By G. L. F. Powell

g samples of Cu-20 wt pct Ag alloy have been mdercooled to a maximum of 197°C by melting under a slag of commercial soda-lime glass in a vitreous silica crucible. No grain refinement of the primary copper was observed in samples undercooled to the maximum of 197°C. When the samples contained a small amount of oxygen, the copper dendrites were partially recrystallized at undercoolings greater than 97°C. In previous papers'-3 reporting the grain structure of undercooled silver and copper, it was observed that grain refinement was dependent on both undercooling and oxygen content. Grain refinement occurred in undercooled silver when the degree of undercooling exceeded the range 153" to 175"C, while in Ag-0 alloys (0.12 wt pct) fine equiaxed grains were exhibited when undercooling was greater than 50°C. Similarly, copper samples undercooled as much as 208°C displayed fan-shaped growth from a single nucleation site, while the grain structure of Cu-O alloys (0.08 wt pct) was fine and equiaxed at undercoolings larger than 150°C. Thus the presence of oxygen greatly reduced the undercooling at which grain refinement occurred. It was also observed that the change in grain size resulted from recrystallization and was not due to an enhanced nucleation rate in the liquid-solid transformation. It is possible that the influence of oxygen on recrystallization is due primarily to its presence as a solute element. walker4,' reported that, although a grain size change did not occur in pure nickel until the undercooling exceeded 150°C, small grains were observed in samples of Ni-Cu alloy solidified at small and large degrees of undercooling. Jackson et al.6 suggested that the fine grained structure of the Ni-Cu alloy resulted from the melting off of dendrite arms during recalescence. This remelting process may occur in alloys as a result of segregation during freezing which causes a variation in liquidus temperature from point to point within a dendrite. It was therefore decided to undercool copper with a metallic alloying element to ascertain whether the presence of a metallic solute would have a similar effect to oxygen in inducing grain refinement. A Cu-Ag alloy was chosen, since both metals had been shown to behave similarly on undercooling. The alloy Cu-20 wt pct Ag was selected since the eutectic constituent outlines the initial growth form of the primary copper, so that the as-frozen grain structure is not obscured if subsequent recrystallization occurs. This paper describes the results of undercooling experiments carried out with Cu-20 pct Ag samples undercooled to a maximum of 197°C and the effect of oxygen content on the grain structure of the undercooled samples. EXPERIMENTAL Melting was carried out in a small cylindrical resistance furnace using "fine" silver granulate and oxygen-free high conductivity copper. The procedure adopted was to melt the required quantity of silver in air in a clean vitreous silica crucible for approximately 15 min, freeze, and add granulated commercial soda-lime glass to form a complete surface slag cover, after which the sample was melted and frozen several times to reduce the oxygen content. The glass slag cover was approximately 3 in. thick. Pieces of copper (=50 g) were added to the crucible until the required quantity to make 350-g samples of alloy had been charged. Each piece was added quickly to the crucible which was held at a temperature slightly above the melting point of silver. The piece was quickly pushed beneath the glass to minimize oxidation and any oxide coating usually decomposed before the piece had settled down into the silver. After the full quantity of copper had been added, the melt was stirred with a silica rod to hasten homogenization and a Pt/Pt 13 pct Rh thermocouple enclosed in a vitreous silica sheath inserted for temperature measurement. Heating and cooling curves were recorded on a potentiometric chart recorder fitted with a zero suppression unit. The milli-voltage range of the recorder was adjusted so that temperatures could be read to 1°C. Heating and cooling curves were taken every hour until three consecutive readings gave the same solidus-liquidus range, consistent with the solidus-liquidus range for this alloy composition by reference to Hansen and Anderko.7 Metallographic examination of samples frozen at this stage, failed to show any variation in composition from bottom to top of the ingot. Consequently, it was considered that the melt was homogeneous at this stage and undercooling experiments were then car-

Jan 1, 1970

By G. H. Enzian

W. C. Ellis—The intergranular fracture observed by these authors in brass seems to be characteristic of metals when tested under similar conditions. It has been observed by us in room temperature tests on lead alloys subjected to constant stress when the stress has been low enough to afford a small strain rate. If, however, the test be carried out at a high stress and therefore at a large strain rate, a characteristic, tapered, transcrystalline fracture is obtained. The same change of fracture has been observed by others with decrease of strain rate and increase of temperature for other metals—for example aluminum—and may be presumed, as the authors point out, to be general for metals. These findings suggest a plastic flow mechanism under conditions of small strain rate and high corresponding temperature differing from classical block slip. The required conditions point to a process fundamentally diffusive in nature—a less organized process than block slip. Nabarro18 has shown that plastic flow can occur by stress induced diffusion of vacant sites— a process of self-diffusion. Movements of a pseudo-viscous nature at grain boundaries are suggested in the work of Ke.15 Deformation near to a grain boundary by other than a slip mechanism appears necessary to Boas and Hargreaves.19 Wood and Rachinger20 report a cellular structure in slowly deformed alumi- num—the cell size is larger, the higher the temperature and the slower the strain rate. Presumably in the latter case diffusive movements occurred in the cell boundaries. In any case the nonslip mechanism seems somewhat obscure and further work is indicated. Such studies will undoubtedly clarify the nature and behavior of lattice imperfections—the very core of the strength and plastic properties of metals. F. H. Wilson and E. W. Palmer (authors' reply)—It is certain that the metallic behavior which has been termed "creep" includes many interdependent phenomena of which a nonslip type of plastic flow may well be one. The reports to which Mr. Ellis refers are illustrative of the many different observations that must be correlated for a complete understanding of creep. The list could be extended considerably. For example, we ourselves have been impressed by the sensitivity of creep phenomena to the presence of minor impurities and feel that this aspect of the problem warrants more thorough study than it has yet received. References 18 F. R. N. Nabarro: Report of Bristol Conference on Strength of Solids. P. 75, (1948) London. 19 Boas and Hargreaves: Proceedings Royal Society. (1948) 193. 89. 20 wood and Rachinger: Journal Institute of Metals. (1949) 17, 237.

Jan 1, 1951

By D. J. Schmatz, H. I. Aaronson, H. A. Domian

Diffusion kinetics in disordered hcp Cd-Mg alloys have been investigated by means of the Kirkendall effect and concentration-penetration curves determined with an electron-microprobe analyzer. Self-diffusion coefficients of both species were determined at the three marker compositions obtained, averaging 27.6, 46. 7, and 78.1 at. pct Mg, by means of the Darken analysis. These coefficients were then corrected for the unequal and concentration-dependent partial molar volumes of the two elements with the Balluffi analysis, and for the vacancy flux effect by the Manning analysis. The latter correction reduced the Balluffi correction produced larger changes in the self-diffusiv-ities; neither, however, produced statistically significant changes in the Do's or the H'S. The most striking result of this investigation is that at all three compositions and at all temperatures studied both the uncorrected and corrected self-difjusivities of magnesium are higher than those of cadmium. The Cd-Mg system is the first one found in which the higher melting, lower vapor pressure element diffuses more rapidly. Both an empirical correlation due to Toth and Searcy and considerations of the atomic mechanism of diffusion indicate that this anomaly is probably due to a comparatively low value of the activation energy required for a magnesium atom and a vacancy to exchange sites, perhaps occasioned by the higher compressibility of magnesium atoms. KIRKENDALL effect studies have been previously reported for only two hcp solid solutions: the E phase of the Zn-Cu system1 and the a phase of the Cd-Hg system.' In neither investigation were the marker-movement studies supplemented with the concentration-penetration curve determinations necessary to evaluate self-diffusivities by means of the atano and the Darken analyses. The present program was undertaken to obtain both types of data on a hexagonal solid solution in order to provide more detailed information relevant to the mechanism of diffusion in this type of lattice. The Cd-Mg system was chosen for this study because the disordered solid solution extends across the entire phase diagram at temperatures above 253"c5 and the substantial difference in the melting points of the component pure metals promised that marker movements would occur at reasonably rapid rates should the diffusivities of the two species be as unequal as might be anticipated. The experimental convenience of the relatively low melting points of cad-miun and magnesium and the availability of extensive and accurate activity data6 (required for application of the Darken analysis) were additional reasons for selecting this alloy system. Since the anisotropy of diffusion is not large in either pure cadmium7 or pure magnesium,' the diffusion couples were prepared from polycrystalline components. The presence of a well-defined texture in the couples—the c axis of individual crystals tended to be normal to the diffusion direction— however, provides a fair degree of crystallographic definition to the data obtained. The principal (and entirely unexpected) finding of this investigation, that magnesium, the high-melting low-vapor pressure element, diffuses more rapidly than cadmium, in contradiction to a broad range of results in fcc and bcc alloys, as well as in the previously studied hcp alloys,172 makes the self-diffusivity determinations of immediate interest in understanding the origin of this anomalous result. EXPERIMENTAL PROCEDURE The cadmium (Belmont Smelting and Refining Co.) and magnesium (Dow Chemical Co.) used in this study were both of 99.99 pct purity. Alloys containing 51.0 and 65.6 at. pct Mg were prepared from these materials by melting under a MgC12-base flux in a high-purity graphite crucible. These alloys were subsequently hot-worked and then homogenized in a helium atmosphere at temperatures close to their solidus points. Sandwich-type diffusion couples of the type g/d/g were prepared from the pure metals by solid-state diffusion. Two-piece alloy couples of Mg/65.5 at. pct Mg (Mg/gCd) and Cd/51.0 at. pct Mg (Cd/CdMg) were welded by a liquation technique. The individual components of both types of couple were initially cylinders 1.27 cm in diam and in length; the ends of these cylinders were machined accurately flat and parallel. For both welding techniques, the pure cadmium cylinders and the alloys were chemically polished in a mixture of 40 pct ethyl alcohol, 40 pct hydrogen peroxide (30 pct conc), and 20 pct nitric acid,g while those of pure magnesium were polished in a solution of 10 pct nitric acid in ethyl alcohol.' Immediately afterwards, both metals were rinsed in freshly distilled acetone, and then in similarly purified methanol.' The Mg/Cd/g couples were assembled in a carefully cleaned stainless-steel welding fixture, in which a screw operating through a self-centering arrangement permitted a controlled pressure to be exerted upon a couple prior to welding.'' Tungsten marker wires 0.005 cm in diam were placed at the d:g interfaces of some of these couples, and imbedded in the couples during the application of pressure. As soon as a couple had been assembled, the welding fixture was inserted into a Pyrex capsule containing a packet of zirconium chips at each end. The capsule

Jan 1, 1967

As knowledgeable men in the industry know, a mineral occurrence is found through prospecting but an ore deposit is "made" -made through, first, imaginative and effective exploration; thence through efficient engineering, sales and management. There are two main phases of exploration-reconnaissance and target investigation-each of which can be further divided into two additional stages (see accompanying table). The search for a new ore deposit within a known and geologically mapped mining district involves only the last two stages, whereas the search for a new orebody in a virgin geologic environment involves at least three stages and often the full sequence. Of course, some of the exploration stages may be bypassed depending on available results of previous mineral surveys and/or exploration by individuals, business concerns, and governments.

Jan 10, 1967

By D. H. Forbes, H. M. Manasevit, F. L. Morritz

Single-crystal thin films of molybdenum have been grown. by the pyrolytic decomposition of molybdenum hexafluoride in a hydrogen ambient on various insulating substrates at temperatures front 650° to 900° C. Single-crystal discs of various orientations of magnesium aluminate spinel, a aluminum oxide, magnesium oxide, and the natural facets of beryllium oxide were all observed to exert epitaxial control on the depositing film. Determinations of the crystallographic relationships existing between film and substrates have been made, using X-ray diffraction three-circle goniometry and Laue back-reflection techniques. Using these data, crystallographic overlays have been constructed which suggest a possible interfacial geometry on the basis of a match between metal deposit atoms and metal ion sites in the substrate. A continuing program has been in effect in the Auto-netics Laboratories over the past several years aimed at the development of electronic materials in new and useful forms using chemical vapor deposition techniques. During the course of these investigations, the epitaxy of silicon1"5 and tungstenep7 on single-crystal metal oxide insulators was studied extensively. The deposition of molybdenum is a logical extension of the tungsten work since the crystal structure is identical and the lattice dimensions differ by less than 1 pct. The pyrolytic decomposition of molybdenum hexafluoride in hydrogen was used to grow molybdenum films on the oxide substrates AlzOs, MgA1~04, MgO, and Be0 at from 650" to 900°C, depending on the substrate material. Under the experimental conditions to be described, monocrystalline films of controlled orientation were obtained. The materials investigated and their crystal structure are listed in Table I. EXPERIMENTAL The molybdenum depositions were effected by the hydrogen reduction of molybdenum hexafluoride (MoFe) in a flowing system of hydrogen at atmospheric pressure. The schematic of the apparatus is shown in Fig. 1. The hydrogen, purified by passage through a heated palladium thimble, was mixed with the vapor of the liquid MoFe maintained in a steel bottle at room temperature (25°C). The mixture was passed over the substrate, which was heated by rf induction of a sup-

Jan 1, 1969

By [Dipl. -Ing. ] Karl Angerer

The "New Austrian Tunneling Method" is one of the most significant developments in European tunneling in the last 15 years. I hope this report will show the significance of this tunneling method, which was developed in Austria exactly 18 years ago and which is now used in many European countries. In Austria from 1948 to 1953, the Moll tunnel with a length of 11.6 km (about 7.3 miles) was constructed as a part of the Kaprun power plant. Depth of overburden varied from 1000 to 1400 m, and there were many rock bursts in calcareous-schist formations. Here for the first time it was found that a thin concrete lining would help to prevent rock bursts if it was sprayed on the rock soon after blasting. During construction of the Prutz-Imst tunnel in Austria from 1953 to 1956, the shotcrete lining was sprayed on the phyllite surface a certain distance behind the blasting face to prevent rapid rock decomposition. This method was also tried in soft-rock sections of the tunnel where steel and wood supports usually were necessary. To prevent loosening of the rock, application of the sprayed concrete was tried immediately after blasting. This method made it possible to tunnel through very soft ground. Where necessary, the shotcrete was supplemented by steel arches and mesh reinforcement. At that time (1953-1956), the machines and equipment for guniting or spraying concrete were being improved rapidly and it became possible to spray aggregates up to 25 mm in diam. Hardening accelerators brought quicker strength and better adhesion of the shotcrete-this also made it possible to use the method in wet tunnels. If the tunnels are extremely wet or flowing with water, it is necessary to seal off the wet rock or drain the water, using, for instance, the Oberhasli method. After these first successful steps with the new Austrian method, large portions of the Schwarzach power plant in Austria were designed and built. At this operation, shotcrete was used almost exclusively for tunneling work. It was on this site where, for the first time, a tunnel 120 m long with a 45-sq- m section was driven through overburden without one piece of timber

Jan 1, 1970

By William Kelly

An extensive swamp covers a large part of the town-site of Norway and adjacent laud. Through this swamp run two parallel oreformations. In the north one is the Aragon mine. The south one passes into the swamp on the Harrison property. On the edge of the swamp, about 1000 feet from the Aragon mine, a diamond drill, in the fall of 1889, located the ore-bearing formation and a probable ore-body. To explore further and develop this ore, the Penn Iron Mining Company proposed, in the spring of 1890, to sink a shaft. The drill had shown the depth of the glacial drift to be more than 60 feet. A test-pit near the location of the proposed shaft had struck, at a depth of 20 feet, an amount of water which a 200gallon pump was unable to lower. At the Aragon, a few years before, a shaft had been sunk to hard pan with great difficulty and many delays by the usual method of driving laths. Under the conditions it was decided to sink a caisson- or dropshaft. Two 40-horse-power boilers, a Lidgerwood engine with 4foot drum, and a good derrick were set up; and two No. 10 Kuowles

Jan 1, 1892

By William P. Blake

This camp is just now startled by the alarming suggestion that unless there shall speedily be an appreciation in the value of silver, and a decrease in the cost of salt, it will be prudent business policy to close the Alice mines and mills until the conditions of production are more favorable. Such an event would be a great blow to the prosperity of Butte. It would throw some hundreds of men out of employment, and it might lead to the adoption of the same policy by other companies, which, like the Alice, have not been able to pay dividends to their shareholders for a long time. The question arises, and becomes emphatic: If, under the present adverse conditions, the mines and mills cannot be made to pay a proper profit, why should they continue to be worked ? The owners mentally ask: Shall we go on exhausting our mines, pouring out a stream of silver for the maintenance of the community, and the support of the rail ways, or shall we husband our reserves, withdraw the miners from our slopes, and wait for more favorable conditions ? This is the impending question, and all concerned dread to meet and answer it. Let us briefly review the situation and forecast, if possible, what the solution of' the problem will be. It must be understood that the discussion does not include, or refer to, the immense copper-producing interests of the camp, which may or may not be upon a very much more satisfactory basis. It will be confined chiefly to the operations of the Alice company, sta tistics of which are at hand, without involving the other silver com panies in the conclusions beyond those inevitable from well-known facts, patent to all. There are at present in Butte and in its vicinity in the principal mills an aggregate of 290 stamps dropping upon silver-ores: Alice,...........80 stamps. Moulton,. .........40 " Lexington,...50 " Silver Bow,.........30 " Blue Bird,..........90 " The Alice mills at present, with their 80 stamps, devour, in round numbers, from 100 to 120 tons a day. The actual amount

Jan 1, 1888

By P. Barnes

Several statements have been made to the Institute, somewhat detached from each other, as to the cost of some parts of these works, but they have not included any extended description of the buildings or machinery. The general plan of the work connected with the water supply differs, in some important details, from that which has been common either in the Pittsburgh district or elsewhere, and a somewhat extended description may be of interest to the Institute, in connection with a note of the cost of the work. The plan as a whole, and nearly all the important details, were developed by Mr. William P. Shinn, C.E., the general manager of the Company. The immediate and responsible charge of the work was in the hands of Mr. John C. Lewis, C.E., to whom had been committed all the work of this general description, including the laying out of the whole of the foundations, the erection of the buildings, and the grading and laying down of the entire railroad system. The continuous operation of the machinery and other fixtures of these waterworks, for more than three years, has fully demonstrated the correctness and econonly of the plan adopted. No casualties of any moment have befallen the apparatus, and no improvements have been suggested as important except that the gate at the river end of the conduit should have been made more completely water-tight, so that the whole length of the conduit could be pumped out dry without resort to any temporary dam in the conduit itself. In general terms the works of the Edgar Thomson Company are situated on a plateau, about 52 feet above the low-water level of the Monongahela River, and about 2000 feet from its bank. The site of the works is bordered on one side by Turtle Creek, a small stream which drains a considerable area of coal mining territory. This creek is about 100 feet from the group of buildings which have been erected, but it flows into the Monongahela River at a point, about 1200 feet further up than that selected for the entrance to the waterworks conduit. It was ascertained by analysis that the water in the creek contains an important percentage of sulphate of lime, while the water of the river is of unusual purity, in respect of any salts

Jan 1, 1879

By Richard Dunmore

Tests of the MRDE firedamp prediction method have been carried out in a number of longwall districts with different conditions. The method itself and its development have been described previously At many test sites the prediction has been good, i.e. the calculated gas emission levels have agreed with measured values, averaged over a period of many weeks, within a few percent. In other cases, where there have been larger discrepancies between calculation and measurement, investigations have shown that these may be attributed to particular conditions of mining or geology. Recognition of these conditions in advance of mining is clearly desirable to improve the accuracy of the initial prediction. It has been shown that variations in gas emission rates depend largely on coal production in terms of the weekly advance of the coal face. Although there appears to be a random element present, variations in gas emission levels calculated from changing face advances agree well with measurement. The accuracy of prediction therefore depends on how well face advance can be forecast and needs to be updated as the working proceeds in the light of the face performance actually achieved. Continuous monitoring of the mine environment provides the information necessary to compare actual gas emission with predicted levels, and computerised systems make it possible to carry this out in real time. Predictions can thus be adjusted to take account of emission levels measured in previous weeks These adjustments, whether they are made after the first few weeks or subsequently during the district life, would also be used to alert management to particular abnormalities or significant changes in gas emission.

Jan 1, 1982

By Lane D. Schultz, John D. McLennan, Jean-Claude Roegiers

During construction of the intake tunnels for a nuclear power facility in Ohio, evidence of a potential geological discontinuity was discovered. Assuming that the discontinuity might still prevail underneath the site, it was decided to measure the stress profile across the discontinuity. This information would be used to assess future stability on the basis of predicted shear stresses acting along the fracture. Seven intervals were hydraulically fractured to determine the magnitude and orientation of the stress tensor, in order to infer the shear stresses acting along the discontinuity. The formation consists of tightly interbedded shales. This, in combination with the shallow depths, would be expected to lead to horizontal hydraulic fractures -- a situation which generally provides limited information. Careful testing procedures, and meticulous interpretation, allowed the determination of the horizontal stress components as well as the vertical component, via the initiation and/or propagation of multiple fractures. The measured stresses fall within the range of stress magnitudes and orientation determined in other areas of the northeastern and north-central United States and in southern parts of Canada. In addition, a small stress gradient anomaly was recorded at depth. On a different scale, the measured stress regime is also evaluated in light of the regional geological setting.

Jan 1, 1982

By William R. Webster

I have continued the investigation of the Pottstown Iron Com pany's basic Bessemer keel plates on the line referred to in my paper of last October (Trans., xxi., 766)) and have added a study of the hardening effects of sulphur, which were not taken into account at that time. The results are so encouraging that I now give them in full. For some months we have graded all the steel at these works by the table given in my former paper, and checked the grading by the forging-tests as described in the paper of Mr. Joseph Hartshorne, read at the same meeting (Trans., xxi., 748). The steel thus graded was bloomed for the plate orders. Then one slab was rolled into a plate for the order, and a tension-test was made of this plate. By the result of this tension-test we were guided in rolling the balance of the heat. Out of several hundred heats graded in this manner, 95 per cent. met the requirements of the orders in every respect, and were accepted; but these results will no doubt be improved upon, when the influence of sulphur is also considered.. The hardening effect of sulphur seems to be about 500 pounds per each .01 per cent. of increase. In the table accompanying the pres ent paper, the ultimate strength with .06.5 per cent. sulphur agrees with the old table where sulphur was not considered; that is, for all steels with less than .065 per cent. sulphur we now get lower re sults, and for those with more sulphur, higher results. Making this allowance for sulphur, the assumed ultimate strength of a 3/8-inch plate of pure iron is reduced from 38,000 pounds per square inch to 34,750 pounds. With this as a basis, I have constructed my new table, giving each of the elements, carbon, phosphorus and manganese the same hardening effect as before, to wit : Carbon is credited with a constant effect of 800 pounds per each, 0.01 per cent. Phosphorus shows greater effect in high-carbon than in low-carbon steels. For 0.07 and 0.08 C, it has about the same effect as carbon, that is, 800 pounds for each .01 P. This increases to 1500 pounds per .01 P in 0.15 C steel, or nearly twice the effect of carbon. This

Jan 1, 1894

By Donald Barton

THIS paper outlines a time-saving graphical method of calculation for application to the interpretation of observations with the Eötvös torsion balance. Preliminary to the treatment of this short cut method which has been found practicable, the principal formu-las by which the student of interpretation can calculate the gradient and differential curvature produced by different types of bodies in different types of situa-tions are presented and discussed. It is necessary to split most geologic bodies into a series of simpler ones for which not too complicated formulas are avail-able. The gradient and differential curvature effects are calculated for each of the simple bodies and then summed to the total effect for the whole body. The calculations are considerable in number and, though more tedious than difficult, should be' entrusted to an experienced calculator. Considerable facility in qualitative interpretation can be acquired by the geophysicist from experience and from a thorough study of the types of gradient and differential curvature anomalies produced by the dif-ferent types of possible structural situations. How-ever, semi-quantitative calculations' of the probable structure bring out many relations that are not evident in a simple inspection of torsion balance results ; it throws out as impossible or improbable certain of the alternative structural possibilities that may seem equally probable under simple inspection of the results; it will determine more accurately the position of the crest of the structure; and reduce considerably the un-certainty in the interpretation and it is necessary to intelligent interpretations. The calculation of such cross-sections consists of a trial-and-error calculation of a body that will give gradient and differential curvature effects as closely as possible the same as those observed. From his knowledge of the gradient and differential curvature produced by different types of bodies, the geophysicist sketches a tentative cross-section of the structure as indicated-to him-by the observed results of the torsion balance survey, and the calculator then splits the struc-ture into blocks, and calculates the gradient and differ-ential curvature block by block. If, as rather usual, the calculated .gradient and differential curvature pro-files diverge considerably from, the respective observed ones, it is necessary to add and subtract blocks from the cross-section until a close agreement is obtained .between the calculated and observed profiles. The com-plete calculations have to be gone through for each block that is added or subtracted.

Jan 9, 1928

Jan 1, 1948

Jan 1, 1948

Jan 1, 1943

Jan 1, 1943

Jan 1, 1936

Jan 1, 1936

Jan 1, 1925