By L. J. Buteau, R. E. Reed-Hill, W. A. Slippy

In a zirconium {1121} twins tend to have coherelzt boundaries and thus do not usually taper to a point when they intersect a grain boundary. Under the proper conditions, a (1121) twin may deform a boundary in such a manner as to clearly rcveal the twinning shear. Measurements of these grain-bounrlary rotatzons yield a value of 0.63 for the (1151) twinning shear. The magnitude of the observed shear and its shear sense are in excellent agreement with the assumption that the second undis-torted plme (K2) for this form of twinning is the basal plane (0002). The present value of the tzvinninz shear, which is approximately three limes larger than Rapperport&apos;s value? is in excellent agreement with reported results of Sokuskii and Prolsenko.5 RECENTLY westlake&apos; reported a study of the twinning modes of zirconium based on ~ap~er~ort&apos;s2 values for the twinning elements. He observed that two of the modes, (1012) and {1122), can be explained by relatively simple dislocation models. A workable model for (1121) twinning, however, proved to be very complex and questionable. Because Rapperport&apos;s second undistorted plane, (K2), for (1121) twinning has large indices, {ll2l6), it is possible that the difficulty in defining a model for (1121) twinning lies in an incorrect value for K2. A measurement of this twinning element has therefore been made, using a method based on observations of the shear displacement of grain boundaries at positions where they are intersected by (1121) twins. EXPERIMENTAL PROCEDURES The zirconium specimens were deformed in tension on an Instron machine either at the temperature of liquid nitrogen (77ºK), or prestrained at liquid nitrogen temperature and then further deformed at room temperature. Straining at 77°K was employed in order to nucleate (1 121) twins in large numbers, since simple ropm-temperature tensile deformation favors (1012) twinning. Specimens were machined from 1/2-in.-thick plate. The material was arc-melted sponge zirconium annealed to an ASTM grain size 4 and containing, in parts per million, 380 Fe, 880 0, <40 Hf, 32 N, and < 5 H. The specimen gage length and diameter were 1.25 and 0.130 in., respectively. To insure a gage section initially free of twins, the last 60 thousandths of the specimen diameter was removed by acid machining.

Jan 1, 1963

By E. T. Dumble

In the Bosquejo Geoldgico de Mexico, published in 1897 by the Secretaria de Fomento as Nos. 4, 5 and 6 of the Boletin del Institute Geologico de Mexico, the Director, Jose C. Aguilera, after a detailed account of the geological observations made by himself and his assistants on their several trips through the various districts of the Republic, gives in Part 2 a synopsis of the geology of Mexico, describing . al1 the formations recognized, the rocks comprised in them, their geographical distribution, disturbances, principal eruptions and economic features, as explanatory of the Geological Map of Mexico. In Part 3 Prof. Ordonez describes many of the interesting eruptive rocks of Mexico." This work brings together in a very satisfactory way about all of the published results of geological investigations in Mexico; and although the determinations of the authors with reference to some of the sedimentary deposits are very different from those of other writers, they seem to be based upon good paleontological grounds in each instance. From the map and the text of this paper it appears that the condition of knowledge in regard to the geology of the State of Sonora, at the time of its publication, was about as follows: The western portion of the State, lying between the coast line of the Gulf of California and the foot-hills of the Sierra Madre mountains, is largely Quaternary, interrupted by areas of Azoic rocks and of later eruptives, with two or three limited exposures of limestones of the Cretaceous; while the eastern or

Jan 1, 1900

By Paul A. Beck

While the recrystallization properties of most of the practically important metals are known in considerable detail, those of lead are still relatively little known in spite of some valuable contributions in recent years. This condition probably is due to the difficulties involved in applying the usual methods of investigation. The microscopic method of discriminating between the elongated deformed grains of the familiar lenticular shape and the equiaxed recrys-tallized grains is not successful with fully refined lead: lenticular grains cannot be seen under the microscope with any amount of deformation whatever. The probable cause of this phenomenon was recognized long ago. With large deformation the time of recrystallization at room temperaturc is shorter than the period of preparation of the specimen for microscopic examination; with small deformation the deformed grains arc not noticeably elongated in the first place. However, with small cleformation the migration of the grain boundaries can be observed. The only systematic investigations yet published on the recrystallization of lead, those by R. S. Russell, 1-3 make use of the conditions just described. Russell considered recrystallization completed when no further migration of boundaries could be observed. A serious objection to this method arises from the fact that there is no evidence to support the view that grain-boundary migration results only from recrystallization. If such migration does result from other sources after recrystallization is completed—after the deformed grains have been replaced by new unde-formed grains—the "time of recrystallization" as determined by Russell may be too long. Furthermore, the method is subject to the above.-mentioned limitation because of the unavoidable period of preparation of the sample. According to Russell, even with the fastest technique 5 min. clapsed before the deformed samples were ready for examination, and consequently no reearystallization time shorter than 5 min. could be measured. The lack of success in detecting the recrystallization of lead by the usual hardness or tensile tests is again caused by the time necessary for

Jan 1, 1940

By Paul A. Beck

While the recrystallization properties of most of the practically important metals are known in considerable detail, those of lead are still relatively little known in spite of some valuable contributions in recent years. This condition probably is due to the difficulties involved in applying the usual methods of investigation. The microscopic method of discriminating between the elongated deformed grains of the familiar lenticular shape and the equiaxed recrys-tallized grains is not successful with fully refined lead: lenticular grains cannot be seen under the microscope with any amount of deformation whatever. The probable cause of this phenomenon was recognized long ago. With large deformation the time of recrystallization at room temperaturc is shorter than the period of preparation of the specimen for microscopic examination; with small deformation the deformed grains arc not noticeably elongated in the first place. However, with small cleformation the migration of the grain boundaries can be observed. The only systematic investigations yet published on the recrystallization of lead, those by R. S. Russell, 1-3 make use of the conditions just described. Russell considered recrystallization completed when no further migration of boundaries could be observed. A serious objection to this method arises from the fact that there is no evidence to support the view that grain-boundary migration results only from recrystallization. If such migration does result from other sources after recrystallization is completed—after the deformed grains have been replaced by new unde-formed grains—the "time of recrystallization" as determined by Russell may be too long. Furthermore, the method is subject to the above.-mentioned limitation because of the unavoidable period of preparation of the sample. According to Russell, even with the fastest technique 5 min. clapsed before the deformed samples were ready for examination, and consequently no reearystallization time shorter than 5 min. could be measured. The lack of success in detecting the recrystallization of lead by the usual hardness or tensile tests is again caused by the time necessary for

Jan 1, 1940

By J. A. Bownocker

THE Pittsburgh is one of the most important coal beds of Ohio. It was the last of the great coal beds to be worked extensively in that State, has the largest area of virgin coal, and will in all probability be the last of the great deposits to be exhausted. The line of outcrop sweeps nearly southwest in a sinuous line from Jefferson County on the north to Lawrence on the south, a distance on a bee-line of at least 150 miles. (Fig. 1.) The maximum width of the area under which this coal is due is about 55 miles, but in most places it is less than half that and in the two southern counties it is in places restricted to narrow ridges. Here as elsewhere the Pittsburgh coal forms the base of the Monongahela formation, and the following section taken from Condit shows the position of this bed with reference to certain higher ones in this field:1 FEET INCHES Shales and thin beds of limestone 24 5 Coal, Meigs Creek, No. 9 4 0 Shale, sandy 11 0 Coal 0 8 Shale, clayey 6 0 Coal, Lower Meigs Creek 3 0 Shales,clayey 2 0 Limestones and thin layers of clay 25 0 Unseen 11 0 Coal, Redstone 2 0 Unseen 11 0 Coal, Pittsburgh, No. 8 8 0 Clay 5 0 Limestone 4 0 From the standpoint of continuity the Pittsburgh coal of Ohio must be classed with the patchy type. As the map shows, the coal is thin or wanting along many miles of the line of outcrop. The large deposits form three separate areas, which, in order of their importance, are generally known as (1) the Belmont, (2) the Federal Creek, and (3) the Gallia fields.

Jan 10, 1926

By C. E. Shoenfelt

There was a notable decrease in drilling operations in 1940 in all of the Rocky Mountain states except Montana, where the two large fields on the Canadian border, Cut Bank and Kevin-Sunburst, were espe-cially active. The expanding markets for Montana natural gas made necessary the more intensive development of such fields as Rowdoin, Cedar Creek and Devon. While there were no important oil and gas discoveries in 1940 in any of the Rocky Mountain states, a few small pools were opened, which may constitute separate areas but may prove with later development to be extensions of old fields. Some of the old fields were extended and deeper pay zones were discovered in others. These have given the areas greatly increased oil reserves and therefore are just as important as the discovery of new fields. The more important of the developments in 1940 are given, by states, in the following paragraphs. Colorado Hiawatha Field, Moffat County.—The Mountain Fuel Supply Co. began the development at Hiawatha of its oil reserves, which were discovered in about 1929, and late in the summer oil began moving from the field by truck to the shipping point at Rock Springs, Wyoming. The Hiawatha field of northwestern Moffat County was discovered in 1927 by the Sormir Petroleum Co., with the completion of No. r Florence Wilson for 4,5,000,000 cu. ft. of gas a day from a Wasatch sand lens at 2200 it. In later development of the field, oil showings were reported in several wells but no development of this resource was undertaken until 1940, when a test of the oil possibilities was started with the release in April of a location for No. 5-A Wilson on the S\W. SW. NW. of sec. 23-1zN-1ooW., on the east side of the field. The Well had an initial production of 327 bbl. of oil a day pumping from three Wasatch (Tertiary) sands between 2005 and 2540 ft. It was drilled to 2562 ft., where the 65/8-in. casing was cemented and gun-perforated at 2005 to 2125 ft., 2260 to 2335 ft. and 2513 to 2540 ft. At the end of the year, this well was averaging zoo bbl. of oil per day, pumping. Two other wells were drilled for oil on Hiawatha during the summer—one a small well of 60 bbl. per day and the other a small gas well. Powder Wash Field, Moffat County.—The development of the Powder Wash field in northwestern Colorado was resumed in 1940 by the Mountain Fuel Supply Co., with the release of a location for No. 2-A Musser in the CWL.NW.SE. of sec. 4-1rN-97W. The Powder Wash field was discovered in 1931 by the Mountain Fuel Supply Co. and the discovery well, No. I Musser, on C.NW. of sec. 5-IIN-97W., was completed at 2152 ft. in the Hiawatha member of the nonmarine Wasatch for-mation for an open flow of 34,000,000 cu. ft. of gas per day under a natural pressure of 685 lb. per sq. inch. Oil was discovered in the Powder Wash field on Nov. 26, 1936, in the company&apos;s No. I Carl Allen on the NE.SW.SE. of sec. 32-12N-97W. The oil production was

Jan 1, 1941

By C. E. Shoenfelt

There was a notable decrease in drilling operations in 1940 in all of the Rocky Mountain states except Montana, where the two large fields on the Canadian border, Cut Bank and Kevin-Sunburst, were espe-cially active. The expanding markets for Montana natural gas made necessary the more intensive development of such fields as Rowdoin, Cedar Creek and Devon. While there were no important oil and gas discoveries in 1940 in any of the Rocky Mountain states, a few small pools were opened, which may constitute separate areas but may prove with later development to be extensions of old fields. Some of the old fields were extended and deeper pay zones were discovered in others. These have given the areas greatly increased oil reserves and therefore are just as important as the discovery of new fields. The more important of the developments in 1940 are given, by states, in the following paragraphs. Colorado Hiawatha Field, Moffat County.—The Mountain Fuel Supply Co. began the development at Hiawatha of its oil reserves, which were discovered in about 1929, and late in the summer oil began moving from the field by truck to the shipping point at Rock Springs, Wyoming. The Hiawatha field of northwestern Moffat County was discovered in 1927 by the Sormir Petroleum Co., with the completion of No. r Florence Wilson for 4,5,000,000 cu. ft. of gas a day from a Wasatch sand lens at 2200 it. In later development of the field, oil showings were reported in several wells but no development of this resource was undertaken until 1940, when a test of the oil possibilities was started with the release in April of a location for No. 5-A Wilson on the S\W. SW. NW. of sec. 23-1zN-1ooW., on the east side of the field. The Well had an initial production of 327 bbl. of oil a day pumping from three Wasatch (Tertiary) sands between 2005 and 2540 ft. It was drilled to 2562 ft., where the 65/8-in. casing was cemented and gun-perforated at 2005 to 2125 ft., 2260 to 2335 ft. and 2513 to 2540 ft. At the end of the year, this well was averaging zoo bbl. of oil per day, pumping. Two other wells were drilled for oil on Hiawatha during the summer—one a small well of 60 bbl. per day and the other a small gas well. Powder Wash Field, Moffat County.—The development of the Powder Wash field in northwestern Colorado was resumed in 1940 by the Mountain Fuel Supply Co., with the release of a location for No. 2-A Musser in the CWL.NW.SE. of sec. 4-1rN-97W. The Powder Wash field was discovered in 1931 by the Mountain Fuel Supply Co. and the discovery well, No. I Musser, on C.NW. of sec. 5-IIN-97W., was completed at 2152 ft. in the Hiawatha member of the nonmarine Wasatch for-mation for an open flow of 34,000,000 cu. ft. of gas per day under a natural pressure of 685 lb. per sq. inch. Oil was discovered in the Powder Wash field on Nov. 26, 1936, in the company&apos;s No. I Carl Allen on the NE.SW.SE. of sec. 32-12N-97W. The oil production was

Jan 1, 1941

By A. G. Starliper, H. Kenworthy, A. Ollar

Vapor pressure determinations were made on synthesized germanium sulfides. Germanium and cadmium were removed from sphalerite concentrates by fuming. The fume was retreated to separate some of the cadmium from the germanium and, at the same time, upgrade the germanium to more than 5 pet content. MANY sphalerite concentrates contain certain impurities which have economic value as byproducts. These may include the volatile sulfides of germanium, cadmium, and lead. The objectives of the research reported in this paper were to study the fundamental volatility characteristics of germanium sulfides, to increase the recoveries of ger-

Jan 1, 1957

By Robert Maes, Robert de Strycker

The Fe-Ni-As phase diagram has been established by the study of about a hundred alloys, by microscopic observation, and by thermal analysis, with arsenic contents up to 50 pct. The iron and nickel arsenides present extensive solid-solution fields, owing to the substitution of nickel by iron and vice versa; the extent of the solubility field of each compound has been determined with an accuracy of ±1 pct. In the investigated range of compositions, the solidification reactions were established, and the temperatures of the invariant reaclions detevmined with a preciston of iZ°C in the most favorable and ±5°C in the least favorable cases. The isothermal lines of the liquidus surface have also been drazum, with an accuracy estimated at i5°C. Reactions in the solid state, which take place for the formation or the decomposition of certain phases , were investigated in detail. ThE constitution diagram of the Fe-Ni-As system is fundamental for the understanding of the properties of nickel speiss; these by-products of the extraction of certain nonferrous metals indeed often contain the three elements iron, nickel, and arsenic as main constituents. The Fe-Ni-As system has already been the object of earlier investigations. In 1932, Guertler and Savels-berg&apos; have presented some elements of the ternary phase diagram, for arsenic contents up to 55 pct (all percentages in this paper are given in weight percent), including the vertical section FezAs-Ni&s2. This investigation is, however, incomplete and certain anomalies suggested the necessity to verify the results published by these authors: the section Fe2As-Ni5AsZ, for example, is presented as quasi-binary, with a field of complete miscibility in the solid state, even though these compounds do not have the same structure. Recently, ~useck&apos; established an isothermal section at 800°C in the Fe-Ni-As system by X-ray diffraction and microscopic examination of water-quenched alloys. These techniques are sometimes inaccurate for the determination of the fields where alloys are liquid at the investigated temperature, and they may lead to erroneous conclusions when a compound exists at the investigated temperature but is not stable at room temperature and cannot be maintained by quenching. LIMITING BINARY PHASE DIAGRAMS The Fe-As constitution diagram has been the object of several investigations which have been reviewed by Hansen and Anderko.3 For the Ni-As phase diagram, a recent study has been effected by Yund.4 In this system, Heyding and calvert5 have determined the existence of a compound of unidentified structure at arsenic contents slightly higher than those corresponding to Ni5As2 and at temperatures lower than about 200°C; by analogy with iron and cobalt arsenides, this compound could correspond to the formula Ni2As, as suggested by Kulle-rud; although this is not definitely established. In the region of arsenic contents from 35 to 55 pct, Fried-rich7 detected anomalies in the solidification reactions; an interpretation of these anomalies was given by Hansen ,8 which assumed that the solidification reactions in practice are not in equilibrium, but are meta-stable. The main features of the Fe-Ni constitution diagram are the existence of a complete miscibility field, at least at high temperatures, for the fcc phase (which will be designated by My in the remainder of this work) and of a limited solubility field for the bcc phase (designated by Ma). EXPERIMENTAL METHODS The fundamental technique used in this investigation was microscopic observation, which allowed the determination of the reactions occurring during solidification of the alloys, and possible reactions in the solid state.

Jan 1, 1968

By Joseph R. Stephens

Deformation substructures of&apos; polycrystalline tungsten, W-2, 9, and 24 pct Re, and W-3 pct Ta were studied by tra?zsrnission electron microscopy. The stress-strain curve for unalloyed tungsten showed gradual yielding followed by work-hardening. Electron nzicrographs indicated a gradual increase in dislocation density with increase in strain up to 5.0 pct. Dislocations, although frequently jogged, were straight over moderate distances and were in a randorn array. Stress-strain curves for alloy specimens of W-2 and 9 pct Re and W-3 pct Ta exhibited a drop in stress at yielding followed by only slight work-hardening. Electron micrographs of these specimens after strains of 0.05, 0.1, and 0.5 pct revealed no change in dislocation substructure from the unstrained specimens. After 2.0 pct strain, the three alloys exhibited dense networks. W-3 pct Ta was characterized by straight, frequently jogged dislocations comparable with the dislocation structure in unalloyed tungsten after a similar amount of strain. In contrast, W-2 pct Re exhibited dislocations that contained widely spaced jogs, while W-9 pct Re had developed a cell structure after the relatively srnall strain of 2.0 pct. The W-24 pct Re alloy contained a few dislocations after 0.1 pct strain, while after 0.5 pct strain twins were evident. Dislocation slip bands apparently preceded the twins. The stress-strain curve for the alloy indicated that twinning commenced after approximately 0.25 pet strain. These results indicate that the primary effect of low rhenium concentrations (2 and 9 pct) in tungsten is to increase dislocation multiplication after macroyielding by reducing the Peierls-Nabarro force (lattice resistance to dislocation motion). The dislocation bands that precede twins in W-24 pct Re may be caused by localized internal stresses resulting fro a metastable structure, for example, clustering of rhenium atoms. The effect of high rhenium additions (22 a 65 pet* Rproperties of tungsten. Klopp, Witzke, and Raffo5 reported bend transition temperatures as low as -100°F (200°K) for dilute electron-beam-melted W-Re alloys tested in the worked condition. Recrystalliza-tion increased the bend transition temperature, but alloys with 2 to 4 pct Re were still markedly superior to unalloyed tungsten. Fractographic examinations of tungsten and W- 3 pct Re and W- 5 pct Re alloys by Gilbert 6 revealed that these low rhenium alloys showed a greater tendency toward cleavage failure than did tungsten. Garfinkle 7 showed that rhenium additions, up to 9 pct, to (100) oriented tungsten single crystals increased the proportional limit stress and decreased the flow stress and the rate of work-hardening. In addition, while deformation in unalloyed (100) oriented crystals apparently involved both (110)100) and (112) slip, crystals with rhenium contents of 5 andpct or more deformed primarily by (112) slip. The mechanism by which high and low rhenium additions affect the mechanical properties of tungsten is still not well-established. The present investigation was undertaken to determine by transmission electron microscopy the effects of low rhenium additions, 2 and 9 pct, and a high rhenium addition, 24 pct, on dislocation substructure in the early stages of deformation of polycrystalline electron-beam-melted tungsten. Unalloyed tungsten and a W- 3 pct Ta alloy were included for comparison. EXPERIMENTAL PROCEDURES Materials. Triple electron-beam-melted tungsten, W-2, 9, and 24 pct Re, and W- pet Ta were used for this investigation. Chemical analyses of the cast ingots are given in Table I. A description of the starting metal powders and melting and fabrication pro-cedures for unalloyed tungsten and the W-Re alloys is reported.5 The W-3 pet Ta alloy was processed in a similar manner. Compression specimens measuring 0.300 in. (7.6 mm) in length by 0.130 in. (3.3 mm) in diam were machined from swaged rods. All alloy specimens were annealed in a vacuum of 8 x 10- 6 Torr (10&apos;2iVper sq m) for 1 hr at 3600°F (2255°K). The recrystallized grain size ranged from 0.06 to 0.08 mm diam for the alloy specimens. Unalloyed tungsten was annealed at 2400° F (1589°K) for 1 hr to produce a recrystallized grain diameter of approximately 0.12 mm. Specimens were electropolished in a 2 pet NaOH solution to a diameter of 0.125 in. (3.18 mm) to remove surface notches resulting from grinding and to improve reproducibility of t data. The ends o the compression specimens were ground flat, parallel to each other, and perpendicular to the longitudinal axes with 4/0 emery paper. Compression Tests. The compressive stress-strain apparatus used for compression tests is described in detail by Stearns and Gotsky.9 Room-temperature compression tests were conducted at a crosshead speed of 0.01 in. per min (0.25 mm per min).

Jan 1, 1969

By H. J. Levinstein, H. J. Guggenheim

RbFeF3 is a transparent ferromagnet with a large faraday rotation which permits the direct observation of magnetic domain structures in bulk crystals. If the position of dislocations within the crystal were known a study of domain wall dislocation interactions would be possible. In this paper an etch pitting solution is described which gives a one-one correspondent between the etch pits and the dislocations intersecting the (100) surfaces of RbFeF3 crystals. In addition, RbFeF3 is shown to have sufficient plasticity so that known arrays of dislocaticms can be put into the crystal. It is concluded that RbFeF, is an ideal material for the investigation of domain wall dislocation interactions. THE influence of lattice defects on the motion of domain walls in ferromagnetic materials has been studied extensively both theoretically and experimentally.4 The experimental data obtained has been qualitative in nature due to the lack either of a quantitative knowledge of the magnetic domain array in the material or of the nature of the dislocation configuration in the material. At room temperature RbFeFJ has the cubic perovskite structure. It is ferromagnetic below 86°K.5,6 It is also transparent and has a large faraday rotation in the magnetic state.7 The domain structure of this material is observable in three dimensions in crystals which are millimeters in thickness.&apos; Since RbFeF3 satisfies the requirements of having an easily visible three-dimensional magnetic domain structure, it was of interest to determine if the dislocation structure of the material could be determined and if the material was sufficiently plastic so that dislocations could be introduced into the as grown crystals. This is a report of the results of that investigation. EXPERIMENTAL PROCEDURE The crystals of RbFeFs used in this experiment were grown by a technique described elsewhere.5 In order to obtain flat strain-free surfaces, the samples were first cut to the crystal orientation desired and the surfaces were polished by employing standard metallographic techniques. The samples were then immersed in a solution of 1 to 3 g of KOH in 100 ml of water. This solution removes the damaged surface layers uniformly leaving a film on the surface of the sample. Etch pits are obtained by immersing the sample in an approximately 50-50 solution of 30 pct peroxide and concentrated acetic acid. The film formed during the KOH treatment turns deep red in color in the etching solution and flakes off the sample. The etching time required depends upon the pit size desired and

Jan 1, 1970

By C. P. Proctor, J. T. Crawford

TROUGH washers were among the earliest methods used for concentrating ores; they are referred to by Agricola about the middle of the sixteenth century as already being used while the hand- operated jigging sieve had only recently come into use. For cleaning coal the trough washer apparently was first used in France and Belgium .about 1841. The early trough washers were intermittent and the refuse at least was shoveled out by hand. The invention of a continuous jig washer, by a Frenchman, Berard, in 1848, acted as a stimulus to coal washings in jigs and retarded progress in trough washing&apos; in the nineteenth century. Chapman and Mott describe a number of trough washers developed in England and on the Continent from 1850 to 1900, such as the Bell and Ramsay, Ramsay, Bell and Green, Wunderlich, Scaife, McLellan; Lodge, Elliott, Blackett, and Murton. , The later of these removed the refuse mechanically, either intermittently or continuously, but in ways that interfered with stratification. THE RHEOLAVEUR A Belgian engineer, Antoine France, is responsible for the development of means to remove refuse materials continuously from a trough washer while preserving stratification and preventing the loss of coal with the refuse. The methods and equipment devised, which have become known throughout the world as Rheolaveur, were initiated at the St. Nicholas mine near Liége, Belgium, about 1912. This installation consisted of two units to wash 20 to 8-mm. (13/15 to 5/16 in.) and 8-mm. to 0 (5/16-in. to 0), each having only two superimposed inclined troughs. The first few "Rheo" boxes on the top trough removed refuse directly and the remaining Rheo boxes discharged impure refuse to the lower trough for rewashing. On the lower trough the first few boxes removed refuse and the following boxes removed a middling product

Jan 1, 1943

By Klaus Schwerdtfeger

The rules of solution of oxygen from H2O-H2-He gas and of nitrogen from N2-H2 gas in shallow melts of liquid iron were measured at 1610o and 1600o C, respectiuely. Concentration profiles were detemined in the liquid iron. Tire rate data indicate that the solution process is controlled by diffusion in the iron melt. The diffusivities for oxygen and nitrogen in liquid iron, as calculated from the present data, are DFe-o = (12 ± 3) < 10-5 sq cm per sec and DFe-N = 11 ± 2) X 10-5 sq cm per sec at the temperatures employed. AN attempt was made by Shurygin and Kryukl to measure the diffusivity of oxygen in liquid iron. In their experiments a silica disc was rotated in liquid iron containing oxygen, and the rate of formation of liquid iron silicate was measured. Assuming that the rate of dissolution of silica is controlled by diffusion of oxygen in the iron, the oxygen diffusivity was computed from the rate data giving Dfe-0 = 6.1 X 5 sq cm per sec at 1600°C. Although this value seems to be of the right order of magnitude, there is no proof of the correctness of the assumptions involved in the interpretation of these rate data. The oxygen concentration in the iron at the iron-iron silicate interface was taken to be that in equilibrium with the silica-saturated silicate melt. That is, it was assumed that no concentration gradient existed in the liquid silicate. This is a questionable assumption, unless it is proved that the thickness of the silicate layer is very much smaller than that of the diffusion boundary layer in the iron. Furthermore, Shurygin et al.1 used the Levich equation2 to interpret their rate data. This equation was derived for mass transfer between a solid disc and a single-phase liquid. The hydrodynamic and diffusion boundary layers in the iron stirred by a disc, via coupling of the silicate melt, may be appreciably different from those predicted by Levich&apos;s derivations. In the present work the diffusivities of oxygen and nitrogen in liquid iron were measured at 1610" and 1600oC, respectively. EXPERIMENTAL METHOD Iron melts contained in high-purity gas-tight alumina crucibles were reacted with H2O-H2-He gas for the determination of the oxygen diffusivity and with N2-H2 gas for the determination of nitrogen diffusivity. At the end of the reaction period, the samples were quenched in a cold H2-He gas stream at the top of the furnace. Oxygen or nitrogen contents in the iron were determined by chemical analysis. Two different types of diffusion experiments were perforxed. To determine concentration profiles, a few rate measurements were made using 4-cm-deep melts. The solidified samples were sliced into discs and each disc was analyzed for oxygen or nitrogen. In another series of experiments, oxygen or nitrogen was diffused into shallow melts (about 0.5 to 1 cm in depth) and the total sample was analyzed to obtain an average concentration of the diffusate. In most experiments, 4- to 5-mm-ID alumina crucibles were used. Some experiments were also made in smaller (3 mm) and larger (7 mm) diam crucibles. This variation in diameter caused no difference in the reaction rate, within the limits of experimental uncertainty. To promote the establishment of a stable density profile in the melt, all the samples were suspended in the lower end of the hot zone so that the top of the melt was hotter by a few degrees. Molybdenum wire resistance heating was used. The reaction tube of the furnace was a gas-tight recrystal-lized alumina tube. In most experiments the furnace was heated by an ac power supply. To check the possibility of inductive stirring, some experiments were carried out in a dc operated furnace, with essentially the same results. The temperature of the furnace was controlled automatically in the usual manner. The temperature was measured with a Pt/Pt-10 pet Rh thermocouple and is estimated to be accurate within ±5°C. The iron used was prepared by melting and vacuum-carbon deoxidizing electrolytic "Plastiron" in a zir-conia crucible. The main impurities are: Si 0.004 pct P, S <0.002 pct Cr 0.005 pct N 0.001 pct Zr 0.002 pct O 0.003 pct Mn 0.004 pct C 0.002 pct The gas composition was controlled by constant pressure head capillary flowmeters. Oxygen was removed from the gas mixture by passing it through columns of platinized asbestos (450°C) and anhydrone. Selected H2O contents were obtained by passing the purified gas through oxalic acid dihydrate-anhydrous oxalic acid mixtures held at constant temperature in a water bath. Water vapor pressure data for the oxalic acid dihydrate-anhydrous oxalic acid equilibrium were taken from the 1iterature.3 The flow rate used was about 1.5 liters per min. The whole system was checked for tightness at regular intervals.

Jan 1, 1968

By D. E. Peacock, B. Harris

The mechanical behavior of a niobium (columbium)TUNG alloy containing 20 wt pet Ta. 15 wt pet W, and 5 wt pct Mo has been studied in the temperature range 77° to 423°K. All specitrzens tested, apart from those into which oxygen was introduced deliberately, were fully recrystallized at 1500°C, had an average grain diameter of approximately 0.03 mm, and a combined carbon, ox-vgen. nitrogen, and hydrogen content of not not more than 250 ppm The meckatnical behavior of this alloy was found to be similar in seine respects to that of unalloyed bcc transilion metals. Both yield and flow stresses were sensililae to changes in deformation rate and both increased rapidly as the temperature was lowered below 150°C. A detailed examination revealed, however, that most of the temperature dependencc of the yield stress could be accounted for by the temperature dependence of the elaslic, modulus, whish is not true of the unualloyed metals. In lension at moderate strain rates, the trunsition fvom ducfile to hvittle behavior occurred just belour room teunperature bur incveasing the oxygen content from 190 to 200 pptn raised the transition temperature to about 4000K. TUNGSTEN and molybdenum have been found to be very effective high-temperature solid-solution strengtheners of niobium, but the amounts of these elements that can be added are limited if the alloy is to retain useful room-temperature ductility. It has been shown, however, that partial replacement of niobium with tantalum lowers the ductile-to-brittle transition temperature of such alloys and allows larger additions of molybdenum and tungsten to be made. Some of the high-temperature properties of niobium alloys containing these elements have been reported by Bartlett et al.,&apos; and the work presented here describes the low-temperature behavior of one of these, a solid-solution alloy containing, by weight, 20 pct Ta, 15 pct W, and 5 pct Mo. The elastic modulus, the temperature and strain-rate dependence of the yield and ultimate tensile stresses, and strain-hardening effects are discussed and compared with those of unalloyed niobium. EXPERIMENTAL MATERIAL AND PROCEDURE The material used in this investigation was produced from a 6-in.-diameter, double arc-melted ingot. This was can-extruded at about 1150°C to a 3-in.-diameter billet, and after annealing for 1 hr at 1345°C the billet was heated to 1315OC and part rolled and part forged to 0.5-in.-thick plate. The resulting material exhibited a cold-worked structure

Jan 1, 1965

By H. l. Burghoff, J. S. Porter

This paper presents the results of an investigation of the effect of cold-working and annealing treatments upon the occurrence of preferred orientation in annealed brass wire. The subject has received less consideration than has the same phenomenon in annealed brass sheet or strip, and perhaps very properly so in view of the obvious and undesired results obtained in the forming or drawing of strip having preferred orientation, which results are in contrast with the lack of any spectacular visual evidence in wire. The factors of cold-working and annealing that control preferredness in strip are naturally expected to function similarly in wire. Indeed, one might expect the condition to be commoner in annealed wire, because the severity of the cold-working between anneals in commercial Practice is usually much greater for wire than for strip. For example, a wire that is to be finished in the annealed condition on a diameter of 0.040 in. is commonly subjected to a final reduction of 90 per cent between the last two anneals, the large reduction being accomplished in the successive drafts of a multiple-die machine. Wire for rivets, for instance, on 0.125-in. diameter, although given a slight reduction of about Io per cent after the final anneal, may have been given a prior reduction of 75 to 80 per cent. Barrettl states the fiber axis of annealed 70-30 brass wire to be [111], with some indication of [IOO] as a secondary fiber axis. Croft and Sachs2 have reported briefly on some differences in brass wire with random and with preferred orientations. They showed statistical plots of the twin-band angles with respect to the wire axis or direction of drawing as observed on an axial plane. They also pointed out that the resistance of the wire to corrosion-cracking when externally stressed and exposed to a mercurous nitrate solution decreased as the degree of the preferred orientation increased. Material and PRocedure All the wire for the investigation was processed from one portion as cut for extrusion from a cast billet of the following analysis: 70.13 per cent copper; 0.01 lead; 0.01 iron; 0.02, nickel; 29.83 zinc (by difference). The billet section, 8 in, in diameter, was extruded hot to 3/4-in. diameter, after which it was processed by alternate cold-drawing and annealing treatments as indicated in Fig. I. The earliest anneals in process were at about 1100°F. and the next to the last reductions by drawing were 58 per cent. The diameter of the finally annealed wire was 0.132 in. Semifinal anneals were at 800°F., 950°F. and 1100°F. and reductions of 47.5, 74, 83.5 and 89.5 per cent were employed in drawing to 0.132 in. The final anneals were at 87s°F., 1050°F. and 1250°F. and were

Jan 1, 1944

By H. l. Burghoff, J. S. Porter

This paper presents the results of an investigation of the effect of cold-working and annealing treatments upon the occurrence of preferred orientation in annealed brass wire. The subject has received less consideration than has the same phenomenon in annealed brass sheet or strip, and perhaps very properly so in view of the obvious and undesired results obtained in the forming or drawing of strip having preferred orientation, which results are in contrast with the lack of any spectacular visual evidence in wire. The factors of cold-working and annealing that control preferredness in strip are naturally expected to function similarly in wire. Indeed, one might expect the condition to be commoner in annealed wire, because the severity of the cold-working between anneals in commercial Practice is usually much greater for wire than for strip. For example, a wire that is to be finished in the annealed condition on a diameter of 0.040 in. is commonly subjected to a final reduction of 90 per cent between the last two anneals, the large reduction being accomplished in the successive drafts of a multiple-die machine. Wire for rivets, for instance, on 0.125-in. diameter, although given a slight reduction of about Io per cent after the final anneal, may have been given a prior reduction of 75 to 80 per cent. Barrettl states the fiber axis of annealed 70-30 brass wire to be [111], with some indication of [IOO] as a secondary fiber axis. Croft and Sachs2 have reported briefly on some differences in brass wire with random and with preferred orientations. They showed statistical plots of the twin-band angles with respect to the wire axis or direction of drawing as observed on an axial plane. They also pointed out that the resistance of the wire to corrosion-cracking when externally stressed and exposed to a mercurous nitrate solution decreased as the degree of the preferred orientation increased. Material and PRocedure All the wire for the investigation was processed from one portion as cut for extrusion from a cast billet of the following analysis: 70.13 per cent copper; 0.01 lead; 0.01 iron; 0.02, nickel; 29.83 zinc (by difference). The billet section, 8 in, in diameter, was extruded hot to 3/4-in. diameter, after which it was processed by alternate cold-drawing and annealing treatments as indicated in Fig. I. The earliest anneals in process were at about 1100°F. and the next to the last reductions by drawing were 58 per cent. The diameter of the finally annealed wire was 0.132 in. Semifinal anneals were at 800°F., 950°F. and 1100°F. and reductions of 47.5, 74, 83.5 and 89.5 per cent were employed in drawing to 0.132 in. The final anneals were at 87s°F., 1050°F. and 1250°F. and were

Jan 1, 1944

By Robert Pike

THE first authentic description of an iron bath for the deposition of iron is probably that of Bottger in 1846, who used a bath containing ferrous sulfate and ammonium chloride. In 1861, Kramer deposited iron from ferrous chloride solution. Electrolytic iron was produced in 1.869 by Bietz, who used it for making some magnetic tests. In the same year, Klein is said to have worked out his process. Jacobi1 in 1869 described the results obtained in electroplating with iron on copper for making dies and plates for bank notes, by Klein&apos;s process. A letter from Klein to Jacobi describes the bath more fully. It consisted of FeSO4 + (NH4)2S04. Lenz2 described ?some properties of electrolytically precipitated iron. He used Klein&apos;s bath, FeSO4 + MgSO4 + MgCO3, to neutralize and obtained fine-grained and hard iron. His conclusions were as follows: 1. Electrolytic iron and copper contain gases, notably hydrogen. 2. The volume of gas absorbed by iron varies within wide limits, but it is easy for iron to take up very considerable quantities of gas. 3. The absorption of gas is principally in the first formed layers of iron. 4. When iron is heated, gas begins to come off below 100°, principally hydrogen. 5. Heated to redness, reduced iron oxidizes in water, in part at least at the expense of the oxygen of the water, decomposing it and setting free hydrogen, which is partly or wholly absorbed. Siemens,3 in 1889, was the first to propose a general process embodying a step for leaching a sulfide mineral with ferric chloride or sulfate and a step for regenerating the leach and depositing iron on a cathode in a diaphragm cell. So far as is known, Siemens did not carry out his patent

Jan 1, 1930

By George Holderer

THE Enos Coal Mining Co. owns an area underlaid by coal, of approximately 5000 acres. This property is situated 9 miles from Oakland City, in the southern part of Indiana. The mine has been in operation 5 years, during which time some 350 acres have been stripped, and stripping is now proceeding at the rate of about 100 acres per year. TOPOGRAPHY These coal lands consist of gently-rolling agricultural fields which in times past were farmed for wheat. There is no timber and but very little brush to contend with. The overburden varies from 10 to 60 ft. in depth. A thin bed of slate overlies the coal, followed by limestone, which varies from 3 to 15 ft.; this, in turn, is followed by sandstone, slate, shale and clay. There is a very wide variation in the thickness of all of these beds. The coal has an average thickness of 5 ft., and is a good grade of high-volatile bituminous. MINING OPERATIONS Briefly, the sequence of operations is: drilling holes with churn drills; blasting with L. 0. X.; stripping overburden to uncover coal and, finally taking up the coal, which is sent to a tipple for cleaning and sizing. In order to show what is being accomplished by the use of L. 0. X., results will be shown from May to November, 1926, inclusive, and compared to the same period in 1925. No work was done in No. 1 pit during May, 1925, hence all figures are unduly low for this month. Drilling There are in use 8 No. 44 Loomis clipper drills, caterpillar traction with gasoline engines; recently these were equipped with extra heavy stems, measuring 26 ft. overall and 4 ½ in. dia., to increase the speed of drilling. In addition, 4 No. 1 ½ G non-traction drills have been acquired, and are used to save the time of the larger drills when recleaning is necessary.

Jan 1, 1927

By George Holderer

THE Enos Coal Mining Co. owns an area underlaid by coal, of approximately 5000 acres. This property is situated 9 miles from Oakland City, in the southern part of Indiana. The mine has been in operation 5 years, during which time some 350 acres have been stripped, and stripping is now proceeding at the rate of about 100 acres per year. TOPOGRAPHY These coal lands consist of gently-rolling agricultural fields which in times past were farmed for wheat. There is no timber and but very little brush to contend with. The overburden varies from 10 to 60 ft. in depth. A thin bed of slate overlies the coal, followed by limestone, which varies from 3 to 15 ft.; this, in turn, is followed by sandstone, slate, shale and clay. There is a very wide variation in the thickness of all of these beds. The coal has an average thickness of 5 ft., and is a good grade of high-volatile bituminous. MINING OPERATIONS Briefly, the sequence of operations is: drilling holes with churn drills; blasting with L. 0. X.; stripping overburden to, uncover coal and, finally taking up the coal, which is sent to a tipple for cleaning and sizing. In order to show what is being accomplished by the use of L. 0. X., results will be shown from May to November, 1926, inclusive, and compared to the same period in 1925. No work was done in No. 1 pit during May, 1925, hence all figures are unduly low for this month.

Jan 2, 1927

By Martial P. Corriveau

Almost everyone agrees that coal and oil shale are the only fossil fuel resources in which the United States is self-sufficient. Of the two, only coal has a technology sufficiently developed to be of intermediate term benefit. Since it takes at least 20 years to bring advanced technology into practice, it seems logical that the major focus on energy developments should be aimed at coal. Meanwhile, we need to trade-off between actions to meet our immediate needs and the various political regulations and social demands that are disrupting the coal industry and the industries dependent upon it. The largest single user of coal is the electric power generation industry. Over 300 million tons of coal are presently being consumed each year. In view of the 5-to 7-years lead time to bring in a base-load fossil-fuel fired generating station, our requirements for double this tonnage in 1980 are already well forecast; that is, if the coal companies are allowed to mine and the utilities are allowed to burn the coal.

Jan 2, 1974