By James A. Voigt

"The efficient separation of metal species from aqueous streams by precipitation techniques requires a fundamental understanding of the various processes that occur during precipitation. These processes include particle nucleation, particle growth by solute deposition, agglomerate formation, and agglomerate break-up. The application of the population balance approach has been used to develop a kinetic model that accounts for these competing kinetic processes. The usefulness of the model is illustrated through its application to the precipitation of yttrium hydroxynitrate, YHN. The kinetic parameters calculated from the model equations and system specific solution chemistry are used to describe several aspects of the effect of pH on the precipitation of the YHN. Implications with respect to the simultaneous precipitation of more than one cation type are also discussed through use of example systems. The effects of solution chemistry, precipitator design, and solvent choice are considered.IntroductionThe application of precipitation technologies to the separation of metals from solution is widely used. Regardless of its application, be it in such diverse areas as the preparation of metal oxide powders for use in commercial products or as a unit operation in the removal of trace metals during wastewater clean up, the fundamental processes involved are the same. These processes include: nucleation from solution, either homogeneous or heterogeneous; growth from solution with chemical reaction either in solution or at the precipitate/solution interface; growth by particle agglomeration; and particle break-up by collisional or shear forces. The effectiveness of the operation and the properties of the precipitate formed, or ""quality"" of the product, are determined by the competing kinetics of the different processes. The kinetics of the processes, in tum, are determined by system-specific solution chemistries and the conditions used to carry out the precipitation operation. For example, generally, when system conditions are such that the supersaturation driving force for precipitation is very high, growth species normally do not have the time to organize themselves with a high degree of crystallographic order and the precipitate is amorphous. In this case nucleation rates are invariably extremely high and the primary mechanism for growth is the agglomeration of nuclei. Conversely, when the supersaturation levels for the same system are reduced, the kinetics of the nucleation and growth processes also are greatly reduced, and a crystalline precipitate can be formed, since the growth species have time to order on particle surfaces."

Jan 1, 1996

By J. D. Miller

Gold adsorption from cyanide solutions by activated carbon has been studied at great length during the past decade. Findings from past research are reviewed and discussed with respect to structural features of various carbons, including carbon black, activated carbon, graphite and diamond.

Jan 1, 1991

By Kuniaki Murase, Tetsuji Hirato, Yasuhiro Awakura

"Electrodeposition of CdTe was studied using aqueous ammonia-alkaline electrolytic baths in which Cd11-and Te1V-ions are dissolving as Cd11(NH3)/+ and Te1vol-ions, respectively. Ca-thodic polarization curves of the baths suggest the presence of strong interaction between the Cd11-and Te1V-ions; electrodeposition of tellurium is inhibited by the presence of Cd(NH3)/+ ions. The interaction makes it possible to electrodeposit CdTe films with stoichiometric composition. Polycrystalline CdTe thin film of about 1 µm thickness was electrodeposited at 343 K from ammonia-alkaline solutions (pH= 10.7) containing TeO32-(<20 mmol dm-3) and Cd(NH3)/+ ( < 60 mmol dm-3) ions. Increasing Cd(NH3)/42+/TeO32- mole ratio or decreasing total concentration of ammonia/ammonium-ion gave flat and smooth crystalline CdTe deposits at constant cathode potential-0.70 to -0.30 V vs SHE at 343 K.IntroductionCadmium telluride (CdTe) is well-known as a compound semiconductor whose band gap, i.e. 1.44 eV, is suitable for solar energy conversion with a photovoltaic cell. Various methods, such as CVD (chemical vapor deposition) and electrodeposition, of preparing CdTe thin films for solar cells have been investigated.Acidic sulfate solutions with a pH of 1-2 are usually employed for CdTe processing by electrodeposition.1-3) The electrodeposition of compound semiconductors is usually achieved (i) at a higher cathode potential than the redox potential of less-noble species, can in this case, and (ii) under the condition of diffusion-limiting current of a more noble species, Te1Y.4) There-fore, a suitable CdII/TeIV concentration ratio in the acidic electrolytic baths, resulting in the deposition of stoichiometric CdTe, is determined by the diffusion-limiting current density of TeIV- reduction, i.e. the concentration of HTeIVO2+ · Since the solubility ofTe1v species HTeIVO2+ in the acidic solutions is quite low, the rate at which CdTe is deposited from the acidic solutions is extremely slow."

Jan 1, 1998

By E G. Prado

We have confirmed on bench scale the removal of chlorides and alkalies (+95%) and over 2/3 of the zinc, lead and cadmium from EAF dusts. This has been achieved with arrononium acetate solutions alone, or with combinations of water wash, amonia-ammonium carbonate and ammonium acetate solutions. Also confirmed are the process routes for the recovery of the aforementioned elements into marketable products. The technology involves the complete recycling of the reagents. The FAF residue is returned to the electric furnace without risk of impurities buildup. Commercial scale testing with the recycled dust was satisfactory, including quality of the slag and its behavior during the melting stage. A cursory feasibility evaluation is presented.

Jan 1, 1994

By B. Erik Ydstie, Tor Lindstad, Vianey Garcia-Osorio

"As a result of the high temperatures present in a Carbothermic Aluminum Process the content of aluminum and aluminum sub-oxide in the gases leaving this process is high. These gases as well as energy must be recovered. In a Vapor Recovery Unit were the aluminum compounds react in a series of Heterogeneous Non-catalytic Reactions forming solid, liquid and gas products. The different product phases depend on the temperature present in the system. In this work we present dynamic model of the Vapor Recovery Unit of a conceptual Carbothermic Aluminum Process. Because of the complexity of the system several models are developed and coupled to capture the essential physics of the multiphase reaction problem. A Shrinking Core Model describes the reaction mechanisms. Then material and energy balances are coupled with the thermodynamics properties from the FACT database of thermodynamic properties, resulting in a system of nonlinear Partial Differential Equations. In the paper we describe the model development and governing equations for the reaction mechanisms and fluid flow. Finally we review the numerical schemes created for the solution of the model system. The model can be used for control and design purposes.IntroductionThe Carbothennic Processes for producing Aluminum can be divided into two groups (Motzfeldt et al. (1989)) In the first approach pure alumina is produced and reduced to pure aluminum. In the second approach an alloy (e.g. aluminum and silicon) is made and then aluminum is produced from the alloy. The history of both processes has been described by Ginsberg et al. (1965). At least three aluminum producers began largescale testing of this process in the 60's Alcan, Pechey-Ugine and Reynolds. Alcoa did some smaller scale experiments.Alcoa was one of the first companies to produce aluminum by Carbothennic Reduction (Foster et al. (1956)) and US Patent 2,829,961 April 8, 1958. In this process a carbon containing molten aluminum phase was a floated on top of an oxy-carbide melt. During the cooling the dissolved carbon deposited as aluminum carbide. The carbide was then separated from the molten aluminum by a fluxing agent. This process was successful but economic unfeasible."

Jan 1, 2001

By J. D. Miller

Air-sparged hydrocyclone (ASH) flotation is a high-capacity flotation technology originally developed in the Department of Metallurgical Engineering at the University of Utah for processing mineral resources. However, the technology has been found to be useful in industrial waste processing, in the recycle of secondary resources, and in remediation of environmental problems. For example, areas in which the ASH technology is expected to have potential application include cleaning of waste coal fines, air stripping to remove volatile organics from drinking and process water, water disinfection by ozone or chlorine sparging, dispersed oil removal from water, and contaminated soil remediation. Recently, the ASH has been studied extensively for deinking flotation in the wastepaper recycling industry and has been shown to have excellent efficiency/capacity. In fact, a 20-million-dollar plant has been in operation since June 1992. The ASH technology can provide a specific capacity hundreds of times more than that which can be achieved with conventional flotation equipment and in certain instances is expected to provide superior separation efficiencies when compared to other technologies. The design and principles of ASH flotation are described. Experimental data for fine coal flotation, volatile organics stripping, and deinking flotation for paper recycle are presented and discussed. Finally, other potential areas of application for environmental technology are considered.

Jan 1, 1993

By S. Illendula, B. Q. Li, R. A. Mirshams

"An integrated mathematical model is developed to represent the thermomechanical behavior of the materials and microstructure evolution during metal forging. The model development is based on the finite element solution of the thermoviscoplastic deformation of metals coupled with the internal state variable model describing the microstructure evolution involving work hardening, recovery, recrystallization and grain size distribution. The procedures for the integration of the microstructure model into the macro finite element model are described. Computed results for both macro and micro phenomena during metal forging, such thermomechanical deformation such as velocity field and effective strain rate and materials characteristics such as distribution of grain size and recrystallization volume fraction, are presented.1. IntroductionThermomechanical behavior and material microstructural evolution are two critical, interrelated aspects associated with metal workpiece undergoing large plastic deformations such as encountered in forging processes. In much of the modeling work up to date, these two aspects have been addressed separately. Die designs and forging processes are investigated using finite element based thermomechanical models while material dynamics during forging is studied, more often than not, as a separate subject. For many industrial applications, especially those involving novel, light and high strength materials, it is critical to combine these two aspects into a single, integrated model so that materials dynamics and thermomechanical deformation during forging processes can be considered simultaneously [1], thereby providing required information for intelligent process design and optimal process control."

Jan 1, 1998

By Lev Levin, Sergei Lesokhin

"The formation of titanium carbide during hot filament assisted carburizing of NiTi alloy was investigated. Phase content and morphology of the diffusion zone were examined by X-ray diffraction, X-ray microanalysis, SEM, and Auger electron spectroscopy. The growth of stable and adherent TiC film was observed. A non-planarity of interphase boundary was noticed. The applicability of the chemical diffusion approach to the analysis of the experimentally observed interface instability is discussed. A criterion, taking into account the influence of growth stresses on the stability of the flat interface, is developed by means of linear perturbation analysis.Introduction.Equiatomic intermetallic NiTi belongs to a class of materials exhibiting the shape-memory effect. The unusual property of this compound promotes its application in many fields, from aerospace technologies to medicine. The relatively high ductility ofNiTi also permits its use as a matrix material in metal-ceramic composites. The objective of this work was to investigate the possible incorporation of a ceramic material (titanium carbide) into NiTi by gas carburizing.Free energy calculations indicate the potential to obtain TiC by carburizing Ni-Ti binary phases. The main obstacle to such a process is the high affinity of titanium to oxygen. At moderate temperatures the formation of TiC is preferable to titanium oxidation only if the partial pressure of oxygen is extremely low [1]. This problem was overcome in this work by the use of hot filament assisted gas carburizing. Due to chemical reactions occurring near the hot filament, the gas mixture, initially consisting of methane and molecular hydrogen, was enriched by atomic hydrogen [2], drastically decreasing the content of free oxygen in the carburizing atmosphere.The second part of this article concerns the theoretical analysis of reasons that lead to the development of the experimentally observed morphology of the diffusion zone. In particular, the influence of the growth stresses on the morphology of an interphase boundary is investigated."

Jan 1, 1996

By R. Lanza, M. Hytros, N. Saka, I. Jureidini, J. H. Chun, D. Kim

"A novel method for delineating the solidification front in metal casting has been developed using the attenuation phenomenon of electromagnetic radiation (y-rays or x-rays) and computed tomography (CT). The densities of the liquid and solid phases that exist during metal casting may differ anywhere from 4 to 12 % depending on the metal. As in the medical imaging field, CT provides an excellent means of mapping this density variation in a solidifying casting into two-or three-dimensional images.In an effort to develop an industrial-scale sensor, laboratory-scale experiments have been conducted using a cobalt-60 (Co60) radioisotope and a sodium-iodide (Nal) scintillation detector. The CT image reconstruction was performed on a crucible containing pure tin in a two-phase state. Although the spatial resolution and data acquisition speed were not optimum, the CT images clearly differentiate the liquid and solid phases of the tin in the crucible. To maximize resolution and minimize data acquisition time, a linear accelerator (linac)-based CT sensor is being developed and tested for application in the continuous casting of steel and aluminum alloys.IntroductionIn all casting processes, the quality of a finished product and its production rate depend upon the shape and movement of the solidification front. From a quality perspective, it is well documented that solidification kinetics (heat and mass transfer, fluid flow, microstructure evolution) greatly influence the final properties of castings [l,2,3]. Product shortcomings, such as surface defects, cracks, macro-and microsegregation, and inclusions are directly controlled by the solidification process. By understanding the role the solidification front plays in the casting process, product quality may be dramatically increased through the reduction of defects."

Jan 1, 1997

By F. H. A. Abdalla

A process is described for the recovery of valuable nonferrous metals from steelmaking dust by suiphatizing roasting using ammonium sulphate. Maximum recoveries of soluble metal sulphates achieved at optimum conditions were> 99.0 %. Selective metal separation of the soluble sulphates in the leached liquors were performed either by controlling the roasting temperature or by adjustment the pH values of the leached liquor ranging from 3.6-6.2. Either pure zinc oxide orland tin oxide could be obtained at optimum conditions, and the products were evaluated chemically and by X-ray analyses. The residues rich in iron oxide can be removed and recycled. The mechanism of sulphatizing roasting process was considered. A general flow-sheet for the overall process of treatment the steel making dust to recover its valuable nonferrous metals was suggested, which ca be applied for other nonferrous bearing materials.

Jan 1, 1996

By Y. A. Chang, J. Woodford, C. R. Kao

Reactive diffusion studies between NbC and Si were carried out at 1300 °C under a vacuum of 10-5 torr and a uniaxial pressure of 1 MPa. The annealing time ranged from 8 to 100 hours. The Si used was single crystal silicon; the NbC was hot-pressed powder compact. A NbSi2+SiC two-phase reaction layer formed with NbSi2 as the matrix and SiC as discontinuous particles. The microstructure of the reaction product is homogeneous, dense, and fine. The NbSi2 grain size and SiC particle size are in the micron range. The growth of the reaction products follows parabolic kinetics. Extrapolation of the data to zero thickness suggests an apparent incubation time of 3.5 hours. However, for short annealing time «60 hours), the thickness data can be approximated by linear kinetics with an initial growth rate of about 2 11m/hr. Based on these experimental observations, a growth mechanism for the reactive diffusion between Si single crystal and NbC powder compact is proposed. We propose that the nucleation sites for the SiC particles are at the voids of the NbC powder compact. This proposed nucleation mechanism offers a potential way of controlling the SiC particle size by changing the void size and void density of the NbC powder compact. This hypothesis, if proven to be true, will allow us to control mechanical properties of the composites by tailoring the SiC particles formed. It is also pointed out that the microstructure requires Si to be the dominant diffusing species and to diffuse through the reaction layer, while Nb and Conly have to undergo local rearrangement.

Jan 1, 1996

By Deyou Yin, Kongfang Feng, Bo Wang, Jieyu Zhang, Xin Hong, Shaobo Zheng, Jinyin Xie

"The flow patterns and mixing characteristics in a water model of C-H2 smelting reduction furnace are experimentally studied in this paper. Water modeling is employed to investigate the features of gas jet stirring and the fluid flow patterns in the bath of a smelting reduction furnace during the top, bottom, and side combined blowing process. The influence of the gas flow rate for top, bottom and side nozzles, angle, submerged depth of each side nozzles and the height of the top nozzle has been examined. It showed that the gas flow rate of side nozzles and bottom nozzle had a key role on the fluid flow and mixing characteristics. The gas jet from the top nozzle could change the agitation and fluid flow pattern caused by the gas jets from the side nozzles in the bath.IntroductionFacing the current natural resources decrease and the environmental degradation, smelting reduction iron-making technique is believed to be the most representative at present. Mid last century, the concept of producing liquid iron or semi-steel directly from ore fines and inexpensive fuel was the subject of considerable pilot plant development activity. Among these projects, the direct smelting process, which is the reduction and melting of iron-bearing materials by carbon and other hydrocarbons in the vessel containing a molten bath, is the most popular one. A number of direct smelting processes have been developed around the world, e.g. COREX, DIOS, HIsmelt, AISI, ROMELT, etc.These studies put forward a new technology, which through bottom nozzle blowing rich hydrogen, top nozzle blowing rich oxygen and provide preheating ore and solvent, side nozzles blowing oxygen-coal to realize smelting reduction iron-making process. Owing to the metallurgy reactions always in high temperature, which is above 1600 °C, it is difficult to visualize the mixing behavior and measure the desired phenomena in the reduction vessel. With water modeling, the primary advantages are that it is relatively easy to observe and measure the flow phenomena in the bath."

Jan 1, 2011

By Yousef Mohassab, Manoranjan Misra, Monalisa Panda, Eman Wahbah

This work studies the removal of arsenic (V), arsenate, and arsenic (III), arsenite, from aqueous solution using calcined Quintinite-3T. The two adsorbents Quintinite-3T was prepared, calcined at different temperatures, and characterized by XRD, BET, and SEM. The surface area of the calcined Quintinite-3T was 193.4 m2/g. The particles size ranged from 12 to 56 nm for the uncalcined Quintinite-3T and from 24 to 42 nm for the calcined Quintinite-3T. Kinetic analysis, adsorption isotherm, and factors affecting the adsorption were investigated. Calcined Quintinite- 3T retained As(v) and did not release it back to water even after an entire month.

Jan 1, 2016

By Mitsutaka Hino

The contents of gangue minerals, such as Al2O3. P2O5, crystalline water and so forth in the iron ore imported to Japan tend to increase year by year. Though the increments of such gangue contents arc approximately 0.1-0.2 mass%, some problems for the blast furnace operation in ironmaking process have already been reported, In order to clarify the mechanism of harmful effect caused by the small increment of gangue minerals, mainly Al2O3. on the blast furnace operation, the dripping behavior of Fe,O-CaO-SiO2-Al2O3-MgO slag from the iron funnel, which simulated the micro-porosity in sinter ore, has been observed with the wide range of basicity, Al2O3, Fe2O and MgO contents. The effect of MgO on the dripping behavior of slag has been summarized in this paper. It was found that the addition of 2mass% MgO resulted in large increase of hold-up on the most of the conditions. When Fe2O content was less than 20mass% and the basicity was lower than 0.8, MgO lowered the hold-up even if the slag contained 10mass% Ah03. Every slag hold-up showed the minimum at the basicity of less than unity on the conditions of constant Fe2O and Al2O3 contents, This trend became remarkable when the slag contained 2 mass% MgO.

Jan 1, 2003

By Jinrong Zhang

Major components of soil were tested for their ability to attenuate cyanide. Feldspar, kaolinite, plagioclase and bauxite are found to degrade cyanide at an appreciable amount mainly through adsorption. A soil near a mining site in northern Nevada was studied in detail using a tall column. Many species of cyanide were anlyzed to determine the mechanisms of the reactions of cyanide with soil. Volatilization, adsorption, oxidation, precipitation and complexing were quantitatively identified, being 5 to 10, 11.7, 4.2, 7.3 and 4 per cent of the total cyanide added, respectively. It is found that the oxidation of cyanide to cyanate is due to the catalytic effect of nickel and copper leached from the soil. Precipitation of metal-cyanide complexes occurred at low pH values.

Jan 1, 1991

By Masatoshi Ogasawara

Saganoseki smelter & refinery operated two flash smelting furnaces, producing a combined 330,000 metric tons per year (hereinafter mtpy) of copper. In 1996, however, it successfully shifted to a single furnace operation while maintaining production at the same level. Since then, the production capacity has been further increased to the present 470,000 mtpy by technological improvements. Also, in order to reduce the converter load which represents a bottleneck in efforts to increase production, the matte grade was gradually increased and currently runs at 65 to 66% attaining the low copper content in the slag (hereinafter slag loss) of 0.7 to 0.8%. This paper introduces some improvements, recent operation results and thermodynamic analyses.

Jan 1, 2003

By Defeng Zhou, N. Trubaki, Jian Meng, Fanzhi Menga, Xiaojuan Liu, Yanjie Xia

"The microstructure and the electric conductivity of (Ce0.9Nd0.1)1 xMxO2 d (M=Mo, W) solid solutions were investigated. It has been found that their conductivity containing the grain (s gi ), the grain boundary (s gb) and the total conductivity (s t ) at 300°C- 700°C can be ranked as: (Ce 0. 9Nd 0. 1 ) 0.99 W 0.01 02- d (s gi = 0.065 S.cm·1, (s gb = 0.265 S.cm·1, s t = 0.039 S.cm-1) > (Ce0.9Nd0.1)0.99Mo0.01O2- d (s gi = 0.053 S.cm·1, s gb = 0.142 S.cm·1, s t = 0.029 S.cm-1) > Ce0.9Nd0.1 s 2- d (s gi 0.045 S.cm-1, s gb = 0.091 S.cm-1, s t = 0.018 S.cm-1) measured at 700°C. The highest conductivity is obtained in (Ceo.9Ndo.1)0.99W0.01O2 d. These results indicate that (Ceo.9Nd0.1)0.99W0.01O2- d is the most promising electrolyte materials of intermediate-temperature solid oxide fuel cells among (Ce0.9Nd0.1)1-xMxO2- d. IntroductionRare-earth (e.g. La3+, Nd3+, Gd3+ and Sm3l doped ceria-based ceramic materials have been acknowledged to be attractive electrolytes for solid oxide fuel cells operating below 600°C due to their high ionic conductivity [1, 2]. In order to improve ionic conductivity of these electrolytes further, in recent reports [3-6], some aids such as Mo03 [3] etc. in a limited amount can be used which causes extremely high conductivity. For example, Zhou et al. found that with MoO3 doping, the grain boundary conductivity of Nd3+ doped CeO2- d increased notably especially at lower temperatures due to the effect of severely undersized do pants [3]. It is well known that the size of W6+ (rw6+ = 0.60 Å) is close to Mo6+ (rMo6+ = 0.62A) because of lanthanide shrinkage. Thus, rare-earth doped ceria e.g. Nd3+ doped CeO2g with WO3 in a limited amount will be probably good and even better electrolytes. However, much less information is available about these materials. Therefore, in our paper, (Ce0.9Nd0.1)0.99 1-xMxO2- d (M=Mo, W) solid solutions have been prepared and characterized. Much higher conductive electrolytes are found in the series of (Ce0.9Nd0.1)0.99 M0.01O02- d particularly (Ce0.9Nd0.1)0.99W0.01O2- d"

Jan 1, 2012

By K. Adham

"Fluidized beds are utilized in a wide range of high-temperature applications throughout the metals and materials industry. Their main advantage is the fast and uniform heat and mass transfer between the hot combustion gases and the particulate solid feed. A further benefit can be the lowering of the processing plant's energy consumption, through heat recovery from the fluid bed processes used for solids heating. Here, the enhanced energy efficiency of fluidized systems is investigated and the modeling results are discussed for three configurations: the flash tube, the single bubbling bed and the multi-stage fluid bed. Key thermal design aspects of each system are identified based on results from process simulations, in order to benchmark their main operating features and overall energy efficiency. Suitability and applicability of each configuration is also discussed based on a number of process and material property considerations.IntroductionCombustion based heating of particulate solids is commonly done using three different types of fluidized beds. The flash tube (FT) is similar to a hot pneumatic transport system. The single-stage fluidized bed (FB) typically uses in-bed combustion. The multi-stage fluidized bed (MSFB) can have two or more stages stacked into a tower.Flash tube (FT) suspends the incoming solid charge in a high-velocity stream of hot combustion gases. To maintain the solids suspension in the FT, two parameters are required: high velocity for elutriation of the particles and adequate solid-to-gas ratio for avoiding high pressure drops and solids drop-out [l].The fluid bed (FB) works at much lower velocities than the flash tube. Therefore, most of the solids are not conveyed in the gas stream, but are only suspended in a liquid-like manner. At minimum fluidization velocity (Umr), the gas flow exerts just enough force on the solids to keep them suspended in place [2].Multi-stage fluid bed (MSFB) heats up the solids as they are transferred from an upper bed level to a lower one, counter-current to the rising flow of hot gases generated at the lowest stage. As the temperature and volumetric flow of the gases decrease from bottom to the top stage, smaller bed diameters can be used in the energy recovery stages [3]."

Jan 1, 2014

By Emilia Visileanu, Eftalea Carpus

"Ecological economic policy shall be understood as the sum of political, economical and environmental measurements aimed at the entire economy dematerialization and the dematerialization shall be ""imposed"" since the designing stage of goods and services"". European textile and clothing industry with a long leading tradition in terms of innovation, fashion and creativity, continues to be one of Europe's major industrial sectors. Textile industry affects the environment by high consumption of water, energy and chemicals, as well as by the large amount of waste it generates as a result of using a large number of chemicals and technological processes.Textile waste prevention, reduction and ecological exploitation require the implementation of new management and education tools.Introduction“Europe must learn from the experience of global economic and financial crisis ""- this was the conclusion of the European Commission that has elaborated a ten-year strategy designed to reinvigorate the economy and make possible a growth which is ""intelligent, sustainable and favorable to inclusion"", by a better coordination of national and European policies.Adapting infrastructure and logistics that encourage the marketing of ""sustainable"", ""fair traded"" and ""green"" products as well as other special „green” products will facilitate the movement towards dematerialization and eco-efficiency among producers."

Jan 1, 2012

By Martin Brueggemann

In 1993, the El Paso Smelter began operation of the first commercial CONTOP copper smelting furnace. The CONTOP process was chosen for the plant modernization due to its low capital cost and the ease that it could be incorporated into a 100 year old existing smelter. After four years of operation, CONTOP has proved itself to be a reliable copper smelting technology. This paper will discuss a brief start-up history, current operation, and future modifications and improvements.

Jan 1, 1998