By A. J. Giroux

"The use of Ishikawa cause and effect diagrams in an analysis of requirements for improving safety and productivity at Falconbridge's Strathcona Mill is presented. The analysis lead to numerous small improvements being made with the cumulative effect being a significant improvement in both areas.INTRODUCTIONMill management in the 90's involves the major requirements to improve both safety and productivity in the workplace. These objectives, once seen as unrelated or even mutually exclusive, are now accepted as being complementary. Managers, trained either on the job (coming up through the ranks) or in an engineering discipline followed by first and second line supervisory experience are now turning to methods developed in consumer product manufacturing to ensure that all the components are in place to ensure the ore processing facilities are safe and efficient.This paper shows how management at Falconbridge' s Strathcona Mill used the Ishikawa ""fishbone"" diagram ( 1) , a method further developed by Deming(2), to put into place a comprehensive safety and productivity process. The Ishikawa/Deming concept is that no one element or program will itself continually improve a process or service. It is only by examining and then improving all the elements that are involved in the process or service that continuous improvement is obtained. The process was built on the Deming principle of worker ownership where management is the facilitator for putting into place the mechanisms whereby workers can themselves improve the operation. The process is illustrated mainly by examples of the changes made in the hope that these may be of direct help to other operations."

Jan 1, 1993

By S. Gregory

Many gold treatment plants have sulphides and coarse particle gangue components that contain gold in their tailings (cyanide leach residues and flotation tailings). Coarse and very fine liberated gold may also be present in some tailings streams. Two issues usually govern the economics of recovering additional gold from gold occluded in sulphide and gangue particles. The liberation characteristics of the gold in the sulphide and coarse gangue (gold liberation versus grind size) is the first and most important of the two. If fine grinding can liberate a reasonable amount of the gold, then the next important issue is how effectively these two constituents can be concentrated. Flotation will achieve high sulphide recovery but is usually costly. Selectivity is also an issue because of entrainment. Continuous centrifugal gravity concentration offers a viable solution to the recovery of both sulphides and coarse gangue however selectivity is also likely to be a problem. The possibility of improving concentrate grade by using a Falcon B separator was investigated. This paper describes a program of test work carried out on a gold leach tailings using a laboratory Falcon '13' separator. The program involved three different bowl angles: 10, 12 and 14 degrees and two bowl speeds (giving 250 and 350G accelerations). A number of tests were also performed on samples that had free gold present to ascertain the size-by-size recovery of gold in these samples.

Jan 1, 2005

By J. I. Gazzarri

A model of solid oxide fuel cell AC impedance behaviour has been developed and is used to simulate the frequency response of a single cell with and without mechanical damage. The results indicate that the presence of mechanically induced damage within the components of a solid oxide fuel cell can be detected by comparing the frequency response of the undamaged cell with that of a cell in which in-plane cracking or delamination has occurred. The presence of such defects manifests itself as a new semicircle in the Nyquist impedance diagram of the full cell. A parametric study reveals the resolution capabilities of the method in terms of the geometrical characteristics of the defects.

Jan 1, 2005

By V. A. Chanturiya, T. N. Matveeva, N. K. Gromova, T. A. Ivanova

"The research is aimed at solving the problem of increasing the extraction of gold from refractory ores, which are the main source of growth in gold production in the next decades. The purpose of the research is the development and scientific substantiation of the reagent modes for flotation extracting of gold from refractory ores using eco-friendly low-cost herbal modifiers (HM), providing increase in gold recovery and quality of gold concentrates. In the course of research laboratory techniques for the preparation of experimental samples of HM were developed, which included the sequence of operations of grinding Heraclium leaves and stems grinding, 2-stages extraction at a temperature of 50-60 °C, short-term ultrasonic treatment, filtration and subsequent unification of extracts. According to the developed method, the experimental samples of HM and conducted research were tested to analyze their sorption and flotation activity related to the extraction of gold from refractory gold ores.New data on adsorption and flotation properties of Heraclium stems and leaves extracts (HSE) in selective flotation of Au-sulfide minerals were obtained using UV-spectroscopy, scanning electronic and laser microscopy and atomic force microscopy. The dimensions and shapes of adsorbed hydrophilic films of herbal reagents were identified and mechanism of formation of stable insoluble compounds on the surface of minerals in flotation was explained.Research flotation tests carried out on samples of refractory gold ore of one of Russia deposits showed the possibility of effective use of herbal modifiers to improve qualitative and quantitative indicators of enrichment compared with the standard reagent regime. New reagent modes, using herbal modifiers in an amount of 5 to 10 ml of the extract (300 - 600 g / t, respectively) improves the quality of the concentrate: gold content attains 14.7 g / t, 1.34 times higher than in the baseline experiment and provides a gain of 3.13% extraction.The developed reagent regime with herbal modifiers is the author's original design, patented (patent of the Russian Federation) and have no analogues in the world of mineral processing. (Application number 2015116125 from 04.28.2015, ""The method of flotation separation of sulfide minerals using herbal modifier"", Russia). Actual application of new plant extracts as modifiers in flotation of sulfide minerals is the possibility of replacing of highly toxic chemical compounds by environmentally safe substances of plant origin. Implementation of the developed methods of extracting gold from refractory minerals with herbal modifiers will help to improve gold recovery at 3-5% and the quality concentrate of not less than 1.2 times, leading to higher productivity and a reduction of the negative man-made effects on the environment ."

Jan 1, 2016

By A. D. Walters

"IntroductionScreens are used in coal preparation plants for four basic functions, namely:I. Scalping off large size run-of-mine coal for initial size reduction;2. Sizing of coal treatment in different process streams;3. Removal of magnetite (dense medium) from clean coal and refuse;4. Dewatering.Canadian coal preparation plants use screens extensively in the above functions. Even plants where no beneficiation takes place, screening and crushing are carried out in the size reduction process.Description of Process UnitsThe type of screen used in coal preparation plants generally falls into the following categories:Fixed Screens and Grizzlies (for large coal)Often a simple rugged construction, either set horizontally above a bin or inclined with the coal flow.Fixed Sieves (for fine coal)They are used for dewatering and/ or size separation of slurried coal or discard. The sieve bend, the Vor-Siv, the Wilmot riffle and the cross flow screen fall into this category. The most commonly used in coal preparation plants is the sieve bend, Figure 1. Coal slurry is fed tangentially onto a fixed curve wedge wire screen deck. The solids are separated at a predetermined particle size, delivering a partially dewatered overproduct and a dilute underflow. The coal slurry is initially delivered to the sieve bend via a feed box. A series of baffles spreads the feed evenly across the width of the deck. The slurry drops from the last baffle, passes through the feed spout and is fed tangentially to the screen. It is important that the feed should contact the surface immediately at the front end of the sieve bend. It is possible to lose as much as 250Jo of screening area with a poorly fitted screen box.The full stream of coal slurry flowing over the sieve bend decreases in depth, in increments of approximately •;4 the slot width each time it passes a slot. Sieve bends make a size separation at 112 to 2h the slot width. This feature virtually eliminates blinding of the screen surface. Slot sizes are normally quoted in millimetres, available standard slot sizes are from 2 mm to 0.125 mm. The sieve bend is also widely used in coal preparation for preliminary dewatering."

Jan 1, 1989

By A. Y. Senchenko, Y. V. Kulikov

"In recent decades HPGR technology has proven itself in comminution circuits of mining plants. High technical and economic performance, lower specific energy consumption and reliability of HPGR equipment makes it an efficient alternative to conventional circuits using stage crushing and rod/ball milling, as well as to AG/SAG circuits. However, despite all the advantages of this technology the correct selection of key and auxiliary equipment is very important since errors at testing and design stages may lead to discrediting of the whole concept of HPGR application. There is a great variety of possible circuit configurations using HPGR, e.g. with circulation of edge product, with crushing of the whole discharge and circulation of screen oversize, successive two-stage crushing, etc. Each type of minerals will require its own optimal crushing circuit. In this context the testing methodology for selection of an optimal configuration becomes of prime importance. It is common knowledge that the best simulation of material crushing and softening within a HPGR can be obtained only in the course of a large-scale pilot test. The main approaches applied to this kind of testworks are described in this article. Special aspects of HPGR technology design and industrial operation are revealed as well. Some operational issues of HPGR equipment and of circuit as a whole were detected. They are related to regions specifics, plants location, and other factors. Process solutions proposed to deal with these issues are also indicated in the article. INTRODUCTIONDesign and construction of the processing plants involving High Pressure Grinding Rolls (HPGR) technology becomes more and more common in mining as this technology has specific technical and economic advantages against the circuits with autogenous/semiautogenous mills (AG/SAG) and other circuits. The main advantage of the technology is low energy consumption and low operation costs respectively. The presence of microcracks and increased content of fine size fractions in the crushed product contribute to reduction of energy required for further ball grinding. Besides, HPGR technology applies a special wear resistant liner that enables significant reduction of operation costs of grinding media and liner comparing with AG/SAG circuits."

Jan 1, 2016

By K. Scalise, M. Teixeira, K. C. Kocsis, J. Parrish

"This paper aims to introduce and discuss a newly developed algorithm, which can be uploaded on smart watches and other mobile devices to inform and protect underground personnel working in hot and humid environments. Using this algorithm, the metabolic rate (M) of a worker can be determined in “real-time”. In addition, besides warning signs and alarm signals emitted by the smart watch, the algorithm has the ability to determine work-rest time periods based on the worker’s physiological parameters (e.g. age, height, weight, gender) and the climatic parameters (Td, Tw, flow velocity). This paper also investigates whether a re-designed auxiliary ventilation system can provide appropriate work conditions in the production stopes. INTRODUCTION An underground environment with high temperature and humidity conditions generated from various heat and moisture sources can significantly affect the thermoregulation processes of the human body. This can lead to heat-related illnesses such as heat rash, heat cramps, heat exhaustion, and heat stroke. Heat stroke is a serious illness that carries a high risk of fatality, if the underground workers are not immediately treated and the climatic conditions are not corrected (McPherson, 1993). There are two methods used to control the climatic conditions in underground mines: (1) Using ventilation and cooling systems to reduce the thermal stress on the mine workers, and (2) Reducing the heat transferred to the ventilating air from major sources such as: strata, auto-compression, mining equipment, groundwater, blasting, etc. The heat from strata and auto-compression is transferred to the ventilating air at varying degrees, based on factors such as the virgin rock temperature (VRT), the thermal properties of the surrounding rock formations, and the surface air temperature. However, the use of mining equipment and blasting processes can be managed to reduce their contribution to the mines’ overall heat load. To provide appropriate work conditions, selecting the most suitable cooling method depends on the level of heat to be removed, the location of the problem areas, and economic constraints (Brake & Bates, 2002; McPherson, 1993). Because every mine is unique, it is essential to monitor the climatic conditions to select the most appropriate method of cooling. A majority of the time, simply adjusting or re-designing the auxiliary ventilation system can efficiently remove the heat and dilute the contaminants. This may involve moving the ducting system, changing the size of the duct, changing the size of the auxiliary fan, or switching from forcing to an exhausting fan arrangement. If the required air volumes are higher than the existing primary ventilation system can supply, other measures may need to be taken to increase the airflow delivery. This may include regulating the flow in some areas of the mine to increase airflow to the desired area, adding booster fans, or replacing the primary fans."

Jan 1, 2019

By K. Mayhew, K. Murray

The CESL Copper Process was developed as a hydrometallurgical alternative to smelting and refining for copper sulphide concentrates. As the majority of such concentrates contain appreciable gold and silver values, effective recovery of these metals is essential to the economics of this technology. Unfortunately, conventional cyanide processing cannot be used on the residue from the copper process, clue to its unusual characteristics when compared with naturally occurring gold and silver ores. An abundance of elemental sulphur, as well as the presence of cyanide soluble copper, leads to the formation of both thiocyanate and copper cyanide which is detrimental to process economics clue to excessive cyanide consumption. This, however, can be reduced to acceptable levels by process innovations such as pressure cyanidation and cyanide recovery. This paper outlines the successful application of the CESL Gold Process to various gold-bearing copper concentrates from bench to demonstration scale.

Jan 1, 2011

By Mengsu Hu, Yuan Wang, Jonny Rutqvist

Material interfaces and typical boundary conditions are boundaries influencing the existence, uniqueness and stability of numerical solutions of water flow in heterogeneous media. The Numerical Manifold Method (NMM) with a two-cover-meshing system is an ideal method to handle boundaries, considering its flexibility with no need to adjust mathematical nodes onto boundaries, the meshing efficiency, and its integration precision. In this study, we derive and compare two new approaches for boundary constraints, i.e., a discontinuous approach with Lagrange multiplier and a continuous approach with jump function in the frame of NMM. In the discontinuous Lagrange multiplier method (LMM), Dirichlet boundaries or the material interfaces are regarded as discontinuities which are linked by Lagrange multipliers. In the continuous Jump function method (JFM), the material interfaces are regarded as inner interfaces, where the refraction law is realized by constructing jump terms with discontinuity of hydraulic gradient in its normal direction. Both the continuous and discontinuous approaches make full use of the aforementioned advantages of NMM and are established based on a clear physical meaning of water flow by our energy-work seepage model. The newly derived boundary-constraint approaches were coded into an NMM water flow model and tested for precision and efficiency on different simulation examples. We first tested both LMM and JFM for an idealized heterogeneous model, comparing the numerical results with analytical solutions. Then we tested both approaches with a heterogeneous model and compared the results of hydraulic head and specific discharge. We proved that both approaches are very suitable for material boundaries considering the accurate realization of the boundary constraints and the flexibility with no need for mesh-conforming.

Jan 1, 2015

By D. F. Malan

"This document highlights some of the topical problems associated with the design and support of deep tabular excavations in hard rock. The displacement discontinuity boundary element method has been used for at least five decades to analyse stress and displacement distributions around narrow width excavations with complex plan outlines. The assumption is made in most cases that the rock mass surrounding the excavation is perfectly elastic. Although this approach works well to minimise stress concentrations in practice, it has limitations as important parameters, such as the effect of mining rate, cannot be investigated. Recently, a limit equilibrium model has been studied as a means to enhance standard layout design exercises by including an interactive on-reef damage model. This approach can include explicit energy release dissipation computations. A second problem faced by engineers in the mining industry is the evaluation of pillar and remnant stress. The paper highlights two aspects namely the effect of element size in displacement discontinuity modeling on pillar stress and the difficulty to estimate the effect of total closure on the regeneration of stress in old mining areas. Regarding the support of the tabular excavations, current efforts are focussed on providing improved aerial coverage using hangingwall bolting and temporary nets. An unresolved issue is the installation of permanent mesh in low stoping width areas. INTRODUCTIONSince 1886, more than 50 000 tons of gold has been mined in the Witwatersrand Basin of South Africa (Hartnady, 2009). The nearby platinum mines also saw significant growth in recent years and more than 80% of the world’s platinum group metal reserves are contained in the Bushveld Complex of South Africa (Nell, 2004). Apart from the economic aspects, the mines served as an outstanding rock engineering “laboratory” for many decades owing to the deep, tabular nature of the excavations. The period from 1960 to 1980 was especially lucrative in terms of research and world-renowned researchers investigated the support and rockburst problems (e.g. see Cook et al., 1966; Salamon, 1968; Bienawski, 1973; Wagner, 1984). Many of the rock-related problems nevertheless persist up to the present day and this paper explores some of these problems and recent progress. The production of gold declined substantially in recent years (Hartnady, 2009) and well-directed rock engineering research can play a meaningful role to slow this trend. The objective of the document is to highlight critical areas requiring additional research and not to discuss the topics in detail. The reader is referred to the many references for additional information. The paper only focuses on three areas namely numerical modelling, pillar stress estimation and aerial support. Although these are diverse topics, it is included in one paper to illustrate the many unsolved and practical problems associated with deep tabular excavations."

Jan 1, 2015

By J. W. Choung, T. Fu, Z. A. Zhou

An on-line visualization technique and methodology was developed to investigate the role of fine sphalerite (< 10 um) aggregation in flotation. The images of particle aggregates under different operating conditions were recorded and analyzed. The effect of impeller design on particle aggregation was demonstrated. This difference was not mainly due to the energy input into the system, but due to the resultant hydrodynamic conditions created by the impeller and their effect on particle interactions. The recorded image showed that adding fine silica (- 5 um) did not interfere with fine sphalerite aggregation, thereby showing no effect on the sphalerite recovery. Effect of the enlarged aggregate size on increasing flotation recovery was confirmed. Although Malvern Mastersizer produced consistently lower estimates of aggregate size than those by the image analysis, both methods responded to the changes in operating conditions in the similar trend. It was shown from this study that on-line visualization technique is a powerful tool for studying fine particle aggregation and morphology in the context of diagnosis for the flotation separation.

Jan 1, 2004

By M. Turek

Cost management in the conditions of increasing competition and unforeseen market turbulence constitutes one of the key areas of the enterprise?s activity. In the last two years the demand for hard coal on the domestic and global market of non-renewable resources has increased significantly. Polish hard coal mining industry, as an industry in the stage of decline, received a chance for rejuvenation. However, one of the most significant conditions of seizing this opportunity is the rationalization of mining costs and improvement of production effectiveness. Due to the significance of this issue, the main objective of the paper is to identify the possibilities of improving the production effectiveness in the hard coal mining industry. In order to meet such an objective, in the first part of the paper we measured effectiveness in the Polish hard coal mines in years 2006- 2011. The research encompassed three out of five mining enterprises operating in the country. Then based on the received results, guidelines concerning the improvement of effectiveness of production were created, taking into consideration infrastructural, technical, economic and organizational determinants. Furthermore, opportunities and threats for improving the production effectiveness, stemming from the external conditions have also been indicated.

Aug 1, 2013

By M. Nejati, A. Paluszny, R. W. Zimmerman

A numerical method is proposed to propagate multiple discrete fractures leading to primary fragmentation in a mine that is being worked using block caving. Deformation is computed using the finite element method, fractures are represented explicitly, and the mine domain is discretized by an unstructured mesh. Bedding planes are represented by systematically varying the elastic modulus of the rock and by defining horizontal weakness planes. Fractures and matrix are represented using parametric surfaces, and tips are defined by their boundary curves. Tip advance is controlled by a failure criterion, and a criterion for propagation direction and magnitude, based on the evaluation of the modal stress intensity factors. A novel domain integral approach is applied to accurately compute stress intensity factors (K) ahead of fracture tips in three dimensions. The method does not require a structured volumetric mesh structure around the crack tip, as integration is performed over a series of virtual surface domains along the crack front. The method is efficient, as it makes direct use of automatically generated, arbitrary tetrahedral meshes, and approximates stress intensity factors (KI, KII, KIII) along each crack front using Interaction-integrals. As opposed to the JIntegral, the method does not decompose K a-posteriori, but instead uses an auxiliary field to directly compute modal K. When using this method, numerical approximations of K do not exhibit dependence on the mesh layout, and require meshes that can generally be ten times coarser than are required by displacement- and stress-based methods. Volumetric meshing requires only, on average, 17% of each computation step. Thus, cracks do not follow any pre-existing mesh structure, and the method is well suited for high-density fracture datasets. The method is demonstrated for primary fragmentation of a mine area covering 110 initial draw points, immediately beneath a 2m high undercut. Displacement is constrained at all boundaries except the surface of the undercut. The growth of the fractures is investigated at the onset of the undercut. Ninety initial disc-shaped fractures are taken into account, each having an initial radius of 10 m. Fractures grow around the undercut, intersect the bedding plane boundaries, and the domain is fragmented as a result.

Jan 1, 2015

By W. Swidzinski

"Zelazny Most" post-flotation copper mine tailings pond is the only place to of storeing wastes for KGHM POLSKA MI EDZ S.A. The flotation tailings is are the main waste stream in copper mining in Poland. Sufficient storage capacity for tailings is crucial for , thus uninterrupted production of copper is crucially related to the possibility of storing wastes in the pond. The pond covers a Its over 14 km2 arca, almost 50 m high dams making this dame this construction one of the largest in the world. The risk assessment of potential damage due to un stable ility loss of dams or environmental contamination, as well as safely constructing damsincrease of dams within the design criteriaprocess, require quick access to a large amount of the monitoring data , which in vast amount have to be monitored, that needs to be analyzed and processed and reported, every day. This In the paper describes the numerical information system "SyZeM" , used for designated to the "Zelazny Most" pond, baseding on the Oracle database and Geographical Information System , to manage the graphical and descriptive data in coherent way., is presented. The main structure of the system, as well as the methodology of storing, processing and reporting the geological, geotechnical, hydrogeological, geophysical, chemical and survey data are shown. The aspects of Optimizing optimal and risk mitigation and safe management of copper wastes and risk mitigation with the help of "SyZeM" are discussed.

Jan 1, 2007

By Matej Petružálek, Tomáš Svitek, Tomáš Lokajícek

"Migmatite from the Skalka region (Czech Republic) was chosen as the experimental rock material. It has macroscopically visible plane parallel structure (foliation). The foliation was caused mainly by biotite grains arrangement. The cylindrical samples of migmatite with subhorizontal, subvertical and oblique foliation were uniaxially loaded up to the failure. Network of 8 broad band sensors was employed for acoustic emission monitoring and ultrasonic sounding. A grid search method with anisotropic velocity model was used for AE hypocenters localization. The source types of successfully localized events were determined from the average first arrival amplitude. Structural anisotropy of tested rock material caused the anisotropy of its mechanical properties (peak strength, Young’s modulus) as well as a different way of fracturing process in dependence on the angle between axial stress and foliation plane. The combination of splitting, shearing and sliding was found to control the fracturing of sample with subhorizontal foliation. The shearing and sliding was dominant in fracturing of samples with oblique foliation. With greater dip of foliation, the role of sliding increased at the expense of shearing. Due to the favorably oriented system of microcracks already present, the shearing and splitting was at the same level during fracturing of the sample with subvertical foliation before nucleation began.INTRODUCTIONThe process of failure of low porosity rocks depends on their mechanical properties and actual stress and temperature condition. At the low pressure and low temperature, the most common way is brittle failure, which is a progressive process requiring the initiation, growth and coalescence of cracks (Lockner, 1993). Stress strain behavior of low porosity crystalline rocks, during the laboratory compression experiments, is divided into four characteristic stages: crack closure, elastic region, stable crack growth and unstable crack growth which leads to the brittle failure, Brace et al. (1966) , Bieniawski (1967), Lajtai (1974), Cai et al. (2004), Nicksiar and Martin, 2012 and 2013.The fracturing process of stressed rock begins with the crack initiation (sci), which for low porosity rocks occurs approximately at 40-50% of peak strength (sp) (Cai et al., 2004; Nicksiar and Martin, 2013). After the sci, the dilatancy begins and stable crack growth follows up to the crack damage threshold (scd), which is approximately at 80% of sp (Cai et al., 2004). After crossing the crack damage level, there is an unstable crack growth accompanied with nucleation of fault plane (sn) at 97-100% of sp. (Rao et al., 2011). The stress drop accompanied with formation of macro scale shear failure plane follows after peak stress is crossed."

Jan 1, 2015

By Renliang Shan

Site conditions of China?s coal roadways are complex and changeable, and scientific classification of them is the fundamental basis for coal roadway support design, with great significance for ensuring proper roadway service. Upon analysis of the issues, a commentary regarding the research progress on classification of the stability of rocks surrounding coal roadways in China has been achieved from the point of view of classification methods and indexes. The shortcomings and applicable scope of rock stability classification methods related to coal roadways have been analyzed. It has been asserted that combining artificial neural networks with fuzzy mathematics, combining fuzzy mathematics with grey theory, applying new avenues such as support vector machine algorithms or unascertained average classification, and making classification indexes more scientific are future directions for development of rock stability classification for coal roadways.

Aug 1, 2013

By J. Thiriar

The electrolytic tan/chouse at CCR was recognized by management as lagging behind modem refineries in terms of productivity, energy efficiency and controls. The operation was also burdened by high maintenance costs of cells, floors and electrolyte recirculation systems. A bench marking program was started in 1986 to evaluate processes and other technology by visiting major copper refineries in North America, Europe and Japan. The basic principles necessary to optimize the operation were defined, and a program called CCR 2000 was prepared for approval of the necessary capital investments. This paper describes the results obtained to date and outlines the remaining work to complete the modernization program, in particular, the control of electrolytes, the elimination of the Baltimore groove and studies to modernize the stripping operation or adopt permanent cathode technology.

Jun 1, 1993

By J. Fellowes, V. Landais, J. Robson, J. Carr

"Aerospace Al-Zn-Mg-Cu (7xxx) alloys are known to be susceptible to environmentally assisted cracking (EAC). This phenomenon has been studied intensively for many decades, leading to empirically adopted methods to mitigate this problem through overaging and composition design. In parallel, many theories have been developed to explain EAC in 7xxx, but none is yet universally accepted. Today, a number of emerging techniques offer potential to shed new light on EAC in 7xxx. The purpose of the present paper is to demonstrate how X-ray tomography (XCT) combined with electron microscopy can be used to identify the true crack path in 3-dimensions, and hence identify material for site specific electron microscopy analysis. Composition mapping over large areas to high accuracy has been performed using a modern electron microprobe analysis system. This has been combined with transmission electron microscopy to investigate local composition in matrix and precipitates at high resolution. This combination of techniques across length scales offers the potential to provide new insights into the links between local composition, microstructure, and EAC resistance.INTRODUCTION Environmentally-assisted cracking (EAC) is a phenomenon which dramatically decreases the performance of metals and can cause premature failure of large structures. Observed in situations where components were not subjected to critical loads and no widespread corrosion was involved, this type of brittle failure is extremely difficult to predict. The EAC designation covers a number of phenomena, e.g. stress corrosion cracking (SCC), hydrogen embrittlement (HE), corrosion fatigue (CF), etc. Initially identified in steels, EAC can also affect other metals such as high-performance aerospace aluminium alloys, and this phenomenon has been a concern for industries for decades. Extensive research has been conducted on the effects of various environments (moist air, saline water, dry hydrogen gas, etc.) on microstructures and crack propagation, however no consensus has been reached and the exact nature of the mechanisms that control EAC is still being debated (Birnbaum & Sofronis, 1994; Gangloff, 2007; Holroyd & Scamans, 2013; Lynch, 2012; Oriani, 1972; Scamans, Alani & Swann, 1976, Young & Scully, 2002)."

Jan 1, 2018

"Successive seismic waves may cause progressive weakening of a fault zone, which has been recognized as the mechanism of earthquake aftershocks. However, it is unclear that how a fault zone slips under each wave cycle and how slip displacement accumulates under continuous wave cycles. This laboratory study provides direct evidences on the slip process of a simulated granular fault zone dynamically induced by an incident wave without the effects of late-arriving and reflected waves. The experimental observations show forward and backward slip paths of the fault zone and partially recovered slip displacement after a wave incidence. The unrecovered slip displacement after each wave cycle can be accumulated until it reaches a critical slip distance for seismic faulting, which may reinterpret delayed triggering in earthquake dynamics. The limited interseismic period restricts fault self-healing in strength. The experimental results also indicate that the dynamically induced frictional slip on the fault zone is associated with a complex frictional system, including seismic wave radiation, frictional slip initiation and normal stress vibration. Different from the dynamically induced frictional slip on the fault zone, the statically induced frictional slip causes a permanent increase of slip displacement along the shear loading direction. INTRODUCTIONAn earthquake mainshock may induce aftershocks by suddenly changing external stresses applied to another fault zone in the near field (Kilb et al., 2000) and by slightly perturbing a fault zone from a critical steady state to stick-slip faulting in the far field (Gomberg and Davis, 1996). The dynamically induced frictional slip on a fault zone has been recognized as the mechanism of earthquake aftershocks (Marsan and Lengliné, 2008; van der Elst and Brodsky, 2010). Although earthquake aftershocks have been extensively studied by many seismological methods, a simplified laboratory fault zone can provide possible interpretation on real faulting and detailed analysis on a friction process (Dieterich, 1979; Nielsen at al., 2010). According to a few laboratory experiments related to the dynamically induced frictional slip on a simulated fault zone (e.g., Uenishi et al., 1999; Johnson et al., 2012), the slip process induced by successive seismic waves exhibits continuous motions. However, it is unclear that fault slip response under each wave cycle and slip displacement accumulation under continuous wave cycles."

Jan 1, 2015

By C. Graham

Thin Spray-On Liners (TSLs) have been researched and in development for over two decades and yet their fully functional and widely justifiable application in mining has yet to be achieved. While the explanation for this is partly technical, it is also clear that proving and communicating the operational and economic case for why a mine should change from mesh or shotcrete liners to a TSL is not a trivial matter. Evidence must be presented and communicated effectively, that is both obvious and compelling for a mine operator. The paper describes recent work carried out and directed towards this end, with funding from CAMIRO?s Deep Mining Research Consortium and additional support from 3M Canada and ABB Canada. The essential progress that has been, or is in the process of being made, will be described in providing the necessary proof of acceptable or superior TSL performance in the following areas: polymer formulation, health and safety, geotechnical specification, robotic liner application, business case economics and yielding ground support effectiveness. Future plans are also presented to demonstrate the performance of a new 3M composite TSL/yielding bolt support system in underground trials where the substrate rock is intended to fail through a number of mining-induced mechanisms.

Aug 1, 2013