By A. G. H. Anderson, Eric R. Jette

A few years ago, while the writers worked on the constitution of ternary and quaternary alloys consisting mainly of iron, chromium and siliconl,2 some information on microstructures and hardness, not incorporated in the published work, alas obtained. It has not been possible to do any further work on the properties of the alloys. The information possessed is hereby presented for the interest it may have in connection with the constitution of the alloys. Microstructures Referring to the iron-chromium-silicon diagram,' the regions that received most attention were those in which the sigma phase appears. It was found that the mode of occurrence of this phase varied much with the condition under which it mas formed, and the mode influenced considerably the hardness of the alloys. In some slowly cooled alloys, well within the alpha + sigma-phase boundary, sigma occurs in pabterns suggesting a eutectic. The structure of such an alloy is shorn in Fig. 1, showing it to be partly coarsely laminated and partly globular mottled. In other annealed and slowly cooled alloys, the lanlinated structure is entirely absent, and sigma appears in an irregular distribution of sharply cornered elongated areas (Figs. 2 and 3). These areas all possess a more or less mottled structure. A carbide phase is also visible in these two photomicrographs; it is represented by bright white arras of various shapes, sometimes apparently enveloping the sigma. Quenched and aged specimens, whose compositions arc: located near the phase boundary between alpha and sigma + alpha regions, have structures not unlike martensite (Figs. 5 and 6). Fig. 4 shows the structurc of alloy No. 35 as quenched from 1100" C.; it is a typical solid solu-

Jan 1, 1938

By Gilbert Francklyn

The requirements of coals for the manufacture of coal gas, water gas and producer gas will be considered sparately and a short description of each gasmaking process will be given. In this report the term "gas coal" is confined to coals suitable for the manufacture of city gas in horizontal, inclined or vertical retorts. The report does not refer to coke-oven practice.' Briefly, the process of manufacture consists of distilling the coal at high temperature in an externally heated retort out of contact with the air. The products of distillation, consisting of gas, tar, ammonia, etc. are collected and purified. The residue consists of coke, which is removed from the retort at the end of the carbonizing period. To supply the heat required in the process, a portion of the coke produced is converted into producer gas, which is burned under the retort settings. Qualities of Gas Coals The chief qualities that coal must possess in order to be classified as a gas coal are as follows: 1. Gas Yield.—The coal must be capable of yielding gas in sufficient volume and of a satisfactory quality. The yield depends considerably upon the temperature of distillation; a higher temperature will give a larger yield of gas, but the qualit,y of gas (now measured by the British thermal units per cubic foot) will be lower, while a lower carbonizing temperature will give less gas of higher heating value. The true measure of the yield is the number of British thermal units produced in the gas from a given quantity of coal. This number is obtained by multiplying the cubic feet of gas from 1 lb. of coal by the British thermal units per cubic foot of gas; it is called B.t.u. feet per pound. It is found that the

Jan 1, 1930

By Eric R. Jette, A. G. H. Anderson

A few years ago, while the writers worked on the constitution of ternary and quaternary alloys consisting mainly of iron, chromium and siliconl,2 some information on microstructures and hardness, not incorporated in the published work, alas obtained. It has not been possible to do any further work on the properties of the alloys. The information possessed is hereby presented for the interest it may have in connection with the constitution of the alloys. Microstructures Referring to the iron-chromium-silicon diagram,' the regions that received most attention were those in which the sigma phase appears. It was found that the mode of occurrence of this phase varied much with the condition under which it mas formed, and the mode influenced considerably the hardness of the alloys. In some slowly cooled alloys, well within the alpha + sigma-phase boundary, sigma occurs in pabterns suggesting a eutectic. The structure of such an alloy is shorn in Fig. 1, showing it to be partly coarsely laminated and partly globular mottled. In other annealed and slowly cooled alloys, the lanlinated structure is entirely absent, and sigma appears in an irregular distribution of sharply cornered elongated areas (Figs. 2 and 3). These areas all possess a more or less mottled structure. A carbide phase is also visible in these two photomicrographs; it is represented by bright white arras of various shapes, sometimes apparently enveloping the sigma. Quenched and aged specimens, whose compositions arc: located near the phase boundary between alpha and sigma + alpha regions, have structures not unlike martensite (Figs. 5 and 6). Fig. 4 shows the structurc of alloy No. 35 as quenched from 1100" C.; it is a typical solid solu-

Jan 1, 1938

By L. S. Darken, H. A. Wriedt

The equilibria at 1 atm total pressure and 600° to 1300°C (1112° to 2372°F) between gas mixtures with various partial pressures of the reactive constituents (principally sulfur dioxide, carbon dioxide, water vapor, oxygen or carbon monoxide, and hydrogen) and coexisting solid phases (groups variously including calcium oxide, calcium carbonate, calcium sulfide, calcium sulfate, iron, ferrous sulfide, and the iron oxides) are examined. Tables and charts show the combinations of temperature, oxygen activity, and carbon dioxide partial pressure under which the various groups of the solid phases coexist and the corresponding sulfur dioxide pressures. In the presence of calcium sulfide, calcium sulfate, and calcium oxide, the partial pressure of sulfur dioxide has a peak value at each temperature which increases from 101 atm at about 800°C (1472°F) to 1 atm at about 1200°C (2192°F). With water vapor present, hydrogen sulfide may predominate among gaseous sulfur compounds, particularly at low temperatures and oxygen activities; under all other circumstances considered, sulfur dioxide is the dominant gaseous sulfur-bearing species.

Jan 1, 1974

By Henry R. Linden

The demand for natural gas continues to increase at higher than anticipated rates, partly because of its widening price advantage over most other fossil fuels when the cost of air-pollution control is included. However, there are clear indications that the natural gas supply from the conliguous 48 states and continental shelves will not keep up with this rapid growth in demand indefinitely. Projections are presented which define the extent of potential deficiencies from the 1970's to the year 2000. Among the sources of supplemental gas - imported pipeline natural gas from Canada and Mexico, tanker import of liquefied natural gas, and synthetic pipeline gas from coal and oil shale -by far the most abundant at potentially competitive costs is pipeline gas from coal. The state of development and relative economics of the various coal gasification processes are reviewed. It is shown that synthetic pipeline gas could become a very substantial market for bituminous coal and lignite at current mine-mouth prices - 60-70 million tons of coal for each trillion cubic feet of synthetic pipeline gas produced. This corresponds to only slightly more than the current annual increase in gas demand. Although annual discoveries (gross additions to proved reserves) of natural gas in the United States are still on a general upward trend from the current level of 22 trillion cu ft annually, most forecasters do not expect this to increase substantially in the foreseeable future. For example, the updated (to include 1966 and 1967 data) mathematical model of natural gas discovery and production in the U.S. developed by the Institute of Gas Technology (IGT)' projects that discoveries will level out at about 25 trillion cu ft annually in the late 1970's and during the 1980's and then decline to about 21 trillion cu ft by the year 2000 (Fig. 1). This adds up to a new supply for the period 1968-2000 of about 790 trillion cu ft. Experts who usually reflect the producers' viewpoint, such as Radford L. Schantz of Foster Associates,* are relatively more pessimistic. In contrast, a forecast just made by the U.S. Dept. of the Interior is much more optimistic.3 It assumes an increase in gas discoveries of 2.2% per year over the period 1965-80, reaching about 30 trillion cu ft in 1980. If this rate of increase were extended to the year 2000, annual discoveries would reach 46 trillion cu ft at that time, for a total over the period 1968-2000 of about 1100 trillion cu ft. To these forecasts of new gas discoveries must be added proved reserves of roughly 290 trillion cu ft,4 bringing total U.S. supplies for the rest of the century to nearly 1100 trillion cu ft (IGT) and possibly as high as 1400 trillion cu ft (U.S. Dept. of the Interior). This is approximately the same range as that of two estimates of total remaining recoverable natural gas supply: Potential Gas Committee, 980 trillion cu ft5 and IGT, 1450 trillion cu ft.6 Only the 1965 estimate by the U.S. Geological Survey7 suggests that economically recoverable natural gas supplies will not be exhausted around the end of the century. These forecasts are, naturally, based on the assumption that changes in technological, economic, and regulatory environment as they affect the gas industry will be of an evolutionary, not revolutionary, nature. The various forecasts of potential natural gas supply must now be compared to forecasts of natural gas demand (Table I). The general consensus is that the recent Future Requirements Committee projection to 1990' (extended to the year 2000 by the most recent U.S. Bureau of Mines (USBM) projection9) represents the minimum gas requirements (Table 11). They add up to a total of 1030 trillion cu ft for the period 1968-2000. Even this minimum anticipated gas demand exceeds the total remaining supply estimate by the Potential Gas Committee and would nearly exhaust the proved reserves plus new discoveries projected by IGT. The supply situation would appear much tighter if the demand projections of the Texas Eastern Transmission Gorp.10 and the American Gas Assn.(A.GA.)'' were used (Table I). Yet, these higher forecasts probably do not include the effects of such new markets as gas fuel cells, use of liquefied natural gas as a transport fuel, etc. They also may not fully reflect the impact of air quality control on the fuel market. Obviously, the probable discrepancy between projected supply and demand can only be accommodated in four ways. 1) Rapid increase in exploration and drilling activity to provide new supplies in the amount projected by the optimistic U.S. Dept. of the Interior forecast, coupled with an increase in net pipeline imports from Canada and Mexico from the present 0.5 trillion cu ft per year

Jan 1, 1970

By Mary Louise Theodore, R. G. Aspden, D. A. Colling

T RACES of sulfur have a marked influence on the physical and mechanical properties of many iron-base alloys. The commonly used combustion method for the determination of sulfur content is not accurate enough at the 50 ppm level by weight and below to be useful in determining the influence of sulfur. Kriege and Wolfe' have described a method for the determination of sulfur in iron alloys in which the sulfur is evolved as hydrogen sulfide followed by reaction with N, N-dimethyl-p-phenylenediamine, and iron (111) to form methylene blue which is measured spectrophoto-metrically. This method of determining sulfur has been used to study the activity of sulfur in Fe-Si-S alloys,' but has not been previously applied to the determination of sulfur in Fe-Ni alloys because of the insolubility of nickel in dilute hydrochloric acid. Dissolution of nickel in dilute hydrochloric acid, however, can be greatly accelerated by the addition of a small amount of platinic chloride.3 By combining these two techniques in a procedure in which 0.005 pct platinic chloride in 1:l hydrochloric acid is used as the dissolving fect on the strength of the material. However, ductility is influenced by the presence of discontinuous precipitation. In Fig. 5, percent elongation data at room temperature and 1400°F is shown for two sets of specimens of Waspalloy which were solution heat treated at 1950°F and either quenched or slow cooled to the aging temperature and then aged for 100 hr at 1292" and 1598ºF, respectively. At room temperature the existence of a discontinuous precipitation cell at grain boundaries (see data point marked by arrow) has no apparent effect on ductility. However, at elevated temperatures a pronounced lowering of ductility occurs when discontinuous precipitation has occurred in the specimen. It would appear that the morphology of discontinuous precipitation "cells" at grain boundaries would be highly conducive to the initiation of cracks which in turn lead to premature "grain boundary" failure.

Jan 1, 1970

By Alden B. Greninger

That metallographic structures analogous to the martensite of steel may be found in certain copper-aluminum and copper-tin alloys has been known for many years; similar structures recently were found in certain copper-zinc a1loys.l In all three of these alloy systems the martensite structures result from transformation of the metastable fi phase when the speed of cooling from the B range is sufficiently high to suppress decomposition into equilibrium phases. In the normal decomposition of solid solutions into equilibrium phases, diffusion is needed to bring about the necessary changes in concentration, and the rate of reaction falls almost to zero at temperatures slightly above room temperature. The rates of reaction for martensite processes, however, are not dependent upon temperature; the transformation does not require rendjustments of concentration. For example, the martensite transformation in 60:40 (B) copper-zinc does not begin until the temperature has dropped to about minus 30" C., and then continues down to minus 130" C. and probably even at lower temperatures.' Furthermore, martensite processes apparently proceed only while the tempcrature is falling, within the proper range, and cease completely while the temperature is held constant ;$ and they cannot be suppressed by extremely rapid cooling although the rate of cooling for some alloys may be increased to over 10,000 times the critical cooling velocity. Isaitschew, Kaminsky and Kurdjumow2 account for these observed behaviors of rnartensite processes by postulating that the mechanism 6I... consists in a regular rearrangement of the lattice in such a way

Jan 1, 1939

A SERIES of papers on strategic and otherwise important mineral products was prepared some ten years ago under the joint auspices of the Committee on Foreign and Domestic Mining Policy of the Mining and Metallurgical Society of America and the Committee on Industrial Preparedness of the American Institute of Mining and Metallurgical Engineers. These papers were later published in a joint volume entitled International Control of Minerals (1925). Amongst them was one on manganese. The Subcommittee on Manganese prepared its paper in two forms. One was intended for inclusion with the series above referred to and approached its subject more particularly as an international problem. The other dealt more definitely with manganese as an element in the problem of national defense. This last was first written under date of January 24, 1924 as a confidential report, for and at the request of the War Department. It was later released and published, in slightly modified form, as a separate pamphlet by the Industrial Preparedness Committee of the American Institute of Mining and Metallurgical Engineers. After the lapse of eight years, in view of the vital position of manga-nese in the problem of industrial preparedness against a war emergency, the War Department made a request to have the conclusions of 1924 reviewed and brought up to date. To comply with this request the manganese subcommittee was reconvened (with a somewhat changed personnel) and exhaustive studies were once more made of the entire subject of manganese. A new report, with specific recommendations, was submitted to the War Department in February, 1932. This second report is now herewith released for publication. Certain specific conclusions and recommendations as expressed to the War Department are omitted. Otherwise the report stands as prepared and submitted by the manganese subcommittee of 1931. The members of this committee were: C. Minot Weld, Chairman, R. C. Allen, Arthur S. Dwight, J. W. Furness, D. F. Hewett, Reno H. Sales, Theodore Swann and Scott Turner. ARTHUR S. DWIGHT, Chairman, Committee on Industrial Preparedness.

Jan 1, 1933

By Albert Sauveur

The following propositions and corollaries are intended to present, as concisely as possible, some of the evidences gathered while studying the microstructure of steel. Each proposition is accompanied by photo-micrographs showing the structure of illustrative samples. But it must be understood that the special instances thus chosen for illustration are by no means the only ones on the examination of which the propositions are based. On the contrary, they have been taken almost at random among a great many, in some instances more than a hundred, similar cases. Proposition I. A slow and undisturbed cooling from a temperature x or higher produces crystallization. Plate L, Plate II., Fig. 1, and Plate V., Figs. 1, 2, 3 and 4 show the crystalline structure of several pieces of steel. Plate I. reveals this structure in the center of a slowly-cooled Bessemer ingot, 1.5 feet from the top. Plate II., Pig. 1, is from a small 2-in, square testingot of the same heat, slowly cooled. Plate V., Figs. 1, 2, 3 and 4 show the structure of different parts of steel rails. The original photographs were all magnified 70 diameters, and have been reduced in engraving to 63, or to 55 diameters, as shown in the plates. Proposition 11. Undisturbed cooling from an initial temperature lower than x is not accompanied by crystallization. Plate III., Fig. 5, shows the structure of a piece of rail-steel forged from a white heat until it had fallen to dull-red. The structure is almost amorphous. Practically no crystallization has taken place during the subsequent cooling. Corollary.—Pieces of steel finished at a temperature lower than x do not take a crystalline structure.

Jan 1, 1894

By Frank H. Riddle, Wilfrid R. Foster

GENERAL treatment of the various minerals of importance in refractories appears in the chapter entitled "Refractories" elsewhere in this volume. The present chapter is restricted to a discussion of minerals of the sillimanite group and brings up to date the excellent information contributed by Prof. Paul F. Kerr to the first edition (1937). Since the appearance of that edition, the status of the group has changed some- what. Kyanite remains the preferred source material for mullite refractories but total consumption of kyanite has increased considerably.85 The exigencies of World War II forced an increased dependence on domestic sources and led to an intensification of the search for higher-grade deposits of kyanite and allied minerals. The first discovery of massive kyanite similar to that of India has been reported from Georgia.37 British East Africa has joined India as a substantial supplier of our imported kyanite, but that from India continues to hold preference.85 During World War II, prices of both domestic and foreign grades reached peaks unparalleled since the earliest years of the use of kyanite and as yet have shown no tendency to return to prewar levels. Topaz, by virtue of the deposit outlined in South Carolina, merits inclusion in the group.20,36,95 Large andalusite deposits, which threaten to rival our one large domestic occurrence, have been found in Russia.69,88 Sillimanite has not yet attained an important position among these useful minerals because of the lack of accessible deposits of high-quality material in adequate supply.37,50,58 Tests by the Bureau of Mines have indicated the possibilities of economically beneficiating low-grade sillimanite and kyanite.105.106,140 Government, university, and industrial

Jan 1, 1949

By Alden B. Greninger

That metallographic structures analogous to the martensite of steel may be found in certain copper-aluminum and copper-tin alloys has been known for many years; similar structures recently were found in certain copper-zinc a1loys.l In all three of these alloy systems the martensite structures result from transformation of the metastable fi phase when the speed of cooling from the B range is sufficiently high to suppress decomposition into equilibrium phases. In the normal decomposition of solid solutions into equilibrium phases, diffusion is needed to bring about the necessary changes in concentration, and the rate of reaction falls almost to zero at temperatures slightly above room temperature. The rates of reaction for martensite processes, however, are not dependent upon temperature; the transformation does not require rendjustments of concentration. For example, the martensite transformation in 60:40 (B) copper-zinc does not begin until the temperature has dropped to about minus 30" C., and then continues down to minus 130" C. and probably even at lower temperatures.' Furthermore, martensite processes apparently proceed only while the tempcrature is falling, within the proper range, and cease completely while the temperature is held constant ;$ and they cannot be suppressed by extremely rapid cooling although the rate of cooling for some alloys may be increased to over 10,000 times the critical cooling velocity. Isaitschew, Kaminsky and Kurdjumow2 account for these observed behaviors of rnartensite processes by postulating that the mechanism 6I... consists in a regular rearrangement of the lattice in such a way

Jan 1, 1939

By Heihachi Kamura

The reduction of iron oxide, such as Fe203, to iron in the blast furnace is performed principally by carbon monoxide, but partly by solid carbon by the two following reactions: Fe2O3 + 3CO = 2Fe 4- 3CO2 2Fe2O3 + 3C = 4Fe + 3CO2 It is known that reduction by carbon monoxide takes place at a much lower temperature than reduction by carbon and that the reducing action of earbon monoxide progresses to the inside of the ore in lump form by gaseous diffusion. In the reduction by carbon, however, the reducing action takes place only at the contact surface of the ore and carbon, so that the more complete the reduction by carbon monoxide, the more efficient is the operation. However, the reduction does not progress as shown in the foregoing equation, because carbon dioxide acts oxidizingly on the metallic iron to such a degree that when the gaseous composition reaches a certain proportion of carbon dioxide to carbon monoxide, the reduction practically stops, even though the gases are moving slowly through the heated ore. The proportions of carbon monoxide and carbon dioxide in the gas depend on the kind of iron oxide and the temperature of reduction, also on the duration of time in the reaction. The longer the time of the reaction, the higher the proportion of carbon dioxide obtained in the gas, but finally it will attain to a condition of equilibrium. Chemical Equilibrium of Iron, Oxygen, and Carbon Investigations concerning the equilibrium between iron, oxygen, and carbon have been carried out by E. Baur and A. Glaessner,1 who deter-

Jan 1, 1925

By Takuski Stanislaw, Alfons Krawiec

Rock bursting is a particular hazard in the pit-coal mines of Poland due mainly to the physical-mechanical properties of the rock and the geological-tectonic structure of the Upper Silesian Coal Basin. Mining and geophysical methods of predicting and preventing rock bursts are discussed. These include: seismologic methods, various kinds of shock blasting, torpedoing, and injecting water under high pressure.

Jan 1, 1978

By L. S. Deitz

This part of the symposium deals with the problems encountered by the consumer of nonferrous scrap, that is, the smelter and refiner who melts the selected scrap items and produces foundry ingots of specified compositions or billets for rolling or extrusion in nonferrous mills. The fundamental problems are quite similar for all secondary' nonferrous metals. However, these remarks will be confined to the copper-base alloys since in the sorting, melting and refining of these alloys probably all the usual types of problems are encountered; in addition, papers are being presented later on secondary lead, zinc and aluminum. While metallurgical

Jan 1, 1943

By Ernest Wiltsee

The Half-Moon mine, situated three miles west of the town of Pioche, exhibits geological features which are peculiar and interesting. The general formation in the vicinity of Pioche consists of a quartzite, usually covered with an overlying limestone containing strata of shale. In the camp itself, where the original mines are situated, the quartzite has been denuded, and the principal veins outcrop in this formation; to the west, the quartzite is again covered with limestone, containing thin strata of shale.

Jan 1, 1893

By R. W. Raymond

Some months ago I heard from a party of returned tourists an amusing story of a Chinese laundryman in the National Park who had included in his cabin a hot spring, of which he was accustomed to avail himself in his business, and who, on one occasion, having thrown a lot of linen into this spring to soak overnight, had added a piece of soap to facilitate the process, and had been considerably surprised when, stimulated by this soap, the spring had suddenly become a geyser and wrecked his establishment. The story went on to say that the practice of "soaping" geysers to make them, active had become general, but had been forbidden by the authorities.

Jan 1, 1889

By Theo B. Comstock

Since 1892 the writer has published several articles in the Engineering and Mining Journal concerning the relations of the

Jan 1, 1901

By A. J. Lyon

The stability and permanence of any structural material used in aircraft are of paramount importance. The spontaneous hardening, or age-hardening, which takes place in some of the aluminum alloys under ordinary conditions of temperature and atmosphere, is accompanied by an increase in tensile strength and proportional limit and a decrease in elongation or ductility. Within the last few years the introduction of a number of strong and ductile casting alloys led to a study by the Materiel Division, Air Corps, of the permanence of the physical properties in several of these alloys. It has been found that even though some alloys have good properties directly after casting or heat treatment, they are not satisfactory for stressed parts that require a combination of strength and ductility. It has also led to the conclusion that all alloys that can be hardened by artificial aging—heating in a temperature range below 170" C. (340" F.)—will harden spontaneously if allowed to stand for a sufficient length of time. It follows that, in aircraft work where the factors of safety are limited on account of the necessity of keeping the weight of the structures as low as possible consistent with their safe operation, the properties of the alloys in the stable or final condition should be used as a basis for design rather than the properties obtained on the material directly after casting. The work of Wilm in Germany, Hanson and Gayler at the National Physical Laboratory in England, and Merica, Jeffries, and others in the United States, has shown that the spontaneous hardening is characteristic to a greater or less extent in all aluminum-base alloys in which the solubility in the solid state of the alloying constituents decreases with the temperature. It has been shown that, by heating to a temperature as near as possible to the melting point of the material and soaking at that temperature for a sufficient length of time and then quenching or cooling rapidly, a maximum amount of the soluble constituents can be retained in solution and the condition of maximum hardening effect upon aging can be obtained. Also, in ordinary sand and chill castings, without heat treatment, a sufficient amount of the alloying constituents is held in solution to cause important changes in the final physical properties.

Jan 1, 1929

By Edward B. Hughes, Frank G. Norris

OXIDATION is characteristic of all processes for making steel from pig iron. This thought has been aptly expressed by H. W. Graham13 in the most recent Howe Memorial Lecture, "The process of steel-making consists of using iron oxide to reduce the carbon content of the pig iron to the desired level." Direct oxidation refers to the reaction that results from introducing oxygen either alone or mixed with other gases directly into the steel bath. In working a heat, oxygen in some form is added to the steel to remove the undesirable constituents as oxides. There are two general methods of supplying this oxygen to the open hearth bath. The method in which the oxygen is added as a, compound such as C02-or iron ore is designated an indirect method because the steel bath must first decompose the compound to attain oxygen in a usable form. The other method in which oxygen is added to the bath in the elemental or gaseous form, more or less diluted by other gases such as nitrogen, is a direct, method because no decomposition is necessary before the oxygen reacts with iron to form FeO which is dissolved in the bath in a usable form. Bubble formation (at least of a macroscopic size) presents no problem in case of direct oxidation because the reacting agent (oxygen) is in the form of bubbles when entering the metal. Regardless of whether oxygen is introduced into the bath directly or indirectly, several reactions proceed concurrently. In the presence of the bath of molten iron, FeO is formed either by oxidation of iron by oxygen or reduction of oxides by iron. This FeO dissolved in the molten iron is the source of oxygen for the oxidation of manganese, carbon, silicon, and phosphorus if these are present. The oxidation of carbon from steel is the controlling steelmaking reaction. The introduction of oxygen into the bath, its reaction in the elimination of impurities, and its control by the use of de-oxidizing additions have been subjects of importance since steel was first made by the bessemer process. Direct oxidation is, in a sense, an application of the bessemer principle to the open hearth process. Graham13 states: "The use of oxygen or air jets introduced into the metal bath is essentially an effort to approach in the open hearth the turbulence, rapid interface reaction, and high production rate per hour that exists in the bessemer process." The general subject, "Oxygen in Steelmaking," was given new life by the studies of Herty and associates starting about1925. The current interest in elemental oxygen is intimately related to the large scale production of oxygen developed during the war period. Some of the first applications were made during the early summer of 1946 at the Steel Co. of Canada using oxygen with the fuel. Such a use is of considerable interest and importance in contributing to faster heats but is not the subject of the present discussion which deals entirely with the introduction of elemental oxygen directly into the open hearth bath. A recent article12 reviewing the current

Jan 1, 1948

By C. A. Heiland, W. H. Courtier

The investigations described were made on a portion of Clear Creek basin near Golden, Colo. (-4 portion of the area under survey is shown in Fig. 1. The photograph was taken in the vicinity of station No. 2 of Line 11.) Three principal purposes were in the minds of the investigators: 1. To repeat with modern, more sensitive and more reliable instruments magnetometric placer investigations previously made. 2. To disprove the recently advanced theory that deposits of the glacial period have no pronounced magnetic effects. 3. To develop in detail the theory of the magnetic effects produced by placer deposits. Six years ago, the first magnetic observations were published, which proved that it is possible to locate gold-bearing channels with relatively crude instruments.' Two years ago, K. C. Laylander published results obtained with similar instruments.2 The measurements of the latter were discussed by the senior author of this paper.3 At that time, however, the material available for such a discussion was somewhat scarce and not made with the most modern magnetic instruments, although very brilliant results were obtained. Therefore, the senior author felt that magnetic investigations should be made on very clear geologic conditions with the most modern instruments. Comparison of Magnetometers The junior author undertook this work in the spring of 1928. The magnetic field balances, for vertical and horizontal intensities, designed by Schmidt were used (Figs. 2 and 3). The scale value of these instruments was approximately 257 and 157, respectively. The middle

Jan 1, 1929