There is plenty of sulphur available but not at the price currently being paid for brimstone. Immediate shortages may be felt before the market adjusts, making marginal sources and by-product sulphur and acid available. (See P. 403) Government aid for mineral exploration is available and regulations governing applications are available from The Defense Minerals Administration, Dept. of Interior. lust ask for M0-5 and also for the contract form which is MP-103.

Jan 5, 1951

By L. J. Howell, A. S. Roy, H. H. Kellogg

KNOWLEDGE of the phase diagram of salt systems is important for selection of the optimum con- ditions for electro winning of the refractory metals from fused salts. This note summarizes the studies of the NaC1-rich portion (0 to 22 mol pct HfC14) of the NaC1-HfC14 phase diagram. Melts in this composition range have vapor pressures well below one atmosphere and melting points between 548° and

Jan 1, 1959

By M. R. J. Wyllie

In a recent publication1 wetting phase relative permeability was exvressed as: and it was stated that a similar expression applied, mutatis mutandis, to non-wetting phase relative permeability; i.e., In Equations (1) and (2), Sw and S0 are respectively the wetting and non-wetting phase saturations as a fraction of the pore volume; PC is the capillary pressure; I; the wetting phase electrical resistivity index; IN, the analogous non-wetting

Jan 1, 1951

By M. R. J. Wyllie

In a recent publication1 wetting phase relative permeability was exvressed as: and it was stated that a similar expression applied, mutatis mutandis, to non-wetting phase relative permeability; i.e., In Equations (1) and (2), Sw and S0 are respectively the wetting and non-wetting phase saturations as a fraction of the pore volume; PC is the capillary pressure; I; the wetting phase electrical resistivity index; IN, the analogous non-wetting

Jan 1, 1951

By Orville R. Lyons

THE Russellton preparation plant of Republic Steel Corp., located north of Pittsburgh, Pa., prepares 395x0-in. Thick-Freeport coal by means of a 13-ft 6-in. diam Chance cone and 16 No. 7 Deister tables. The plant feed ranges between 370 and 410 tons per hr, of which approximately 31 pct is 1/4xO-in. size, and the plant reject ranges between 14 and 16 pct of the feed.

Jan 6, 1953

By Augustus Locke

Jan 1, 1923

By Augustus Locke

Jan 1, 1923

By David J. Mack

The structures and properties of the copper-aluminum alloys have been the subject of much study since the classic investigation of Carpenter and Edwards1 focused attention on. the engineering utility of these alloys. It was recognized at an early date that the metallographic structures developed in the aluminum bronzes were similar to those developed in steels, both in the annealed and the rapidly cooled state. Most investigators have been concerned with the acicular, martensitic-like structure formed from the 0 solid solution upon rapid quenching; the transformation of the ß under equilibrium cooling to a lamellar eutectoid having been relatively neglected. With the introduction in 1930 by Davenport and Bain2 of the isothermal transformation technique for studying eutectoidal decompositions, a new field was opened. Although an enormous amount of work has since been done on the isothermal transformation of steel, study of structurally analogous systems has been almost totally overlooked. The outstanding exception was the prize-winning paper† of Smith and Lind1ief³ ho investigated the decomposition of the 0 phase in copper-aluminum alloys by isothermal methods. This was followed in 1934 by Wasserman's review' of available information on analogous transformations in eutectoid alloys. Since that time no comprehensive study of isothermally transformed eutectoids analogous to steel has appeared, although many valuable contributions have been made to an understanding of the structures developed in such systems. Important papers have been published by Kurdjumow, Gridnew and co-workers, Obinata,18.'9 Greninger,20.21 and Others. The work to be described in this paper was an outgrowth of preliminary studies on the isothermal transformation of a entectoid aluminum bronze, after it became apparent that the alloy under study was reacting somewhat differently than the similar alloy used by Smith and Lindlief. Preliminary Experiments The material used in this study was a high purity aluminum bronze especially prepared by Ampco Metal, Inc. It analyzed: Copper—88.07 pet, Aluminum—11.89 pct, Iron-—0.02 pet, Manganese—-.OI pct, Others—Balance. Although some disagreement exists on the exact composition of the eutectoid, this alloy was believed to be of essentially eutectoid composition even though some pro-eutectoid* delta particles existed in the microstructure of furnace cooled specimens. Specimens transformed isothermally at temperatures slightly below the eutectoid showed relatively large amounts of pre-eutectoid delta, but as will be shown later, this results

Jan 1, 1949

By A. M. Kivari

OPERATIONS at the cement plant of the Permanente Corporation, in the hills about 45 miles south of San Francisco and 12 miles west of San Jose, are interesting to the members because of the adoption of modern hydrometallurgical methods for handling and beneficiating raw materials. Closed-circuit grinding, classification, hydro-separation, flotation, agitation, and thickening are familiar terms at this cement plant. These methods make it possible to process refractory limestone into suitable materials for the manufacture of modern cements. Construction of the plant, having originally a design capacity of 7000 bbl. of cement per day, was started in June 1939, and the first clinker was ground on the following Christmas Day. At present the capacity is about 12,000 bbl. of finished cement per 24 hr., most of the production being low-heat cement.† About 3130 tons of limestone, 620 tons 0f clay and 100 tons of gypsum are required daily for this output. Occasionally iron oxide is added to the clay to obtain the desired composition. This, together with the gypsum, is purchased from outside sources. Up to the present time, the corporation has produced low-heat, normal, moderate heat, moderate-sulphate-resisting, high-early-strength, oil-well, modified-oil-well, and plastic cements. Most of the present production is for Shasta Dam, near Redding, Calif., the total demand being 5,800,000 bbl, of cement. Following are some of the cement requirements of the Shasta Dam specifications: [PERCENT Chemical composition: Loss in ignition2.25 Insoluble residue0.75 SO32.25 MgO5.00 Uncombined lime in clinker (CaO)1 .25 Percentage of iron oxide to alumina ratio1.5 Compound composition: Tricalcium silicate (3CaO.Si02)Not more than 3,5 Dicalcium silicate (2CaO.Si02)Not less than 40 and not more than 65 Tricalcium aluminate (3CaO.Al2O7)Not more than 7 Tetracalcium aluminoferrite (4CaO.A12O3.Fe203) Not more than 0 Fineness:] The average specific surface in the bin sampled shall be not less than 1800 sq. cm. per gram and no individual sample less than 1600 sq. centimeters. Compressive strength: The average compressive strength-in pounds per square inch of three mortar cubes composed of one part cement and 2.75 parts fine testing sand, by weight, shall be equal to or greater than the following:

Jan 1, 1941

By Walter C. Lawson

THE first plans were made in 1930 for the mining by open-pit methods of the low-grade disseminated ore body now known as the Morenci open pit. It was not until 1937, however, that final plans were completed and the decision reached to go ahead with the actual development. Many advances were made in open-pit mining equipment during that period of seven years, therefore the ways and means of attack actually used were very different from those originally contemplated. Diesel-operated bulldozers, big trucks, full-revolving electric shovels and electric churn drills constitute the major equipment finally purchased for this modern stripping operation. Neither the bulldozers nor the big trucks were considered in the early operating plans, for at that time bulldozers had not been used in mining operations and the trucks as yet were undesigned. The full-revolving shovel and the churn drills were not new developments in open-pit equipment, but both had undergone remarkable manufacturing transition, emerging far more efficient and far more dependable than their predecessors. Even the ordinary drilling steel had been fundamentally changed. It was now threaded so that the dulled cutting bits could be detached and replaced, thus eliminating the costly transportation of long bars to the drill shop for resharpening. The decision to use trucks in the preliminary stripping operations was based on the desirability of this type of transportation to economically prepare the pit for rail haulage, coupled with the success that the contractors had had with them on other big excavation jobs. There are at present no plans for the use of trucks beyond the preliminary work, inasmuch as rail haulage will give lower costs after roadbeds and benches are once established. For many years to come, both ore and waste haulage will be over favorable grades. The average length of ore haul between the pit and an assembly yard will be about two miles. From there the crushers will be 1 1/3 miles with a connecting track grade of 0.4 per cent. The upper ore benches of the pit will be reached from the yard by a series of four switchbacks over a ruling grade of 4.0 per cent compensated for curvature. Tracks to the dumps will be on 0.2 per cent grades.

Jan 1, 1938

By Carl Zapffe

The object of the Bradley process is to free manganese oxide from its associated gangue and separate the contained iron oxide by dissolving the manganese and precipitating it from the solution. This results in producing two oxides as concentrates, the one to be converted into a manganese sinter and the other into an iron sinter. The manganese sinter may be made to contain as high as 70 per cent. inanganese and as low as 1 per cent. silica, with phos'phorus not to exceed 0.02 per cent, and from that figure downward to about 0.005 per cent., and with sulfur at 0.007 per cent. The iron sinter contains about 2.50 per cent. manganese, making the total recovery of the manganese 98 per cent. The method involves selective roasting, which converts the manganese into a form in which it is soluble in an aqueous solution of ammonium sulfate, then precipitating the manganese as a hydrate by using ammonia gas, then stabilizing and washing the hydrate, followed by sintering; concurrently most of the iron oxide is converted by roasting into an insoluble form and becomes a residue with magnetic qualities, which makes possible the recovery of much of the iron in the ore. Leaching manganese by using sulfur dioxide gas was shown possiblc Inany years ago. Mr. Bradley tried it for a year, working in conjunction with the original experimenters of that method, and found that while relatively pure inanganese oxide could be produced, the likelihood of developing a commercial process along this line was not very encouraging. He also attempted leaching with nitric and sulfur acids, but the cost of recovery mounted and the quality of the product was not as good Mr. Bradley tried nearly every leaching method proposed, and the expen-ments were made on a large scale in the spacious laboratories of John C. Wiarda & Co., in Brooklyn, N. Y. Insufficient encouragement was discernible in the results obtained. Upon the suggestion of N. Arthur Laury, of John C. Wiarda & Co., Bradley undertook using arnrnoniurn sulfate. Because a high rate of recovery appeared feasible, Bradley planned the erection of a 4-ton pilot plant at the State of Minnesota Mines Experiment Station, at Minneapolis. The results of that work are described in this treatise.

Jan 1, 1929

By R. A. Meussner, R. J. Goode

Six intermediate phases occur in the Nb-Zn sysThese phases form by peritectic reactions at 1120°, spectively. The Nb Zn 15 phase appears as the minor phase in the eutectic structure, and the terminal phases remain nearly pure niobium and zinc even at high temperature. Vapor -pressure measurements on the four high-temperature phases (Nb Zn to Nb Zn 3) permitted estimates of the composition limits of these phases and the calculation of approximate values of AFO, AH°, and AS°. 1 HE present study of the constitution of the binary Nb-Zn system was a part of an analysis of the mechanism by which coatings of the Nb-Zn intermediate phases protect niobium against oxidation at high temperature.' Since the primary interest in these phases was in coating service, attention in this study was given principally to the four phases stable at high temperature with only cursory attention to the two low-temperature phases. The solubility studies of niobium in zinc by Martin, Knighton, and Feder2 and the reports from the present study of the Nb-Zn coating represent the only published data pertaining to this system. Previously Hodge, Evans, and Hoskins, in an experimental survey, had noted that niobium was not resistant to attack by molten zinc, but no further observations were reported. EXPERIMENTAL PROCEDURES a) General. The nature of the binary Nb-Zn system precluded the use of more conventional methods of determining the phase equilibria such as thermal analyses of a series of cast alloys. An extrapolation of the liquidus data of Martin, Knighton, and Feder2 to higher temperatures suggested that the solubility of niobium in zinc would remain low in the entire temperature range of interest. The preliminary results of the present studies showed that all of the high-temperature intermediate phases form by peritectic reactions. Thus the sluggish nature of this type of reaction and the steepness of the liquidus indicated that thermal analyses would not yield reliable data. The peritectic reactions, of course, precluded the direct formation of samples of the individual phases from the melt. b) Materials. The niobium and zinc used in the present studies were of high purity. The niobium, in the form of 0.1-in.-diameter rods, contained 30 ppm 0, 30 ppm N, and 15 ppm C. Aside from 0.05 pct Ta, the metallic impurities (iron, titanium,

Jan 1, 1965

By F. J. Martin, W. G. Hubler

The Beattie mine is at about the center of Duparquet township in the Province of Quebec, Canada. It is 22 miles northwest of the town of Noranda. The elevation is approximately 1200 ft. above sea level. This locality, long considered a favorable one from the geological point of view, has been prospected for over 20 years, but no discoveries of economic importance were made until the present orebody was found by John Beattie in 1930. The specific gravity of the ore is 2.77. The gold occurs in intimate association with the sulfides, pyrite and arsenopyrite, which in turn are very finely disseminated in a silicified porphyry. The bulk of the gold is associated with the pyrite, only a small proportion being with the arsenopyrite. There are small amounts of magnetite, ilmenite and chalcopyrite present in the ore. There is also some hematite in the ore that is mined from near the surface in the open pit. Metallurgical Problems and Methods or Attack 1. The ore is extremely hard and resistant to grinding. 2. The sulfide minerals are finely disseminated in the gangue. 3. The gold, in turn, is so intimately associated with the sulfides that grinding to even 5 microns will not release all of the values for cyanidation. 4. It is necessary to make a high ratio of concentration in order to obtain a product sufficiently high in gold to meet high shipping and treatment charges. Hardness of the Ore.—Owing to the extreme resistance of the ore to grinding, it was recognized that grinding costs would be high. Microscopic tests showed that grinding to 95 per cent minus 325 mesh would be necessary to liberate a sufficient amount of the values in order to obtain a tailing assaying 0.02 oz. gold per ton, which is considered to have the economical minimum gold content that can be obtained. It is not feasible to grind this hard low-grade ore (0.18 to 0.20 oz.) to 95 per cent minus 325 mesh, so it was necessary to overcome the problem in another way. The following method was decided upon: (1) Fine crushing to minus 1/4 in.; (2) relatively coarse primary grinding; flotation of low-grade concentrates in the primary and rougher circuits and discarding the

Jan 1, 1935

By N. Brown, H. Green

The effect of quenching temperature and of aging temperature and time on compression stress-strain curves of ß brass was investigated. Age softening occurs at a rate which decreases with decrease of quenching temperature below the critical temperature for ordering. The activation energy for softening is 15,400 cal per mol. No matter how rapidly brass is quenched or what the temperature from which it is quenched, practically complete order is obtained at room temperature. It has been demonstrated that with respect to the specific heat,',' electrical resistivity," X-ray diffraction, and microstructure, the slowly cooled and rapidly quenched specimens are the same and that complete long range order exists in both cases. However, Smith" showed that the hardness of ß brass depended upon the cooling rate and the temperature from which brass is quenched. Smith showed that the hardness was a maximum for specimens quenched from about 445 °C and that the as-quenched structure softened at room temperature at a rate depending upon the temperature prior to quenching. This softening after quenching is in this paper referred to as age softening. The results of this investigation are qualitatively the same as the findings of Smith. However, a more detailed analysis of these phenomena has been possible since the stress-strain curve offers a more sensitive index of the state of the metal than hardness. It is the purpose of this paper to show how the mechanical properties are related to the ordering of ß brass. A 200-lb ingot made from electrolytic copper and electrolytic zinc was extruded to 1/2in. rod. Chemical analyses at frequent intervals along the rod showed that the alloy contained 51.5 pct Cu with the greatest impurity being iron, at 0.01 to 0.001 pct. To obtain a constant test material, the 1/2in. extruded rod was warm-rolled to % in. diameter at 200°C and then recrystallized to a grain size of 2.0 mm. The specimens for the compression test were % in. high and % in. in diameter. The specimen ends were polished on 600 metallographic paper and coated with Molykote for a lubricant. The compression rig consisted of an anvil resting on the machined table of the Baldwin Southwark testing machine and a plunger fixed to the movable cross

Jan 1, 1954

By Jos. J. Walsh

Ventilation within a coal mine is essential to the welfare of those employed therein, from the standpoint of health, safety, and efficiency. While the saving of life and the preserving of health are the chief reasons for ventilation, efficiency and production are increased. In spite of the fact that we speak of air as having a certain composition, the proportions of oxygen, nitrogen, and carbon dioxide are not fixed, but vary between small limits. The different elements are not chemically united, they are merely mixed and each is free and can be separated with little energy. For this reason air in the mine workings is seldom found in a pure state. Factors that necessitate ventilation in coal mines are those that change the composition of pure air. Contamination of mine air results from the burning of oil-fed flames, the use of explosives, the oxidation of coal, and the liberation of gases by the coal. The extent to which these factors exist governs the size and general plan of the ventilating applianccs required. An efficient ventilating system is one that will furnish air at the working faces in sufficient volume to dilute and render harmless noxious gases and at the same time maintain an oxygen content closely approaching that of pure air. In a well-ventilated mine, the oxygen seldom falls more than 0.5 per cent. below normal. The carbon-dioxide content of the air in the average coal mine will vary from 0.1 to about 0.8 per cent., which amounts are not harmful. Three per cent. of carbon dioxide in air doubles the frequency and the depth of breathing; it is plainly noticeable and if breathed continuously for several hours its effect would probably be harmful. Slight reductions in the oxygen content of the air, such as occur in well-ventilated mines, have no debilitating effect on the worker. A person not exerting himself would fail to observe any unusual physical effect in an atmosphere: containing 17 per cent. of oxygen. This condition, however, or even a condition showing an oxygen content below 20 per cent., would indicate poor ventilation and that the elements which tend to reduce the efficiency of the worker are present, namely water vapor and a high wet-bulb temperature.

Jan 1, 1923

By Jos. J. Walsh

Ventilation within a coal mine is essential to the welfare of those employed therein, from the standpoint of health, safety, and efficiency. While the saving of life and the preserving of health are the chief reasons for ventilation, efficiency and production are increased. In spite of the fact that we speak of air as having a certain composition, the proportions of oxygen, nitrogen, and carbon dioxide are not fixed, but vary between small limits. The different elements are not chemically united, they are merely mixed and each is free and can be separated with little energy. For this reason air in the mine workings is seldom found in a pure state. Factors that necessitate ventilation in coal mines are those that change the composition of pure air. Contamination of mine air results from the burning of oil-fed flames, the use of explosives, the oxidation of coal, and the liberation of gases by the coal. The extent to which these factors exist governs the size and general plan of the ventilating applianccs required. An efficient ventilating system is one that will furnish air at the working faces in sufficient volume to dilute and render harmless noxious gases and at the same time maintain an oxygen content closely approaching that of pure air. In a well-ventilated mine, the oxygen seldom falls more than 0.5 per cent. below normal. The carbon-dioxide content of the air in the average coal mine will vary from 0.1 to about 0.8 per cent., which amounts are not harmful. Three per cent. of carbon dioxide in air doubles the frequency and the depth of breathing; it is plainly noticeable and if breathed continuously for several hours its effect would probably be harmful. Slight reductions in the oxygen content of the air, such as occur in well-ventilated mines, have no debilitating effect on the worker. A person not exerting himself would fail to observe any unusual physical effect in an atmosphere: containing 17 per cent. of oxygen. This condition, however, or even a condition showing an oxygen content below 20 per cent., would indicate poor ventilation and that the elements which tend to reduce the efficiency of the worker are present, namely water vapor and a high wet-bulb temperature.

Jan 1, 1923

By L. J. Buteau, R. E. Reed-Hill, W. A. Slippy

In a zirconium {1121} twins tend to have coherelzt boundaries and thus do not usually taper to a point when they intersect a grain boundary. Under the proper conditions, a (1121) twin may deform a boundary in such a manner as to clearly rcveal the twinning shear. Measurements of these grain-bounrlary rotatzons yield a value of 0.63 for the (1151) twinning shear. The magnitude of the observed shear and its shear sense are in excellent agreement with the assumption that the second undis-torted plme (K2) for this form of twinning is the basal plane (0002). The present value of the tzvinninz shear, which is approximately three limes larger than Rapperport&apos;s value? is in excellent agreement with reported results of Sokuskii and Prolsenko.5 RECENTLY westlake&apos; reported a study of the twinning modes of zirconium based on ~ap~er~ort&apos;s2 values for the twinning elements. He observed that two of the modes, (1012) and {1122), can be explained by relatively simple dislocation models. A workable model for (1121) twinning, however, proved to be very complex and questionable. Because Rapperport&apos;s second undistorted plane, (K2), for (1121) twinning has large indices, {ll2l6), it is possible that the difficulty in defining a model for (1121) twinning lies in an incorrect value for K2. A measurement of this twinning element has therefore been made, using a method based on observations of the shear displacement of grain boundaries at positions where they are intersected by (1121) twins. EXPERIMENTAL PROCEDURES The zirconium specimens were deformed in tension on an Instron machine either at the temperature of liquid nitrogen (77ºK), or prestrained at liquid nitrogen temperature and then further deformed at room temperature. Straining at 77°K was employed in order to nucleate (1 121) twins in large numbers, since simple ropm-temperature tensile deformation favors (1012) twinning. Specimens were machined from 1/2-in.-thick plate. The material was arc-melted sponge zirconium annealed to an ASTM grain size 4 and containing, in parts per million, 380 Fe, 880 0, <40 Hf, 32 N, and < 5 H. The specimen gage length and diameter were 1.25 and 0.130 in., respectively. To insure a gage section initially free of twins, the last 60 thousandths of the specimen diameter was removed by acid machining.

Jan 1, 1963

By R. H. Richman

Coarse-grained Fe-Ni-C martensites formed at subzero temperatures were strained in compression at room temperature and the plastic deformation modes examined as a funclion of carbon content. At very low carbon levels, defovmation occurs hy wavy slip; commencing at about 0.05 pct C, mechanical twinning accounts for an increasing proportion of the plastic flow. Beyond approximately 0.4 pct C the deformation appears to be entirely by mechanical twinning. The habit planes of the operative twin modes were determined to be (113), (0131, and "(089)" in decreasing frequency of occurrence. Some of the implicaticms of Ihe o6served deformation modes upon the structure and properties of ferrous martensites are discussed. METALLURGISTS have long sought to explain the mechanical properties of ferrous martensites, particularly the extraordinary hardness and strength of the high-carbon varieties. Until recently the lack of precise knowledge of the structure of martensite crystals was the most serious barrier to understanding; however, the advent of thin-foil techniques for transmission electron microscopy has removed much of the mystery from martensite structure. Observations by Kelly and Nutting,"&apos; and many others since, indicate that Fe-C based martensite crystals are internally twinned to a degree dependent upon the carbon content, and that a martensite plate containing 0.8 wt pct C or more consists of a stack of twin-related lamellae with each lamella on the order of l00A thick. Such a structure would be expected to influence greatly all aspects of metallurgical behavior, and many of the properties of Fe-C based martensites have been rationalized accordingly. Recent independent experiments led Winchell and cohen3 to conclude that the strength of ferrous martensite is derived primarily from solid solution hardening of the iron lattice by interstitial carbon atoms. Strength contributions from precipitation, dislocation-atmosphere interactions, clustering, short-range order, crystallite size, and so forth, were considered to be of secondary importance. In the view of Winchell and Cohen, the twinned structure of martensite serves mainly to limit the effective length of dislocation lines in the lattice, and thereby confers an added measure of hardening. Few properties of metallic crystals are as sensitive to metallurgical structure as are deformation mechanisms. It is somewhat surprising therefore, that, except for metallographic evidence of mechanical twins in strained martensite,4 no systematic examination of plastic deformation

Jan 1, 1963

By Raymond Mancha

TO determine the optimum inside dimension of an airshaft, it is necessary to strike the proper balance between the cost of power for air friction and turbulence losses within the airshaft, on the one hand, and the cost of sinking the airshaft, on the other. An airshaft larger than necessary is extravagant because the increased amortization rate exceeds the reduction in power cost. Conversely, an airshaft smaller than is needed wastes more power than can be justified by the corresponding reduction in amortization rate. The airshaft power is a function of the air volume Q cu. ft. per min. and the air-pressure drop p in. water gauge across the airshaft. † The airshaft pressure drop is calculated by the formula: R X l X O X Q2 P= 5-2 X A3 wherein R is the air-friction coefficient for the portion of the airshaft 1 ft. deep, 0 ft. in perimeter and A sq. ft. in area, when passing an air volume of Q cu. ft. per minute. The airpower w kw. dissipated within the airshaft is computed by the formula: w= 0.746Q X P 6345 With a combined over-all unit efficiency of the fan and drive of E per cent, the air-shaft power requirements become W = 100w There are 8760 hours per year, so with energy at I cent per kilowatt-hour the annual cost per kilowatt for continuous operation is $87.60; therefore, with energy at C¢ per kw-hr. the annual airshaft power cost MI dollars per year becomes: M1 = 87.60W X C which, expressed by the component parts, becomes: M1 V 5.2X4&apos; / XQ Z 0.746 X 100 X 87.60 X C V 60 X E ) The amortization rate a dollars per year per dollar invested includes both depreciation and interest on the investment. These in turn involve the expected useful life of the airshaft and available molletary interest rate. For the purpose of this discussion the cost of airshaft sinking is assumed to comprise a fixed move-in charge Y dollars, which covers the cost of transporting, erecting and removing the shaft-sinking equipment and is independent of the air-shaft size. Also, it is assumed that the cost of shaft lining, if any, is fixed at $X per cu. yd. of lining material and that excava-

Jan 1, 1947

By J. D. Lubahn

The Bauschinger effect, or rounding of the corner of the stress-strain curve upon reloading, represents a temporary apparent softness that is more pronounced at large strains than small and for complete unloading than for partial unloading. Interrupted creep tests on copper exhibit a similar temporary softness (high creep rate) upon reloading. The fact that the strainwise dying-out time of these effects is the same in both tensile and creep tests shows that they are related. Thus, the term Bauschinger effect appears to embrace behavior following partial or complete unloading and reloading in addition to behavior following reversed loading. It is suggested that the term may properly apply also to certain creep behaviors following a small load decrement. INTERRUPTED tensile tests at low temperatures show1 a rounding of the corner of the stress-strain curve for reloading, which indicates a temporarily low deformation resistance. In the absence of recovery, the curve soon rises to the value that would have prevailed if the test had not been interrupted. The rounding of the reloading tensile curve has sometimes been referred to1 as the Bauschinger effect, although the term is more commonly applied to low deformation resistance in compression following tensile prestrain. The unusually broad usage of the term Bauschinger eflect in ref. 1 seems justified by the obvious interconnection of the various behaviors to which it has been applied.&apos; In fact, the following discussion will indicate that still broader usage might be desirable. The Bauschinger effect is common at room temperature but apparently disappears at higher temperatures.2 Interrupted creep tests and tensile tests were made on certified OFHC copper (nongaseous impurities exclusive of silver were 0.004 pct), cold drawn 84 pct to ½ in. diam, and annealed at 600" (about 0.025 mm grains) or 850°C (about 0.2 mm grains). The tests were made in standard creep or tensile machines, using an O.S. Peters microformer-type extensometer or, for the small plastic strains, a special arrangement employing General Electric magnetic gage heads.&apos; Interrupted creep tests at room temperature show3,4 an initial softness after reloading, manifested by an initial creep rate that is higher than that which would have prevailed if the test had not been interrupted. Fig. 1 shows some typical examples. This effect is apparently temporary (as is that in tensile tests): in four of the five tests shown, the log rate vs strain curve becomes parallel to an

Jan 1, 1956