By A. G. Metcalfe, A. Siede

The hardening of annealed copper during fatigue testing appears to be independent of the applied stress and to occur largely within the first 4000 cycles. Copper hardened by fatigue is more resistant to annealing than copper hardened by static means, and softens by a multistage process. Creep studies at 300°C show that copper hardened by fatigue also has greater resistance to creep than statically hardened copper. Some theoretical explanations are discussed. RECENT interest in the behavior of metals subjected to fatigue stems from observations of phenomena which could not be explained by current theories of the structure of metals. In 1953 Bullen et al.l showed that the hardening caused by fatigue at low stresses did not cause severe bending of the lattice as did hardening by static methods. This was later confirmed by Wood, 'and Broom and Ham.3 Clarebrough et al4 showed that as the stress level used in fatigue hardening was increased, bending of the lattice was introduced, eventually approaching that of metals deformed by conventional cold-working methods. The type of hardening introduced by fatigue has other interesting characteristics. Kemsley5 showed that copper fractured by fatigue at low stresses resisted annealing as compared to copper hardened an equal amount by static means. The work of Clarebrough etal, shows that the manner of energy release during annealing differs for fatigue-hardened and statically hardened metal in both magnitude and temperature range of release. In addition to hardening of the lattice, fatigue has been shown to cause softening in materials previously hardened by static methods,5 and also in age-hardened alloys.7 The superposition of a small fatigue stress on the static loading of high-temperature alloys has been shown to increase their resistance to creep.' The present work was an attempt to determine the relationship between fatigue hardening, resistance to annealing, and the creep properties of pure copper. EXPERIMENTAL PROGRAM The program described here was designed to answer three questions: 1) Can stress-cycle combinations well below the failure values give significant increases in hardness? 2) Does hardening, under different stress-cycle combinations, give increase resistance to annealing? And if so— 3) Does superior resistance to annealing confer superior creep properties over statically hardened material? Three-quarter hard OFHC copper was annealed in vacuo at 550°C for 1 hr to produce a strain-free material having a fine grain size and uniform hardness. (The standard deviation of the mean hardness of the annealed samples was less than + 1.9 Dpn). Annealing was performed after machining the fatigue specimens so as to avoid work-hardened surfaces. Jigs were used to avoid distortion. The fatigue properties of the annealed copper were determined using an accurately aligned Baldwin-Sonntag SF1-U machine operating at 1800 cycles per min. This limited the minimum number of cycles which could be examined to about 4000 stress reversals. Since failure resulted in specimen damage, hardness increase with number of cycles was measured by testing specimens fatigued to different fractions of the failure values. The results are shown in Fig. 1, and are superimposed on the S-N curve of the copper in Fig. 2. The resistance to annealing of fatigue-hardened material was compared to that of material hardened by uniaxial tensile straining. Specimens hardened to equal values by both methods were progressively annealed for 1 hr at temperature in vacuo. After each annealing treatment the hardness was measured using a Leitz Durimet hardness tester with a 500-g load. At least five tests were made for each hardness determination. The standard deviation for individual specimens varied from 0.26 to 1.48 hardness points. The results are shown in Figs. 3 to 5. The discontinuous nature of the annealing process has been brought out by drawing idealized curves through the data points. This can be justified by the consistency of the results as well as by general agreement with results of Kemsley.5 The creep resistance of fatigue-hardened and

Jan 1, 1960

By J. Chipman, J. C. Fulton

Reduction of Si from slag to carbon-saturated iron is a very slow reaction. The rate is nearly independent of stirring but is accelerated markedly by increased temperature. In a slag containing 45 pct SiO2, 38 pct CaO, 17 pct Al2O3, the energy of activation is approximately 130 kcal. AT temperatures of 1450" to 1600°C occurring in the hearth of the iron blast furnace, chemical reactions are normally expected to proceed with great rapidity. Many of the reactions of iron making are indeed quite rapid and attain a condition corresponding roughly to a state of equilibrium before metal and slag are tapped from the furnace. The one conspicuous exception is the reaction by which carbon in the coke or metal reacts with silica in the slag to deliver silicon to the metal. From the practical viewpoint the slowness of this reaction is indeed fortunate, for if it were fast enough to reach equilibrium during the time of contact, it would be difficult to produce pig iron of the desired low silicon content. The one other reaction which under certain circumstances can also be very slow is the transfer of sulfur from blast-furnace metal to slag. In their laboratory exeriments on this reaction, Hatch and Chipman found that at least 5 hr were required for the attainment of equilibrium in a small crucible and that the reaction was not accelerated by increasing the rate of stirring. Subsequently it was shown2 that the presence of a reducible oxide MnO greatly inhibited sulfur removal, and finally that SiO2 itself3 under some conditions has sufficient oxidizing Dower to interfere with sulfur transfer. The kinetics of sulfur removal are now rather well understood,4 and it has been shown3,5 that when the silicon content of the metal is high enough to prevent reduction of SiO,, the desulfurizing process is rapid. Thus the observations of slow removal of sulfur are associated with the coincident slow reduction of SiO2, a process which transfers both silicon and oxygen to the metal phase. It is, of course, the oxygen which interferes with sulfur removal. An explanation of the slowness of the silica reduction reaction has not been obtained. The sulfur transfer process has been shown by the authors5 to be at least partially transport-controlled in the absence of interference by silica. Under the experimental conditions. 99 pct of the total transfer at 1600" was accomplished within an hour. Under similar conditions the reduction of silica may not proceed half-way to equilibrium6 in 8 hr. It is scarcely imaginable that silica reduction could be transport-controlled when the slag contains 44 pct SiO2 and the metal about 1.4 pct C. The experiments reported here show definitely that it is controlled by a slow step or steps in the chemical reaction. One might expect to find such a slow step in the breaking of SiO bonds or in the slow removal of oxygen by carbon at the slag-metal or metal-crucible interface or by bubble formation. EXPERIMENTAL PROCEDURE The experimental procedure used in this investigation was similar to that used in the study of the kinetics of desulfurization.5 A sketch of the graphite crucible and stirrer used in the current work is shown in Fig. 1. The quantity of metal and slag used was adjusted so that the slag-metal interface was located between the top and bottom blades on the stirrer; the top of the slag layer was above the top blade. The stirrer shaft was hollow down to the metal level and served as thermocouple well or optical pyrometer target. Stirring speeds of 0 to 500 rpm were used. A carbon monoxide atmosphere was maintained in the furnace by flushing the gas over the slag surface, except in run No. 220 when it was bubbled

Jan 1, 1960

By Elmars Ence, Harold Margolin

The titanium-aluminum system has been investigated in the composition region 0 to 34 pct Al in the temperature range 800" to 1450°C. The phases encountered in this region were: a,ß, TiAl3, The reactions observed are as follows: 13 ; L - 6T. A1, 0 (15 pct Al) + 6 (18 pct Al) - yTi Al (16.5 pct Al) at -1170°C andP (7 pctpct Al) + y (9.2 pet Al) - ah(9 pct Al) at - 1060°C. A eutectoid reaction: y — a +d belm 700°C is postulated. THE Ti-A1 system has been the sub.ect of a number of investigations. Several of these1-3 have indicated extensive solubility of A1 in both a and ß titanium. Ence and Margolin, as a result of work on the Ti-A1-0 system:'5 have shown that the a solubility ofalumi-num is considerably restricted, and found that a compound, Ti2A1 existed in the region formerly designated as Q a This structure was identified as hexagonal with c/a = 0.803. Pietrokowsky confirmed the existence of this phase7 and pointed out that the structure was isomorphous with Ti3Sn.8 Although the existence of Ti,A1 has been confirmed by others,9-12 there has been considerable disagreement regarding the composition and mode of formation. A detailed reinvestigation of the Ti-A1 system has been published by Sagel et al.13 The tentative diagram indicated two phases, a, and e, occurring in the former all a region. The a, phase has the same structure as Ti2A1 and was indicated as having a broad region of solubility. Epsilon, a tetragonal phase, was shown to form within the a, solubility region. AS a result of unpublished work,14 Ence and Mugy3 olin disagreed with the interpretation of Sage1 et al., although some common features existed. The present study was conducted in an attempt to clarify prevailing uncertainties. EXPERIMENTAL PROCEDURE Alloy Preparation—Alloys were prepared from iodide titanium (99.9 pct Ti with less than 0.01 pct Zr) or Bureau of Mines electrolytic titanium (BHN-73) and high purity aluminum (99.99 pct). Alloys were arc-melted in argon or helium atmosphere as 15-g buttons in the composition range up to 34 pct Al. Depending on need, alloys were made in increments varying from 0.25 to 2 pct Al. Up to five 15-g buttons of some compositions were made. Weight losses during melting did not exceed about 1 pct of the charge and chemical analysis revealed that both titanium and aluminum were evaporated. In general, nominal and analyzed compositions agreed within 0.5 pct and therefore nominal compositions were used in plotting the data. Unavoidably, some overlap of composition occurred, particularly where small increments of A1 were used. The small increments were primarily used to obtain alloys which would fall into the narrow a -, r region and this purpose was achieved. In general, the data obtained from Bureau of Mines base titanium and iodide titanium alloys were in agreement. Forging—Both as-cast and forged samples were employed. Samples were heated for hand forging by an oxygen-hydrogen torch to the region 1200" to 1300°C. A titanium anvil and cover plate were used to prevent any iron pick-up and consequent formation of a low melting point compound. Frequent reheating kept the temperature in the desired range. Under these conditions, alloys containing up to 15.5 pct could be successfully forged. To check on the depth of contamination, forged alloys were heated slightlybelow the ß transformation temperature. Metal was removed to a depth below the contaminated surface so revealed, and the subsequent results obtained from these samples agreed closely with those secured from as-cast material. Heat Treatment—Prior to heat treatment, all alloys were vacuum annealed to remove hydrogen. Samples

Jan 1, 1962

By W. N. Miner, R. O. Elliott

Electrical-resistivity )measurments were made be-trueetz room temperatrive and 1.5 oK on five different stocks of cerium metal, and the results were correlated with the types, amounts, and distribution of the impurities present. Magnesium, which appeared to be distributed as a solute throughout the cerium matrix, was found to have a large effect on the residual resistivity, 1 at. pct Mg being sufficient to increase the residual resistivity by about 10 microhm-cm. The formation of ß by repeated thermal cycling between room temperature and liquid-helium temperature is attributed to the deformation and faulting that occurs during the ? D a transformation. In preparation for starting a proposed study of cerium-rich alloys, we examined samples from severa1 stocks of cerium metal in order to choose the purest stock for future use in making the alloys. Low-temperature electrical-resistivity data were used to gain initial information about the purities of the stocks. Additional information was subsequently obtained from chemical analyses, density measurements, optical metallography, and electron-micro-probe analyses. Cerium that has been annealed at high temperature and cooled to room temperature has the fee crystal structure (? phase) with a = 5.16Å. When cooled further, in the region between about 250" and 150°K, some of the fee phase transforms to the double hcp form (ß phase) with a = 3.68 and c = 11.92Å. The remainder of the room-temperature fee form (and perhaps some of the hexagonal phase) transforms electronically in the vicinity of 100° K to the more dense or "collapsed" fee form (a phase), a - 4.85A, by transferring about 0.5 electron per atom from the 4f level to the valence band. Very little work related specifically to the effects of impurities on the physical properties of cerium has been reported in the literature. Gaume-Mahn1, 2 has studied the effects of calcium, magnesium. iron, silicon, and tantalum on the electrical resistivity and magnetic susceptibility of cerium between 60o and 300°K. Gschneidner, Elliott, and McDonald3 have discussed the effects of total impurity content on the hysteresis of the a —? (reversible) transformation and on the formation of the 4 and "a-? intermediate" phases. Smith and Morrice* have reported the effect of total impurity content on the resistivity of cerium at 4 and 293°K. In none of these reports, however, is it apparent that the distributions of the impurities were determined, L.r., whether the impurities were present in inclusions or in solid solution in the matrix is not mentioned; nor does it appear that the phase purity of the cerium was always considered. In the present study, five different stocks of cerium were involved. One was represented by a single sample of electrowon cerium, which was all that had remained from a stock of high-purity material obtained from the U.S. Bureau of Mines, Reno, Nev., in 1959. The other four stocks were recently purchased from commercial sources and were specified to be 99.9 wt pct pure. EXPERIMENTAL Cerium stocks designated as #1, #2, #4, and #5 were obtained from commercial suppliers for the specific purpose of finding a reliable source of high-purity cerium. Although the purity level of the cerium was specified to be 99.9 pet, the specifications did not include limits as to the amounts of various impurities that would be acceptable. Consequently the chemical analyses of the different stocks varied widely. Stock #3, which had been obtained from the U.S. Bureau of Mines and which was the purest on the basis of chemical analyses, consisted of a single specimen of electrowon cerium. It was included in the examination for purposes of comparison. Table I contains the chemical and spectrographic-

Jan 1, 1968

By J. F. Smith, J. R. Ogren, N. J. Magnani

The uapor pressrcres of magnesium over binary alloys of magnesium with twelve of the yare-earth eletnetzts have been measured by the Knudsen effuion method in the temperature range 675° to 910°K. These vapor-pressure measurments were combined with data concerning the tevtrlitzul magnesium solubility and the vapor pressure of pure magnesinm to evaluale the standuvd free energies of pluase jormation. These free-etzergy values indicate that the CsCl structures of the heacy rave earths tend to be somewhat less stable than those of the light rare earths. This dif-]eying- behaviov covrelates with differences which have been obsevz~ed in other alloy systetns wherein a phuse appeurs, disappeavs, or changes crystal stvucture as the atomic number of the rare-earth com-ponent is changed. This behauior also appears to correlate with the struclurul rariations within the rare-earth elements themselves, and it is speculated that cariations in the spatial extent of the 4f orbitals are responsihle. STUDIES of the phase relationships and crystal structures in the binary systems between rare-earth metals (lanthanons) and magnesium are extensive but far from complete. However, the currently available information1-10 does produce a rather interesting pattern. This is illustrated in Table I. If one excludes europium and ytterbium from consideration because of their generally atypical behavior, it can be seen from the table that the phase relationships in the magnesium-rich regions show a distinctly different pattern for the lighter lanthanons as compared to the heavier lanthanons. For the lighter lanthanons, LnMg2 phases occur from lanthanum to gadolinium with the cubic MgCu2 structure, LnMg3 phases occur from lanthanum to terbium with the BiLi3 structure, and magnesium-rich phases occur from lanthanum to gadolinium with stoi-chiometries between Ln5Mg42 and LnMg12. In contrast, for the heavier lanthanons, those LnMg2 structures which have been examined have the hexagonal MgZn2 structure, LnMg3 phases have not been observed beyond terbium, and the magnesium-rich phases occur with the a manganese structure near a stoichiometry of Ln5MgZ4. The heavy lanthanon-magnesium systems thus appear to be analogous to the Y-Mg system""2 wherein YMg has the CsCl structure, YMg2 has the MgZn2 structure, and the region Y4Mgz5-Y5Mg24 has the a manganese structure, and no other intermediate phases are observed. Similarity in alloying behavior between yttrium and the heavy lanthanons occurs commonly, and on this basis it seems likely that LnMg2 phases will be found with the MgZn2 structure in the binary systems of dysprosium, thulium, and lutetium with magnesium when the appropriate investigations are made. In the case of the magnesium-rich phases of the lighter lanthanons, only the Ce-Mg phase relationships have been investigated thoroughly and in detail, and until similar investigations are made for the other systems there will remain questions as to which magnesium-rich stoichiometries represent equilibrium phases and what systematic variations occur in the sequence from lanthanum to gadolinium. Thus the data in Table I show that only the LnMg phases occur with the same crystallographic structure throughout the sequence from lanthanum to lutetium. It was speculated that the relative stability of these LnMg phases might vary from one lanthanon to the next in such a way as to presage the differences which occur among the more magnesium-rich lanthanon-magnesium phases. On this basis the present investigation of the thermodynamics of phase formation was Gndertaken for the LnMg phases. PROCEDURE AND RESULTS A generalized phase diagram for the lanthanon-rich portion of a lanthanon-magnesium alloy system is shown in Fig. 1 where ß represents a high-temperature bcc

Jan 1, 1968

By K. D. Jacob, W. L. Hill

Fluorine recovery in the United States has been restricted chiefly to manufacture of ordinary superphosphate and wet-process phosphoric acid. However, there is an expanding use of fluorine by industry in the form of hydrofluoric acid. Improved methods for recovering fluorine from phosphate rock would yield an adequate supply of fluosilicates and a substantial contribution to the hydrofluoric acid requirement. THE bulk of natural phosphates is comprised of calcium phosphates, which are usually apatites;' calcium aluminum phosphates such as pseudowavel-1ite; and aluminum phosphates, which occur in extensive deposits, notably on Grand Connetable Island." Nearly all deposits of current commercial value are apatite, often with admixed material of other classes. In the trade coarsely crystalline material, mainly fluorapatite of igneous origin, moves as apatite, whereas the fine-grained material of sedimentary origin is marketed as phosphate rock. The latter classification includes the phosphate shales in western North America. Although several genetic varieties of phosphate rock are recognized, most known reserves are of marine origin. Calcium phosphate is concentrated from Florida land pebble and Florida hard rock deposits and from Tennessee brown rock deposits. Phosphate Rock as a Fluorine Carrier: More than two decades ago Reynolds and Jacob surveyed the fluorine content of commercial phosphate rock from various parts of the world. Later these samples were re-analyzed by a new and more reliable method of determining flourine. The revised results with interim additions of new samples, published a few years ago in a brief summary," are shown in Figs. 1-3. Through the points representing the respective varieties of rock medial straight lines are drawn. In some instances the lines are well defined by the points; in others, where scattering renders the position of the best line uncertain, the greater weight is given points near the end of the covered range. Wherever distinct varieties are not recognized among regional deposits the custom is to identify the sample with the geographical location of the deposit. Although all rock varieties cannot be classified with certainty, the plotted results exhibit three distinct types of rock in which the F to P2O5 ratio diminishes, remains sensibly constant, and increases, respectively, as the grade of rock increases. Existence of two types of Florida land pebble, Fig. 1, is supported by additional results recently supplied by a producer." Generally speaking, phosphate rock from continental deposits carries considerably more fluorine, and apatite and insular phosphates less, in proportion to the phosphorus content than is required by the formula for fluorapatite. Exceptions to this are apatite from Canada and certain samples of Florida waste-pond phosphate. The manner in which excess fluorine is held and the nature of the carbonate in carbonate apatite are discussed in recent articles. High-grade calcium phosphates with F to P2O5 ratios less than 0.05 have been found in Curacao, Christmas Island," Mexic,13 and elsewhere. The calcium aluminum phosphates and aluminum phosphates aften carry notable amounts of fluorine. The F to P2O, ratio for one sample of pseudowavel-lite concentrate was 0.05." Aluminum phosphate from Grand Connetable Island is very low in fluorine, whereas some aluminum phosphate minerals" carry as much fluorine as highly fluorinated phosphate rock. Fluorine in Domestic Phosphate: The curves shown in the figures permit interpolation of the F to P2O5 ratio corresponding to the midpoint of selected ranges in grade of any one of the several varieties of phosphate. Multiplication of the interpolated ratio by the mid-range grade (P2O5) yields a figure for the percentage of fluorine in this grade. Then, with the use of the mid-range grade, the amount of fluorine held in phosphate reserves can be estimated, see Table I. Accordingly, on Jan. 1, 1950, the fluorine complement of known domestic reserves exceeded 420,000,000 long tons of the element. A previous figure," deduced in 1940 by a simpler procedure

Jan 1, 1955

By R. D. Vaughn

The analysis of laminar flow of power-law non-Newtonian fluids in narrow, eccentric annuli is employed in this paper to discuss the problems of lubricant flow in journa! bearings and of errors introduced by eccentricity in experimental studies with concentric annuli on extruders and wellbore annuli. The velocity profile and pressure loss-flow rate equations are developed for the laminar flow region. In addition, the expected error in flow rate and pressure-loss measurements for concentric annuli as a result of eccentricity is determined. For example, a 10 per cent displacement of the core of an almost concentric annul us would cause a 1.8 per cent decrease in the observed pressure loss for a fluid with a power-law exponent n of 0.25. The corresponding increase in the observed volumetric flow rate would be 7. 5 per cent. INTRODUCTION Non-Newtonianism and eccentricity occur simultaneously in two engineering problems: (1) flow of lubricants in journal-bearings and pressure-reducing bushings, and (2) flow of non-Newtonian fluids in plastic extruders and wellbore annuli. The lubricants used for moving parts are often non-Newtonian in character — often they are plastic in behavior. A solution to the problem of flow of non-Newtonian fluids in narrow eccentric annuli is particularly pertinent to this problem. In all experimental studies of laminar flow of fluids in concentric annuli, such as in extruders and well casings, the error due to eccentricity must be estimated or studied. A number of publicationsl-4,6,7 have dealt with this problem for Newtonian fluids; however, I am not aware of work for non-Newtonian fluids. This work is directed to the non-Newtonian problem. Before the solution to the problem is given, the pertinent conclusions from the work on Newtonian fluids will be reviewed. Heyda 1 and Redberger and Charles 2 have published general solutions to the problem of the laminar flow of Newtonian fluids in eccentric annuli, apparently without knowing of the earlier work of Ca ld well 3 and Bairstow and Berry,4 which is reported by Dryden, et al. 5 Although several mathematical routes are encompassed by the work of these authors, the results appear to be equivalent. Redberger and Charles2 show that the error caused by eccentricity in concentric annuli is negligible for small diameter ratios (k < 0.5); however, for large diameter ratios (k + l), the error in the predicted flow rate can be as great as 100 per cent or more. Partial solutions to the problem are available from the work of Dryden,5 Tao and Donovan6 and Piercy, et a1.7 Tao and Donovan examined the case of flow in narrow, eccentric annuli (k + 1) with and without rotation of the annular core. These authors also reviewed previous work on this subject and verified their approach with experimental data. Dryden gives the solution for the limiting case of complete eccentricity or tangency. Piercy, et a l. published an early solution to the problem of narrow eccentric annular flow. The conclusions of Redberger and Charles2 and the experimental proof of Tao and Donovan6 both suggest that the region of large diameter ratios (k + 1) is of main interest and that the parallel planes approximation to the solution in this region is satisfactory. This method will now be extended to the laminar flow of non-Newtonian fluids in narrow eccentric annuli. THEORETICAL SOLUTION The geometrical aspects of the problem are illustrated in Fig. 1. To represent the non-Newtonian fluid the power-law model was selected. This model has many disadvantages which have been pointed out; nevertheless, its simplicity, its frequent and wide applicability justify its use in this work. Fredrickson and Bird8 and Savins9 have used it as a basis for a theoretical study of laminar flow of non-Newtonian fluids in concentric annuli.

Jan 1, 1966

By E. C. W. Perryman

IN spite of the large amount of work which has been carried out on the recrystallization of aluminum and its alloys, there has been no complete investigation of the recrystallization characteristics of A1-Mg alloys. The most complete investigation is that reported by Bungardt and Osswald&apos; who, working with commercial-purity materials, found that the temperature both of beginning and of complete recrystallization increased with magnesium content up to about 2 pct Mg, then decreased with a further increase in magnesium up to 5.0 pct, and thereafter increased again. Michaud and Segolz working with 99.93 pct A1 also found the temperature of beginning of recrystallization to decrease as the magnesium content increased from 2.13 pct to about 4.5 pct. Chossat3 using aluminum of 99.99 pct purity found that 0.12 pct Mg had no effect but that 0.4 pct Mg increased the recrystallization temperature by about 30°C. That no effect was found for 0.12 pct Mg does not agree with the later results reported by Demer and Beck4 who found that 0.025 pct Mg in 99.99 pct A1 increased the time for complete recrystallization and furthermore increased the activation energy for the recrystallization process. Kratz" using 99.997 pct A1 found that 0.5 pct Mg increased both the temperature of beginning and of complete recrystallization by 100°C. Chadwick and Hooper" working with commercial-purity material found that 1 pct Mg increased the temperature of complete recrystallization by about 40 °C for cold reductions in the range 17 to 72 pct. With smaller amounts of cold work produced by stretching (10 pct strain), they found no significant effect of magnesium. The latter result agrees with that obtained by Williams and Eborall&apos; who found no effect of 2 pct Mg on the recrystallization temperature of commercial-purity aluminum strained 10 pct or less by stretching. Experimental Procedure Material Used: The chemical analyses of the materials used throughout this investigation are given in Table I. Fabrication: The alloys were cast in iron molds which had been washed thoroughly with alumina. After scalping, the ingots were annealed for 16 hr at 450°C, pressed, annealed at 450°C for 16 hr and hot rolled to 0.25 in. After hot rolling, the slabs were alternately annealed and cold rolled to 0.036 in. Cold-rolling reductions between intermediate anneals were kept at about 30 pct and a high intermediate annealing temperature of 450°C was used so as to obtain, as nearly as possible, similar starting grain sizes for the different materials. All intermediate anneals were done in a salt bath and were followed by cold-water quenching so as to retain all the magnesium in solid solution. The final cold reductions investigated were 20, 30, 40, 50, 60, and 80 pct. The initial grain sizes, that is, the grain size before the final cold reduction, were all very similar. Annealing Procedure: Specimens, 1 in. sq, were cut from the 0.036 in. sheet and annealed in a salt bath, the temperature of which was controlled to k2"C. Separate specimens were annealed for different times at 350°, 375", 400°, and in one or two cases at 415°C and after annealing were quenched in cold water. The time taken for a specimen to reach temperature was approximately 5 sec. Metal-lographic examination after annealing showed that no precipitation of Mg+413 occurred during cooling. Procedures Used for Determining Recrystallization Characteristics: All specimens were electrolyti-cally polished and etched by the method described previously1° and polishing was continued until about 0.002 in. had been removed from each side of the specimen. Using this technique, the smallest recrys-tallized grain which could be observed with cer-

Jan 1, 1956

By G. Derge, Ling Yang, John Henderson

Self-diffusion coefficients of aluminum have been measured by the capillary reservoir technique in liquids of the CaO-SiO2-Al2O3 system containirg equimolar portions of CaO and SiO2, in the temperature range 1400o to 1520oC. For the melt containing 6.0 mole pct Al2O3 the results can be expressed by the equation D = [(4.3 * 0.3) x 104] exp [(-85,000 * 17,500)/RT]cm~sec-&apos;; for the melt containing 12.5 mole pct Al2O3, by the equation D = (5.4 i 0.2) exp [(-60,000 * 10,00O)/RT] cm2sec-: A concept of the constitution of these melts has been developed which proposes that the ratios O/(Si +Al) and Al2 O3/CaO determine the dominant species present. In recent years considerable work has been done on the system CaO-SiO2-A12O3 with a view to elucidating the structure of liquids of this system. Conductivity,&apos; electromotive force, 3 density,4 and activity5 measurements have all contributed to an understanding of the problem, but as yet there is no entirely satisfactory theory that can account for all the observed experimental results. In principle, measurements of self-diffusion coefficients should give further information which is not obtainable in other ways. Self-diffusion coefficients for calcium, silicon,6 and oxygen7 have been measured. The present investigation extends the series of self-diffusion coefficient measurements to include aluminum and develops a concept of constitution for liquids of this system which is compatible with all the observed experimental results. EXPERIMENTAL The technique used in the measurement of the self-diffusion coefficient of aluminum was the capillary-reservoir method,8 A126 being incorporated in the melt contained in the capillary and inactive aluminum in the reservoir melt. This method was chosen because it minimizes convection currents&apos; in the diffusion zone. It has the further advantage that the boundary conditions are such that a slight modifica- tion of Anderson and saddington&apos;s8 solution of Fick&apos;s Law yields an equation which requires measurements only of the length and the initial and final average specific activities of the solidified melt within the capillary. where t is the diffusion time, Co is the average specific activity of the melt contained in the capillary at t = O, C is the average specific activity of the melt contained in the capillary at t = t, 1is the length of the capillary, and D is the self-diffusion coefficient. The equation is of somewhat different form than those previously applied to high temperature diffusion studies because the specific activity of the melt in the reservoir was negligible both before and after diffusion. The diffusion apparatus is shown schematically in Fig. 1. It consisted of a silicon carbide resistance furnace containing the inactive melt in a graphite crucible, internal dimensions 7/8 by 4 in., enclosed in a 1 1/4- by 1 1/2- by 30-in. McDanel tube. A 3/8-in. McDanel thermocouple sheath to which graphite radiation shields and a graphite protection tube were affixed, was used to hold the capillaries. By moving this sheath through a rubber seal at the top of the McDanel tube the capillaries could be lowered into or raised out of the melt. Temperature was measured with a Pt-Pt 13 pct Rh thermocouple which was calibrated periodically against a standard couple. The furnace temperature was controlled to ± 5°C through the thermocouple immersed in the melt. Temperature variation over the depth of the melt was less than ± 3°C. The inactive melts were prepared from pure native quartz, assaying better than 99.9 pct SiO2, A.R. grade A12O3 and A.R. grade CaCO,. The same quartz and CaCO3 were used in preparing the active melts, the

Jan 1, 1962

By L. Hartsell Cash

INTRODUCTION Created in 1944 to help rebuild those economies, principally in Europe, which were seriously damaged or destroyed during the Second World War, the World Bank--or to use its correct name, the International Bank for Reconstruction and Development-began its operational phase by making a loan to the Government of France to accomplish two tasks: (i) to import coal for space heating purposes; and (ii) to buy new machinery and equipment to help rehabilitate its coal mines. Once the thrust of reconstruction in postwar Europe was largely accomplished, the World Bank Group (for today the World Bank has three separate lending windows) turned to mobilizing funds to improve living standards in developing countries, which remains its primary goal today. Over this period of time, the World Bank Group has continued to assist the world mining industry in various ways and, since 1955 the World Bank Group has financed mining or mineral processing projects with loans/credits totalling $1.5 billion. The World Bank Group consists of two institutions--the World Bank itself and the International Finance Corporation (IFC), which was founded as a separate institution in 1956 and three separate lending windows--the World Bank, the International Development Association (IDA), and IFC. The World Bank loans are provided at commercially-related interest rates but have grace periods usually of up to 3 to 5 years and repayment periods ranging from around 15 to 20 years. Since the World Bank raises its operating funds on the international capital markets in varying currencies and in varying interest rates, it relends a basket of currencies at floating interest rates which are fixed every six months to reflect the Bank&apos;s own borrowing cost. At the present time, the interest rate is just below 10% per year and in addition, a one-time front-end fee of 1/4 of 1% is charged. Also, a commitment fee of 3/4% per year is charged on the undisbursed amount of the loan itself. For loans to industrial and mining projects, it is normal to charge an additional guarantee fee of 1 to 1.5% in addition to the annual interest rate. This guarantee fee is payable to the government of the country in which the project is carried out since, by its charter, the World Bank is required to have the guarantee of the host government for each loan made in a specific country. By far the greatest source of lending funds within the World Bank Group is that of the World Bank itself and for the fiscal year ending June 30, 1984, the World Bank approved loans totalling $12 billion. The second lending window within the World Bank Group is IDA which performs the same functions as the Bank itself and has the same staff. Nevertheless, its loans (called credits) are made on much softer terms and are made to the poorest nations only. IDA funds are subscribed by the wealthier countries, usually as grants, and these are relent as credits to those countries with the lowest per capita income. IDA credits are made for 50 year periods, including 10 years of grace, to the government itself. The credits are interest free, but there is a service charge of 3/4% per year on the amount withdrawn and outstanding to defray the administrative costs of IDA. Credits approved during fiscal 1984 totalled $3.5 billion. The third lending window is IFC. While IFC is a separate corporation and operates quite separately from the World Bank and has its own staff and regulations, it works very closely with the World Bank on its overall approach to the mining sector and to a particular country. IFC&apos;s mission is essentially to supply venture capital and to stimulate development of the local private sector in capital markets as well as to promote the international flow of private capital to developing countries. Unlike the World Bank and IDA, the IFC does not lend directly to governments

Jan 1, 1985

By Maurice Lacasse, Pierre Legast

GENERAL OUTLINE For more than one hundred years, asbestos ore has been mined on Les Mines d’Amiante Bell&apos;s property at Thetford-Mines , Quebec, Canada. In 1878, the first tons of fibre were produced. The mine operated as an open pit until 1951 at a yearly production of about 330 000 mt of ore. Since 1951, the mine has operated underground using a block caving method. The mine produced 725 000 mt per year until 1978, when the rate of production was increased to 1 100 000 mt. The ore was produced entirely fm the first lift on 650 level until 1976. Then, a second lift on 950 level was put into operation to replace production facilities fm the first lift which is now exhausted. Annual fibre production is 72 500 mt with grades £ran 3 to 7. The total work force is 600 people. The host rock is a peridotite partially serpentinized. The asbestos fibre seams occur as stockwork deposit structurally controlled by talcose shear zone. The geological rock formations are heavily jointed and have a wide range of competence. Asbestos ore bodies have an heterogeneous nature which des difficult geological interpretation. THE GRIZZLY METHODS A full gravity method was used on the first level where the caved ore was drawn from finger raises onto grizzly bars spaced at 480 mn. Oversize blocks were reduced by secondary blasting. The ore fell by gravity in- to the ore pass below the grizzly chamber and was loaded into 5.7 mt haulage cars through a 1.2 m wide chute. Access to the undercut drift was fm the grizzly drift through finger raises. The undercut trough was drilled and blasted in a 1.2 m interval ring sequence into a slot situated at the end of each panel. The undercut stope was emptied through the finger raises. The undercut retreated from South to North at blast interval determined by the finger raises spacing. Fig. 1 represents the various steps involved with the grizzly method. Extraction drift dimensions were opened 1.8 m wide x 2.4 m high with anchor rock bolts and wire mesh where safety required them during excavation. Grizzly chambers were excavated at 2.4 x 2.4 x 4.6 m long on a 7.6 x 7.6 m grid spacing. Ore passes with dimensions of 1.5 x 1.5 m were developed from the haulage drift. On the extraction level, headings were drilled with jacklegs and cleaned by slusher into ore passes to the haulage chutes. The support used in the grizzly chambers was square concrete structure with 150 mn H beam reinforcement. The H beam was partially buried in the concrete and had one free face to allow for difference frequency of blast vibration between concrete and steel. The supported brow of the chamber had an opening 1.5 x 2.1 m. Ore passes were ring concreted 150 mn thick without any reinforcement. A 24 MPa compressive strength concrete was pumped and poured in pre-assembled forms. Based on the success of this method on the first level, the same layout was repeated on the second level. With the start of undercutting on the second lift, signs of deterioration were noticed in extraction drifts. At first, there was great concern as the operators were confident that standard repair techniques could cope with such a situation. An intensive program of support repair and a reduction of draw resulted. The following method of repairs were used: 1) Steel square sets of 150 mn H beam at 0.6 m intervals were installed. 2) This was reduced later to 0.3 m interval and eventually to a skin to skin steel structure. 3) Yieldable arches were introduced spaced at 0.9 m intervals, linked laterally with 150 m. H beam. 4) The yieldable arches spacing was then reduced to 0.46 m and eventually installed skin to skin. However, this support was not successful.

Jan 1, 1981

By M. Hansen, C. C. Wang

THE 6 phase of the Cu-Sn system (Cu,Sn, = 32.53 pct Sn) was considered to be stable down to room temperature until Owen and Iball showed by X-ray analysis that it undergoes a eutectoid decomposition into the a and e phases at a temperature near 300°C. Their findings have been confirmed by other investigators,2-5 a11 of whom used X-ray diffraction studies of powdered specimens. The transformation temperature has been reported by various authors as lying between 300" and 380°C. To our knowledge, no microscopic evidence of the eutectoid reaction has been published, as yet. It was in connection with other work that longtime annealings at 300°C were conducted with alloys containing 22, 32.6, and 35 pct Sn (nominal compositions) prepared from electrolytic copper and electrolytic tin and cast in a small iron mold. The specimens were first annealed at 700°C for 5½ hr and quenched from 400 °C after cooling to, and annealing at, that temperature for 9½ hr. After this treatment the sample with 22 pct Sn was cold worked for 15 pct reduction in thickness; the 32.6 and 35 pct alloys were too brittle to be cold worked. The final anneal at 300°C was done in a sealed pyrex glass bulb for 63 days. Fig. 1 represents the microstructure of the annealed alloy with 22 pct Sn. It shows primary a solid-solution crystals in a matrix of the (a + 8)-eutectoid formed at 520 °C. The a crystals contain 8 inclusions which precipitated from a due to the decrease in the solubility of tin in copper with fall in temperature. The decomposition of the 8 phase into a (light) and E (dark) can clearly be seen in some areas of the (a + 8)-eutectoid matrix. However, the decomposition is far from being completed, even after the long-time anneal used. Figs. 2 and 3 depict the microstructures of the annealed 32.6 pct alloy, which was intended to consist entirely of 6 phase. Due to some loss in copper on melting, the composition is slightly higher in tin. Accordingly, the sample after quenching from 400 "C consisted of grains of the 8 phase with the e phase arranged along the grain boundaries and as a Wid-manstatten precipitate within the 6 grains. After an annealing time of 63 days, the eutectoid decomposition, 6 + a + e, is still in its early, initial state. The pearlitic type of eutectoid is nucleated at the c crystals, preferably those surrounding the grain boundaries of the 8 phase. The appearance of the (a + €)-eutectoid in the 35 pct Sn alloy was very similar to that shown in Figs. 2 and 3. Again, the eutectoid decomposition nucleated at the 6 phase and proceeded from there into the 8 areas. As is evident from Fig. 2, the rate of decomposition of the 6 phase at 300°C is extremely sluggish: In the representative area shown only about 5 pct of the 8 phase has undergone the eutectoid trans- formation after annealing for 63 days. On the other hand, Owen and Williams2 have reported that X-ray photographs of powdered samples with between 17.5 and 34 pct Sn did not show 8 lines after annealing for only five to seven days at 300°C. This is in accordance with the fact that the rate of reaction in powdered samples is higher than in massive specimens, as a result of the excess free energy of the powder (due to its greater surface area). The authors wish to express their thanks to C. A. Johnson for preparation of the micrographs.

Jan 1, 1952

By A. J. Sedriks

ALTHOUGH the occurrence of a readily visible tarnish on the stress-corrosion fracture surfaces of titanium alloys tested in oxygenated nitrogen tetrox-ide solutions has been reported,&apos; the possibility that the formation of this tarnish is a requirement for cracking to proceed does not appear to have been considered. It has been proposed that failure occurs in this system as a result of some electrochemical-mechanical process.2 However, recent studies3-6 of the stress-corrosion cracking of a brass in certain ammoniacal solutions, which also cause visible tarnishing, have led to the view that failure occurs by the repeated formation and fracture of a brittle surface film of cuprous oxide. The purpose of this note is to point out the similarities which exist between the tarnish which forms on a brass and that found on titanium alloys failed in nitrogen tetroxide, and to suggest, by analogy, that a similar tarnish-rupture mechanism may be operative in the latter case. The titanium alloy selected for the present study contained 5.2 pct Al, 2.5 pct Sn, 0.025 pct C, 0.16 pct Fe, 0.014 pct N, 0.012 pct H, 0.07 pct 0, and 0.002 pct Mn by weight. Vacuum-annealed alloy strips measuring 4 by 0.25 by 0.04 in. were used to prepare self-stressed test specimens. Each specimen was made from two strips by bending the end portions and spot welding them together to produce curved sections of uniform bending stress. (The exact details of preparing such specimens have been described by Lisagor el al.7) The curvature in the strips determines the ma-magnitude of the outer fiber stress, which in the present specimens was 100,000 psi (yield stress = 120,000 psi). The specimen surface in the spot-welded end regions was shot-peened to induce compressive stresses and thereby eliminate the possibility of stress-corrosion cracking in these regions. The test environment was nitrogen tetroxide, initially containing 99.5 pct N2O4, 0.1 pct H2O, and 0.08 pct C1, through which oxygen had been bubbled for 30 min. During testing the tetroxide was subject to an oxygen pressure of 250 psi. The duration of the test was 96 hr, and during this time stress-corrosion cracks propagated through some 50 pct of the thickness of the specimens. After testing, the tarnish was liberated from the fracture surface by immersion in a methanol-5 pct bromine solution, and then examined by electron dif- fraction and transmission electron microscopy using a JEM-7 electron microscope. The possibility that the bromine solution had affected the structure of the tarnish was investigated by an "in silu" examination of the stress-corrosion fracture surface using a reflection electron diffraction attachment designed for handling bulk specimens. Typical areas of the tarnish liberated by the me-thanol-bromine solution are shown in Fig. 1. Fig. l(a) reveals that the tarnish consists of individual platelets, and from Fig. l(b) it can be seen that the platelets are joined together to form a semicontinuous film, the boundaries of the titanium substrate grains being retained in the tarnish. Electron-diffraction patterns taken from these areas exhibited diffraction spots typical of a monocrystal. The diffraction pattern shown in Fig. 2 was taken from the central area in Fig. l(n). Monocrystal patterns obtained from areas containing numerous individual platelets can only be explained by assuming that their growth is governed by the titanium substrate (i.e., their growth is epitaxial). In other areas, the tarnish had folded over or became mechanically damaged, and these areas gave diffraction patterns consisting of "spotted" rings, enabling interplanar spacings of the tarnish lattice to be determined. These spacings, measured using a

Jan 1, 1968

By John F. Elliott, Robert D. Pehlke

The rate of reaction of nitrogen with liquid iron and with binary alloys of iron and Al, Cb, Cr, Ni, O, S, Si, and W were measured. The surface active elements, oxygen and sulfur, decrease the rate markedly. The other alloying elements have very little effect on the rate except when they function as deoxidizers, The rates of absorption and de-sorption were found to be equal. Several possible reaction mechanisms which may control the rate are considered. In order to describe completely the behavior of nitrogen in steelmaking processes, the mechanisms of mass transfer between the gaseous and liquid phases, nitrogen and iron, respectively, must be understood. A kinetic study to determine the nature of these mass transfer processes was undertaken, and the results of that investigation are presented in this paper. Specifically, the study was directed toward determining the influence of alloying elements on the rates at which pure nitrogen gas at constant pressure is absorbed and desorbed by liquid iron solutions: A previous paper1 reported measurements of the equilibrium solubility of nitrogen in liquid binary iron alloys. The experimental data are presented and discussed first and then several possible rate limiting mechanisms are considered. PREVIOUS RESEARCH The results of several investigations on the rate of absorption of nitrogen by liquid iron and iron alloys have been reported.2-14 There is little agreement on the rate coefficients among these studies because of the influence of geometry on the experimental system and of the purity of the liquid iron. The rate was found to be influenced by alloying content for the binary liquid iron systems: Fe-Al,2 Fe-C,4,6 Fe-Cr,4,5,8 Fe-Mn,5 Fe-Ni,5,8 Fe-O,9,10 Fe-O,9,10 and Fe-Si.2,6,7,11 Several investigators12"15 have reported that the rate of nitrogen absorption is increased in a reducing gas mixture and decreased in an oxidizing atmosphere. A mechanism for the retardation by oxygen of the absorption of nitrogen has been described by Naeser18 as the formation of an iron oxide film at the gas-metal interface. The film slows the absorption rate until it disolves in the metal, thus permitting nitrogen to enter the liquid iron. Karwat17 discussed the influence of oxygen in terms of the formation of gaseous molecules of nitrous oxide which represent a higher energy form than the nitrogen and oxygen or the oxidizing gas and consequently constitute an energy barrier for the process. Fischer and Hoffmann10 showed that the oxygen markedly reduces the rate of absorption of nitrogen, the rate constant being one order of magnitude smaller in liquid iron containing 0.15 to 0.24 pct 0 as compared to that in melts containing 0.001 to 0.02 pct 0. Although Chipman and Murphy2 reported that the rate of absorption of nitrogen in liquid iron was essentially independent of temperature, Eklund3 found that the rate increases strongly with increasing temperature as did Kootz4 and Saito.5,6 Karnaukhov and Morozov7 also reported a large temperature coefficient, but related it to increased stirring at higher power inputs in an inductively heated system. All of the authors above have treated their results assuming that the reaction is diffusion controlled, that the surface reaction is in equilibrium with nitrogen gas, and that a "first order" reaction takes place. Karnaukhov and Morozov7 and Humbert; who studied the rate of absorption in a closed system by observing pressure changes in the system as a function of time, concluded that their results best fit a diffusion-type analysis. This was further verified by von Bogdandy, Dick, and stranski18 and Fischer and Hoffmann10 who found the initial rate of

Jan 1, 1963

By A. E. Dwight, A. F. Berndt

Binary and ternary alloys of uranium with transition metals were prepared with U2X stoichiometry. The compounds U2Tc, U2Rh, U2Os, and U2lr were formed by peritectic or peritectoid transformations, and were shown to be isostructural with U2Ru. The lattice constants are presented. Miscibility relationships obtained from the study of ternary alloys are graphically summarized in terms of an area-of-stability plot. The compound U2Re is not isostructural with either U2Ru or U2Mo. A series of compounds with stoichiometry U2X has been prepared in which X is technetium, rhodium, rhenium, osmium, or iridium. The only other U2X compounds, for which X is related to the above transition metals by proximity in the periodic table, are U2Mo and U2Ru. The structure of U2Mo is the tetragonal C11b type (MoSi2 type)1 and U2Ru is monoclinic, with a new structure type.&apos; This investigation was undertaken to determine if any of the above compounds are isostructural with either U2Ru or U2Mo and to find the range of occurrence of these phases. EXPERIMENTAL Alloys were prepared from stoichiometric amounts of electrolytic uranium (99.99 pet pure) and transition metals of 99.5 pet purity (98+ pet pure Tc), by arc melting on a water-cooled copper hearth under an Ar-He atmosphere. Weight losses were negligible. The buttons were homogenized at temperatures between 700o and 800°C (900°C for U2Tc) in evacuated capsules and air-cooled. The X-ray powder specimens were annealed briefly at the temperature of homogenization. Except in the case of the technetium alloy, metallographic examination was used to determine the number of phases present. The radiation hazard involved in handling technetium precluded the use of metallography to examine U2Tc. The temperature and mode of formation of the U2X phases were determined by heating the metallographic specimens to successively higher temperatures, until examination indicated the presence of chilled liquid or a peritectoid transformation. RESULTS The U2X compounds investigated were found to be formed under the following conditions: UzTc unknown U2Ru peritectic 897o ± 3°C U2Rh peritectoid 755o ± 5°C U2Re peritectoid3 below 750°C Uas peritectic4 920°C U2Ir peritectoid 775o ± 5oC Debye-Scherrer patterns for the above U2X phases were made with CuKa radiation (nickel filter). The similarities in the positions and intensities of the strongest lines in the front-reflection region strongly suggested that U2Tc, U2Ru, U2Rh, U2Os, and U21r are isostructural with only minor differences in the unit-cell dimensions. The known lattice constants and intensities of the Debye-Scherrer rings for U2RU2 were used as a guide in order to index the low-angle X-ray reflections of the U2TC, U2Rh, U2Os, and U2Ir powder patterns. Approximate lattice constants for these compounds were thus obtained and were used along with the intensities observed for U2Ru to index the strongest lines in the back-reflection regions. A sin2 2? correction term was included and the lattice constants were refined and standard deviations estimated by least squares. Comparison of observed and calculated values of Q(= 4 sin2?/?2) used in these calculations are given in Table I. In each case when the positions of lines could not be resolved on the films they were not measured. The final lattice constants, with their standard deviations, are given in Table 11, along with the unit-cell volume and X-ray density. The values of the atomic volume5 of the transition ele-

Jan 1, 1965

By H. Margolin, A. Coucoulas

Fused alumina or silica crucibles were used as the containing vessel. X-ray powder photographs were taken with CrKcll radiation and the use of Straumanis type Norelco cameras of 114.6 mm diam. Crystallographic data for these compounds are shown in Table I. These results are in agreement with others of this series reported previousiy by Wernick and Geller.l The abnormally large atomic volume of Eu and Yb metal3 is manifested in EuAl2, and YbAl2, when one compares them with the compounds reported in Ref. 1. However, the behavior of Yb in the Ni compound is the same as that observed in Ni5Yb having the Cu5Ca structure.4 Thus, it appears that Yb has a valence closer to 3 only in the Ni compounds; i.e.. the 2s and Id electrons are lost to the conduction band.1,4 Europium in EuAl2 appears to have a valence closer to 2. In previous work.&apos; X-ray patterns of ingots of NdCo2 indicated a multiphase material with faint indication of the presence of a phase having the MgCu2 structure. It was thought that NdCo2 formed peri-tectically from the melt, resulting in a multiphase system when cooled under nonequilibrium conditions. An X-ray pattern of a sample from a melt cooled more slowly than in past work showed that the major phase was NdCo2. The lattice constant, Table 1, is in excellent agreement with the value one can predict from the data of Ref. 1. One of the other phases was identified as Co5Nd. The author wishes to thank J. H. Wernick for his guidance in this work, and D. Dorsi for the preparation of these compounds. &apos;J. H. Wernick and S. Geller: AIME Trans., in press. &apos;J. H. Wernick and S. E. Haszko: to be published. &apos;F. H. Spedding and A. II. Daane: Progress in Nuclear Energy, Series 5, Eds.: H. M. Finniston and J. P. Howe, McGraw-Hill Book Co., 1956. &apos;S. E. Haszko: to be published. &apos;J. H. Wernick and S. Geller: unpublished work. 6J. 11. Wernick and S. Geller: Acia Cryst., 1959, vol. 12, p. &apos;162. A reinvestigation of the lattice parameters of Ti-Sn alloys by the present authors has revealed consistently hiher c and a values than those obtained by Worrier. The difference is most pronounced in the c-parameters which are, therefore, used as a basis of comparison. This discrepancy was not due to air contamination, since precautions were taken to exclude this possibility. Specimens for Debye-Scherrer photograms were prepared by arc-melting 15-g buttons of Bureau of Mines titanium and 99.99 pct Sn, with compositions of 6, 8, 10, and 12 at. pct Sn. These buttons were forged under an oxygen-acetylene torch to 1/8-in. sq rods to produce relatively fine grained material. Scale and some surface were ground off, and the rods, after wrapping in molybdenum and titanium sheet, were vacuum annealed 15 min at 800 °C to remove hydrogen. Heat treatment of one of the samples at 875°C to produce ß and reveal a at the surface showed no surface contamination. Following the vacuum treatment, the specimens were wrapped in molybdenum and annealed for 1 week at 800°C under two atmospheres of argon. After water-quenching, the rods were ground so that the thickness tapered to 0.1 mm at the tips. The ground specimens were then recapsuled as previously and reannealed 1 hr at 800°C to remove cold work. The

Jan 1, 1961

By G. T. Smith, R. C. Moyer

Cadmium, along with other impurities such as lead, gallium, germanium and indium, is characteristically found associated with zinc ores, the average ratio of zinc to cadmium being about 200 to 1. The increasing demand for cadmium has led most zinc producers to develop a means for its recovery. The separation and recovery of this byproduct constitutes an important development in the metallurgical field. Zinc sulphide concentrates, principally from domestic sources, are processed at Donora Zinc Works and they assay approximately 60 pct zinc, 30 pct sulphur, 0.37 pct cadmium, and 0.8 pct lead. Concentrates are roasted to convert zinc sulphide to zinc oxide. Sulphur evolved as sulphur dioxide is used to manufacture 60º Baume sulphuric acid by the lead chamber process. The roasted calcine is sintered to remove the remaining sulphur and volatile impurities. Fume from the sintering machines is collected by Cottrell pre-cipitators and sent to the Cadmium Department for cadmium removal. The sintered product, a crude zinc oxide, is then mixed with coke and salt and charged into horizontal retorts for reduction to zinc metal. Furnace residues are then passed through a Waelz kiln which recovers practically all of the remaining zinc as an oxide. This oxide is collected by Cottrell precipi-tators and returned to the sintering plant for further processing. The following discussion covers operating procedure, and equipment used in the Cadmium Department for the manufacture of cadmium and its byproducts. (See attached Flow Sheet, Fig 1.) The production of cadmium may be divided into several steps, each of which will be discussed separately. These steps are as follows: 1. Raw Materials—Sinter Plant Cottrell dust, acid sludge and sulphuric acid. 2. Sulphating—Separation of lead. 3. Purification—Separation of impurities other than zinc. 4. Precipitation—Separation of cadmium from zinc. 5. Briquetting—Preparation of sponge for charging to furnace. 6. Smelting—Distillation of cadmium metal. 7. Remelting—Casting into commercial shapes. 8. Recovery of Rare Metals—Separation of germanium, gallium and indium. Raw Materials The raw material, or Sinter Plant Cottrell dust, from which the cadmium is manufactured, is recovered by Cottrell units collecting fume from two Dwight-Lloyd sintering machines. An average analysis of this dust is 36 pct zinc, 1.5 pct sulphur, 17 pct lead, and 5.5 pct cadmium, with associated elements in smaller amounts. A lesser tonnage of material removed from the sintering machine fans, and called fan cleanings, is also treated for cadmium. It is lower grade material and analyzes approximately 41 pct zinc, 1.2 pct sulphur, 14 pct lead, and 4 pct cadmium. Cottrell dust and fan cleanings are delivered to the Cadmium Department by monorail crane in bell-bottomed dump buckets. Acid sludge and 60" Bauine sulphuric acid are received from the Acid Department. The acid sludge is a mixture of lead sulphate, sulphuric acid and zinc sulphate, and is recovered mainly from the floors of the acid chambers or storage tanks. The acid sludge is delivered to the Cadmium Plant in a lead lined bucket. The 60º Baume sulphuric acid is delivered through a lead pipe to a lead lined storage tank. Sulphating Four well ventilated lead lined sulphating tanks, 8 1/2 ft in diam by 12 ft deep, are used. These are steel tanks lined with 20 lb lead on the bottom and 16 lb lead on the ides, equipped with Hastelloy side agitators. 15 hp motors drive 24 in. propellers at 450 rpm. There are water connections to stuffing boxes to keep sludge from entering the bearings. The tanks are covered with removable wooden lids and are connected to marine plywood

Jan 1, 1950

By F. R. Cattoir, R. W. Kimball, C. T. Anderson

ONE of the principal impurities in all steels is sulphur. Sulphur-bearing, manganese-free steels exhibit hot shortness. Manganese is added to steel to improve the hot-working properties. If no sulphur were present in steel, it is probable that hot shortness would be nonexistent. This paper is the first of a series to be issued by this Laboratory reporting the measurements of hot forgeability tests and the physical properties of Fe-C alloys to which additions of various alloying elements have been made. The present paper describes the results- obtained by the addition of varying amounts of sulphur to Fe-C alloys. To obtain control over residual elements in the various charges melted in the arc furnace, it was considered advantageous to use sponge iron from one source as the melting stock rather than scrap metal having an unknown history. Small amounts of unwanted alloying elements might be introduced into the charge when scrap was used, thereby influencing the results of the various heats. A sponge iron having a high silica-lime ratio was used. Ore from Sunrise, Wyo., had been reduced to sponge iron and briquetted at the Bureau of Mines sponge-iron plant at Laramie, Wyo. The briquettes were 5 in. in diam and 2 to 3 in. in thickness, and weighed about 10 lb each. The chemical analysis of the sponge iron is as follows: C, 0.67 pct; Mn, 0.10; SiO2, 4.75; CaO, 1.4; P, 0.044; S, 0.72; MgO, 0.4; A12O3, 1.1; total Fe, 87.5; Fe metallic, 79.2; and reduction, 90.5 pct. Where a reducing agent was required, crushed graphite electrodes usually were used. The charcoal available contained 0.20 pct S. An analysis of the available coke showed it to contain 0.70 pct S. Where high sulphur heats were required, elemental sulphur additions were made to the ladle. Limestone of good quality was obtained locally and had the following analysis: CaO, 53.7 pct; MgO, 0.8; ignition loss, 42.4; R2O3, 0.2; SiO2, 3.0; and P2O5, 0.014. Melting Procedure Sponge iron was melted to produce metal stock for the experimental alloys in a silica-lined, three-phase, direct-arc, size ST, Moore Rapid Lectromelt furnace with a 500 kva rating. Fig. 1 shows this furnace installation. About 25 tons of sponge iron was melted in 75 heats, averaging 927 lb of sponge iron to the heat. An addition of carbon was required to complete the reduction of a portion of the iron oxide remaining in the sponge to prevent high losses of iron oxide in the slag and a low carbon content in the resulting metal. As reducing agents in preparing the melting stock, charcoal, coke, and a carbon product resulting from the thermal decomposition of natural gas were used. The quantity varied from 20 to 60 Ib per furnace charge, with an average of 38 lb. An average analysis of the metal obtained gave 0.52 pct C, about 0.01 pct Mn, 0.070 pct P, and 0.092 pct S. The average yield of metal was 647 lb with 241 1b of slag, the sponge-iron recovery being 70 pct. The metal obtained in melting the sponge iron was cast into pigs weighing about 20 lb each to facilitate recharging into the furnace for further refining. The pouring of the pigs is shown in Fig. 2. The average power consumption for the production of the 24 tons of metal obtained was 1704 kw-hr per ton.

Jan 1, 1954

By C. G. Dunn

This note describes a method for revealing micro-structures in tantalum through an {hkl} effect which was found during a study involving amorphous and crystalline tantalum oxides. Three steps are involved. First, an amorphous film of Ta2O5 is formed anodically1 on the surfaces of the tantalum. The amount needed depents on the thickness of the substrate tantalum; 1600Å of oxide, however, is generally satisfactory in the 1/2 -mil (12 µ) to 3-mil thickness range. The film at this point is uniform in color. Second, the anodized specimen is heated to 800°C in. vacuo during a period of a few minutes and held at temperature for 5 min. During such a treatment some oxygen leaves the oxide through dissolution into the substrate tantalum (e.g., at 10-8 Torr oxide films thinner than about 800 completely disappear on 5-mil strip). Considerable crystallization of the amorphous oxide also occurs adjacent to the metal/oxide interface but not throughout the oxide thickness. The thickness of oxide needed as a residue is not too critical; values between 500 and 1000Å (optical estimate&apos;) may be most useful. (The presence of a residual oxide layer after the heat treatment usually is not apparent; in fact, in most instances the surfaces have a metallic appearance. This can be the case also for thicker residual films needed in the detection of a crystalline oxide phase by surface X-ray diffraction—e.g., if the initial oxide film is 3000Å thick, enough crystalline oxide is formed for X-ray detection.) The third step eliminates the metallic appearance at the surface and reveals (or produces) a varied colored film of tantalum oxide. Two methods can be used and both will be illustrated. If the specimen is dipped in 48 pct HF for a few seconds, the tantalum is found to be covered with a multicolored oxide. Moreover the colors correlate with the grain structure of the substrate tantalum through an orientation dependence of the type illustrated in Fig. 1, where results of an orientation analysis by the Laue X-ray method have been plotted. Other film conditions would have provided a different set of colors for the same orientations. Any such correlation, however, provides a basis for a qualitative assessment of the distribution of orientations in a large sample. The cold-rolled structure of tantalum foil produced by a recrystallization anneal and a cold-rolling reduction of 95 pct is not easily obtained by usual metal-lographic methods.&apos; The structure, however, is easily revealed by the present technique, Fig. 2. The alternative third step is to reanodize the specimen. The optical nature of the final anodic film depends on the presence of the crystalline oxide phase; color variations indicate optical thickness variations in the film. As the reanodization voltage is increased from zero, straw and light brown colors appear (as usual), followed now by variations in color from grain to grain depending on {hkl} orientation. Suitable end points, which are determined by voltage and time, are easily established. Fig. 3, for example, shows the grain structure developed in 5-mil tantalum strip during a 30-min re-crystallization and grap-growth anneal at 1800°C. An anodic film of 1600Å thickness was added prior to the special 800°C anneal. Reanodization was done at constant current density (near 0.2 ma per sq cm) in an aqueous solution of H3PO4 (0.01 pct) and was terminated after the initial brown colors were replaced by a deep blue at approximately 30 v. Although good grain contrast can be obtained with bright field illumination, even greater contrast for black and white micrographs may be obtained with polarized light, as in Fig. 3.

Jan 1, 1967

By F. W. Glaser, Benjamin Post

A LTHOUGH most transition metals form a wide variety of boride compounds, the existence of only one zirconium boride, ZrB2, had been established prior to this investigation.&apos; The crystal structure and some properties of a hitherto unreported zirconium boride, ZrB12, are described in this paper. Only one other dodecaboride of a transition metal, UB12, has been reported up to the present.&apos; Chemical analysis of the new compound showed 44 pct Zr and 56 pct B, compared with 41 pct Zr and 59 pct B computed for ZrB12. The difference is within the range of error of the analytical method employed. ZrB12 shows marked metallic properties. It is obtained as a fine black powder. Measurements of electrical resistivity were made at —79°C, + 22°C and +64°C. At 22°C the electrical resistivity is approximately 60 microhm-cm. Over this range the temperature coefficient of resistivity is +0.00162. The thermal conductivity at room temperature is 0.122 watts per cm per "C. The product of the electrical resistivity and thermal conductivity is therefore 8.05, which is not far from the normal Wiedemann-Franz ratio (approximately 7.5 at room temperature). These measurements were made on hot pressed samples which were not always high density specimens. The hardness of ZrB12 on the Rockwell A scale varies between 92 and 92.5. Crystal Structure Determination Single crystals of ZrB12 of a size suitable for X-ray diffraction analysis could not be obtained and powder samples had to be used. Filtered Cu radiation was used throughout. Powder diagrams were indexed on the basis of a face-centered cubic unit cell. After correction for film shrinkage, a Bradley and Jay extrapolation³ to ? = 90" indicated that a, = 7.408 ±0.002A. The volume of the unit cell is 406.5A.V he assumption that there are four "molecules" of ZrB12 per unit cell leads to an X-ray density of 3.63 g per cc. The measured density is 3.7 g per cc (as measured by the immersion method). Relative intensities of reflections were determined by integrating the intensities of diffraction peaks using the count register of a North American Philips wide range spectrometer. Intensities measured in this way showed good agreement with photographic intensities estimated visually using multiple film techniques. The usual Lorentz, polarization, and multiplicity corrections were applied to the observed intensity measurements. There are striking similarities between ZrB12, and UB12. The unit cell of the latter is also face-centered cubic and contains four molecules. a, = 7.473, compared with 7.408 for ZrB12. The radius ratio rB/rU is 0.57; rB/rZr is 0.54. In both ZrB12, and UB12 the four metal atoms in each unit cell are in special positions; only the boron positions need be determined. The latter may be inferred from the extent to which diffraction of X-rays by the 48 boron atoms reinforces or weakens the diffraction by the metal atoms. This effect is relatively much greater in the case of the zirconium compound. In their determination of the crystal structure of UB12, Berthaut and Blum&apos; assumed holohedral symmetry (space group Oh5 , Fm3m) and reported that the U atoms are in positions 4(a): 000; 01/2 1/2; ½ 0 ½ ; ½ ½; the boron atoms were reported to be in positions 48(i) with x = 1/6: ½xx; ½xx; x½x; x½x; xx½; xx½; ½xx; ½xx; x½x; x½x; xx½; xx½

Jan 1, 1953