By Kati Tschöpe

Cathode wear has become an increasing challenge in the aluminum industry due to the use of more graphitized materials. Today, there exist no standard laboratory methods for measuring cathode wear where different commercial materials can be ranked. The typical average wear rate in an electrolysis cell is quite small. The aim of this work was to design a test method where the wear could be accelerated compared to industrial cells. It was focused on polarized tests where the cathode is exposed to electrolyte, which gives higher aluminium carbide solubility. The cathode materials were characterized by microscopy and image analysis.

Jan 1, 2011

By R. R. Rogers

Abstract The degree of cathodic protection of steel and the anode corrosion rate were determined when anodes and waters of different compositions were used at temperatures similar to those in domestic hot water tanks. Twenty different anode materials, sixteen of them magnesium-zinc-aluminium alloys, were immersed in six different synthetic waters resembling those to be found in various parts of Canada. The results showed that (1) both the degree of cathode protection and the average anode corrosion rate are affected materially by the composition of the anode material and of the water; (2) poor cathode protection is associated with low anode corrosion rate; (3) when the cathode is fully protected, the anode corrosion rate may be comparatively low or comparatively high, depending upon the composttion of the water; (4) an important relationship exists between the magnesium content of the preferred anode and the composition of the water; (5) the degree of protection is increased as the SO4 + Cl concentration of the water is increased and thus as its specific resistance is decreased. Introduction Fairly recently, the use of the active metal magnesium for the cathodic protection of less active metals has received a considerable amount of attention. This interest has been stimulated by the fact that the wartime demand for magnesium was greatly in excess of the present peacetime demand and there is a natural desire to continue operating the large magnesium plants which were built during the war. Information regarding the use of zinc and aluminium for this purpose also has been published. There is a great demand for domestic hot-water tanks which will resist corrosion satisfactorily. This problem is rather complex in view of the fact that the composition of the water used in such tanks varies greatly and depends upon the locality. The present investigation deals with the effect of water composition and anode composition on the cathodic protection of steel under conditions approaching those which exist in hot water tanks.

Jan 1, 1948

By R. R. Rogers

Introduction The subject of cathodic protection is not new. In 1824 Sir Humphry Davy, in publishing the results of his investigations for the British navy, pointed out that copper could be protected from sea-water corrosion by connecting it electrically with zinc or iron. Since that time much work has been clone in this field, particularly in the protection of metals from the action of sea water, neutral brines, and treated and untreated waters. Special mention should be made of the successful protection of underground pipe-lines which formerly were badly corroded by the water in the ground. So far, magnesium alloy and zinc anodes have been the most popular. However, fairly recent work has indicated that aluminium anodes will give good service under certain conditions. The principle of cathodic protection has been applied extensively in coating steel articles with zinc and in cladding aluminium alloy sheet with pure aluminium. A valuable discussion of the fundamentals and applications of cathodic protection recently was presented in the Corrosion Handbook. A useful list of references was included in the article.

Jan 1, 1949

By G. T. Adel, P. E. Richardson, R. Pazhianur

Cathodic protection using impressed current was employed to reduce mill wall wear during ball milling. Wear rates were determined from weight-loss measurements made on four 1-in.-diam mild steel coupons that were installed flush with the interior surface of the mill wall. Grinding tests were conducted on quartz, pyrite and quartz-pyrite mixtures at pH levels of 4.6, 7.1 and 9.2. Cathodic protection was shown to reduce mill wear by 30% to 60%. An examination of the coupon surfaces using scanning electron microscopy showed that cathodic protection greatly reduced pitting corrosion. The presence of a sulfide mineral, such as pyrite, was found to increase the wear rate significantly, possibly due to galvanic interactions. It was also found that the wear rate is significantly higher than the sum of abrasive wear and the corrosive wear, due to a synergistic effect.

Jan 1, 1998

By R. Pazhianur

Cathodic Protection using impressed current was employed to reduce the wear of the mill wall during ball mill grinding. Wear rates were determined from weight-loss measurements made on four, I-inch diameter, mild steel coupons installed flush with the interior surface of the mill wall. Grinding tests were conducted on quartz, pyrite and quartz-pyrite mixtures at pH values of 4.6, 7.1 and 9.2. Cathodic protection was shown to reduce mill wear by 40-60010. An examination of the coupon surfaces using scanning electron microscopy showed that cathodic protection greatly reduced pitting corrosion. The presence of a sulfide mineral, such as pyrite, was found to increase the wear rate significantly, possibly due to galvanic interactions. It is also found that the wear rate is significantly higher than the sum of abrasive wear and the corrosive wear, due to a synergistic effect.

Jan 1, 1996

By R. E. Moore

Refractories are unique ceramic materials, which are used in large quantities in steel making furnaces, metal smelting vessels, and glass melting tanks. They are required to possess high thermal shock properties and good slag corrosion resistance as well as creep resistance at high temperatures. Therefore, they are made from very refractory minerals such as lime, periclase, corundum, spinel, and zirconia. Slags are vitreous materials produced as a residue in steel refining processes. They cover a wide range of compositions and may contain pure oxides, silicates, and sulfides as well as fluoride phases depending on the melting and smelting processes. These minerals exhibit spectacular cathodoluminescence color under electron bombardment; therefore, cathodoluminescence (CL) microscopy is found to be a superior technique for the characterization of refractory corrosion by slags. Examples included in this study are (1) reaction of fluorine containing mold slags with ZrO2-C nozzle refractories promoting crystallization of the Cuspidine, Ca4Si2O7(F,OH)2, (2) corrosion of fusion cast refractories in TV panel glassmaking furnaces and formation of glass defects, and (3) reaction of spinel based castable refractories with copper smelting slags.

Jan 1, 2001

By R. D. Hagni

Pyrometallurgical products from lime roasting of refractory gold ores, pyrite, and arsenopyrite have been examined for their mineralogy, porosity, permeability, retention of contaminant sulfur and arsenic, and potential effectiveness of gold extraction. Cathodoluminescence microscopy, supplemented by X-ray diffraction and scanning electron microscopy-energy dispersive analysis study, has shown that the products phases have characteristic cathodoluminescence properties as follows: anhydrite (CaS04), deep blue; unreacted portlandite (Ca(OH)2), deep purple; oldhamite (CaS), light yellow to rarely pink or orange; a sulfur-rich, arsenic-poor phase, violet; an arsenic-rich, sulfur-poor phase, non-CL. Within the temperature range examined (400-850°C), hematite exhibits greater porosity and permeability at the intermediate roast temperatures of 600-650°C.

Jan 1, 1993

By R Graber, R Johnson

North American steelmaking practices have evolved based on access to iron ore raw materials containing very low phosphorus contents, typically less than 0.025 per cent P. Cleveland-Cliffs managed Tilden iron ore operation produces iron ore pellets exceeding 0.030 per cent P, which by global standards would be considered low phosphorus, but has limited penetration in the North American iron ore market due to phosphorus content. Recently cathodoluminescence microscopy has augmented more standard ore characterisation techniques enhancing our understanding of the genetic history and process mineralogy of TildenÆs complex martite ore. This paper highlights the unique capabilities that cathodoluminescence microscopy provides for phosphorus mineral identification in fine-grained iron ores.

Jan 1, 2005

By Musa Karakus

Ceramic build-ups are synthetic mineral deposits formed in critical locations in or near the throats of inductor units in channel induction furnaces, the preferred melting and holding furnaces used in iron foundries. The build-ups are undesirable because they slow down melt circulation, increase power consumption and cost. and decrease the quality of the metal. This study involved the determination of the mineralogy of build-up samples and the quantitative measurement of phase abundance in those build-ups by cathodoluminescence microscopy. These undesirable deposits usually are hard and dense and contain variable amounts of entrained metallic iron. The non-metallic phases dominantly consist of oxides and silicates of several refractory elements, AI, Mg. Ca, Si, and Fe. Minor amounts of the sulfides of Ca. Mg, Fe and REE elements, especially Ce and La. and the oxides and silicates of Ce and La elements are locally present in the build-ups. The build-up samples were found to be ideally suited for study by cathodoluminescence, which has provided an easy means for rapid re-cognition of the phases present in the build-ups. The phase compositions were determined by electron microprobe analysis. The phases identified and their characteristic cathodoluminescence shown in the ceramic build-up samples were: spinel (bright green, blue-green, and red). forsterite (red and purple), periclase (dark reddish-brown, blue. and orange), corundum (red, blue, orange, and white), anorthite (yellow, yellow-green, blue, and blue-purple), hibonite or calcium hexaluminate (dark green), mullite (dull red-brown), gehlenite (deep blue), silica(dark brown, pink, purple, red. and blue), monticellite (light violet blue and light pale yellow-orange), silicon carbide (orange), oldhamite (bright yellow and orange). Ce-La silicate phases (purple), and glass (orange, dull red, and purple). Non-luminescent phases were: hercynite, Fe-oxides, Ce-La-oxides, Fe-sulfides, and metallic iron.

Jan 1, 1989

By Norihiro Murayama

Syntheses of zeolitic materials were carried out from coal fly ash by alkali hydrothermal treatment as part of the reuse and recycle technologies of coal ash, For the obtained zeolites, the cation exchange capacity and acid resistance, which are very important in the practical use of cation exchanger in aqueous solution, are investigated during this stufY, The cation exchange amounts of the NaP, CaP and K-CHA zeolites are measured for various cations such as K+, Na +, NH4+ Ca2+, Mg2+, Pb2+, Cd2+ and so on. The change in crystallization degree are researched as a function of pH. The simultaneous removal ability of NH4+ and PO43- in solution is examined for an example of the water purification with CaP zeolite. From these results, the characteristic and its mechanism of cation exchange are clarified for the various zeolitic materials obtained from coal fly ash.

Jan 1, 2003

By Neil S. Fishman

Tabular uranium ore in the Grants uranium region, New Mexico, occurs as tabular layers of a urano-organic mixture suspended within host sandstones of the Morrison Formation. The intimate urano-organic association points to the organic material as the main ore control. Petrographic evidence indicates that the organic material was postdepositionally introduced into the host sandstone, probably as humic acids; however, the mechanism by which these acids precipitated from solution remains uncertain. A model, the cation scavenging model, is proposed in this paper to explain humic acid precipitation. The model, supported by evidence from regional alteration studies of the host sandstones, proposes that cations responsible for humic acid precipitation were scavenged from framework grains which altered during passage of the humic-rich fluids through the host sandstone. This process, coupled with the affinity of organic molecules for each other, caused flocculation of humic acids into tabular zones. The precipitated humic substances then continued to concentrate uranium to form the orebodies. The cation scavenging model requires only one solution, the humic-bearing solution, in the precipitation process. All cations necessary for humic acid precipitation originated in the host sandstones. This model contrasts with a previously proposed model--the brine interface or two solution hypothesis--in which it was proposed that a cation-rich brine introduced into the host sandstones provided the cations necessary for humic acid precipitation. The brine hypothesis has several drawbacks, one of which is unrealistic hydrologic reconstructions necessary to accommodate mineralization at various stratigraphic horizons in the Morrison Formation. Moreover, no mineralogic evidence exists to suggest a brine occupied the host sandstones at the time of mineralization. The proposed cation scavenging model for humic acid precipitation not only readily accounts for humic acid precipitation, but also is consistent with geologic observations and regional alteration studies.

Jan 1, 2013

By G. Rinelli, Arthur F. Colombo, Donald W. Frommer

With the opening of the Tilden mine near Ishpeming, MI, a new era in iron ore beneficiation was begun. A description of a U. S. Bureau of Mines investigation is summarized to illustrate the selective flocculation-deslime-flotation process developed by the Bureau and used at the Tilden concentrator, which is also briefly described. The operating parameters for the selective flocculation-cationic flotation of an oxidized taconite from the Mesabi range are discussed. A water reclamation system using lime and a cationic flocculant was applied to reclaim the effluents from a 900-pound-per-hour flotation pilot plant. About 80 percent of water requirements were recovered, and the calcium content of the reclaimed water was found to be more important than clarity in influencing the selective flocculation and flotation processes. Although reclaimed waters with about 10 ppm calcium registered turbidities of approximately 5,000 ppm SiO2 equivalents, the concentrates produced using these waters contained 64 percent Fe and =5.0 percent SiO2 and had accompanying iron recoveries of 75 percent. Lower grade concentrates resulted from using reclaimed water with higher calcium contents and lower turbidities.

Jan 1, 1976

This paper describes the results of a laboratory study on the upgrading of Algoma siderite by the amine flotation of silica and silicate gangue. The experiments indicate that a virtually complete removal of silica is possible in a rougher flotation con-ducted in tap water at natural pH, without prior desliming of the ore. Grinding considerably finer than the apparent liberation size is essential for maximum silica rejection. A cationic collector, Aeromine 3037, gave best results when used in combination with a modifier. Of the several modifiers tested, a Dutch potato dextrin, Dextrin 4356, was found to be the most effective. Both iron recovery and the grade of the final iron product are enhanced by floating the pyrite contained in the ore prior to the amine flotation of the silica, and by scalping the magnetics from the silica concentrate. F OR over twenty years, the Algoma Ore Properties Division of The Algoma Steel

Jan 1, 1963

By David L. Gefvert

A general review of the role of cationic flotation reagents in the beneficiation of phosphate, iron, and potash ores. The three major types of cationic collectors-amines, ether amines, and condensates will be compared and contrasted. The effect of particle size, water chemistry, and water temperature on the choice of cationic flotation reagents for each industry will be discussed.

Jan 1, 1986

By K. E. Hjelmstad

Solution mining operations often encounter difficulty maintaining adequate leach solution flow into the ore formation because of loss of formation permeability near the injection well. Permeability loss caused by swelling and breakup of clays and fine particle migration can often be the cause of the problem. Combined permeability and leaching tests were done in the laboratory on samples of clay bearing ores to evaluate a clay-stabilizing polymer's effectiveness in preventing the problem. Test results indicate that treating the ores with cationic polymers could maintain permeabilities two to five times greater than the long-term permeabilities present in untreated ores. Both alkaline (pH 8.5) and acidic (pH 2.0) leaches were used in the permeability leaching tests. To determine the reasons for the success of the clay stabilizing polymer, clay swelling tests and zeta potential measurements were made on untreated ore samples and on ore samples treated with the cationic polymer. Test results indicate the cationic polymer could reduce the degree of negative charge on fine particles and their tendency to disperse, as well as reduce clay swelling. Test results indicate a potentially beneficial effect on operating parameters such as capacity and injection pressure during leaching, if clays and fines are kept stabilized. This may be done by treating the zone of high fluid velocity near injection wells with cationic polymers.

Jan 1, 1991

By K. E. Hjelmstad

Solution mining operations often encounter difficulty maintaining adequate leach solution flow into the ore formation because of loss of formation permeability near the injection well. Permeability loss caused by swelling and breakup of clays and fine particle migration can often be the cause of the problem.

Jan 1, 1989

Inn mining communities throughout the western United States, cows have always been part of the landscape as they graze on surrounding rangelands. Until recently, mining companies regarded these animals as something to be kept off their properties — especially any freshly reclaimed lands. During the last few years, though, this situation has begun to change. Today, cattle can be seen in a handful of mine settings, moving up and down the slopes of mine tailings and waste rock. These animals are being used by several companies to do some of the reclamation work once performed by large earth-moving equipment, mechanical spreaders, rippers and seed drillers. This is because cows can contour slopes more naturally and produce and spread soil nutrients in ways that tractors and ripping machines cannot.

Jan 1, 1999

By Les Philips

National Institute for Safety and Health?s (NIOSH, USA) Office of Mine Safety and Mine Safety and Health (OMSHR) has definitions for: -Proximity Detection as detection of personnel, vehicles and other objects near a machine using some type of sensor technology -Proximity Warning (aka Collision Warning) as detection of personnel, vehicles and other objects near a machine resulting in alarms that ?Warn the operator only ?Warn the operator and nearby personnel (two-way) -Collision Avoidance as the processing of sensor information resulting in control signals or actions that alter machine status/movement to avoid a collision by ?Computer control ?Human control

May 1, 2013

By Huasheng Chen, Gaifeng Xue, Jing Zhang, Mingsheng He, Bin Liu, Yexian Ouyang, Shoujun Peng

Based on the investigation and study of the topography, microstructure and composition of the buildups which form in the surface of carbon sleeve in continuous annealing furnace for lowand medium-grade non-oriented silicon steel produced by CSP process, combined with production process of silicon steel, the mechanism and major causes for forming buildups of carbon sleeve are discussed from the factors such as CSP process, the quality of carbon sleeve and so forth. Meanwhile, some countermeasures to reduce the formation of the buildups are put forward.

Jan 1, 2015

By L. B. Lindemuth

TO those who are in a position to carry the thought to a conclusion, I would like to present a theory of the cause of blisters in ' galvanized sheets. Blisters that are caused from piping and shrinkage cavities will not be considered, because the reason for their formation is entirely obvious. Blisters that periodically occur, with no apparent system of location, number, size or grouping, and then disappear with no apparent change in manufacturing method, are the ones to which this theory would apply. Examination of blisters of the latter type has shown that they contain hydrogen gas at atmospheric pres-sure, and that occasionally traces of oxide or sulfide are found on the inner surface of the blisters. These two characteristics have led to the rather general idea that hydrogen gas generated in pickling, and that iron oxide supposed to be inherent in the ingot and causing weak spots, were, in some manner, responsible for the development of blisters in galvanizing. The theory which I wish to advance is that these blisters are caused by moisture that has penetrated the steel after the annealing operation. This moisture comes from the atmosphere, or from pickling or wash-ing, and when it is suddenly expanded into superheated steam in galvanizing, the increase in volume is so great that it cannot escape with sufficient rapidity through the small opening which it entered as moisture. The pressure so generated forces the sheet apart along those lines of lamination that may be found in practically all flat sections of steel rolled comparatively cold.

Jan 5, 1927