By Kuniaki Murase, Tetsuji Hirato, Yasuhiro Awakura

"Electrodeposition of CdTe was studied using aqueous ammonia-alkaline electrolytic baths in which Cd11-and Te1V-ions are dissolving as Cd11(NH3)/+ and Te1vol-ions, respectively. Ca-thodic polarization curves of the baths suggest the presence of strong interaction between the Cd11-and Te1V-ions; electrodeposition of tellurium is inhibited by the presence of Cd(NH3)/+ ions. The interaction makes it possible to electrodeposit CdTe films with stoichiometric composition. Polycrystalline CdTe thin film of about 1 µm thickness was electrodeposited at 343 K from ammonia-alkaline solutions (pH= 10.7) containing TeO32-(<20 mmol dm-3) and Cd(NH3)/+ ( < 60 mmol dm-3) ions. Increasing Cd(NH3)/42+/TeO32- mole ratio or decreasing total concentration of ammonia/ammonium-ion gave flat and smooth crystalline CdTe deposits at constant cathode potential-0.70 to -0.30 V vs SHE at 343 K.IntroductionCadmium telluride (CdTe) is well-known as a compound semiconductor whose band gap, i.e. 1.44 eV, is suitable for solar energy conversion with a photovoltaic cell. Various methods, such as CVD (chemical vapor deposition) and electrodeposition, of preparing CdTe thin films for solar cells have been investigated.Acidic sulfate solutions with a pH of 1-2 are usually employed for CdTe processing by electrodeposition.1-3) The electrodeposition of compound semiconductors is usually achieved (i) at a higher cathode potential than the redox potential of less-noble species, can in this case, and (ii) under the condition of diffusion-limiting current of a more noble species, Te1Y.4) There-fore, a suitable CdII/TeIV concentration ratio in the acidic electrolytic baths, resulting in the deposition of stoichiometric CdTe, is determined by the diffusion-limiting current density of TeIV- reduction, i.e. the concentration of HTeIVO2+ · Since the solubility ofTe1v species HTeIVO2+ in the acidic solutions is quite low, the rate at which CdTe is deposited from the acidic solutions is extremely slow."

Jan 1, 1998

By Michael E. Stout

M.A. Industries, Inc. has developed and is now offering on a commercially available basis, complete systems to recover and recycle lead from spent SLI batteries. The system begins with the breaking and separation of the component parts of the batteries and subsequent treatment of the effluent water produced by this operation. The recyclable materials recovered from this process are metallic lead, lead paste and polypropylene. The lead paste is introduced into a process to convert it from a lead sulfate to a lead carbonate. The process also regenerates the salt solutions into reusable carbonate. The lead carbonate is then leached into an acid bath where it is later recovered by a proprietary electrolytic process. The metallic lead is recovered in a short rotary furnace producing metal for further refining and alloying. The polypropylene is further washed and then introduced to a reclaim extruder along with the proper modifiers and additives. The resulting resin can then be sold on the open market to injection molding processors. This complete system greatly reduces the amount of waste to be disposed of and completely complies with all applicable EPA guidelines.

Jan 1, 1993

By Billy W. Osborne

The use or primary dross as a source for aluminum ion in the manufacture of aluminum sulfate offers opportunities for an inexpensive raw material. The aluminum sulfate industry in the US is a mature market with numerous small plants operating close to major users. The majority of manufacturers use either bauxite or aluminum oxide trihydrate as a source for the alum¬inum ion.. However, using process technology developed and patented by IWC, the oxides are removed from primary dross for use in manufacturing aluminum sulfate prior to metal recovery. This process offers the benefit of reducing costs for metal recovery. This paper discusses some of the methodology used in this process.

Jan 1, 1995

By R. Hurman Eric

The dew-point technique of activity measurements take advantage of the volatility of a component in solution. The pressure of the volatile component over a sample is determined from observations of the temperature at which condensation of the vapor occurs. The method is applicable best when the vapor pressure of the components would differ by about two to three orders of magnitude. Experimentally, this is a closed system involving the use of evacuated and sealed transparent quartz sample probes. Furthermore reliable vapor pressure data of the volatile component is essential along with a specialized high temperature furnace capable of giving reproducible results. In this context, the vertical Dew-Point Furnace (DPF) was designed and built after elaborate trails until enough proficiency was gained for reprodueible results. Over the years the DPF was modified and improved. The DPF developed was versatile and could easily be used for activity measurements in the isopiestic mode (another method of measuring activities of a volatile component in a solution). The necessary ancillary systems; namely evacuation-flushing-evacuation followed by sealing of quartz sample probes under vacuum were also perfected over the years. As and when necessary the dew-point technique was supplemented by classical equilibration-quenching method employed on the sealed quartz sample probes to reveal necessary phase equilibrium information. The following were studied utilizing the above technique: (i) Activities in CuzS-PbS and FeS-PbS binaries and CU2S-FeS- PbS ternary at 1200°C; (ii) Activities in CuzS-SnS and FeS-SnS binaries and Cu2S-FeS-SnS ternary at 1200°C; (iii) Phase equilibria and thennodynamic in Cu-Pb-S, Fe-Pb-S, Fe-Sn-S, Cu-Sn-S and Ag-Sn-S systems. Most recently the following systems have been tackled: (i) Phase equilibria and thennodynamics in the Ag-Pb-S and Sn-Pb-S systems; and (ii) Activities in Ag2S-FeS-CuzS-PbS quaternary at 1200°C.

Jan 1, 2003

By Matthias Merzkirch, Volker Schulze, Kay Andre Weidenmann

"Unidirectionally reinforced light weight compounds based on light metals such as the aluminium alloy EN A W-6082 are adequate materials for the future use in transportation means like automobiles and airplanes. Due to the occurring cyclic loads knowledge about the crack growth behaviour of such composites is needed. The investigations at a load ratio of R = 0.18 show that the crack growth rate of the aluminium matrix is reduced if reinforced by spring steel wire with a reinforcing ratio of only about 1 Vol.-%. Additionally, the acoustic emission analysis allows detecting crack growth within the matrix material, crack propagation along the interface wire/matrix and crack closure which could also be determined with the help of a self designed capacitive displacement measuring gauge. The damage behaviour could be verified by metallographic and SEM investigations.IntroductionIn the field of lightweight structures for transportation means the need for light, strong and stiff materials, in particular composite materials, is increasing in order to save resources and costs. Lightweight materials such as aluminium and magnesium alloys are highly efficient candidates to be used in the composite extrusion process [1] which allows for a simple production of unidirectionally reinforced profiles with a large diversity of geometries at low costs. Figure 1 depicts the principle of the composite extrusion process; within the first part of the tool the billet material is split into several strands whereas the middle part of the tool allows the supply of the reinforcing elements. The third part of the tool rejoins the matrix material and the reinforcing elements and defines the final shape of the profile."

Jan 1, 2011

By J. P. Gu, C. Beckermann

"Melt convection and macrosegregation in casting of a large steel ingot is numerically simulated. The simulation is based on a previously developed model for multicomponent steel solidification with melt convection, and involves the solution of fully coupled conservation equations for the transport phenomena in the liquid, mush, and solid. Heat transfer in the mold and insulation materials, as well as the formation of a shrinkage cavity at the top are taken into account. The numerical results show the evolution of the temperature, melt velocity, and species concentration fields during solidification. The predicted variation of the macrosegregation of carbon and sulfur along the vertical centerline is compared with measurements from an industrial steel ingot that was sectioned and analyzed. Although generally good agreement is obtained, the neglect of sedimentation of free equiaxed grains prevents the prediction of the zone of negative macrosegregation observed in the lower part of the ingot. It is also shown that the inclusion of the shrinkage cavity at the top is important in obtaining good agreement between the predictions and measurements.IntroductionMacrosegregation in large steel ingots is one of the most well-known and now classical problems in the field of solidification and casting [1]. Commonly found macrosegregation patterns in steel ingots are a positively segregated zone at the top, negative segregation near the bottom in the equiaxed zone, inverse segregation near the ingot surface, V-segregates along the centerline, and A-segregates in the columnar zone [2, 3]. It is well established that the macroscopic transport of species leading to macrosegregation can occur by a variety of mechanisms, including thermally and solutally driven natural convection of the melt in the mushy zone, flow due to solidification contraction, and the sedimentation of free equiaxed crystals. Fredriksson and coworkers [ 4,5] provide recent overviews of the solidification transport phenomena and macrosegregation in ingot casting."

Jan 1, 1999

By E. A. van Dijk

Dusts from steel-making processes contain substantial amounts of zinc. Such dusts are also a hazardous waste and dumping them becomes unacceptable from environmental point of view. Therefore processes that can recover zinc and possibly other metals from steel-making dusts are being investigated. The aim of this paper is a contribution to the more fundamental kinetic aspects of zinc reduction from silica free calcium ferrite slags. The effects of alumina, lime and magnesium oxide contents of the slag, the COICO, ratio and the effect of initial Fe2O3/CaO ratio were studied experimentally at 1400°C The results indicated that the reduction of zinc from molten slag was possibly a first order reaction. As expected higher COICO, ratios increased both the extent and the rate of reduction. It was also observed that a higher iron content of slag improved the reduction of zinc from calcium ferrite slags. This fact seems to support the proposed mechanism that zinc is partly reduced by ferrous iron to zinc vapour and that ferric iron is reduced by carbon monoxide. The reduction rate of zinc in these slags was decreased by increasing alumina content of the slag. Alumina decreased the calculated optical basicity of the slag showing the fact that reduction of zinc oxide was more favorable in more basic slags. Probably the formation of complex ions by alumina and zinc oxide such as ZnAl2O32+ lowers the activity of Zn2+ ions in the slag and hence render them more difficult to reduce.

Jan 1, 1999

By Jesus Gonzalez

Peirce-Smith converters (PSC) are long cylindrical chemical reactors where copper matte reacts with air. Traditionally, air is injected laterally through submerged tuyeres at different subsonic velocities. However, the accumulated experience in steelmaking, particularly in the basic oxygen furnace (BOF) process, shows that the gas bottom injection may improve the mixing efficiency of a liquid pool. The aim of bottom injection is to maximize the copper kinetic energy meanwhile avoiding excessive reactor splashing. When gas is injected from a single orifice at the bottom of a liquid pool, two main gas flow regimes can be identified, bubbling and jetting. In this work, a PSC with bottom air injection is studied by means of multiphase 3D CFD numerical simulations considering multiple air velocities. Special attention is paid to the bubbles and jet formation mechanism. The mixing efficiency is measured by calculating the turbulent kinetic energy of the copper matte.

Jan 1, 2008

By Renxing Li, Yongyong Gong, Yufeng Cheng, Zhenxing Yin, Xin Cao, Qijie Zhai

"The influence of electric current pulse (ECP) on the solidification structure of SUS430 ferritic stainless steel (FSS) was investigated in the current study. The technology of ECP has been widely used to improve the properties of metals with relatively low cost. The parallel electrodes were inserted into the free melt surface to constitute a current loop. The different influences of three parameters on solidification structure were studied by changing the peak current value, frequency and treating time respectively. The results indicated that the ECP significantly increased the number of equiaxed grains of SUS430 FSS. The as-cast structure without ECP treating was almost wholly columnar, while the number of equiaxed grains of the specimen, which was treated 3min with a peak current of 400kIA, increased to 2698 in the observed surface. To get the best refinement, an optimum range of these three parameters is required and the peak current value plays the most important role.IntroductionFor the lack of nickel resource and the pressure of environment protection, ferritic stainless steel is increasingly adopted to replace the austenite stainless steel because of its low nickel content and good mechanical properties. SUS430 steel is a typical example with excellent performance and relatively low price to replace the application of austenitic stainless steel[1-3]. This type of steel with high thermal conductivity coefficient, low expansion coefficient, good oxidation resistance, excellent stress corrosion resistance and other fantastic characteristics is often used to make components which need to have resistances for atmosphere, water, steam and oxidizing acid corrosion[4]. Since the developing of columnar grains and low toughness at high temperature, its products are easily crinkled and cracked during the subsequent rolling process[5]. The application of ferritic stainless steel is limited by these defects[6-8]."

Jan 1, 2012

By Selim Coskun

In this study, tungsten matrix composites reinforced with 2 wt% TiC particles were mechanically alloyed (MA?d) for 3h, 6h, 12h and 24h. 1 wt% Ni is used as sintering aid which is added before and after mechanical alloying. Microstructural and phase characterizations of composite powders and sintered samples were carried out via SEM and XRD analyses. Furthermore, density and hardness measurements of as-consolidated and sintered samples were carried out. Additionally, DSC experiments were conducted to investigate the sintering behavior of the MA?d powders.

Jan 1, 2009

By Steven M. Puricelli

Sulfuric acid plants associated with smelters, have historically been an overworked and often neglected pollution control device. They could do little more than manage the wide fluctuations in gas flow and SO2 strength from the smelter. With the introduction of flash smelting, the picture began to change, but the fluctuating batch converters continued to dictate acid plant design. More recently, the commercial use of continuous converting processes utilizing high levels of oxygen enrichment has dramatically upgraded the SO2 strength and stabilized the gas flow to the acid plant. The SO2 gas now issues continuously and at concentrations that allow for compact and, cost effective acid plants. Relieved of the burden of excessive dilution air, the heats of reaction can also be recovered as medium pressure steam and used to drive a generator, making the acid plant a net producer of power and a valuable asset to balance sheets. This concept was put into practice at the Kennecott Utah Copper Corporation smelter modernization project, located in Salt Lake City, Utah. The new acid plant, which was commissioned in June of 1995, is a sophisticated, low environmental impact, energy producing plant, worthy of review. This paper examines the key features of this acid plant, such as controlling its tail gas, by catalysis alone, to an environmentally friendly, 100 ppm of SO2, while feeding the acid plant converter with an efficient 14% SO2. The acid plant is also a prudent steward of energy resources, recovering 220,000 lb/hr of 140 psig steam from process heat which is used to generate a substantial 20 MW of gross power. Also discussed will be some of the ongoing issues, such as handling of selenium and fluorine in the gas cleaning sections, as well as a review of some. of the problems that were identified and resolved. Today&apos;s modem acid plants, by necessity, are becoming a producer of quality, valuable products, making the acid plant an asset and not a liability. Plants like Kennecott are already gaining wider acceptance and are expected to be the vision of the future.

Jan 1, 1998

By A. F. Giamei, F. Landis, M. O. Duffy, R. J. Mador

"The directional solidification of complex advanced gas turbine airfoils must be carried out without the nucleation of undesirable grains and with minimal shrinkage. Such problems are typically eliminated by using a number of mold design and process iterations. A more efficient approach is envisioned where a solidification model is generated and utilized to accelerate process development. Towards this end, the directional solidification (DS) of simple geometrical shapes in a crystal grower apparatus has been simulated with MARC finite element nonlinear thermal analyses.The finite element models of cylindrical (2D) and rectangular (3D) cross-section bars in the DS environment are presented. Temperature dependent properties, the impact of latent heat of fusion and a time-dependent radiation boundary condition constitute the more salient features of the MARC models. Solidification zone thermal behavior is predicted during the withdrawal transient for the specific case of nickel based superalloys grown in ceramic shell molds. Comparisons of analytical results with experiments demonstrate notable prediction accuracy. INTRODUCTIONSingle crystal and uni-directional crystal turbine blades require tightly controlled conditions if metallurgically and mechanically acceptable parts are to be produced. Gated blade geometry and process parameters must be precisely determined if incorrect grain structure, orientation and shrinkage are to be avoided. Since purely experimental development programs designed to evaluate these parameters can be excessively costly and time-consuming, an effort combining engineering analysis and verification by experiment has been initiated at Pratt & Whitney. Comparison of analytical predictions and measured data for geometries simpler than a turbine blade, namely cylindrical and rectangular bars, comprised the initial stage of this effort. Subsequent tasks involve modeling geometries of increasing complexity and ultimately the simulation of the directional solidification of the turbine blade, shown schematically in Figure 1. This paper summarizes the results of the initial stage of the effort."

Jan 1, 1986

By David Van Aken, Arpana S. Murthy, Simon Lekakh, Von L. Richards

"Three heats of 17-4PH stainless steel: with zero, three percent, and seven percent cobalt addition were melted in a 45kg (1 00lb) induction furnace under argon; and cast into no-bake molds and preheated investment shell molds. Specimens were sealed into quartz tubes under vacuum, and homogenized at 1200°C from 2h to 72h. Computational thermodynamics and optical microscopy were used to predict and characterize the microstructures. The lath martensite packet size and the amount of 8-ferrite were observed to be inversely related. A compromise between decrease in segregation and increase in lath martensite packet size was chosen for the optimum homogenization treatment. The specimens were austenitized, quenched, and characterized for retained austenite using x-ray diffraction. Age hardening kinetics were studied at 454°C (850°F), 468°C (875°F), and 482°C (900°F); and, the activation energies for precipitation of copper were calculated. Tensile properties and Charpy V-notch impact energies were measured in the peak aged condition. Fracture surfaces were observed using scanning electron microscopy and Energy Dispersive Spectroscopy. The addition of cobalt was found to be beneficial for the improvement of strength as well as notch toughness.IntroductionSegregation in the as-cast condition is one of the drawbacks of metal casting. This paper presents a study on the homogenization treatment of 17-4 PH cast stainless steel and the effect of cobalt addition on tensile properties and Charpy V-notch toughness. Lattice dilatation studies show that additions of up to 6% Co to iron has a negligible effect on the lattice parameter, whereas both the modulus of elasticity and shear modulus increase with increasing cobalt additions5• An ordering reaction has been reported in cobalt-containing, maraging steels and contributes to the hardening during ageing1-4• Although, cobalt addition in maraging steels has been extensively researched, and has been reported to be beneficial; it has not been explored much in other age-hardening stainless steel systems. In a previous study, the addition of 3% Co in cast 17-4 PH martensitic age-hardenable steel was found to improve the strength and elongation while maintaining the charpy V-notch toughness6."

Jan 1, 2011

By Liu Wei-feng

Base on the thermodynamic calculation of vapor pressure of lead, antimony and arsenic at high temperature, the possibility of separating lead, antimony and arsenic in different temperature was analyzed ,and the practice of producing qualified antimony white from lead-antimony alloy by direct blowing was introduced in detail in this paper. The blast furnace reduction smelting was brief introduced firstly, and then alkaline refining was applied to removing arsenic from lead-antimony alloy that contains As1%,Sb39%,Pb58%,the arsenic in the treated lead-antimony alloy could decrease to 0.009% by that method. The antimony white containing Sb2O3 99.5% could be produced by air blowing in the special furnace at 650? from the treated lead-antimony alloy. And the electrolytic lead could be achieved by electrolysis from the lead-rich alloy which contained 83% lead.With high-grade product being obtained the process was shortened. The technology has been applied successfully many years in Guangxi, China.

Jan 1, 2009

By Jan Petter Maehlen

Solid H-absorbing materials are in focus of ongoing R&D to offer viable solutions for the hydrogen storage and supply systems aimed on use of hydrogen as energy carrier for automotive transportation. Low operating pressures, combined with high gravimetric and volumetric efficiencies, together with fast kinetics of hydrogen release at ambient temperatures (providing conditions for a low energy loss due to decomposition), are the most important features of the ?ideal? H storage material. Hydrides of the light elements are the only possible candidates to build systems with an overall efficiency similar to those accommodating liquid or compressed (700 bar) hydrogen. One promising material from this point of view is aluminium trihydride, alane AlH3 with a gravimetric storage capacity of 10 wt.% H. This work was focused on studies of the crystal structure and thermal decomposition of alane by application of powder synchrotron X-Ray diffraction.

Jan 1, 2006

By A. Patti, S. Reutzel, D. M. Herlach, L. Ratke, I. Egry

Cu-Co shows a metastable miscibility gap in the region of the undercooled melt. Undercooling of the melt below the binodal leads to separation of the melt into a Co-rich LI-phase and a Curich L2-phase. Experimentally, undercooling into the metastable miscibility gap is realised by means of electromagnetic levitation (EML), processing in drop tube (DT) and by melt flux embedding. As undercooling is large in these experiments, the velocity of the solidification front is high and the microstructure is frozen in instantaneously. Samples have been undercooled and solidified in the TEMPUS-facility (container less electromagnetic processing under weightlessness) during parabolic flight under reduced gravity conditions. Microstructures of solidified samples have been analysed and compared to those processed under gravitational conditions. The influence of convection on phase growth is much lower in reduced gravity. The microstructure shows spherical droplets of the minority phase, statistically dispersed in the majority phase.

Jan 1, 2004

By G. Lissens

In this work the electrochemical combustion of dissolved organic species in a single compartment cell containing a titanium mesh cathode and a boron doped diamond anode has been studied, The organic molecules involved were complexing agents such as EDTA (ethylenediaminetetraacetic acid) or NTA (nitrilotriacetic acid) used in metal plating shops and bright nickel plating bath additives, From batch experiments, it is shown that complete decomplexing of EDTA and NIA is feasible. Complete TOC (Total Organic Carbon) removal from solutions containing 0.01 M EDTA, 0.02 M NTA and bright nickel plating bath additives could also be achieved. Recycling experiments show that decomplexing of EDTA and NTA solutions can be obtained at an average electrical energy input of ~20kWh.kg-1 of complexing agent. Decomplexing rates of respectively 3.l3 mmol.Ah-1 for EDTA and NTA have been obtained, The Instantaneous Current Efficiency (ICE) was 71% for EDTA and 95% by NTA, Simultaneous recovery of Cu from a 0.01 M Cu-EDTA solution has also been evaluated. A solution (1.8 dm3) containing 0.01 M EDTA and 528 ppm of Cu was treated in a single compartment cell at a current density of 2 A.dm-2. 73% of the TOC could be removed and a final copper concentration of 8 ppm was obtained.

Jan 1, 2003

An EAF dust generated in a Swedish steel mill has been leached in hydrochloric acid at The solution obtained has been subjected to purification by cementation followed by precipitation of zinc with sodium carbonate. The thermal decomposition of the precipitate was studied using thermal analysis and X-ray diffraction. The results show that during the calcination of the precipitate three different reactions occur. The decomposition of the solid phases Zn5(CO3) (OH)6, CaZn(CO3)2 and CaCO3 occur completely at 370°C, 560°C and 940°C respectively, yielding a final product containing 61.9% ZnO and 38.1% CaO. Methods to minimize calcium and manganese in the final product are discussed.

Jan 1, 2003

By A. Onozaki

The Iijima Refinery was put into operation in 1972 and today has an annual production capacity of 156,000 tons of SHG electrolytic zinc. At the Iijima Refinery, the recoveries of gold and silver are 98.0% and 98.2%, respectively. Gold contained originally in the zinc concentrates reports in the Cu-Pb-Ag residue produced in the residue treatment process. Silver contained in the concentrates is distributed between the Cu-Pb~Ag residue and the copper cake produced in the purification process. The Cu-Pb-Ag residue, which contains gold and silver, is sent to the Oyachi flotatfon plant of the Kosaka Smelter; about 82% of the gold and about 85% of the silver are recovered in the copper flotation concentrate.. In this paper, the distribution of gold and silver in the Iijima. Refinery is discussed and operational results of the Oyachi flotation plant are presented.

Jan 1, 1990

By S. B. Bortnikova

This paper presents the results of an investigation of the gold-silver oxidized ores at the Salair mine. West Siberia. High losses of precious metals during primary ore processing are the result of outdated technology that is not suited to treat the present ore compositions. The main mineralogical forms of gold and silver and their confinement to different grain size fractions have been determined. About 50% of gold in the slime fraction and 60% of the silver in the form of acanthite that are scattered from the secondary minerals are lost to the waste. The results of these investigations have provided the basis for the recommendation of a new technological process to upgrade the current practice of the gold extraction plant and for methods to reprocess the concentrates.

Jan 1, 1995