By H. S. Price, R. L. Reed, J. E. Warren

The behavior of the reverse-combustion process in a linear adiabatic system is theoretically investigated by means of an idealized physical model. T his model is described by a pair of non-linear equations involving heat and mass transfer which are coupled by a concentration-dependent reaction-rate function of the Ar-rhenius type. The differential equations governing the quasi steady-state temperature and concentration distributions are approximately solved by using either physical or mathematical simplifications. It is shown that the reverse -combustion process can be mechanistically described by simple physical models whose behavior equations can be solved formally. It is further demonstrated that the derived reverse-combustion equations can be solved numerically within the error limits for the experimental data. The theoretically predicted peak temperature-flux-velocity relationship exhibits reasonable agreement with experimental data obtained from Athabasca tar sand. The principal contribution of this work lies in its usefulness as a starting point for developing a more comprehensive theory. A description of the vaporization-coking process must be obtained; then, the theory must be extended to three dimensions to include geometrical effects and heat losses. INTRODUCTION In another paper,'" he physical processes visualized as occurring during reverse combustion have been described. In this paper, the extent to which an elementary theory can account for experimental observations is determined. Theoretical results that can be used to estimate some of the behavior characteristics of importance to this process are also presented. Since it is not possible to include all the features of the combustion mechanism of which we are currently aware, the mathematical formulation refers to the highly idealized system developed herein. This simplified physical model is based on the simultaneous transfer of mass and heat accompanied by a chemical reaction: it is described mathematically by a pair of coupled, nonlinear differential equations. Similar sets of equations have been studied extensively in the field of flame propagation; an excellent review of these investigations has been published by Evans.1 FORMULATION OF THE PROBLEM It will be recalled that the experiments are performed with a thin-walled cylindrical tube that is uniformly packed with sand and oil. The system is maintained substantially adiabatic by means of heat supplied externally in such a way that the radial temperature gradient in any plane normal to the axis of the tube approaches zero. Initially, the tube is at ambient temperature, except at one end where it is rapidly heated to a predetermined temperature. When the prescribed temperature is achieved, air is caused to flow into the cold end of the tube. As the oxygen in the air stream contacts the hot oil, a localized exothermic reaction takes place. The generated heat is conducted and convected away from the reaction zone so that definite temperature and concentration profiles are rapidly established and move uniformly in a direction opposite to that of the air flow (Fig. 1). As a consequence of this mode of oxidation, all of the oxygen in the air is consumed; then, the remaining nitrogen and the gaseous combustion products sweep out all vaporized hydrocarbons and leave an immobile hydrocarbon-coke on the sand.

?ADAIR, ARTHUR C., Corp 4th Co., 1st. Training Bat., 154th Depot Brigade. ADAMS, HENRY, Major: Chemical Warfare Service. ARLUCK, A. A Headquarters, 1st Corps of Artillery. ASKIN, THOMAS B. H Ensign. BANKS, H. R., 2d Lieut Canadian Engineers. BAYLESS, G. E. S Supply Dept. U. S. Submarine Base. BELL, L. R Co. C, 302d Engineers. BELLIS, ARTHUR E., Capt Ordnance Reserve Corps. I BIRRETT, HOWARD, Lieut., Aviation Section, U. S. Signal Corps, Ellington Field. BOISE, PAUL T 2d Regiment, 24th Squadron. ?BRADLEY, CLARENCE I Convois Automobile Section 585. BROWN, GEORGE M Co. G lot Engineer Replacement Regiment. BUCKINGHAM, ALBERT U. S. S. " Coronet," S. P. 194, Section Base No. 7. BURNS J. J Co. 1-B, E. R. O. T. C. BURT, Co. B, let Engineers Replacement Regiment. ||BYERS, WHEATON B., 2d Lieut Ordnance Dept. CANTON, WILLIAM R., Sgt Headquarters Co., 80th F. A. CARSON, JOSEPH A., Capt A.S. S. R. C.' CHAPMAN, LEWIS C. Corp 29th engineers. CHETNEY, P. C., 2d Lieut 15th Bat. Headquarters Co. CHEVRILLON Louis French Red Cross. CHIDESTER, W. B., 1st Lieut 24th Machine Gun Bat. CHURCH, JOHN L., Capt 308th Engineers. CLAGHORN, D. MONTGOMERY, 1st Lieut 45th Engineers. CLAQHORN, JAMES L., Lieut Aviation Section, Signal Corps. CLARKE, ALEXANDER F U. S. Naval Aviation Service. COMINS, WALDO H. Ca t 41st Co., 164th Depot Brigade. COOK, FREDERICK A., Capt., Engineer Reserve Corps, Asst. to Div. Engr. 79th Division. COOPER, CLAUDE H. Capt C. A. R. C., 50th Artillery. COPELAND, N. R., Lieut. ||CORBY H.. G., 1st Lieut Co. D, 109th Supply Train. CORSA, BEAN, Capt Co. D, 612th Engineers. CORTESE, EMILIO Italian Army. COULDREY PAUL S., Corp British Expeditionary Forces. || CRAGIN, RODNEY S Co. E, 115th Engineers. CURRIE, JOHN M., Ca t Royal Engineers. || CUTTING, G. W., 2d Lieut U. S. Reserves, Field Artillery. V DARRINGTON, PAUL N., 1st Lieut U. S. Infantry. DAVIS, ANGUS W., Lieut-Col British Expeditionary Forces. || DAVIS, THORNTON, 1st Lieut 13th Field Artillery. ELAND, FREDERICK A., Major Engineer Reserve Corps. DOUGLAS, JAMES $ American Red Cross. DOVE, D. R., Candidate 21st Training Battery, F. A. C. O. T. C. Dover JAMES J 6th Co. C. B. DOWS, DAVID,Capt Coast Artillery, Officers Reserve Corps. || DRAKE, M. 6., 2d Lieut Headquarters Co., 325th Infantry. I || EMMERSON, E. Roy British Navy. EVERIT, RICHARD STURTEVANT Heavy Artillery Officers' Training Camp.

Jan 1, 1923

By George H. Eldridge

The existence of phosphate of lime within the State of Florida has been known for over a decade; but until the spring of 1887, the extent and value of its deposit.;, possibly with one exception, were unsuspected. In that year Col. T. S. Moorehead, induced by a statement made by Mr. J. F. Le Baron, examined the gravels of the Peace river, recognized the importance of the deposits, acquired such tracts as were regarded as desirable, and established the pebble-phosphate industry, making his first shipment in May, 1888, to the Scott Manufacturing Company, of Atlanta, Ga. The establishment of the pebble-phosphate industry upon Peace river was followed, a year later, by the discovery in Marion county of an entirely different class of phosphate, now commonly known as hard-rock phosphate. This discovery was made early in June, 1889, by Mr. Albertus Voght, in a well which he was sinking upon his place near the site of the present town of Donnellon, about 20 miles southwest of Ocala. To it, more than to any other cause, is due the rapid and remarkable development of the present great industry of the State. It was, however, Mr. John F. Dunn, of Ocala, who turned to advantage the accidental discovery of Mr. Voght. After acquiring a knowledge as to the chemical composition and value of the material, Mr. Dunn and hid associates purchased several thousand acres of land and organized the Dunnellon Phosphate Company for active operations. From Dunnellon as a center, prospecting rapidly extended in all directions, until at the present day important mines have been opened over a well-defined tract more than 200 miles long and about 6 miles wide. This tract lies par-

Jan 1, 1893

By F. W. Davis

SOME idea may be gained of the tremendous consumption of refractories by the open-hearth steel manufacturers from a statement made by A. T. Green at a meeting reported by T11.e Industrial Chemist of London, as follows: "At a very progressive steel plant in the Midlands, with a battery of five open-hearth furnaces working. twelve months and making 3000 tons of steel per week, the cost of refractories per ton of steel produced averages about $0.50 for the actual open- hearth casting and $0.12 for those operations incidental to the rolling of the metal." .These figures, when translated into the annual tonnage of steel, represent a very considerable expenditure.

Jan 1, 1930

By B. M. Larsen, K. Heindlhofer

THIS paper describes a relatively simple electrical apparatus that, through the close analogy between the flow of heat and of electricity, enables one to solve quickly and with satisfactory accuracy many complex problems in heat flow. This device, developed in 1935, has proved especially useful in the solution of certain practical problems relating to the design and efficiency of regenerators for an open-hearth furnace or coke oven, yielding within a few hours information that would take weeks or even months to acquire by mathematical1.2 or experimental3 methods of comparable accuracy. Its description now is prompted by growing interest in such analogues, as shown by several recent papers.4.5 The analogy between flow of heat and of electricity appears to have been recognized first by Maxwell who, in his famous Treatise on Electricity and Magnetism (1881) says: The analogy between the theory of the conduction of electricity and that of the conduction of heat is at first sight almost complete. If we can take two systems geometrically similar, and such that the conductivity. for heat at any part of the first is proportional to the conductivity for electricity at-the corresponding part of the second, and if we also make the temperature of any part of the first proportional to the electric potential at the corresponding point of the second, then the flow of heat across any area of the first will be proportional to the flow of electricity across the corresponding area of the second. .. Thus, in the illustration we have given, in which flow of electricity corresponds to flow of heat, the electric potential to temperature, electricity tends to flow from places of high to places of low potential, exactly as heat tends to flow from places of high to places of low. temperature He noted, however, that this analogy is restricted: ... there is, however, one remarkable difference between the phenomena of electricity and those of heat. Suspend a conducting body within a closed conducting vessel by a silk thread, and charge the vessel with electricity. The potential of the vessel and of all within it will be instantly raised, but however long and however powerfully the vessel be electrified, and whether the body within be allowed to come in contact with the vessel, or not, no signs of electrification will appear within the vessel, nor will the body within show any electrical effect when taken out. But if the vessel is raised to a high temperature, the body within will rise to the same temperature, but only after a considerable time, and if it is then taken out it will be found hot, and will remain so till it has continued to emit heat for some time. The difference between the phenomena consists in the fact that bodies are capable of absorbing and emitting heat, whereas they have no corresponding property with respect to electricity. According to this statement the application of the analogy would be limited to problems of steady flow that do not involve heat-capacity effects. In spite of this

Jan 1, 1945

By James P. Kimball

The object of the present memoir is to pot on record some practical experiments by the writer in smelting a silicions native magnetite with no other flux than the silicates of its own gangue.' This work was undertaken in the spring of 1878 for Messrs. Naylor & Co., of' Boston, to whom I am indebted for the privilege of here communicating its results, these having hitherto only been simply announced.* So far as I am aware these are the first instances of the kind ill this country that non-calcareous; or rather non-carbonatbed, magnetite have successfully been used strictly alone as self-fluxing ores in the blast furnace; that is, without the addition of' calcareous flux in the form either of limestone, quicklime, calcareous ore, or basic (calcareous) slag. Previous to the spring of 1878, when the Chateaugay magnetic ore was first brought to illy notice. its use had been limited to Catalan forges, after " separation " at the ore bed. The blooms and billets made from it in the several forges of Messrs. Weed $ Williams, and of Mr. Williams, were well known in the trade as among the best in the market. Tile Chateaugay ore beds proving of great magnitude, and the ore exceptionally low in phosphoric acid, it commended itself for blast-furnace purposes to Messrs. Naylor & Co., who employed me to blow-in the charcoal furnace at Pittsford, Vt., on this ore in the spring of 1878, a previous trial of this ore in the same furnace in the fall of 1877 having proved abortive. This was therefore the first time that Chateaugay ore was successfully smelted in a blast furnace, although since well known as a blast-furnace ore possessing superior and exceptional qualities. The Pittsford furnace, although rebuilt in 1844, and subsequently improved by the former owner, the late J. Prichard, is one of the few furnaces of the old type with open breast (Sumpfofen) still active in this country, Its improvements 011 furnaces of the period,

Jan 1, 1881

Jan 4, 1951

By P. W. Bridgman

It is a commonplace that experimental physics in the last few decades has discovered manifold complexities in the atomic and subatomic levels, where it was thought for hundreds of years that no structure existed, as is witnessed by the derivation of the word "atom" itself. The field of exploration opened by the discovery of the electrical structure of the atom was so fundamental, rich and stimulating, that it has been almost exclusively cultivated by physicists since they obtained their first intimations as to the nature of the basic facts. Only within the last few years has it begun to dawn on us that we have overshot an enormous domain in which are situated many phenomena of fundamental importance for all the practical uses to which we put matter in our daily lives; the domain, that is, of most of the phenomena of interest to the biologist and the metallurgist. Furthermore, we are beginning to find that this intermediate domain is not entirely simple, but that it contains unsuspected complexities, some of them derived from the complexities of structure on the atomic and subatomic levels, and some of them emergent as matter collects itself into large aggregates, which often offer the key to the explanation of hitherto baffling large-scale properties of matter. Today I want to describe and consider some of these newly discovered complexities in the behavior of matter in bulk. The application to metallurgical problems is not always direct, but I hope to be able to suggest that such general notions as to structure as those here discussed must have important reactions on our attitude toward the problems of metallurgy. Three different sorts of phenomena of this kind to which I shall direct your attention are (1) the so-called structure sensitive phenomena, (2) complexities of such a nature that they are masked by the presence of extraordinarily small amounts of impurities, and (3) complexities depending on internal molecular rearrangements which can be understood only from the point of view of the quantum theory.

Jan 1, 1931

By H. C. Fiedler

X HE development of the cube-on edge secondary re-crystallization texture in Si-Fe strip requires that normal grain growth be restrained. It has been shown that the degree of restraint and hence the completeness of secondary recrystallization depends upon the size and number of second-phase particles, which in turn is dependent upon the prior processing history.1y2 The purpose of this note is to show that, for heats in which manganese sulfide particles are providing the restraint to grain growth, the choice of hot rolling temperature depends upon the manganese content. The making and processing of the heats to the final gage of 0.012 in. has been described.3 The compositions are given in Table I. Apparent in Fig. 1 is the decrease in the ability of strips hot-rolled from 1175°C to undergo secondary recrystallization as the manganese content increases. It has been shown that 1175°C is below the solubility temperature of 0.014 pet S in even the 0.038 pct Mn alloy: and the observed behavior is attributed to an increasing fraction of the sulfur forming large manganese sulfide particles at the heating temperature for hot rolling. This fraction of the sulfur is thus unavailable to subsequently form the small, uniformly dispersed particles which are needed to restrain normal grain growth. Since the sulfur is completely in solution at 1325°C,3 strips from all three alloys show strong secondary recrystallization behavior when hot-rolled from that temperature.

Jan 1, 1969

By R. F. Dickerson, D. A. Vaughan, A. F. Gerds

ALTHOUGH the metallurgy of uranium has been under intensive study since the early 1940's, no systematic effort has been made to identify the non-metallic inclusions in uranium. Uranium carbide (UC), which is probably the most common inclusion found in graphite-melted metal, has been tentatively identified by previous investigators, but the other nonmetallic inclusions have received little attention. Since metallography is a valuable tool in metallurgical studies, the metallographic identification of the nonmetallic inclusions in uranium is important. Such an investigation has been completed and the identification of slag-type inclusions and of uranium monocarbide, uranium hydride, uranium dioxide, uranium monoxide, and uranium mononitride is described. Metallographic Preporation It is often possible to prepare specimens for metal-lographic examination equally well by several methods. The specimens which were examined in this work were prepared by one of two acceptable methods. For the convenience of the reader, both methods will be discussed in detail and will be referred to simply as Method I or Method II in the subsequent sections. For both Methods I and 11, specimens for microscopic examination usually were mounted either in bakelite or in Paraplex room temperature mounting plastic. Method I—Specimens were ground in a spray of water on a revolving disk covered successively with 120-, 240-, and 600-grit silicon carbide papers. It was necessary to perform the final grinding operation carefully on worn 600-grit paper to keep the scratches as fine as possible. After washing and drying, the specimens were polished for 3 to 4 min on a slow speed wheel (250 rpm) covered with a medium nap cloth. Diamet Hyprez Blue diamond polishing paste, Grade 00, 0 to 2 µ, was used as abrasive with kerosene as lubricant on the wheel. Specimens were washed thoroughly in alcohol and final polished electrolytically in an electrolyte composed of 1 part stock solution (118 g CrO, dissolved in 100 cm3 H2O) with 4 parts of glacial acetic acid. A stainless steel cathode was used. At an open circuit potential of 40 v dc, a polishing time of 2 sec retained inclusions well with the bath at room temperature. If additional etching was required to sharpen the interface between the metal and the inclusions, an electrolyte composed of 1 part stock solution (100 g CrO3 and 100 cm8 H20) and 18 parts glacial acetic acid was used at room temperature. Best results were obtained by etching for from 10 to 15 sec at 20 v dc in the open circuit. Surfaces obtained by this method are suitable for microscopic examination. However, if desired, they may be etched further with other chemicals. Method 11—Rough grinding was done on a wet 180- or 240-grit continuous grinding belt. The specimen was then ground by hand successively on 240-, 400-, and 600-grit silicon carbide papers in a stream of water. Final polishing was accomplished on a 4 in. high speed wheel (3400 rpm) covered with Forstmann's cloth. Linde B levigated alumina, suspended in a 1 volume pet chromic acid solution, was the abrasive. Specimens usually were polished in 5 min or less by this technique. Often the inclusions present in the metal were identified in the mechanically polished condition. When etching was required to outline inclusions more sharply, one of the two following methods was used. In the first method, the specimen is etched lightly while electropolishing in the chromic-acetic acid solution described above (1 part of stock solution to 4 parts of acetic acid). The electrolyte was refrigerated in a dry ice-ethyl alcohol bath and specimens were etched at 60 v dc on the open circuit for 2 or 3 cycles of 3 to 4 sec each. The second technique utilizes electrolytical etching at about 10 v dc (open circuit) in a 10 pet citric acid solution at room temperature. X-Ray Diffraction Technique The major problem in the identification of inclusions in metals by X-ray diffraction techniques is the extraction of a sufficient amount of each type of inclusion to obtain an X-ray diffraction pattern. In the present study, X-ray diffraction patterns were obtained from individual inclusions of the order of 10 µ diam. The polished and etched samples shown in the micrographs were examined at a magnification of X54 or XI00 with a binocular microscope. This allowed sufficient working distance to extract the inclusions with a needle probe for powder X-ray diffraction analysis. Friable inclusions such as MgF2, CaF2, UO2, and UH3 could be freed from the metal by probing the as-polished and etched surface. The fine particles then were picked up on the end of a Vistanex-coated glass rod (0.002 in. diam) which was held in a brass adapter made to fit the powder X-ray diffraction camera. The end of the glass rod was centered in the path of the X-ray beam. In the case of the UC, UO, and UN inclusions which are smaller in size, more metallic in appearance, and less friable than the other inclusions, it was necessary to etch the inclusion in relief before extraction. UN inclusions etched sufficiently in relief in the electrolytic polishing solution described in Methods I and II by increasing the polishing time. UN inclusions were relief etched by extending the

Jan 1, 1957

By Charles P. Williams

The lead-bearing area of Missouri has been subdivided, geographically, into the Southeastern, the Central, and the Southwestern

By C. A. Hansen

Page Introduction............................206 Power Characteristics in Zinc Sulfate Electrolysis........... 207 Current Efficiency......................... 207 Corrosion Rates..........................216 Voltage Required by the Zinc Cell..................219 Power Requirements of the Zinc Cell ................221 Impurities in Zinc Electrolyte.....................222 Non-cumulative Impurities.....................223 Cumulative Impurities ....................226 Impurities in General........................228 Temperature and the Stability of the Zinc Cell..............229 Practical Expedients for Control of the Zinc Cell...........234 Acknowledgments...........................234 Appendix................................235 Discussion...................:.......... - 236 Introduction It has been the experience of the writer, during some five years' work with electrolytic zinc, that the zinc cell is perhaps more sensitive to impurities in the electrolyte than the analytical methods as yet developed for the chemical identification and determination of these impurities; but that, when proper purification methods have been applied to a given solution, the behavior of the cell is quite independent of the original sources from which the zinc sulfate has been derived. It has also appeared that the behavior of the zinc cell is the best and surest check on the correctness and thoroughness of the purification methods used, because it indicates the presence of both current impurities and cumulative impurities derived from the leaching of the ore; it also indicates whether these impurities are current or cumulative, at least in so far as they are of serious importance commercially.

Jan 1, 1919

By F. F. Aplan, P. H. de Bruyn

The adsorption density of hexyl mercaptan was measured at the gold-solution and the gold-vapor interfaces. This collector is strongly adsorbed at low concentrations, a monomolecular layer being formed at the gold-solution interface at concentrations as low as 2 x 10'6 moles per liter. A maximum contact angle of 83 ± 3° is observed. From a thermodynamic analysis of the experimental data the changes in surface tension at the gold-gas and gold-solution interface are calculated. The data also suggest that the adsorption density of mercaptan at the gold-gas interface exceeds that at the gold-solution interface. In the equilibrium state, a simple flotation system consists of three phases, the solid to be floated, air, and an aqueous solution in stable contact along a line. During the process leading to this final state, a solid-gas interface is created at the expense of a portion of the liquid-gas and solid-liquid interfaces. This change of state is achieved by addition of a collector and, if necessary, suitable modifying agents to the system. By a combined application of the Gibbs Adsorption and the Young Equations, de Bruyn, Overbeek and Schuhmannl were able to show theoretically that the equilibrium distribution of the collector at all three interfaces determines the magnitude of the contact angle. Their analysis led them to conclude that the equilibrium adsorption density of the collector at the solid-gas interface exceeds its density at the solid- liquid interface. This paper succeeded in focussing attention on the neglected role of the solid-gas interface in flotation. In recent years the application of radiotracer, infrared, electrochemical and electro-kinetic techniques to studies of the solid-liquid interface2-5 enhanced our understanding of adsorption processes at this interface. Except for the measurement of contact angles, the solid-gas interface received no attention in fundamental flotation studies. In an attempt to apply the analysis of de Bruyn, Overbeek and Schuhmann to a simple flotation system, an investigation of the adsorption of hexyl mercaptan onto gold was undertaken. Gold was chosen as the solid phase in order to keep the number of dissolved chemical species in the solution phase to a minimum. Hexyl mercaptan (1 - hexanethiol) was selected as collector because its relatively high vapor pressure at room temperature makes it possible to obtain adsorption measurements at the solid-gas interface. This flotation system consists, therefore, of a pure solid phase (gold), an aqueous solution of a weakly dissociated collector (1 -hexanethiol), and a gaseous phase, nitrogen saturated with respect to both water vapor and mercaptan vapor. EXPERIMENTAL MATERIALS AND METHODS Materials: Liquid 1-hexanethiol (C6H13SH) was obtained from Distillation Products Industries and was further purified by double distillation. The purity of the final product was established by boiling point and refractive index measurements. For the adsorption studies from aqueous solution, the radiotracer element, sulfur-35, (half life 87.1 days, 0.169 Mev beta ray) was synthesized into the mercaptan by Tracerlab Inc., Boston, Mass. A close boiling fraction of the synthesized compound was used in the adsorption studies. The specific activity of the radioactive compound was 10 millicuries per gram.

Jan 1, 1963

By H. A. Doerner

PROPOSALS to use hydrocarbon or natural gases for the reduction of zinc from oxide materials may be traced back through Patent Office files to the early years of the present century. Natural gas at rates cheap enough to compete with solid fuels has been available at or near one major zinc district for more than a decade. That the seemingly meritorious and economically interesting applications of these proposals have not devel-oped into workable processes for direct production of zinc by natural gas cannot be completely ascribed to the proverbial conservatism of the zinc industry. It is possible to produce spelter commercially in normal times from zinc oxide and carbonaceous reducing agents without having a very precise understanding of the chemistry of the process. The reduc-tion by hydrocarbons is not, however, in this class, and the technical complexity of this reduction metallurgy and chemistry prohibits solution of the inherent difficulties by the "hit and miss" methods that are some-times thought to be practical. In a thermodynamic study of the chemistry of zinc smelting, Maier1 made a preliminary study of the chemistry of the use of methane for reducing zinc oxide by thermodynamic means, pointing out that the following reactions, the limits of which could be theoretically predicted, were important: ZnO + CH4 = Zn(gas) + CO + 2H2 [1] CH4 = C -I- 2H2 [2] ZnO + CO = Zn(gas) + CO2 [3] ZnO + H2 = Zn(gas) + H2O [4] Other possible reactions, not discussed in the reference quoted, are: CO2 + CH4 = 2CO + 2H2 [5] H2O + CH4 = CO + 3H2 [6]

Jan 1, 1933

By G. Caetani, E. Burt

Jan 1, 1907

By Warnie Flint

PERSONAL INJURY ACCIDENTS According to statistics compiled by the National Safety Council, US Bureau of Mines, American Medical Association, and other agencies, accidental injuries cause more deaths than all the leading diseases. NO one is immune to an accident. Probably the best way to describe an accident is to say that it is an unexpected happening. The automobile driver is not expecting a terrifying crash, the electrician does not expect to be electrocuted, nor is the coal miner expecting the roof to fall on him. All personal injuries will not result in death. There is a multitude of victims who arc living proof of what accidents can mean to an individual-victims who are blind, paralytic, missing arms, legs, etc. In most instances the earning power of these individuals is gone, and they arc utterly dependent upon family or welfare. For many years there seemed to be an attitude that prevailed in industrial America that accidents were inevitable, and that so many fatalities and injuries should be expected. This, of course, was utter nonsense. Since the birth of such organizations as The National Safety Council, American Society of Safety Engineers, and the US Bureau of Mines, much progress has been made in reducing accidents. The enactment of compensation laws greatly contributed to the progress that has been made. Does this mean that all accidents can be prevented? Unfortunately, it does not. Human psychology indicates that men will work unsafely or perform unsafe acts for the following reasons : 1) Lack of Knowledge or skill. 2) Conflicting motivations, such as: (a) to be more conformable, (b) to save time or effort, (c) to be accepted by a group. 3) Physical or mental condition. Nearly everyone desires his own safety, hut not all individuals are willing to do what they know to do to insure their own safety.

Jan 1, 1981

By R. H. Fillnow, D. J. Mac

IT has been demonstrated that alloys in systems structurally analogous to steel undergo reactions during heat treatment similar to those of steel, and yet very little work has been done on such systems, particularly from the standpoint of isothermal transformation. The literature shows that most of the isothermal work has been done on copper-alu-minum alloys.'-3 One paper has been reported on a eutectoid copper-silicon alloy,' and one on iron-nitrogen alloys.' There are no published reports of previous investigations on the isothermal transformation of a eutectoid beryllium bronze. At least two papers have been reported on isothermal age-hardening phenomena in beryllium-copper alloys of lower beryllium content.5,6 No information on eutectoid transformations in this alloy is given in Rimbach's book, "Beryllium." ' This paper reports the results of an investigation on the isothermal transformation characteristics of a eutectoid beryllium bronze. Materials Used and Procedure The eutectoid beryllium bronze used in this investigation was centrifugally cast at the Ampco Metal Co., Inc.. Milwaukee. Wis. A master beryl-lium-copier alloy, purchased from the Brush Beryllium Co., was used to make the beryllium addition to the copper. The alloy was melted under a protective carbon cover and Centrifugally cast into a graphite mold preheated to 920°F. Some trouble with segregation of beryllium in the melt was encountered but was eliminated by violent stirring during melting and pouring. Since very thin .specimens were used for the various heat treatments, only one casting of the four prepared was necessary for the complete isothermal study, thus eliminating any discrepancies caused by a change in composition. The analysis of this casting was 94.035 pct copper and 5.965 pct beryllium. A slight trace of iron was found. The castings were sawed into specimens approximately 3/32 in. in thickness. The specimens were first given an "austenitizing" heat treatment at 788°C, well within the single phase beta region, in a vertical tube furnace. The specimens were then quenched individually into an adjacent molten salt bath and held there for a definite time, after which they were quenched into water at room temperature. Temperature was held to ± 2°C in the salt bath. No homogenizing treatment was given the specimens other than the soak at 788°C. Despite the fact that this was a cast alloy, no evidence of segregation or coring was found in the microstructure of any specimen, either as cast or as heat-treated. Upon completion of the heat treatment, the speci-mens were subjected to metallographic examination

Jan 1, 1951

By J. Szekely, G. P. Martins

A formulation is given for describing the rate of expansion of spherical bubbles rising in liquids the freeboard of which is evacuated. The computer solution of the resultant differential equations has shown that, for low freeboard pressures (less than about 5 mm Hg), on approaching the free surface the bubbles expand much less rapidly than predictable from equilibrium considerations. In other words, in this region the pressure inside the bubbles will be significantly larger than the static pressure in the liquid corresponding to the position of the bubble. These theoretical predictions were confirmed by experimental work, using two-dimensional air bubbles rising in mercury. The important consequence of these findings is that the expansion of gas bubbles in vacuum degassing operations will be a great deal less than expected from hydrostatic considerations. This would lead to a significant reduction in the available interfacial area and may explain the apparent poor efficiency of many vacuum degassing units. VACUUM degassing as a treatment for liquid steel has gained widespread popularity in recent years; the number of known installations exceeds several hundred at the present time.' Although much information is available on both the thermodynamics of the system and the overall performance of various industrial units, much less is known about the fundamental aspects of the process kinetics.2-4 The basic physical situation common to virtually all vacuum degassing operations is the interaction between gas bubbles (swarms of bubbles) and the surrounding molten metal, held in a container, the freeborad of which is at a low absolute pressure. Once formed (or introduced from an external source) the bubbles will ascend, due to the buoyancy forces, and, during this ascent, a significant increase in their volume will occur. This progressive increase in the bubble volume is due to two factors: a) the continuous reduction in the static pressure acting on the bubble during its rise; and b) mass transfer into the bubble from the surrounding molten steel. In a recent paper Richardson and Bradshaw developed equations5 for describing mass transfer into gas bubbles from molten metals at reduced pressures. However, in deriving these expressions it was assumed that the pressure inside the bubble was identical to the static pressure in the adjacent liquid. In other words, the volume of the bubble was considered to be in equilibrium with the pressure of the fluid adjacent to it. This assumption, thus their analysis presented, was thought to be reasonably accurate for most of the bubble's ascent; however, it was unlikely to be valid in the immediate vicinity of the free surface, held at a low pressure. It was pointed out in the discussion6 that the region close to the surface may be of considerable importance as both the driving force and the interfacial area available for mass transfer are at their highest value here. The ' 'anomalous" behavior of gas bubbles when approaching a free surface at low pressures was recently confirmed in a preliminary investigation by Szekely and Martins. ?1 Here high-speed motion photography was used to study air bubbles rising in a column of n-tetradecane with a freeboard pressure of 0.1 mm Hg. It was found that significant distortion of the bubbles occurred on approaching the free surface; furthermore, the expansion observed was much less than what one could expect from hydrostatic considerations, i.e., factor a previously discussed. It follows from the foregoing that a detailed study of these phenomena would be justified both from fundamental considerations and because of their potential relevance to technology. The purpose of the paper is to present a more realistic formulation for the expansion of a gas bubble approaching a low-pressure region, together with a comparison of the theoretical prediction with experimental measurement. An inert bubble will be considered in the first instance; it is thought that the understanding of the fluid mechanics is an essential first step toward the realistic formulation of the mass transfer process. This latter problem will be the subject of a subsequent publication. FORMULATION The Physical Model. Consider a spherical bubble, of initial radius Ro, rising in a fluid, having a density pL. Initially let the bubble be at a distance H from the free surface, and at a pressure Pgo, as illustrated in Fig. 1. Pgo, the initial pressure in the bubble, is given by the following equation: pgo = Po = Ptp +pLgH [ la] where Po is the pressure in the liquid corresponding to the initial position of the bubble and Ptp is the pressure at the free surface. The fluid pressure at

Jan 1, 1970

By George A. Morrison

THE Columbia Chemical Division of the Pittsburgh Plate Glass Co. is at Barberton, Ohio, 35 miles south of Cleveland. For many years large tonnages of limestone have been brought to the Barberton plant from distant points. The stone is here burnt in vertical kilns, the resultant product then hydrated and the hydrated lime used in chemical processing. To eliminate the expense of these shipments, the company decided to investigate a limestone bed known to exist on company property at Barberton, where the stone is used. The bed lay at a depth of more than 2000 ft. and was known locally as the "Deep Lime." Chemical analyses of sludge from churn-drill holes made some years ago proved that the limestone was of sufficient purity to warrant diamond-drill exploration. Four diamond-drill holes were put down at well-spaced intervals, to represent fairly an area of four miles by one mile. Cores logged as to chemical and physical conditions were found to compare closely, and to corroborate the earlier evidence that the limestone was of superior quality for chemical use. A plant of 300 tons per hour was subsequently decided upon. SITE The yard at the chemical plant was already so congested that location of the projected mine within its area could not be considered. Eventually a site was selected 2 miles northwest of the plant, near the main line of the Erie Railroad. Here 412 acres were owned outright by the company and stone rights were obtained on 250 additional acres. This location required a transportation line of nearly 2 miles (8800 ft.), crossing two major highways, and to avoid interruption of deliveries to the plant, overpasses were planned. GEOLOGY The limestone in the immediate vicinity lies about 2200 ft. below the surface. Geologists* identify this stone as Delaware of Devonian age. It is overlain by 18 ft. of unconsolidated (sand and gravel), 100 ft. of water-bearing sandstone, and finally 2080 ft. of shale into which sandstone in thin layers is interbedded. The contact of shale and limestone is abrupt, flat-lying and very pronounced. Berea sandstone, often found at 520 ft., is absent, but Euclid sandstone was encountered, together with a seepage of oil and a small amount of methane gas. The limestone bed itself is 345 ft. thick, and overlies 200 ft. of gypsum. The lower part becomes dolomitic as it approaches the gypsum. A detailed study of the drill cores indicates that the upper 50 ft, are highest in lime and reasonably low in silica. The physical make-up shows several separating cherty layers. These occur at definite horizons and cause distinct partings, which become horizontal planes of

Jan 1, 1943

By Charles Austin

IN a recent paper the authors1 discussed the reactions to tempering of hypereutectoid steels quenched from 1000° C., as revealed by studies on changes in hardness, electrical resistivity, coercive force and metallo-graphic characteristics. The data, which related specifically to temper-ing temperatures of 550°, 650° and 710° C., for varying periods up to 125 hr., permitted the following important conclusions: 1. The rate of softening of the steels at the temperatures examined differed markedly although the steels were of "similar" general chemi-cal composition. 2. The temperature of maximum softening spread over a range from about 650° C. to the eutectoid inversion. 3. The divergence in behavior was ascribed, at least in part, to a profound difference in tendency to graphitization on annealing at sub-eutectoid temperatures. 4. The mode of spheroidization of the cementite, as revealed by metallographic studies, also varied considerably in the different steels. The purpose of the present investigation is to pursue further the study of the difference in behavior of the steels on tempering over a wider range of temperature. To this end the following features have received particular attention: 1. Comparison of temperatures of maximum softening of the various steels when the quenched samples were tempered for 5 hr. and for 75 hr. followed by furnace cooling and by quenching in water. 2. Determination of the effect of quenching temperature, prior to tempering, on the rate of softening. Quenching temperatures of 1000° and 850° C. were used in the investigations. 3. Examination of the microstructures obtained with the various heat-treatments employed.

Jan 1, 1938