By Jiang Feng, Zhang Libo, Peng Jinhui, Guo Zhanyong, Ju Shaohua, Lei Ting

The clean utilization of the residue containing chloride, CuCl residue, produced from zinc hydrometallurgy is very important for the recycle of valuable metals. And drying is the main process in recycling. In this study, response surface methodology was used to optimize operating conditions of the drying of CuCl residue in a convection oven and desirability function used as the methodology for the optimization. Optimization factors were air temperature (80–100°C), material thickness (10–25mm) and process time (80–120min) while investigated responses was final moisture content. The optimum conditions were found to be the temperature of 95.48°C with the material thickness of 13.47mm for the process time of 89.48 min. Under optimum conditions, the predicted moisture content of CuCl residue was 4.11% while the experimental date was 4.13%. The experimental value after process optimization was found to agree satisfactory with the predicted value. After drying, XRD was used to analyze the main phases of CuCl residue. The CuCl residue is made up of CuCl,Cu2O, ZnS and other compounds.

Jan 1, 2015

By C. B. Piazzarollo

Ceramic materials exhibit dispersion results after being subjected to various levels of stress, from the point of view of mechanical strength. With the focus on sustainable development and to improve the strength of these material, was incorporated ornamental rock waste into clay in up to 10% in mass to conform some samples, that was fired to 750ºC, 850ºC and 950ºC and submitted to technological tests. This paper presents an analysis of the technological properties of the samples through the use of Weibull statistic to determine which the best firing temperature for these red ceramic materials. The Weibull Modulus indicates a greater homogeneity for samples with 10R at 950ºC.

Jan 1, 2015

By Run Huang, Xuewei Lv, Lei Lei, Guibao Qiu, Chenguang Bai

"The TiO2-rich slag and pig iron can be produced from ilmenite concentrate by the electric furnace process. In this study, ilmenite concentrate was reduced in a vertical furnace equipped with a weighting data acquisition system. The effects of reducing agent (carbon) amount on the iron reduction were studied. The phase transformation, morphology and chemical compositions of reduced samples were investigated by X-ray diffractometry (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS), respectively. It was found that the reductive degree of ilmenite concentrate increased with the increase of reducing time. The phases of reduced samples were mostly iron, rutile, Ti3O5 and Fe2TiO5. The mass loss percentage increased with increasing the carbon amount from 8% to 12%. When the carbon amount exceeded 12%, the mass loss percentage decreased with the increasing of carbon amount.IntroductionIlmenite and rutile are the main raw materials for producing titania pigment and titanium metal. With the development of the titanium industry, huge amounts of titanium resources are needed. As sources of high-grade titania mineral decrease worldwide, more attention should be paid to the processes involving low grade mineral such as ilmenite ore. In ilmenite, MgO and CaO are the gangue parts. Therefore, the ilmenite refining becomes more and more popular. In the previous studies, the methods of ilmenite refining are electric furnace smelting, direct acid leaching, selective chlorination and thermal reduction [1]. Electric furnace smelting method is widely used in the titanium industry, however, which consumes a great deal of energies and has a high CO2 emission. Its essence is to remove iron oxides and obtain a high titania slag. So the thermal reduction of ilmenite concentrate is an important step in titanium industry, which can decrease carbon reagent consumption and save energy.Over the past several decades, many studies have been carried out on the mechanism and kinetics of the reduction of different ilmenite ores, which are as follows: The carbothermal reduction of Panzhihua ilmenite initiated at about 860 oC. In the temperatures ranging from 900 oC to 1400 oC, the reaction rate was changed like a shape of “M”. That was to say that the reaction rate increased with the growth of temperature at first, then decreased, afterward increased again and at last the reaction was arrested [2]. The Mohammad A.R group [3, 4] showed that the carbothermal reduction of primary ilmenite concentrate was faster in hydrogen and initiated at a lower reduced temperature than in argon and helium. The reduction in argon and helium had about the same rate and extent. Titanium oxycarbide started at 1000°C in hydrogen. The conversion of primary ilmenite concentrate to metallic iron and titanium oxycarbide at 1200 °C was completed in 300 minutes. Monoxide as the reductant to reduce ilmenite had been studied intensively by a few research groups [5, 6]. The rate and the degree of reduction depended on the formation of a metallic shell of iron which inhibited the transfer of CO to the reaction zones; titanium had a strong effect on the mechanism and rate of reduction of iron oxides. Wang and Yuan [7] studied the reductive kinetics of the reaction between a natural ilmenite and carbon. At temperature below 1100°C, chemical reaction was the rate controlling step, at 1100 to 1250°C mixed controlling was rate controlling step, above 1250°C diffusion through the product layer controlled the reaction. Zhang [8] investigated the reduction of natural, sintered and preoxidized ilmenite concentrates in hydrogen methane mixtures. Preoxidation and sintering of ilmenite concentrates changed their phase composition and caused a sharp decrease in specific surface area of raw materials and an increase in carburization temperature. Sintering also increased the metallization temperature of iron."

Jan 1, 2011

By Mostafa O. El-Bealy

"To estimate the interdendritic cracking tendency in casting processes, a new model for interdendritic cracking criteria has been proposed. The model combines a concept of the alloying element effect on the interdendritic strain generation and therefore on the susceptibility of interdendritic cracking phenomena. A susceptibility of interdendritic cracking is modeled by using El-Bealy's interdendritic cracking susceptibility function ""BJCSF' and the opening displacement between the dendrites ""EIA "". These concepts are modeled based on the previous experimental observations and ElBealy' approach. The model is implemented numerically for a one-dimensional model problem with some similarities to the casting of steel. The variation of some key parameters that are known to influence the frequency and severity of the interdendritic cracking is then studied.I. INTRODUCTIONInterdendritic cracking ""hot tearing"" commonly encountered in both ferrous and nonferrous castings (1,2]. It is generally believed that interdendritic cracks start to nucleate and develop in the interdendritic strain region within the mushy zone [l-5]. The interdendritic strain region is then definitely coherent, but continuous films of liquid still exit (4,5]. This distinguishes interdendritic cracks from cold cracks forming during the casting process after complete solidification (6,7].Much effort has been put into the understanding of the interdendritic cracking phenomena, and several theories have been proposed. Fellini [8] stated that interdendritic crack ""hot tear"" will result if the material is subjected to too high of accumulated strain within so called vulnerable part of the solidification interval. Kinosita et. al. [9] and Campbell (10] also emphasized the role of tensile stresses in the forming of interdendritic cracks. Most interdendritic cracks criteria simply consider the size of solidification interval, stating that solidification range is associated with a lager interdendritic cracking susceptibility than a short range. Clyne and Davies (11] formulated a more refined such criteria based upon the time spent in different regimes of the solidification interval. They defined a vulnerable region in which thin continuous films of interdendritic liquid exist, and the permeability is low. When thermal strains are induced in this region, the film is not able to sustain the stresses, and an interdendritic crack will form."

Jan 1, 2001

By Denise Cristina de O. Nascimento

Natural lignocellulosic fibers are increasingly being used as polymeric matrix composite reinforcement owing to economical and environmental advantages as renewable and biodegradable materials. Among these, the piassava fiber extracted from a palm tree native of South America stands as one of the most rigid with a potential to be used as composite reinforcement. Therefore, the present work investigates the notch toughness behavior, by Izod impact tests, of epoxy composites reinforced with up to 40 % in volume of continuous and aligned piassava fibers. It was found that the incorporation of piassava fibers results in significant increase in the impact energy of the composite. Scanning electron microscopy analysis showed that the nature of the piassava fiber interface with the epoxy matrix is the major responsible for the superior toughness of the composite.

Jan 1, 2009

By Baozhong Ma, Yonggang Wei, Shiwei Zhou, Bo Li, Chengyan Wang, Hua Wang

The effects of additives with Na2S, Na2SO4 and CaSO4 on phase transformation of nickel laterite ore in low-temperature reduction roasting process using carbon monoxide were investigated. The results showed that diffraction peaks of forsterite increased with increasing reduction temperature for 30min with the addition of 10wt% Na2SO4 and 50vol% CO, and diffraction peaks of forsterite increased with increasing the content of Na2SO4 at 900°C for 30min. Comparing the above three additives, phase transformation of nickel laterite ore were strongly influenced with the addition of 10 wt% Na2SO4 and 10 wt% Na2S. Calcium sulphide from the thermal decomposition of CaSO4 was carried out in the reaction product. SEM-EDS analysis result deduced that increasing the dosage of Na2SO4 from 10wt% to 15wt% could promote the polymerization of ferronickel and improve the grade of nickel in ferronickel.

Jan 1, 2015

By Minting Li, Hailong Yang, ChangWei, Cunxiong Li, Gang Fan, Xingbin Li, ZhiganDeng

The filtration problems on acid leaching sludge of high silicon zinc ore have been paid extensive attention in zinc hydrometallurgy. It was found that soluble silica can be effectively converted into silica precipitate with good settling, filtration and washing properties, and the filtration rate can be in excess of 800 L/m2 · h under certain leaching conditions. According to investigating on the filtration rate, viscosity and concentration of silica of leaching sludge or liquor, the filtering temperature can tremendously improve the filtration property of pulp. At the same time, the experimental data indicated that the viscosity of leaching liquor was the key factor influencing filtration property of leaching sludge.

Jan 1, 2016

By C. Y. Tang, Z. H. Chen, T. C. Lee

"In sheet metal forming process, the forming limit and strain distribution are governed by plastic instability and fracture following strain localization. It has been proved that the temperature gradient caused by plastic deformation as well as friction is one of the crucial factors to induce the strain localization in high-speed metal forming processes. In this paper, a numerical simulation of the sheet metal extrusion process has been conducted by using thermal-mechanical coupling finite element method. An improved mixed finite element method has been used to solve the large deformation elasto-plastic problem. In thermal phase, the transient heat transfer finite element method together with the Crank-Nicholson algorithm has been employed to determine the temperature field. Both the numerical results and the experimental observations reveal that the temperature gradient plays an important role in inducing the strain localization, which eventually leads to fracture failure in the sheet metal extrusion process.IntroductionSheet metal extrusion is such a process where the extrusion punch penetrates into one surface of the sheet metal material to let it extrude and flow towards the outlet of the die. This process can be used to produce protruding parts on a strip material. In engineering applications, the quality of the product is affected by many factors such as stress state, loading speed, material properties and lubrication condition. The research on failure mechanisms and improvement of formability in sheet metal forming processes by exploitation of differential thermal conditions has been of great interest recently [1-3]. It has been proved that the temperature gradient caused by plastic deformation, heat transfer, and friction between sheet and tools is one of crucial factors to affect 'the formability in high speed sheet metal forming processes [4]. In our previous study of sheet metal extrusion, it has been observed that plastic deformation is highly localized and some specimens are subjected to fracture failure in the form of crack propagation [5]. To understand this failure phenomenon, the effects of temperature gradients must not be ignored."

Jan 1, 2001

By Mim Li, Huimin Lu, Lisha Yang

"CuInS2 thin films solar cells have drawn much attention for their low-cost, stability and high conversion efficiency. The electrodeposition of Cu-In precursor films, as the first step in making CuinS2 solar cells electrochemically in the air-and water-stable ionic liquid based on choline chloride/urea eutectic mixture has been investigated at constant potential. Compared with aqueous electrolytes, the large electrochemical window as well as the high thermal stability of this ionic liquid allow the direct electrodeposition of Cu-In precursor films. Then the precursor films were sulfuretted in a tube furnace at different sulfurization temperatures to optimize the films properties. The films obtained were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS).IntroductionCuInS2 is one of the most prospective absorber materials for low cost thin film solar cells, with a high conversion efficiency that exceeds 32% in terms of theory and nearly 13% in laboratory level [1-2]. In addition to its long-term stability, CuinS2 has a band gap energy Eg ranging from 1.3 to 1.55 eV and an optimal optical absorption coefficient reaching 105cm-1 [3-4]. CuinS2 thin films have been prepared by several methods such as spray pyrolysis [5-6], r.f.sputtering [7], vacuum evaporation [8-9] and electrodeposition. Comparing with vacuum methods, electrodeposition has lots of advantages such as less energy consumption, preparation big area thin film, stable system and enabling cheaper films.The electrodeposition of most technologically important metals has been shown to be possible from a wide range of ionic liquids. These ionic liquids are currently applied in a wide variety area. It is reported that the cell efficiency of chalcopyrite absorber layer (CIS, CISeS, and CIGS) via an electrodeposition route in laboratory condition has reached 11.3% [10]. Copper and indium alloy film is regarded as important precursor for the production of compound semiconductors with sulfur. The electrodeposition of the alloy film from room temperature ionic liquid (RTIL) has not been widely investigated. Only few alloy films, such as ZnTe, CdTe, GaAs and AlSb have been electrodeposited."

Jan 1, 2011

By Saad Elias Kaskah

"The Box-Behnken Design (BBD) is used to model the sacrificial Cathodic Protection System (SCPS) to find the factors effectiveness behaviour. For protection potential assessment the BBD receives (resistivity of environment, sacrificial anode alloy, distance between anode and cathode and surface area for the structure to be protected) as input and gives the protection potential as output. By applying BBD with their analysis tools we get many results. The important results which are the factors individual effectiveness on the sacrificial cathodic protection (SCP) process are the resistivity which has the greatest effect on the potential protection (rank=l) followed by sacrificial anode alloy type (rank=2), surface area for structure protected required (rank=3) and distance between anode and cathode (rank=4). The interaction of sacrificial anode alloy and cathode area {X2X4 ) has significant effect on CP process with the limits which are used in this work while the other factors interaction (X1X2, X1X3, X1X4,X2X3, X3X4 ) has insignificant effect on the limits which used in this work.IntroductionFor carbon steel in seawater the normal corrosion potential E '°""_is in the range -550 to -600 mV vs. Ag/AgCI [1]. The most effective method to overcome the corrosion is cathodic protection {CP) which represents a control method in the steel wall corrosion. Cathodic protection has been used in several areas including marine and underground structures, storage tanks, and pipelines [2]. Sacrificial anodes system generates protective current which depends upon the inherent potential difference between the anodes and the structure to be protected. If the structure is made of iron or steel, any metal that is more active in the electromotive force series can theoretically be used as anode material [3]. There are many factors influencing on cathodic protection like resistivity (NaCl content), chemical composition of sacrificial anode alloy, distance between anode and cathode, surface area of cathode, temperature, humidity, velocity of solution, dust, impurities, bacteria and etc .. The present work studied four factors: NaCl content, resistivity), chemical composition of sacrificial anode alloy, distance between anode and cathode, surface area of cathode) with different three levels of values for each one. Then this work will find the optimum value from the factors levels that tacked to investigated there influencing on sacrificial cathodic protection system."

Jan 1, 2013

By Hélio Wiebeck, Fabio J. Esper, Wildor T. Hennies, Guillermo R. Martín-Cortés, Francisco R. Valenzuela-Díaz

"Natural rubber reinforced commonly with carbon black to produce vulcanized material, turns into a new environmentally friendly nanocomposite when carbon black is replaced by organically modified clays of Brazil. Carbon black is substance derived from the oil refining process with consequent pollution to the environment. Its substitution in this industrial process must contribute to diminish the oil derived products dependence. As the added clays are only a third in weight of the traditionally carbon black added, then, to obtain the same final volume it is necessary to add low cost neutral filler that does not damage the technological characteristics of the final material. This paper presents results using as neutral filler of this type rice husk ashes from industrial wastes. Experiences realized with this nanocomposite material show results of quality and technological characteristics similar or superior to those of the rubber made with carbon black.IntroductionTraditionally rubbers are black or a very dark color. But they can have different appearance when filler of distinct composition of the carbon black is used. The carbon black is substance derived from the oil gotten during the final phases of the mineral fuel treatment with consequent pollution of the environment. Carbon black show nanometric grain sized distribution and a depth black color, because these properties it is also used for computer printers inks production. The substitution of this substance, traditionally used as a reinforced load in the rubber production, will have to contribute in such a way to diminish the dependence of these products as to diminish the pollution of the environment. The present work shows the results of the use of another kind of mineral nanoparticulate material substituting carbon black in the production of some rubber products. This nanoparticulate material is the organic modification of smectite clay treated with some types of ammonium quaternary."

Jan 1, 2008

By Xi-chang Shi, Yun-feng Fu, Bai-zhen Chen, Hui Xu, Xiang Xiao

"Extracting boric acid from saline brine by boron specific ion-exchange resin was investigated. Effects of resin amount, temperature, time and stirring speed on boron adsorption rate were studied in the experiments. The results indicated that the XSC-700 resin showed excellent boron absorbability and it performed better property for elution. The maximum boron adsorption capacity was 6.16 mg/ml in the optimum conditions: the resin concentration of 5 ml/(100 ml brine), the temperature of 60°C, the time of 5-6h and the stirring speed of 100 r/min. Boron was eluted from the resin with HCl and boric acid was crystallized by evaporating the eluate. The product of boric acid was in pure form as confirmed by XRD and other analysis techniques.1 IntroductionBoron has a number of minerals in nature such as tincal, colemanite, ulexite, and kemite, etc. [1-2]. Boron and its compounds are chemical materials of significant value. The principal industrial uses of boron compounds are in the production of glass, porcelain, enamels and detergents. Other uses include fertilizers, metallurgy, and nuclear shielding [3-4]. In recent years, because of the large-scale mining boron ore, ore resources are drained gradually. With the development of science and technology, the boron mineral resources will be unsatisfied with the future requirement. There exits abundant boron resources in salt lakes which cover about 40% of the total reserves in China. If we can obtain boron from salt lakes, it will produce great economic interests [5-6]. Therefore, actively seeking boron from salt lake and other resources in suitable conditions has become a hot spot in the research organizations of boron resources development and utilization in the world [7].There are many methods such as acid crystallization, solvent extraction and ion exchange processes suggested effective for boron extraction from aqueous solutions. Acid crystallization method has the shortcomings of complicated procedures, the pollution caused by hydrochloric and other ingredients returning to salt lakes during the extraction process. Although solvent extraction process increases the boron acid recovery efficiency, the cost of production is high [8-9]. However, Chelating resin extracting boron has the characteristics of simple process, easy operation and no pollution. It was reported that chelating resins containing functional groups show a high selectivity for boron extraction [10-12]. Therefore, ion exchange technique which is now the most practical application of significance and most extensively used ha"

Jan 1, 2011

By G. G. Barbante

Copper anode slimes are a valuable source of the precious metals, and selenium and tellurium. They are mineralogically complex and this has led to a great variety of process flowsheets for treating them. The traditional pyrometallurgical method utilises oxidation in a reverberatory furnace, but has numerous shortcomings. Recently deep-bath intensive smelting methods have been developed for use in the larger refineries. Despite these process advances, the thermodynamics of the reactions involved remains poorly understood. An initial description of the thermodynamics of slimes smelting is presented, but is severely limited by a lack of basic data. It is shown that slimes smelting is superficially similar to copper converting, but has many unique features. More basic thermodynamic data on selenium-based systems are needed before the process model presented can be further refined, and work in this direction has already commenced.

Jan 1, 1994

By Denise Crocce Romano Espinosa, Andrea Moura Bemardes, Jorge Alberto Soares Tenorio, Daniella Cardoso Buzzi, Tatiana Scarazzato

"In copper plating processes, a fraction of raw materials are incorporated to the final products, while other portions are discarded as effluents. In this study, the application of electrodialysis (a membrane treatment process) was studied for treatment of wastewaters from cyanide-free strike baths, in order to reuse the components of this bath: copper and HEDP. The synthetic solutions studied consider 1 % of ion concentration of the bath used in this process, simulating the rinsing waters to be discarded. The electrodialysis allowed a percentage extraction up to 73% of copper ions and 72% of HEDP from the effluent. Complexes formation between the acid and copper indicates the possibility of recovery of components in the same compartment, obtaining a concentrated solution of these substances that can be reinserted in the process, for compensating drag-out losses. A diluted solution is also obtained, that can be reused as water in rinsing tanks.IntroductionIn metal finishing industries, contaminants in wastewater and the type of treatment required are determined according to the type of operation [l]. Generally, electroplating industries employ conventional wastewater treatments, e.g. oxidation of cyanide and chemical precipitation. This stage promotes reactions with soluble compounds to produce an insoluble precipitate, removed by physical separation. The sludge is dried by press-type filters [2].In this manufacturing sector, part of the raw materials are discarded as hazardous waste. The cost of discarded compounds and the treatment and disposal of waste may compromise profit margins. In addition, water consumption per unit of production stimulates the development of methods able to recover and reuse the largest possible amount of water [3].In some plating processes, cyanide-based substances are used as complexing agents and as raw materials in form of metal salts [4]. However, the toxicity associated with cyanide has been promoting research for the development of new raw materials in plating processes.A study conducted in Brazil [4] evaluated the modification of a commercial cyanide-free bath for processes of copper coating on Zamak. In the performed study, a new alkaline copper bath was formulated using l,hydroxyethane-1,1-diphosphonic acid (HEDP), an organic compound known for forming stable complexes with metal ions.As results of the study, the operational conditions and the formulation of a bath to obtain adherent, uniform and bright layers were established (Table I) [4]."

Jan 1, 2014

By Xuewei Lv, Guibao Qiu, Jiaqing Yin, Chenguang Bai

"The iron ore sinter is one of the main raw materials for the blast furnace (BF) process. In the production of iron ore sinter, the cooling speed of the sinter determines its quality. In addition, the heat recovery devices are installed in the cooling machine for energy saving. The cooling parameters like gas flow rate and the size of sinter should be optimized for getting the gas with a higher temperature and a good quality of sinter simultaneously. In this study, the commercial simulation software COMSOL was used to establish a model for simulating the cooling process of the iron ore sinter. Moreover, three different gas flow rate (1.5, 3, 5m/s) and three different diameter of sintered particles (50, 70, 100mm) were investigated with the model. As a result, in certain porosity, a higher cooling speed was achieved when smaller size or larger gas flow rate was used. And lower gas flow rate was beneficial for the heat recovery. The model could intuitively present the exchange of heat between the sinters and air, as well as the flow and temperature fields during the cooling process.IntroductionIron ore sinter plays a great role in iron and steel industry for many Asian countries such as China, Japan and India. As a part of the sintering procedure, the impact of cooling process on the quality of iron ore sinter couldn't be neglected. On the other hand, the massive iron ore sinters which were at high temperature contain extremely large amount of heat. However, it was reported that there's very few of them recovered in China with an average recovery rate of nearly 10.5% at 2004 [1]. Thus, more reasonable cooling procedure should be developed to get high quality product and heat recovery rate simultaneously."

Jan 1, 2011

By Jinliang Zhang, Jian Pan, Deqing Zhu

"Limestone and burnt magnesite were added to vary MgO content and basicity (CaO/SiO2 ratio) of pellets for investigating their influences on the properties of specularite pellets. At fixed MgO content, the addition of limestone does not affect on the properties of green balls significantly. The addition of burnt magnesite has obvious influence on the quality of green balls, especially on the thermal shock temperature. Without burnt magnesite, the thermal shock temperatures are about 400°C, and, the thermal shock temperature increases to 600~630°C by adding burnt magnesite. For preheated pellets, when the burnt magnesite is added, the compressive strength will be decreased. For roasted pellets without burnt magnesite, the calcium additives can form binding phase of calcium-ferrite, and suitable liquid phase will improve recrystallization of hematite, but excessive liquid will destroy the structure of pellets, so the compressive strength of pellet increases firstly and then decreases. When adding burnt magnesite, the compressive strength will increase as the basicity increases. When the basicity is more than 0.2, the compressive strength of the pellets various MgO content and basicity is above 2500N/pellet and then MgO-bearing fluxes can be added to prepare pellets with good high temperature properties.IntroductionWith the rapid development of the steel industry in China, oxidized pellets, possessing good mechanical and metallurgical properties, are becoming indispensable burdens for blast furnace ironmaking [1-3]. However, this has resulted in the shortage of domestic iron concentrates, so many Chinese steel plants begin to use imported hematite concentrate to prepare pellets. Compared with magnetite pellets, the hematite pellets require high roasting temperature and narrow roasting temperature range (1300–1350°C) and possess low compressive strength [4,5].1"

Jan 1, 2012

By Z. W. Zhang, Songsong Xu, Jinhui Li, Yun Zou, Yu Zhao

High strength low alloy (HSLA) steels with high strength, high toughness, good corrosion resistance and weldability, can be widely used in shipbuilding, automobile, construction, bridging industry, etc. The microstructure evolution and mechanical properties can be influenced by thermomechanical processing. In this study, themomechanical processing is optimized to control the matrix microstructure and nano-scale precipitates in the matrix simultaneously. It is found that the low-temperature toughness and ductility of the steels are significantly the matrix microstructure during enhancing the strength by introducing the nano-scale precipitates. The effects of alloying elements on the microstructure evolution and nano-scale precipitation are also discussed.

Jan 1, 2016

By Jun Chang, Jin-hui Peng, Jing Chen, Li-bo Zhang

The leaching of indium from refractory zinc oxide flue dust(ZOFD) is attempted to utilize microwave sulfating roasting process, followed by water leaching. The ZOFD and roasted product were characterized by XRD and SEM/EDS analysis. The effects of various roasting parameters, such as roasting temperature/duration, the proportion of sulfuric acid, as well as the leaching parameters such as the leaching duration and liquid/solid ratio, were assessed. The results indicate that nearly 97% of indium could be leached under the following conditions: mass ratio of concentrated sulfuric acid to ZOFD to be 0.5, roasting temperature of 150 ℃ and duration of 1.5 hours; while the optimal leaching conditions hold at temperature of 25 ℃ for 1 hour, with 4:1 of liquid/solid ratio. The indium leaching rate by the microwave roasting increased by 8% as compared with the conventional roasting process under identical conditions.

Jan 1, 2015

By F. Robert Hubbard

IMCO Recycling Inc. has developed a new, patented technology for the production of fertilizer, K-SOIL?, as a by-product of its aluminum recycling operations. This new technology can substitute for conventional technology which now results in a saltcake residue that is placed in 'landfills. Four years of research and development work by IMCO culminated in a U. S. patent issued April 5, 1994. As part of the technology development effort, IMCO engaged the services of a nationally renowned research organization and a prominent university. These two organizations have conducted in-depth agronomy studies In the laboratory, greenhouse, and the field. Results have shown K-SOIL? to be performance equivalent, on a nutrient content basis, to conventional potash fertilizer. The first field applications on commercial farms were made in the spring of 1994. K-SOIL? is a potassium-bearIng, granular solid which may find use in fertilizer blends, direct application, and other forms of fertilizer products. The overall benefit of this new technology is to create a useful by-product rather than generate a useless residue and, thereby, reduce or eliminate the amount of salt cake now placed in landfills. As such, It is a significant, step toward IMCO's ultimate goal of complete recycle.

Jan 1, 1995

By J. H. Corrigan

A series of six papers describing the Falconbridge Dominicana Ferronickel project were presented at the International Laterite Symposium held as a joint project of TMS-AIME in February 1979 at New Orleans. A review of the ore mineralogy, as well as. the processing and environmental practices as they exist today at Falcondo with emphasis on modifications put into practice since 1979 are presented in two papers: Part I.- Mineralogy and Ore Dressing E.W. Lithgow - General Superintendent ? Mines Falconbridge Dominicana, C. por A. Bonao, Dominican Republic Commercial volumes of nickeliferous laterite ores overlie part of a 90 km long belt of peridotites in central Dominican Republic. Protores are serpentinized harzburgites and dunites, with lesser serpentinite. The ore mineralogy consists mostly of goethite, serpentine-group minerals, quartz and poorly crystallized, X- ray amorphous materials. Minor constituents are hematite, gibsite, olivine and enstatite. In the Ore Dressing plant, the mine feed is subjected initially to proper sizing and blending to produce a homogenized mix. Subsequent drying and upgrading, by selective crushing and screening of rock kagments through a Barmac circuit, complete preparation of the ore for pyrometallurgical processing. Part II.- Pyrometallurgy, Fuel and Power Generation J.H. Comgan - Manager ? Production Falconbridge Dominicana, C. por A. Bonao, Dominican Republic Falcondo's energy requirements are based on oil which is refined on site to provide distillate to carry out drying and selective reduction of the nickeliferous ore in the shaft furnaces, plus bunker oil to produce electrical power for process melting, refining and ancillary use. The dryer product at 1.68% Ni is briquetted and passed counter current to hot reducing gas in 12 vertical shaft furnaces. The hot calcine discharge is melted in two high power electric furnaces at very high secondary voltage. The crude ferronickel is ladle refined and cast as 15 kg ingots or 125 gm ferrocones.

Jan 1, 1993