By G. A. Alers, J. H. Bechtold, R. W. Armstrong

The plastic flow of .molybdenum was studied in compression at temperatures below the ductile-to-brittle transition in tension. It was found that molybdenum is ductile in compression at all temperatures down to —196°C. The yield strength continues to increase with decreased test temperature below the tensile ductile-to-brittle transition temperature range. Difficulty was encountered in correlating the experimental data obtained with existing theories of plastic flow. THE body-centered-cubic metals as a group show a rapid and very large increase in yield strength with decreasing test temperature.' It is of fundamental importance to the understanding of the mechanism of plastic flow that this general characteristic be examined carefully. Unfortunately, brittle fracture in low-temperature tensile tests prohibits the measurement of flow properties at very low temperatures. By using compression tests, fracture can be suppressed and the plastic flow of the bcc metals can be studied far below their tensile ductile-to-brittle transition temperatures. Molybdenum was chosen for this experiment and plastic-flow data were obtained down to —196°C.

Jan 1, 1959

By Chauncey L. Berrien

The United Verde Copper Company's mine is at Jerome, Ariz. The orebodies arc of the schist replacement type, the main sulfide mass being a large lens-shaped body approximately 7 acres in cross-sectional area. In general, the mineralization is found along the iron schist contact, with the orebodies extending about 1000 ft. along this contact and varying from a few feet to 250 ft. in width. Three types of ore are mined; schist porphyry and the so-called "heavy" or "massive sulfide" ore. Approximately 50 per cent. of the total tonnage mined at present is of the latter class. A representative analysis of this ore indicates 42 to 46 per cent. sulfur. Because of the high sulfur content, blasting in this ore is an extremely hazardous operation. not only does it endanger the lives of men who may be in the mine at blasting time but it also becomes a potential fire menace when timber is in close proximity to shots being fired in these massive sulfides. The origin of the fires of 38 years ago, embers of which are glowing to this day, may perhaps be attributed to dust explosions due to blasting in the massive sulfides of those early square-set stopes. Dust Explosions Dust explosions in coal mines are a common source of mine disasters. That such explosions may be of common occurrence in metal mines is not generally known, but it is known that metal-mine dust will explode and such explosions have been investigated by the U. S. Bureau of Mines at the Pittsburgh Experiment Station. Samples of "heavy sulfide" ore from the United Verde mine were used in the tests. After studying the results of the tests it was concluded1 that: 1. Dust explosions were initiated in sulfide ore dust in the gallery with a charge of as low as 75 g. of 60 per cent. gelatin dynamite. 2. The exploding dust generated considerable pressure.

Jan 1, 1930

By William E. Ford, Edward Salisbury Dana

296. Definition of Specific Gravity. - The specific gravity of a mineral is the ratio of its density * to that of water at 4' C. (39'2' F.). This relative density may be learned in any case by comparing the ratio of the weight of a certain volume of the given substance to that of an equal volume of water; hence the specific gravity is often defined as: the weight of the body divided by the weight of an equal volume of water. The statement that the specific gravity of graphite is 2, of corundum 4, of galena 7-5, etc., means that the densities of the minerals named are 2; 4, and 7'5, etc., times that of water; in other words, as familiarly expressed, any volume of them, a cubic inch for example, weighs 2 times, 4 times, 7.5 times, etc., as much rn a like volume, a cubic inch, of water. Strictly speaking, since the density of water varies with its expansion or contraction under change of temperature, the comparison should be made with water at a fixed temperature, namely 4' C. (39'2' F.), at which it has its maxi- mum density. If made at a higher temperature, a suitable correction should be introduced by calculation. Practically, however, since a high degree of accuracy is not often called for, and, indeed, in many cases is impracticable to attain in consequence of the nature of the material at hand, in the ordinary work of obtaining the specific gravity of minerals the temperature at which the observation is made can safely be neglected. Common variations of temperature would seldom affect the value of the specific gravity to the extent of one unit in the third decimal place.

Jan 1, 1922

By Kenneth A. Moon

Kenneth A. Moon (U.S. Army Materials Research Agency)—The authors are to be congratulated for a very interesting and valuable paper. Their discussion of the structural implications of the results shown in their Fig. 5, however, requires a small correction. The model of Speiser and Spretnak with 0 = 1 and z' = 2 is perfectly reasonable for the Ti-O a phase, but Eq. [3] is valid only for solutions sufficiently dilute that the number of empty sites excluded by more than one filled site is negligible. The composition at which intrinsic saturation occurs therefore cannot be deduced from Eq. [3], but but must be decided by consideration of the structural details of the phase in question. In this case, intrinsic saturation is expected not at the composition Ti3O but at Ti2O, because Ti2O has the anti-Cd structurel4 for which each filled octahedral site has two nearby empty sites, one in the hexagonal plane immediately above it, and one in the similar plane below it. The other two models, with ?=1/3 and 1/2, imply a distinction between octahedral sites in pure titanium which is not easy to justify. The problem of extending Speiser's and Spretnak's treatment in a general way to more concentrated solutions will be the subject of a forthcoming publication by the writer. M. T. Hepworth and R. Schuhmann, Jr. (authors' reply)—The authors wish to thank Dr. Moon for calling to their attention the paper by Holmberg which presents the results of X-ray studies of Ti-O solutions ranging from 0 to 33 at. pct 0 and quenched from various annealing temperatures between 400" and 1800°C. Within these ranges, Holmberg found three types of phases: 1) At high oxygen contents (above 25 at. pct) and low annealing temperatures, he found the anti-Cd(OH)2 structure referred to by Dr. Moon. In this structure each titanium atom is in contact with 3 oxygens and each oxygen is in contact with 6 titaniums, the "available" oxygen sites corresponding to every other layer of octahedral sites in the titanium matrix. The limiting composition is Ti2O. However, this anti-Cd(OH)2 structure was not observed for samples containing 25 at. pct 0 or less. 2) For the specimen containing 25 at. pct 0 annealed at 400°C an ordered Ti3O structure was observed. This structure is related to the anti-Cd(OH)2 structure but differs from it by providing only two oxygens adjacent to each titanium atom and thus is consistent with the model represented by Eq. [5] in our paper, with 6 = 1/3, z' = 0. 3) For dilute solutions and for more concentrated solutions annealed at higher temperatures, the structure corresponds to that of the metal with random distribution of oxygens among all the octahedral sites. Thus, it is interesting to observe that the thermo-dynamic indications of ordering in the vicinity of Ti3O can now be supported qualitatively at least by Holmberg's X-ray evidence of the existence of an ordered phase of the composition Ti3O. That is, for solutions with oxygen contents close to that of Ti3O, both the thermodynamic data and the X-ray data are more consistent with models based on the ordered structure of Ti3O than they are with the model which Dr. Moon suggests corresponding to "intrinsic saturation" at Ti2O.

Jan 1, 1963

INTRODUCTION The geology of porphyry copper deposits in the southern Cordilleran orogen is the subject of this chapter. The area considered extends northwest from southern Mexico to the Columbia volcanic plateau, the Cascade volcanic province, and the Idaho batholith. Transversely it is a belt some 800 km (500 miles) in width bounded on the west by the Sierra Nevada range. Included within this area are many large segments considered unfavorable for hosting porphyry copper deposits, which are mentioned in the text. The region and its porphyry copper deposits have probably been more intensely studied and reported in the literature than any other area in the world. This summary considers regional geologic controls that governed formation of porphyry copper deposits within this province. Geologic factors that influenced the mineralogy and metallogeny of the deposits are also examined. Discussions with H. R. Cornwall have greatly helped in writing this section. GEOLOGIC SETTING The geologic setting has been summarized by Anderson (1966), Burchfiel and Davis (1972), Rogers, et al. (1974), and Lowell (1974). No porphyry copper deposits in this area are known to be pre-Triassic, so Mesozoic and Tertiary events will be stressed. Figs. 40 and 41 show basic data believed most pertinent to the topic of porphyry copper deposits. Pre-Middle Jurassic: Figs. 40 and 41 contain the principal structural and crustal ele¬ments found in the Cordilleran orogen after Anderson (1966), Schmitt (1966), Coney (1972), Rogers, et al. (1974), and Lowell (1974, 1976), together with location of some of the more important porphyry copper deposits. The western limit of the Precambrian craton is shown in Fig. 40 (Rogers, et al., 1974). East of that limit the crustal environment through which the porphyry copper plutons ascended includes the Precambrian basement as well as varying thicknesses of Paleozoic shelf and platform accumulations. The northwestern and western portion of the southern Cordilleran orogen west of the Rogers, et al. (1974) limit of Precambrian basement has what Churkin (1974) calls a thin continental crust. Brooks (1976) and Churkin (1974) describe oceanic volcanic

Jan 1, 1978

By J. D. McBeth, G. M. Potter, Ramon Pizarro

Heap leaching is used by the Carlin Gold Mining Co., Carlin, Nev., to supplement conventional processing of gold ore by agitation-leaching and countercurrent decantation. Selected open-pit ore containing about 0.072 oz Au per ton is crushed to 3/4 inch, dumped by truck on an asphalt pad, and leached by sprinkling with dilute cyanide solution for 7 days. The heap is then drained and removed by front-end loader to tailings disposal. About 70 percent of the gold is dissolved. Leach solution from the heap joins the pregnant solution from countercurrent decantation for gold recovery by zinc precipitation. Four leach pads, each with a capacity of 1,400 tons of ore, are in use. About 10,000 tons of ore are heap leached monthly from about April through October. Heap leaching is recessed during freezing weather. Labor, equipment, and reagent requirements for heap leaching are presented.

Jan 1, 1974

By C. A. Heiland

FOR the past three years, the senior writer has carried out, with inter-ruptions, a series of investigations into the characteristics of prospecting seismographs of a wide variety of construction. Early in 1932, a com-plete equipment was developed for both refraction and reflection observa-tions; its first function being, however, the application in reflection shooting. The performance of the equipment proved to be highly satis-factory in a series of field tests' which were carried out by the junior writer, whose services were loaned to the Colorado School of Mines by courtesy of the Plains Exploration Co. in Denver. The various problems that were encountered in the construction of the equipment, in its application in the field, and in the interpretation of the results, are fully treated in Publication 47 of the Department of Geophysics of the Colorado School of Mines. Its first part deals with the various problems encountered in the design of the instruments, and presents a discussion of such topics as the free and forced oscillations of damped and undamped mechanical seismographs, the action of oscil-lographic recording instruments and amplifiers, the characteristics of electromagnetic seismographs, and the requirements of damping, natural frequencies and static magnification for the pickups, amplifiers and oscillographs used in refraction and reflection seismographs. Further-more, a detailed discussion of the various methods of static and dynamic tests of seismic receivers, and a description of the reflection equipment developed at the School of Mines is presented. Unfortunately, a delay has occurred in the publication of the first part of this investigation concerning the instrument problems. There-fore, the second part, dealing with the field problems, is herewith pre-sented first.

Jan 1, 1933

By W. H. Emerson

In the summer of 1894, a specimen of corundum from Acworth, Ga., which mas reputed to be of markedly inferior quality for the manufacture of corundum-wheels, was received by the Geological Survey of Georgia, with the request that it be analyzed, in order to ascertain whether this inferiority was associated with any peculiarity of composition. In its appearance there was nothing uncommon, though it seemed to be rather easily scratched with a knife, while, at the same time, it scratched agate easily. An analysis gave the following results: Alumina, 94.58; silica, 1.77; magnetic oxide of iron, 0.69; calcium oxide, 0.44; and water, 2.51 per cent. There is nothing unusual in this composition, except the amount of water, which is usually, in southern corundum at least, from 0.3 to about 1 per cent. Concerning this corundum, the Mineral Resources of the United States, 1893, pp. 676 and 677, Bays: "It is supposed that this variety of corundum contains a little water, as it is

Jan 1, 1900

By E. Hornbogen

Discontinuous precipitation in a iron can occur by at least two different mechanisms. These mechanisms are compared, using observations made on an Fe-22 at. pct Zn alloy and an Fe-19.5 at. pct Mo alloy. In the Fe-Zn alloy, precipitation began on grain boundaries. These boundaries moved into the supersaturated solid solution, providing nucleation sites and an easy path for diffusion. The precipitated phase pew as lamellae, perpendicular to the PRECIPITATION reactions are called discontinuous if the nucleation of particles does not occur on individual sites in the supersaturated matrix.' In discontinuous precipitation, nucleation and growth occur on a reaction front that moves into the supersaturated solution and leaves a two-phase aggregate behind. The term cellular precipitation2 has also been used, but the term autocatalytic precipi- moving reaction front. The orientation of the depleted iron differed from that of the supersaturated iron. In the Fe-Mo alloy the growing precipitate particles apparently created dislocations in the growth front which served as nucleation sites. The precipitate grew on (110) planes of the iron, and growth occurred through volume diffision. The depleted iron retained the orientation of the supersaturated solid solution. tation seems to describe the nature of such reactions best. The basic effect of such a precipitation mechanism in a solid is that it is able to move or create sites that can catalyze nucleation. Such sites can be grain boundaries and dislocations. A mechanism of autocatalytic precipitation must, therefore, include some rational process by which a grain boundary may move into the supersaturated matrix or by which dislocations may be generated in front of the reaction. Discontinuous precipitation is always in competition with individual nucleation and growth of par-

Jan 1, 1963

By J. D. Verhoeven

The effectiue distriblltion coefficient has been Measured in a series of vertical, normal freezing experirtzents with large current densities passing through the solid-liquid interface. The results indicate that the effect of the current on solute redistribution is due to electvotransport in the liquid. The high currents produced extensive mixing in the liquid which was considerably reduced by solidifying in small lubing. Analysis of the convection indicates that it probably vesulls from a horizontal temperature gradient produced by the Joule heating- of the electvic crirver~t. Due to the strong dependence of this convection upon the specimen radius, it is conclnded that only for specit~ens with radii of less than somewhere between 1 and 2 mm wilt electric field freezing be getlerally effec-tire at enhancing the purification of zone-melting experittierats in loe-melting alloys. Experiments on 0.8-mm lubes illustrate some interesting potential applications of this techniqne as a means of solute control on smcrll specimens. In a number of papers published within the last few years'-4 it has been found that passage of large dc currents through the solid-liquid interface of a freezing alloy produces a change in the solute redistribution accompanying the solidification. It had been predicted theoretically by Hucke et al.s and by Pfann and Wagner that such an effect would occur as the result of electrotransport within the liquid boundary layer at the solid-liquid interface. These authors independently derived the following relation between the effective distribution coefficient and the variables of the process: Where k0 is the equilibrium distribution coefficient, V is the mobility of the solute relative to the solvent, E is the electric field intensity, D is the solute diffusion coefficient, R is the rate of interface motion, and 6 is the boundary layer thickness. Both groups of authors show that this equation predicts the possibility of extending the purification ability of zone-melting experiments by the addition of an electric current. However, there are other effects in addition to electro-transport which could be produced by the high dc current and might, perhaps, invalidate the applicability of Eq. [I]. For example, high electric current might affect the interface reaction or perhaps the equilibrium distribution which was assumed to exist at the interface. It was the purpose of this work to determine the applicability of Eq. [I] by systematically investigating a simple system for which all of the necessary parameters were known. It was of particular interest for speculating on the potential usefulness of this technique to determine the maximum practical field intensities obtainable, and the effect of these high fields upon convective mixing in the liquid. The initial work in this study was published in a previous paper3 which will be referred to as I. In that work, a current density of 2000 amps per sq cm was used with specimen diameters of 5 mm. The results gave a qualitative confirmation of Eq. [I.], and also showed that a large amount of convective mixing was produced in the liquid by the current. The present study is an extension of that work to smaller specimen diameters and higher current densities. Two points were overlooked in I and will be emphasized here: a) the value of ko has not been well-established in the Sn-Bi system and b) the observed convection could be due to thermal convection produced from the Joule heating. EVALUATION OF k0 To evaluate Eq. [ I.] it is necessary to know the value of the equilibrium distribution coefficient, k,. Tn I the value of k, was taken as 0.3 from a published phase diagram.7 According to ansen' the best data on the phase boundaries of the Sn-Bi system are those of Davidson.5 The data of Davidson give a k, value ranging from 0.21 to 0.25 for the compositions studied in this work, or an average value of around 0.23. In a recent publication, Rigaud and Tougas'10 determined ko by means of a solidification technique. For an alloy of approximately the same composition as that used in this work they obtained a ko value of 0.39. Hence, there is considerable uncertainty in the value of ko and, consequently, a series of experiments were made to determine k, more accurately.

Jan 1, 1968

By H. P. Willard, Conrad Martin

SINCE the deposits were found in 1927 in the Paradise Range of western Nevada, more than 1 mil- lion tons of magnesite and half a million tons of brucite have been mined and processed into a variety of granular refractory materials used as furnace linings by the steel industry. An additional million tons of magnesite were used during World War II to produce magnesium metal, and some magnesium oxide from the area is going into magnesia cements. Located near Gabbs, Nev., on the west flank of the Paradise Range, the principal bodies occupy an area a mile long by half a mile wide, and lesser occurrences have been found in a belt more than four miles long and in places almost two miles wide. Magnesite reserves containing less than 5 pct lime are estimated at more than 25 million tons. Reserves of better grade material are considerably less.

Jan 4, 1957

By P. F. MINISTER

AT Lime Spur, Mont., the East Butte Copper Mining Co. has been quarrying limestone for twenty years. The quarry is beside the Northern Pacific R. R. in the Jefferson River canyon, 4 ½ miles east of Cardwell, at Lime Spur, Montana. HISTORY This quarry was opened early in 1900 by Dan Morrison of Whitehall, the discoverer of the Morrison cave, to supply a demand for smelter flux. Limestone was sold to the Pittsmont smelter of The East Butte Copper Mining Co. and to the Butte Reduction Works. As no particular effort was made at the quarry to select the rock that delivered to the smelters was unduly high in magnesia and impurities. The East Butte com¬pany, therefore. Bought the quarry. in 1909 and confined operations to the high-grade beds in order to supply rock of the desired purity for its own smelter and the Butte Reduction Works until the latter shut down. It also developed a market for some of its rock with the sugar factories. The latter market increased until in later years all rock, larger than 4 in. in size over a bar grizzly, was being shipped to the sugar factories, and the rock smaller than 4 in. was being used as a flux in the blast furnaces at the Pittsmont smelter. In 1924, the East Butte concluded a contract with the Anaconda company for the treatment of its ores, and the Pittsmont -smelter -was shut down: which made the minus 4-in. rock a useless by-product. Since there was not enough revenue in the sugar rock alone and also because of limited waste room it became necessary, if Lime Spur was to continue to operate, to increase- the proportion of plus 4-in. rock and to develop a market for the minus 4-in.

Jan 1, 1930

By E. W. Cawthorne, R. I. Jaffee, C. M. Craighead

SOLUTION of a solid metal or alloy in a molten metal bath is used daily in melting operations, extractive metallurgical processes, and in brazing. It is generally recognized that temperature, time, agitation, and the composition of the solute metal and the solvent bath all affect solution rate. However, there is little information available in the literature on the kinetics of the process or the relative effect that these variables have on solution rate. In connection with an aluminum brazing study, data on the solution of aluminum in an A1-Si* bath to promote rapid solidification. The chemical analyses were made on drillings taken from the cast plates. The results of this work are listed in Table I. The thermal-analysis data were obtained on 200 gram samples cooled at approximately 1.5" per min. A calibrated chromel-alumel couple was used. The thermal arrests were recorded autographically on a General Electric photoelectric potentiometer recorder. The instrument was calibrated to 22.5 pct. The thermal emf was bucked with a Leeds and Northrup semiprecision potentiometer so that 1 mv represented the full scale of the GE recorder. Referring to Table I, it will be noted that the analytical results tend to be lower than the intended compositions by about 0.3 pct Si in the higher ranges. In view of the known difficulties in obtaining accurate silicon determinations by wet analysis when the silicon content is high and in view of the care that was employed in weighing and preparing the alloys, the intended compositions are believed to be more accurate than the analyses. Furthermore, when the thermal-arrest data are plotted against the intended compositions, a smooth curve is obtained, as shown in Fig. 1. This is not the case when the data are plotted against the analytical results. It will be noted from Table I that the 12.5 pct Si alloy (melt 4) showed a primary arrest at 577.6"C and the eutectic at 576.l°C. The metallographic examination of this chill-cast plate sample showed a small amount of primary silicon. These results, Fig. 1, place the eutectic at slightly less than 12.5 pct Si and are in rather good agreement with the unpublished Hanford data. In all of the subsequent work, the composition of the A1-Si dipping baths was determined by thermal analysis (spread between the primary arrest and the eutectic temperature) employing 12.5 pct Si and 577.2 °C as the composition and temperature of the eutectic. Material Preparation and Selection of the Techniques: At the beginning of this work, it was anticipated that, owing to oxide film present on the surface of the aluminum, difficulty would be encountered in obtaining rapid uniform wetting of aluminum specimens dipped in the A1-Si bath. The following etchants were investigated as possible methods of providing a thin uniform oxide film on the specimen surface: 1—phosphoric acid (H³O4), 2—fluoboric acid (HBFI), 3—sodium hydroxide (NaOH), and 4—hydrofluoric acid (HF). Tests with sheet .specimens (2x½x0.06 in.) of 2s aluminum prepared with these etchants indicated that the fast uniform wetting required for this work could not be obtained if any oxide film existed on the specimen surface. Tests were then conducted by dipping similar specimens etched in 5 pct NaOH and given a thin

Jan 1, 1956

By O. W. Ellis

CERTAIN alloys1 that, as a result of quenching, are retained in the form of homogeneous solid solution are known to increase in hardness and strength on standing at room temperature or on heating at slightly elevated temperatures. Other alloys" that, on rapid cooling, are held in the form of homogeneous solid solution (as, for example, certain steels) behave in like manner on heating to somewhat higher temperatures. The observed increase in the hardness and strength of these alloys, referred to as "aging" or as "secondary hardness," is widely accepted as being occasioned, either in whole or in part, by the precipitation in submicroscopic form of such constituents as were held in supersaturated solid solution as a result of cooling in excess of a certain critical rate. In earlier discussions of the cause of age hardening or secondary hardness, the question of the hardness of the precipitated particles does not appear to have been raised. At present, however, the general opinion appears to be that age hardening and secondary hardness are occasioned by the precipitation of hard particles within the supersaturated solid substance.3 The authors may be wrong in their belief that the last is a prevailing opinion. Nevertheless, it is thought that the following experiments,

Jan 7, 1924

By James Neale

FROM the beginning of its activities, the members of the National Production Committee have felt that the following points were essential to the success of its work: The operators must. feel that their operations were not 100 per cent. efficient; that they should be courteous and fair in their treatment of their employees; and that they should set an example of hard work and patriotic interest in increased production. Every move made must appeal to the sense of fairness of all parties concerned. The men must feel that in working more faithfully, and consequently producing more coal, they are rendering a distinct service to their Government in the time of its great need. As the workers feel that greater efficiency on their part results only in greater profits to the operators, the advantage to the operator should be lost sight of, as far as possible, and the advantage to the Government in fighting the war emphasized. Both operators and workers should know that the Government considered increased production an obligation, and opportunity for service, resting on both parties and not on the operators or the workers alone, and that both parties could very much better the efficiency of the pre-war period. Had the committee intimated that it thought the coal shortage was clue entirely to the idleness and inefficiency of the workers, its campaign would have failed, for the men would have resented the charge because only too frequently their efforts to produce more coal were thwarted by bad management; besides the operators would have lacked stimulus to better effort. On the other hand, had the impression been given that the committee thought that the coal shortage was clue entirely to bad management, the operators would have resented the charge because only too frequently their efforts to produce more coal were thwarted by the idleness and inefficiency of the workers; and the workers, having been thus indirectly pronounced 100 per cent. efficient and patriotic, would have lacked stimulus to better effort.

Jan 2, 1919

[ ]

Jan 1, 1938

By W. A. Lang, K. C. Gilbart, E. Stansfield

It has long been known that coal is unstable and oxidizes in air, even at ordinary atmospheric temperatures; also, that such oxidation affects the analysis of coal. Nevertheless little or no precaution is taken to prevent oxidation in the ordinary methods of analysis, and the possibility of error due to oxidation is sometimes ignored even in researches on coal. Although the general nature of coal oxidation is well known, and many workers have made careful studies of the rate of oxidation of different types of coal exposed to oxygen at different temperatures, yet the amount of oxidation coals undergo in the ordinary process of analysis, and its influence on the determined analysis, is not well known, and the published data are widely scattered through the literature. This paper is a collection, from this laboratory, of data that bear on the subject, together with a brief summary of three methods employed here to evaluate the oxidizabil-ity of coal. The post-Carboniferous coals of Alberta range all the way from anthracite down to lignite. As some of them are notably susceptible to oxidation, the necessity for care was early forced upon our attention, and oxidation has been reduced either by the removal of air with a vacuum pump or by the displacement of air with natural gas (methane). The two routine analytical operations most liable to involve oxidation are the preliminary, partial drying of the crushed coal (called air-drying) and the determination of moisture. The first is a prolonged operation on coarse coal at ordinary temperatures, and the second a short treatment on powdered coal at higher temperatures. Oxidation also occurs in coal samples stored in ordinary sample bottles. In order to gain information for this study, determinations were recently carried out on the same samples in air, in natural gas, and in vacuo. Sixteen coals were tested; three would be classed in the United States as coking bituminous coals, two as noncoking, nonslacking, bituminous coals, and the rest as subbituminous. Table 1 gives typical analyses of these coals as mined.

Jan 1, 1934

By C. H. G. Bushell, James E. Lawver, William Barbarowicz

Proper use of automatic controls in the process industries is a combination of art and science. Although many phases of automatic control theory can be expressed by precise mathematical relationships, the final control arrangement usually requires considerable effort by trial and error before the optimum control circuit is found. The failure of flotation operators to recognize that control circuits require study and plant experimentation before satisfactory operation occurs has led to a popular misconception that flotation plants simply do not lend themselves to automation. This widespread belief has been overcome to some degree in recent years by the numerous installations of automatic controls that have paid their way by increasing profits in terms of increased recoveries, lowered costs, or higher grade concentrates. WHY CONTROL ? Any form of automation must be justified in terms of ultimate return on in- vestment by improving quality, by increasing plant throughput, or by reducing the total operating costs. Generally speaking, automatic controls rarely re- place a mill operator. They assist the operator in holding important variables within predetermined limits. Large tonnage operations usually can justify a great deal of automation because an increase in one or two units of recovery results in enormous savings compared to the capital and operating costs of controls. DETERMINATION OF CONTROL The first questions in considering plant automation are: 1) What variables must be controlled? 2) What are the optimum levels of the variables? The optimum operating conditions for any process are those which maximize profits. Many of the variables active in flotation processing can be determined by experimentation in the laboratory or pilot plant 10. Although laboratory experiments can pinpoint variables, the true optimum conditions existing at plant level usually must be determined by plant scale experiments. In recent years, the concepts of detailed experimental designs in the laboratory, followed by plant experiments, have reached the stage of maturity where

Jan 1, 1962

By J. T. Eash, E. M. Wise

MANY of the platinum metal alloys are hot-forged in the early stages of reduction from ingot and substantial quantities of platinum alloys are commercially employed at very high temperatures in ammonia oxidation units, orifices for forming glass rods and fibers and as cathodes in long-life thermionic amplifiers. They are used also for electrical heating resistors, safety blowout disks, thermocouples and crucibles. The tensile properties at elevated temperatures are important in many of these situations but data on the subject are limited. Creep data also are important, but will not be covered at this time. SCOPE AND CONCLUSIONS Tensile tests were carried out at room temperature and elevated temperatures up to 11000 C. on previously well annealed samples of platinum, palladium and several of their important alloys with compositions shown in Table 1. The results are presented graphically in Figs. 1 to 4. The tensile strengths of platinum and the platinum-base alloys (with the exception of the 10 per cent rhodium-platinum alloy) at 1100° C. are from 16.6 to 18.8 per cent of the strengths of the same alloys (well annealed) at room temperature. The strength ratio of the 10 per cent rhodium-platinum alloy is 22.3 per cent, which is appreciably higher than that of the- other materials tested. The tensile strengths of palladium and the palladium alloy at 1100° C. are from 10 to 11.2 per cent of the room-temperature values. The elongations of platinum and its alloys tend to increase at tempera¬tures above 600° to 800° C., while the two samples of pure palladium show a maximum at 600° C.

Jan 1, 1938

By Donald L. Everhart

Beginning in 1906, data has been compiled on the distribution of uranium in phosphate de- posits. Particular emphasis has been placed on uranium in phosphate by a number of geologists and geochemists in the US Geological Survey in research sponsored by the US Atomic Energy Commission (now Nuclear Regulatory Commission) and the US Department of Energy (DOE) during the 30-year period from 1951 to 1981. A comprehensive study of uraniferous phosphate resources the United States and the Free World was completed, under the auspices of DOE, in 1979. Apatite is the main carrier of uranium in phosphate. Uranium generally replaces calcium in the mineral lattice. In marine phosphorite throughout the world, the uranium content is characteristically in the range of 0.005 to 0.02% by weight. Phosphorite takes in uranium by structural substitution in apatite or other mineral phases, by absorption, or by the formation of independent mineral phases. Apatite derived from the interaction of ground water, guano and limestone is typically relatively low in uranium content-in the 0.001 to 0.005% range. In primary accessory apatite of igneous rocks, as well as magmatic and metasomatic apatite segregations of alkalic rocks and carbonatite, uranium content is generally between 0.001 and 0.01%. In all these phosphate deposit types, secondary enrichment of uranium through

Jan 1, 1983