By Wufeng Jiang, Jiann-Yang Hwang, Suju Hao, Yuzhu Zhang

Magnetite powder and coke powder were used as experimental materials and H2 as reducing agent in a high temperature vacuum tube furnace. The change rules of magnetite powder (MP), mixed coke powder and magnetite powder (MCMP), and carbon coated magnetite powder (CCMP) in the process of reduction were studied. The samples were determined by field emission scanning electron microscopy and X-ray diffraction. The results show that, with the increase of reduction time, the reduction degree of magnetite powder is improved. Under the same reduction conditions, the addition of coke powder improves the reduction rate. Compared with MP, when the reduction time was 120 min, the reduction degree of MCMP was 30% greater; and the reduction degree of CCMP was 39% greater. The mixed grinding of magnetite powder and coke powder is a better way to add carbon. Under the same reduction conditions, compared with MCMP, the reduction degree of CCMP was 9% greater when the reduction time was 120 min. After the reduction of CCMP, the number of pores in the sample increased and the structure was loose. The results of this study have some reference value for improving the reduction rate of magnetite powder.

Mar 1, 2018

By Tianzu Yang, Weifeng Liu, Shu Bin, Lin Chen, Wanda Bin

"Vanyukov Process has been mainly applied for processing copper and nickel sulfide ore for more than 30 years. Based on the understanding of the Vanyukov Process, researchers from China introduced the technology into the areas of lead, antimony and bismuth extraction by changing the furnace structure and technical flow, which greatly extended the application area and raised the processing efficiency, thus developed the oxygen-rich side-blow bath smelting (OSBS) technology in 2000. This contribution reviews the history of OSBS technology from four respects: the quantity, the furnace structure, the process flow and the application area. Its potential research direction and industrial application are also summarized.IntroductionVanyukov bath smelting furnace and related bath smelting technology were developed by researchers from Soviet Union who devoted comprehensive research on fundamental theory as well as engineering technology [1,5]. Vanyukov process has been applied for large industrial production since the 1970s and it is still one of the major methods in modem pyrometallurgy process. The appearance ofVanyukov double district furnace and joint double furnace in the past ten years, which are applied for copper smelting, is the most valuable advances of the Vanyukov process [7,8,9]. However, the application ofVanyukov process was limited in copper and nickel sulfide ore smelting, and few countries adopted this process except Soviet Union."

Jan 1, 2013

By Jiling Wang, Xuefeng Liu, Haojian Duan, Lifeng Zhang, Ying Ren, Wen Yang

"In order to study the influence of MgO-C refractory on steel cleanliness and inclusions during steelmaking process, and to understand the reaction mechanism deeply, laboratory deoxidation and equilibrium experiments were respectively performed in MgO crucibles at 1873K. In the former experiment, after Al addition, steel samples were taken at different holding time. In the latter experiment, different slag components and different contents of carbon and aluminum in steel were considered respectively. The inclusion characteristics of each experiment were analyzed. The results showed that with the increasing of holding time after deoxidation by Al, MgO existed in the small inclusions firstly, and then in the large ones such as the clusters. The MgO content in the inclusions increased with the increasing of holding time, indicating that the MgO in crucible could be individually reduced by the aluminum in the molten steel. The reaction could occur within nine minutes.IntroductionNon-metallic inclusions would have positive or negative effect on steel quality depend on the quantity, size and composition of inclusions. Large inclusions are always detrimental. From the point of view of inclusion property, plastic inclusions are required by steel cord, while hard inclusions are preferred by pipeline steel. One of the most important ways to increase the steel quality is reducing the inclusion size and controlling the inclusion composition in steel. Nowadays, MgO based refractory is used as ladle glaze material with more and more frequency, which results in different inclusion characteristics in molten steel, for example, the inevitable generation of MgO contained inclusions during ladle treatment of steel. In other words, the inclusions in this type ladle will influence on the steel cleanliness and the product property. Thus, keeping an eye on the inclusion formation behavior in the steel with MgO-C ladle glaze is important for the steel industry. There have been a few studies in this regard. Li et al[l] studied the reactions between MgO-C refractory, molten slag and metal using a high temperature X-ray radiographic apparatus. They found that the local corrosion was regarded as due to the cyclic dissolution of MgO and graphite in the refractory into slag and metal phase. The gas bubbles formed according to the reaction of (FeO)+C(s)=Fe(l)+CO(g) greatly influenced the corrosion. On an industrial scale, Du[2] found that ladle glaze is a major source of inclusions in the ladle. An experimental study has been performed by Lehmann in order to estimate the importance of the reaction between a MgO-based tundish refractory and an Al-killed steel[3]."

Jan 1, 2014

By Edward Peters

Scandium (Sc) has unique properties and is one of the more valuable elements in the periodic table. Scandium can be used in solid oxide fuel cells and to produce high strength aluminium alloys of value, for example, in the aerospace industry. Scandium is often grouped together with the rare earth elements (REE). Amongst others, scandium can be found in bauxite residues, so called red mud. It is possible to extract and enrich scandium from red mud by leaching and solvent extraction. Scandium can then be recovered from the pregnant strip liquor by crystallization. The strip liquor will however still contain certain impurity elements. In the present work, a method for obtaining a pure scandium solid phase by direct crystallization from the strip liquor is evaluated. It was found that Fe and Ti co-precipitate with Sc under the conditions employed.

By Takahiro Furuzono

Saganoseki Smelter and Refinery of Pan Pacific Copper Co., Ltd. started treating copper anode slimes using a unique hydrometallurgical process in chloride media in 1997. The process comprises the following stages, decopperizing, wet chlorination, solvent extraction for gold, silver chloride reduction, and separate reduction stages that treat the gold extraction raffinate with sulfur dioxide gas. Precious metals and rare metals in the copper anode slimes are dissolved in an aqueous solution of hydrochloric acid by oxidative leaching, which is termed wet chlorination. Gold is efficiently extracted from the chlorination liquor by dibutyl carbitol in the solvent extraction stage. Gold is reduced by oxalic acid from goldloaded dibutyl carbitol and recovered as gold powder. The gold powder is cast directly into granules or ingots of more than 99.99% purity without electrorefining. Selenium is recovered as a selenium residue by reduction with sulfur dioxide gas and refined through vacuum distillation. The plant was designed to process 132 tonnes of copper anode slimes per month and has a current capacity of 206 tonnes per month due to several enhancements. Compared with the conventional process, the hydrometallurgical process described here provides some advantages, in particular, a higher product quality, shorter gold-retention time, and reduction in environmental load.

By Deepu Philip, Pratik Agarwal, Ajay Kumar Shukla, Ishani Shukla, G Rajesh

Steel plants generally employ static BOF end point control models to arrive at a given temperature and chemistry at the end of blow. These end point models have now been supplemented with chaos control models to steer the blowing process in the right direction while the blow is in progress. Merely arriving at the correct end point temperature is however not adequate because in the subsequent stages as well the temperature variations can be large and unpredictable. The present paper deals with an integrated model to take into account the effect of all parameters affecting temperature and composition from tapping to the start of casting to minimize the use of LF or aluminum heating, and also minimize grade mixing. The application of lean operations strategy is explained in which the previous “Push System’ is changed to a “Pull System”, minimizing the use of ladle furnace or aluminum heating during steelmaking.

Jan 1, 2014

By Wenqiang Bao, Qijie Zhai, Ting Wang, Shaobo Zheng, Huigai Li

The type of inclusions with different sizes in as-cast low carbon steel strip which is deoxidized by Si–Mn has been characterized by scanning electron microscope (SEM) and transmission electron microscopy (TEM). SEM observation and analysis suggested that the type of inclusions larger than 1 μm is manganese silicate. TEM analysis was carried out to investigate the composition and structure of nano-inclusions. Inclusions with diameter about 100 nm are manganese silicate, MnS–Si(Mn)Ox complex particles and isolated cubic Al2O3. Furthermore, HREM observations have revealed that there were two kinds of ultrafine particles in size range of 5–10 nm. One is spherical monoclinic Cu2S; the other is silicon-iron oxide particles with morphology of long strip. In addition, some thermodynamic calculations were performed to explain the corresponding relation between the type of inclusions and their size.

Mar 1, 2017

By Mairyanne S. S. Souza, Sergio Neves Monteiro, Victor Tomazinho Bartolazzi, Dienifer Daiana Konzen

Clay is used in the production and manufacture of materials for the construction of buildings from remote periods. Advances and improvements of its properties have allowed several applications to this raw material. In this work the quality of four types of ceramic tiles manufactured or used in the northwest of the state of Rio de Janeiro and in the southeastern state of Minas Gerais was evaluated. Geometric, physical and mechanical aspects were evaluated according to the Brazilian standard NBR 15310:2009. The results indicate numerous nonconfor- mities with highlights for geometric parameters, surface flatness and yield tests. The nonconformities found in the samples indicate that there was a failure in the production control of the product and in the approval of the control of the lots.

Mar 1, 2018

By Shusen Cheng, Kun Yan

An elastic-plastic stress mathematical model of hot blast stove shell has been established in order to investigate the stress distribution and deformation of the shell. The results show that stress concentration happens along the intersection line of hot blast stove body and the hot blast manifold. The plastic deformation occurs on the hot blast outlet in blast period. The deformation degree of the hot blast shell near the blast outlet in blast period is much larger than that in combustion period. In blast period, the shell near the blast outlet elongates along the horizontal direction and shortens along the vertical direction, the shell near the outlet deforms into an oval. And in combustion period, its deformation isn’t obvious. The repeated deformation of the shell near the outlet between different periods may cause the refractory brick damage and be harmful to the long campaign life of hot blast stove.

Mar 1, 2017

By Shusen Cheng, Dongdong Zhou, Yongqiang Bai

The strength of sinter could affect the permeability and CO gas utilization of blast furnace, and one of the main impacted factors of sinter strength is crack. With the widely use of vanadium-titanium sinter in China, the blast conditions of some blast furnaces became worse since the vanadium-titanium sinter has been added. However, there have little public research for this phenomenon. In this paper, the influence of titanium content on the sinter ore phase structure and crack were studied by DMRX polarizing microscope. In addition, the influence of basicity and oversintering on the sinter ore phase structure were also investigated. The observed results of vanadium-titanium sinter were compared with typical sinter in China, and the influence law of titanium content on the sinter ore crack was obtained.

Mar 1, 2017

By Xueqin Li, Xuewei Lv, Yu Zhang, Wenchao He

In recent years, a new process of “direct reduction-electric furnace smelting separation” has been put forward and developed for recovering the iron, vanadium, titanium and chromium to make full use of the chromium-bearing vanadium titanium magnetite. In the present work, FactSage, one of the most frequently-used thermodynamic calculation software, was used to calculate the migration of Fe, V, Cr and Ti with different nC/nO (mole ratio of carbon and oxygen). The calculation results indicate that the recoveries of Fe, V and Cr increase with increasing nC/nO and temperature respectively. In addition, the recoveries of Fe, V and Cr are up to 90% when the nC/nO value is more than 1.15.

Mar 1, 2018

By Ming-Feng Ye, Guang-liang Wu

The microstructure and mechanical strength variations of chromite pellets preheated and roasted in air were studied systematically. The results show that the chromite (Fe,Mg)(Cr,Fe,Al)2O4 is oxidized to magnesium-rich (Mg,Fe)(Cr,Fe, Al)2O4 and ferrochromium complex oxide (Cr,Fe,Al)2O3 in the preheating process over 500 °C. When the temperature is higher than 1000 °C, the new phase (Cr,Fe, Al)2O3 is formed, which is mainly distributed in the outer layer of a single chromite particle. Inner the particles there are acicular (Cr,Fe,Al)2O3 and unoxidized (Fe,Mg) (Cr,Fe,Al)2O4, which forming an interwoven structure together. The oxidation rates of pellets can reach to superior limits in 20 min. With the temperature increasing from 950 to 1300 °C, the mechanical strength and oxidized rates increase to varying degrees correspondingly.

Mar 1, 2018

By Shusen Cheng, Kun Yan

A three-dimensional mathematical model of hot blast stove pipe shell has been established and used for analyzing the stress distribution and deformation. The results show that stress concentration happens along the intersection line of hot blast main and the hot blast manifold. There is no plastic deformation on the whole pipe region. The shell near the intersection elongates along the vertical direction and shortens along the horizontal direction, and deforms into an oval. The shell of hot blast main rises up, and inclines upward around the end of hot blast main. The hot blast main moves away from the hot blast and the displacement near the middle region is larger, the main deforms into an arch on horizontal surface. The deformation of shell may form a gap between shell and refractory inside and damage the security and stabilization of hot blast stove piping.

Mar 1, 2017

By Shiju Zhang, Yongnian Dai, Songli Liu, Kuisong Zhu, Wenhui Ma, Li Cao

There is an abundance of vanadium-titanium magnetite in Panzhihua, China, which contains more than 8.73 x 10^8 tons of TiO2 accounting for 90.6% of the national reserves. To fully utilize Panzhihua titanium resources, many processes were proposed. The present status and future development of technologies for comprehensive utilization of vanadium-titanium magnetite including blast furnace, electric smelting, and ilmenite upgrading processes are reviewed.

Mar 1, 2017

By Egil Krystad, Merete Tangstad, Kai Tang, Gabriella Trenell

"A new UMG-Si refining concept has been proposed in this paper. Liquid Si and another liquid metal phase (Me) were separated by the molten slag spontaneously based on their different physicochemical properties. Two metal/slag distribution reactions are able to occur in the system simultaneously. Experimental investigation on the B and P distribution equilibria among Si/slag/Me was carried out in the graphite resistance furnace under the inert atmosphere. The B and P doped silicon was in equilibrium with either the SiO2-CaO or SiO2-CaO-l0%CaF2 slags at 1600 and 1650°C, respectively. The pure Fe and Cu metals were used in order to ""capture"" B and P in the slag phases. B and P in samples were determined by the ICP-MS. B and P distribution coefficients for the Si/slag/Me equilibria were compared with the theoretical calculations. The possible kinetic barriers for the Si/slag/Me three-layer equilibria have been analyzed. The metal contaminations in the three-layer equilibria were also examined. The present study provides a new approach for the refining of MG-Si.IntroductionMost of the impurities in the metallurgical silicon (MG-Si) are rather ""dilute'', ranging from few to several thousand ppms. However, the target impurity levels for upgrade metallurgical silicon (UMG-Si) feedstock are often far below the level of ppm. In such extreme case, the conventional refining technologies face the great technical challenges. B removal by slagging has already been implemented industrially. Removal of Pis frequently carried out by the vacuum distillation. The separating treatments for B and P removals lead to increase refining cost, total CO2 emission and longer pay-back time of solar cell module.It is well known that the phosphate capacities of slags in equilibrium with liquid silicon are extremely lower. However, if we introduce another phase that possesses high ""phosphor capacity"" into the Si/slag system, one would expect to continuously remove P from Si through molten slag to the new ""phosphor capturer"". The so-called three-layer refming concept is thus proposed in the present study. Liquid Si and another liquid phase (Me) are separated by the molten slag spontaneously based on their different physicochemical properties. Two metal/slag distribution reactions are able to occur in the system simultaneously."

Jan 1, 2013

By Vineet Kumar Yadav, Akshay Dvivedi, Pradeep Kumar

Near-dry electric discharge machining (EDM) is a process variant of EDM, which uses two-phase flow of liquid and gas as dielectric medium. This article reports the results of an investigation pertaining to the drilling of holes on high speed steel (T2 grade) by a rotary tool near-dry EDM. The One-Factor-At-a-Time (OFAT) approach was used for experimentation. The effects of process parameters, viz. tool rotation speed, peak current, pulse duration, gas pressure and liquid flow rate on material removal rate (MRR) and overcut were investigated. The dielectric medium used was a mixture of glycerin-air. The experimental results reveal that rotation of the tool electrode along with high pressure of two-phase dielectric medium contribute in an effective flushing of inter electrode gap (IEG). Further, in rotary tool near-dry EDM process, higher values of current can be used. This improves process economics in terms of MRR. The MRR measured with rotary tool near-dry EDM was three to four times higher in comparison with conventional EDM. Additionally, appreciable surface quality was achieved.

Mar 1, 2017

By Wing Ka Ng

Substitution of pulverized coal injection by solid biocarbon fuel has the potential to achieve substantial reduction in GHG emissions associated with blast furnace ironmaking. A systematic evaluation was conducted on the performance of solid bio-carbons produced from a single raw biomass source using different pyrolysis technologies. The potential of solid biocarbon in reducing GHG emission of the blast furnace ironmaking process is strongly influenced by its O/C mass ratio. In order to achieve substantial GHG reduction, it is necessary to replace coal injection by solid biocarbon having a low O/C mass ratio. The pyrolysis technology and conditions employed are key parameters influencing O/C mass ratio of the resultant solid biocarbon. Close collaboration between steelmakers and solid biocarbon producers is critical for producing suitable solid biocarbon fuel to replace pulverized coal injection. A successful partnership should pave the way in achieving substantial reduction in GHG emissions of the blast furnace ironmaking process.

By Dave Tahija

"Many investigations are being performed with the goal of removing carbon dioxide from the atmosphere and permanently storing it in geologically stable settings. At the same time, carbon dioxide in the form of dissolved carbonate is steadily accumulating in the world's oceans. Both carbon dioxide sequestration and oceanic accumulation are constrained by the aqueous thermodynamics of the carbonate system. These constraints are illustrated using the STABCAL computer model to generate potential-pH and aqueous distribution diagrams of seawater in contact with various pressures of carbon dioxide gas. STABCAL diagrams and titration simulations are also used to model some potentially useful cation-carbonate sequestrationsystems.IntroductionAtmospheric carbon dioxide concentrations have risen dramatically in the past couple of centuries and are rising still, primarily as a result of human activities, especially the burning of fossil fuels. Increased atmospheric carbon dioxide concentrations have been implicated as a main cause of global warming but have other effects as well.Rising levels of atmospheric carbon dioxide result in increased concentrations of dissolved carbonate complexes in water, including the oceans. These dissolved carbonates interact with other dissolved substances, altering overall seawater chemistry, most noticeably causing lowered pH levels.Some of these chemical changes are observed directly, for instance the general drop in oceanic pH, [1], while others can be inferred and predicted using thermodynamic modeling. The chemistry of dissolved carbonate in seawater is not especially intricate, as such chemical systems go, but neither is it simple enough to be worked out on the back of an envelope. Interactions between the several simple carbonate species and all the major dissolved cations in seawater should be considered, as well as the effects of competing anions, especially chloride and sulphate, since they are much more abundant than carbonate in seawater."

Jan 1, 2011

By Zhihe Dou

SHS reaction system has advantages of heat flux density, energy concentration and reaction speed, with sufficient conditions in thermodynamic and kinetic reaction. This paper invented a new technology of SHS metallurgy of preparing melting point alloys and refractory compounds using its own chemical energy. SHS-leaching process for preparing nano boron powder or ultrafine boride powder and SHS-casting process for preparing titanium-based alloy and immiscible alloy were studied. The results indicate that highly active boron powder of greater than purity of 93%, particle size less than 100nm and purity greater than 98.5%, particle size less than 400nm REB6 can be prepared. With SHS-Casting process, the oxygen content of less than 0.59% ferrotitanium, oxygen content of less than 0.5% titanium alloy and ?40-80*100mm large size of CuCr, Cu-Fe alloy ingots were prepared. This technology has greatly enhanced the thermal reduction method added values of preparing metallurgical products and its competitiveness.

Jan 1, 2014

By M. A. Kader, M. A. Islam, P. J. Hazell, M. Saadatfar, J. P. Escobedo, A. D. Brown

The dynamic pore collapse mechanisms and energy absorption capacity of closed-cell aluminium foams subjected to low velocity impacts have been investigated. Impact experiments were carried out using an instrumented drop-tower with two impactor geometries: a 50 mm square flat steel impactor to investigate pore collapse mechanisms and a 20 mm diameter hemispherical steel impactortostudy indentation resistance.X-ray computedtomography was utilized to generate views of the deformation field within the impacted specimen. The results show that the strain rate and incident impact energy influence the energy absorption capacities of closed-cell aluminium foams. Furthermore, damage initiation, propagation and cell collapse mechanisms under drop weight impact have been elucidated.

Mar 1, 2017