By R. F. Domagala, D. J. McPherson

Iodide zirconium was combined with calculated amounts of ZrO2 or master alloys and arc-melted. Annealing treatments were carried out at 21 temperature levels. Metallographic examination of the heat treated specimens permitted construction of the binary phase diagram from zirconium to ZrO2. Oxygen additions to zirconium raise the transformation temperature as well as the melting point. Features of the diagram include the peritectic formation of beta, the formation of alpha directly from the melt, an intermediate phase ZrOB with a' range of homogeneity, and a eutectic between alpha and Zr02. PHASE relationships in the Zr-0 system were determined in the range 0 to 66. 7 atomic pct 0 (ZrO,). Arc-melted alloys were annealed at temperature levels between 600" and 2000°C. Determination of the phase boundaries was accomplished by metallographic evaluation of specimens quenched from the various temperatures. Incipient melting techniques were used to determine solidus curves, and X-ray diffraction work was employed to study the lattice parameters of the a solid solution and the phase ZrO,. Experimental Procedures Westinghouse "Grade 1" iodide zirconium crystal bar (approximately 99.8 pct pure) was employed for the investigation. This material is substantially free of the impurity inclusions characteristic of most zirconium metal. Previous work has shown it to be the most satisfactory grade for phase diagram studies. The zirconium crystal bar, as-received, was coated with corrosion product from autoclave tests by which its grade designation is determined. The bars were sand blasted lightly, pickled for 1 min in a 20 pct HN0,-5 pct HF aqueous solution, rinsed in water and acetone, and dried. The bars were rolled to about 1/32 in. strip, cut into 10 in. lengths, and pickled again. The material was sheared to approximately Y4 in. squares, cleaned with acetone, and stored for use. Two pounds of specially prepared "chemically pure," and 100 grams of spectrographic grade ZrO, were obtained for the preparation of alloys. The "Specpure" ZrO, was obtained from Johnson, Mat-they Co.. Ltd.. and Titanium Alloy Manufacturing Div. of National Lead Co. supplied the other grade of oxide. The "chemically pure" material (henceforth referred to as C.P. ZrO,) was used for the preparation of all alloys employed in the determination of phase relationships. A limited number of alloys were prepared with the "Specpure" oxide to recheck certain phase boundaries. Analyses of the two grades of oxide are given in Table I. The C.P. ZrOI was received in powder form, not suitable for arc melting. Therefore, this material was compressed to wafers 1 in. in diameter and about Vn in. thick. These were segmented and stored for use. The "Specpure" material, in the form of small granules, was suitable for use in the as-received condition. A nonconsumable electrode arc-melting furnace was used to prepare alloys. A water-cooled copper crucible and tungsten-tipped electrode were employed. The material was placed in the crucible and rapidly melted under a protective atmosphere of helium gas by striking the arc on a tungsten stud and directing it upon the charge material. Details of operation, including drawings of this type furnace, have been published.'

Jan 1, 1955

By W. M. McKewan, R. G. Olsson

In order to improve the understanding of the iron oxide reduction mechanism, the rate of equal molar diffusion of hydrogen and water vapor was measured through disks of porous iron and alumina. The measuretneizts were made at atmospheric pressure at 800°, 900- , and 1000°C. It is shown tint the reduction of dense hematite pellets with hydrogen at these temperatures and at atmospheric pressure is to a great extent limited by gaseous diffusion between the bulk-gas phase and the iron-wustile interface. THE investigation of the reduction of iron oxides with hydrogen has been the subject of numerous papers. Although the effects of temperature, pressure, and gas composition on the rate of iron oxide reduction have been studied, the actual mechanism of the reduction process has not been definitely determined. As a means of improving the understanding of the mechanism, the rate of equal molar counterdiffusion of hydrogen and water vapor was measured through porous iron and porous alumina disks at reduction temperatures. The alumina was used as a basis of compari-son because its pore structure is homogeneous and independent of temperature. The porous iron was prepared by the reduction of dense hematite disks with hydrogen at the temperature of the subsequent diffusion experiment. The hematite disks were made from pellets that were identical to those used by McKewan1,2 in his study of iron oxide reduction with hydrogen. In these investigations the weight loss and rate of movement of the various interfaces were measured as a function of the reduction temperature and gas composition. With these reduction data and the presently reported diffusion data it is possible to determine the importance of H2-H2O transport between the bulk-gas phase and the Fe/FeO interface to the reduction of dense hematite. APPARATUS AND PROCEDURE A porous iron or alumina sample was held in the base plate of a sealed canister containing porous granular wustite, as illustrated schematically in Fig. 1. The canister was suspended from an automatic recording balance in a vertical tube furnace through which flowed hydrogen and water-vapor mixtures of known composition at atmospheric pressure (0.96 atm). Hydrogen from the gas stream diffused through the porous sample, reducing the wustite in the interior of the canister. The water vapor that was formed diffused back to the gas stream. The rate of diffusion was determined from the recorded weightloss data. The furnace, automatic balance, and gas-metering equipment have been described previously.2 The main body of the canister and the tubing extension were made of stainless steel while the base plate was made of high-purity iron. The main body of the canister was % in. in diam. It held approximately 6 g of porous granular wustite that was prepared by reducing 0.1- to 0.2-cm-diam specular hematite particles at 900°C with an H2-H2O mixture of a composition near the iron-wustite equilibrium value. The upper end of the 1/8-in.-diam tubing extension was sealed with a segment of plastic tubing and a tubing clamp. The temperature at the top of the furnace was sufficiently high so that no water vapor condensed inside the extension. In the experiments with porous iron, iron oxide samples were prepared from reagent-grade hematite that was pressed and sintered in a manner previously described.' The resulting pellets had a density of 5.15 ± 0.05 g per cu cm. Each pellet was centerless-ground

Jan 1, 1967

By J. E. Hanlon, S. R. Butler, R. J. Wasilewski

It is known that stoichiometric NiTi transforms to a structure of lower symmetry near room temperature. The present investigation deals primarily with the changes in the electrical and magnetic properties which occur at the transformation. The effects of composition and various heat treatments on electrical properties are also discussed. In recent investigations by Purdy and Parr,' Wang et a1.,2 Dautovich and Purdy,~ Dautovich et a1.,4 and the authors, ~,' NiTi has been observed to undergo a martensitic phase transformation from the ordered CsCl (B2) structure to one of lower symmetry. The crystal structure of the low-temperature modification is still not completely worked out. This transformation occurs near room temperature for the stoichiometric composition. The thermodynamic, elastic, crystallographic, and microstructural characteristics of this transformation for some compositions have been previously reported.'-= In the present investigation, the changes in the electrical transport properties and magnetic susceptibility of NiTi when it undergoes the martensitic phase transformation have been measured. The approximate composition range covered is 48 to 52 pct Ti.* *All compositions are given in atomic percent._____________________ EXPERIMENTAL PROCEDURES AND RESULTS 1) Sample Preparation. The NiTi alloys were prepared from iodide titanium (>99.92 pct Ti) and vacuum-premelted carbonyl nickel (>99.95 pct Ni) by repeated arc melting under gettered argon and casting in a water-cooled copper mold. After the cast buttons were hot-forged at 800" to 950°C, the oxidized surface was removed by grinding and etching. Samples were cut from the worked polycrystalline buttons. After fabrication, the samples were annealed 1 hr at 900°C and water-quenched. The composition of the alloys was assumed to be the same as in the initial feed. This assumption was supported by material balance checks on 100-g arc-melted buttons which demonstrated quantitative recovery to within k0.02 pct. The oxygen content of the alloys was '150 ppma (weight) and the carbon content was 30 to 50 ppm. 2) Electrical Resistivity and Hall Effect. The electrical resistivity was measured over the composition range 48 to 52 pct Ti for temperatures varying from 4.2"K to 900°C. The high-temperature and many of the low-temperature experiments were carried out using conventional 4-probe dc techniques.7 The Hall coefficient and ac resistivity were measured at 20 cps using the apparatus shown schematically in Fig. 1. The equipment is basically an ac potentiometer: The resistive or Hall voltage of the sample is balanced by a comparison voltage provided by a dividing network across a standard series resistance. The off-balance signal is amplified by a Tektronix 122 amplifier and detected by a Princeton Applied Research (PAR) phase-sensitive detector. The precision of the resistivity and Hall coefficient measurements is i0.1 and i3 pct, respectively. The uncertainty in the data is increased by i2 pct from the precision limits because of uncertainty in dimensions and possible end effects. The temperature dependence of the electrical resistivity and Hall effect for a stoichiometric (50.0 pct Ti) NiTi sample are illustrated in Fig. 2. Above 75"C, this sample has essentially the B2 structure, while below about 0°C it is completely in the low-tempera-

Jan 1, 1968

By Hsun Hu

Direct observations were made on the recrystalli-zntion of a cold-rolled (110) [001] crystal of 3 pct Si-Fe by annealing thin sections of the specimen inside the electron microscope during examination. Subgrain formation, presumably by polygonization, occurs rapidly, followed by a slow increase in the subgrain size before recrystallization can be detected. No migration of the subgrain boundaries was observed, and the formation of recrystallization nuclei by coalescence of subgrains is suggested. Re-c~ystallization characteristics of various texture components were individually examined. AS reported in a previous paper: orientations of the various deformation texture components in a 70 pct cold-rolled (110) [0011 crystal of 3 pct Si-Fe were completely confirmed by transmission electron diffraction patterns taken at various areas of the specimen. These orientations can be summarized as follows: Over most areas of the deformed crystal (111) planes are parallel to the surface. These areas correspond to either $- the two main defor: mation textures, the (111) [112] or the (111) [112].2-5 Within a few areas, (100) planes parallel to the surface are frequently found. These areas represent the minor deformation texture component, the (100) [Oll] type, which is derived from rotated Neumann bands.2'4'5 Only in very rare instances are (110) planes found parallel to the surface. This orientation corresponds to the very weak texture component of the (110) [001] type. In a pole figure, this (110) [0011 orientation is located within the orientation spread between the two main (111) [1121 type textures. Usually the electron diffraction patterns taken at various areas of the specimen are very simple ones, i.e., for any one area the pattern consists only of sharply defined spots of a single orientation. In some areas, however, more or less continuous rings of weaker intensities are superimposed on a simple pattern, indicating the presence of a wide range of additional orientations. In order to understand in detail the recrystallization of this cold-worked crystal, the recrywtallization characteristics of each of the various deformation texture components must be examined. This can best be done by using a high-temperature stage and transmission electron microscopy techniques, whereby small areas corresponding to the various texture components can be selected individually for examination. The present paper presents results obtained by this method. MATERIAL AND METHOD Specimens were prepared from a previously studied1 single crystal of a commercial grade 3 pct Si-Fe alloy with an initial orientation (110) [00l], cold-rolled 70 pct from 0.014 in. to 0.004 in. in thickness. Thin foils were prepared by electrolytic polishing as described in the earlier paper.' Specimens of this thin foil were then mounted in a high temperature stage similar to the one designed by Whelan.6 A direct current was used as the heating source. The temperature of the heating grid was calibrated by means of a Pt vs Pt-10 pct Rh thermocouple in a vacuum chamber (0.01 to 0.02µHg). Maximum variation within the temperature range of 250o to 000°C was about ± 25°C. After the desired areas were selected for examination, the specimen was heated to a low temperature for some time while the selected area was constantly watched. When no further change in structure and orientation could be observed, a higher temperature was applied. Photomicrographs and diffraction patterns were taken from time to time during examination, with the heater temporarily turned off* while the photographs were

Jan 1, 1962

By H. C. Chao, W. F. Hosford, L. H. Van Vlack

The negative "plastic Poisson's ratio" suggested in earlier studies of Mus deformation is analyzed, and the results are verified experimentally with NaCl crystals. In the early stages of deformation where the primary {110}(110) slip predominates, compression along. the [001] direction produces contraction along the lateral [011] direction plus a compensating expansion along. the [100] direction. With additional strain, the primary slip is supplemented by secondary {111}(110) slip so that the above contraction diminishes and a more typical deformation appears. THE shape change of bee and fee crystals deformed by compression or tension along [011] has been analyzed in some detail and shown to be responsible for the development of peculiar microstructures in [011] fiber textured polycrystals of these metals.1'3 This paper concerns the unusual shape change accompanying [011] compression of NaCl crystals. It is the direct outgrowth of an earlier investigation of the deformation of manganese sulfide inclusions in steel.3,4 In that investigation, cylindrical specimens of steel containing small oriented crystals of MnS were prepared by powder metallurgy and plastically compressed. The flow of the inclusions was determined relative to that of the steel by sectioning the composite and measuring the length-to-width ratio L/W of the inclusion and diameter-to-height D/H ratio of the steel cylinder on the plane of section. These L/W ratios, normalized by dividing by the initial LO/WO ratio of the inclusion, were compared with the normalized D/H ratio of the steel cylinder. Of particular interest here are the deformation characteristics of an inclusion oriented with [Oil] parallel to the compression axis. When measurements were made on sections parallel to the (100) plane of the inclusion, the L/IV ratios were only slightly in excess of unity, indicating a high apparent hardness of the [011] criented inclusion. However, measurements on a (011) plane of section resulted in L/W ratios which were much larger, Fig. 1. These observations prompted an analysis of the strains resulting from slip in an MnS crystal compressed along [011.]. CRYSTALLOGRAPHIC ANALYSIS Manganese sulfide has the NaCl crystal structure, and the predominant slip system is {110}(110). A secondary system, {111}(110), has also been reported.= {110}(110) Slip. When a crystal is subject to a uni-axial compressive stress 011 along [011], four slip systems, (101)[101.], (101)[101.], (110)[i10], and (110) [ 110], will be equally stressed with a shear stress t = 0.2 011 while the other two {110}( 110) systems will be unstressed. The normal strain En along any reference axis n resulting from slip is given by Schmid's law: en = S COS ?in COS in ?i 111 where ?in and +in are the angles between n and the i slip direction and n and the i slip plane normal, respectively, and where ?i is the shear strain on the i slip system, For the four active slip systems above, the cos ?in cos +in terms are all equal when the reference axes are the [011] compressive axis, [011] and [ 100]. Eq. [I.] therefore reduces to en - cos ?n cos +ny [2] where y =S?i for all slip systems. Substituting the appropriate angles, Eon = 0.25? 110 eon - 0.25y110 [3] €100 = -0.50y 110 The interesting feature of Eqs. [3] is that they predict that the strains in the [011] and [011] directions, resulting from {110}(110) slip, are equal and of the same sign. Thus when a crystal is compressed along [011], it will contract along the lateral [oil] direction

Jan 1, 1967

By Donald E. Grimes

In conjunction with Inland Steel&apos;s development of lead-bearing steels possessing improved machin-ability because of tellurium and/or selenium additions, it was decided to determine liquidus and solidus temperatures in the Pb-PbTe-PbSe sub-ternary system. With the exception of alloys in the PbTe-PbSe system, it is believed that no previous study of this subternary has been performed. Thermal analysis was employed in a general survey of the subternary. In addition to PbTe, PbSe, and pure lead, ten ternary compositions were selected at intervals of ten at. pct. Sixty-gram alloys were prepared by sealing an appropriate mixture of the elements in quartz crucibles with a central thermocouple-well under a vacuum of less than 10 p. All three elements were 99.999+ pct pure with only trace impurities detected by spectroscopic examination. After the alloys had been heated at least 20°C above the liquidus in a Kanthal furnace, cooling and heating curves were obtained. Two or more cooling curves were employed both for the determination of each alloy liquidus and for the solidus of those al- loys containing greater than 50 at. pct Pb. Cooling rates were 0.5° to 3.5°C per min during the 5 min immediately prior to the start or end of solidification. For those ternary alloys containing 50 at. pct Pb, the solidus was determined from heating curves. Temperatures were measured with a Pt/Pt-10 pct Rh thermocouple which was calibrated in the same apparatus against the freezing points of zinc (A. D. MacKay—99.999 pct), antimony (A. D. MacKay-99.999 pct), and copper (ASARCO—99.999+ pct) both before and after the experimentation. The only interruptions in the continuous strip-chart recording of the temperature occurred for brief periods at significant points of interest when direct readings were made with a Rubicon Type B potentiometer sensitive to * 1 µv. The average liquidus and solidus temperatures obtained in this investigation are listed in Table I together with probable errors based on the accuracy of the thermocouple calibration and the reproduci-bility of the data. No chemical analyses of the alloys were performed because the synthetic or as-charged compositions were felt to be reliable. The melting points obtained for PbTe (924.7° ± 0.7°C) and PbSe (1084.0° ± 0.6°C) compare favorably with recent findings of other investigators.&apos;-&apos; As indicated in Table I, both the liquidus and solidus temperatures increase as selenium replaces tellurium for a constant atomic percent lead. As a result, the ternary liquidus and solidus temperatures for a given percent lead lie between the corresponding binary temperatures published in the literature. It should be noted that those ternary alloys containing 50 at. pct Pb exhibit a relatively narrow liquid-plus-solid region (<80°C) when compared with alloys containing greater than 50 at. pct Pb. Alloys with 60, 70, or 80 at. pct Pb not only have a much wider liquid-plus-solid region (>500°C) but also exhibit considerably lower and approximately constant solidus temperatures which thus form a virtually isothermal solidus "plane" slightly below the melting point of pure lead (327.3°C). For these alloys

Jan 1, 1965

By R. D. Nelson, F. E. Bowman

Evidence has been found for a (010)a?(111)B[102]a /,11[341]/B crystallographic relationship between the monoclinic a and B phases of plutonium during the a?B transformation. The results of an X-ray diffraction study, where [010] fiber textured a samples were used in the absence of suitable single crystals indicate that the (OIO)a planes become (111)B planes upon transformation under near-equilibrium conditions. The transformation strain along the fiber axis, which was the [010] direction, was measured dila-tomekically; the measured 8.5 pct expansion compares favorably with the 8.44 pct expansion in the in-terplanar spacing represented by the (010)a?(111)B relationship. From plots of the atom positions in each of the related planes, a correspondence was deduced between the [102]a, direction and the [341]B direction. Further analysis of the two lattice structures in the light of this relationship revealed a rotation about the [102] direction of 1 deg 43 min and a slight shearing in this same direction of about 30 min. THIS paper discusses the (B crystal structure of plutonium and the orientation relationship existing between the monoclinic a and B phases during the a?ß transformation. The kinetics of the a?ß and (3 — a transformations have received extensive consideration, and because of the crystallographic complexity of these phases, the question of the mechanisms by which these transformations occur is especially intriguing. Nelson and Shyne1 evaluated the existing experimental evidence and concluded, from the indirect evidence available, that both the ß ? a and a ? ß transformations occur by a martensitic process. Their data reveal the anisotropic nature of these transformations which suggests the existence of specific crystallographic relationships between the parent and product phases. In this paper, we are concerned with the confirmation of the existence of such a relationship resulting from the a ? ß transformation and the derivation of the crystallographic details necessary to specify it. EXPERIMENTAL RESULTS X-ray diffraction and dilatometric data were obtained from samples of a plutonium having a [010] fiber texture. These cylindrical specimens, approximately 1 cm in diam, were prepared by transforming the ß phase to a under the influence of a uniaxially applied compressive load.&apos; The [0l0] direction is parallel to the direction of applied stress; it is also perpendicular to the (010) planes. This correspondence between the plane normal and the direction having the same indices is, in the monoclinic a plutonium structure, restricted solely to this (010)[010] combination. Such a specimen was mounted in an evacuated, elevated temperature specimen holder on an X-ray dif-fractometer so that the diffracting surface was perpendicular to the fiber axis. The a diffraction pattern, Fig. 1, taken at about 115ºC, revealed the predominance of the (020) reflection. This monoclinic, P 21/rn space group yields no (0k0) reflections when k is odd. The temperature was raised slowly to 160°C to effect the complete transformation to the phase; then it was lowered to 120°C so that a diffraction pattern of the ß could be obtained near the a = ß equilibrium temperature for direct comparison with the a at the same temperature. The (3 diffraction pattern, Fig. 2, obtained under these conditions showed a (222) reflection relatively much more intense than in the random pattern. The other reflections appearing with sig-

Jan 1, 1970

By D. C. Ganow, N. J. Grant, I. R. Silver, A. R. Chaudhuri

The structural changes that result when a metal is "cold worked" lead to higher values of yield and tensile strength on subsequent deformation at room temperature. Further it has been shown that the beneficial effects of cold work are, to some extent, maintained even at elevated temperatures. The strength improvements from prior cold work decrease as the temperature is raised and are a function of grain size, amount of cold work, and strain rate (or time of test). If recrystallization occurs during test, the cold-worked material may even show weaker stress-rupture properties than the annealed material. A question that arises is whether there is a significant effect on the subsequent creep behavior if the prior deformation is performed under creep conditions at high temperatures not too different than the test temperature, but at significantly different strain rates and for various amounts of strain. An answer to this question was sought in the work described in the present paper. PROCEDURE Two materials were used in this work, high-purity aluminum and a solid-solution A1 2 pct Mg alloy. The compositions are shown in Table I. The grain size in the two materials was 0.2 to 0.3 mm. The deformation for both the prestraining and for the creep tests was at constant stress. The procedure adopted was to prestrain a specimen to the desired elongation, remove the load, and cool to room temperature rapidly by spraying. the test bar with cold water. The specimen was then placed in a creep machine, held at the test temperature for less than 5 min, and loaded. Less than 15 min was required to bring the specimen to temperature. The creep stress was based on the diameter resulting from the prior strain, and values of elongation at fracture listed in the tables do not include the respective elongations resulting from the prestrain. The choice of the stresses for the prestrain and for the creep tests was made so that the tests could be completed in relatively short times to maximize any effect of prestrain. The specimens had a gage length of 1 in., the pure aluminum specimens having a diameter of 0.150 in. and the alloy specimens a diameter of 0.125 in. For pure aluminum, prestrain was at 400&apos; and 600°F with testing at 500°F; for the alloy, prestraining was at 700°F and testing at 600°F. RESULTS The prestrain conditions for the aluminum and the alloy specimens are shown in Tables I1 and IV. In addition to showing the time required to achieve the desired prestrain, the expected rupture Lives are given which would have resulted had the creep prestrain been continued to fracture. The prestrained and the annealed specimens were then tested in creep to fracture; the temperature and stress for the pure aliminum specimens being 500o F and 1800 psi and for the alloy, 600&apos; F and 3400 psi. The creep curves for the prestrained and the annealed specimens of pure aluminum showed all three stages of creep; hence in addition to the effect of prestraining on the rupture life, it was also possible to determine the effect of prestraining on the minimum creep rate, and on the time and elongation at the end of each of the three creep stages. The results are shown in Fig. 1 and Table 111.

Jan 1, 1960

By C. R. Clark, G. Swift, D. S. Roberts

The purpose of this investigation was to measure PVT behavior of various types and combinations of heavy hydrocarbon components from the paraffinic, naphthenic and aromatic classes where the relative proportions Of the various components were selected to approximate those of natural gas or gas condensate systems. Synthetic mixtures were used so that the compositions Of the various components could be measured accurately. n-Heptane, methylcyclohexane and methylbenzene were used to represent the paraffinic, naphthenic and aromatic components of the heavy fraction. In the mixtures studied, the heavy fraction composition was held constant at O. O5-mole lraction, the balance being methane except for one mixture where 0.10-mo1e fraction of an intermediate component, propane, was added. The PVT data for the mixtures were determined in a variable-volume, constant-mass apparatus at psuedo-reducedtemperatures from 1.84 to 2.00, over a pseudo-reduced pressure range from 2.3 to 12.0. The experimental results showed that, regardless of the type of heavy material (paraffinic, naphthenic, aromatic, or combinations thereof) mixed with methane or methane and propane, the compressibility factors at equal values of pseudo-reduced temperature and pressure varied by less than 2.2 percent. INTRODUCTION PVT data is used for natural gas and gas condensate fluids in determining reserves of reservoirs and performance of wells, in metering produced fluids, and in recombining samples for laboratory studies. While there are vast amounts of PVT data reported for natural gas and gas condensate systems from which useful correlations have been developed, &apos; the compositional analyses for these systems and the resultant correlations typically were made with components analyzed through some arbitrary carbon number, usually C6, with the residue reported as a lumped "heavy" fraction. The heavy fraction was stoichiometrically recombined on the basis of an apparent molecular weight to give the final compositional analysis. It is virtually impossible to make a systematic analysis of the effect that variation of the relative amounts of paraffinic, naphthenic and aromatic constituents of the heavy fraction of natural systems might have on PVT behavior. Because there is considerable latitude in the relative amounts of these constituents, one speaks of crudes or condensate liquids as being "paraffin base", etc. It is of interest to determine if changes in the relative amounts of these three types of hydrocarbons in the heavy fraction cause significant changes in PVT behavior. If so, steps should be taken to describe better the nature of the heavy fraction in PVT correlations. If not, more confidence can be placed in the correlations presently employed. DESIGN OF THE EXPERIMENTAL INVESTIGATION We attempted to determine if changes in the base of the heavy fraction would cause significant changes in the PVT behavior of gas or gas condensate fluids. Synthetic mixtures were used to enable us to systematically vary the base of the heavy fraction and to analyze accurately the fluids. We found that the heavy fraction of naturally occurring condensate systems seldom exceeds 0.05-mole fraction. Thus, the mole fraction of the heavy fraction in the synthetic systems studied was set arbitrarily at 0.05, to maximize whatever deviations in PVT behavior that might occur. Further, we judged that since the C7 hydrocarbons normally are present in greater quantities than higher carbon number hydrocarbons in naturally occurring systems, the use of n-heptane, methyl cyclohexane, and methylbenzene to represent the paraffinic, naphthenic, and aromatic species in the heavy fraction would be most appropriate. Finally, to enable us to compare our

Jan 1, 1970

By A. M. Gaudin, C. S. Chang

Adsorption was measured for barium ion and laurate radical, using radioactively marked agents, over wide range of concentrations. Laurate adsorbed in absence of barium fails to float. With barium, flotation-effective laurate coating needs not exceed 5 pct of monolayer. Barium adsorption then is several fold larger. No barium laurate coating is obtained. IN general, fatty acids or their alkali salts do not cause clean quartz to float. However, the presence of multivalent ions, such as the alkaline-earth metal ions and heavy-metal ions, can activate quartz and thus make it respond to soap flotation. The mechanism of activation and soap flotation of quartz has been studied.&apos;-&apos; The problem was attacked by making flotation tests rather than by careful adsorption measurements on suspensions of ground quartz in solutions containing the activator and the collector. Attempts have been made to determine the adsorption of barium ion and calcium ion on quartz. The results have only qualitative value as the analytical methods were not adequately precise. Artificial radioactivity and progress in radioactivity detection have introduced a new analytical tool, which can have a sensitivity several orders of magnitude greater than that of other methods."-" In the experimental work described in this paper the radioactive tracers, barium 140 and carbon 14, were employed. Lauric acid was synthesized, having a radioactive carbon atom and was used with Ba" to study the adsorption of barium and laurate ions from aqueous solution on ground quartz. Flotation tests, using the vacuum flotation technique,&apos; were run in conjunction with the adsorption experiments. The object of this investigation was to understand better the reaction mechanism of barium activation and soap flotation of quartz. Methods and Materials Quartz Sample Preparation: Lumps of hand-picked quartz, washed free of stains, were reduced in size to —20 mesh in laboratory crushers. The product was boiled in concentrated hydrochloric acid to remove the abraded iron. The cleaned product then was ground dry in a laboratory porcelain mill, using siliceous pebbles, to pass through a 200 mesh screen. The ground product was deslimed by sedimentation at 37 microns. This —200 mesh +400 mesh material was subjected again to boiling with concentrated hydrochloric acid, followed by washing with distilled water and further desliming. The cycle was repeated until no trace of iron could be detected in the wash liquor. During the final washing, the pH of the wash water was checked to insure the complete removal of the acid from the mineral. The quartz then was rinsed with conductivity water. The resulting product was dried in a drying oven and stored in mason jars. The impurities (spectrographic) were as follows: Al, 0.01 to 0.001 pct; Li, Mg, Mn, Na, each less than 0.001 pct; Fe and Cu not detected. The specific surface of the quartz sample was determined by the krypton gas adsorption method.&apos; The average of two measurements was 881 sq cm per g. The calculated specific surface for 37/74-micron quartz particles, using a surface factor of 1.96; is 900 sq cm per g. This is in good agreement with the measured value of 881 sq cm per g. Beta-Counting Method: The radioactive isotope of barium used in the experimental work was barium 140. It has a sufficiently long half-life, 12.8 days, emits high-energy beta particles (up to 1.0

Jan 1, 1953

By K. Torssell, U. Lindborg

The kinetics of precipitation deoxidation is considered from a theoretical point of view. The size distribution and the total content of deoxidation products are estimated statistically as a function of time, taking into account Stokes and gradient collisions between the particles and separation at the top surface of the bath. The assumption is made that two particles coalesce into one larger particle as a result of a collision. General expressions are derived and calculations are carried out numerically for the case of silica particles in liquid iron. The analysis predicts a three-stage behavior for the removal of oxygen, an incubation stage, a stage of rapid separation, and a slow final stage where the content approaches the equilibrium value. The agreement with experimentally determined size distributions and deoxidation times is considered to be good. A quantitative estimation of such growth mechanisms as diffusion from the melt and redistribution of oxygen from small particles to large ones shows that these latter mechanisms cannot explain the experimentally observed gvowth of inclusions. This also indicates that collisions provide the important growth mechanism. OXIDE inclusions precipitate when a deoxidizer like silicon or aluminum is added to a steel bath. The inclusions grow and the large particles tend to separate from the bath. For each type of oxide the growth determines the sizes of the final inclusions as well as the total inclusion content of the steel. The mechanism of growth is controversial, however. It has been suggested that an inclusion grows principally by diffusion of atoms through the melt to the inclusion particle or principally by collisions and coalescence with other inclusions. Diffusion growth is always present to some extent but recent experiments and calculations by Torssell,&apos; Kniippel et &apos;a1.,2 Sano et al. and Miya-shita4 indicate that collisions may be more important than previously realized. A detailed analysis has so far been lacking. The present paper is a quantitative, statistical analysis of the growth and separation of inclusions and is based on a collision theory. Nuclea-tion is not considered. The numerical estimates are based on the experimental conditions of Torssell&apos;s&apos; investigation and comparisons are made with his observations. Torssell&apos; studied the growth and separation of silica particles in liquid iron. Samples were taken from a 0.6 kg iron bath at various times after the addition of silicon. By a particle-counting technique developed by Bergh and Lindber~the size distribution of the inclu- sions was determined. The number of particles at the first sampling, 10 sec after silicon addition, was of the order of 3 x lo7 to 10&apos; per cu cm, the largest particles having a radius of 2 to 4 pm. The volume fraction was 0.001 to 0.004; i.e., the dispersion was very dilute. During subsequent holding the largest particles increased their radius by a factor of 10 after about a minute, and the whole size distribution was displaced toward larger values. These results were obtained with allowance for precipitation of the equilibrium concentration of oxygen during solidification. The bath contained less than 0.01 pct of C. Figs. 1 and 2 show the typical appearance of the inclusions. Most particles are very closely spherical and appear to have been liquid or semiliquid in the melt. The observed number of inclusions, about 5x 10&apos; per cu cm, is of the same order of magnitude as found by ~er~h.&apos; This is a large value. It follows that the diffusion distances are very short and that the precipitation

Jan 1, 1969

By A. M. Gaudin, C. S. Chang

Adsorption was measured for barium ion and laurate radical, using radioactively marked agents, over wide range of concentrations. Laurate adsorbed in absence of barium fails to float. With barium, flotation-effective laurate coating needs not exceed 5 pct of monolayer. Barium adsorption then is several fold larger. No barium laurate coating is obtained. IN general, fatty acids or their alkali salts do not cause clean quartz to float. However, the presence of multivalent ions, such as the alkaline-earth metal ions and heavy-metal ions, can activate quartz and thus make it respond to soap flotation. The mechanism of activation and soap flotation of quartz has been studied.&apos;-&apos; The problem was attacked by making flotation tests rather than by careful adsorption measurements on suspensions of ground quartz in solutions containing the activator and the collector. Attempts have been made to determine the adsorption of barium ion and calcium ion on quartz. The results have only qualitative value as the analytical methods were not adequately precise. Artificial radioactivity and progress in radioactivity detection have introduced a new analytical tool, which can have a sensitivity several orders of magnitude greater than that of other methods."-" In the experimental work described in this paper the radioactive tracers, barium 140 and carbon 14, were employed. Lauric acid was synthesized, having a radioactive carbon atom and was used with Ba" to study the adsorption of barium and laurate ions from aqueous solution on ground quartz. Flotation tests, using the vacuum flotation technique,&apos; were run in conjunction with the adsorption experiments. The object of this investigation was to understand better the reaction mechanism of barium activation and soap flotation of quartz. Methods and Materials Quartz Sample Preparation: Lumps of hand-picked quartz, washed free of stains, were reduced in size to —20 mesh in laboratory crushers. The product was boiled in concentrated hydrochloric acid to remove the abraded iron. The cleaned product then was ground dry in a laboratory porcelain mill, using siliceous pebbles, to pass through a 200 mesh screen. The ground product was deslimed by sedimentation at 37 microns. This —200 mesh +400 mesh material was subjected again to boiling with concentrated hydrochloric acid, followed by washing with distilled water and further desliming. The cycle was repeated until no trace of iron could be detected in the wash liquor. During the final washing, the pH of the wash water was checked to insure the complete removal of the acid from the mineral. The quartz then was rinsed with conductivity water. The resulting product was dried in a drying oven and stored in mason jars. The impurities (spectrographic) were as follows: Al, 0.01 to 0.001 pct; Li, Mg, Mn, Na, each less than 0.001 pct; Fe and Cu not detected. The specific surface of the quartz sample was determined by the krypton gas adsorption method.&apos; The average of two measurements was 881 sq cm per g. The calculated specific surface for 37/74-micron quartz particles, using a surface factor of 1.96; is 900 sq cm per g. This is in good agreement with the measured value of 881 sq cm per g. Beta-Counting Method: The radioactive isotope of barium used in the experimental work was barium 140. It has a sufficiently long half-life, 12.8 days, emits high-energy beta particles (up to 1.0

Jan 1, 1953

By Nicholas J. Grant, Rolf Nordheim, Bill C. Gissen

The system Cb-Re was examined in detail utilizing pure metals, careful melting techniques, and heat treatments. Metallographic and X-my methods were utilized for phase identification. In addition to soli-dus determinations, the composition limits and mode of formation of the intermetallic compounds 0 and X were determined. The binary constitution diagram Cb-Re has been the subject of a number of investigations.&apos;-7 Two intermetallic phases have been described and tentative diagrams have been proposed. It was the aim of this investigation to obtain a complete and more accurate diagram through the use of purer alloys and improved techniques. The diagram worked out by Knapton7 was published after our experiments were concluded. EXPERIMENTAL METHODS The starting materials were Re powder of 99.95 pct purity, supplied by the Chase Brass and Copper Co., and Cb rondelles of 99.6 pct purity, supplied by the Electro Metallurgical Co. Typical analyses are given in Table I. The alloys were prepared from compacted Re powder and Cb rondelles; for critical compositions master alloys were used. The melts varied from 5 to 50 g and were melted nonconsumably in an Heraeus arc furnace, under ti-tanium-gettered laboratory grade argon. It was necessary to invert the buttons and remelt, followed by crushing and further remeltings, the number of which depended on the nature of the fracture of the alloy. The weight of each alloy was carefully checked after each melting operation. It was found that significant weight losses occurred only when loose Re powder was used. These losses amounted to a maximum of 3 wt pct in such instances, but did not occur after the charge was once molten, regardless of the composition. Typical loss of weight after 4 remelts, including crushing, amounted to 0.2 wt pct. Oxygen pickup during successive melting cycles did not appear to be significant, since the weight gain values never exceeded 0.01 wt pct. Control of the composition of the alloys was not too difficult; however, the problem of homogenization was a far greater one. Optimum alloying conditions were finally achieved by a combination of master alloy production and repeated crushing and remelting cycles. The compositions of the alloys utilized to determine the constitution diagram are listed in Table 11. The weight balance method was used ultimately as the sole analytical method, since repeated checks indicated that it was accurate to 0.2 pct, if the weight losses were small. The results were double-checked by a metallographic study of the homogeneity of the samples, since this was presumed to be the more serious factor. Heat treatments at 1200°C or lower were accomplished by sealing the specimens in Vycor tubes, heating in a Globar furnace, followed by air cooling. This was considered to be an adequate quench because of the very low temperatures involved. For temperatures of 1200" to 1900°, alloys were homogenized and heat treated in a tungsten-filament resistance vacuum furnace. From 1900" to 2750" a tantalum-tube resistance furnace was utilized, operating under a vacuum of 105 mm Hg. The temperature measurements up to 1200" were made by means of platinum-platinum 10 pct Rh thermocouples, with an accuracy of 5°C. For temperature measurements greater than 1200°C, optical pyrometers were used. They were calibrated against a standardized instru-

Jan 1, 1962

By J. L. Zakin, G. K. Patterson, J. M. Rodriguez

Correlation has been obtained between drag-reducing characteristics for turbulent flow in a pipe and measurable properties of several polymer solutions. Several concentrations of high molecular weight polymethyl methacrylate in toluene, high molecular weight polyisobutylene in both toluene and cyclohexane, medium molecular weight polyisobutylene in cyclohexane and benzene and low molecular weight polystyrene in toluene were studied. Data obtained in these nonpolar solvents and literature data for more polar solvents were successfully correlated as the ratio of measured friction factor to purely viscous friction factor vs the modified Deborah number vrl/D0.2 where 71 is the first-mode relaxation time of the solution estimated by the Zimm theory. A shift factor which is a function of intrinsic viscosity 1/(4[?] - 1) allowed all the data obtained with nonpolar solvents to be correlated as a single function. For these systems, most of the data fit a single curve to within + 5 percent of the average friction factor ratio. The shift factor did not give a unique function of the data for the more polar systems. INTRODUCTION The phenomenon of drag reduction in polymer solutions was first studied by Toms1 in dilute solutions of polymethyl methacrylate in mono-chlorobenzene. The drag ratio for flow through circular tubes has been defined2 as the ratio of the pressure. drop of the solution to the pressure drop of the solvent at the same flow rate. The drag ratio is less than 1.0 for a drag-reducing fluid. Practical use of drag reduction is being made in fracturing operations in the petroleum industry.3 A more fundamental quantity is the friction factor ratio, defined as the ratio of the observed pressure drop to that predicted for a solution of the same viscosity characteristics and density at equal flow rates using the Dodge-Metzner friction factor equation4 Viscous solutions with drag ratios greater than 1.0 can have friction factor ratios less than 1.0. For practical applications, it is drag reduction which is of interest. However, for correlation the fundamental ratio is the friction factor ratio. In recent years, drag reduction has been studied extensively. Recent studies have shown that reasonable predictions of the incipience of drag reduction in polymer solutions can be made from the properties of the solutions and the flow Variables.5 However, it has not been possible to predict accurately the amount of drag reduction to be expected for a given polymer solution without any drag-reducing turbulent flow data on the same solution.6 For flow through circular tubes it is well established that there is a concentration effect and a diameter effect on drag reduction. Toms1 observed that drag reduction increases with an increase in the concentration of the solution up to an optimum concentration beyond which, due to the increased viscosity of the solutions, the drag ratio increased with an increase in concentration. Hershey 7 observed that for dilute Newtonian polymer solutions in nonpolar hydrocarbon solvents, a normal transition region may be obtained followed by a departure from the von Karman equation (on a friction factor-generalized Reynolds number chart). The point of departure is a function of diameter: the smaller tubes depart at the lower Reynolds numbers. Concentrated solutions may show no abrupt transition region, but merely an

By R. A. Swalin, L. A. Neimark

The research work presented in this paper had initially a two-fold goal. First, further data concerning the low-temperature recovery of cold work was desired. Recovery phenomena have been extensively studied in face-centered-cubic metals but at the time of initiation of this research, no investigation concerning the low-temperature recovery in body-centered-cubic metals had been made. During the course of the investigation a paper by Martin on the recovery of point defects in molybdenum appeared.&apos; Comparison of our results on tungsten with Martin&apos;s results on molybdenum will be made. Secondly, knowledge concerning the influence of a particular type of impurity addition on the recovery kinetics was desired. It has been known for a long time that extremely small amounts of certain impurity additions exert a profound influence on the recrystallization behavior and the resulting microstructure of tungsten. Small amounts of potassium silicate and aluminum chloride added prior to the reduction of tungsten oxide to the metal have been found by Smithells to raise the recrystallization temperature markedly,2 and yield an ultimate microstructure in which grains several millimeters long are produced in fine wires of say 10 mil diam. If the impurities are added singly, ordinary secondary recrystallization results with none of the spectacular properties of the wire to which special additions were made. Swalin and Geisler3 and Rieck4 have studied the recrystallization behavior of such doped wire in some detail. The former workers found that small amounts of these impurities raised the recrystallization temperature over 400°C and electron microscopic examination revealed no obvious inclusions in the microstructures. In fact. chemical analysis showed that there was <0.001 pct K, <0.002 pct Al, trace of Si, and <0.0003 pct 0 in the wire studied. The possibility that the role of the special impurities is to keep the structure open by void formation and that submicroscopic porosity acts as the inhibiting agent has been discussed.2&apos;3 Meijering and Rieck5 have suggested that the impurities are strung out as second-phase particles in a direction parallel to the drawing direction. It was thought that a kinetic study of recovery could perhaps elucidate the role of the impurities to some extent. When a metal is deformed by cold work three basic types of defects are thought to be introduced into the crystal lattice, namely, interstitials, vacancies, and dislocations. Van Bueren6 has proposed that recovery of cold-worked metal is a four-stage process, each step being the result of the annealing of a primary defect or a combination of defects and having a unique activation energy. The steps in order of increasing activation energy are attributed to a) the diffusion of interstitials recombining with vacancies, b) diffusion of vacancy pairs, c) the diffusion of single vacancies, and d) climb of dislocations. In metals with relatively low- or medium-range melting points the temperatures for recovery are low enough so that the first three steps may occur during room-temperature deformation. For tungsten, because of the high melting point and subsequently high recovery temperature, it was calculated, using Nowick&apos;s approach7 that this recovery would occur in the temperature range 200" to 600°C. It is also known that recovery of X-ray line broadening, presumably due to dislocation climb, occurs at about 600°C.8 EXPERIMENTAL METHOD Two types of cold-rolled 10-mil-diam tungsten wire were used in the investigation; a) pure tungsten, (called undoped) and b) G. E. No. 218 wire (called

Jan 1, 1961

By P. R. Swann, J. G. Parr

Quenched structures were studied in alloys containing up to 12.5 pct cobalt. The subsequent decomposition of a 10 pct cobalt retained-ß phase alloy was investigated using metallographic and X-ray diffraction methods. Hardness measurements also were made during the decomposition process. Precipitation of Ti2Co is by nucleation and growth; and an activation energy of 50,000 cal per mole was determined. The values of the coefficient ß suggest that the precipitate is pearlitic at temperatures between 450 and 475°C, and spheroidal between 500 and 525°C. THIS paper describes part of a series of invesligations into phase transformations in binary alloys of titanium with transition elements. The general approach is similar to that taken in work on titanium-iron and titanium-nickel alloys.&apos; Previous investigators&apos;&apos; have established the titanium-rich end of the titanium-cobalt phase diagram, reproduced in Fig. 1. Orrell and Fontana&apos; showed that alloys containing more than about 6 pct" cobalt quenched from the ß range, produced 100 pcl retained-p phase. The isothermal decomposition of alloys containing between 0.8 pct Co and 15.5 pct CO was investigated by the same workers in the temperature range 650 to 1000°C. They reported that these alloys transformed into a or Ti,Co depending on the cobalt content, but no quantitative data were given. In the work to be described a series of alloys containing 0.8 pct Co to 12.5 pct Co was examined in the quenched condition. The 10 pct Co alloy (the lowest cobalt content to retain 100 pct ß on quenching) was selected for further work on the tempering kinetics of the ß decomposition. Experimental Procedure Since our own melting equipment was not installed at the outset of this work, the Physical Metallurgy Division of the Department of Mines and Technical Surveys (Ottawa, Canada) prepared the alloys. These were made of Japanese sponge, (which when melted had a value of 103 DPH, using a 1-kg load), and electrolytically prepared cobalt. The al- loys, made up to contain 0.8, 1.6, 3.3, 5.8, 8.3, 10.0 and 12.5 pct Co, were homogenized by swaging into rods at 900°C. Filings were taken from the rods, and any iron chips from the file were separated magnetically. Size fractions of both plus and minus 200 mesh (about 75p) were shown by their constitution, after annealing just below the eutectoid temperature, to contain the same cobalt content. Consequently, it was permissible to use the —200-mesh fraction, knowing it to be representative of the rod composition. Quenching in argon was carried out in a newly designed furnace, whose features include (1) an Inconel furnace tube, (2) a positive pressure of argon maintained at all times in the furnace—even when a sample is removed or inserted. The furnace is shown in Fig. 2 and is described in the Appendix. The tempering processes were carried out on powder samples sealed in evacuated quartz capsules. Since the highest tempering temperature was 525OC, no protection against reaction with the quartz was necessary. (Tests were made on filings of iodide titanium and showed no hardness increase after equivalent heat-treatments.) A thermocouple was attached to the capsule, which was heated to the

Jan 1, 1959

By J. R. Lewis, J. H. Hamilton, V. D. Hanson, K. W. Heinlein, J. M.194-000-000-006 Vonfeld, J. P. Denny

TWO overfeed drum-type separators using a suspension of magnetite in water as the separating medium have been installed in the Champion NO. 1 preparation plant of the Pittsburgh Coal Co., Division of the Pittsburgh Consolidation Coal Company. A simplified flow diagram of the Champion No. 1 coarse coal circuit is shown in Fig. 1. A railroad car rotary dump, capable of handling 20 cars per hr, discharges the coal into a hopper. Coal is fed from the hopper of the rotary dump to a 60-in. belt conveyor by two reciprocating pan-type feeders. The belt conveyor feeds the run of mine coal onto the main raw coal screen. The first deck is fitted with 3 in. round hole perforated plate which removes the 3x0-in. coal. The second deck of the screen is equipped with 6-in. lip screens which separate the remaining coal into +6 in. and 6x3 in. The +6 in. coal is transferred to a shaking picking table and then discharged onto the loading boom. The 6x3-in. coal is fed to the No. 2 dense medium vessel for cleaning. The clean coal from this unit flows to a vibrating screen where the medium is removed and the coal sized into 6x4 in. and 4x3 in. The 6x4-in. coal is transferred to the loading booms and the 4x3-in. is conveyed to the clean coal classifying screens to remove degradation. The 3x0-in. raw coal is blended in a system composed of three storage bins having a total capacity of 400 tons. From these bins the coal is fed onto a 48-in. flight conveyor by three reciprocating feeders. This flight conveyor delivers the coal to the Rheo plant. The 3x0-in. coal is then cleaned in two 48-in. Rheolaveur launders each equipped with two Rheo boxes. The first set of boxes removes a primary refuse and the second set produces a middling product which is recirculated in the launders. The cleaned coal and water overflows from the primary launders to two sizing and dewatering shaker screens where the water and — -in. coal are removed for further cleaning in the Rheo fine coal plant. The 3x3h-in. clean coal is combined with the 4x3-in. coal from the No. 2 vessel, sized into 4x2 in., 2x1 34 in., and 1&apos;/4x in., then sent to the loading booms. The 3x0-in. refuse from the primary launders is normally fed to the No. 1 dense medium circuit, but any portion or all of this material can, as an alternate, be processed in the Rheo rewash launder. The primary refuse when fed to the dense medium circuit is screened into YSXO which is cleaned in the fine coal plant and 3x for cleaning in the No. 1 vessel. The clean coal from this vessel is passed over a vibrating drainage and rinse screen, then sluiced to the rewash sizing shaker where it is dewatered and sized for loading. The installation of a pilot plant separating vessel using a suspension of magnetite in water was pro-

Jan 1, 1953

By L. A. Roe, John Jan

Iodine is a soft, lustrous, grayish-black nonmetallic element with a density of 4.9. It is the least active of the four members of the halogen family. The other members are, in order of increasing activity, bromine, chlorine, and fluorine. Iodine is a solid at ordinary temperatures, while bromine is a liquid and chlorine and fluorine are gases. Iodine melts at 113°C and volatilizes at 184.4°C to a blue-violet gas with an irritating odor. It occurs in nature only as iodates and iodides or other combined forms. It was discovered by Bernard Courtois in France in 1811, who noticed its presence as an unknown substance in crude soda ash obtained from burning seaweed. Gay-Lussac recognized it as a new element and named it iode, from the Greek word "ioeides or iodes" for violet color (MacMillan, 1970). The world production is not known with any great certainty, but it is probably between 25 and 35 million lb per year, of which about 30% is consumed in the United States. Geology and Mineralogy Iodine compounds occur as a minor constituent as a mineral in the Chilean nitrate deposits and in solution in brines and seawater. According to the US Geological Survey, it is the 47th most abundant element in the earth&apos;s crust. The minerals lautarite, Ca (I03)3 (calcium iodate), and dietzeite, Cat (103)2 (CrO4), (calcium iodate-chromate) are found in Chilean nitrate deposits which are located in Antofagasta and Tarapaca provinces on the eastern slope of the coast range in a desert area. Various brines contain iodine compounds. Seawater contains about 0.05 ppm of iodine and some seaweeds will extract and accumulate it up to 0.45% on a dry basis. Some coals in West Germany also contain iodine compounds. The known and potential sources of iodine reported in 1968 are given in Table 1. Table 2 lists estimated world iodine reserves. Iodine has been recovered from brines in Java, Indonesia, France, England, and the USSR. Iodine has also been recovered from seaweed in Ireland, Scotland, France, Japan, Norway, and the USSR. The indicated reserves and future resources of iodine are large but have never been adequately measured. Analysis Iodine as the free element can be detected by the characteristic blue color it gives to a starch solution. Quantitatively it is determined as the free element by titration with standard thiosulfate solutions using starch as an indicator. Colorimetric methods are also applicable. Markets and Prices Iodine and its compounds are generally marketed in the form of: iodine, crude; iodine, resublimed; calcium iodates; calcium iodide; potassium iodide, sodium iodide, and numerous organic compounds. Product Specifications Crude iodine, World market: 99-99.5% 12. Crude iodine, US produced, average: 99.8% 12. Crude iodine, USP XVII Specs: not less than 99.8% percent I2. Resublimed iodine is usually 99.9% and ACS specifications call for not over 0.005% total bromine and 0.020% nonvolatile materials (Anon., 1971). Prices, c.i.f. United States, for iodine have been steadily increasing from $1.18 per lb of crude in 1967 to $6.37-7.27 in January 1981 (Anon., 1981). In 1980 the price of iodine increased by 50%.

Jan 1, 1983

By J. H. Hamilton, J. R. Lewis, K. W. Heinlein, V. D. Hanson, J. M. 194-000-000-006 Vonfeld, J. P. Denny

TWO overfeed drum-type separators using a suspension of magnetite in water as the separating medium have been installed in the Champion NO. 1 preparation plant of the Pittsburgh Coal Co., Division of the Pittsburgh Consolidation Coal Company. A simplified flow diagram of the Champion No. 1 coarse coal circuit is shown in Fig. 1. A railroad car rotary dump, capable of handling 20 cars per hr, discharges the coal into a hopper. Coal is fed from the hopper of the rotary dump to a 60-in. belt conveyor by two reciprocating pan-type feeders. The belt conveyor feeds the run of mine coal onto the main raw coal screen. The first deck is fitted with 3 in. round hole perforated plate which removes the 3x0-in. coal. The second deck of the screen is equipped with 6-in. lip screens which separate the remaining coal into +6 in. and 6x3 in. The +6 in. coal is transferred to a shaking picking table and then discharged onto the loading boom. The 6x3-in. coal is fed to the No. 2 dense medium vessel for cleaning. The clean coal from this unit flows to a vibrating screen where the medium is removed and the coal sized into 6x4 in. and 4x3 in. The 6x4-in. coal is transferred to the loading booms and the 4x3-in. is conveyed to the clean coal classifying screens to remove degradation. The 3x0-in. raw coal is blended in a system composed of three storage bins having a total capacity of 400 tons. From these bins the coal is fed onto a 48-in. flight conveyor by three reciprocating feeders. This flight conveyor delivers the coal to the Rheo plant. The 3x0-in. coal is then cleaned in two 48-in. Rheolaveur launders each equipped with two Rheo boxes. The first set of boxes removes a primary refuse and the second set produces a middling product which is recirculated in the launders. The cleaned coal and water overflows from the primary launders to two sizing and dewatering shaker screens where the water and — -in. coal are removed for further cleaning in the Rheo fine coal plant. The 3x3h-in. clean coal is combined with the 4x3-in. coal from the No. 2 vessel, sized into 4x2 in., 2x1 34 in., and 1&apos;/4x in., then sent to the loading booms. The 3x0-in. refuse from the primary launders is normally fed to the No. 1 dense medium circuit, but any portion or all of this material can, as an alternate, be processed in the Rheo rewash launder. The primary refuse when fed to the dense medium circuit is screened into YSXO which is cleaned in the fine coal plant and 3x for cleaning in the No. 1 vessel. The clean coal from this vessel is passed over a vibrating drainage and rinse screen, then sluiced to the rewash sizing shaker where it is dewatered and sized for loading. The installation of a pilot plant separating vessel using a suspension of magnetite in water was pro-

Jan 1, 1953

By Jean-Jacques Prompsy, J. S. Rinehart

The purpose of the present study was to arrive at a better understanding of the stress fields developed within drill bits under dynamic loading and the influence that these stress fields could have on the failure of the drill bits. Particular emphasis has been given to the influence that bit shape has on the establishment of highly localized, potentially destructive stress inhomogeneities within the bit. This paper covers one phase of a broad study involving three velocity regimes: impacts at very low velocities, 0 to 20 ft/sec, a velocity range in which dynamic effects are just beginning to be found; impacts at velocities ranging from 20 to several hundred ft/sec, arange commonly encountered in practical drilling operations; and impulsive loading through the detonation of explosives, a velocity range in which the dynamic effects are greatly exaggerated and made more identifiable. Specifically, fracturing which develops at the end of a cylindrical bar undergoing a shock produced by impact was experimentally investigated, the impacted area being the face of a truncated cone terminating the cylindrical bar. Fracture characteristics were looked at as a function of impact velocity, area of impacted face and cone angle — parameters of considerable importance in the design of drill bit. EXPERIMENTS The specimens were made of Plexiglas, which enabled the fracture pattern to be easily observed. In Plexiglas, the velocity of a longitudinal wave is about 8,700 ft/sec, and the velocity of the transverse wave about 4,200 ft/sec. The specimens were impacted by a steel cylinder whose lower face was parallel to the terminal face of the experimental bit, as shown in Fig. 1. The impacting mass was shifted up and down on two steel rods, dropping from a maximum height of 11 ft, with the velocity varied between 0 and 6.5 m/sec. The initial mass of the cylinder was 4.1 kg, which could be increased by steps up to 8.8 kg by addition of steel plates. The velocity of the steel cylinder was determined by using an electric circuit; as the cylinder dropped, it contacted two steel wires, the first one starting and the second one stopping an electronic counter. Two similar counters connected in parallel were used to corroborate each other. The velocity was checked at each drop as it had been observed to vary somewhat from drop to drop. The two contact wires were located just above the top of the specimen so as to give a value of the instantaneous velocity of the steel cylinder at impact. The distance between the wires was 40 ± 0.5 mm and the discrepancy between the counters was never more than 0.1 m/sec. Thus the velocity was known to within 3.25 per cent. This precision was sufficient with respect to the precision of the machining of the specimens. A very small lack of parallelism between the face of a specimen and that of the impacting hammer resulted in an oblique impact which required a much lower velocity to break the specimen. The experiments had a twofold purpose — (1) to observe the fracture pattern, and (2) to find relationships between the minimum velocity required to generate a fracture within a specimen and the