF2 to increase fluidity, and Na2O to increase the basicity, have been evaluated on laboratory scale from a thermodynamic point of view. This was followed by pilot plant injection experiments in which the kinetics of the relevant desulphurization reactions were evaluated. Finally, full scale industrial trials were conducted. All three phases of the investigation will be discussed with the major emphasis being placed on the kinetic study."

Jan 1, 1996

By Francis C. Furman

Microscopic evidence indicates that the high sinterability of certain commercial dolomites is tied to specific dolomite textural characteristics. This study encompasses detailed characterization of the unprocessed dolomite and sintering doloma results. The chemical and mineralogical compositions, insoluble residue, chemistry homogeneity, crystal size, primary carbonate texture, secondary dolomite texture, deformation structure, porosity type, porosity, and density of the raw dolomite were observed. These characteristics are compared with sintering trials of <74um powder-compacts samples in which holding times were varied. The evolution of the dolomite characteristics are reviewed and related to the final sintered doloma characteristics. The critical characteristics of a single-stage sintering brick dolomite are the following: 1) primary oolitic texture, 2) dolomite purity, 3) dolomite stoichiometry 4) minimal impurities, less than 1 weight {%} Fe2O3 Al2O3 and SiO2, 5) chemical homogeneity, 6) high density, 7) very low porosity, S) very coarse homogeneous crystallinity, 9) nonplanar dolomite texture, 10) abundant strain related slip microdeformation structures, 11) minimal subsequent alteration. Even with grinding to <74um the nonplanar dolomite texture and slip deformation still have a major effect on doloma sintered density. The three newly identified characteristics of single-stage sintered refractory brick dolomite are their primary oolitic texture, secondary nonplanar texture and abundance of stress related microdeformation structures. The primary oolitic texture reflects a homogeneous pure carbonate with respect to chemistry and crystal size secondary nonplanar texture produces crystals with large surface area to volume ratio. Stress related slip deformation moves CO, groups in to the same site of another CO, group but different orientation which is very unstable. All of these characteristics may facilitate the formation of higher density dolorna sinters.

Jan 1, 1995