Search Documents

By Zhao-cheng Liu

Iron oxide red pigment powders of high quality were synthesized from pyrite cinders. Iron ox-ide red pigment powders were synthesized by hydrothermal method from the precursor of Fe(OH)3 and Fe(OH)2 colloid, which were obtained after ammonia solution reacted with acidic leaching solution produced by the reaction of pyrite cinders with sulfuric acid. Effects of reaction concentration, reaction temperature, reaction time, pH value and n(Fe2+)/n(Fe3+) on main properties of oxide iron red were studied by experiments. The prepared particles were characterized by means of X-ray diffraction (XRD) and scanning electron microscope(SEM). The results revealed that the synthesized iron oxide red particles were _-Fe2O3 and pseudocubic with particle size of 0.50~0.75µm. Furthermore, the quality of iron oxide red pigment powders reached the first grade of national standard (GB1863-89 ).

Jan 1, 2009

By Yue-yuan Li

China has abundant magnesite resource, but the low-grade and powder ores have always been rejected, which influences the comprehensive utilization of resource and often causes circumstance problems. The present work investigated the preparation of magnesia whisker using magnesite tailings as starting materials by preparation magnesium carbonate whisker as precursor firstly in the route of calcination, hydration, carbonation and pyrolysis, follows by second calcination of the precursor. The influence of pyrolysis conditions and additives on morphology of magnesium carbonate crystal as well as the influence of calcination conditions on morphology of magnesia whisker was investigated. The results showed that thermal decomposition products was MgCO3?3H2O. Magnesium carbonate whisker with length of 10~60 µm and the length-to-diameter ratio of 10~20 was prepared when soluble magnesium salt was added. While temperature was elevated at 1°C?min-1, magnesia whisker with length of 10~60µm was obtained.

Jan 1, 2010

By Valerio Viti

In High Pressure Die Casting a molten metal is injected through a thin gate into the cast cavity. High injection pressures and high gate velocities create atomization phenomena which can negatively affect the final quality of the cast. In order to control atomization process it is essential to understand the atomization patterns and the two-phase flowfield that exist at the gate exit. In the present work, 2D numerical simulations of the flow of molten Magnesium through a high aspect-ratio rectangular gate are performed using a water analogue for an open and closed cavity. The numerical simulations made use of VOF-type (Eulerian) physical models and Lagrangian models. Further, a sub-grid scale model was implemented that, in conjunction with VOF-type equations can efficiently predict the general atomization pattern without the need for high-resolution grids. The numerical results were compared to experimental data for validation.

Jan 1, 2006

By WU Jian-hui

Keywords: metallic material; nickel powder; thermal decomposition; precursor; fibrillar powder; nanometer scale; passivation treatment The precursor thermal decomposition process of fibrillar nanometer scale nickel powder and passivation treatment of obtained powder are investigated, and the composition and morphology of the products are characterized by use of IR, TGA/DTA, XRD and SEM. The results show that the precursor morphology is a decisive factor to the product morphology of the nickel powder. The morphology of the product derived at low decomposing temperature is irregular. The nickel powders produced at the temperature higher than 480 coheres seriously. The product particles are reunited with the decomposition time prolong. The powder prepared under the optimal condition is fibrillar like woolen yarn; the grain diameter is less than 50nm.

Jan 1, 2005

By Wellington Pereira Inácio

This work investigated the toughness behavior of polyester matrix composites reinforced with up to 30% in volume of long, continuous and aligned sisal fibers by means of Charpy impact tests. It was found that the addition of sisal fibers results in a marked increase in the absorbed impact energy of the composites. Macroscopic observation of the post-impact specimens and SEM fracture analysis showed that longitudinal rupture through the sisal fiber interface with the polyester matrix is the main mechanism for the remarkable toughness of these composites.

Jan 1, 2010

By M. T. Baquera

A comparison of microstructures associated with W single-crystal ([001], [011], [111]) rods prior to deformation (as grown), and after quasi-static compression (at a strain rate of ~1/s) by transmission electron microscopy (TEM) shows several orders of magnitude difference in dislocation density. Dislocation substructures were not significantly different amongst the deformed sample orientations. In contrast, [001] W rods penetrated into steel targets, at impact velocities of ~1.3 km/s, exhibited heavy dislocation densities and dynamic recrystallization as very distinct microstructural regimes accommodating the penetration process. Twinning on {112} also occurred as a precursor to, or remnant of, these microstructures near the projectile head. These results suggest that deformation accommodating the extreme strains and strain rates associated with the penetration of a single-crystal rod into a metal target is not adequately represented by conventional deformation

Jan 1, 2006

By Changqing Su

A batch incubation experiment has been carried out to investigate the optimal condition for the microbial remediation of hexavalent chromium (Cr(VI)) in soils contaminated by chromate ore processing residue at Hunan Iron-Alloy Factory in China. The optimal condition was obtained by comparing the remediation efficiency of Cr (VI) by indigenous bacteria under different culture media, the quantity of nutrient sources, the pH and the temperature. The results indicated that glucose and yeast extract was the optimal component of culture medium and the quantities of the above components were 8 g L-1 and 13 g L-1, respectively. The optimal temperature and pH value were 30_ and 10.0, respectively. A bioreactor was operated under the optimal condition to evaluate the efficiency of Cr(VI) remediation in the contaminated soil. The result showed that water soluble Cr(VI) in soils was reduced from 320 mg kg-1 Cr(VI) of the initial concentration to below detection limit after 30 h in a bioreactor. Thus, there is a large potential to make bioremediation for the reduction of Cr(VI) to Cr(III) by the addition of optimal culture medium under aerobic condition.

Jan 1, 2010

By Taegong Ryu

Nanosized tungsten powder was synthesized by the hydrogen reduction of ammonium paratungstate (APT) in thermal plasma. The effects of operating conditions on the product composition and particle size were investigated. The particle size of synthesized W powder was less than 30 nm in all cases tested. The sintering behavior of the synthesized powder (25 nm average size) was then investigated and compared with those of commercial W powder of 500 nm average size and W powder of 23 nm average size produced by milling the commercial powder. The sintering was done at 1400oC with various holding times. The hardness of the resulting compact from the synthesized W powder (315 VHN) was similar to that from the milled W powder (309 VHN), but the plasma-synthesized powder had a much lower tendency to form cracks. The compacts of both nanopowders were significantly harder than that of the commercial powder (192 VHN).

Jan 1, 2009

A series of electron beam, cold hearth, single melt Ti-6Al-4V plates (nominally 2.5 cm thick) impacted by 2cm diameter, 4340 steel projectiles (with 54g nominal mass) at velocities ranging from 0.633 to 1.027 km/s were sectioned along the impact axis and examined by optical metallography to characterize the formation, growth, and microstructure of adiabatic shear bands. Near ballistic limit velocities, the shear bands propagate towards the rear of the target where they coalesce and grow to provide a cylindrical solid state flow regime for the plug volume.

Jan 1, 2006

By Natalya. N. Ankusheva

The problems of ore-bearing palaevolcanic structures in folded belts are actual because of their high productivity in nonferrous, ferrous and noble metals ores. Now relationships of location and conditions of formation for sulfide-massive and gold-bearing deposits are investigated very well in Urals. But carboniferous sulfide-barite mineralization, for example the barite veins in Arcaimsky palaevolcano are?nt studied enough now [3-5]. The purpose of this research is the studying of mineralogy and thermobarogeochemistry of barite from the hydrothermal veins. It will allow to determine the conditions of its formation and to compare it to the similar mineralization of others ore types.

Jan 1, 2006

By P. N. Anyalebechi

The effects of solidification rate (0.4-26.1 K/s) and alloying elements on the cast microstructures of aluminum alloy 5182 have been investigated with directionally cooled laboratory-size ingots. The alloying elements examined included Mg (3.6-4.7 wt.%), Mn (0.35-0.75 wt.%), Fe (0.11- 0.42 wt.%), Cu (0.03-0.25 wt.%), and Si (0.11-0.28 wt.%). These reflect the chemical compositions of AA 5182 end stocks with high recycled used beverage container (UBC) content. For a given chemical composition, the average dendrite cell and constituent phase particle size decreased with increase in average solidification rate. In general, within the level investigated, Mg did not have a significant effect on the types, volume fractions, and average sizes of the constituent phase particles. However, increase in Mn, Si, Fe, and Cu increased average sizes and volume fractions of the constituent phase particles.

Jan 1, 2010

By Youze Xu

The leaching and reduction of Cr(VI) in soils contaminated by chromium-containing slag were investigated with column experiments. The results showed that Cr(VI) concentration in leachate decreased from 988 mg L-1 to 407 mg L-1 after 7 days when water was used as leaching agent. However, Cr(VI) in leachate in culture medium treatment was not detected at above periods. In comparison, Cr(VI) concentration in leachate from autoclaved soil remained 398 mg L-1 at the end of experiment. The results indicated that the indigenous microorganism was capable of reducing Cr(VI). The amount of Cr(VI) reduction was 335 mg at the whole experiment period and the reduction rate was 67.09 mg d-1. Carbon supply showed minor effect on Cr(VI) reduction. However the reduction capability of Cr(VI) could be improved by combination of the carbon and the nitrogen. The optimal quantity was 5 g L-1 of yeast extract and 4 g L-1 of glucose.

Jan 1, 2009

By Jinwu Kang

The hydraulic turbine blade of the matensitic stainless steel (Cr13%,Ni5%,Mo1%) is a kind of large and curved shape, which is susceptible to deformation in both casting and heat treatment processes. The coupling analysis of heat transfer, phase transformation and stress in heat treatment process of the turbine blade for Three Gorges Project is carried out by using Deform-3D software. Its temperature fields, phase fields and stress fields in heat treatment process are obtained. And its deformation is predicted. In the cooling process of normalizing, the blade exhibits relatively large deformation. Based on the stress analysis and deformation prediction in heat treatment process, an algorithm for the determination of reverse deformation of the blade casting in heat treatment process is presented. And the reverse deformation distribution of blade is obtained.

Jan 1, 2010

By M. Potesser

One of the main targets in the automotive mass industry and supplying industry is the weight reduction of the vehicle for decrease of the fuel consumption. For that reason combinations of different kinds of materials and connections of, for example, steel and aluminium are developed or are already successfully field-tested. A determining factor concerning the quality assessment of the welded joint during hybrid welding is the characterization of the intermetallic Fe-Al layer regarding strength, hardness, morphology and mainly the different phases in which Fe occurs together with the Aluminum (FeAl, Fe2Al5, FeAl3.). A combination of conventional light microscopy, SEM - EDX - analysis, the usage of an atomic force microscope including a Nanoindenter and theoretical thermodynamic calculations turned out to be highly effective. Based on the attained results, the constitution of the intermetallic FeAl layer, influenced by silicon, manganese and zinc, can be predicted.

Jan 1, 2006

By Shirleny Fontes Santos

Muscovite mica crystals lower than 15 mm diameter are discarded as waste in the mining area of Borborema-Seridó (BRAZIL). The objective of this work was the ore dressing and purification of this waste to be used in the preparation of pearlescent pigment. Muscovite was dry ground using knife mills and an ultrasound treatment. It was possible to achieve 67% of mica with particle size lower than 100 µm. This product was used in the preparation of brilliant pigments based on muscovite flakes covered with rare earth oxides (CeO2, PrO2, Ce0,95Pr0,05O2). The pigments were characterized by X-ray diffraction, thermal analysis and scanning electronic microscopy. The color of the resulting pigments was analyzed using the CIELAB method and it showed the following colors: muscovite-CeO2 ? yellow, muscovite-PrO2? black and muscovite-Ce0,95Pr0,05O2 ? orange. Those results have shown that ?trash mica? is suitable for use in pigment preparation.

Jan 1, 2010

By J. E. Hoffman

The operation of the U .S Metals Refining Company, USMR Co. is defined below by the description of a variety of unit processes and operations the author encountered during his tenure with the operation, 1955 - 1978. The operations discussed include: sampling and sweating of radiators, processing of Indian Coin, treatment of insulated wire, baghouse and converter dust treatment, blast furnace and converter operation, the electric arc furnace, antimony control, selenium and tellurium products, electrolyte liberation with soluble anodes, and the precious metals refinery. These operations, although peripheral to the primary copper production circuit, were critical to the company's technological and economic base.

Jan 1, 2000

By Liang Sha

In this study, adsorption of copper by chemically modified orange peel was investigated. A conspicuous change occurs in the surface morphology of the biomass due to modification, which is depicted by SEM images. Equilibrium isotherms and kinetics were obtained and the effects of various factors, including solution pH, contact time, initial metal ions concentration and temperature, were studied by batch experiments. Kinetics was found to be best-fit pseudosecond- order equations. Equilibrium was better described by Langermuir isotherms rather than Freudlich isotherms. At 25?, pH5.30, the maximum adsorption capacity was 70.67mg?g-1 . With increase of temperature, adsorption efficiency decreased. The biosorbent was suitable for repeated use for more than five cycles.

Jan 1, 2009

By Albert Wraith, Thomas Price, Wayne Boyd, Skip (I. E. ) Hills, Cameron Harris

Most Peirce-Smith converters inject air through tuyeres, with nitrogen representing the majority of gas passing through the process. The nitrogen controls the temperature of the vessel by carrying away heat from the reactions, both globally and locally at the tuyere tip. However, nitrogen adds energy to the bath and contributes to splashing and limits the blowing rate. High oxygen smelting has made streams of gas containing high concentrations of sulphur dioxide commonplace, which can be used to substitute SO2 for nitrogen and drastically changes Peirce- Smith converting (and all other smelting/converting processes as well). Less SO2 is required to carry away the same quantity of heat, which allows higher concentrations of oxygen and leads to the possibility of increased production. The paper investigates this substitution, its impact on converter productivity, and on the remainder of the plant. 181

Jan 1, 2009

By T. T. Chen

Copper anodes generated from copper scrap are relatively rich in Sn, Zn and Fe. Because of the presence of oxygen, only trace amounts of Sn occur in solid solution in the copper crystals. Thus, Sn occurs mainly as SnO2, Cu-Sn-Ni oxide and Sn-Ni-Zn oxide in the copper anodes, and Zn and Fe occur mainly as minor constituents in the Sn-Ni-Zn oxide and Cu-Sn-Ni oxide. During electrorefining, these oxide species are liberated from the copper anodes and report directly to the anode slimes. The trace amounts of Sn present in solid solution in the copper crystals dissolve but reprecipitate as Sn arsenate or a Sb-As-Sn-O phase. Accordingly, high Sn contents in copper anodes do not lead to elevated Sn concentrations in the electrolyte.

Jan 1, 2010

By M. Faraji

Inclusions formed in a high-carbon, manganese-silicon killed plain steel (Fe-0.77C wt%) were studied. Various techniques were used to characterise the inclusions, and the latter were classified according to their chemical composition, size and morphology. The main constituent elements entering the inclusions were Mn, S, Al, and oxygen. Alongside MnS and some Al2O3 inclusions many non-metallic inclusions appeared in complex forms, consisting of silicates, sulphides and oxides. Duplex oxy-sulphides, mainly MnS combined with Al2O3, or SiO2 were the most common complex multiphase inclusions in this steel. The nanoindentation technique was used to assess and rate different types of inclusions and data of the hardness and elastic modulus of individual inclusions at room temperature are presented.

Jan 1, 2010