By David B. George

Kennecott Utah Copper adopted Outokumpu Flash Smelting and Kennecott-Outokumpu Flash Converting in 1995, a process based on granulating high grade copper matte. While nickel mattes and very small quantities of copper matte had been commercially granulated for years, no large scale copper matte granulation system had been built. This paper summarizes the history and benefits of copper matte granulation, the Kennecott design basis, the successful operation for over 10 years and potential problems inherent in some matte granulation approaches.

Jan 1, 2006

By Jilai Xue

Fe-Ni alloys can be used as raw material in making stainless steel. Laterite nickel ore is one of mineral resources for producing nickel alloys. In this work, the laterite ore after dehydration at 800 °C and the anthracite as reducing agent were mixed for pre-reduction at 900 °C, and then reduced to form Fe-Ni alloys at 1550-1620 °C through carbon-thermal reduction process. A high Ni-content alloy component in the metallurgical mixture can be formed through pre-reduction. Better separation of the resulting metals from the slag is found with lower Ni-content alloys produced or higher temperatures during reduction. An effective processing of Fe-Ni alloys needs further understanding of the process fundamentals and optimizing of the process parameters.

Jan 1, 2010

By Huang Kai

By adding the solid oxalate acid powder into the solution of nickel chloride or its ammonia coordinated solution, the uniform compound particles were prepared and the precipitated particles were transferred to the mono-dispersed NiO particles by calcination. In this study, the various experimental conditions were investigated, the characteristics of the corresponding obtained particles were analyzed, and the formation mechanism of the particles was elucidated. It was found that the solid oxalate acid provided the solid-solution interface for the precipitation and induced the nucleation and growth of the product particles.

Jan 1, 2005

By Jeremy Gregory

The disposal of end-of-life electronics is an issue receiving increasing scrutiny. This paper evaluates several alternatives for recycling cathode ray tubes (CRTs) within monitors and televisions. The primary recycling options for the glass, reuse in new CRTs or as a smelter flux, are examined from economic and environmental standpoints. The economics are modeled using a cost model that includes dependencies on processing costs, transportation logistics, and incoming material composition. The environmental consequences are modeled using life cycle assessment methodologies to determine the energy embodied in each processing alternative. Results map out preferred processing alternatives across a range of technological and operational conditions. The results indicate that economic costs and environmental consequences are heavily impacted by transportation. The preferred destination of CRT glass for a recycler is highly dependent on the proximity of the consumer to the recycler, although it is generally economically advantageous for the recycler to extensively dismantle the CRTs.

Jan 1, 2006

By A. R. Kiani-Rashid

Controlled graphitization has become known as a practical method for improvement of wear resistance and machining properties in steels. In this paper, the effect of heat treatment on microstructure of CK45 steel has been investigated. Austenitising was carried out at 920°C for 5 hours. Besides, isothermal transformation was conducted at 750°C in the time range of 1-20 hours. The microstructure of the steel considerably changes by this heat treatment process which exhibits the effects of temperature, appropriate austenitising duration and isothermal transformation. Conducted experiments show a suitable distribution of semi-spherical graphite particles especially on the surface of the steel. Also, analyses demonstrate that the amount of formed graphite in the austenitising temperature 920°C is more than graphite in single heat treatment temperature of 750°C.

Jan 1, 2010

By S. N. Lekakh

Phosphorous segregated at grain boundaries during solidification and heat treatment dramatically decreases low temperature toughness of precipitation hardened Fe-Mn-Al-C austenitic steel. A thermodynamic analysis was performed to evaluate the possibility of decreasing P and subsequent segregation by Ca- and Ce-additives in the melt. It was shown that the predicted probability of forming a P containing compounds depends on melt composition and treatment sequence. Experimental heats were performed and several micro- and macro-structural effects of Ca- and Ce-additives were recognized by using an automated inclusion analysis technique.

Jan 1, 2010

By Liang Sha

In this study, adsorption of copper by chemically modified orange peel was investigated. A conspicuous change occurs in the surface morphology of the biomass due to modification, which is depicted by SEM images. Equilibrium isotherms and kinetics were obtained and the effects of various factors, including solution pH, contact time, initial metal ions concentration and temperature, were studied by batch experiments. Kinetics was found to be best-fit pseudosecond- order equations. Equilibrium was better described by Langermuir isotherms rather than Freudlich isotherms. At 25?, pH5.30, the maximum adsorption capacity was 70.67mg?g-1 . With increase of temperature, adsorption efficiency decreased. The biosorbent was suitable for repeated use for more than five cycles.

Jan 1, 2009

By Z. Sun

Imposing a strong magnetic field is considered to be an attractive method to prepare materials with aligned or textured structures due to its intrinsic properties, e.g. non-contact and easily controllable. However, the nature of the strong magnetic field effect still remains unclear and further research is needed. In the present paper, the effect of a strong magnetic field on the solidification of a hypereutectic Al-Cu alloy was investigated. After magnetic field treatment, the primary phase was aligned parallel to the magnetic field direction. Meanwhile, the eutectic micro-structural constituent became elongated and thinner. A theoretical analysis was conducted to have a better understanding of the phenomena. During solidification, the magnetic Faraday and dipole-dipole interaction forces are considered to decrease the solute pile-up in front of the solid-liquid interface and modify the eutectic cell formation. The alignment of the phase is due to the shape magnetic anisotropy and crystal magnetic anisotropy.

Jan 1, 2010

By Aline Maria dos Santos Teixeira

Serpentinite is an ultra basic and metamorphic rock consisting mainly of magnesium, calcium and silicon oxides. The rock under study is a host rock of chromite mine located in Andorinha, BA. The objective of this paper is to evaluate the rock's physical and chemical characteristics to be used as an additional fertilizer of acid soils. After comminution, rock samples were submitted to chemical analysis, XRD, SEM-EDS and TGA. Afterwards, particle size distribution was determined. Result analysis confirms that our rock consists mainly of dolomite, calcite and diopside. According to the result obtained, it can be said that the serpentinite rock has promising applications in agriculture for the correction and additional fertilization of acid soils. However, it is necessary to study the characteristics of the rock such as its dangers and toxicity as well as evaluate them according to the legislation for corrective acidity.

Jan 1, 2010

By C. E. M. Meskers

End-of-life Electronic and Electrical Equipment, o_cially called WEEE, is unjustly regarded as mainly a waste management problem. What is structurally overlooked is the enormous resource impact of these devices. EEE rep- resents a tremendous metal resource, which should be uti- lized through e_ective recycling, which has a much lower environmental footprint than primary production. The actual amount of end-of-life EEE recycled today is embar- rassingly low since insu_cient EEE is collected and part of the collected EEE is exported to developing countries, where it is largely not entering o_cial recycling systems. To achieve a global recycling society issues like technol- ogy, economics, life cycle structure, stakeholder aware- ness and legislation have to be addressed in a global, co-operative manner so that sustainable closed product cycles can be obtained. Requirements for a "global re- cycling society" are de_ned to address today's reality of global ows of used consumer products, taking into ac- count the likely needs of the future.

Jan 1, 2009

By N. V. . Panishev

The Bakal (South Ural, Russia) deposit of iron ore bearing iron carbonate (siderite) with the capacity of more than 1 billion tones belongs to the MMK. This ore cannot be fully processed via blast furnace technology because of high content of MgO. According to the investigations carried out in the USA and Japan in 1999-2004 the ITmk3 (Ironmaking Technology mark three) RHF technology is a breakthrough in Ironmaking. Four iron ore types (hematite, magnetite, high and low Al2O3/SiO2) were tested. Reduction, melting and slag removal can be achieved in just 10 min. The main objective of the investigation is to establish optimum operation conditions for the production of iron nuggets from iron carbonate bearing ore via the ITmk3 by means of the lab scale testing. Samples of iron ore and carbon reductant were chemically and physically analyzed. Green pellets were processed via a lab tube furnace to simulate RHF conditions. The nuggets and slag were chemically analyzed. This preliminary test work provides valuable information which may be used for large-scale testing in a commercially sized RHF.

Jan 1, 2010

By Paul W. Cleary

Keywords: Reactive pellets, CFD, Lagrangian SPH, Pyrometallurgy In several pyrometallurgical processes, reactive pellets are added to a melt. Heat is transferred to the pellets and reaction products such as gases, metal and slag are formed. For many pyrometallurgical processes traditional grid based CFD methods, such as using the Finite Element Method (FEM) and Finite Volume (or Control Volume methods), produce suitable predictions. However, the inclusion of solids in the bath represents significant challenges for these methods. Smoothed Particle Hydrodynamics (SPH), a Lagrangian simulation method, is able to simulate both the fluid component of the bath and any immersed solid materials, tracking the motion of these solids, and their interaction with the fluid, including gas generation. In this paper, we will summarize the key aspects of the SPH method and will show a series of structured examples illustrating the behavior of the different physics sub-systems that are used in the model of the overall system.

Jan 1, 2005

By Georges J. Kipouros

Anhydrous neodymium trichlorids (NdCl3), containing ~1 weight percent neodymium oxychloride (NdOCI) was prepared by the dehydration of neodymium trichioride hexahydrate (NdC13.6H2O). Dehydration of the hexahydrate was conducted in three steps. First, the hexahydrate was slowly heated in air to about 250 °C until all the low temperature water of crystallization was removed. In the second stop, the neodymium hydroxychloride (Nd(OH)2C1) fanned in the first step was decomposed by heating under argon to 430 ° C. Finally the salt was ground and then treated with HCl gas at 330 °C until practically all of the NdOCl was converted to NdCl3.

Jan 1, 1992

By M. Bilal Khan

Thermal stress relief by means of a typical heat treatment cycle (660oC for one hr) is compared with the one achieved through vibratory stress relief at resonant and multiple resonant frequencies for the D-406 HSLA material. Our analysis of the data is based on the microhardness profiles measured for the entire length of scales, namely, base metal, heat affected zone (HAZ) and the weld bead itself. The profiles obtained using the two techniques mimic each other, for an equivalent 70% stress relief level. The data are further qualified by impact testing wherein the zone of interest is projected in the retention groove to provide impact by the pendulum striker in the Charpy mode. Higher equivalent energy absorption in the treated specimens confirms the efficacy of the vibratory method. The present work rectifies earlier anomaly where heat treatment has been reported at 310oC for the same material.

Jan 1, 2009

By Youliang He

Twin-roll casting is an integrated casting and rolling process that involves the continuous solidification of a melt and the plastic deformation of the solidified metal between two rotating rolls. Computer modeling is a valuable tool to help engineers understand the metallurgical process during twin-roll casting. However, commercially available software can only model either the fluid flow/heat transfer of the melt or the plastic deformation of the solid, but not both. In this study, an object-oriented finite element program was developed to simulate the steady-state fluid flow, solidification and plastic deformation of an A7,31 magnesium alloy in a horizontal twin-roll caster. The melt, the mush zone and the solid were treated as a generalized Newtonian flow in an Eulerian reference frame and different constitutive equations were employed to describe the material behaviours. The effect of operational parameters on the solidification process was discussed based on the simulation results.

Jan 1, 2010

By Meghan McGrath

Third generation advance high strength steels with microstructures of acicular ferrite and retained austenite were investigated and meet mechanical property goals. A good combination of strength and ductility were achieved with duplex ferrite and austenite microstructures where cementite formation was suppressed. Transformation induced plasticity (TRIP) behavior produced rapid work hardening. The mechanical properties of two hot-rolled steels with duplex microstructures were compared and had the following compositions: (1) Fe-0.14C-13.87Mn-1.42Si-3.51Al; and (2) Fe-0.06C-14.2Mn-1.85Si-2.38Al. These steels were cast, homogenized, and hot rolled at 900ºC to obtain a refined microstructure with ultimate tensile strengths and elongations to failure of 865 MPa and 39% and 1,217 MPa and 28%, respectively. The amount of metastable austenite in both compositions decreased after tensile testing from 58% and 28% to 6% and 0%, respectively. Microstructures were characterized using optical microscopy, scanning electron microscopy (SEM), and x-ray diffraction.

Jan 1, 2010

By David Norval

Water solidification of mattes, metals, alloys and certain slags with high metal entrainment has customarily not been practiced due to the belief that such processes are too dangerous and unproven in the Pyrometallurgical Industry. Slag granulation on the other hand is extensively applied, although in some cases crudely, with disastrous effects, as a result of not recognising the high heat capacities prevalent in slags. This paper will examine the most common air solidification processes and compare such processes with water solidification, mainly slag and matte granulation processes and design criteria for safe and reliable operation. Finally, purpose designed granulation and solidification processes will be discussed taking into account specific applications and the individual signatures of alloys and slags, emphasising that no slag, matte or alloy responds in similar fashion to a granulation practice.

Jan 1, 2006

By I. Nikolic

Twin-roll casting is an integrated casting and rolling process that involves the continuous solidification of a melt and the plastic deformation of the solidified metal between two rotating rolls. Computer modeling is a valuable tool to help engineers understand the metallurgical process during twin-roll casting. However, commercially available software can only model either the fluid flow/heat transfer of the melt or the plastic deformation of the solid, but not both. In this study, an object-oriented finite element program was developed to simulate the steady-state fluid flow, solidification and plastic deformation of an A7,31 magnesium alloy in a horizontal twin-roll caster. The melt, the mush zone and the solid were treated as a generalized Newtonian flow in an Eulerian reference frame and different constitutive equations were employed to describe the material behaviours. The effect of operational parameters on the solidification process was discussed based on the simulation results.

Jan 1, 2010

By Nobuaki Sato

For the recovery of uranium from spent nuclear fuel, sulfide reprocessing process, which consists of voloxidation, selective sulfurization, and magnetic separation or selective dissolution steps, are proposed. In this paper selective sulfurization of rare-earth oxides in the presence of uranium oxides was studied by thermogravimetry and X-ray diffractometry. In case of the mixture with UO2, the rare earth oxides R2O3 (R=Nd, Eu, etc.) were preferentially sulfurized by CS2 formingoxysulfides and sulfides, while UO2 remained at temperatures lower than 500 °C. When R2O3was mixed with U3O8, first, the reduction of U3O8 to UO2 occurred at low temperatures followed by the sulfurization of R2O3. The separation of rare earth elements from UO2 in suspensionsolution by the use of permanent magnet was examined. The advantage of the proposed process was also discussed by compared with current process.

Jan 1, 2006

By Xuan Li

Aluminum slag is generated when aluminum metals are recycled through a smelting process in the presence of salt. There are small amounts of aluminum metals trapped in the aluminum slag. This research aims at evaluating the use of aluminum slag as an expansion agent for the production of lightweight concrete by taking advantage of the residual aluminum metals in the slag. The research identified key elements of producing lightweight concrete products through utilizing various mixture components including sodium hydroxide (NaOH), lime (CaO), cement, and gypsum. The volumetric expansion rate was investigated and the density and strength of the products were determined. The results show that aluminum slag can be utilized for the production of lightweight concrete products.

Jan 1, 2010