By W. F. Stowasser

A downdraft traveling grate process to agglomerate pelletized iron ore concentrates has been successfully demonstrated in a pilot plant at Carrollville, Wis. Work there followed several years of development in the Allis-Chalmers Mfg. Co. laboratories, and the pilot plant phase was carried out in co-operation with Arthur G. McKee & Co., consultants and engineers to the iron and steel industry. End result of the process is conversion of iron ore concentrates into a form which can easily be transported and smelted in the blast furnace.

Jan 5, 1955

By C. Y. Clayton

In connection with certain cooperative work carried on between the Ordnance Department of the U. S. Army, the U. S. Bureau of Mines, and the U. S. Geological Survey during the year 1918, it was the writers' privilege to make metallographic examinations of a great many test bars and other pieces of nickel-steel gun forgings. The material studied came from many different steel plants throughout the country and consisted both of forgings that had been accepted by the Ordnance Department and those that had failed to pass the specified physical tests. In general, these tests require a minimum tensile strength of 95,000 lb. (42,091 kg.)! an elastic limit of 65,000 lb. (29,483 kg.), an 18 per cent, elongation, and a 30 per cent. reduction in area. An average chemical composition of the steel studied is 0.38 per cent. carbon and 2.9 per cent. nickel. The steel was of both basic electric and basic open-hearth manufacture. The object of the metallographic work was twofold: to assist in detecting defects in the steel and, if possible, to suggest remedies for the same; and to obtain as much information as possible in regard to the relation of the microstructure of the metal to its physical properties. The grcatcr part of the investigation was devoted to defective metal that failed to pass the ordnance specifications. Many types and kinds of more or less serious defects thus came under observation, but most of these were due to the attempts by the manufacturer to meet the enormous demand for ordnance steel with more or less inadequate equipment, and were soon remedied. Two defects, the so-called "flakes" or "snowflakes" and a certain "fibrous" or "woody" fracture, were encountered so frequently and were so disastrous to the steel that the greater part of the study was devoted to them. As a result much information as to their nature and their effects upon the steel and something in regard to some of the conditions that favor their development has been obtained. The purpose of the present

Jan 1, 1920

By G. A. Wells

The consumption of barytes in certain paints, polyurethane foams, seamless flooring, glass, brake linings, plastisol gaskets for food containers, and in fluids used for gastrointestinal X-ray examinations relies on the unique properties of barium sulfate. There are no readily available mineral substitutes. Barytes are also the essential raw material for the manufacture of industrially important barium chemicals. High quality barite ore has become scarce throughout the world. Processing ore into quality end products is both capital and energy intensive. These factors have tended to limit availability and increase Prices which have encouraged the use of alternative or competitive materials and restricted market growth.

Jan 1, 1981

By Allan T. Gwathmey, J. Bruce Wagner, Kenneth R. Lawless

Between 250°and 550°C in oxygen pressures of 10 to 760 mm Hg, the relative oxide thicknesses formed per unit time on the (100), (111), (110), and (320), decreased in this order. The predominant oxide orientation was (001)Fe3O4 and [110] Fe304 A small amount of a-Fe2O3 which exhibited a fiber pattern was observed in all oxides except those formed at 250°c in low oxygen pressures. IN order to understand the properties and behavior of thin films, particularly their role in oxidation reactions, there is needed more experimental information on their structure, composition, and kinetics of formation on clean surfaces of known geometry. The present study was undertaken to obtain such information for thin oxide films formed on single crystals of a body centered cubic metal, iron. Crystals in the form of spheres were used in order to expose all possible crystal planes to the reactant gases simultaneously. Using this procedure the relative rates of oxidation of all planes could be estimated, and those exhibiting, maximum or minimum oxidation rates could be selected for a more intensive study of composition and expitaxy. Since the three types of information were obtained from the same experiment using a single crystal substrate, any differences between rate, composition, and expitaxy on the several planes may be attributed to the influence of the substrate structure. EXPERIMENTAL The starting material for this study was Armco iron rods, 6 in. long and 3/8 or 1/2 in. in diam. The analysis was reported to be 99.8 pct Fe, with major impurities listed as carbon 0.018 pct, manganese 0.027 pct, phosphorous 0.005 pct, sulfur 0.029 pct, silicon 0.005 pct, and copper 0.11 pct. These rods were cleaned with ether and heated in an atmosphere of moist hydrogen at 950°C for three days. The purpose of this treatment was to decarburize the iron and to provide a consistent, uniform grain size for the growth of single crystals. Crystals in the form of rods, up to 1/2 in. in diam and 2 in. long, were prepared by a method similar to that reported by Leidheiser and Buck.2 Spherical crystals, 3/8 and 1/2 in. in diam and having a handle about 1/4 in. in diam by 112 in. long, were machined from the single-crystal rods. After machining, each crystal was etched in aqueous nitric acid to remove the cold-worked metal at the surface. Before each experiment, the crystal was polished mechanically with metallographic papers through number 4/0, and electropolished in a perchloric acid-acetic anhydride mixture by the method of Jacquet and Rocquet.3 The crystal was washed in running distilled water for at least 5 min. The excess water was blotted with a soft paper tissue, and the crystal was placed in an all-glass reaction vessel (See Fig. 1). The crystal was heated at 550°C in hydrogen for at least 8 hr prior to the oxidation in order to reduce any surface oxides and to help relieve any stresses in the metal. For the structure and composition studies, flat faces were cut parallel to (loo), (111), and (110) planes on the iron crystal spheres. The orientation of these faces was checked by a back-reflection X-ray diffraction technique. The faces were within 2 deg of the desired orientation. The flat faces were treated as described above except that prior to electropolishing they were given an additional polish on metallographic felt saturated with twenty-minute levigated alumina. After the crystal was heated in hydrogen for at least 8 hr, the temperature was adjusted to the desired value, and the hydrogen was evacuated. Commercial oxygen which had been purified by successively passing through tubes containing magnesium perchlorate, Ascarite and magnesium perchlorate was admitted to the desired pressure as measured by a mercury manometer. A resistance-wound furnace surrounded the oxidation chamber, and a temperature controller maintained the temperature within ±3°C. The furnace was provided with a small window for observing the crystal. The changes in thickness of the oxide films were followed by observing the interference colors. The oxidation was allowed to proceed until the desired oxide thickness was attained on a given crystal plane. The experiment was terminated by evacuating the oxidation

Jan 1, 1962

By Joseph B. Darby, Paul A. Beck

IN isothermal sections of several ternary systems, the a-phase was found1 to extend in the form of a relatively narrow elongated field, connecting the U-phases that are present in the adjoining binary systems. This was interpreted in accordance with the conception that the U-phase is an electron compound and the ternary U-phase fields were shown in several systems' to extend approximately in the direction of constant average d-shell electron vacancy number per atom. ' However, in the various isothermal sections of the Fe-Cr-Mo system" the ternary a-phase field was

Jan 1, 1958

By Jerry A. Selvaggi, Richard B. Jacob

The High Gradient Magnetic Separator (HGMS), also known as the High Gradient Magnetic Filter (HGMF), is an effective device utilized in magnetic separation. This method of separation is gaining popularity in the separation of submicron material containing feebly magnetics. The most common use of this type of separator is in the removal of iron stained particles to improve the brightness of kaolin clay. Potential areas for use of this magnet include: (1) desulfurization of coal (2) the clean-up of mill effluent (3) removal of fine particulate matter from municipal and indus¬trial waste (4) desulfurization of oil Design, operation, and applications of this separator are further dis¬cussed in papers by R. R. Oder (1975), and R. R. Oder and B. I. Horst (1975). This device is a system composed of an iron enclosure of high per¬mability material housing a set of electrical coils, a canister en¬closing a magnetic matrix (stainless steel wool), an electric power supply and a hydraulic system to maintain specified operating tempera¬ture conditions. See Figure 1.

Jan 1, 1984

By David M. Hopstock

The performance of the most common type of low-intensity dry magnetic separator is analyzed on the basis of fundamental physical principles. Expressions are developed for estimating the optimal choice of design and operating parameters for beneficiation of magnetite ores. By proper choice of these parameters either a high-grade concentrate or a low-grade tailing can be produced from an incompletely liberated feed.

Jan 1, 1976

By P. Somasundaran

An experimental and theoretical treatment of the depressing effect of inorganic electrolytes on the amine flotation of quartz is presented. Experimental data obtained for the amine flotation of quartz as a function of pH with potassium nitrate as depressant was used to test the models for the effectiveness of inorganic ions as depressants. The validity of commonly used assumptions are examined. The surface tension data obtained for dodecylammonium acetate solutions as a function of KNO3, concentration indicated that the collector adsorption on bubble cannot be neglected in the treatments, since this adsorption changes significantly with the addition of the inorganic electrolyte. It also indicated the possibility of significant changes in the specific adsorption potential of the collector occurring with the addition of inorganic electrolytes.

Jan 1, 1975

By J. W. Harshbarger, E. L. Montgomery

The region of metallic ore deposits in northern Chile, southern Peru, western Bolivia, and northwestern Argentina occurs in arid zones at altitudes as high as 6 km (19,700 ft). Because surface water supplies are meager, new mines require unexploited sources of water. Prolific ground water aquifers occur in salar basins in this region of the Andean Highlands. Exploration water wells have been constructed and aquifer characteristics have been tested in eight salar basins. Results indicate ground water quality is good. Aquifer transmissivity and storage computed from results of pumping tests indicate maximum capacities of more than 170 L/sec (2700 gpm) for individual production water wells. Results of investigations conducted by the authors demonstrate that ground water reservoirs in the Andean Highlands comprise a source of large quantities of water for the mineral industry.

Jan 1, 1986

By Barry S. Epstein

Financing the acquisition of a going coal mine operation has not had the exposure other finance-oriented projects have had. Therefore, C.I.T. feels that coal mining people and financial people should improve their understanding of the factors involved in this important type of acquisition. The discussion consists of two major subjects: analysis of the acquisition of the property, and sources and terms of funding the acquisition. Source and Terms of Funding There is a need to keep the competent medium-sized independent operator in the coal business, especially in these times of energy shortage. The creation of a resale market for coal mines encourages new investment in the coal mining business by medium-sized operators and their financial backers. Who provides debt and equity financing to acquire going coal mine operations and on what terms?

Jan 9, 1975

By Dwight K. Smith, Greg Carter

Studies have been conducted on The properties of many deep well cementing compositions to determine their Strength behavior over curing periods to 180 days at elevated tem-peratures and 3,000 psi pressure. This pressure results in essentially the .vat, compressive strength as that obtained with much higher pressures in ac-cordance with the findings of an API subcommittee ' These different compositions include API C1asses A, E, and F cements containig additives such as retarders, berrtorlite, heavy weight materials and pozzolans. All compositions except mixtures of Poz-zolrrrts and hydrated lime show from mild to severe degrees of strength lass over a temperature rang from -730 to 320" F after setting. Pozzolatl-time compositions actually gain in strength with time at these high temperatures. Other chemical find physical properties evaluated to observe their inter-relation.ship with Strength loss show very little correlation except in per-meability. As retrogression in strength increases, the permeability of set cement increases. X-ray difraction patterns on the set products indicate the formation of certain compounds having little or no strength value in those cementing compositions where strength loss was more severe. INTRODUCTION As a result of the growing trend toward deep well completions, a study has been made on the properties of the various cementing slurries presently in use at elevated temperatures and pressure. The strength of these compositions is of prime importance in selecting the most suitable material for use at high temperatures, to determine WOC time and the proper time to perforate with a minimum of shattering. Of primary interest in this investigation was the strength behavior of various compositions currently in use, and the effect of additives on cement after long periods of curing under severe conditions. Earlier investigators have pointed out that the strength of some cements will increase with increasing curing temperature to about 220 to 340" F, but at higher temperatures a loss in strength occurs at extended time intervals. Studies by the API Mid-Continent District Study Committee on Oil Well Cements' outlined a testing procedure whereby field conditions of temperature and pressure could be simulated in the laboratory.' It was observed that retarded cements undergo changes at elevated temperatures and some lose as much as 50 per cent of their early strength when cured at high temperatures. The scope of these tests was limited to curing periods of 1 to 28 days; additives were not covered in this study. Saunders and Walker' found that the use of additives influenced the strength behavior of cements at high temperatures, but studies were conducted only to a seven-day curing period. Ludwig and Pence' conducted an investigation of two types of cements under elevated pressures and temperatures in an effort to explain the causes of this loss in strength phenomenon. It was observed that with retrogression in strength there were other physical and chemical changes which took place as the cement aged. Today there are a number of cementing compositions available for use at well depths below 10,000 ft. Since all these earlier investigations were limited in curing time as well as the number and type of compositions studied, it was believed that a more extensive study should be conducted on the properties of cements at elevated temperatures, and this work should include those compositions actually in general field use at this time.

By E. T. Turkdogan, M. T. Hepworth, R. P. Smith

The permeability of oxygen in 0 iron in the tempera-ture range 700" to 900 C and in 6 iron at 1450°C was determined by the rate of internal oxidation of iron, containing -0.1 pct Al. The solubility of oxygen in zone-refined iron was determined by equilibration with hydrogen-water vapor gas mixtures at 1450" and 1510°C; oxygen solubilities , for iron in equi1ibriu.rn with molten oxide, are found to be 66 and 83 ppm for these two temperatures, respectively. The diffusivity of oxygen in iron at 14500C3 as calculated from the permeability and solubility data, is (4.1 * 0.6) x 10 "B sq cm per sec. OXYGEN is one of the most common impurities present in iron or steel, mainly in the form of oxide inclusions. In the study of many metallurgical problems concerning solid iron, it is often desirable to know with a reasonable accuracy the solubility and diffusivity of oxygen over a wide temperature range. The solubility of oxygen in solid iron has been the subject of numerous studies yielding highly discordant results as seen for example from the literature surveys made by Meijering &apos; and Schenck et a1.&apos; As shown by Kitchener et aL3 and by Sifferlen, the high oxygen solubilities reported by many investigators are the result of oxidizable impurities which are often present in iron. In addition, there have been experimental problems associated with icaccuracy of oxygen analysis of iron containing less than 100 ppm 0. A number of studies have been made on the permeability of oxygen in a and y iron using Fe-Si, Fe-Mn, and Fe-A1 alloys in the internal-oxidation experiments.1&apos;2&apos;5&apos;6 However, no direct measurements have been made of the diffusivity of oxygen in iron. In the present work two sets of experimental measurements were made: permeability and solubility studies at 1450" and 1510°C and permeability studies only in the range 700 to 900°C. In both sets of permeability measurements slab-shaped specimens containing small predetermined amounts of aluminum in solution were exposed at constant temperature to gas mixtures of hydrogen, water vapor, and argon for varying times. These specimens were quenched, sectioned, and examined for oxygen penetration by metallographic observation of aluminum oxide particles which formed. From these data, it is possible to calculate the ratio of the diffusivity of oxygen in iron, D, to the equilibrium constant K for the reaction Hz(g) * O (dissolved in iron) = H,O(g). EXPERIMENTAL Permeability Measurements at 1450°C. An ingot of vacuum-carbon deoxidized iron containing 0.086 pct A1 was prepared, using commercial "Type lO4A Plas-tiron"; after hot rolling, specimens were machined into slabs a by 2 by 2 in. The impurity contents were: S, P < 0.002 pct; C, Mn < 0.01 pct; each of all other Usual impurities < 0.004 pet. The amount of oxide inclusions in this material, determined by a bromine-methyl acetate extraction, corresponded to about 20 ppm 0 in the iron which agreed well with the results of vacuum-fusion analysis. Each specimen was annealed at 1450°C for 1 hr in purified hydrogen, polished to a smooth surface, and then introduced into a controlled oxidizing atmosphere in a recrystallized alumina tube at 1450°C. The constant temperature zone (*3"C) was about 3 in. in length. The gas composition was controlled by mixing argon with hydrogen (using calibrated constant-head flow meters) and passing the mixture through a column of a mixture of oxalic acid dihydrate and 10 pct anhydrous oxalic acid, to establish a required water-vapor content in the gas mixture. The temperature of the oxalic acid dihydrate column was controlled by a thermostat. The total gas flow was in the range 800 to 1000 cu cm per min. The exit gas from the reaction tube was passed through a weighing bottle containing a desiccant, to cross-check the degree of water-vapor saturation, which for all experiments was about 97 pct of those derived from the data of Baxter and Lansing.1 For a typical experiment, a specimen was introduced into the furnace in a stream of dry argon and hydrogen. The specimen was then rapidly raised by a Pt-Rh alloy wire into the hot zone and allowed to reach the reaction temperature, at which time the oxidizing gas mixture was introduced. The oxygen potentials employed were sufficient to oxidize aluminum but not to cause liquid iron oxide to form. After a specified time, the experiment was ended by dropping the specimen onto a water-cooled copper block at the bottom of the reaction tube. The depth of the internally oxidized zone, hereafter called the "case", was determined by sectioning the specimen at right angles to the long direction. The section was then examined under a microscope equipped with a micrometer stage. In general, the oxide particles were fairly uniform in size and distribution, forming a reasonably well-defined interface between the oxidized and unoxidized region. A typical cross section as observed at X30 is shown in Fig. 1. A thermal macroetch was used in one selected specimen to delineate the case. A cross section of a previously oxidized slab was polished and reheated at 1450°C in a hydrogen atmosphere for about 10 min. Upon quenching, the surface relief shown in Fig. 2 was produced; causes of this effect are unknown. Permeability Measurements Below 900°C. A slightly

Jan 1, 1967

By C. R. Ramachandra, C. C. Patel

Flotation of chalcopyrite from a low grade ore was studied by using different xanthates and dixanthogens as collectors and by conditioning the flotation pulp with oxidizing gaseous systems. The improvement in the recovery of chalcopyrite with the oxidizing systems was mainly due to the auto-activation of chalcopyrite, leading to the enhanced adsorption of xanthates and dixanthogens even when the latter were formed by oxidation of the xanthates. With air or oxygen as oxidizing system, the amount of ethyl xanthate required at pH 8.5 was much less than normally employed in the industry, the recovery being 97-99% of chalcopyrite with a concentrate of 24% copper. With isopropyl and isoamyl xanthates, the recovery was improved but the grade was lowered. By conditioning the pulp with air-CO2 or oxygen-CO2 mixture, the recovery was lowered with ethyl xanthate only, mainly due to the depressant action of bicarbonate formed. Flotation with dixanthogens gave cleaner concentrates of chalcopyrite. because iron pyrite did not float with these collectors. Of the dixanthogens tried, diisopropyl dixanthogen gave the highest recovery, 99% chalcopyrite with a concentrate containing 28.5 to 30% copper, when the pulp at pH 8.5 was condi-tioned with air. Isopropyl dixanthogen was found to be the best collector of all the xanthates and dixanthogens studied. It was found that the adsorbed ethyl, isopropyl and isoamyl xanthates at chalcopyrite surface, activated by cupric sulfate, and at iron pyrite surface were oxidized to the corresponding dixanthogens to different degrees in presence of air, oxygen, air-carbon dioxide mixture and oxygen-carbon dioxide mixture.&apos; The dixanthogen formed at chalcopyrite surface was, however, firmly adsorbed while that at iron pyrite surface was easily desorbed. Since dixanthogens formed have greater hydrophobicity than the corresponding xanthates, as revealed by contact angles,1,2 the former were expected to improve the flotation results. It was, therefore, thought desirable to find out the effect of air, oxygen, air-carbon dioxide mixture and oxygen-carbon dioxide mixture on the selective flotation of chalcopyrite when individual xanthates were used as collectors. The effect of direct use of dixanthogens as collectors on the selective flotation of chalcopyrite was also investigated. For these studies, low grade chalcopyrite ore, received from the Indian Copper Corp., Ltd. (I.C.C.), Ghatsila, Bihar, was employed. At the milling plant of the I.C.C., chalcopyrite is floated at a pH of 8.5, employing ethyl xanthate as collector. EXPERIMENTAL Materials Employed: XANTHATES - Ethyl, isopropyl and isoamyl xanthates of potassium were prepared in a pure state by the methods described earlier.4 A 0.03% aqueous solution of a xanthate was freshly prepared in air-free distilled water for flotation studies. DIXANTHOGENS - Diethyl, diisopropyl and diisoamyl dixanthogens were prepared by the oxidation of xanthates by iodine and purified by extraction with petroleum ether. A 0.03% alcoholic solution of dixanthogen was used as a collector. FROTHER - A 0.2% solution of pine oil in ethyl alcohol was employed. SODIUM CARBONATE - A 0.4 N solution was used. ORE - The composition of the -100 +200-mesh size (Tyler standard) powdered ore, as determined by standard methods of analysis, was: copper 1.57%, iron 10.29%, sulfur 3.15% and acid insolubles 66.10%. Iron present as chalcopyrite (CuFeS2) was 1.38%, while that present as iron pyrite (FeS,) was 1.37%. Both chalcopyrite and iron pyrite were found to be liberated from the gangue minerals and from each other, as observed under a microscope. Flotation of Chalcopyrite with Xanthates in Presence of Different Gaseous Systems: Fifteen grams of -100 + 200-mesh size ore were shaken well with 100 ml of distilled water. The pH of the pulp was adjusted to 8.5 by the addition of sodium carbonate solution. Then 0.1 ml of xanthate solution (0.005 lb xanthate per ton of the ore) was mixed with the pulp, and the latter together with washings transferred to a

Jan 1, 1963

By C. M. Schwartz, A. E. Austin, W. B. Wilson

High-temperature X-ray diffraction studies were conducted with Th-U alloys with up to 10 wt pet U. The solid solubility of uranium in thorium as a function of temperature was determined by the method of lattice parameters. Thorium will dissolve up to 2.5 wt pet U at 950°, 4.5 wt pet U at 1150°, and 7.5 wt pet U at 1250°C. Determinations were made of the temperature of the transition of thorium and of the effect of uranium upon the transition. The a to ß transition for thorium was observed to occur at 1330&apos; ±20°C. Mean coefficients of expansion were calculated for thorium and two alloys, and for ThO2 in contact with the thorium, using X-ray lattice-parameter data. Values obtained at 950° C for thorium and Tho2 were 12.1 and 9.40 X 10-6 per OC, respectively. Impurities obtained during the X-ray exposure were identified by diffraction and were essentially Tho2 and ThC, with two additional unknown phases being detected. The effect of the impurities upon the results is discussed. DIRECT investigation (i.e., high-temperature X-ray diffraction studies) of the phase diagram of thorium-rich uranium alloys has been shown to be necessary since recent work1 - has disclosed the presence of an allotropic transformation near 1400°C in pure thorium with the room temperature face-centered-cubic phase transforming to a body-cen-tered-cubic structure at the elevated temperature. The effect upon the transition of the addition of uranium to thorium and of the solubility of uranium in thorium at high temperatures remained unknown, yet was of interest in understanding fabrication procedures and elevated temperature use. The present work was undertaken to provide information in this area by determining the transition temperature, the effect of uranium on the transition temperature, and the solubility of uranium in thorium as a function of temperature. Experimental Work The high-temperature diffraction data were obtained using a camera especially designed for the purpose3 and capable of reaching temperatures in excess of 2000°C at pressures as low as 1 x 10." mm Hg. Temperature regulation was provided by regulating the power input to ±0.1 pet variation, and by regulating the water flow through the camera jacket to provide a constant thermal load. The X-ray sample was a rod nominally 80 mil diam, which was further turned down to 20 mil and then etched to 18 mil over 1/2 in. of one end. This was placed in the sample holder and mounted on the camera so that the smaller part was surrounded by a cylindrical tantalum-sheet radiation-type heating element. Diffraction from the sample was recorded on film after passing through a slot in the heating element and radiation-baffle shield and through beryllium vacuum windows. The X-ray film mounting was of the Straumanis type4 with a camera diameter of 114.59 mm. Since previous work of Chiotti&apos; indicated that impurities considerably alter the transition temperature, chemical analysis of the arc melted iodide crystal-bar thorium samples was obtained prior to testing. The analysis disclosed the material to contain as low as 0.001 ±0,0002 wt pet H and 0.007 ±0.001 wt pet 0. Carbon was 0.003 wt pet and nitrogen less than 0.002 wt pet. This material was sealed in mild steel in an inert atmosphere and subsequently hot rolled to 3/8-in. diam rods at a temperature of 732°C. Following removal of the jacket, the material was pickled and cold swaged to 1/8-in. rods, from which the diffraction samples were prepared. The alloys were similarly prepared, with the uranium being added during arc melting. The uranium analyses of the alloys prepared appear in Table I. The experimental procedure for diffraction examination of the three samples of high-purity thorium differed from those of the Th-U alloys. The original practice, later modified, consisted of pumping down the camera with the diffusion pump on and then admitting liquid nitrogen to the cold trap of the system. This was modified for the Th-U alloys by maintaining liquid nitrogen in the cold trap at all times before and while the diffusion pump was heated. This minor change produced a reduction in the amount of carbon pickup by the sample during exposure to the diffusion-pump vapors. The sample was brought to the desired test temperature and exposed for 21/2 hr at pressures which were usually 2 x 10-6 mm Hg, or lower. Exposures were made at

Jan 1, 1959

INTO their great Pacific Northwest counting house went the members of the Industrial Minerals Division recently, to count their blessings amidst the scenic grandeur and mineral wealth of the State of Washington. From their vantage point in Seattle, those who attended the IMD&apos;s fourth Pacific Northwest meeting turned their sights to the South and Southeast, scanned Montana, Idaho, Oregon and Utah, and predicted a very healthy economic future for their region. The praises of Idaho&apos;s booming phosphate industry were sung by Earl W. Murphy, secretary of that State&apos;s Chamber of Commerce. He said the establishment of Fort Hall, on the banks of the Snake River near Pocatello, first turned the eyes of the world toward what is now the center of the greatest known deposits of phosphate rock-the section adjacent to the common corners of Idaho, Wyoming and Utah. With the founding of Fort Hall, Mr. Murphy said, historians will also rank the construction of the first electric furnaces for the production of elemental phosphorous as equally significant in the commercial history of the West. Those furnaces were installed only last year by the Westvaco Chemical Div. of the Food Machinery & Chemical Corp. at Pocatello, at a cost of $8 million.

Jan 7, 1950

By William Hutton Blauvelt

An official of one of the prominent iron companies of the South recently made the following statement during a discussion of the present conditions of the Southern iron business: " The trouble with us in the South has been that we have been satisfied to buy iron and coal lands, build blast-furnaces, and make pig-iron. We stopped at pig-iron, and as a result we are all poor. The South needs diversified industries, and needs to work up its raw products into articles the Southern market can use. If we had realized this sooner, some of us might now be rich." The South is awakening to this view, and in the Birmingham district alone one basic steel-mill is already in operation, and in a year&apos;s time another and much larger one will be turning out rails and shapes, with rod- and wire-mills in prospect. It is to chronicle another metallurgical step forward in the same district that I have prepared the following description of the new by-product retort coke-oven plant recently put in opera-

Jan 1, 1899

By George W. Toth

This paper describes the features of a computer cost model developed to estimate requirements and costs of individual coal mining projects. Detailed cost analysis procedures for both coal mining and preparation are incorporated into the model. This model has been developed over a period of seven years through funding provided by the Electric Power Research Institute (EPRI). The model follows a process engineering approach for the estimation of all project capital and operating costs. A discounted cash flow analysis procedure is also designed into the model to allow for the solution of cost/ton or cost/MMBtu of clean coal production. The model can be applied to most surface or underground mining deposits and can accommodate a wide variety of coal washing situations. This flexibility makes the model a particularly useful tool for preliminary project analysis, property screening, investment analysis, mining technology assessment, coal cleaning level assessment, and general property valuation.

Jan 1, 1983

By George Mixter

MINING, in contrast to manufacturing, deals with a wasting asset. That which is taken out of the ground is gone, the property is depleted to that extent, and will eventually become exhausted of profitable ore. So the life of a mining company is dependent upon the ability of its management to develop improved methods to permit extraction at a profit of the lower-grade ores which remain, to extend by intelligent exploration the limits of its known ore bodies, and to find and acquire new properties to take the place of those that, for one reason or another, are no longer operated. Its history is a story of constant change, of the working out of properties here and the acquisition and development of properties there, to maintain the vitality of the whole. It is a story of estimating with the tools and the knowledge available the location and extent of hidden ore bodies and of devising the means of extracting

Jan 1, 1948

Aamot, Olav Crone, (M&apos;29) Chem. Engr., Elektro¬kemisk, Raadhusgt, 23; Oslo, Norway. Abadilla. Quirico A., (M&apos;33) Min. Engr., Dir., Bureau of Mines, Manila, P. I. Abbott, Agatin T., ( J&apos;40) Asst. Geol., Trench Mine, Patagonia, Ariz. Abbott, Clarence E., (M&apos;04) Civil Engr., V.P., Tennessee Coal Iron & R. R. Co.. 159&apos;3 Brown Marx Bldg.. Birmingham, Ala. Abel, Raymond L., (M&apos;28) Chem. Engr., Chief of Inspection Div., Pittsburgh Chem. Warfare Pro¬curement Dist., American Batik Bldg., Pitts¬burgh. Pa. Abel, Walter D., (M&apos;32) Min. Engr.. Div. of Cor¬porations, State of Calif.. 403 California State Bldg., Los Angeles, Calif. Abele. Louis T., (M&apos;31) 4800 Patterson Ave.. Richmond, Va. Abell, Leo M., (M&apos;311 Research Met., Mount Mor¬gan Ltd., Mount Morgan, Queensland, Australia. Abenius, Hakan V., (M&apos;37) c/o Falu Gruva, Falun, Sweden. Abernathy. G. E., (M &apos;33S) Geol., Kansas State Geol. Survey. Pittsburg, Kan. Abernathy, Jack. H.. (M&apos;40) Chief Engr., Sunray Oil Co.. Philtower B1dg., Tulsa. Okla. Ahorn, Robert H., (M&apos;19) Asst. Met., Research Lab., U. S. Steel Corp., Lincoln Highway, Kearny, N. J. Abraham, A. W., (M&apos;30) Petr. Engr., Richfield Oil Corp., 555 S. Flower St., Los Angeles. Calif. Abramowitz, William L., (J&apos;40) Chem., National Oil Products Co., Harrison, N. J. Abrams, Charles Jackson, (M&apos;36) Gen&apos;l Supt., Climax Molybdenum Co.; Climax, Colo. Abstein, Henry T., (M&apos;27) Yellow Pine, Idaho. Ackerman, D. E., (M&apos;35) McKinsey & Co., 2 Wall St., New York, N. Y. Ackerman. E. Dumont, (A&apos;3S) Petr. Geol.. Dist. Geol., Quiriquire&apos; Dist., Standard Oil Co. of Venezuela, Caripito, Venezuela.

Jan 1, 1941

The Institute conducts jointly with the American Society of Civil Engineers, American Society of Mechanical Engineers and American Institute of Electrical Engineers, certain activities as listed below, and is joint owner with them of certain properties situated at 29 West 39th Street in New York City United Engineering Trustees, Inc. When Mr Carnegie made his gift, "for the erection of a suitable union home" for the engineering societies, United Engineering Trustees, Inc (then United Engineering Society) was chartered un¬der Chapter 703, Laws of the State of New York, 1904, for "the advancement of the engineering arts and sciences in all their branches, and to maintain a free public engineering library " The Corporation was further empowered to acquire real and personal property and to use, maintain and occupy it, with the provision that any building erected by the Corporation shall be used perpet¬ually as a meeting place and headquar¬ters for the Founder Societies Thus the Carnegie gift realized the ideal of bring¬ing the engineering societies together under one roof, and the Corporation through its members nominated in equal numbers by the four Founder Societies had the necessary authority to act for the Founder Societies in their joint in¬terests in owning and operating for them not only Engineering Societies Building, but in the course of time, Engineering Societies Library, and The Engineering

Jan 1, 1952