Search Documents

By S. Rick Gilbert

In the course of producing a final metal product, smelters, refineries, and other metallurgical facilities produce wastes which often come under the ?scrutiny of Federal and state regulatory agencies. Many of these wastes contain combinations on zinc, copper, lead, cadmium, nickel or other metals. Frequently in the form of reverts, dusts, or sludges, these metal-containing wastes are often buried in a landfill or speculatively accumulated for future action. Environmental liability can be reduced in many cases by selecting,-a recycling facility which can re-process the waste for.' metal recovery. Encycle, at its hydrometallurgical facility Corpus Christi, has Successfully processed a variety of metallurgical by-products and wastes and returned those contained metals to commerce.

Jan 1, 1995

By Zhijing Zhang

A thermodynamic structure model for alkali borate melts is developed to describe the distribution of structural groups in the alkali borate melts as a function of compositions. Fractions of threefold coordinated boron atoms and fourfold coordinated boron atoms in the potassium borate melt are calculated for the entire composition range and compared with results reported in the literature. The model has been used for structural interpretation for the borate anomaly in viscosity, which regards the borate anomaly as a manifestation of the various antithetical effects caused by the introduction of alkali oxide into boric oxide. It has been found that the viscosities of alkali borate melts increase or decrease according to the changes in rigidity and spatial connectivity of the glass network structure, which is a function of temperature and composition.

Jan 1, 2001

By Tiejun Chun, Marcus Emrich, Jian Pan, Deqing Zhu, Vinicius Mendes

"Joint projects of studies of hematite acid pellet have been implemented to develop technological solutions for using Vale hematite pellet feed in Chinese palletizing plant. Beneficial improvements on the pellets quality were achieved by adjusting the blends composition and using new technology of pre-treating the blended pellet feed with HPGR (High Pressure Grinding Roller) on rotary kiln pellet technology. The drop strength of green balls increased from 3.4 to 6.0 times from 0.5m height, at the same time, the bentonite dosage decreased from 1.5wt% to 0.7wt%. The compressive strength of roasted pellets reaches 2500 N/pellet. The reduction swelling index of roasted pellets is below 15%.IntroductionWith the fast development of steel industry in China, the production of pellets has been further expanded. Pellets are used as a high quality charge for blast furnace and the annual output is around 80Mt pellets [1]. According to the developmental trend, sinter will be replaced by pellets due to the larger environmental impact of sintering plants when compared to pelletizing plants. For example, the specific CO2 emission in sintering process is around 2.5 times higher than in pelletizing process. However, the steel industry of China has been confronted with a serious shortage of domestic pellet feed due to the low iron grade of Run-of-Mine ore despite of huge reserves of iron ores [2]. Therefore, more pellet feed, mainly hematite, has been imported to make pellets."

Jan 1, 2011

By J. Kevin Cotchen

The results of "submerged arc" electric furnace processing of a variety of materials is discussed with respect to the process and products, including the characteristics of the products (e.g. TCLP or Toxicity Characteristics Leaching Procedure). The materials melted include slags and wastes containing various metal oxides including copper, tin, lead, zinc, chrome, nickel and other associated elements. The findings of these tests are compared to those reported in the literature for other operations treating similar "wastes".

Jan 1, 1992

By Bemd. E. Langner

At Norddeutsche AfFmerie the CollaMat is an important instrument for controlling the activity of glue in copper electrolyte. Thanks to on-line measuring of the glue activity appropriate action can to taken in the event of sudden changes, such as an intemption in the glue supply, as well as long-term trends, such as continuously decreasing glue activity over days or weeks. Laboratory tests on the dependence of glue degradation on temperature have shown that relatively small increases in temperature of only 3OC cause the half change value of the glue degradation to reduce by 25 %. It is a similar picture with the sulphuric acid concentration in electrolyte. An increase in the acid concentration from 160 g/l to 200 g/l can - depending on the temperature - likewise result in a decrease in the half change value of up to 25 %.

Jan 1, 1995

By N. Tsuneyama

Sumitomo Metal Mining Company has been operating Waelz Kiln at the Shisaka Works for 12 years to recover zinc and lead from electric arc furnace (EAF) dust. To increase the capacity and cut down the operating cost, some improvements have been carried out resulting in the capacity of 60,000 t/ y of EAF dust as compared with 32,000 t/ y in 1977. The current capacity is equivalent to 20% or EAF dust generated in Japan. The number of workers has been decreased by the introduction of an automatic control system, and the productivity per worker is now twice as much as 10 years ago. This paper will describe the progress of the operation at the Shisaka Works after the previous? paper reported in "Zinc' 8 5? and summarize the status or EAF dust recycle in Japan.

Jan 1, 1990

By Sutham Niyomwas

Biomorphic Cellular TiCIC ceramics were produced by vacuum-infiltrating carbon preforms with Ti02 sol and subsequent synthesis by the carbothermal reduction process. The carbon preforms used in the study were obtained by pyrolysis of parawood and neem wood. The effect of infiltration time on the composition and microstructure of the biomorphic TiCIC ceramic was analyzed by X-ray diffractometry and scanning electron microscopy. The biomorphic structure of the TiCIC ceramic is consistent with that of the biotemplate natural parawood and neem wood.

Jan 1, 2008

By Lauri E. K. Holappa

Ferrochrome, as the central constituent in stainless steels is one of the most rapidly growing primary metallic products. In this contribution results of a comprehensive study on the reduction process of chromite ore to FeCr are presented including thermodynamic examination, experimental work on kinetics and mechanisms in solid state, and smelting reduction conditions as well as kinetic modelling of solid state reduction.

Jan 1, 1999

By K. G. Wang, M. E. Glicksman, P. Crawford

"We formulate the mathematical solution to late-stage multi particle diffusion in finite systems. The transition from finite system behavior to that for an infinite system is established. Large-scale simulations are reported regarding the dynamics of phase coarsening. Even in the case of a small volume fraction (Vv = 10-4), the particle size distribution is broader than that for the well-known Lifshitz-Slyozov limit at zero volume fraction. We also report the first simulation studies of extremely low volume fraction, for which corresponding experiments, as well as other simulations, do not exist at present for comparison. However, in the case of moderate volume fractions (Vv = 0.1), the fiucutations in the volumetric growth rate of particles are extracted from our simulations. These simulations provide additional insight into the statistical nature of diffusion interactions, including multiparticle stochastics during microstructural evolution.IntroductionPredicting microstructure evolution in alloys remains one of the cornerstones of materials science. Phase coarsening is a common process in microstrucural evolution that leads to a decrease in the excess total interfacial energy of the system. The system typically consists of separate and identifiable units, or domains, such as second-phase particles distributed in a matrix. During phase coarsening, larger particles grow at the expense of small particles. Over time, this ""competition"" results in an increase in the average size of the particle population, and in a concomitant decrease in the number of particles.Particle size and microstructure of many cast alloys depend on similar coarsening processes. Indeed, properties of these materials, such as strength, toughness, ductility, and electrical conductivity, depend on the material's average particle size and particle size distribution (PSD). Understanding and controlling microstructures in two-phase systems are clearly of widespread technological importance."

Jan 1, 2001

By S. N. Ojha, Gouthama, R. K. Mandal

"Spray deposition processing of liquid immiscible alloys, based on AI-Pb and Cu-Pb systems have been investigated. Process variables have been optimized to generate uniform dispersion of ultrafine second phase particles in· the matrix of the primary phase. Mechanisms governing the microstructural evolution in this synthesis methodology are discussed. Results of the present investigation are used to demonstrate that rapid solidification of atomized droplets initially provides a high nucleation rate of the second phase during the liquid phase separation. The solid matrix phase nucleates at a later stage and grows with a high velocity enabling trapping of the dispersed phase. Subsequent alteration in the size and size distribution of the second phase is suggested to arise further during deposition of high velocity droplets. Possible reasons for this effect are brought out. Microstructural features of atomized powders and spray-deposits of these alloys are presented to support the present approach of synthesizing composites. IntroductionIn recent years, synthesis of advanced materials with metastable microstructures and ultra fine dispersion of second phase particles has led to the development of novel techniques of materials processing. The other requirement of such a processing methodology is to achieve near-net shape geometries in less number of processing steps. The solidification processing method via spray deposition route qualifies these criteria. This process primarily involves atomization of a melt by high energy gas jets into spray of droplets which are subsequently propelled by the kinetic energy of the gas towards a deposition substrate to build-up a thick high density preform. Although the concept of spray deposition was pioneered by Singer [1] in the early seventies, the fundamentals of the deposition process has been understood only recently [2-4]. Several benefits of spray deposition processing are by now well established [5,6]. Rapid solidification effects are inherent in spray deposition processing due to high heat exchange rate at the droplet-gas interface and also on the deposition surface by force convection. Since considerable heat extraction occurs from the atomized spray prior to droplet consolidation, a relatively low processing temperature is ensured in this process. As a result deleterious coarsening phenomenon can be minimized. In addition, controlled maneuvering of the substrate provides the capability of the process in producing disc, sheet or tube shape preforms of difficult to work materials in a single operation. A significant improvement in properties, resulting from microstructural homogeneity and refinement in grain size induced by spray deposition has been reported for several alloy systems [7,8]."

Jan 1, 1994

By J. P. Gu, C. Beckermann

"Melt convection and macrosegregation in casting of a large steel ingot is numerically simulated. The simulation is based on a previously developed model for multicomponent steel solidification with melt convection, and involves the solution of fully coupled conservation equations for the transport phenomena in the liquid, mush, and solid. Heat transfer in the mold and insulation materials, as well as the formation of a shrinkage cavity at the top are taken into account. The numerical results show the evolution of the temperature, melt velocity, and species concentration fields during solidification. The predicted variation of the macrosegregation of carbon and sulfur along the vertical centerline is compared with measurements from an industrial steel ingot that was sectioned and analyzed. Although generally good agreement is obtained, the neglect of sedimentation of free equiaxed grains prevents the prediction of the zone of negative macrosegregation observed in the lower part of the ingot. It is also shown that the inclusion of the shrinkage cavity at the top is important in obtaining good agreement between the predictions and measurements.IntroductionMacrosegregation in large steel ingots is one of the most well-known and now classical problems in the field of solidification and casting [1]. Commonly found macrosegregation patterns in steel ingots are a positively segregated zone at the top, negative segregation near the bottom in the equiaxed zone, inverse segregation near the ingot surface, V-segregates along the centerline, and A-segregates in the columnar zone [2, 3]. It is well established that the macroscopic transport of species leading to macrosegregation can occur by a variety of mechanisms, including thermally and solutally driven natural convection of the melt in the mushy zone, flow due to solidification contraction, and the sedimentation of free equiaxed crystals. Fredriksson and coworkers [ 4,5] provide recent overviews of the solidification transport phenomena and macrosegregation in ingot casting."

Jan 1, 1999

By Stephen Gale, David Clarry, Edmund Smith, Jon Feldman

"In 2006, a Canadian steel maker embarked on an ambitious initiative to become “Best in Class in Energy Management”. This initiative provides the framework for this paper, with some augmentation from other energy management projects carried out by Hatch. The initiative focused on identifying energy/GHG management improvements leading to low-cost implementation of energy savings or GHG emission reduction. The key components of the approach were:• Review site energy management practices and benchmark internationally.• Review best technical practices and benchmark against public energy intensity data.• Conducted a site-wide Energy Assessment and physical review of operating areas.• Facilitation of on site-workshops with staff to prioritize savings opportunities, as well as identify and remove implementation barriers.• Development of an Energy Management Action Plan for implementation of improvements.Most organizations can produce, with relative ease, a list of ideas for saving energy, implementing them is the challenge. This paper addresses these issues as well as the profitability of the energy efficiency improvements and the consequences for GHG emissions.IntroductionWhen one of the authors was an undergraduate engineering student at the University of Cape Town in South Africa, the technical drawing instructor made a statement that was both humorous, and mildly profound. He claimed that the most successful engineer is one who is both lazy and diligent. Lazy, in the sense that the engineer is constantly on the lookout for an easier, more efficient, way to do something. Diligent, in the sense that the engineer will work tirelessly to come up with a good technical solution for the easier way. This paper, somewhat of an anomaly in a compilation of technical proceedings, hopes to break the mould a little, and to show a “lazy-diligent” way of reducing the carbon emissions from an industrial facility, using a steel plant as an example."

Jan 1, 2008

By Batric Pesic

Reactions of metallic iron were studied in several different aqueous solution systems: water, medium salt solution used for the growth of T ferrooxidans, ferric iron solution and solution containing T ferrooxidans. Each system was studied under abiotic and biotic conditions in the presence of T ferrooxidans and as a function of pH, particle size of iron powder, temperature, ferrous and ferric iron concentrations. It was found that metallic iron reacts with water differently than does with ferric iron in water. Surprisingly, T ferrooxidans were non-functional in the dissolution of metallic iron. Also, the reactions of metallic iron with pure water were indistinguishable from the reactions with water containing medium salts for bacterial growth. The reactions with ferric iron were also independent of medium culture compounds. The mechanisms of metallic iron reactions with ferric ions are different from the mechanisms of metallic iron reactions with water.

Jan 1, 2001

By Selim Coskun

In this study, tungsten matrix composites reinforced with 2 wt% TiC particles were mechanically alloyed (MA?d) for 3h, 6h, 12h and 24h. 1 wt% Ni is used as sintering aid which is added before and after mechanical alloying. Microstructural and phase characterizations of composite powders and sintered samples were carried out via SEM and XRD analyses. Furthermore, density and hardness measurements of as-consolidated and sintered samples were carried out. Additionally, DSC experiments were conducted to investigate the sintering behavior of the MA?d powders.

Jan 1, 2009

By R. Luo, R. V. Kumar

"The co-deposition of cobalt and nickel as a binary alloy has been studied by both cyclic voltammetry and long-period controlled-potential electrolysis. Cyclic voltammetry experiments showed that the cathodic current density for the mixed Co-Ni (Co-Ni=1:3) electrolyte is noticeably higher than that obtained on electrolyte containing single CO2+ or Ni2+ (II) salt of the same ionic strength. The onset potential observed for the mixed salts electrolyte was also less cathodic (negative) than that for the single metal salts, respectively. The effects of a number of operational and compositional parameters on the co-deposition of cobalt and nickel were studied. The parameters under investigation include cathode (deposition) potential, temperature, CI-/Sol ratio in the electrolyte, the amount of additives such as H3B03, and acidity of the electrolyte.Optimum operational conditions were established for the deposition of cobalt and nickel binary alloy. These results are discussed with respect to feasibility of reclaiming cobalt, nickel and chromium from mixed superalloy scraps by melt-refining (under nitrogen and/or ammonia), followed by electrorerining of cast anode for co-depositing Co/Ni and thermal decomposition of chromium nitride for recovering chromium metal."

Jan 1, 1997

By Jintao Gao, Zhancheng Guo, Chong Li

A new approach to enrich MFe and RO phase from the converter slag by super gravity was investigated. The samples obtained by the gravity coefficient G=600 and cooling rate V=5K/min from 1623K to 1373K appeared significant stratification and the MFe gathered at the bottom of sample. With the help of metallographic microscopy and X-ray diffraction, it is found that large quantity of white RO phase gathered at the lower part of the sample as the concentrate, with volume fraction appearing gradient distribution along the direction of super gravity, while the upper part was mainly composed of dicalcium silicate as the tailing. The mass fractions of the FeO, MgO and MnO in the concentrate are up to 40.46%, 6.9% and 3.91%, while that in the tailing are just 11.65%, 2.15% and 1.55%. The recovery ratios of FeO, MgO and MnO in the concentrate are 60.35%, 58.45% and 72.24%, respectively.

Jan 1, 2016

By J. D. Miller

Gold adsorption from cyanide solutions by activated carbon has been studied at great length during the past decade. Findings from past research are reviewed and discussed with respect to structural features of various carbons, including carbon black, activated carbon, graphite and diamond.

Jan 1, 1991

By Elliot Schwartz, Julian Szekely

"In this paper we describe an experiment that was recently performed on the IML-2 Space Shuttle mission in which the thermophysical properties of molten metals were measured using electromagnetic levitation. In the planning of these experiments calculations had to be performed to predict the levitation and stirring forces, heating rates, sample deformation, and internal flows within the sample. These predictive calculations were essential for both the planning of the experiments and for the re-planning of experimental runs during the actual Space Shuttle mission.Introduction""Materials Processing in the Computer Age"" involves the use of mathematical modeling to obtain a quantitative understanding of the phenomena that govern materials processing operations. Microgravity, or space shuttle experimentation represents a specific case in point here; the very high cost of the space shuttle flights, the very limited flight opportunities that are available, and the tight resources aboard a shuttle clearly mandate that these experiments be very precisely planned and that all possible opportunities for mathematical modeling be fully exploited.The purpose of this paper is to present the results of calculations performed for the planning of a space shuttle experiment involving electromagnetic levitation and wherever possible present a comparison of the computational predictions with both experimental measurements and asymptotic analyses. Finally we shall seek to discuss the practical implications of both the computational methodologies and the potential experimental findings."

Jan 1, 1994

By Kenneth P. Michalek, James E. Kelly, Jonathan A. Dantzig

"Many investigations have been reported regarding the simulation of continuous casting with emphasis on in-mold heat transfer. These analyses have been limited, however, because they require either estimation or measurement of the characteristic heat transfer between the ingot and the mold. In this paper, a self-consistent model 'is presented for calculating the heat transfer between a solidifying continuous casting and the mold, in the context of the continuous casting of steel. Using both thermal and stress analyses, the air gap formed during continuous casting is calculated and used to compute the heat transfer coefficients. Iteration between the thermal and stress analyses is used to determine a self-consistent solution. IntroductionThe continuous casting process for steel is illustrated schematically in Fig. 1. Molten steel is tapped into a tundish from which it flows at a controlled rate into the continuous casting mold. The initial shell of the casting forms in the mold by transfer of heat from the metal through the mold wall to the cooling water. The remainder of the casting is solidified by application of water sprays, and/or radiation cooling below the mold.Heat transfer in the mold portion of the process is important because it controls the formation of various defects which are deleterious to subsequent processing. Examples of defects formed in this region are surface irregularities, such as cold folding and oscillation marks, and more serious defects, such as longitudinal or transverse cracks. A more catastrophic problem which may occur is a breakout, in which the shell ruptures and molten steel is discharged in an uncontrolled way."

Jan 1, 1986

By R. F. Hammen

Copper is one of the most widely used metals in industrial processes and is also present in most mining operations. Extraction of copper from solutions often proves difficult due to the presence of complexing agents. ChromatoChem, Inc. has developed a Solid Phase Extraction (SPE) support (HiPAC) for removal and recovery of metals from wastewater. The HiPAC SPE support employs chelating agents covalently coupled to a long linker molecule. Several solutions containing copper and complexing agents were tested including 1) copper and carbonate, pH 9.8, 2) mixed metals and anions with copper and cyanide, pH 11, and 3) copper and the chelating agent EDTA, pH 11. The copper was extracted from solutions one and two at high pH, but the EDTA containing solution needed the pH lowered to make the copper available for capture. In each example, the copper concentration was significantly reduced by HiPAC SPE treatment.

Jan 1, 1994