By John A. Gann

The following investigation constitutes a brief réumé of the more important binary magnesium alloys from the standpoint of metallo-graphic technique, and the effect of heat treatment on structure and properties. The comparative newness of the subject justifies this procedure as a preface to a more detailed study of each individual series of alloys. The work was started with the idea of practical application in the industry rather than as a theoretical investigation. The alloy compositions studied were selected as those most likely to show whether heat treatment would produce beneficial results. Furthermore, it was considered satisfactory to use commercial 99.9 per cent. magnesium, the best commercial grade of alloying ingredients, and to limit the time of heat treatment at the expense of incomplete equilibrium. These facts must be kept in mind when examining the results obtained, and the conclusions drawn. Preparation of Alloys All melts were made in an oil-fired cast-steel pot, approximately 12 in. dia, by 12 in. deep. Approximately 15 lb. of flux and 50 lb. of magnesium were melted and the calculated amount of alloying metal was added. After thorough alloying and puddling, the metal was chill cast in a graphite mold with four 1/2 by 1/2 by 4 in. bars fed from a common sprue and runner. The next higher composition alloy in a given series was made by adding the calculated amount of metal to the heel from the preceding cast. The pot was thoroughly cleaned after each series and new flux then introduced, thus avoiding possible contamination from earlier melts. The percentage compositions given in Table 1 are the calculated values. While not all alloys were analyzed, enough were checked to indicate that the reported compositions are correct to a few tenths of one per cent. A more detailed description of the foundry methods employed has been given in a previous paper. 1

Jan 1, 1929

By C. Y. Clayton

In connection with certain cooperative work carried on between the Ordnance Department of the U. S. Army, the U. S. Bureau of Mines, and the U. S. Geological Survey during the year 1918, it was the writers' privilege to make metallographic examinations of a great many test bars and other pieces of nickel-steel gun forgings. The material studied came from many different steel plants throughout the country and consisted both of forgings that had been accepted by the Ordnance Department and those that had failed to pass the specified physical tests. In general, these tests require a minimum tensile strength of 95,000 lb. (42,091 kg.)! an elastic limit of 65,000 lb. (29,483 kg.), an 18 per cent, elongation, and a 30 per cent. reduction in area. An average chemical composition of the steel studied is 0.38 per cent. carbon and 2.9 per cent. nickel. The steel was of both basic electric and basic open-hearth manufacture. The object of the metallographic work was twofold: to assist in detecting defects in the steel and, if possible, to suggest remedies for the same; and to obtain as much information as possible in regard to the relation of the microstructure of the metal to its physical properties. The grcatcr part of the investigation was devoted to defective metal that failed to pass the ordnance specifications. Many types and kinds of more or less serious defects thus came under observation, but most of these were due to the attempts by the manufacturer to meet the enormous demand for ordnance steel with more or less inadequate equipment, and were soon remedied. Two defects, the so-called "flakes" or "snowflakes" and a certain "fibrous" or "woody" fracture, were encountered so frequently and were so disastrous to the steel that the greater part of the study was devoted to them. As a result much information as to their nature and their effects upon the steel and something in regard to some of the conditions that favor their development has been obtained. The purpose of the present

Jan 1, 1920

By John A. Gann

The following investigation constitutes a brief réumé of the more important binary magnesium alloys from the standpoint of metallo-graphic technique, and the effect of heat treatment on structure and properties. The comparative newness of the subject justifies this procedure as a preface to a more detailed study of each individual series of alloys. The work was started with the idea of practical application in the industry rather than as a theoretical investigation. The alloy compositions studied were selected as those most likely to show whether heat treatment would produce beneficial results. Furthermore, it was considered satisfactory to use commercial 99.9 per cent. magnesium, the best commercial grade of alloying ingredients, and to limit the time of heat treatment at the expense of incomplete equilibrium. These facts must be kept in mind when examining the results obtained, and the conclusions drawn. Preparation of Alloys All melts were made in an oil-fired cast-steel pot, approximately 12 in. dia, by 12 in. deep. Approximately 15 lb. of flux and 50 lb. of magnesium were melted and the calculated amount of alloying metal was added. After thorough alloying and puddling, the metal was chill cast in a graphite mold with four 1/2 by 1/2 by 4 in. bars fed from a common sprue and runner. The next higher composition alloy in a given series was made by adding the calculated amount of metal to the heel from the preceding cast. The pot was thoroughly cleaned after each series and new flux then introduced, thus avoiding possible contamination from earlier melts. The percentage compositions given in Table 1 are the calculated values. While not all alloys were analyzed, enough were checked to indicate that the reported compositions are correct to a few tenths of one per cent. A more detailed description of the foundry methods employed has been given in a previous paper. 1

Jan 1, 1929

MINING ENGINEERING presents the annual membership report of the Society of Mining Engineers; see page 147.

Jan 7, 1964

By Robert Rhea Goodrich

This research was done partly in the non-ferrous laboratory of the Department of Metallurgy of Columbia University, under the direction of Dr. Edward I?. Kern, and completed elsewhere. Acknowledgment is due to Prof. Arthur L. Walker, Dr. Edward F. Kern and Dr. William Campbell of the Department of Metallurgy, for their kind advice and for the inspiration derived from their instruction. This report is given under the following heads: Petrographic Description (Microscopic Study); Sampling and Preparing Ore for Treatment; Chemical Analysis; Treatment of Ore. Petrogeaphic DescRiption Texture: variable. Fine to medium mixed aggregate. Original Structure: Obscurc. Secondary structure: Fractured; healed. Mineralogy (Minerds are grouped for interpretation purposes and are arranged, in each group in approximate order of abundance)

Jan 1, 1916

By Norman Braly

THE following is not offered as an extended paper on the subject of shaft sinking, but more as a description of the present practice of shaft sinking in the Butte district. The Anaconda company is sinking at present the following shafts: Badger State, Moose, Mountain Consolidated, Mountain View, Pennsyl-ania and Tropic. At the High Ore and Leonard mines the shafts are being deepened by sinking two compartments and will subsequently be enlarged to the full working size by raising alongside the compartments which are now being sunk. The following other companies are also sinking shafts: Butte-Alex Scott, Butte and Zenith City, Boston and Corbin, North Butte Mining Co. (at the Granite Mountain shaft), East Butte Co. (at the Pittsmont shaft), and the Rainbow Lode Development Co. Shaft Timbering. The shafts of the Butte district, generally speaking, are of three compartments arranged in a straight line, and the pump compartment is usually arranged for the use of an auxiliary hoisting cage, as well as for carrying pipe lines and electric wires. The Rainbow shaft is practically square, and of three compartments. The length of the shafts outside of timber will vary from 17 to 22 ft., and the width from 6 ft. 6 in. to 7 ft. Fir timber is used in all shaft work. This may be obtained from the Coast, when it is known as Coast fir, or from Idaho or Montana, when it is known as native fir. The native fir seems to be the tougher wood, but it is hard to obtain clear lumber in the lengths and sizes necessary for shaft work. Some of the shaft timber of the Anaconda company has been treated with creosote as a preservative, but this practice has not come into general use, as the ground of the camp is so heavy that the timbers usually crush before they rot. The size of timber most .used for shaft work is 12 by 12 in., while 10 by 12 in., 10 by 14 in. and 12 by 14 in. are used for some of the special pieces around the shaft. The new Leonard shaft is timbered with 14 by 14 in. wall plates throughout.

Jan 8, 1913

In the Philippines, where distances are spoken of in terms off fight time, the Sipalay copper mines are two flight hours southeast of Manila on the island of Negros. After landing at the airport in Bacolod, it is then 170 km (106 milers) by surface transportation to Marinduque Mining and Industrial Corp.'s expanding copper operation. While copper deposits were discovered in the area in 1936-and one mine, the Binulig, began operations soon after-it wasn't until 1956 that stripping at Sipalay and construction of a 4000-t/d (4400-stpd) mill began. The mill went into operation in May 1957, and the first shipment of copper concentrate was made three months later.

Jan 8, 1978

By N. E. Maccallum

(Cleveland Meeting, October, 1912.) ALMOST half a century has passed since the Siemens brothers, after tedious and costly experiments, finally began the manufacture of open-hearth steel. The furnace of that time was very small, having a hearth-capacity of from 3 to 4 tons, and we can appreciate the wonderful development that has taken place in those 50 years by the knowledge that to-day furnaces of 50 times the original capacity are in operation. As the new steel process assumed importance, and furnaces began to grow in number and in size, a question arose, to which no satisfactory answer has ever been given, and that was: ?What is the safe and economical limit of the open-hearth furnace?" Various stopping-places have been suggested, and 20, 30, 40, and 50 tons have each been advocated, but all such arbitrary restrictions have been passed, and 60 tons would probably represent the average furnace, although in a few instances from 70 to 80 tons are regularly tapped into one ladle. The furnaces which are the subject of the present paper have gone far beyond even these limits, and since, in my opinion, they mark another step in the progress of open-hearth steel, they will be considered fairly and frankly, in order that those to whom the matter may be of interest may be able to judge and form their own Conclusions. Short accounts of the work of these furnaces have appeared from time to time in various technical journals, of which the following is a brief résumé. These furnaces are the property of the Phoenix Iron Co., of Phoenixville, Pa., and their distinctive and important feature is, that they charge to twice the capacity of one ladle, and tap simultaneously into two ladles, with a device for controlling the flow into either. In this way the capacity of the furnace is not limited, as formerly, but heats of any size within the capacity of two ladles may be charged.

Oct 1, 1912

By C. W. Chen

MARTENSITE transformations in ß Cu-Al alloys have been studied by Greninger1 and other investigators. According to Greninger, the parent phase ß1 an ordered body-centered-cubic structure obtained from ß phase by suppressing the eutectoid decomposition, transforms into an ordered hexagonal-close-packed phase in composition containing 12.9 to 14.7 pct Al. The M, temperature decreases with increasing aluminum content; for the alloy containing 14.5 pct Al, for example, the ß1??' transformation occurs below room temperature. More recently, Kurjumow2 studied the transformation in ß Cu-Al alloys with the addition of nickel. His report stimulated new interest in the subject due to the observation of completely reversible transformation without hysteresis in the transformation temperature ranging from 10° to —10°C. In the present paper some characteristics are described of the transformation of Cu-Al-Ni alloys that were partly studied by Kurjumow. Experimental Procedure High purity copper (99.999 pct) and aluminum (99.99 pct) and electrolytic nickel were used in the preparation, by the Bridgman technique, of single crystal specimens which contained aluminum and nickel of 14.5 and 0.5 to 3.0 pct, respectively. Polished surfaces were prepared mechanically. Specimens were then chemically etched to remove distorted material, homogenized at 1000°C for several hours, and quenched drastically to room temperature in a 10 pct NaOH bath to produce the parent phase ß1. The transformation was studied under a microscope and, in some cases, recorded by means of motion pictures. A device similar to that designed by Greninger and Mooradian3 was used to cool and reheat the specimens. Results and Discussion When the specimens were cooled below room temperature, the ß1 to ?' transformation began at 10°C with the appearance of ?' crystals In relief, Fig. la. As the specimen temperature dropped further, the transformation continued, either by the growth of the ?' crystals, with the ß1 — ?' interface moving into the ß1 phase, Fig. 1c and 1d, or by the formation of new ?' crystals, Fig. 1b. As a consequence of the former process, banded structure is observed as a common feature of the low temperature phase. According to the theory of the formation of martensite by Wechsler, Lieberman, and Read,' the bands of ?' phase are probably twin-related, as is the case in the diffusionless phase change of In-T1 alloys,5 but this was not revealed by X-ray tech- niques. New ?' crystals, in needle form, often emerged suddenly across the ?' bands during the transformation. These acicular crystals then grew, both in length and in width, see Fig. 2a through 2d. The transformation on cooling is completed at about -35°C. Upon heating, the reverse transformation started at —10° C, in a manner nearly opposite to the transformation on cooling, and completed at 35°C. There was no noticeable change in the transformation temperature when the nickel content was varied within the limits previously mentioned. Through control of the specimen temperature, the transformation can be started, stopped, or reversed at will. This phenomenon has frequently been observed in the martensite transformation of many nonferrous alloy systems. Other systems are Au-Cd6 and In-Tl.5 ow-- ever, in the latter systems, the transformation is accomplished by single interface motion if the specimen composition is homogeneous and the temperature gradient in the specimen is uniform and sharp, whereas in the Cu-Al-Ni specimens, only multiple interface transformation is observed. The speed of the interface motion appears to be a functionof the rate of temperature change and the temperature gradient across the specimen length. In one case, in which the temperature increased at the rate of 10°C per min and there was no temperature gradient along the specimen axis, the speed of the disappearance of a ?' plate was determined, by the study of the motion pictures made, to be 26 µ per sec. Quench markings were observed on the polished surfaces of specimens. The markings were grouped into one or more sets of different orientations, and were parallel in each set. The ?' plates formed in subsequent transformation were parallel to the markings, indicating that the ?' plates and the quench markings had the same geometric relation-ship to the ß1 matrix. The quench markings on two intersecting surfaces of a specimen were therefore used in the determination of the habit plane of transformation, by the trace method suggested by Barrett.' Results obtained from five sets of markings in three specimens indicate that the habit plane is an irrational plane about 2" from one of the {221} planes. This is very close to the habit plane (3" from 221 planes) of ß Cu-Al alloys containing more than 13.0 pct Al.1 The martensite transformation of Cu-Al-Ni alloys is reproducible. No sluggishness was found between consecutive transformation cycles, although a slight difference in the distribution pattern of the ?' plates was observed, compare Figs. Id and 2d. The transformation can be strain-induced. This characteristic has been tested by a simple method. When a specimen was elastically strained slowly in a vise, ?' plates were gradually produced in the same fashion as during transformation on cooling, This test was done at room temperature, and thus above the M,

Jan 1, 1958

Jan 1, 1965

By Louis G. Bailey

This paper .reviews some of the key developments which have been made in the synthesis of the III-V compound semiconductors and the associated progress in obtaining high-quality material for device development. The history of the investigation of the semi-conducting properties of these materials has indicated the need for synthesis techniques capable of producing rnaterial of high chemical purity and physical perfection. The progress in the area is described, and the present status of quality of several compounds is discussed. In addition, recent studies of localized epitaxial deposition of GaAs into semi-insulating GaAs substvates for the development of arrays of devices ave reviewed. In conclusion, some important areas for future research and developrnent are discussed. INTEREST in III-V compounds as semiconductors dates back to the period 1950 to 1952, when Goryunova, Ioffe, and, in particular, Welker determined that 111-V compounds were structural analogs of the group IV elements carbon, silicon, germanium, and tin and that they were also semiconductors.'-3 Since that time interest in the properties of these materials has ex- panded rapidly. During 1953 and 1954, the first reports of rectification, photoconductivity, and optical absorption in these materials came from several investigators. In 1955, recombination radiation from samples of GaAs, InP, and GaSb was reported by ~raunstein .' This radiation was produced by injected minority carriers from point and large-area contacts. From 1955 to 1960, efforts increased on preparing large, pure specimens of these materials for the study of basic physical phenomena and device exploration. By 1960, materials preparation and the understanding of the physics of some of the materials had advanced to where some very interesting and potentially useful phenomena came under study. The first observation of electric-field-induced changes in the optical absorption edge (Franz -Keldysh effect) of 111-V compounds was reported for GaAs by Moss in 1961.' In 1962 the study of recombination radiation advanced rapidly. Keyes and Quist6 and Pankove and Berkey-heiser7 reported high radiative efficientices obtained from recombination, and then the first injection electroluminescent lasers in GaAs were announced by Hall ef al.,' by Nathan et al.,O and by Quist ef al.,'O and in Ga(As, P) alloys by Holonyak and Bevacqua." Hil-sum has reviewed the early work leading to the first observations of laser action in GaAS." Recombination processes in GaAs, Gap, and the other 111-V com-

Jan 1, 1968

By Dilip K. Das, Douglas T. Pitman

ONE of the major uses of barium in metallic form is as a getter material in vacuum tubes. Because of the high chemical reactivity of the metal, Ba-Al alloys are extensively used. Numerous methods for the preparation of Ba-Al alloys have been published, a few of which1-4 are cited here. Most of these methods were found to be quite elaborate, involving the reduction of BaO, and not too well adapted for the close control of the final composition of small amounts of alloys prepared for laboratory use. A simple laboratory method for the preparation of Ba-A1 alloys in small batches starting from pure metals was devised, so that it was possible to control the desired compositions to within 1 pct. The pertinent features of the alloy system Ba-Al5 are 1) an intermediate compound BaAl, with the melting point of 1050°C, and 2) a eutectic between aluminum and BaAl4 at 98 pct Al. The accompanying sketch shows the experimental arrangement for the preparation of the alloys. Weighed amounts of aluminum and barium were placed in an alumina and a stainless steel crucible, respectively. According to the supplier's specification, the purity of the metals used in the alloys is as follows: a) aluminum rods—99.9 pct Al, and b) barium rods—99.5 pct Ba. The stainless steel crucible, tapered at the bottom and having a 1/16 in. diam hole, rested on top of the alumina crucible. The assembly was placed inside a graphite sleeve which rested on a refractory platform. The platform moved the assembly up and down through the field of a radio frequency coil. A glass bell jar was placed between the crucible assembly and the radio frequency coil to maintain a steady flow of helium around the melt. A small window was cut out on the wall of the alumina crucible to observe the progress of the re- action and to record the temperature with an optical pyrometer. The platform was first raised high enough to move the barium out of the radio frequency coil field in order to allow only the aluminum to melt. The assembly was then lowered so that the barium began to melt and flow out through the small orifice into the molten aluminum. In order to keep the violence of the exothermic reaction under control, the rate of flow of barium was carefully regulated by raising or lowering the crucible assembly. All the samples prepared by this technique were examined by a Norelco X-ray diffractometer using CuKa radiation, The diffraction specimens were prepared by placing the finely powdered samples in flat specimen holders. The Ba-Al alloys prepared with a high barium content were found to consist mainly of BaAl4. The structure of BaAl4 has previously been reported by Alberti and Andress.8 They found that BaAl4 was body-centered-tetragonal with an a0 = b0 = 4.530Å and c0 = 11.14Å. An alloy whose composition was found by chemical analysis to be almost 100 pct BaA1, was used to determine the relative intensities. The d-spacings were obtained from the same alloy to which a small amount of tungsten had been added as a calibrating material. Accurate values for a, and c, were calculated according to the method proposed by Taylor and Floyd.' The calculated values are: a, = b, = 4.566Å and c0 = 11.250Å. The measured d-values for BaAl4 are shown in Table I along with relative peak intensities above background and hkl indices. Acknowledgment The authors are grateful to L. J. Cronin, the head of the Techniques Dept., for suggesting the problem and for his constant interest. References 1Froges and Camargue: German Patent No. 809107, 1951. French Patent No. 935324, 1949. 2E. Bonnier: Annales de physique, 1953, vol. 8, pp. 259-312. 3M. Orman and E. Zemhela: Prac Institute of Metals; 1952, vol. 4, pp. 437-445. 4E. Fujita and H. Yokomizo: Reports Gov. Chemical Industrial Research Institute, Tokyo, 1952, vol. 47, pp. 291-297. 5E. Alberti: Ztsch. fur Metallkunde, 1934, vol. 26, p. 6. 6E Alberti and K. R. Andress: Ztsch. fur Metallkunde, 1935, vol. 27, p. 126. 7 A. Tnslor and R. W. Floyd: Acta Crystallographica, 1950, vol. 3, p. 285.

Jan 1, 1958

By R. E. Hudrlik, G. W. Preckshot

The diffusion coefficients of silver from solid silver in molten lead were measured to within ± 0.8 pet in a columnar type diffusion cell ower, the temperature range of 326° to 530°C. Fick's law describes the process up to 530°C where the laminar mechanism appareltly breaks down. These is negligible resistance at the interface as shown by mathematical analyses. The diffusion coefficients are found concentration independent. IT would seem that diffusion in liquid metals would be free of such effects as molecular structure, dissociation. polarization. and compound formation. This view was taken by Gorman and preckshot in their study of diffusion of copper from solid copper into molten lead. They reported diffusion coefficients which were independent of the concentration over the range of 478° to 750°C. They found that the Stokes-Einstein equation with constant radius of the diffusing specie represented the diffusion data better than Eyring's rate theory equation and Sheibel's correlation. The radius of diffusion was found to be that of the doubly charged copper. There appeared to be no resistance across the solid-liquid boundary. In the present work the diffusion coefficients for silver in liquid lead were measured over a range of temperatures of 350° to 505°C. The solubility of silver in lead over the range of 303° to 630°C was also obtained. These results are compared with calculated or correlated values or with data in the literature. EXPERIMENTAL Procedure—The experimental equipment techniques and procedures were those reported in detail by Gorman and preckshot9 and will not be repeated here. Measured values of WT, Co, A. L were obtained for various diffusion times and the diffusion coefficient was computed for the case of no resistance at the interface9, 11 by: WT/CoAL = 1- 8/p2 n=1 1/(2n - 1)2 exp[-(2n - 1)2p2 Dt/4L2] [1] or where there was resistance at the interface by: WT = 1- ?n=1 2h2/ap2L [sxp [-Dan2t]/[(h2 + an2) L + h] The roots an are those of the transcendental equation3 tan (an L) = Iz/cun. The diffusion coefficient is that defined by Hartley and Crank.7 The total silver in the lead cylinder and equilibrium slug was determined by a cupellation technique' with proper correction for losses. Analysis of known samples showed that this method is surprisingly accurate. The amount of silver in the lead adhering to the silver cylinder was obtained in the same fashion as shown by Gorman and preckshot.9 The small errors involved in this determination are not critical since the silver in this adhering lead layer is only 3 to 15 pet of the total diffused. Materials—Electrolytic silver containing 99.9+ pet Ag obtained from General Refineries of Minneapolis, Minn. was used for all but runs 7 and 8. For the balance of the runs this silver was reduced with hydrogen at 1100°C and its oxygen content was found to be about 0.017 pet. For the runs. 7 and 8, phosphorous-reduced silver of the same purity was obtained from Handy and Harman Co. of Chicago, Ill. The densities of the phosphorus-reduced silver and the hydrogen-reduced electrolytic silver were 10.484 and 10.487 g per cm3, respectively. These values agree with those reported for pure silver. Silver which was reduced at 900 C had an average density of 9.998 g per cm3, indicating porosity. This silver was used for a number of runs which were not tabulated in Table I. These are indicated by crosses on Fig. 2. The 99.999 pet Pb was obtained from the National Lead Co. Research Laboratory of Brooklyn, New York. DISCUSSION OF RESULTS The diffusion and solubility results are reported in Table I for eleven runs using either phosphorus-reduced electrolytic silver or hydrogen-reduced silver at 1100° C. The solubility data shown in Fig. 1 show the excellent agreement with that reported by Heycock and Neville.8 The data of Friedrichs5 apparently are in error. The experimental solubility data of this work are reported to 0.3 pet. The experimental diffusion coefficients computed from Eq. [1] are reported within 1.2 pet of the mean and are plotted in Fig. 2. These are expressed within +0.8 pet of the experimental values over the entire temperature range by: D= 8.26 x 10 -5 e-1925/RT . [3] There appears to be little difference due to the

Jan 1, 1961

By D. J. Mack, R. E. Reiswig

Six examples of the peritectoid transformation were selected from the literature and studied by the method of isothermal transformation. The kinetics and mechanisms of five of the examples are presented as TTT diagrams and photomicrographs. The exist-enc- of a peritectoid in the sixth case is doubtful. ALTHOUGH the peritectoid transformation per se has been known for many years, no precise published data exist concerning the kinetics or mechanisms involved in transformations of this type, except for the brief treatment by Rhines, et al. 1,10 Bearing in mind the fact that investigations of recent years are uncovering more and more peritectoids and suspected peritectoids, a thorough study of the well-established peritectoids appeared to be in order. It was for this reason that a study of the kinetics and morphological mechanisms of six binary peritectoids was undertaken. The six peritectoids selected from the literature for study were those reported at 7.02 wt pct Al-Ag, 26.0 wt pct Sb-Cu, 30.5 wt pct Sb-Cu, 32.3 wt pct Sn-Cu, 8.35 wt pct Si-Cu, and 21.2 wt pct Al-Cu. These selections were based on availability and purity of components, ease of preparation and heat-treatment, and estimated reliability of the available equilibrium diagrams in the regions of interest. EXPERIMENTAL PROCEDURE The alloys used in this investigation were induction melted in electrode-grade graphite and chill-cast in cast-iron split molds. In all cases, the alloys were so brittle that they could easily be broken into samples weighing 1 or 2 g. Chemical analyses showed that the alloys used were close to the respective peritectoid compositions reported in the literature and that the impurity levels were low in all cases. Metallographic examination showed uniform distributions of phases in all samples, indicating uniformity of composition in the samples studied. Isothermal transformation studies were carried out in fused-salt media, using the familiar inter-rupted-quench method. Uniformity of temperature in the salt baths was maintained by continuous stirring with a stainless-steel agitator. On the basis of actual observations of the temperature fluctuations, the estimated temperature control was + 10C for the Ag-Al and Cu-Sb alloys and ±30C for the Cu-Sn, Cu-Si, and Cu-Al alloys. The accuracy of all temperature measurements was estimated to be ±1°C. It was found necessary to mount metallographic specimens of the Ag-Al alloy in cold-curing methyl methacrylate, since the temperatures encountered in mounting in bakelite or lucite caused an appreciable degree of transformation to the ß phase. For the other alloys, wood-flour-filled bakelite mounts were used to avoid extraneous X-ray diffraction lines during the later examination of the metallographic specimens on a Norelco Geiger-counter d if f r ac tomete r. In the X-ray diffraction procedure, agreement between the published diffraction patterns and those obtained in this study was good. This was particularly important for phase identification, since the literature contained little in the way of micrograph description in some cases. Etching of the silver-aluminum alloy for metallographic examination was done by swabbing with either of the following reagents: 1) 10 g CrO3, 1 g (NH4), SO2, 0.5 g NH4NO3, 100 ml H2O, or 2) 10 ml NH4OH, 1 ml 20 pct KOH, 4 ml 3 pct H2O2, 5 ml H2O. The other alloys were etched with the usual bichromate etchant: 2 g K2Cr2O7, 1.5 g NaC1, 8 ml conc. H2SO4, 100 ml H20 (swabbed vigorously). EXPERIMENTAL RESULTS A) The Ag-Al peritectoid at 7.02 wt pct Al— The phase equilibrium involved in this peritectoid is shown in Fig. I.2 The phase boundaries in the vicinity of the peritectoid were most comprehensively established by Hume-Rothery, et al,3 who placed the equilibrium temperature at 448 °C and the equilibrium compositions of the a ß' and y phases at 6.11, 7.02, and 7.24 wt pct Al, respective The alloy used in this study analyzed4 6.95 wt pct A making it slightly hypoperitectoid according to the accepted equilibrium diagram. The rate of the transformation a+ y — ß' varies rapidly with degree of undercooling below the equilibrium temperature, passing through a maximum in the vicinity of 350°C. Thus the TTT dia-

Jan 1, 1960

By Norman Pilling

The effects of lead and tin up to maximum contents of about 0.1 per cent. each, in the presence of oxygen between 0.04 and 0.30 per cent., have been studied. Tin is retained efficiently in the oxidized condition, whereas lead is not. An approximate relation between the lead-oxygen and tin-oxygen contents is deduced which, if observed, permits the presence of these elements without detrimental effect. Excess of lead beyond this limit affects ductility and rolling properties adversely and an excess of tin correspondingly diminishes the conductivity. It is shown that copper carrying a combined lead and tin content of several hundredths per cent., yet fully equal in quality to electrolytic wirebar, may be produced under commercial conditions. TIN is not normally found in more than bare traces in current grades of American electrolytic copper, and lead is rarely found to more than a few thousandths per cent. In the electrolytic refining of copper these metals do not present great difficulty in separation and their presence in any considerable amount in copper that has been refined by this method need not be tolerated. On the other hand, the effect of these elements is not entirely academic, as a considerable tonnage of scrap copper liberally contaminated with them has been reclaimed by the fire-refining process into metal with a residual lead and tin content of several hundredths per cent., yet having excellent working properties and fully equal in quality to current grades of electrolytic wirebar. Such copper has been found entirely suitable for use in the manufacture of electrical apparatus. In the absence of oxygen, tin is known to depress the conductivity rapidly, and lead to impair ductility and the rolling properties, yet the effects of these metals on commercial grades of copper-i. e., copper containing from 0.03 to 0.10 per cent. of oxygen-apparently has not received systematic attention. Occasional reference is made to the fact that in the presence of oxygen lead may be tolerated, yet Addicks says,1 in regard to overpoling: "The unstable condition can be controlled by adding certain substances, notably lead, in small quantities, but as mere

Jan 2, 1926

By M. A. Childers

Recent work with controlled laboratory tests.' field experience and a new analytical approach indicate that casing centralization, pipe movement and relative rheological properties between the mud and cement (yield point and density) are the three controlling factors in successfu1 primary cementing of dual casing. Turbulent flow has been demonstrated to be unnecessary under the severe displace ment conditions of parallel dual strings of casing. Simultaneous reciprocation of dual casing in directionally drilled boreholes is highly dependent on centralization and on the rapid initiation of pipe movement once the casing has been run to total depth. Successful cementing of 30 out of 32 dual, 3%-in casing wells substantiated these conclusions. A review of 15 dual, 3 1/2-in. casing wells completed prior to the adoption of these principles disclosed only one success. Mathematical and graphical techniques permit the engineer to analyze and anticipate the success or failure of a cementing operation. Standoff, mud displacement and reciprocation can be analyzed mathematically and planned in deep, directional or straight boreholes by review of annular geometry, relative rheological properties between the mud and cement, and forces caused by caring weight, functional drag and differential sticking. Introduction The objective in primary cementing is to displace the drilling fluid with cement that will bond to the formation and casing to prevent communication through the annulus. The predominant cause of failure appears to be channels of gelled mud that remain in the annulus after cementing.1 '* Past investigations have noted many procedures that could improve the displacement process.2-' These procedures include centralization, chemical preflushes, mechanical mud cake removers, controlled flow rates in certain regimes, pipe movement an1 control of mud and cement properties. Not until recently have the effects of many of these procedures been isolated so that their individual importance could be determined. In a recent paper,' a comprehensive and analytical laboratory study of various factors controlling the displacement process concluded that there are three major factors in obtaining complete mud displacement by the cement slurry. 1. Good relative rheological properties between the mud and cement. The cement should be heavier and have a yield point and plastic viscosity higher than the mud being displaced. Buoyancy forces often can dominate the displacement process. 2. High degree of standoff or centralization. The more centered the casing, the greater the likelihood of complete mud displacement and removal. 3. Pipe movement obtained by rotation or reciprocation. Often unfavorable rheological properties between the mud and cement, and poor standoff can be compensated by pipe movement. This work demonstrates the compatibility of the latter concepts with field results extended to the more severe dual casing displacement process. Early Experience With Dual 3'/t-In. Primary Cementing Early slim casing completions in the West Delta Block 73 field, offshore Louisiana, included 17 dual 3%-in., 3 single 3% -in. and 1 dual 2% -in. casing installations. Table I provides data on these earlier wells. Usually, common Class A cement was placed across the pay zone and 12 percent gel cement was placed to a height of 500 ft above the highest productive sand. Centralizers (6%-in. OD maximum expansion) were placed two or three per joint on both casing strings from total depth through the completion intervals and at least one per joint for the remainder of the cement sheath. A number of techniques and procedures were attempted to improve cementing success. Casing was run simultaneously or separately with a number of mud conditioning and circulating techniques. Mechanical aids such as cement bonders, slmiding sleeves, turbulizers and various sizes and strengths of centralizers were used. Common and gel cements were mixed with fresh or sea water with a number of different additives to control retardation and dispersion. Cements were thinned and mixed at high rates to try to induce turbulent flow in the annulus. On one well the "slow flow" method was used." Perforating was accomplished with a jet orienting gun. Unsuccessful cement jobs were indicated by production of extraneous fluids or by pressure communication between zones. On test, five wells flowed water, four flowed sand and six had pressure communication with the other string or the 10%-in. casing. A total of 25 remedial squeeze ce-

Jan 1, 1969

By R. H. Harrington

THE definition of precipitation-hardening is well understood and its principles have been subjected to study for some time. However, the variation of properties with double aging, combined with strain-hardening, gives promise of new and useful phenomena. Properly to understand these distinctions, definitions of these terms are necessary. Precipitation-hardening. This reaction usually depends upon an alloy having such a composition that it consists only, or in major part, of but one phase, a solid solution, at a high temperature, so that, upon slow cooling, this solution breaks down into two phases, the solid solution and a compound. By heating the alloy to the temperature for maximum solution of the compound, quenching, and reheating to a suitable lower temperature for critical dispersion precipitation of the compound, useful properties of the alloy may be developed to a maximum. Double Aging.-Dougle aging in part is similar to the process for precipitation-hardening, consisting of heating a precipitation-hardening alloy to the solution temperature, quenching, reheating to the suitable dispersion precipitation temperature, strain-hardening, and again reheat-ing to a suitable temperature to develop certain useful properties to a maximum. The strain-hardening may be induced by two methods: (1) a rate of cooling from the first reheat may suffice to strain the solid solution lattice of the alloy; or (2) the alloy may be cold-worked to a suitable degree between the two reheats.

Jan 1, 1936

By Robert Mehl

IN examining the progress of metallurgical science, the critic must remember that most of our present knowledge of metals and alloys has been accumulated through the needs of industry and commerce rather than through the desire and efforts of a large body of scientists interested primarily in developing a science of metals. The progress of metallurgy, scientifically speaking, has been irregular, and little given to the exhaus-tive exploitation of important scientific fields. The experienced engineer now recognizes the need for the development of the basic science upon which his engineering rests. In addition to the increase in knowledge which results from the normal requirements of industry, a development of the basic science of the behavior of metals and alloys is as desirable in metallurgy as in any other branch of science and engineering. The continued growth of the science of metals-as of every other science-requires studious attention to the principles that underlie the behavior of matter, with the result that knowledge in the several fields of interest should continue to increase. Among the various subjects recognized as important in physical metallurgy few have a wider significance than that of diffusion in solid metals. The phenomena of diffusion are intimately related to many basic problems of the metallic state, but in addition to this, the process of diffu-sion is of first importance practically. The formation of alloys by the annealing of mixed powders, first practiced by Faraday and Stodart81 in 1820 and in more recent years investigated by Masing187,189 and others, has led to the development of special alloys like Carboloy, Vascoloy-Ramet, Genelite, Elcon68, and has recently been applied to the production of noble-metal alloys for electrical contacts"'.

Jan 1, 1936

By Ernest F. Burchard

A Reconnaissance of the manganese- and chrome-ore deposits of Cuba was made by the writer, as a representative of the U. S. Geological Survey, in company with Mr. Albert Burch of the Bureau of Mines, under instructions of the Secretary of the Interior, in the spring of 1918. The Cuban Government courteously detailed Sr. E. I. Montoulieu, a mining engineer connected with the Treasury Department, to act as escort and associate throughout the work on the island. The object of the study was to obtain authentic information for use of the United States Government as to the location, character, quantity, and availability of the manganese- and chrome-ore deposits in Cuba. Accordingly, the work comprised examination of such deposits as seemed to be of promise, without regard to stage of development, with a view to a determination of the quantity and quality of ore likely to become available for shipment during 1918 and 1919, and of the tonnage of ore in reserve. Wile it was possible to visit most of the deposits that seemed to be of promise, there was not sufficient time to visit all that were brought to our attention, some of which may have merit. Moreover, the necessity for paying particular attention to the ore deposits and the mines precluded the possibility of making more general studies of the geology of the region, and of making satisfactory collections of country rock and of fossils, and so for other details as to the geography and geology of Cuba the reader is referred to the report by Hayes, Vaughan, and Spencer.l Mr. Burch returned to the United States about 10 days in advance of the writer, who continued, in company with Sr. Montoulieu, investigations of reported deposits in Pinar del Rio, Matanzas, and Santa Clara Provinces. On his arrival in Washington, Mr. Burch submitted to the Director of the Bureau of Mines a summary of the results of the work to date. Later the writer published, as Press Bulietin 190. 380 of the U. S. Geological Survey, a statement concerning the chrome and man-

Jan 1, 1920

By Herbert Clark Hoover, Lou Henry Hoover

PREVIOUSLY I have dealt with the methods of separating silver from copper. There now remains the portion which treats of solidified juices ; and whereas they might be considered as alien to things metallic, nevertheless, the reasons why they should not be separated from it I have explained in the second book. Solidified juices are either prepared from waters in which nature or art has infused them, or they are produced from the liquid juices themselves, or from stony minerals. Sagacious people, at first observing the waters of some lakes to be naturally full of juices which thickened on being dried up by the heat of the sun and thus became solidified juices, drew such waters into other places, or diverted them into low-lying places adjoining hills, so that the heat of the sun should likewise cause them to condense. Subsequently, because they observed that in this wise the solidified juices could be made only in summer, and then not in all countries, but only in hot and temperate regions in which it seldom rains in summer, they boiled them in vessels over a fire until they began to thicken. In this manner, at all times of the year, in all regions, even the coldest, solidified juices could be obtained from solutions of such juices, whether made by nature or by art. Afterward, when they saw juices drip from some roasted stones, they cooked these in pots in order to obtain solidified juices in this wise also. It is worth the trouble to learn the pro- portions and the methods by which these are made. I will therefore began with salt, which is made from water either salty by nature, or by the labour of man, or else from a solution of salt, or from lye, likewise salty. Water which is salty by nature, is condensed and converted into salt in salt-pits by the heat of the sun, or else by the heat of a fire in pans or pts or trenches. That which is made salty by art, is also condensed by fire and changed into salt. There should be as many salt-pits dug as the circumstance of the place permits, but there should not be more made than can be used, although we ought to make as much salt as we can sell. The depth of salt-pits should be moderate, and the bottom should be level, so that all the water is evaporated from the salt by the heat of the sun. The salt-pits should first be encrusted with salt, so that they may not suck up the water. The method of pouring or leading sea-water into salt-pits is very old, and is still in use in many places. The method is not less old, but less common, to pour well-water into salt-pits, as was done in Babylon, for which Pliny is the authority, and in Cappadocia, where they used not only well-water, but also spring-water. In all hot countries salt-water and lake-water are conducted, poured or carried into salt-pits, and, being dried by the heat of the sun, are converted into

Jan 1, 1950