By Zhao-cheng Liu

Iron oxide red pigment powders of high quality were synthesized from pyrite cinders. Iron ox-ide red pigment powders were synthesized by hydrothermal method from the precursor of Fe(OH)3 and Fe(OH)2 colloid, which were obtained after ammonia solution reacted with acidic leaching solution produced by the reaction of pyrite cinders with sulfuric acid. Effects of reaction concentration, reaction temperature, reaction time, pH value and n(Fe2+)/n(Fe3+) on main properties of oxide iron red were studied by experiments. The prepared particles were characterized by means of X-ray diffraction (XRD) and scanning electron microscope(SEM). The results revealed that the synthesized iron oxide red particles were _-Fe2O3 and pseudocubic with particle size of 0.50~0.75µm. Furthermore, the quality of iron oxide red pigment powders reached the first grade of national standard (GB1863-89 ).

Jan 1, 2009

By Wellington Pereira Inácio

This work investigated the toughness behavior of polyester matrix composites reinforced with up to 30% in volume of long, continuous and aligned sisal fibers by means of Charpy impact tests. It was found that the addition of sisal fibers results in a marked increase in the absorbed impact energy of the composites. Macroscopic observation of the post-impact specimens and SEM fracture analysis showed that longitudinal rupture through the sisal fiber interface with the polyester matrix is the main mechanism for the remarkable toughness of these composites.

Jan 1, 2010

By Jorge Gibson, P. Chris Pistorius, Megha Jampani

Increased utilization of natural gas in blast furnace ironmaking can decrease both the cost and the carbon intensity of ironmaking, given current US natural gas prices. In this paper, three ways to utilize natural gas are compared: tuyère injection, prereduction of iron ore, and shaft injection. The basis for comparison includes coke replacement ratios, carbon intensity and furnace productivity. These were calculated using relevant mass and energy balances, a blast furnace productivity correlation based on the bosh gas flow rate, and measured and modeled prereduction kinetics. Of the natural gas utilization methods, prereduction has the highest effective coke replacement ratio (and hence the largest advantage in raw material cost), but is likely to have the highest capital requirement.

Mar 1, 2017

By Taufiq Hidayat

Accurate description of complex phase equilibria provide the foundations for the improvement of non-ferrous pyrometallurgical smelting and recycling processes. Recent advances in microanalysis and experimental techniques enable accurate phase equilibria characterisation. Quantitative microanalytical techniques including Electron Probe X-ray Microanalysis and Laser Ablation ICP-MS enable the concentrations of major and minor elements present in different phases in samples to be accurately measured providing data that cannot be obtained using bulk chemical analysis techniques. High-temperature equilibration experiments coupled with the subsequent analysis of elementary reactions at micro- and macro-scales ensure the attainment of equilibrium conditions, and therefore, ensure true phase equilibria information is obtained. Examples of the application of the improved methodology on the investigation of phase equilibria of low-order and complex, multi-component gas/slag/matte/metal/solids Cu2O–PbO–ZnO–Al2O3–CaO–MgO– FeO–Fe2O3–SiO2–S systems and the distribution of minor element are provided. The experimental study is closely integrated with thermodynamic database development for the above system. Example of implementation of the research outcomes into industrial operations is demonstrated.

By Taegong Ryu

Nanosized tungsten powder was synthesized by the hydrogen reduction of ammonium paratungstate (APT) in thermal plasma. The effects of operating conditions on the product composition and particle size were investigated. The particle size of synthesized W powder was less than 30 nm in all cases tested. The sintering behavior of the synthesized powder (25 nm average size) was then investigated and compared with those of commercial W powder of 500 nm average size and W powder of 23 nm average size produced by milling the commercial powder. The sintering was done at 1400oC with various holding times. The hardness of the resulting compact from the synthesized W powder (315 VHN) was similar to that from the milled W powder (309 VHN), but the plasma-synthesized powder had a much lower tendency to form cracks. The compacts of both nanopowders were significantly harder than that of the commercial powder (192 VHN).

Jan 1, 2009

By A. G. Merma

In this work, the electrocoagulation technique was studied in order to treat chemically stabilized concentrated oil-water emulsions. This study was mainly focused on the effects of operating parameters such as initial pH, current density, reaction time, electrode distance and inlet concentration on the separation of oil as measured by the chemical oxygen demand -1(COD) method. The synthetic emulsion was prepared from Shell - Talpa 30 oil (3g.L-1) and sodium dodecyl sulfate (1.0 g.L), having a Zeta potential around -70 mv at pH 8.7. The process was carried out in an electrocoagulation cell with a set of four parallel monopolar electrodes. This set consisted of two aluminum plate anodes and two 316L stainless steel plate cathodes. Kinetic curves showed that the electrocoagulation process exhibits three phases: (1) an initial phase, where the COD did not decrease because the solution had not reached the minimum amount of dissolved aluminum required to cause the break-up of the emulsion, (2) a reactive phase during which COD decreased due to possible agglomeration of the precipitates and (3) a steady-state phase where the COD did not change. The results showed that the period to reach the reactive phase decreased as the current density increased and the pH values decreased.

Jan 1, 2009

By WU Jian-hui

Keywords: metallic material; nickel powder; thermal decomposition; precursor; fibrillar powder; nanometer scale; passivation treatment The precursor thermal decomposition process of fibrillar nanometer scale nickel powder and passivation treatment of obtained powder are investigated, and the composition and morphology of the products are characterized by use of IR, TGA/DTA, XRD and SEM. The results show that the precursor morphology is a decisive factor to the product morphology of the nickel powder. The morphology of the product derived at low decomposing temperature is irregular. The nickel powders produced at the temperature higher than 480 coheres seriously. The product particles are reunited with the decomposition time prolong. The powder prepared under the optimal condition is fibrillar like woolen yarn; the grain diameter is less than 50nm.

Jan 1, 2005

By Run Huang, Xuewei Lv, Songli Liu, Chenguang Bai

"Titanium alloy was prepared from titania-bearing blast furnace slag (Ti-BF slag) by aluminothermic process in an induction furnace. The effects of aluminum amount on the titanium silicon yield and titanium recovery ratio were studied. The phase transformation and chemical composition of the prepared alloy were investigated by X-ray diffractometry (XRD) and X-ray fluorescence (XRF) respectively. It was found that the mass fraction of silicon and aluminum increased with increasing the aluminum amount, however, the mass fraction of titanium increased first and then decreased with increasing the aluminum amount. Furthermore, both the titanium alloy yield and titanium recovery ratio increased with the increase of aluminum amount. The main phases of the alloy were TixSiy and AlTi3. The titanium alloy samples prepared in various conditions had a composition (wt.%): 38–50% Ti, 29-34% Si, 4-11 Al%, 1.6-2.2 Mn%.IntroductionPanzhihua and Xichang regions in the southwest of China are rich in vanadium-titanium magnetite containing iron, vanadium, titanium and gangue. According to the characteristics of the resource, iron and vanadium are successfully recovered with a blast furnace process and a converter process. However, most content of titanium are entered in the blast furnace slag with TiO2 22% -26% and metallic Fe 2%–6% called Ti-BF slag. Due to the dispersed distribution of Ti in various fine grained mineral phases with a complex combination between Ca, Al and Si, it is difficult to recover the Ti components[1]. This slag is generated at a current rate of 3.6 million tons per year, which adds to the existing 70 million tons of slag produced so far[2]. The slag has had to be piled as large as the mountains, which not only waste of resources but also cause a pollution of the environment. Therefore, the study of integrated utilizing Ti-BF slag has become very significant."

Jan 1, 2012

By J. Phillip Mackey

A whole new group of non-ferrous pyrometallurgical processes with the ability to utilize tonnage oxygen and capture sulphur dioxide were developed and commercialized over the period 1940s–1980s. Many of these earlier process developments were undertaken with limited knowledge of the process chemistry and influence of key process variables; in many cases, piloting helped provide much new physico-chemical data, but gaps remained. The second generation versions of these technologies of today provide all the primary copper, nickel and lead produced worldwide by pyro-metallurgical smelting. Further, process development has continued and a new generation of copper and lead smelting technologies have also been developed in China since the 1990s. The older reverberatory and blast furnaces have been progressively replaced by the newer technologies—a good example being the introduction in 1992 of the copper IsaSmelt technology at the Mt. Isa smelter in Australia where the former fluid bed roaster and reverberatory furnaces were replaced by a single new smelting unit, together with an acid plant for sulphur dioxide collection. The development of these new technologies was made possible by investment in fundamental and applied research. The lesson for the future is, in order to sustain these improvements, continued investment in research and development capability is required—to do otherwise is to risk obsolescence and lack of competiveness in the world market. Dr. Peter Hayes at The University of Queensland is one of the many researchers and process engineers who have contributed to the fundamental understanding of metallurgical processes over this period of rapid change in technologies. The present paper briefly outlines some of the many contributions Peter Hayes has made to the understanding of kinetics, mechanisms and phase equilibria in metallurgical systems, and metallurgical process development.

By Youze Xu

The leaching and reduction of Cr(VI) in soils contaminated by chromium-containing slag were investigated with column experiments. The results showed that Cr(VI) concentration in leachate decreased from 988 mg L-1 to 407 mg L-1 after 7 days when water was used as leaching agent. However, Cr(VI) in leachate in culture medium treatment was not detected at above periods. In comparison, Cr(VI) concentration in leachate from autoclaved soil remained 398 mg L-1 at the end of experiment. The results indicated that the indigenous microorganism was capable of reducing Cr(VI). The amount of Cr(VI) reduction was 335 mg at the whole experiment period and the reduction rate was 67.09 mg d-1. Carbon supply showed minor effect on Cr(VI) reduction. However the reduction capability of Cr(VI) could be improved by combination of the carbon and the nitrogen. The optimal quantity was 5 g L-1 of yeast extract and 4 g L-1 of glucose.

Jan 1, 2009

By Jinwu Kang

The hydraulic turbine blade of the matensitic stainless steel (Cr13%,Ni5%,Mo1%) is a kind of large and curved shape, which is susceptible to deformation in both casting and heat treatment processes. The coupling analysis of heat transfer, phase transformation and stress in heat treatment process of the turbine blade for Three Gorges Project is carried out by using Deform-3D software. Its temperature fields, phase fields and stress fields in heat treatment process are obtained. And its deformation is predicted. In the cooling process of normalizing, the blade exhibits relatively large deformation. Based on the stress analysis and deformation prediction in heat treatment process, an algorithm for the determination of reverse deformation of the blade casting in heat treatment process is presented. And the reverse deformation distribution of blade is obtained.

Jan 1, 2010

By M. Potesser

One of the main targets in the automotive mass industry and supplying industry is the weight reduction of the vehicle for decrease of the fuel consumption. For that reason combinations of different kinds of materials and connections of, for example, steel and aluminium are developed or are already successfully field-tested. A determining factor concerning the quality assessment of the welded joint during hybrid welding is the characterization of the intermetallic Fe-Al layer regarding strength, hardness, morphology and mainly the different phases in which Fe occurs together with the Aluminum (FeAl, Fe2Al5, FeAl3.). A combination of conventional light microscopy, SEM - EDX - analysis, the usage of an atomic force microscope including a Nanoindenter and theoretical thermodynamic calculations turned out to be highly effective. Based on the attained results, the constitution of the intermetallic FeAl layer, influenced by silicon, manganese and zinc, can be predicted.

Jan 1, 2006

By J. Samir

The objective of this study is to simulate the isothermal filling up of moulds by a RTM process when adopting CV/FEM and VOF method and when also taking into account the presence of obstacles coupled to the effect of the thickness and reinforcement layers variation. The codes developed intended to ensure an optimal positioning of the injection points and of the vents and also to determine optimal injection pressures, in order to minimize the cycle times. These codes use a mesh generator proper to the team, allowing a discretization of the domain in triangular unstructured elements, with the possibility of a local refinement and inserts inclusion.

Jan 1, 2009

By M. Faraji

Inclusions formed in a high-carbon, manganese-silicon killed plain steel (Fe-0.77C wt%) were studied. Various techniques were used to characterise the inclusions, and the latter were classified according to their chemical composition, size and morphology. The main constituent elements entering the inclusions were Mn, S, Al, and oxygen. Alongside MnS and some Al2O3 inclusions many non-metallic inclusions appeared in complex forms, consisting of silicates, sulphides and oxides. Duplex oxy-sulphides, mainly MnS combined with Al2O3, or SiO2 were the most common complex multiphase inclusions in this steel. The nanoindentation technique was used to assess and rate different types of inclusions and data of the hardness and elastic modulus of individual inclusions at room temperature are presented.

Jan 1, 2010

By Qingwei Wang

This study focused on acidic wastewater from producing sulfuric acid system in zinc smelter containing mercury 21.48mg/L, zinc 55.85mg/L, lead 38.50mg/L, copper 1.68mg/L, cadmium 10.25mg/L, As 29.86mg/L treated by biologics. The factors of pH value, the ratio of biologics to mercury, complexing time, hydrolytic time and temperature were studied in this paper. Experimental results indicated that at pH value 10, quantity of biologics to mercury ratio was 16, complexing time 30min, hydrolyzation time 20min, temperature at 40?, concentration of mercury in treated water was removed to 22.15µg/L. At same time heavy metals such as Zn, Pb, Cu, Cd, As was removed by biologics, the remained concentration in treated water was Zn 0.53mg/L, Pb 0.12mg/L, Cu 0.01mg/L, Cd low to 0.01mg/L and As 0.023mg/L. According to EDAX analysis, mercury content in complexing sediment reached 28.49% easily to recycle as raw material and low concentration of heavy metals in hydrolytic sediment easily to dispose and treat.

Jan 1, 2009

By Napisporn Memongkol

Syntheses of Al-TiC-Al2O3 and Al-SiC-Al2O3 composites were obtained in situ by carbothermal reduction of mixtures of Al powder, TiO2 powder and activated carbon powders and Al powder, SiO2 powder and activated carbon powders. The reductions were carried out in a horizontal tube furnace under flow of inert gas. The standard Gibbs energy minimization method was used to calculate the equilibrium composition of the reacting species. The synthesized products were mixtures of aluminum reinforce with titanium carbide and alumina and aluminum reinforce with silicon carbide and alumina. The effect of the reaction temperature (1000 o C ? 1200 o C) and condition of precursors on the Al powder, TiO2 powder and activated carbon powders and Al powder, SiO2 powder and activated carbon powders were investigated using XRD and SEM method. The synthesized products showed those composites with aluminum matrix and titanium carbide and alumina as reinforced phases and aluminum matrix and silicon carbide and alumina as a reinforced phase was formed.

Jan 1, 2006

By K. Morsi

Carbon nanotube (CNT) reinforced metallic composites have been recently generating significant scientific interest, due to their expected superior properties compared with other composites. Out of the metallic matrices investigated for reinforcement with CNTs, aluminum has received considerable attention. A major problem has been the dispersion of CNTs in metallic matrices. This paper discusses preliminary results on the mechanical dispersion of CNTs in aluminum powder, powder processing, stability and characterization of aluminum dispersed with CNTs at reinforcement levels equal to and below 5 wt.%.

Jan 1, 2009

By Mark Osborne, Ray D. Peterson, C. Edward Eckert

"The theoretical melting energy requirement for a typical hypoeutectic aluminum-silicon alloy is approximately 520 BTU/lb. It has been demonstrated, however, that even a state of the art secondary processing-automated lost foam casting operation can exceed this value by at least an order of magnitude when the actual thermal energy input from melting to solidification is monitored. Metal transfer and holding operations constitutes over 65% of this expenditure. The authors present relative benchmark energy expenditure information by unit operation for an offsite melting/lost foam casting line with a daily throughput in excess of 100,000 lbs. Efficiency improvements through optimization of the current process, and anticipated energy values at the culmination of a U.S. Department of Energy sponsored project to develop, integrate and demonstrate an advanced melting, transportation, and dispensation system will be cited.IntroductionThe size of the U.S. aluminum remelt pool was approximated to be 14.21 billion kg (31.27 billion pounds) by a recent study?, with the engineered castings (foundry) sector accounting for 3.25 billion kg (7.16 billion pounds) or 23% of that total. This study considered overall process yield and all major contributors to scrap. The values cited, therefore, are more meaningful than simply tabulating annual pounds shipped by sector.The foundry sector consists of Sand Castings, PM Castings and Die Castings categories appearing in Figure 1. All other categories comprise the wrought alloy sector. Wrought alloy production enjoys an energetic benefit from both scale and a relatively continuous operation. Many foundry operations, however, operate in batch mode at less than design metal throughput with characteristically longer melt holding periods. Since any detention of molten metal beyond melting represents an overhead use of energy, melt holding (secondary) energy expenditures can appreciably inflate melting energy requirements in the foundry."

Jan 1, 2009

By P. J. Mackey

Over the course of Dr. Robertson’s career, the ferrous and non-ferrous plants have seen enormous changes in technology and increases in plant capacity, essentially amounting to a “technological revolution”. In iron and steel, the “mega” blast furnace of some 6,000 m3 working volume is now standard (~10,000 tonnes (mt) of pig iron/day). Similar huge changes in process technology and plant size have occurred in the non-ferrous industry. As an example, the fuelfired reverberatory furnace, once the mainstay of the copper industry, has disappeared - replaced by large capacity flash and bath smelting technologies. The energy consumption per unit mass of metal produced has also been reduced considerably. Our understanding of the thermodynamics and mechanisms of metallurgical reactions, a field to which Dr. Robertson has significantly contributed, has made great strides. This paper reviews these changes with particular reference to the copper smelting industry, providing also comments on expected future trends.

Jan 1, 2014

By Yushiro Hirai

Saganoseki smelter & refinery had operated two flash smelting furnaces from 1973, attaining 330,000 mtpy of copper production in 1989. In 1996, however, it carried out a "integration of two flash furnaces". That is, it doubled the feeding capacity to one flash furnace to shut down another furnace while maintaining the same production. Single flash furnace operation has successfully started in March 1996 accomplishing a great reduction of the total production cost. The production had reached to 350,000 mtpy in 1997, and further increased to 450,000 mtpy by executing the expansion program with single flash furnace in 1998. This paper introduces results of the single flash furnace operation and describes about an outline of the expansion.

Jan 1, 1999